17O nuclear magnetic resonance study of Na2O-P2O5 glasses

  • The preparation and structural investigation of 17O-enriched xNa2O–(100-x)P2O5 glasses (46.5<=x<=62.8) by nuclear magnetic resonance (NMR) is described. Enriched phosphoric acid was prepared by hydrolysis of PCl5 with 17O-enriched water and neutralized with sodium carbonate. The sodium metaphosphate was then melted at 800 °C for 15 h and quenched. Polyphosphate and ultraphosphate glass compositions were prepared by remelting the metaphosphate with sodium carbonate and phosphorus pentoxide, respectively. 31P magic angle sample spinning (MAS) NMR was used to determine the Na2O/P2O5 content in the glasses. 17O NMR spectra (quadrupole echo for non-rotating samples and multiple-quantum excitation for rotating samples (MQMAS)) show two oxygen sites in the samples with large quadrupolar coupling constants (4.7 and 7.7 MHz), in accordance with the high phosphorus electronegativity. According to the correlation of 17O quadrupolar constants with bond ionicity, these two components are attributedThe preparation and structural investigation of 17O-enriched xNa2O–(100-x)P2O5 glasses (46.5<=x<=62.8) by nuclear magnetic resonance (NMR) is described. Enriched phosphoric acid was prepared by hydrolysis of PCl5 with 17O-enriched water and neutralized with sodium carbonate. The sodium metaphosphate was then melted at 800 °C for 15 h and quenched. Polyphosphate and ultraphosphate glass compositions were prepared by remelting the metaphosphate with sodium carbonate and phosphorus pentoxide, respectively. 31P magic angle sample spinning (MAS) NMR was used to determine the Na2O/P2O5 content in the glasses. 17O NMR spectra (quadrupole echo for non-rotating samples and multiple-quantum excitation for rotating samples (MQMAS)) show two oxygen sites in the samples with large quadrupolar coupling constants (4.7 and 7.7 MHz), in accordance with the high phosphorus electronegativity. According to the correlation of 17O quadrupolar constants with bond ionicity, these two components are attributed to bridging P–O–P and non-bridging P–O...Na oxygens. The average P–O–P bond angle is estimated with the quadrupolar asymmetry derived from the fit of the static echo spectra. The MQMAS spectrum shows a distribution of non-bridging oxygen chemical shifts, attributed to a variation of bond length and angle.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:M. Zeyer, L. Montagne, V. Kostoj, G. Palavit, D. Prochnow, Christian Jäger
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of non-crystalline solids
Jahr der Erstveröffentlichung:2002
Verlag:North-Holland Publ. Co.
Verlagsort:Amsterdam
Jahrgang/Band:311
Ausgabe/Heft:3
Erste Seite:223
Letzte Seite:232
ISSN:0022-3093
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:27.10.2005
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.