TY - CONF A1 - Trappe, Volker A1 - Kalinka, Gerhard A1 - Loose, Florian T1 - Carbon fibre composites exemplarily research at BAM N2 - Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given. T2 - Meeting KCarbon CY - Berlin, Germany DA - 15.06.2023 KW - Lightweighting KW - Carbon Fibers KW - Recycling KW - Push-out Test KW - multi scale testing PY - 2023 AN - OPUS4-58094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalinka, Gerhard A1 - ElAbshihy, K. T1 - Circumventing boundary effects while characterizing epoxy/copper interphases using nanoindentation N2 - Characterization of the size and mechanical properties of interphases is essential when designing multicomponent materials. When nanoindentation is used to investigate the size and mechanical properties of an interphase, a common challenge is that the indenter or the stress zone formed around it are often restricted by the reinforcement, making it difficult to distinguish the mechanical property variations caused by the interphase itself from those caused by the boundary effect. In this work, a testing system was developed that allows determining the indent affected zone and accounting for it in the interphase measurements of an epoxy/Cu system. Using finite element analysis, we confirmed the validity of the proposed system. Nanoindentation was used to investigate the Interphase between copper and two different epoxy systems; amine-cured and anhydride-cured. Nanoindentation results showed that a copper layer that is only 10 nm thick still exhibits a constriction effect on the indentations in its vicinity. The amine-cured epoxy did not show any sign of interphase existence using the introduced method. However, a soft interphase with a thickness of ~1.7 μm was measured on theanhydride-cured epoxy. Furthermore, we show that the proposed system can be used to determine the interphase thickness as well as its relative mechanical properties regardless of the indentation depth. This system can be further used for investigating other polymer/metal interphases to better understand the factors influencing them, thus helping engineer the interphase size and properties to enhance composite performance. KW - Interphase KW - Polymer-metal KW - Epoxy KW - Copper KW - Composites KW - Nanoindentation PY - 2017 DO - https://doi.org/10.1080/09276440.2017.1286878 SN - 0927-6440 SN - 1568-5543 VL - 24 IS - 9 SP - 833 EP - 848 PB - Taylor & Francis CY - UK AN - OPUS4-39128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Testing the fibre matrix interface of short glass fibre reinforced PMCs with using the push out technique N2 - With this presentation, the push-out technique is explained. The focus of the experimental work is on the characterization of the fiber-matrix interface of short fiber reinforced composites. The reinforcing component was glass fibers and the matrix polymer was PA6.6 and PPA. It is demonstrated for the first time that the push-out technique ca be applied on injection molded short fiber PMC and is sensitive to the mechanical interface properties. Further studies are planned on the influence of multiple processing, the temperature and humidity. T2 - Composirtes United Workshop „Fiber Matrix Interphases“ CY - Online meeting DA - 09.11.2023 KW - Polymer Matrix Composite KW - Glass Fibres KW - PA6.6 KW - PPA KW - Push-out Test KW - Interface Strength PY - 2023 AN - OPUS4-59053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taketa, I. A1 - Kalinka, Gerhard A1 - Gorbatikh, L. A1 - Lomov, S. A1 - Verpoest, I. T1 - Influence of cooling rate on the properties of carbon fiber unidirectional composites with polypropylene, polyamide 6, and polyphenylene sulfide matrices N2 - The longitudinal and transverse strength of three unidirectional thermoplastic prepreg systems: carbon fiber/polypropylene (CF/PP), polyamide 6 (CF/PA6), and polyphenylene sulfide (CF/PPS) are studied and analytical formulas are proposed for the estimation of matrix and fiber/matrix interface properties from composites properties. Since the matrices are semi-crystalline thermoplastics, the influence of cooling rate on the strength is statistically evaluated. While the 0° tensile strength is found to be independent of the cooling rate, the 90° tensile strength is strongly influenced by the matrix type and cooling rate. The matrix modulus increases as the cooling rate is decreased; the degree of crystallinity also increases. The matrix residual stress, interfacial shear strength, and mode II interlaminar fracture toughness are also found to depend on the cooling rate, with the trends different for different matrices. KW - Matrix residual stress KW - Thermoplastic prepreg KW - Unidirectional composites KW - Cooling rate KW - Interfacial strength PY - 2020 DO - https://doi.org/10.1080/09243046.2019.1651083 SN - 0924-3046 SN - 1568-5519 N1 - Die originale japanische Version des Artikels erschien in: Journal of the Japan Society for Composite Materials, Jg. 44, Nr. 4 (2018), S. 123-128. - The original Japanese version of the article was published in: Journal of the Japan Society for Composite Materials, vol. 44, no. 4 (2018), pp. 123-128. VL - 29 IS - 1 SP - 101 EP - 113 PB - Taylor & Francis CY - London AN - OPUS4-45433 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Micro indentation near stiff-soft phase boundaries T2 - Polydays 2004 CY - Potsdam, Germany DA - 2004-10-04 PY - 2004 AN - OPUS4-4703 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Testing the interface shear strength of carbon fibre reinforced composites T2 - Polydays 2006 CY - Berlin, Germany DA - 2006-10-04 PY - 2006 AN - OPUS4-13804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Monitoring the interface crack propagation with micromechanical test devices T2 - Interfacial Phenomena in Composite Materials CY - Berlin, Germany DA - 2001-01-28 PY - 2001 AN - OPUS4-12107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalinka, Gerhard A1 - Hinrichsen, G. T1 - Two-dimensional computer simulation of spherulite formation by branching lamellae KW - Thermoplaste KW - Kristallisation KW - Sphärolithe KW - Lamellen KW - Modellrechnungen PY - 1997 SN - 0323-7648 SN - 1521-4044 VL - 48 SP - 256 EP - 261 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-12004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - An Advanced Indentation Technique for the Characterization of the Fibre-Matrix Interface T2 - Gordon Conference on Composites CY - San Buenaventura, CA, USA DA - 1997-01-05 PY - 1997 AN - OPUS4-12102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Energy Quantification of Interface Debonding Processes Using 'Stiff' Test Devices T2 - Gordon Conference on Composite Materials CY - San Buenaventura, CA, USA DA - 2001-01-28 PY - 2001 AN - OPUS4-12108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, Eckhard A1 - Kalinka, Gerhard A1 - Meretz, S. A1 - Hampe, Andreas T1 - Pull-out of Single Fibres KW - Verstärkungsfaser KW - Verbundwerkstoffe KW - Interface KW - Adhäsion KW - Reibung KW - Haftung KW - Thermoplast PY - 1994 SN - 0945-0084 VL - 84 IS - 5 SP - 25 EP - 26 PB - Hanser CY - München AN - OPUS4-11989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Micro indentation near stiff-soft boundaries T2 - "Nanomech5, 5th European Symposium on nano-Mechanical Testing" CY - Hückelhoven, Germany DA - 2004-09-07 PY - 2004 AN - OPUS4-4704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hinrichsen, G. T1 - Computer simulation of spherulitic formation and crystallization in semicrystalline polymers T2 - Europhysics Conference on Macromolecular Physics CY - Prague, Czech Republic DA - 1995-07-17 PY - 1995 AN - OPUS4-12085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Energy based characterization of the fiber-matrix interface unsing the pull-out and the push-out test T2 - Micro Mat '97 CY - Berlin, Germany DA - 1997-04-16 PY - 1997 AN - OPUS4-12100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Energy orientated data interpretation of pull-out and push-out test for the investigation of residual stresses T2 - Interface Phenomena in Composite Materials CY - Berlin, Germany DA - 1999-09-08 PY - 1999 AN - OPUS4-12093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Interfacial properties and their determination by using stiffness optimized test devices T2 - Workshop on Micro-Mechanics Measurement Technologies, NIST CY - Gaithersburg, MD, USA DA - 1997-05-28 PY - 1997 AN - OPUS4-12103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalinka, Gerhard A1 - Boro, I. A1 - Augustin, G. A1 - Hampe, Andreas A1 - Hinrichsen, G. T1 - Fatigue Behaviour of High-Performance Fibre-Reinforced Composites with a Thermoplastic Matrix KW - Verbundwerkstoffe KW - Ermüdung KW - Biegeschwingung KW - Thermoplaste KW - Glasfaser PY - 1990 SN - 0723-0192 VL - 80 IS - 5 SP - 36 EP - 38 PB - Hanser CY - Munich AN - OPUS4-11999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - A model of spherulitic crystallization based on growing lameallae T2 - 9th Microsymposium of Electron Microscopy in Materials Science CY - Lutherstadt Wittenberg, Germany DA - 2004-05-06 PY - 2004 AN - OPUS4-4702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Energy Dissipation of the Fibre-Matrix Debonding Process Investigated with the Indentation Technique T2 - Interfacial Phenomena of Composite Materials IPCM'95 CY - Eindhoven, Netherlands DA - 1995-09-11 PY - 1995 AN - OPUS4-12098 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Micro indentation and scratch tests for surface characterisation T2 - XXII. Donauländergespräche über die natürliche und künstliche Alterung von Polymeren CY - Berlin, Germany DA - 2001-09-17 PY - 2001 AN - OPUS4-7506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Torsten T1 - Deformation behavior of alumina and zirconia springs at room temperature N2 - At high temperatures and in harsh environments ceramic springs are often superior to metallic springs and allow for innovative solutions. A recently proposed application involves ceramic springs with metallized surfaces as capacitive force sensor. A strictly linear stress-strain characteristic of the spring is a precondition for such a sensor. Helical ceramic springs with rectangular cross-section have been produced from sintered hollow cylinders. Alumina, ATZ, Y-TZP, and Ce-TZP springs with identical dimensions were characterized and compared regarding deformation behavior. Spring deformation was investigated under various load scenarios. Dynamic compression was performed with deformation speeds from 0.3 to 30 mm/min. Spring constants of alumina springs are strain rate independent. By contrast, Y-TZP spring constant increases by approximately 3 % within the experimental framework. A high-precision test facility was developed to characterize spring displacement in nm range under static tensile load over long periods of time. Spring elongation with asymptotic course was observed for zirconia containing materials at room temperature. This effect is particularly strong in the case of Y-TZP. Up to 0.3 % time-dependent elongation was measured after 24 h under constant load. Deformation is completely reversible after unloading. Alumina springs do not show any time-dependent deformation under identical test conditions. Contrary to alumina springs, a non-linear stress-strain behavior of TZP springs at room temperature was proved in both test series. It is supposed, that pseudo-elasticity caused by stress-induced phase transformation from tetragonal to monoclinic is responsible for this special behavior of TZP springs. T2 - D-A-CH Keramiktagung CY - Leoben, Austria DA - 06.05.2019 KW - Phase transformation KW - Ceramic spring KW - Force-distance diagram KW - Deformation behavior PY - 2019 AN - OPUS4-48026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker T1 - Advanced lightweight applications – recycling versus reliability and fossil energy footprint N2 - Advanced light weight applications like aircrafts and wind turbine blades are made of fibre reinforced plastics (FRP) with continuous fibre reinforcement and must withstand a high thermo-mechanical cyclic loading. The quality of the fibre matrix interface has a high impact on the fatigue life and was continuously improved over the years since the 50th. The fatigue life of glass fibre reinforced plastics (GFRP) used in aircraft industry is 10 to 100 times higher compared to glass fibre non crimp fabrics used for wind turbine blades. To assure a constant and reliable high quality and strength of reinforcement fibres, synthetic fibre production is state of the art (CF, GF). There is a need for recycling GFRP and CFRP waste due to the upcoming use. Pyrolysis and solvolysis are more expensive than the mechanical route however enable a more sustainable recycling. Natural fibres and recycled synthetic fibres have a high scatter in quality and strength. Hence it is a challenge to optimize the production / recycling processes to get a reliable quality for any demanding (second life) application. Chemical routes for using renewables resources and recycling, is going to be a