Zurück zur Trefferliste

Advanced life prediction by microstructural simulation of short cracks in a low carbon steel

  • This paper deals with life prediction by observation and simulation of short fatigue cracks in cyclically loaded smooth and notched specimens made of 0.15 wt-% carbon steel SAE1017. The measured crack behaviour was simulated in a microstructural environment. Reference tests under constant amplitude loading allowed to determine model parameters and hence a reasonable life prediction by simulation resulted even for service loading. Short crack behaviour was a measurable property for damage also to compare smooth and notched specimens.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Joachim Hünecke, Dieter Schöne, Dietmar Klingbeil, Claus-Peter Bork
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):International Journal of Fatigue
Jahr der Erstveröffentlichung:2006
Verlag:Elsevier
Verlagsort:Oxford
Jahrgang/Band:28
Ausgabe/Heft:9
Erste Seite:993
Letzte Seite:1000
Freie Schlagwörter:Ermüdung; Fatigue; Gefüge; Kurze Risse; Lebensdauer; Life prediction; Microstructure; Notch; Service loading; Short cracks; Simulation
DOI:10.1016/j.ijfatigue.2005.07.049
ISSN:0142-1123
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:17.07.2006
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.