TY - CONF A1 - Weltschev, Margit T1 - Compatibility of polymers with aged heating oil containing 10 % and 20 % biodiesel under static conditions N2 - Biodiesel is viewed as a major source of energy. In areas such as the European Un-ion, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies. Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil. The polarity of biodiesel increases its solvency and facilitates permeation and extrac-tion. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers. Exposure tests to determine the resistance of polymers frequently used for compo-nents in middle distillate facilities, such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and a blend of heating oil and 20 % biodiesel (B20) were al-ready performed. The objective of this research was to determine the resistance of these polymers in 8-year aged heating oil blend B10 and 1-year aged blend B20 at 40 °C. Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was deter-mined for the evaluation of the compatibility. A significant reduction in Shore hardness was determined after exposure of ACM and PUR test specimens in 1-year aged B20. The tensile strength of PUR test specimens in 1-year aged B20 was reduced by more than 50 %, and the breaking elongation by more than 30 %. A decrease in breaking elongation was measured for POM test specimens after ex-posure to 1-year aged B20 by 25 % (limited resistance). 8-year aged B10 had a stronger effect than 1-year aged B20 on the polymers. ACM test specimens were softened by B10 resulting in a drop of Shore hardness by over 20 %. B10 reduced tensile strength and breaking elongation of PUR test specimens by over 50 %. In contrast, the breaking elongation of POM was increased by over 270 %. It can be concluded that the polymers HNBR, FKM, PA6, PE and PVC are resistant in 1-year aged B20 whereas ACM and POM are limited resistant. PUR is not re-sistant. HNBR, FKM, PA6, PE and PVC are resistant in 8-year aged B10, whereas PUR and POM are not resistant, and ACM just limited resistant. T2 - EUROCORR 2020 CY - Online meeting DA - 07.09.2020 KW - Aged heating oil with 10% and 20% biodiesel KW - Resistance of polymers KW - Tensile properties KW - Shore hardness PY - 2020 AN - OPUS4-51240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Analytik - Daten, Formeln, Übungsaufgaben N2 - Seit seiner erstmaligen Veröffentlichung im Jahre 1894 als „Logarithmische Rechentafeln für Chemiker“ und ab 1982 als „Rechentafeln für die chemische Analyse“ begleitet der „Küster‐Thiel“ Generationen nicht nur von Laborantinnen und Laboranten sowie Studierende hilfreich bei der analytischen Arbeit. Mit der 108. Auflage änderte sich 2016 der Titel dieses in der „Studium“‐Reihe des De Gruyter Verlages herausgegebenen Standardwerkes ein weiteres Mal. Die 109. Auflage des Klassikers der chemischen Analytik‐Literatur setzt die Tradition fort, mit zahlreichen anschaulichen Erklärungen, Beispiele und Rechnungen Chemikern, Physikern und Ingenieurswissenschaftlern an Universitäten und Fachhochschulen; Auszubildenden und Laboranten ein übersichtliches und aktuelles Arbeitsmittel für den analytischen Alltag zur Verfügung zu stellen. Nutzern früherer Ausgaben wird der Umstieg auf die neue Ausgabe empfohlen, damit auch sie auf dem neuesten Stand arbeiten können. KW - Analyse KW - Labor KW - Formeln KW - Laborarbeit PY - 2020 DO - https://doi.org/10.1002/maco.202070106 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 10 SP - 2 EP - 3 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51415 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Materialkunde der Nichteisenmetalle und ‐legierungen N2 - Die Werkstoffklasse der Nichteisenmetalle gewinnt wegen ihrer unzähligen Anwendungsmöglichkeiten nicht nur im Maschinen‐ und Anlagenbau eine immer größere technische und wirtschaftliche Bedeutung, sodass es unabdingbar ist, insbesondere Studierenden der Material‐ und Werkstoffwissenschaften und des Maschinenbaus, den aktuellen Wissensstand auf diesem Gebiet zu vermitteln. Mit dieser Neuerscheinung veröffentlicht der Wiley‐VCH‐Verlag ein solches Lehrbuch. Kompakt und übersichtlich machen die beiden Autoren den Leser in 10 Kapiteln auf verständliche Art mit dieser Thematik vertraut. Dabei kommt ihnen ihre durch langjährige Lehrtätigkeit erworbene didaktische Erfahrung sehr zugute. Alles in allem bietet dieses Lehrbuch durch seinen von den Natur‐, über Material‐ zu Ingenieurwissenschaften weitgespannten Bogen einen interessanten und übersichtlichen Einstieg in die Welt der am häufigsten verwendeten Nichteisenmetalle, wobei es keinen Anspruch auf Vollständigkeit erhebt. KW - Werkstoffprüfung KW - Legierung KW - Korrosion PY - 2020 DO - https://doi.org/10.1002/maco.202070086 SN - 1521-4176 VL - 71 IS - 8 SP - 4 PB - Wiley‐VCH CY - Weinheim AN - OPUS4-51073 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Deposition of Brine Components on Materials in Geothermal Conditions T1 - ОСАЖДЕНИЕ КОМПОНЕНТОВ ГЕОТЕРМИЧЕСКИХ ВОД НА МАТЕРИАЛЫ В ГЕОТЕРМАЛЬНЫХ УСЛОВИЯХ N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment. This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin. The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water. Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation. N2 - Поскольку геотермальные скважины являются реальным источником энергии для замены поставок ископаемого топлива, было разработано множество технологий для использования преимуществ геотермальной энергии. Тем не менее, условия эксплуатации на геотермальных установках во многих случаях являются экстремальными с точки зрения коррозии из-за химического состава гидротермальных жидкостей и температур. Таким образом, выбор материалов на основе предварительной квалификации имеет важное значение для обеспечения безопасной и надежной работы геотермальных объектов. Во время работы исследовательской установки в Грос Шёнебек (Groß Schönebeck) в скважине было обнаружено воздействие меди и свинца. Необходимо изучить возникшие механизмы и меры для предотвращения депозиции или образования коррозии, а также потенциальное влияние таких осаждений на коррозионную стойкость металлов, используемых для оборудования. Этот доклад посвящен оценке коррозионного поведения углеродистой стали и коррозионно-стойких сплавов в геотермальной воде, содержащей медь и / или свинец, моделирующей условия в Северогерманском бассейне (North German basin). Представлено поведение этих металлических материалов в геотермальной воде, полученной путем электрохимических измерений и испытаний на воздействие. В то время как углеродистая сталь демонстрирует коррозию и отложения, высоколегированный материал демонстрирует более высокую стойкость в соленой геотермальной воде. На основании этих результатов пригодность исследуемого коррозионно-стойкого сплава дана для использования в данных условиях, тогда как углеродистая сталь создает трудности из-за ее восприимчивости к депозиции солей меди и свинца. T2 - ХV International Conference Problems of Corrosion and Corrosion Protection of Materials “CORROSION-2020” CY - Online meeting DA - 15.10.2020 KW - Copper KW - Lead KW - Corrosion KW - Steel KW - Geothermal PY - 2020 UR - http://www.ipm.lviv.ua/corrosion2020/ AN - OPUS4-51438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Loose, Florian T1 - End-of-Life Carbon Fiber Reinforced Polymers in Steelmaking - Accessing a C-Rich Residue Stream as Alternative Reducing Agent N2 - As one of the most energy and carbon consuming industries, steelmakers have an intrinsic interest in the development of technologies, reducing their carbon footprint as well as their carbon input. Besides generating new feedstocks from biomass or waste polymers, the valorization of carbon fiber reinforced polymer (CFRP) waste streams seems to be extremely promising based on the high carbon content of carbon fibers (CF), chars from CFRP and even unprocessed CFRP waste of >92%, 98% and 79%, respectively. Although, reduction of environmental impact from those high-performance materials was achieved by the development of smart recycling solutions, the continuous truncation by mechanical treatment of CF over multiple cycles, analogous to paper fibers, and the large global CFRP waste stream of 62 kt/a demand for a sustainable management of end-of-life (EOL) CFRP. Recently it was demonstrated that CF can be used safely as reductant in pyrometallurgical processes in a downhole electric furnace without significant WHO fiber emission. Therefore we anticipate a huge potential of CF based materials as sustainable reductant for steelmaking in an electric arc furnace (EAF). To facilitate the applicability of EOL CFRP in steelmaking, we investigated the interaction between CF based materials and liquid metal phases, appearing during the process, on different scales. Particularly, we examined the reactivity, wettability and dissolution behavior of CF and CFRP concerning liquid slag and steel. The presented results indicate that understanding the impact of the microstructure of CF on their behavior is crucial for their application in EAF steelmaking without risking potential hazards by WHO fiber emission. Besides the detailed elucidation of structure reactivity relationships of CF, the broader impact on circular economy will be presented. T2 - ESTEP Workshop Resi4Future: Residue valorization in iron and steel industry - sustainable solutions for a cleaner and more competitive future Europe CY - Online meeting DA - 20.11.2020 KW - Carbon Fibers KW - Steelmaking KW - Electric Arc Furnace KW - Secondary Recources KW - Sustainability PY - 2020 AN - OPUS4-51613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -