Probing the heat affected zone by chemical modifications in femtosecond pulse laser ablation of titanium nitride films in air

  • A new approach is presented to quantify the so-called "heat affected zone" (HAZ) during femtosecond laser pulse processing. Ablation of titanium nitride (TiN) thin films (~3 μm thickness) by multiple femtosecond laser pulses (τ=130 fs, λ=800 nm) in air environment was studied by means of two different surface analytical methods both being sensitive to chemical alterations at the surface. Scanning Auger electron microscopy was applied for a visualization of the spatial distribution of specific elements (Ti, O) within the laser-modified areas. The chemical state of the irradiated surface was revealed by complementary x-ray photoelectron spectroscopy. Both methods were used for a depth-profiling chemical analysis (tracking the elements Ti, N, O, and C) using an Ar-ion beam for surface sputtering. In a narrow laser fluence range slightly below the ablation threshold of TiN significant superficial oxidation can be observed leading to the formation of substoichiometric TiO2-x. At fluencesA new approach is presented to quantify the so-called "heat affected zone" (HAZ) during femtosecond laser pulse processing. Ablation of titanium nitride (TiN) thin films (~3 μm thickness) by multiple femtosecond laser pulses (τ=130 fs, λ=800 nm) in air environment was studied by means of two different surface analytical methods both being sensitive to chemical alterations at the surface. Scanning Auger electron microscopy was applied for a visualization of the spatial distribution of specific elements (Ti, O) within the laser-modified areas. The chemical state of the irradiated surface was revealed by complementary x-ray photoelectron spectroscopy. Both methods were used for a depth-profiling chemical analysis (tracking the elements Ti, N, O, and C) using an Ar-ion beam for surface sputtering. In a narrow laser fluence range slightly below the ablation threshold of TiN significant superficial oxidation can be observed leading to the formation of substoichiometric TiO2-x. At fluences above the ablation threshold, an increased titanium concentration is observed within the entire ablation craters. Following upon sputter removal the elemental distribution into the depth of the nonablated material, the results allow an estimation of the heat-affected zone for femtosecond laser ablation in air environment. According to our analyses, the HAZ extends up to a few hundreds of nanometers into the nonablated material.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Jörn BonseORCiD, Jörg KrügerORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of applied physics
Jahr der Erstveröffentlichung:2010
Verlag:American Institute of Physics
Verlagsort:Melville, NY
Jahrgang/Band:107
Ausgabe/Heft:5
Erste Seite:054902-1 - 054902-5
Freie Schlagwörter:Femtosecond laser ablation; Heat affected zone; Photoelektron spectroscopy; Scanning Auger electron microscopy; Titanium nitride; X-ray
DOI:10.1063/1.3311552
URL:http://link.aip.org/link/?JAP/107/054902
ISSN:0021-8979
ISSN:1089-7550
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:03.03.2010
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.