good approach especially for polymer-matrix systems to get 100% quality (back) compared to the state of the art. Finally, a proper design, life-time extension and repair is preferable to recycling to keep the carbon footprint as low as possible. T2 - 27. INTERNATIONALES DRESDNER LEICHTBAUSYMPOSIUM CY - Dresden, Germany DA - 13.06.2024 KW - Polymer Matrix Composites KW - Carbon Fibre KW - Recycling KW - Circular Economy PY - 2024 UR - https://leichtbausymposium.de/deu/ AN - OPUS4-60683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - The Fracture Process in the Fibre/Matrix Interphase T2 - The Fifth International Conference on Composite Interfaces CY - Gothenburg, Sweden DA - 1994-07-20 PY - 1994 AN - OPUS4-5908 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - Energy based characterization of the fibre-matrix interface using the pull-out and push-in test T2 - Interfacial Phenomena in Composite Materials 97 CY - Eger, Hungary DA - 1997-03-01 PY - 1997 AN - OPUS4-12087 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Friction Measurement on fiber reinforced polymer composites with using the indentation technique T2 - European Conference on Composite Materials ECCM-8 CY - Naples, Italy DA - 1998-06-03 PY - 1998 AN - OPUS4-12089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - An Advanced Equipment for Single-Fibre Pull-Out test designed to monitor the fracture process T2 - Interfacial Phenomena in Composite Materials CY - Cambridge, England DA - 1993-09-13 PY - 1993 AN - OPUS4-12095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hampe, Andreas A1 - Kalinka, Gerhard A1 - Meretz, S. A1 - Schulz, Eckhard T1 - An advanced equipment for single-fibre pull-out test designed to monitor the fracture process KW - Verbundwerkstoffe KW - Thermoplaste KW - Adhäsion KW - Reibung KW - Haftung KW - Interface KW - Schubfestigkeit KW - Scherfestigkeit KW - Messmethode PY - 1995 SN - 0010-4361 VL - 26 IS - 1 SP - 40 EP - 46 PB - Butterworth-Heinemann CY - Guildford, Surrey AN - OPUS4-11988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Energy based characterization of the fiber-matrix interface unsing the pull-out and the push-out test T2 - Interfacial Phenomena of Composite Materials IPCM'97 CY - Eger, Hungary DA - 1997-09-01 PY - 1997 AN - OPUS4-12101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - The Fracture Process in the Interphase Investigated by the Single Fiber Pull-out Test T2 - Composites Testing and Standardisation ECCM-CTS 2 CY - Hamburg, Germany DA - 1994-09-13 PY - 1994 AN - OPUS4-12009 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - Measurement of the Interfacial Toughness in Composites by Micromechanical Experiments T2 - 4th Arab International Conference on Polymer Science & Technology CY - Cairo, Egypt DA - 1997-09-08 PY - 1997 AN - OPUS4-5929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Characterization of the fibre-matrix interface with the indentation technique T2 - 6th International Conference on Composite Interfaces (ICCI-VI) CY - Zichron Ya'akov, Israel DA - 1996-05-05 PY - 1996 AN - OPUS4-12086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Auer, C. A1 - Kalinka, Gerhard A1 - Krause, T. A1 - Hinrichsen, G. T1 - Crystallization Kinetics of Pure and Fiber-Reinforced Poly(phenylene Sulfide) KW - Verbundwerkstoffe KW - Thermoplaste KW - Kristallisation KW - Kristallisationskinetik KW - Erstarrung KW - Avrami KW - Modellrechnung KW - Simulation PY - 1994 SN - 0021-8995 SN - 1097-4628 VL - 51 SP - 407 EP - 413 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-11991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, T. A1 - Kalinka, Gerhard A1 - Auer, C. A1 - Hinrichsen, G. T1 - Computer Simulation of Crystallization Kinetics in FIber-Reinforced Composites KW - Verbundwerkstoffe KW - Thermoplaste KW - Kristallisation KW - Kristallisationskinetik KW - Erstarrung KW - Avrami KW - Modellrechnung KW - Simulation PY - 1994 SN - 0021-8995 SN - 1097-4628 VL - 51 SP - 399 EP - 406 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-11992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lüders, C. A1 - Kalinka, Gerhard A1 - Li, Wei A1 - Sinapius, M. A1 - Wille, T. T1 - Experimental and numerical multiscale approach to thermally cycled FRP N2 - Due to the different thermal expansion of the constituent materials, cyclic thermal loading of FRP induces alternating stresses in the material at two scales: at the micro scale (level of fibre–matrix-interaction) and at the macro scale (level of the multidirectional laminate). Especially the micro scale effect is not comprehensively investigated yet. Additionally, computational investigations mostly neglect this effect due to the homogenous modelling of the composite material. As this effect is assumed to significantly contribute to the fatigue of FRP at thermal loads, the present paper suggests an experimental and numerical multiscale approach including Experiments at the different involved material scales to separately observe the effects acting at these scales. The approach also includes numerical modelling for each scale to complement the knowledge gained from the Experiments and to create a basis for the consideration of the micro effect even in macroscopic fatigue models treating homogeneous modelled composites. The main focus of the contribution is to bring the overall Approach up for discussion, rather than to present the multiscale modelling details. KW - Fatigue KW - Thermal cycling KW - Fibre reinforced plastic KW - Cryogenic KW - Carbon Fibre KW - Epoxy Resin PY - 2020 DO - https://doi.org/10.1016/j.compstruct.2020.112303 SN - 0263-8223 VL - 244 SP - 112303 PB - Elsevier Ltd. CY - Niederlande AN - OPUS4-50844 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - The Single Fibre Pull-Out Test Performed with a Microcomposite Sample T2 - The Seventh International Conference on Composite Interfaces - ICCI-VII CY - Fujisawa, Kanagawa, Japan DA - 1998-05-10 PY - 1998 AN - OPUS4-5940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hinrichsen, G. T1 - The Fiber/Matrix Interphase: New Insights into an old Problem T2 - INTERNATIONAL CONFERENCES ON POLYMER CHARACTERIZATION POLYCHAR-6 CY - Denton, TX, USA DA - 1998-01-07 PY - 1998 AN - OPUS4-12006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Eckhard T1 - Effect of Transcrystallization in Carbon Fibre Reinforced Poly(p-phenylene sulfide) Composites on the Interfacial Shear Strength Investigated with the Single Fibre Pull-out Test T2 - Europhysics Conference on Macromolecular Physics CY - Prague, Czech Republic DA - 1995-07-17 PY - 1995 AN - OPUS4-12084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hinrichs, V. A1 - Leistner, A. A1 - Kalinka, Gerhard A1 - Schulz, Eckhard A1 - Hinrichsen, G. T1 - Viscoelastic properties of the interphase in fibre reinforced polymers - measurement and simulation KW - Polymer KW - Glass fibre KW - Interphase KW - Coating KW - Glass transition KW - Dynamic KW - Viscoelastic PY - 1999 VL - 6 IS - 2 SP - 93 EP - 101 PB - North-Holland CY - New York, NY AN - OPUS4-12003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Testing the fibre-matrix adhesion in fiber reinforced polymers using the single fibre push-out method T2 - 8th European Conference on Applications of Surface and Interface Analysis (ECASIA 99) CY - Seville, Spain DA - 1999-10-04 PY - 1999 AN - OPUS4-12106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian T1 - Microscopical failure processes in fiber reinforced polymers - Mechanical aspects of the adhesion between fiber and matrix T2 - 11th International Conference on Mechanics and Technology of Composite Materials CY - Sofia, Bulgaria DA - 2006-10-02 PY - 2006 AN - OPUS4-13239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Eckhard T1 - Investigation on mechanical behaviour of heterogeneous polymeric systems and fibre reinforced composites using micro indentation and scanning force microscopy T2 - 18th Disc. Conf. and 56th PMM CY - Prague, Czech Republic DA - 1998-07-20 PY - 1998 AN - OPUS4-6451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang T1 - Evaluation of the Adhesion Behaviour of Optical Fibers for Sensors Embedded in Cementitiuos Materials T2 - International Workshop on Fiber Optic Sensors for Construction Materials and Bridges CY - Newark, NJ, USA DA - 1998-05-03 PY - 1998 AN - OPUS4-12091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Juntaro, J. A1 - Pommet, M. A1 - Kalinka, Gerhard A1 - Mantalaris, A. A1 - Shaffer, M.S.P. A1 - Bismarck, A. T1 - Creating Hierarchical Structures in Renewable Composites by Attaching Bacterial Cellulose onto Sisal Fibers KW - Nanotubes KW - Cellulose KW - Polymer KW - Interface KW - Hierarchical Structures PY - 2008 DO - https://doi.org/10.1002/adma.200703176 SN - 0935-9648 SN - 1521-4095 VL - 20 IS - 16 SP - 3122 EP - 3126 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-18258 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas T1 - Comparison of the Interfacial Toughness Measured by the Single Fibre Pull-Out, the Indentation and the Fragmentation Test T2 - NIST, Workshop on Micro-Mechanics Measurement Technologies for Fiber-Polymer Interfaces CY - Gaithersburg, MD, USA DA - 1997-05-28 PY - 1997 AN - OPUS4-5928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Eckhard T1 - Investigation of polymeric composites reinforced with high oriented short glass fibres using the single fibre push-out test T2 - Euro-Conf. Surfaces and Interfaces in Polymers and Composites CY - Lausanne, Switzerland DA - 1997-06-03 PY - 1997 AN - OPUS4-6439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Influence of water on the fibre-matrix adhesion investigated by the single fiber indentation method T2 - 4th European Conference on Adhesion, 1st World Congress on Adhesion an Related Phenomena CY - Garmisch-Partenkirchen, Germany DA - 1998-09-06 PY - 1998 AN - OPUS4-12105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Comparison of Interfacial Properties obtained by using Single Filament Embedded Tensile Test and Push-in Test T2 - Recent Advancement of Interfacial Materials Science on Composite Materials '97 CY - Kyoto, Japan DA - 1997-05-07 PY - 1997 AN - OPUS4-12213 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Eckhard T1 - Investigations of the mechanical behaviour of heterogeneous polymeric systems and fibre reinforced composites using micro indentation and scanning force microscopy T2 - Special Lectures, 18. Disc. Conf. And 56the PMM.: Mech. Behaviour of polymeric materials CY - Prague, Czech Republic DA - 1998-07-20 PY - 1998 AN - OPUS4-12092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Munz, Martin A1 - Chung, Jae Un A1 - Kalinka, Gerhard ED - Possart, W. T1 - Mapping Epoxy Interphases T2 - 7th European Conference on Adhesion ; 7th EURADH CY - Freiberg, Germany DA - 2004-09-01 KW - Interface KW - Interphase KW - Epoxy KW - Copper (Cu) KW - Polyvinylpyrrolidone (PVP) KW - AFM/SFM KW - DSI KW - EDX/EDS KW - Stiffness KW - Modulus KW - Interdiffusion PY - 2005 SN - 3-527-31263-3 VL - 7 SP - 103 EP - 123 PB - Wiley-VCH CY - Weinheim AN - OPUS4-10894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Kalinka, Gerhard ED - Zachariev, G. T1 - Microscopical Failure Processes in Fiber Reinforced Polymers - Mechanical Aspects of the Adhesion between Fiber and Matrix T2 - 11th International Conference on Mechanics and Technology of Composite Materials CY - Sofia, Bulgaria DA - 2006-10-02 KW - Composite materials KW - Failure process KW - Adhesion PY - 2006 SP - 37 EP - 42 PB - Bulgarian Academy of Sciences CY - Sofia AN - OPUS4-14027 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munz, Martin T1 - On the stiffness gradient at the interface between an amine-cured epoxy and a thermoplast T2 - 6. Workshop 'Rasterkraftmikroskopie in der Werkstoffwissenschaft' an der Uni Erlangen, Inst. für Werkstoffwissenschaften veranstaltet vom Arbeitskreis 'Rastersondenmikroskopie in der Werkstoffwissenschaft' im Fachausschuss Metallographie der Deutschen Gesellschaft für Materialkunde (DGM) CY - Erlangen, Germany DA - 2005-02-17 PY - 2005 AN - OPUS4-7137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Kalinka, Gerhard T1 - Local failure processes in fiber reinforced polymers N2 - The breakage of a fiber and its effect on the strain energy is studied in a model composite, this is, a single fiber embedded in a dogbone specimen. The fracture process is recorded by an acoustic emission device, the crack patterns are monitored under a microscope. A finite element analysis is performed in order to estimate the energy released by different failure scenarios. The abilities and limitations of the acoustic emission analysis in characterizing different failure types in fiber reinforced composites are evaluated. T2 - ICCM17 - 17th International conference on composite materials CY - Edinburgh, UK DA - 2009-07-27 KW - Fiber KW - Interface KW - Composite material KW - Failure KW - Acoustic emission KW - Fracture mechanics KW - Energy release rate KW - Finite element analysis PY - 2009 IS - D7:8 SP - 1 EP - 10 CY - Edinburgh, UK AN - OPUS4-21295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hinrichs, V. A1 - Kalinka, Gerhard A1 - Hinrichsen, G. T1 - An Avrami-based model for the description of the secondary crystallization of polymers N2 - A mathematical model for the description of the overall crystallization of polymers has been developed which separates the pure geometric spreading of the semicrystalline superstructures from the increasing crystallinity inside these entities. The model uses the Avrami theory for the geometric part and a freely optional function for the increasing local crystallinity. The two functions are combined by a mathematical procedure called convolution. The free option of the local crystallinity function enables this model to permit calculation of this function, which is not accessible to direct measurement. Thus with given Avrami parameters and measured values of the time-dependent overall crystallinity, this function of the local crystallinity (secondary crystallization function) can be calculated. The model has been applied to test data produced by computer simulations. KW - Thermoplaste KW - Kristallisation KW - Nachkristallisation KW - Sphärolithe KW - Kristallisationskinetik KW - Modellrechnung PY - 1996 DO - https://doi.org/10.1080/00222349608220382 SN - 0022-2348 SN - 1525-609X VL - 35 IS - 3-4 SP - 295 EP - 302 PB - Dekker Chemistry CY - New York, NY AN - OPUS4-11983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, Eckhard A1 - Kalinka, Gerhard A1 - Auersch, W. T1 - Effect of Transcrystallization in Carbon Fiber Reinforced Poly(p/phenylene sulfide) Composites on the Interfacial Shear Strength Investigated with the Single Fiber Pull-Out Test N2 - The effect of transcrystallinity in carbon fiber reinforced poly(p-phenylene sulfide (PPS) composites on the apparent shear strength was investigated with the single fiber pull-out test. Transcrystalline zones around the reinforcing fibers do not seem to improve the adhesion level significantly. Neighbor fibers hinder the formation of the transcrystalline zone and a ductile fracture behavior can be observed. However, the apparent strength level is slightly higher for composites containing such reinforcing neighbor fibers compared with single fiber composite samples. During annealing a brittle interface can be formed in the multifiber composite yielding a higher level of the apparent shear strength. KW - Thermoplaste KW - Kristallisation KW - Transkristallisation KW - Interface KW - Verbundwerkstoffe KW - Pull-out KW - Haftung KW - Adhäsion KW - Reibung PY - 1996 DO - https://doi.org/10.1080/00222349608220393 SN - 0022-2348 SN - 1525-609X VL - 35 IS - 3-4 SP - 527 EP - 546 PB - Dekker Chemistry CY - New York, NY AN - OPUS4-11987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nowak, H. A1 - Kalinka, Gerhard A1 - Hinrichsen, G. T1 - Investigations on the cold crystallization of pure and filled PETP by dielectric measurements N2 - The cold crystallization of pure and filled poly(ethylene terephthalate) (PETP) after quenching from the melt has been investigated by dielectric measurements in two different modes: The first one using constant heating-rate (in the temperature range from 320 to 480 K) and the second one under isothermal conditions (at 378 K). The complex dielectric constant (ε´, tan δ) is influenced by crystallization. Two α-relaxation regions are identified: The αa-relaxation region from the pure amorphous phase and the α´-relaxation region from the spherulitic phase. The investigations on the filled systems (PETP + 10% aramid puple, PETP + 30% short glass fibres) prove that an influence of the fillers on the time delay and rate of crystallization and on the geometry of the growing spherulites exists. KW - Verbundwerkstoffe KW - Gefüllte Kunststoffe KW - Elektrische Eigenschaften KW - Verlustfaktor KW - Dielektrische Analyse PY - 1993 SN - 0323-7648 SN - 1521-4044 VL - 44 IS - 1 SP - 25 EP - 28 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-11995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thomason, J.L. A1 - Kalinka, Gerhard T1 - A technique for the measurement of reinforcement fibre tensile strength at sub-millimetre gauge lengths N2 - The strength of composite reinforcement fibres is normally measured on samples of much greater length than the actual residual fibre lengths found in many composite materials. This is due to a number of limitations of the standard techniques which are employed. We present a description of a technique which enables values for the tensile strength of composite reinforcement fibres at short gauge lengths to be obtained. The technique is based on an adaptation of a micro-mechanical test apparatus for fibre pullout measurements. Data is presented which was obtained at gauge lengths of 180–380 µm on E-glass and S-2 glass® fibres taken from different chopped reinforcement products. The technique can be used at gauge lengths as short as 20 µm. The data indicates that the values of average fibre strength in these products are significantly below the pristine glass strength values. KW - Verstärkungsfaser KW - Kurzfaser KW - Längenabhängigkeit KW - Glass fibres KW - Strength KW - Mechanical testing KW - Festigkeit KW - Faser PY - 2001 DO - https://doi.org/10.1016/S1359-835X(00)00122-6 SN - 1359-835X VL - 32 IS - 1 SP - 85 EP - 90 PB - Elsevier CY - Oxford AN - OPUS4-12012 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bismarck, A. A1 - Carreyette, S. A1 - Fontana, Q.P.V. A1 - Greenhalgh, E.S. A1 - Jacobsson, P. A1 - Johansson, P. A1 - Marczewski, M.J. A1 - Kalinka, Gerhard A1 - Kucernak, A. A1 - Shaffer, M.S. A1 - Shirshova, N. A1 - Steinke, J.H.G. A1 - Wienrich, Malte T1 - Multifunctional epoxy resin for structural supercapacitors N2 - Polymer-based electrolytes based on commercially available epoxy resins were prepared through the addition of a liquid electrolyte, a solution of a lithium salt in an ionic liquid. The polymer monoliths were characterized using impedance spectroscopy, 3-point bending test, scanning electron microscopy (SEM) and nitrogen adsorption (BET). The balance of ionic conductivity and flexural modulus is crucially dependent on the relative proportions of epoxy resin to electrolyte. Also the effect of the liquid electrolyte on curing kinetics and processing was assessed by complex viscosity measurements and differential scanning calorimetry (DSC). Only one out of the three resins investigated exhibited a significant acceleration effect. T2 - ECCM15 - 15th European conference on composite materials CY - Venice, Italy DA - 2012-06-24 KW - Multifunctional epoxy KW - Polymer electrolyte KW - Morphology KW - Ionic liquid PY - 2012 SN - 978-88-88785-33-2 SP - 1 EP - 8(?) AN - OPUS4-28694 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Elabshihy, Karim T1 - Investigation of the time-dependent behavior of cnt-filled epoxy using nanoindentation N2 - Epoxy/Carbon nanotube (CNT) composites are interesting materials that could be used in a wide variety of applications. In this study, CNT contents of 0.25, 0.5, 1 and 2 wt% were used for reinforcing epoxy. A nanoindentation device and a temperature regulating system were developed in order to investigate the effect of CNTs on the time-dependent properties of epoxy using relaxations and creep tests on the nano scale. The relaxation tests showed a significant shift for the relaxation spectrum towards shorter times with introducing a low CNT content of 0.25 wt%. Additionally, creep tests showed that both the holding time at a constant load and the unloading velocity have a major effect on the contact stiffness. However, there was no effect for the CNTs on the creep behavior with contents lower than 1 wt%, which was related to the presence of a percolation threshold around this value. T2 - Nanobrücken 2013 CY - Dresden, Germany DA - 20.03.2013 KW - Epoxy KW - CNT KW - Time-dependent KW - Nanoindentation PY - 2013 AN - OPUS4-35533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ho, K.K.C. A1 - Kalinka, Gerhard A1 - Tran, M.Q. A1 - Polyakova, N.V. A1 - Bismarck, A. T1 - Fluorinated carbon fibres and their suitability as reinforcement for fluoropolymers N2 - The interaction between direct fluorinated carbon fibres and various fluoropolymers (ethylene-chlorotrifluoroethylene, poly vinylidene fluoride, fluorinated ethylene propylene copolymer and tetrafluoroethylene-perfluoro alkoxy vinyl ether copolymer) was studied by means of direct wetting measurements between fibres and the polymer melts and single fibre pull-out tests. The results of both techniques allow the adhesion behaviour between the fibres and the matrices to be predicted. The results obtained show that a low degree of surface fluorination of carbon fibres leads to an improved wettability between the fibres and fluoropolymer melts and this is an indicator for an improved thermodynamic work of adhesion. The apparent interfacial shear strength as measure of practical adhesion, determined by the single fibre pull-out test, increases with increasing degree of surface fluorine content up to a maximum, which depends on the degree of fluorination of the matrix used. The improved interaction between the fibre and the matrix is due to an enhanced compatibility at the fibre/matrix interface. KW - Adhesion KW - A. Carbon fibres KW - B. Debonding KW - B. Interfacial strength PY - 2007 DO - https://doi.org/10.1016/j.compscitech.2007.02.012 SN - 0266-3538 VL - 67 IS - 13 SP - 2699 EP - 2706 PB - Elsevier CY - Barking AN - OPUS4-15814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pommet, M. A1 - Juntaro, J. A1 - Heng, J.Y.Y. A1 - Mantalaris, A. A1 - Lee, A.F. A1 - Wilson, K. A1 - Kalinka, Gerhard A1 - Shaffer, M.S.P. A1 - Bismarck, A. T1 - Surface modification of natural fibers using bacteria: depositing bacterial cellulose onto natural fibers to create hierarchical fiber reinforced nanocomposites N2 - Triggered biodegradable composites made entirely from renewable resources are urgently sought after to improve material recyclability or be able to divert materials from waste streams. Many biobased polymers and natural fibers usually display poor interfacial adhesion when combined in a composite material. Here we propose a way to modify the surfaces of natural fibers by utilizing bacteria (Acetobacter xylinum) to deposit nanosized bacterial cellulose around natural fibers, which enhances their adhesion to renewable polymers. This paper describes the process of modifying large quantities of natural fibers with bacterial cellulose through their use as substrates for bacteria during fermentation. The modified fibers were characterized by scanning electron microscopy, single fiber tensile tests, X-ray photoelectron spectroscopy, and inverse gas chromatography to determine their surface and mechanical properties. The practical adhesion between the modified fibers and the renewable polymers cellulose acetate butyrate and poly(l-lactic acid) was quantified using the single fiber pullout test. KW - Composires KW - Bacteria KW - Surface KW - Cellulose natural fibers PY - 2008 DO - https://doi.org/10.1021/bm800169g SN - 1525-7797 VL - 9 IS - 6 SP - 1643 EP - 1651 PB - ACS Publ. CY - Washington, DC, USA AN - OPUS4-23162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Godara, A. A1 - Gorbatikh, L. A1 - Kalinka, Gerhard A1 - Warrier, A. A1 - Rochez, O. A1 - Mezzo, L. A1 - Luizi, F. A1 - van Vuure, A.W. A1 - Lomov, S.V. A1 - Verpoest, I. T1 - Interfacial shear strength of a glass fiber/epoxy bonding in composites modified with carbon nanotubes N2 - In recent years, carbon nanotubes (CNTs) grown on fibers have attracted a lot of interest as an additional reinforcing component in conventional fiber-reinforced composites to improve the properties of the fiber/matrix interface. Due to harsh growth conditions, the CNT-grafted fibers often exhibit degraded tensile properties. In the current study we explore an alternative approach to deliver CNTs to the fiber surface by dispersing CNTs in the fiber sizing formulation. This route takes advantage of the developed techniques for CNT dispersion in resins and introduces no damage to the fibers. We focus on unidirectional glass fiber/epoxy macro-composites where CNTs are introduced in three ways: (1) in the fiber sizing, (2) in the matrix and (3) in the fiber sizing and matrix simultaneously. Interfacial shear strength (IFSS) is investigated using single-fiber push-out microindentation. The results of the test reveal an increase of IFSS in all three cases. The maximum gain (over 90%) is achieved in the composite where CNTs are introduced solely in the fiber sizing. KW - A. Carbon nanotubes KW - A. Hybrid composites KW - A. Polymer-matrix composites (PMCs) KW - B. Interfacial strength PY - 2010 DO - https://doi.org/10.1016/j.compscitech.2010.04.010 SN - 0266-3538 VL - 70 IS - 9 SP - 1346 EP - 1352 PB - Elsevier CY - Barking AN - OPUS4-22171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ho, K.K.C. A1 - Lamoriniere, S. A1 - Kalinka, Gerhard A1 - Schulz, Eckhard A1 - Bismarck, A. T1 - Interfacial behavior between atmospheric-plasma-fluorinated carbon fibers and poly(vinylidene fluoride) N2 - Atmospheric-plasma fluorination was used to introduce fluorine functionalities onto the surface of carbon fibers without affecting their bulk properties. The interfacial adhesion between atmospheric-plasma-fluorinated carbon fibers and poly(vinylidene fluoride) (PVDF) was studied by means of direct wetting measurements and single fiber pullout tests. Measured contact angles of PVDF melt droplets on modified carbon fibers show that short exposure times of carbon fibers to atmospheric-plasma fluorination (corresponding to a degree of surface fluorination of F/C = 0.01 (1.1%)) leads to improved wettability of the fibers by PVDF melts. The apparent interfacial shear strength as a measure of practical adhesion, determined by the single-fiber pullout test, increases by 65% under optimal treatment conditions. The improved practical adhesion is not due to the formation of transcrystalline regions around the fibers or a change of the bulk matrix crystallinity or to an increased surface roughness; it seems to be due to the compatibilization of the interface caused of the atmospheric-plasma fluorination of the carbon fibers. KW - Carbon fibers KW - Fluorination KW - Contact angle KW - Interface KW - Adhesion KW - Surface area KW - Fiber properties PY - 2007 DO - https://doi.org/10.1016/j.jcis.2007.04.076 SN - 0021-9797 SN - 1095-7103 VL - 313 IS - 2 SP - 476 EP - 484 PB - Elsevier CY - Orlando, Fla. AN - OPUS4-16026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wienrich, Malte A1 - Kalinka, Gerhard A1 - Greenhalgh, E.S. A1 - Carreyette, S. A1 - Bistritz, Martina A1 - Shirshova, N. A1 - Houllé, M. A1 - Asp, L. E. A1 - Bismarck, A. A1 - Fontana, Q.P.V. T1 - Impact of ionic liquid on the mechanical performance of matrix polymer for fibre reinforced materials for energy storage N2 - For the concept of using structural materials such as carbon fibre reinforced plastics as energy storage devices, new matrix polymers are required. These polymers must provide ionic conductivity as well as adequate mechanical strength. In the EU-Project StorAGE this requirements are fulfilled by adding ionic liquid to commercial polymers. The mechanical properties of these mixtures materials were characterized by using a 3-point-bending device. In addition, single fibre pull test were performed in order to get information on the interfacial shear strength. Adding of ionic liquid has an impact on the mechanical performance of the materials. A decrease of the flexural strength and modulus of less than 10% of the value of the reference materials took part. The interfacial shear strength decreased to a value of around one third compare to the reference material. T2 - ECCM15 - 15th European conference on composite materials CY - Venice, Italy DA - 2012-06-24 KW - Multifunctional epoxy resin KW - Fibre-matrix adhesion KW - Single fibre pull-out test KW - Ionic liquid PY - 2012 SN - 978-88-88785-33-2 SP - 1 EP - 4(?) AN - OPUS4-28695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Qian, Hui A1 - Bismarck, A. A1 - Greenhalgh, E.S. A1 - Kalinka, Gerhard A1 - Shaffer, M.S.P. T1 - Hierarchical composites reinforced with carbon nanotube grafted fibers: The potential assessed at the single fiber level N2 - The feasibility of reinforcing conventional carbon fiber composites by grafting carbon nanotubes (CNTs) onto the fiber surface has been investigated. Carbon nanotubes were grown on carbon fibers using the chemical vapor deposition (CVD) method. Iron was selected as the catalyst and predeposited using the incipient wetness technique before the growth reaction. The morphology of the products was characterized using scanning electron microscopy (SEM), which showed evidence of a uniform coating of CNTs on the fiber surface. Contact angle measurements on individual fibers, before and after the CNT growth, demonstrated a change in wettability that can be linked to a change of the polarity of the modified surface. Model composites based on CNT-grafted carbon fibers/epoxy were fabricated in order to examine apparent interfacial shear strength (IFSS). A dramatic improvement in IFSS over carbon fiber/epoxy composites was observed in the single fiber pull-out tests, but no significant change was shown in the push-out tests. The different IFSS results were provisionally attributed to a change of failure mechanism between the two types of tests, supported by fractographic analysis. KW - Composites KW - Nano tubes KW - Grafting KW - Interface PY - 2008 DO - https://doi.org/10.1021/cm702782j SN - 0897-4756 SN - 1520-5002 VL - 20 IS - 5 SP - 1862 EP - 1869 PB - American Chemical Society CY - Washington, DC AN - OPUS4-34568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tran, M.Q. A1 - Ho, K.K.C. A1 - Kalinka, Gerhard A1 - Shaffer, M.S.P. A1 - Bismarck, A. T1 - Carbon fibre reinforced poly(vinylidene fluoride): Impact of matrix modification on fibre/polymer adhesion N2 - The quality of interfacial interaction is dictated by the surface chemistry of the carbon fibres and the composition of the matrix. The composition of poly(vinylidene fluoride) (PVDF) was modified by the addition of maleic anhydride grafted PVDF. The surface properties of the various matrix formulations were characterised by contact angle and electrokinetic measurements. Carbon fibres were modified by industrial electrochemical oxidation and oxidation in nitric acid, or the use of a traditional epoxy-sizing of industrially oxidised fibres. The surface composition, morphology and wetting behaviour of the carbon fibres was characterised. The interaction between modified PVDF and the carbon fibres was studied by direct contact angle measurements between PVDF melt on single carbon fibres and by single fibre pull-out tests. The best wetting and adhesion behaviour was achieved between PVDF containing 5 ppm grafted maleic anhydride (MAH) and epoxy-sized carbon fibres. The addition of MAH-grafted PVDF to the unmodified PVDF caused the apparent interfacial shear strength to increase by 184%. The apparent interfacial shear strength of this fibre–matrix combination allowed for the utilisation of 100% of the yield tensile strength of PVDF. KW - A. Carbon fibres KW - A. Coupling agents KW - B. Interface KW - B. Adhesion KW - Wetting PY - 2008 DO - https://doi.org/10.1016/j.compscitech.2008.02.021 SN - 0266-3538 VL - 68 IS - 7-8 SP - 1766 EP - 1776 PB - Elsevier CY - Barking AN - OPUS4-18259 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wettmarshausen, Sascha A1 - Friedrich, Jörg Florian A1 - Meyer-Plath, Asmus A1 - Kalinka, Gerhard A1 - Hidde, Gundula A1 - Weidner, Steffen T1 - Coating of carbon fibers with adhesion-promoting thin poly(acrylic acid) and poly(hydroxyethylmethacrylate) layers using electrospray ionization N2 - Thin coatings of poly(acrylic acid) (PAA) and poly(hydroxyethylmethacrylate) (PHEMA) were deposited onto carbon fibers by means of the electrospray ionization (ESI) technique in ambient air. These high-molecular weight polymer layers were used as adhesion promoters in carbon fiber–epoxy resin composites. Within the ESI process, the carbon fibers were completely enwrapped with polymer in the upper 10 plies of a carbon fiber roving. As identified with scanning electron microscopy also shadowed fibers in a bundle as well as backsides of fiber rovings were pinhole-free coated with polymers (‘electrophoretic effect'). Under the conditions used, the layers have a granular structure. Residual solvent was absent in the deposit. PAA and PHEMA films did not show any changes in composition and structure in comparison with the original polymers as analyzed by X-ray photo-electron spectroscopy and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Single-fiber pullout tests of coated fibers embedded in epoxy resin showed significantly increased interfacial shear strength. It is assumed that chemical bonds between carbon fiber poly(acrylic acid) and epoxy resin contribute significantly to the improved interactions. KW - Adhesion promotion KW - Thin polymer layers KW - Electrospray ionization (ESI) KW - Carbon fiber–epoxy resin laminates KW - Layer topography PY - 2015 DO - https://doi.org/10.1080/01694243.2015.1040980 SN - 0169-4243 SN - 1568-5616 VL - 29 IS - 15 SP - 1628 EP - 1650 PB - VNU Science Press CY - Utrecht AN - OPUS4-34564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalinka, Gerhard A1 - Leistner, André A1 - Hampe, Andreas T1 - Characterisation of the fibre/matrix interface in reinforced polymers by the push-in technique N2 - The push-in test is the only micromechanical test method that is not restricted to artificial fibre/matrix arrangements, but allows the in situ characterisation of interfaces in composites fabricated and stressed under realistic conditions. However, with the application of this method to reinforced polymers some problems arise both in the mathematical model for evaluating test data and in the practical performance of the test. Because in some cases the deformation of the relatively compliant polymeric matrices cannot be neglected, an extension of the existing model is required. For this purpose, the elastic energy of the material around the debonded part of the fibre is estimated and included in the energy-balance analysis. Because of the small diameter of the fibres usually used for reinforcing polymers, a test apparatus was designed which ensures a high positioning accuracy in the xy plane as well as in the z direction. In order to minimise thermal and mechanical influences, the microscope for fibre selection and the force sensor/indenter are directly connected together and the apparatus is designed to be stiff in all components. A solid-state bending joint guarantees very precise control of the axial movement. Three examples of the application of this easy-to-handle and low-cost test apparatus are presented briefly in the paper: assess fibre/matrix combinations, measures to improve the interfacial adhesion and the influence of water on the interface. KW - Interface KW - Test method KW - Characterisation KW - Indentation KW - Push-in PY - 1997 SN - 0266-3538 VL - 57 IS - 8 SP - 845 EP - 851 PB - Elsevier CY - Barking AN - OPUS4-12011 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Torsten T1 - Helical zirconia (TZP) springs manufacturing and testing under mechanical and thermal load N2 - Helical springs with a rectangular cross-section have been machined from sintered and grinded hollow cylinders with high geometrical precision and good reproducibility. Such springs made from tetragonal zirconia polycrystal (TZP) ceramic show excellent edge quality because of high fracture toughness and bending strength of the starting material. Hence, springs with desired geometric dimension and tailored spring constant can be manufactured for highly demanding applications at high temperatures and in harsh environments. Prior to any practical use, application limits of springs under mechanical and thermal load have to be analyzed. Therefore, different displacement experiments were carried out on the helical TZP springs. - Dynamic displacement tests at various temperatures from -15°C to +60°C using a piezo actor to load/unload springs with frequencies between 1 and 40 Hz: Springs remained undamaged and the spring constants were not altered, even after more than one million cycles of compression loading. - Long-time displacement measurements under static tensile loading at room temperature with a high-precision interferometer test facility: Significant spring elongation under constant strain was surprisingly proved over a period of many hours already at room temperature. - Creeping experiments for 48 h under static compression load at different temperatures up to 1000 °C: After cooling down and load removing no permanent length reduction of springs was observed for test temperatures up to 700 °C. However, reshaping of TZP springs by plastic deformation is possible at higher temperatures and opens up additional possibilities for spring design and manufacturing. T2 - German Ceramic Society, Annual Meeting 2018 CY - München, Germany DA - 09.04.2018 KW - Ceramic springs KW - Manufacturing KW - Mechanical and thermal testing PY - 2018 AN - OPUS4-44728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plichta, T. A1 - Sirjovona, V. A1 - Zvonek, M. A1 - Kalinka, Gerhard A1 - Cech, V. T1 - The Adhesion of Plasma Nanocoatings Controls the Shear Properties of GF/Polyester Composite N2 - High-performance fibre-reinforced polymer composites are important construction materials based not only on the specific properties of the reinforcing fibres and the flexible polymer Matrix but also on the compatible properties of the composite interphase. First, oxygen-free (a-CSi:H) and oxygen-binding (a-CSiO:H) plasma nanocoatings of different mechanical and tribological properties were deposited on planar silicon dioxide substrates that closely mimic E-glass. The nanoscratch test was used to characterize the nanocoating adhesion expressed in terms of critical normal load and work of adhesion. Next, the same nanocoatings were deposited on E-glass fibres, which were used as reinforcements in the polyester composite to affect its interphase properties. The shear properties of the polymer composite were characterized by macro- and micromechanical tests, namely a short beam shear test to determine the short-beam strength and a single fibre push-out test to determine the interfacial shear strength. The results of the polymer composites showed a strong correlation between the short-beam strength and the interfacial shear strength, proving that both tests are sensitive to changes in fibre-matrix adhesion due to different surface modifications of glass fibres (GF). Finally, a strong correlation between the shear properties of the GF/polyester composite and the adhesion of the plasma nanocoating expressed through the work of adhesion was demonstrated. Thus, increasing the work of adhesion of plasma nanocoatings from 0.8 to 1.5 mJ·m−2 increased the short-beam strength from 23.1 to 45.2 MPa. The results confirmed that the work of adhesion is a more suitable parameter in characterising the level of nanocoating adhesion in comparison with the critical normal load. KW - Mechanical properties KW - Plasma nanocoatings KW - Glass fibre KW - Polymer composite KW - Short-beam strength KW - Interfacial shear strength KW - Work of adhesion PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521844 DO - https://doi.org/10.3390/polym13040593 VL - 13 IS - 4 SP - 593 PB - MDPI CY - Basel,Schweiz AN - OPUS4-52184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barnefske, Lena T1 - Self-healing silicone rubber for F-POF partial discharge sensors in HV cable accessories N2 - To avoid a catastrophic failure of insulation in high-voltage (HV) applications, a monitoring of partial discharges (PD) is necessary. Fluorescently labelled polymer optical fibres (F-POF) offer an electrically passive method for PD detection in HV facilities. F-POF could be embedded into HV cable insulation material, which are usually made of silicone rubber. Due to the difficult accessibility of HV cable accessories, a self-healing silicone rubber, based on incorporated capsules, with prolonged service life after PD detection represents an attractive material design for HV electrical insulation. T2 - 26th International Conference on Plastic Optical Fibres CY - Aveiro, Portugal DA - 13.09.2017 KW - Fluorescent polymer optical fibres KW - Partial discharge detection KW - High voltage cable accessories KW - Self-healing KW - Silicone rubber PY - 2017 AN - OPUS4-42511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gebhardt, M. A1 - Manolakis, I. A1 - Chatterjee, A. A1 - Kalinka, Gerhard A1 - Deubener, J. A1 - Pfnür, H. A1 - Chakraborty, S. A1 - Meiners, D. T1 - Reducing the raw material usage for room temperature infusible and polymerisable thermoplastic CFRPs through reuse of recycled waste matrix material N2 - In this work, a closed loop recycling process is investigated, which allows polymerised bulk thermoplastic matrix (Elium 150) from production waste (also referred to as recyclate) to be reused as additive in composite manufacturing by vacuum assisted resin infusion (VARI) of virgin Elium 150 monomer. It is shown that this process can save up to 7.5 wt% of virgin material usage in each processing cycle. At the same time, the thermal stability and stiffness of the composite increases with the proportion of recyclate introduced. Contemporarily, the shear and bending properties have also been observed to improve. Gel permeation chromatography (GPC) showed that the changes observed are due to an increase in molecular weight with the recyclate content. In particular, a correlation between the molecular weight and the shear properties of the composite was discovered using single fibre push-out tests. KW - Mechanical properties KW - Recycling KW - Carbon fibres KW - Fibre/matrix bond PY - 2021 DO - https://doi.org/10.1016/j.compositesb.2021.108877 SN - 1359-8368 VL - 216 SP - 108877 PB - Elsevier Ltd. CY - Niederlande AN - OPUS4-52711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Guerra, E. S. S. A1 - Silva, B. L. A1 - Melo, J. D. D. A1 - Kalinka, Gerhard A1 - Barbosa, A. P. C. T1 - Microscale evaluation of epoxy matrix composites containing thermoplastic healing agent N2 - Among the strategies to produce healable thermosetting systems is their modification by the addition of thermoplastic particles. This work investigates the influence of poly(ethylene-co-methacrylic acid) (EMAA) on fibermatrix interfacial properties of a glass fiber reinforced epoxy matrix composite. Epoxy-EMAA interactions were evaluated using differential scanning calorimetry (DSC) and infrared spectroscopy. The effects of EMAA on the epoxy network formation were evidenced by changes in glass transition temperature, cure kinetics and alteration of chemical groups during cure. Interfacial shear strength (IFSS) measurements obtained by single fiber pull-out tests indicate similar interfacial properties for pure and EMAA modified epoxy. Additionally, the potential for self-healing ability of an EMAA modified epoxy was demonstrated. However, IFSS after a healing cycle for the EMAA modified epoxy was lower as compared to the pure epoxy, because of the lower fiber-EMAA interfacial shear strength. So, thermoplastic healing agents has not only to fill cracks in the matrix material, but also have to be optimized regarding its interface properties to the reinforcing fibers. KW - Interfacial strength KW - Fiber/matrix bond KW - Self-healing KW - Polymer-matrix composites (PMC) PY - 2022 DO - https://doi.org/10.1016/j.compscitech.2022.109843 SN - 0266-3538 VL - 232 SP - 1 EP - 9 PB - Elsevier Ltd. CY - Niederlande AN - OPUS4-56379 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Greenhalgh, E.S. A1 - Ankersen, J. A1 - Asp, L. E. A1 - Bismarck, A. A1 - Fontana, Q.P.V. A1 - Houlle, M. A1 - Kalinka, Gerhard A1 - Kucernak, A. A1 - Mistry, M. A1 - Nguyen, S. A1 - Qian, H. A1 - Shaffer, M.S.P. A1 - Shirshova, N. A1 - Steinke, J.H.G. A1 - Wienrich, Malte T1 - Mechanical and microstructural characterisation of multifunctional structural power composites N2 - Although the inherent anisotropy of polymer composites has presented daunting technical challenges, these materials now offer engineers considerable opportunities for efficient structural design. More recently, the advent of multifunctional composites which can fulfill more than one role within a system has attracted considerable interest, providing designers with exciting opportunities to innovate. Of particular interest here are structural power composites, which simultaneously carry mechanical load whilst storing/delivering electrical energy. Although the development of these composites is highly challenging, often with conflicting constituent requirements, the STORAGE consortium has had considerable success in the development of these materials for automotive applications. The focus of this paper is structural supercapacitors, the basic architecture of a single cell of which is shown in Fig. 1. This entails two carbon fibre woven lamina (electrodes) which sandwich a glass fibre woven lamina (separator), all of which is embedded within a multifunctional matrix (electrolyte). This architecture has been the focus of the research to date, leading to components such as that shown in Fig.1 having been fabricated. This paper reports on the mechanical properties and microstructures of the different reinforcement and matrix combinations for structural supercapacitors. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Structural electrolyte KW - Multifunctional supercapacitor KW - Fractography KW - Ionic conductivity KW - Mechanical properties PY - 2013 SP - 2228 EP - 2237 AN - OPUS4-29272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gebhardt, M. A1 - Malolakis, I. A1 - Kalinka, Gerhard A1 - Deubener, J. A1 - Chakraborty, S. A1 - Meiners, D. T1 - Re-use potential of carbon fibre fabric recovered from infusible thermoplastic CFRPs in 2nd generation thermosetting-matrix composites N2 - The research presented here attempts to assess the potential for re-using carbon fibre (CF) fabrics recovered from recycling infusible acrylic thermoplastic carbon fibre reinforced polymer composites (CFRPs) in a universal manner, i.e. by combining with a wide variety of matrices to manufacture 2nd generation composite laminates by resin infusion. The 2nd generation composites have been compared in terms of bulk and interfacial properties against counteparts processed with virgin carbon fibre fabric infused with the same matrices. Generally, an increase in damping (tanδ) was observed in all 2nd generation composites, which can be attributed to a residual thin thermoplastic layer present on the recovered fibres. The interfacial adhesion of the 2nd generation Composites was investigated by shear tests and scanning electron micsoscopy, and also appears to be less influenced by the type of matrix. KW - Composite recycling KW - Thermoplastic matrix KW - Thermosetting resin KW - Fibre/matrix bonding PY - 2021 DO - https://doi.org/10.1016/j.coco.2021.100974 VL - 28 SP - 100974 PB - Elsevier Ltd. CY - Niederlande AN - OPUS4-53639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Elabshihy, Karim T1 - Nano-mechanical characterization of epoxy/Cu interphase N2 - Characterization of the mechanical properties of interphases is essential when designing multicomponent materials such as fiber-reinforced matrices, protective coatings or multi-layered structures for integrated circuits. It can provide vital information about the durability of the finished product as a composite because failure is often initiated in the interfacial region induced by internal or external stress during fabrication or service. Nanoindentation is a powerful tool for investigating mechanical properties on the micro/nano scale. However, there are some challenges associated with conducting nanoindentation near interface regions. One main challenge is that the small thickness of the interphase region (typically 1-2µm) makes it difficult to apply several adjacent indents without overlap. Another issue is that the indentations are usually restricted by local reinforcement, and it becomes difficult to isolate the change in mechanical properties due solely to interphase formation. In this study we try to gauge the feasibility of nanoindentation for characterizing epoxy/Cu interphases. We develop a sample preparation method and optimize nanoindentation parameters in an attempt to avoid the restrictions mentioned above. Atomic force microscopy (AFM) and finite element analysis are employed as reference techniques to evaluate the effectiveness of our technique. We show the influence of preparation method and nanoindentaion parameters on measurements of interphase properties and how they relate the mentioned challenges. T2 - Nanobrücken 2016 CY - Saarbrücken, Germany DA - 02.03.2016 KW - Composite KW - Epoxy KW - Interphase KW - Nanoindentation PY - 2016 AN - OPUS4-35496 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Heinz A1 - Schulz, Eckhard T1 - Local AC current contrast on carbon fiber surfaces imaged by scanning force microscopy N2 - After a delamination process in a C-fiber reinforced polymer composite, the identification of the polymer residue of poly-(phenylene sulphide) on carbon fiber surfaces gives important information on the composite failure mechanism. Using scanning force microscopy (SFM) in its lateral force imaging mode or with the stiffness imaging mode, it is almost impossible to distinguish the two composite components owing to a very low material-based contrast of the local friction and compliance. The new technique using contrast based on a local AC current measurement allows a clear identification of the conducting carbon fiber and the non-conducting polymer coverage. KW - Matrix adhesion KW - Films KW - Photoconduction KW - Composites PY - 1995 DO - https://doi.org/10.1002/actp.1995.010460505 SN - 0323-7648 SN - 1521-4044 VL - 46 IS - 5 SP - 379 EP - 384 PB - Wiley-VCH Verl. CY - Weinheim, Germany AN - OPUS4-6848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Heinz T1 - Improving polymer matrix additives for composite structures: a focus on boehmite N2 - The aims of the Research Unit „Acting Principles of Nano-Scaled Matrix Additives for Composite Structures“ (DFG FOR 2021) are based on different synergetic pathways. Challenges are to achieve an improved damage tolerance combined with unchanged processability and a proof of the nano-based effect from molecular scale up to structural level. First of all, a comprehensive understanding of the acting mechanisms of nano-scaled ceramic additives onto polymer matrices of continuous fibre reinforced polymer composites with respect to improved matrix dominated properties is in focus. To proof of the nanoscopic and microscopic effects up to structural level; experimental investigations start on the functional correlation between the particle properties and the resulting properties of the epoxy as suspension and in the solid state. This includes tests for the resulting composite structures as well. Along the entire process chain different multi-scale simulations are performed from molecular modelling up to the macroscopic, structural level. The combination of experimental investigations and simulation methods enables a holistic understanding of the acting principles and basic mechanisms. Specialized techniques based on Scanning Force Microscopy are the basis of our analysis of physicochemical properties of the boehmite nanoparticles and their polymer environment. A surface map of mechanical properties as an input for simulations facilitate a deeper understanding of such composites across all scales. This enables us to understand the macroscopic structure-property relationship and to predict failure mechanisms as well as routes for optimization. T2 - 92nd DKG annual meeting and symposium on high performance ceramics CY - Berlin, Germany DA - 19.03.2017 KW - Boehmite nanoparticle KW - Intermodulation AFM KW - Composite structures KW - Pull-out test KW - Thermoset KW - Crack propagation energy PY - 2017 AN - OPUS4-39519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schreier, Andy T1 - Distributed Brillouin sensing in polymer optical fibers N2 - A brief overview about the results obtained within the BAM PhD framwork. T2 - Meeting of the Terahertz-Photonics-Group at IHF, Technische Universität Braunschweig CY - Braunschweig, Germany DA - 17.07.2019 KW - Brillouin KW - Distributed sensing KW - Polymer optical fibre PY - 2019 AN - OPUS4-48501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schukar, Vivien A1 - Kusche, Nadine A1 - Kalinka, Gerhard A1 - Habel, Wolfgang T1 - Field deployable fiber bragg grating strain patch for long-term stable health monitoring applications N2 - A fiber Bragg grating (FBG) strain patch specially adapted for long-term and high-strain applications has been developed and characterized. The design concept for the patch is based on a glass-fiber reinforced plastic (gfrp) carrier material. The developed concept for the FBG integration into the carrier material was derived from reliable integration procedure of FBG sensors into composite structures. The patches' temperature sensitivity, strain gauge factor, fiber–matrix interface adhesion and fatigue behavior were characterized. As a result, FBG strain patches with linear temperature and strain behavior, as well as excellent fatigue resistance, were developed and can be used as part of a monitoring system for advanced composite materials in aerospace structures or wind turbine power plants. KW - Fiber Bragg grating KW - Patch KW - Strain gauge factor KW - Temperature sensitivity KW - Push-out test KW - Validation KW - Fatigue behavior PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-276271 DO - https://doi.org/10.3390/app3010039 SN - 2076-3417 VL - 3 IS - 1 SP - 39 EP - 54 PB - MDPI CY - Basel AN - OPUS4-27627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Bioinspired hybrid organic-inorganic copolymers N2 - The demand for high-performance materials has strongly increased over the last decade. One way to improve their performance is to introduce material gradients as found in Nature (for example squid beaks, spider fangs, mussel byssal threads). One path towards the achievement of such material gradients is the synthesis of hybrid (gradient) copolymers, for instance based on silane and organic monomers. Since not all gradient copolymers can be synthesized by utilising the reactivity ratios of the monomers, forced gradients have to be used. However, in order to obtain gradient copolymers at high conversions, living or pseudo-living copolymerizations have to be performed and so far only few hybrid (organic / inorganic) gradient copolymers have been reported. In this contribution we will present the synthesis of a novel organic / inorganic hybrid copolymer via controlled radical polymerization. T2 - 5th International Conference on Multifunctional, Hybrid and Nanomaterials CY - Lisbon, Portugal DA - 06.03.2017 KW - Hybrid organic-inorganic copolymers KW - RAFT polymerization KW - ATRP polymerization PY - 2017 AN - OPUS4-39464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shirshova, N. A1 - Bismarck, A. A1 - Carreyette, S. A1 - Greenhalgh, E.S. A1 - Johansson, P. A1 - Marczewski, M.J. A1 - Jacobsson, P. A1 - Kalinka, Gerhard A1 - Shaffer, M.S.P. A1 - Wienrich, Malte A1 - Steinke, J.H.G. T1 - Correlations between mechanical properties and ionic conduction of structural electrolytes with bicontinuous morphologies N2 - Electrolyte systems that can carry mechanical load while allowing for high levels of ionic conductivity are an important prerequisite for structural power storage devices. Introduction of structural power storage into the variety of consumer products will allow saving in weight and volume. Moreover, using a supercapacitor/battery system in hybrid electric vehicles (HEV), the supercapacitor part will extend the battery lifetime by protecting it from the high peak currents. To successfully produce structural power storage requires the development of multifunctional electrolytes where one has to simultaneously maximize mechanical properties and ionic conductivity. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Structural electrolyte KW - Multifunctional supercapacitor KW - Bicontinuous morphology KW - Epoxy resin KW - Ionic conductivity KW - Mechanical properties PY - 2013 SP - 72 EP - 79 AN - OPUS4-29273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhandarov, S. A1 - Mäder, E. A1 - Kalinka, Gerhard A1 - Scheffler, C. A1 - Poitzsch, C. A1 - Fliescher, S. T1 - Investigation of interfacial strength parameters in polymer matrix composites: Compatibility and reproducibility N2 - Effects of various geometrical and physical factors, as well as the method of data reduction (analysis of experimental forceedisplacement curves) on the values of local interfacial strength parameters (local IFSS, td, and critical energy release rate, Gic) determined by means of a single fiber pull-out test are discussed. Experimental results of our pull-out tests on several fiberepolymer matrix systems showed that td and Gic weakly depended on geometrical factors. However, the pull-out test appeared to be sensitive to the conditions of specimen formation and testing, such as changing the nature of the contacting surfaces (fiber sizing) and the fiber pull-out rate. Of several methods of td and Gic Determination from a forceedisplacement curve, the most reliable and reproducible one is the approach based on the values of the maximum force recorded in a pull-out test and the interfacial frictional force immediately after fiber debonding. KW - Interface KW - Interfacial shear strength KW - Pull-out composite materials KW - Polymer matrix composites KW - Critical energy release rate KW - Geometrical factors PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-460918 DO - https://doi.org/10.1016/j.aiepr.2018.06.002 SN - 2542-5048 VL - 1 IS - 1 SP - 82 EP - 92 PB - Elsevier CY - Amsterdam AN - OPUS4-46091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blaker, J. J. A1 - Anthony, David B. A1 - Tang, G. A1 - Shamsuddin, S.-R. A1 - Kalinka, Gerhard A1 - Wienrich, Malte A1 - Abdolvand, Amin A1 - Shaffer, M. S. P. A1 - Bismarck, A. T1 - Property and shape modulation of carbon fibers using lasers N2 - An exciting challenge is to create unduloid-reinforcing fibers with tailored dimensions to produce synthetic composites with improved toughness and increased ductility. Continuous carbon fibers, the state-of-the-art reinforcement for structural composites, were modified via controlled laser irradiation to result in expanded outwardly tapered regions, as well as fibers with Q-tip (cotton-bud) end shapes. A pulsed laser treatment was used to introduce damage at the single carbon fiber level, creating expanded regions at predetermined points along the lengths of continuous carbon fibers, while maintaining much of their stiffness. The range of produced shapes was quantified and correlated to single fiber tensile properties. Mapped Raman spectroscopy was used to elucidate the local compositional and structural changes. Irradiation conditions were adjusted to create a swollen weakened region, such that fiber failure occurred in the laser treated Region producing two fiber ends with outwardly tapered ends. Loading the tapered fibers allows for viscoelastic energy dissipation during fiber pull-out by enhanced friction as the fibers plough through a matrix. In these tapered fibers, diameters were locally increased up to 53%, forming outward taper angles of up to 1.8°. The tensile strength and strain to failure of the modified fibers were significantly reduced, by 75% and 55%, respectively, ensuring localization of the break in the expanded region; however, the fiber stiffness was only reduced by 17%. Using harsher irradiation conditions, carbon fibers were completely cut, resulting in cottonbud fiber end shapes. Single fiber pull-out tests performed using these fibers revealed a 6.75-fold increase in work of pull-out compared to pristine carbon fibers. Controlled laser irradiation is a route to modify the shape of continuous carbon fibers along their lengths, as well as to cut them into controlled lengths leaving tapered or cotton-bud shapes. KW - Composite KW - Irradiation KW - Pull-out tests KW - Pulsed laser treatment KW - Single carbon fibers PY - 2016 DO - https://doi.org/10.1021/acsami.6b05228 SN - 1944-8244 SN - 1944-8252 VL - 8 IS - 25 SP - 16351 EP - 16358 PB - ACS Publications CY - 1155 Sixteenth Street, NW, Washington, DC 20036, USA AN - OPUS4-37699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Palantöken, Sinam A1 - Bethke, K. A1 - Zivanovic, V. A1 - Kneipp, Janina A1 - Rademann, Klaus A1 - Kalinka, Gerhard T1 - Cellulose hydrogels physically crosslinked by glycine: Synthesis, characterization, thermal and mechanical properties N2 - Biopolymers are very efficient for significant applications ranging from tissue engineering, biological devices to water purification. There is a tremendous potential value of cellulose because of ist being the most abundant biopolymer on earth, swellability, and functional groups to be modified. A novel, highly efficient route for the fabrication of mechanically stable and natural hydrogels is described in which cellulose and glycine are dissolved in an alkaline solution of NaOH and neutralized in an acidic solution. The dissolving temperature and the glycine amount are essential parameters for the self-assembly of cellulose chains and for Tuning the morphology and the aggregate structures of the resulting hydrogels. Glycine plays the role of a physical crosslinker based on the Information obtained from FTIR and Raman spectra. Among the prepared set of hydrogels, CL5Gly30 hydrogels have the highest capacity to absorb water. The prepared CL5Gly30 gels can absorb up to seven times their dry weight due to its porous 3-D network structure. CL5Gly10 hydrogel exhibits 80% deformation under 21 N force executed. The method developed in this article can contribute to the application of heavy metal adsorption in aqueous solutions for water purification and waste management. KW - Biopolymer KW - Cellulose KW - Hydrogel KW - Natural KW - Synthesis PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-486845 DO - https://doi.org/10.1002/APP.48380 SN - 1097-4628 SN - 0021-8995 VL - 136 SP - 48380, 1 EP - 11 PB - Wiley CY - USA AN - OPUS4-48684 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krauklis, A. E. A1 - Starovka, O. A1 - Gibhardt, D. A1 - Aouissi, H. A. A1 - Burlakovs, J. A1 - Sabalina, A. A1 - Fiedler, Bodo A1 - Kalinka, Gerhard T1 - Reversible and irreversible effects on the epoxy GFRP fiber-matrix interphase due to hydrothermal aging N2 - Epoxy R-Glass Fiber-Reinforced Polymer (GFRP) composite plates were hydrothermally aged at 60 ◦C for 23, 75, and 133 days. The water content reached 0.97 wt%, 1.45 wt% and 1.63 wt%, respectively. The studied GFRP matrix was inert to hydrolysis or chain scission, allowing for investigation of irreversible changes in the fiber-matrix interphase due to hydrothermal aging upon re-drying. During each period, a subset of the specimens was removed from the water bath and dried in a chamber. The weight loss upon drying was explained with epoxy leaching (impurities), sizing-rich interphase hydrolysis, glass fiber surface hydrolysis, accumulated degradation products escaping, and water changing state from bound to free. The influence of hydrothermal aging on the fiber-matrix interfacial properties was investigated. Lower interfacial strength of hydrothermally aged (wet) samples was attributed to plasticization of the epoxy, plasticization and degradation of the sizing-rich interphase (including formation of hydrolytic flaws), and hydrolytic degradation of the glass fiber surface. The kinetics of epoxy-compatible epoxysilane W2020 sizing-rich interphase hydrolysis provided an estimate of ca. 1.49%, 4.80%, and 8.49% of the total composite interphase degraded after 23, 75, and 133 days, respectively. At these conditions, the interface lost 39%, 48%, and 51% of its strength. Upon re-drying the specimens, a significant part of the interfacial strength was regained. Furthermore, an upward trend was observed, being 13%, 10% and 3% strength, respectively; thus, indicating a possibility of partial recovery of properties. KW - GFRP KW - Hydrothermal Ageging KW - Interphase KW - Water Diffusion KW - Desorption KW - Interfacial Strength PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581554 DO - https://doi.org/10.1016/j.jcomc.2023.100395 SN - 2666-6820 VL - 12 SP - 1 EP - 9 PB - Elsevier B.V. CY - Amsterdam, Niederlande AN - OPUS4-58155 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalinka, Gerhard A1 - Sahin, M. A1 - Schlögl, S. A1 - Wang, J. A1 - Kaynak, B. A1 - Mühlbacher, I. A1 - Ziegler, W. A1 - Kern, W. A1 - Grützmacher, H. T1 - Tailoring the interfaces in glass fiber-reinforced photopolymer composites N2 - The present work provides a comparative study on the interface and adhesion properties of surface modified single glass fibers embedded in an acrylate matrix. To facilitate a covalent bonding at the fibermatrix interface, the fibers are functionalized with selected organosilanes that comprise either passive (unsaturated C¼C bonds of methacrylate moieties) or photoactive functionalities (photocleavable bis(acyl)phosphane oxide groups). Immobilization of the functional silanes is carried out by a classic silanization reaction involving a condensation reaction across the surface hydroxyl groups of the inorganic glass fibers. The change of the physico-chemical properties of the fibers due to desizing and subsequent surface modification is monitored by X-ray photoelectron spectroscopy and zeta potential measurements. In addition, scanning electron microscopy is used to follow the changes in surface morphology. After the modification step, the desized and modified single fibers are embedded in a photocurable acrylate resin formulation. By performing single fiber pull-out tests, maximum pull-out force, friction strength and apparent interfacial shear strength are determined as a function of the coupled silanes. The results reveal that the attached organosilanes lead to a significant increase in adhesion strength, whilst the performance of the photo-cleavable organosilane is superior to the passive methacryl-functional derivative. KW - Photocleavable organosilanes KW - Fiber-matrix interface KW - Photopolymer composites KW - Single fiber pull-out test KW - Surface modification PY - 2018 DO - https://doi.org/10.1016/j.polymer.2018.03.020 SN - 0032-3861 VL - 141 SP - 221 EP - 231 PB - Elsevier Ltd. CY - New York AN - OPUS4-44784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Controlled Self-Assembly of Janus Dendrimers via Microfluidics N2 - Unilamellar vesicles self-assembled in water from natural and synthetic phospholipids (liposomes), amphiphilic block copolymers (polymersomes), and more recently amphiphilic Janus dendrimers (dendrimersomes) as hollow soft structures in the nano size regime have attracted increasing interest as they can mimic primitive and contemporary biological membranes, and can be configured into biomimetic nanocapsules with application in nanomedicine such as gene, proteins and drug carriers or theranostics. Compared to other amphiphilic structures, the molecular structure of Janus dendrimers can be precisely controlled: by using the vast range of tools from organic chemistry their size, architecture, density, generation as well as the number of endgroups of the individual dendrons can be modified as desired. Unfortunately, the controlled production of the supramolecular aggregates made thereof is still a challenging task. Conventional batch-based techniques such as the solvent injection method or the film hydration method typically go along with a lack of control over mixing and thus over size, morphology and size distribution. The micromixer technology is a promising method for the controlled preparation of supramolecular assemblies as it allows control of mixing at microscale level. In addition, such microfluidic systems benefit from a high mixing efficiency, a low mixing time as well as from a reproducible and continuous synthesis. Herein, we report on the microfluidic-controlled self-assembly of Janus dendrimers as dendrimersomes and the impact of the mixing parameters on the self-assembly process. T2 - 10th International Dendrimer Symposium CY - Weihai, China DA - 05.08.2017 KW - Micromixers KW - Janus dendrimers KW - Vesicles KW - Self-assembly PY - 2017 AN - OPUS4-41464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, Luman A1 - de Greef, Nils A1 - Kalinka, Gerhard A1 - Van Bilzen, Bart A1 - Locquet, Jean-Pierre A1 - Verpoest, Ignaas A1 - Won Seo, Jin T1 - Carbon nanotube-grafted carbon fiber polymer composites: Damage characterization on the micro scale N2 - Multiwall carbon nanotubes (CNTs) e carbon fibers (CFs)hybrid materials were produced by directly growing CNTs on CFs by means of chemical vapor deposition. For the latter, the oxidative dehydrogenation reaction of C2H2 and CO2 was applied, which allows growing CNTs without damaging the CF surface. Uni-directional nano-engineered carbon fiber reinforced composites (nFRCs) were fabricated by impregnating these hybrid materials with epoxy. The nFRCs subjected to single fiber push-out tests revealed a decrease of the interfacial shear strength (IFSS) of about 36% compared to the carbon fiber composites without CNTs. By means of transverse three-point bending tests performed on pre-notched composite beams inside a scanning electron microscope, the fracturing behavior parallel to the fibers was studied in-situ. The nFRCs showed significantly reduced fiber/matrix debonding while CNTs pull-out, CNTs bridging as well as matrix failure occurred. These results demonstrate that the presence of CNTs in nFRCs affects the stress distribution and consequently the damage Initiation as well as the damage propagation. The presence of CNTs suppresses the stress concentration at the fiber/Matrix interface and reduces the debonding of CFs from the matrix. However, our results indicate that the stress concentration shifts towards the CNTs' ends/matrix interface and causes promoted matrix failure leading to lower IFSS. KW - Carbon fibres nanotubes interface PY - 2017 DO - https://doi.org/10.1016/j.compositesb.2017.06.004 SN - 1359-8368 SN - 1879-1069 VL - 126 SP - 202 EP - 210 PB - Elsevier CY - Niederlande AN - OPUS4-42202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shirshova, N. A1 - Bismarck, A. A1 - Greenhalgh, E.S. A1 - Johansson, P. A1 - Kalinka, Gerhard A1 - Marczewski, M.J. A1 - Shaffer, M.S.P. A1 - Wienrich, Malte T1 - Composition as a means to control morphology and properties of epoxy based dual-phase structural electrolytes N2 - Structural electrolytes were prepared using a fully formulated commercially available high performance epoxy resin (MTM57) and an ionic liquid based electrolyte: lithium bis(trifluoromethylsulfonyl)imide (LiTFSI) dissolved in 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMIM-TFSI). Through a systematic study, the composition of the formulations was found to have a greater effect than the curing temperature on the morphology and properties of the resulting structural electrolytes. The presence of lithium salt is essential to form a structurally homogeneous electrolyte. Bicontinuous morphologies containing continuous (coarse) epoxy networks surrounded by connected spherical epoxy nodules were obtained with different length scales upon varying the lithium salt concentration. Increasing the LiTFSI concentration improved the miscibility of MTM57 with the electrolyte and decreased the characteristic length scale of the resulting bicontinuous microstructure. The properties of the structural electrolytes correlated with the morphology, showing increased Young’s modulus and decreased ionic conductivity with increasing lithium salt concentration. The miscibility of the epoxy system with the electrolyte was also improved by substitution of EMIM-TFSI with an equal weight of an aprotic organic solvent, propylene carbonate (PC); however, the window of PC concentrations which resulted in structural electrolytes with bicontinuous microstructures was very narrow; at PC concentrations above 1 wt %, gel-like polymers with no permanent mesoporosity were obtained. KW - Functional composites KW - Mechanical properties KW - Elastic properties KW - Epoxy KW - Morphology KW - Electrolyte PY - 2014 DO - https://doi.org/10.1021/jp507952b SN - 1932-7447 SN - 1089-5639 VL - 118 IS - 49 SP - 28377 EP - 28387 PB - Soc. CY - Washington, DC AN - OPUS4-34565 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Qian, H. A1 - Kalinka, Gerhard A1 - Chan, K.L.A. A1 - Kazarian, S.G. A1 - Greenhalgh, E.S. A1 - Bismarck, A. A1 - Shaffer, M.S.P. T1 - Mapping local microstructure and mechanical performance around carbon nanotube grafted silica fibres: Methodologies for hierarchical composites N2 - The introduction of carbon nanotubes (CNTs) modifies bulk polymer properties, depending on intrinsic quality, dispersion, alignment, interfacial chemistry and mechanical properties of the nanofiller. These effects can be exploited to enhance the matrices of conventional microscale fibre-reinforced polymer composites, by using primary reinforcing fibres grafted with CNTs. This paper presents a methodology that combines atomic force microscopy, polarised Raman spectroscopy, and nanoindentation techniques, to study the distribution, alignment and orientation of CNTs in the vicinity of epoxy-embedded micrometre-scale silica fibres, as well as, the resulting local mechanical properties of the matrix. Raman maps of key features in the CNT spectra clearly show the CNT distribution and orientation, including a ‘parted’ morphology associated with long grafted CNTs. The hardness and indentation modulus of the epoxy matrix were improved locally by 28% and 24%, respectively, due to the reinforcing effects of CNTs. Moreover, a slower stress relaxation was observed in the epoxy region containing CNTs, which may be due to restricted molecular mobility of the matrix. The proposed methodology is likely to be relevant to further studies of nanocomposites and hierarchical composites. KW - Nanotubes KW - Silica fibres KW - Nano indentation KW - Mapping PY - 2011 DO - https://doi.org/10.1039/c1nr10497g SN - 2040-3364 SN - 2040-3372 VL - 3 IS - 11 SP - 4759 EP - 4767 PB - RSC Publ. CY - Cambridge AN - OPUS4-34718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Upper Critical Solution Temperature (UCST)-type thermoresponsive polymers from acrylamide-based monomers N2 - UCST-type thermoresponsive polymers that phase separate from solution upon cooling present a tremendous potential not only in aqueous media where they can be used in drug delivery, diagnostic and microfluidic applications, but also in water/alcohol mixtures, where they can be used for instance in sensing systems for alcohol-soluble drugs. However, only a few thermoresponsive polymers have been reported that present an UCST in a relevant temperature range and “green” solvents such as water or ethanol. In this context, acrylamide-based monomers can be very useful building blocks for designing novel UCST-type polymers because of their hydrophilic nature (with the right side chain) and propensity to form hydrogen bonds. We want to present our latest results on the copolymer poly(acrylamide-co-acrylonitrile) (P(AAm-co-AN)) that present a UCST in water as well as on two homopolymers based on an acrylamide derivative of 2,6-diaminopyridine, namely poly(N-(6-aminopyridin-2-yl)acrylamide) (PNAPAAm) and poly(N-(6-acetamidopyridin-2-yl)acrylamide) (PNAcAPAAm) that show UCST-type thermoresponsiveness in water/alcohol mixtures. Our focus for P(AAm-co-AN)) is its aggregation behaviour above and below its phase transition temperature as the size of thermoresponsive polymeric systems is of prime importance for biomedical applications (as size dependent processes take place in the body) and is linked to the optical properties of a material that matter in materials science. In the case of PNAPAAm and PNAcAPAAm, we focused on the co-solvency/co-non solvency effect on the phase transition temperature in water/alcohol mixture. Indeed, polymers with UCST behavior below 60°C in water/alcohol mixtures are extremely promising for the preparation of “smart” materials for sensing. T2 - Soft smart responsive materials workshop: Fundamentals and applications (SmartCECAM) CY - Mainz, Germany DA - 11.05.2017 KW - Thermoresponsive polymers KW - UCST-type polymers KW - poly(acrylamide-co-acrylonitrile) KW - 2,6-diaminopyridine-based polymers KW - co-solvency in water/acohol mixture PY - 2017 AN - OPUS4-40211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shirshova, N. A1 - Bismarck, A. A1 - Carreyette, S. A1 - Fontana, Q.P.V. A1 - Greenhalgh, E.S. A1 - Jacobsson, P. A1 - Johansson, P. A1 - Marczewski, M.J. A1 - Kalinka, Gerhard A1 - Kucernak, A.R.J. A1 - Scheers, J. A1 - Shaffer, M.S.P. A1 - Steinke, J.H.G. A1 - Wienrich, Malte T1 - Structural supercapacitor electrolytes based on bicontinuous ionic liquid-epoxy resin systems N2 - 'Structural electrolytes' retain the desirable mechanical characteristics of structural (epoxy) resins whilst introducing sufficient ionic conductivity to operate as electrolytes in electrochemical devices. Here, a series of ionic liquid–epoxy resin composites were prepared to identify the optimum system microstructure required to achieve a high level of multifunctionality. The ionic conductivity, mechanical properties, thermal stability and morphology of the cured epoxy based structural electrolytes were studied as a function of phase composition for three fully formulated high performance structural epoxy systems. At only 30 wt% of structural resin and 70 wt% of ionic liquid based electrolyte, stiff monolithic plaques with thicknesses of 2–3 mm were obtained with a room temperature ionic conductivity of 0.8 mS cm-1 and a Young's modulus of 0.2 GPa. This promising performance can be attributed to a long characteristic length scale spinodal microstructure, suggesting routes to further optimisation in the future. KW - Epoxy KW - Ionic liquid KW - Supercapacitor PY - 2013 DO - https://doi.org/10.1039/c3ta13163g SN - 2050-7496 SN - 2050-7488 VL - 1 IS - 48 SP - 15300 EP - 15309 PB - RSC CY - London [u.a.] AN - OPUS4-29735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Camp, N. V. A1 - Kalinka, Gerhard A1 - Bergeler, J. T1 - Light-cured polymer electrodes for non-invasive EEG recordings N2 - We invented the first non-metallic, self-adhesive and dry biosignalling electrode. The PEDOT polymer electrode changes its aggregate state and conductivity by a light curing procedure. The electrode can be applied as a gel underneath hair without shaving. With the aid of blue light, the electrode can be hardened within a few seconds at the desired location on the scalp. The cured polymer electrode is highly conductive and can be applied on a very small location. Unlike other EEG electrodes, our electrode does not lose conductivity upon drying. Furthermore, our electrode strongly bonds to Skin and does not require any additional adhesive. Short circuits due to an outflow of gel are prevented with this technique. Therefore, the PEDOT polymer electrode is extremely well suited for applications that, up to now, have been challenging, such as non-invasive EEG recordings from awake and freely moving animals, EEG recordings from preterm babies in the neonatal intensive care unit or long-term recordings in the case of sleep monitoring or epilepsy diagnostics. We addressed two technical questions in this work. First, is the EEG recorded with polymer electrodes comparable to a standard EEG? Second, is it possible to record full-band EEGs with our electrodes? KW - Light curing KW - Polymer KW - Electric conductivity PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-459803 UR - https://rdcu.be/7aPD DO - https://doi.org/10.1038/s41598-018-32304-6 SN - 2045-2322 VL - 8 IS - 14041 SP - 1 EP - 9 PB - Nature Publishing Group CY - London AN - OPUS4-45980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Greenhalgh, E.S. A1 - Ankersen, J. A1 - Asp, L. E. A1 - Bismarck, A. A1 - Fontana, Q.P.V. A1 - Houlle, M. A1 - Kalinka, Gerhard A1 - Kucernak, A. A1 - Mistry, M. A1 - Nguyen, S. A1 - Qian, H. A1 - Shaffer, M.S.P. A1 - Shirshova, N. A1 - Steinke, J.H.G. A1 - Wienrich, Malte T1 - Mechanical, electrical and microstructural characterisation of multifunctional structural power composites N2 - Multifunctional composites which can fulfil more than one role within a system have attracted considerable interest. This work focusses on structural supercapacitors which simultaneously carry mechanical load whilst storing/delivering electrical energy. Critical mechanical properties (in-plane shear and in-plane compression performance) of two monofunctional and four multifunctional materials were characterised, which gave an insight into the relationships between these properties, the microstructures and fracture processes. The reinforcements included baseline T300 fabric, which was then either grafted or sized with carbon nanotubes, whilst the baseline matrix was MTM57, which was blended with ionic liquid and lithium salt (two concentrations) to imbue multifunctionality. The resulting composites exhibited a high degree of matrix heterogeneity, with the ionic liquid phase preferentially forming at the fibres, resulting in poor matrix-dominated properties. However, fibre-dominated properties were not depressed. Thus, it was demonstrated that these materials can now offer weight savings over conventional monofunctional systems when under modest loading. KW - Carbon fibres KW - Functional composites KW - Mechanical properties KW - Elastic properties KW - Fractography PY - 2014 DO - https://doi.org/10.1177/0021998314554125 SN - 0021-9983 SN - 1530-793X SP - 1 EP - 12 PB - Sage CY - London AN - OPUS4-34567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Upper critical solution temperature (UCST)-type thermoresponsive polymers from acrylamide-based monomers N2 - UCST-type thermoresponsive polymers (i.e. that phase separate from solution upon cooling) present a tremendous potential not only in aqueous media where they can be used in drug delivery, diagnostic and microfluidic applications but also in water/alcohol mixtures, where they can be used for instance in sensing systems for alcohol-soluble drugs. However, only a few thermoresponsive polymers have been reported that present an UCST in a relevant temperature range and “green” solvents such as water or ethanol. In this context, acrylamide-based monomers can be very useful building blocks for designing novel non-ionic UCST-type polymers because of their hydrophilic nature (with the right side chain) and propensity to form hydrogen bonds. We will present our latest results on the UCST-type thermoresponsive behaviour of acrylamide- and 2,6-diaminopyridine-based homopolymers and copolymers in water or water/alcohol mixtures, and give some insights about the rational design of UCST polymers relying on H-bonding. T2 - Bioorganik 2017 – 26th Symposium "Bioorganic Chemistry" for young researchers CY - Berlin, Germany DA - 20.09.2017 KW - Thermoresponsive polymers KW - UCST polymers KW - 2,6-diaminopyridine KW - Acrylamide PY - 2017 AN - OPUS4-42007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barnefske, Lena A1 - Wachtendorf, Volker T1 - Self-healing silicone rubber for fluorescent partial discharge POF sensors in high-voltage cable accessories N2 - To avoid a catastrophic failure of insulation in high-voltage (HV) applications, a monitoring of partial discharges (PDs) is necessary. Fluorescently labelled polymer optical fibers (F-POF) offer an electrically passive method for PD detection in HV facilities. F-POFs could be embedded in HV cable accessories, which are usually made of silicone rubber. Herein they detect the light emitted by the PD and convert it into an electrical signal that can be monitored. Due to the difficult accessibility of HV cable accessories, a self-healing silicone rubber with prolonged service life after PD detection represents an attractive material design for HV accessories. With this contribution, we would like to present and discuss the possibilities of combining self-healing materials with POF-based sensors for PD detection in HV applications. T2 - 26th International Conference on Plastic Optical Fibres CY - Aveiro, Portugal DA - 13.09.2017 KW - Fluorescent polymer optical fibres KW - Partial discharge detection KW - High voltage cable accessories KW - Self-healing KW - Silicone rubber PY - 2017 SN - 978-989-97345-2-4 SP - paper 16, 1 EP - 5 AN - OPUS4-42510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Upper critical solution temperature (UCST)-type thermoresponsive polymers from hydrogen-bonding monomers N2 - UCST-type thermoresponsive polymers (i.e. that phase separate from solution upon cooling) present a tremendous potential not only in aqueous media where they can be used in drug delivery, diagnostic and microfluidic applications, but also in water/alcohol mixtures, where they can be used for instance in sensing systems for alcohol-soluble drugs. However, only a few thermoresponsive polymers have been reported that present an UCST in a relevant temperature range and “green” solvents such as water or ethanol. In this context, acrylamide-based monomers can be very useful building blocks for designing novel non-ionic UCST-type polymers because of their hydrophilic nature (with the appropriate side chain) and propensity to form hydrogen bonds. We will present our latest results on the UCST-type thermoresponsive behaviour of acrylamide- and 2,6-diaminopyridine-based homopolymers and copolymers in water or water/alcohol mixtures, and give some insights about the rational design of UCST polymers relying on H-bonding. T2 - Deutsche Physikalische Gesellschaft (DPG)-Frühjahrtagung 2018 CY - Berlin, Germany DA - 11.03.2018 KW - Thermoresponsive polymer KW - UCST-type polymer KW - H bonds KW - Diaminopyridine KW - Acrylamide PY - 2018 AN - OPUS4-44569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Upper Critical Solution Temperature (UCST)-type Thermoresponsive Polymers from Hydrogen-Bonding Monomers N2 - UCST-type thermoresponsive polymers (i.e. that phase separate from solution upon cooling) present a tremendous potential not only in aqueous media where they can be used in drug delivery, diagnostic and microfluidic applications,but also in water/alcohol mixtures, where they can be used for instance in sensing systems for alcohol-soluble drugs. However, only a few thermoresponsive polymers have been reported that present an UCST in a relevant temperature range and “green” solvents such as water or Ethanol. In this context, acrylamide-based monomers can be very useful building blocks for designing novel non-ionic UCST-type polymers because of their hydrophilic nature (with the appropriate side chain) and propensity to form hydrogen bonds. We will present our latest results on the UCST-type thermoresponsive behaviour of acrylamide- and/or 2,6-diaminopyridine-based homopolymers and copolymers in water or water/alcohol mixtures, and give some insights about the rational design of UCST polymers relying on H-bonding. T2 - Bordeaux Polymer Conference BPC 2018 CY - Bodeaux, France DA - 28.05.2018 KW - Acrylamide KW - Thermoresponsive polymer KW - UCST-type polymer KW - H-bonds KW - Diaminopyridine PY - 2018 AN - OPUS4-45155 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rabe, T. A1 - Kalinka, Gerhard A1 - Mieller, Björn T1 - Manufacturing and deformation behavior of alumina and zirconia helical springs at room temperature N2 - Ceramic helical springs with identical dimensions were produced by hard machining from alumina, alumina toughened zirconia (ATZ), and tetragonal zirconia polycrystals (TZP) stabilized with different oxides. According to the results of the spring constant determination under deformation rates of 3 mm/min, the deformation behavior of all ceramic springs obeys to Hook’s law. However, variation of the deformation rate, tests under constant load, and spring recovery behavior revealed differences in the deformation behavior of alumina, TZP, and ATZ springs. Alumina springs exhibited time-independent deformation in all tests. In contrast, anelastic deformation at room temperature was demonstrated in all springs containing TZP. This deformation is completely reversible over a period of several days. Anelastic behavior is particularly pronounced in Y-TZP springs, whereas Ce-TZP springs exhibit comparatively very low but still reliably detectable anelasticity. Oxygen vacancies in the TZP ceramic are considered the most likely explanation for the anelastic behavior of TZP springs at room temperature. KW - Alumina KW - Creep KW - Elastic properties KW - Zirconia PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571858 DO - https://doi.org/10.1111/jace.19085 SN - 0002-7820 SP - 1 EP - 14 PB - Wiley-Blackwell CY - Oxford [u.a.] AN - OPUS4-57185 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertin, Annabelle T1 - Building macromolecular mimetics of cell constituents N2 - One of the holy grails in chemistry is to reconstitute some of life’s functions with or within synthetic materials. In this contribution, we demonstrate that “simple” macromolecular architectures such as dendritic amphiphiles, Janus dendrimers, thermoresponsive and hybrid organic-inorganic (co)polymers enable to mimic some of the functions of proteins for biomineralization, natural bactericides, biological membranes or the stimuli-responsive cytoskeleton. T2 - Chemiedozententagung 2018 CY - Jena, Germany DA - 05.03.2018 KW - UCST-type polymers KW - Bioinspiration KW - Thermoresponsive polymers PY - 2018 AN - OPUS4-44442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -