Hydrothermal stability of zeolite SAPO-11

  • The hydrothermal stability of SAPO-11 was studied in water of autogenous pressure as function of the temperature. SAPO-11 remained crystalline up to 190 °C. Thereby, it was observed, parent as well as hydrothermally treated samples showed similarities to the isotypic structure of zeolite AlPO-11 called here AELdry. After fully hydration of the samples, AELdry changed completely into a hydrated AELwet structure of another framework symmetry. The transition from calcined to hydrated state was reversible for both the parent and the hydrothermally treated samples. 27Al and 31P NMR MAS spectra showed a single resonance typical for AlPO4 type tetrahedra for the calcined parent and hydrothermally treated samples. Upon hydration, the single AlPO4 resonance signal split into three different signals as is the case for the corresponding 31P signals. By means of NH3-TPD measurement a loss of acidity was detected after the hydrothermal treatment as follows from a framework desilication. NitrogenThe hydrothermal stability of SAPO-11 was studied in water of autogenous pressure as function of the temperature. SAPO-11 remained crystalline up to 190 °C. Thereby, it was observed, parent as well as hydrothermally treated samples showed similarities to the isotypic structure of zeolite AlPO-11 called here AELdry. After fully hydration of the samples, AELdry changed completely into a hydrated AELwet structure of another framework symmetry. The transition from calcined to hydrated state was reversible for both the parent and the hydrothermally treated samples. 27Al and 31P NMR MAS spectra showed a single resonance typical for AlPO4 type tetrahedra for the calcined parent and hydrothermally treated samples. Upon hydration, the single AlPO4 resonance signal split into three different signals as is the case for the corresponding 31P signals. By means of NH3-TPD measurement a loss of acidity was detected after the hydrothermal treatment as follows from a framework desilication. Nitrogen and water adsorption decreased systematically. At 210 °C a non-zeolitic, non-porous phase was irreversibly formed. The XRD pattern of this phase shows resemblance to a synthetic aluminium phosphate of the tridymite structure type.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:W. Lutz, R. Kurzhals, S. Sauerbeck, H. Toufar, J.-C. Buhl, T. Gesing, Wolfgang Altenburg, Christian Jäger
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Microporous and mesoporous materials
Jahr der Erstveröffentlichung:2010
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:132
Ausgabe/Heft:1-2
Erste Seite:31
Letzte Seite:36
Freie Schlagwörter:Hydrothermal stability; Phase transformation; SAPO-11; Silicoaluminophosphate; Zeolite
DOI:10.1016/j.micromeso.2009.08.003
ISSN:1387-1811
ISSN:1873-3093
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:19.04.2010
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.