  • This paper indicates that the tribological behavior under dry sliding of a Fe3Al-niobium carbide (NbC) composite prepared by pyrometallurgical synthesis was compared to NbC-based hard metals bonded by cobalt or Fe3Al. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC with ∼60% NbC was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks, as a metallurgical interphase was formed between matrix and NbC grains.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Mathias WoydtORCiD
Koautor*innen:H. Mohrbacher
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):39. Int. Conf. Expos. on Advanced Ceramics and Composites
Jahr der Erstveröffentlichung:2015
Freie Schlagwörter:Cobalt; Grains; Hard metals; Matrix; Metal matrix composites; Niobium carbide
Veranstaltung:39. Int. Conf. Expos. on Advanced Ceramics and Composites
Veranstaltungsort:Daytona Beach, Florida, USA
Beginndatum der Veranstaltung:25.01.2015
Enddatum der Veranstaltung:30.01.2015
DOI:10.1002/9781119211310.ch10
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.