TY - CONF A1 - Fellinger, Tim-Patrick T1 - Bioinspired atomically dispersed M-N-C catalysts via active-site imprinting into nitrogen doped carbons N2 - Proton-exchange membrane fuel cells are amongst the most promising energy conversion technologies today. Herein non-precious iron-coordinated nitrogen doped carbons (Fe-N-Cs) are very promising alternatives for Pt-based cathode catalysts.[1-3] The early reports on the application of such materials date back to the 1960´s when Jasinski demonstrated that - similar to natural porphyrins - N-coordinated transition metal complexes can be active sites for the ORR.[3] The preparation of these catalysts was strongly optimized over the years; still they typically remain with harsh reaction conditions that complicate the selective formation of active FeN4 sites. The employment of pyrolytic temperatures has been a dogma for the synthesis of MN4 sites, however coming with unfavorable side reactions. We recently introduced a mild procedure, which is conservative toward the carbon support and leads to active-site formation at low temperatures in a wet-chemical step, essentially decoupling the preparation of nitrogen doped carbons (NCs) from the preparation of the active sites.[4, 5] The key concept therein is the so-called active site imprinting into the NC using the less reactive template ions Mg2+ [4] or Zn2+.[5] The presentation will introduce the concept of active site imprinting with a focus on Fe-N-C electrocatalyst development and testing. The broad potential of the synthetic approach will be exemplified by recent results, including the selective synthesis of tetrapyrrolic single site catalysts, the assignment of the role of the transition metal compared to the carbon scaffold and a facile method to evaluate specific activity. T2 - GDCh Electrochemistry 2022 CY - Berlin, Germany DA - 27.09.2022 KW - Bioinspired carbon catalysts PY - 2022 AN - OPUS4-61960 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hartfiel, Reni T1 - Zweistufiges Screening von One-Bead-One-Peptide-Bibliotheken linearer & cyclischer Peptide gegen Pflanzenviren N2 - In der Masterarbeit wurde ein Screening gegen den CCMV mit einer linearen Peptidbibliothek entwickelt, wobei zwei lineare Binder identifiziert wurden. Das resynthetisierte Peptid wurde auf seine Bindungseigenschaften mittels ELISA und MST untersucht. Aufgrund eines Aminosäurefehlers in der selbst durchgeführten Resynthese des Peptids sind die Ergebnisse nicht vollständig übertragbar. Um eine umsetzbare Cyclusgröße für die Peptidbibliothek zu finden, wurden Ringgrößen mit sechs bis acht Aminosäuren untersucht. Da keiner der gewählten Ringgrößen bevorzugt war, wurde die Ringgröße aus acht Aminosäuren für die Peptidbibliothek gewählt. Der Ringschluss wurde durch die Bildung einer Disulfidbrücke erreicht. Dadurch war die Alkylierung der vorhandenen Thiolgruppe in den Abbruchsequenzen notwendig. Neben den etablierten Alkylierungsreagenzien Iodessigsäure, Iodacetamid und Acrylamid wurden zwei Epoxide mituntersucht. Hierbei konnte nur bei Acrylamid und Propylenoxid eine vollständige Alkylierung beobachtet werden. Eine synthetische Peptidbibliothek aus zehn Aminosäuren pro Kopplungsschritt und einer Peptidlänge von acht Aminosäuren wurde erfolgreich nach der Split-and-Mix-Synthese hergestellt. Neben den kanonischen Aminosäuren wurde die synthetische Aminosäure 3-(3-Pyridyl)-alanin in die Peptidbibliothek mit eingebaut. Peptidsequenzen aus der cyclische Peptidbibliothek konnte mittels MALDI-TOF-MS identifiziert werden. Es konnte außerdem gezeigt werden, dass synthetische Aminosäuren mit proteinogenen Aminosäuren erfolgreich übersetzt werden. Anschließend wurde das entwickelte Screening auf eine cyclische Peptidbibliothek übertragen. Dabei konnte kein Binder identifiziert werden, da zu viele Nebenreaktionen auftraten. Ein alternativer Ringschluss über die Seitenketten von Lysin und Cystein wurden mit ortho-Phthaldialdehyd und 2,4,6-Trichloro-1,3,5-triazin (Cyanurchlorid) untersucht. Beide Bedingungen wiesen keinen erfolgreichen Ringschluss auf. Obwohl der Ringschluss über die Seitenketten von Lysin und Cystein nicht erfolgreich war, sollte ein Austausch von Cystein angestrebt werden, so dass kein freies Cystein in den Abbruchsequenzen vorhanden ist und die Alkylierung überflüssig wäre. Der Ringschluss durch Verwendung anderer Seitenketten bietet einen vielseitigen Ansatz. KW - CCMV KW - Pflanzenvirus KW - Peptidbibliothek KW - Peptid-Aptamer KW - Alkylierung KW - Cyclisierung KW - MALDI-TOF-MS KW - Fluoreszenz KW - Chip KW - Sequenzierung KW - Peptid-Synthese PY - 2022 SP - 1 EP - 81 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hicke, Konstantin A1 - Liao, Chun-Man A1 - Chruscicki, Sebastian A1 - Breithaupt, Mathias T1 - Vibration Monitoring of Large-Scale Bridge Model using Distributed Acoustic Sensing N2 - Results of DAS measurements along a large-scale concrete bridge model are presented. The improvement of measurable dynamic strain range is demonstrated. Vibration modes obtained by DAS correspond well to those determined from broadband seismometer measurements. T2 - 27th International Conference on Optical Fiber Sensors (OFS-27) CY - Alexandria, VA, USA DA - 29.08.2022 KW - Distributed acoustic sensing KW - Vibration modes KW - Bridge monitoring KW - WS-COTDR KW - Fiber-optic vibration monitoring PY - 2022 SP - 1 EP - 4 PB - Optica CY - Washington D.C., USA AN - OPUS4-56082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neuschaefer-Rube, U. A1 - Illemann, J. A1 - Sturm, M. A1 - Bircher, B. A1 - Meli, F. A1 - Bellon, Carsten A1 - Evsevleev, Sergei T1 - Validation of a fast and traceable radiographic scale calibration of dimensional computed tomography N2 - A fast and highly precise method of determining the geometrical scale factor of computed tomography (CT) measurements has been validated successfully by Bundesanstalt für Materialforschung und -prüfung (BAM), the Federal Institute of Metrology (METAS) and Physikalisch-Technische Bundesanstalt (PTB) within the scope of AdvanCT (Advanced Computed Tomography for dimensional and surface measurements in industry), a project funded in the European Metrology Programme for Innovation and Research (EMPIR). The method has been developed by PTB and requires only two radiographic images of a calibrated thin 2D standard (hole grid standard) from two opposite directions. The mean grid distance is determined from both radiographs. From this and with the help of the calibration result, the radiographic scale and therefore the voxel size is determined. The procedure takes only a few minutes and avoids a time-consuming CT scan. To validate the method, the voxel sizes determined via this method were compared with voxel sizes determined from CT scans of calibrated objects. Relative deviations between the voxel sizes in the range of 10−5 were achieved with minimal effort using cone-beam CT systems at moderate magnifications. KW - Dimensional metrology KW - Voxel size KW - Industrial CT KW - Geometrical magnification PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-553271 DO - https://doi.org/10.1088/1361-6501/ac74a3 SN - 0957-0233 VL - 33 IS - 9 SP - 1 EP - 9 PB - IOP Publishing CY - Bristol, UK AN - OPUS4-55327 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stroyuk, O. A1 - Raievska, O. A1 - Barabash, A. A1 - Batentschuk, M. A1 - Osvet, A. A1 - Fiedler, Saskia A1 - Resch-Genger, Ute A1 - Hauch, J. A1 - Brabec, C. J. T1 - "Green" synthesis of highly luminescent lead-free Cs2AgxNa1-xBiyIn1-yCl6 perovskites N2 - A new “green” and mild synthesis of highly stable microcrystalline Cs2AgxNa1-xBiyIn1-yCl6 (CANBIC) perovskites under ambient conditions was developed that is scalable to the multi-gram production. Under UV illumination, the CANBIC perovskites emit intense broadband photoluminescence (PL) with a quantum yield (QY) of 92% observed for x = 0.35 and y = 0.01-0.02. The combination of strong UV absorbance and broadband visible emission, high PL QY, and long PL lifetimes of up to 1.4 μs, along with an outstanding stability makes these CANBICs a promising material class for many optical applications. KW - Fluorescence KW - Perovskites KW - Solar cell KW - Automated synthesis KW - Green synthesis KW - Quantum yield KW - Integrating sphere spectroscopy KW - Absolute fluorescence KW - Quality assurance KW - Nano KW - Particle KW - Application KW - Semiconductor KW - Quantum dot KW - Renewable energy PY - 2022 DO - https://doi.org/10.1039/d2tc02055f SN - 2050-7526 VL - 10 IS - 27 SP - 9938 EP - 9944 PB - Royal Society of Chemistry AN - OPUS4-55453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Rudolf T1 - Advanced materials broadening the scope of antibody-based analytical methods N2 - Immunoanalytical Techniques, i.e., antibody-based analytical methods, have been used for decades in clinical diagnostics. What makes them attractive for other fields of application is their short time-to-result and high sensitivity. Microplate-based assays such as ELISA have been adopted early in environmental and food analysis. Yet, to make immunoassays even faster, more sensitive, robust, and, most desirable, portable, advanced materials, sometimes developed for other purposes, can be profitably used to achieve these goals. Materials can be novel labels, e.g., chemical or particle labels, such as fluorophores or nanoparticles. Carrier particles, such as magnetic or polymer beads, make it possible to adopt the assays to meso- or microfluidic set-ups and encoding them opens the path to multiplex analysis. Specialty electrodes can enable for higher sensitivity in electrochemical detection. All this broadens the scope of application and lowers effort and cost for analysis at the point-of-need. T2 - ChemForum - Kolloquium des Instituts für Strukturchemie CY - Lisbon, Portugal DA - 07.09.2022 KW - Immunoassay KW - Biosensor KW - Antibody PY - 2022 AN - OPUS4-56782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard T1 - Multifunctional Elastomer/Graphene Nanocomposites N2 - A few layer/multilayer graphene (MLG) with a specific surface area of BET=250 m2/g is proposed as an efficient multifunctional nanofiller for rubbers. The preparation method, i.e., ultrasonically-assisted solution mixing of master batches followed by two-roll milling, strongly influences the dispersion in the elastomeric matrix and is fundamental for the final properties. When homogenously dispersed, single stacks of only approximately 10 graphene sheets, with an aspect ratio of 34, work at low loadings, enabling the replacement of large amounts of carbon black (CB), an increase in efficiency, and a reduction in filler load. The appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing, gas barrier properties, electrical and thermal conductivity, as well as mechanical properties of different rubbers, as shown for chlorine-Isobutylene-Isoprene rubber (CIIR), nitrile-butadiene rubber (NBR), natural rubber (NR), and styrene-butadiene rubber (SBR). 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of CB. The stronger interactions between MLG and NR or SBR also resulted in a reduction in the elongation at break by 20% and 50%, respectively, while the same parameter was hardly changed for CIIR/MLG and NBR/MLG. CIIR/MLG and NBR/MLG were stiffer but just as defomable than CIIR and NBR. The strong reinforcing effect of 3 phr MLG was confirmed by the increase of greater than 10 Shore A in hardness. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards flammability, the latter shown by the reduction in heat release rate in the cone calorimeter. We investigated MLG also as a synergist for reducing the aluminium trihydrate loading in flame retardant hydrogenated acrylonitrile-butadiene (HNBR), polybutadiene chloroprene (BR/CR), and chlorosulfonated polyethylene rubber(CSM). The higher the nanofiller concentration is, the greater the improvement in the properties. For instance, the permeability decreased by 30% at 3 phr of MLG, 50% at 5 phr and 60% at 10 phr, respectively. Moreover, the MLG nanocomposites improve stability of mechanical properties against the effects of weathering. In key experiments an increase in UV-absorption and a pronounced radical scavenging were proved as stabilizing mechanisms. In a nutshell, MLG is an efficient multifunctional nanofiller ready to be used for innovative rubber development. T2 - 19th European Polymer Congress, EPF 2022 CY - Prague, Czech Republic DA - 26.06.2022 KW - Graphene KW - Nanocomposite KW - Rubber KW - Elastomer PY - 2022 AN - OPUS4-55196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Residual stresses and micromechanical properties of additively manufactured metals: why do we need a paradigm shift? N2 - An overview of the challenges and successes in the methodology to characherise residual stresses and micromechnical properties in additively manufactured metals T2 - CAM2 Annual Seminar 2022 - 5-year journey CY - Gothenburg, Sweden DA - 24.10.2022 KW - Additive Manufacturing KW - Residual stress KW - AGIL KW - MANUFACT KW - Micromechnical properties PY - 2022 AN - OPUS4-56466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Experimental and numerical characterization of hydrogen diffusion in thick-walled submerged arc welded joint of S420G2+M offshore steel grade N2 - Offshore wind turbines are an important goal in national energy strategies worldwide. Foundation structures are manufactured from submerged arc welded (SAW) plates with thicknesses up to 200 mm. In that connection, high-strength steels like the S420G2+M are more and more applied offering the possibility for increased stability and load-bearing capacity of the foundations. These offshore steel grades can show a susceptibility for delayed hydrogen assisted cold cracking of the weld joints. For that purpose, a minimum waiting time (MWT) of up to 48 h (dependent on applied standards) is recommended before non-destructive testing is allowed and conducted. But this concept is based on older steel grades that have been used for three or more decades. Nowadays, the metallurgical improvements (clean steels, proper rolling, and heat treatment) of base materials and well as welding consumables must be anticipated. Hence, the MWT concept should be critically discussed as it is assumed to be very conservative. For that reason, the focus of this study was to investigate the diffusion behavior in S420G2+M steel and its multi-layer SAW joint. Electrochemical permeation experiments were carried at room temperature. Boundary conditions were anticipated in terms of using different sample thicknesses. From the experimental data, hydrogen diffusion coefficients and absorbed diffusible hydrogen concentrations had been calculated. It was shown that hydrogen diffusion in the base material is increased compared to the weld metal. In addition, the sample thickness had a significant on the calculated diffusion coefficients. The minimum and maximum diffusion coefficients had been used for numerical modelling of the hydrogen diffusion in the welding joint. It became clear that a MWT must be always regarded together with a critical initial diffusible hydrogen concentration for the evaluation of a possible delayed cracking as diffusion times were mostly > 48 h due to the thick plates. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - Submerged arc welding KW - Diffusion KW - Minimum waiting time KW - Electrochemical permeation PY - 2022 SP - 1 EP - 11 CY - Ghent, Belgium AN - OPUS4-56075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Richter, Tim T1 - Hydrogen diffusion and desorption characteristics of a CoCrFeMnNi high entropy and a CoCrNi medium entropy alloy N2 - High-entropy alloys (HEAs) are innovative high-performance materials that have attracted more and more research attention. HEAs are characterized by a solid solution of typically five equiatomic metallic elements. In addition, medium-entropy alloys (MEA, with three elements) are of interest and become more and more important. Depending on the alloy concept, HEAs and MEAs show exceptional mechanical properties, especially high-strength and ductility combinations at both cryogenic and elevated temperatures combined with excellent corrosion resistance. Future structural HEA/MEA components can be exposed to potential applications with hydrogen containing environments like high-temperature water in pressurized nuclear reactors or aerospace structures. Other potential applications could be in materials for vessel walls in the field of cryogenic and high-pressure hydrogen storage. So far, the susceptibility of HEAs/MEAs to hydrogen assisted cracking (if any) and the hydrogen diffusion is not investigated in detail yet and can limit or extend possible applications of HEA/MEA as structural materials. In our work, we focused on the hydrogen absorption, diffusion, and distribution in a HEA (CoCrFeMnNi the original Cantor-alloy) and a MEA (CoCrNi). Cathodic hydrogen charging was carried out for the hydrogen ingress, and thermal desorption analysis (TDA) revealed complex hydrogen trapping in both alloy types up to 300 °C. The absorbed total hydrogen concentrations were > 100 ppm for the HEA and > 40 ppm for MEA. In addition, the assessment of the peak deconvolution is not trivial and must consider both experimental and microstructure influences. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - High-entropy alloy KW - Multiple principal element alloy KW - Thermal desorption analysis KW - Diffusion PY - 2022 SP - 1 EP - 11 CY - Ghent, Belgium AN - OPUS4-56076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -