TY - CONF A1 - Deland, Eric A1 - An, Biwen Annie A1 - Sobol, Oded A1 - Yao, J. A1 - Skovhus, T. L. A1 - Koerdt, Andrea T1 - Environmental conditions impact the corrosion layer composition of Methanogen induced microbiologically influenced corrosion (Mi-MIC) N2 - Microbiologically influenced corrosion (MIC) is a now well-known challenge and affects industry, society and infrastructure. For a long time, the impact of methanogen-induced MIC (Mi-MIC) was underestimated. This was mainly due to the rather low published corrosion rates and the presumed corrosion product siderite, which is not electrically conductive. In our laboratory, we were able to show that this trivialization or underestimation of Mi-MIC was due to the nature of the testing. The static systems used so far do not provide environmentally relevant information about the corrosion rate and the corrosion product, especially for methanogens To further illustrate the importance of the environment on the MIC process, we established a multiport flow column (MFC), to simulate the natural environment. With this method, and in contrast to published results using the static conditions, we obtained ten times higher corrosion rates. We analyzed the corrosion products with a combination of techniques, like ToF-SIMS, SEM-EDS and FIB-SEM, and found strong evidence that siderite is not the sole corrosion product of Mi-MIC. The corrosion layers contain phosphorus, oxygen, magnesium, calcium and iron and lacked on carbon-related species. It is hypothesized that methanogens may have influenced the nucleation process of siderite, converting bicarbonate into carbon dioxide for methanogenesis. This results in increased localized corrosion and reduced siderite formation. To verify and deepen our understanding of Mi-MIC, we are currently studying the influence of additional environmental parameters (e.g. pH, salinity, flow rate etc.) on Mi-MIC and the subsequent impacts on corrosion rates and the corrosion products. Overall, results of this study will expand the current understanding of MIC from both analytical and mechanistic points of view, thus aiding the development of different mitigation strategies for various industry sectors. T2 - Eurocorr 2021 CY - Online meeting DA - 20.09.2021 KW - Methanogen-induced microbiologically influenced corrosion KW - Carbon steel KW - SEM-EDS KW - Modelling studies PY - 2021 AN - OPUS4-54043 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deland, Eric A1 - An, Biwen Annie A1 - Sobol, Oded A1 - Yao, J. A1 - Skovhus, T. L. A1 - Koerdt, Andrea T1 - Environmental conditions affect the corrosion product composition of Methanogen induced microbiologically influenced corrosion (Mi-MIC) N2 - Corrosion is a very expensive and serious problem in the different industry sectors, eg. Petroleum-, On- and off-shore, infrastructure. It is estimated that 20% of all corrosion damage is caused by microorganisms or microbiologically influenced corrosion (MIC). Several microorganisms are known to cause corrosion, including sulfate-reducing bacteria, nitrate-reducing bacteria, methanogens etc. For several years, methanogens were regarded as a mild corroder (~0.065 mm/yr), largely due to a lack of detailed investigation on the corrosion mechanism under real-environment simulated conditions. Resulting in the common belief that siderite, a non-conductive compound, is the sole corrosion product (CP) of methanogen-induced MIC (Mi-MIC). To simulate natural environmental conditions, we developed and introduced the multiport flow column system (MFC), a multi-sectional corrosion flow-cell. Using the MFC, we obtained ten times higher corrosion rates than previously reported. With a combination of several analytical techniques, such as ToF-SIMS, SEM-EDS and FIB-SEM, we found strong indication that siderite is not the sole corrosion product of Mi-MIC. The corrosion layers contained phosphorus, oxygen, magnesium, calcium and iron. The differences in the CP between static and dynamic environments demonstrated the impact of testing procedures on the corrosive potential of methanogens. To further verify and deepen our understanding of Mi-MIC, we are currently studying the influence of additional environmental parameters (e.g. pH, salinity, flow rate) on Mi-MIC. Overall, results of this study will expand the current understanding of MIC from both analytical and mechanistic points of view, thus aiding the development of different mitigation strategies for various industry sectors. T2 - ISMOS-8 CY - Online meeting DA - 08.06.2021 KW - Methanogen-induced microbiologically influenced corrosion KW - Carbon steel KW - ToF-SIMS KW - Modelling studies PY - 2021 AN - OPUS4-54041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deland, Eric A1 - Kleinbub, Sherin A1 - An, Biwen Annie A1 - Sobol, Oded A1 - Yao, J. A1 - Skovhus, T. L. A1 - Koerdt, Andrea T1 - Is Methanogen-induced microbiologically influenced corrosion (Mi-MIC) underestimated? N2 - The role of methanogens in microbiologically influenced corrosion (Mi-MIC) is often neglected, due to 1) low reported corrosion rates and 2) the suspected corrosion product siderite, which is electrically non-conductive. Typically, MIC corrosion studies are carried out using batch cultures, which did not represent the dynamic conditions, i.e. pipeline and provide insufficient information on the overall corrosion potential. We established a unique approach, a multiport flow column (MFC), to simulate pipeline conditions and obtained 10-times higher corrosion rates than previously published. Our result showed that testing procedures have a large impact on the corrosive potential of methanogens. We found strong indications with a combination of ToF-SIMS, SEM-EDS and FIB-SEM analyses that siderite is not the sole corrosion product. The corrosion layers contain phosphorus, oxygen, magnesium, calcium and iron. To verify and deepen our understanding of Mi-MIC, we are currently studying the influence of other environmental parameters (e.g. pH) on Mi-MIC. T2 - VAAM 2021 CY - Online meeting DA - 18.03.2021 KW - Methanogen-induced microbiologically influenced corrosion KW - Carbon steel KW - MIC Island PY - 2021 AN - OPUS4-54042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -