Investigation of hot cracking susceptibility via Modified Varestraint Transvarestraint testing of high-strength filler material
- MVT testing was conducted in Transvarestraint mode in multiple welding conditions and under a range of bending speeds. The materials observed were high strength filler metals used in GTAW namely DIN EN ISO 16834-A G 69 4 M21 Mn3Ni1CrMo (G69), 16834-A G 89 6 M21 Mn4Ni2CrMo (G89 6), 16834-A G 89 5 M21 Mn4Ni2,5CrMo (G89 5) and a filler wire 18276-A T 89 4 ZMn2NiCrMo M M21 1 H5 (T89). For evaluation light optical microscope pictures were used. Pixels containing cracks were manually segmented using a self-written program. Out of the segmented images data including crack length, position and area can be calculated for every crack. The results show dependencies of solidification cracking on the test parameters.
Autor*innen: | Arne KrommORCiD |
---|---|
Koautor*innen: | Philipp Liepold, Thomas Kannengießer |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2024 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik |
Freie Schlagwörter: | High strength steel; Solidification cracking; Varestraint test |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Energie / Windenergie | |
Veranstaltung: | IIW Intermediate Meeting Comission II-C |
Veranstaltungsort: | Incheon, Republic of Korea |
Beginndatum der Veranstaltung: | 12.03.2024 |
Enddatum der Veranstaltung: | 14.03.2024 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 25.03.2024 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |