The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts

  • The effect of support structure and of removal from the base plate on the residual stress state in Selective Laser Melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after the cutting from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support stress redistribution took place after removal of the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress relieving heat treatments are stillThe effect of support structure and of removal from the base plate on the residual stress state in Selective Laser Melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after the cutting from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support stress redistribution took place after removal of the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress relieving heat treatments are still needed.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • User meeting poster HZB TM.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Tatiana Mishurova, Tobias Thiede, Sandra Cabeza, Giovanni Bruno, Arne Kromm, Naresh Nadammal
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
Organisationseinheit der BAM:5 Werkstofftechnik
8 Zerstörungsfreie Prüfung
8 Zerstörungsfreie Prüfung / 8.5 Mikro-ZfP
9 Komponentensicherheit
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen
5 Werkstofftechnik / 5.0 Abteilungsleitung und andere
DDC-Klassifikation:Naturwissenschaften und Mathematik / Chemie / Analytische Chemie
Freie Schlagwörter:Additive manufacturing; Residual stress; Selective laser melting; Synchrotron X-ray diffraction
Themenfelder/Aktivitätsfelder der BAM:Analytical Sciences
Analytical Sciences / Zerstörungsfreie Prüfung und Spektroskopie
Veranstaltung:User Meeting HZB 2018
Veranstaltungsort:Berlin, Germany
Beginndatum der Veranstaltung:14.12.2017
Verfügbarkeit des Volltexts:Volltext-PDF im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:15.12.2017
Referierte Publikation:Nein