Effects of amorphous nano-silica additions on mechanical and durability performance of SCC mixtures

  • In the recent years the application of nanotechnology in building materials has increased exponentially. One of the most referred and used nano-materials is amorphous silica with particles size in the nano-range, even though its application and effect in concrete has not been fully understood yet. It has been reported that nano-silica (nS) addition increases the compressive strength and reduces the overall permeability of hardened concrete due to the pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified microstructure (nano-filler and anti leaching effects). These effects enhance the durability of concrete structures such as bridges, quays or off-shore oil facilities in marine environments. In this study two different types of nano-silica were applied in self-compacting concrete (SCC), both having similar particle size distributions (PSD) but produced in two different processes (fumed powder silica and precipitated silica in colloidal suspension).In the recent years the application of nanotechnology in building materials has increased exponentially. One of the most referred and used nano-materials is amorphous silica with particles size in the nano-range, even though its application and effect in concrete has not been fully understood yet. It has been reported that nano-silica (nS) addition increases the compressive strength and reduces the overall permeability of hardened concrete due to the pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified microstructure (nano-filler and anti leaching effects). These effects enhance the durability of concrete structures such as bridges, quays or off-shore oil facilities in marine environments. In this study two different types of nano-silica were applied in self-compacting concrete (SCC), both having similar particle size distributions (PSD) but produced in two different processes (fumed powder silica and precipitated silica in colloidal suspension). The influence of nanosilica on SCC was investigated with respect to the properties of concrete in the fresh state (workability) and hardened state (mechanical properties and durability). Additionally, the densification of microstructure of the hardened concrete was verified by SEM and EDS analyses. The obtained results demonstrate that an efficient use of nano-silica in SCC can improve its mechanical properties and durability. Considering the reactivity of the two nano-silica studied, colloidal type shown more reactivity at early age, which influenced all the final SCC properties.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:G. Quercia, P. Spiesz, Götz Hüsken, J. Brouwers
Persönliche Herausgeber/innen:S. Jacobsen, H. Justnes, R. Cepuritis, K. Hornbostel, Y. Peng
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):ICDC 2012 - 1st International congress on durability of concrete (Proceedings)
Jahr der Erstveröffentlichung:2012
Erste Seite:A2-4, 1-15
Freie Schlagwörter:Chloride and Freeze-thaw; Concrete; Durability; Nano-silica; Self Compacting
Veranstaltung:ICDC 2012 - International congress on durability of concrete
Veranstaltungsort:Trondheim, Norway
Beginndatum der Veranstaltung:2012-06-18
Enddatum der Veranstaltung:2012-06-21
ISBN:978-82-8208-031-6
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Nein