TY - THES A1 - Ecker, Melanie T1 - Development, Characterization and Durability of Switchable Information Carriers based on Shape Memory Polymers N2 - The aim of this thesis was the development of switchable information carriers based on shape memory polymers (SMPs) and the investigation of their durability. Deployed as a new kind of security label, such technology may be an effective tool to prevent counterfeiting and product piracy. Thermoplastic as well as thermoset SMPs turned out to be applicable as a specific substrate for the fabrication of switchable information carriers. In particular, a physically cross-linked and semi-crystalline poly(ester urethane) (PEU), and a chemically cross-linked epoxy-based polymer were investigated. Both SMPs were able to undergo distinct changes in shape upon triggering, which is commonly known as the shape memory effect (SME). A key step for the fabrication of switchable information carriers was the development of a suitable technique for a surface-specific coloring of the polymeric base material. In particular, it was necessary to have a thin coat of paint in order to assure sufficient surface contrasts within the subsequently laser-engraved barcodes (e.g. quick response (QR) codes). In detail, coloring was conducted by diffusion of staining solutions, based on organic dyes, into the polymeric matrix. As a result of properly selected exposure times, homogenous layers of paint having thicknesses of about 100 μm, could be produced. In order to obtain room temperature stable, temporary shapes with non-decipherable code information, various programming procedures were applied to the information carriers. These were either based on tensile or on compressive deformation. For instance, when using plane steel plates in the course of compressive deformation, code areas were randomly distorted. By contrast, selective distortions could be achieved using a steel ball type indenter. However, the triggering of the SME resulted in almost complete shape recoveries. As a result, the information carriers could reliably be switched back to readable states. Before the developed information carriers can be brought onto the market, it is important to evaluate their durability against various environmental impacts. Artificial weathering was conducted exemplarily on blue and black colored QR code carriers based on PEU. Various scenarios were selected: exposure to UVA irradiation and aging in aqueous solution. In both cases, the durability was investigated at temperatures below and above the switching temperature of the employed SMP. It turned out, that the limiting factor for the usage of switchable information carriers was a lack of contrast and thus was dye-related. In the case of UV irradiation, the color of the dyes started fading, culminating in unreadable QR codes. For hydrolytic degradation, the non-colored code regions were stained in the course of aging. This originates from the fact that the organic dyes used for coloring were soluble in water. As a consequence, they were able to diffuse easily in and out of the swollen polymeric matrix. For both scenarios, aging at elevated temperature caused acceleration of the observed effects. However, the shape memory properties of the PEU were only slightly influenced by the applied aging scenarios. Next, an additional thermo-responsive security feature was added to the information carriers. Therefore, thermochromic pigments (T-PIGs) were embedded into a PEU matrix. However, in contrast to the organic dyes, the size of the thermochromics microcapsules was too large to diffuse into the polymeric matrix. Thus, another procedure for a surface-specific coloring of the PEU was developed. This mainly included the preparation of a PEU-paste doped with T-PIG by solution mixing. The thermochromic paste was deposited by means of a solvent casting technique as thin layer atop the PEU plaque. After solvent evaporation, tightly connected PEU/PEU-T-PIG laminates were obtained. Beyond that, the layer thickness was adjustable by using a doctor blade for the paste deposition. Subsequent laser ablation finalized the QR code carriers. These were readable at room temperature, but unreadable above the color switching temperature of the employed T-PIGs due to a lack of contrast. Hence, the obtained multifunctional information carriers were characterized by distinct shape memory properties and tunable color switching performances. Furthermore, the combination of several T-PIGs having different colors and switching temperatures resulted in surfaces with multiple and unique temperature-dependent changes in color. Besides that, information carriers with temporarily concealed information could be obtained by covering the QR code with an additional layer doped with T-PIG. N2 - Ziel der Arbeit war es, schaltbare Informationsträger aus Formgedächtnispolymer (FGP) zu entwickeln, und diese auf ihre Beständigkeit gegenüber unterschiedlichen Umwelteinflüssen zu untersuchen. Eingesetzt als neuartige Etiketten könnten diese zur fälschungssicheren Kennzeichnung von Waren verwendet werden. Sowohl thermoplastische als auch duroplastische FGPs waren geeignete Ausgangsmaterialien für solche Informationsträger. Im Speziellen wurde sowohl ein physikalisch quervernetztes, semikristallines Poly(ester urethan) (PEU), als auch ein chemisch quervernetztes, amorphes FGP auf Epoxidbasis näher untersucht. Ein wichtiger Schritt für die Entwicklung von schaltbaren Informationsträgern aus FGP war die Entwicklung eines Färberverfahrens, bei dem das Polymer nur oberflächennah eingefärbt wird. So konnten ausreichend hohe Kontraste in den anschließend mittels Lasergravur eingebrachten Barcodes (z.B. QR engl. quick response Codes) erreicht werden. Die Färbung der Polymeroberflächen durch Diffusion von organischen Färbelösungen in die Polymermatrix stellte sich als probate Methode heraus. Dabei konnte die Eindringtiefe der Farbstoffe durch die Einwirkzeit auf etwa 100 μm eingestellt werden. Um die Informationsträger in stabile, temporäre Formen mit unlesbarer Information zu überführen, wurden unterschiedliche thermomechanische Programmierungsmethoden angewendet. Sowohl Druck- als auch Zugverformung stellten sich hierfür als geeignet heraus. In beiden Fällen waren die Informationen im programmierten Zustand aufgrund zu großer Verzerrungen der QR Codes unlesbar. Durch den Einsatz von konfigurierbaren Stempelwerkzeugen während der Druckverformung war es darüber hinaus möglich, selektive Verformung der Oberfläche zu erreichen. Nach dem Auslösen des Formgedächtniseffektes kehrten die Etiketten nahezu in ihre ursprüngliche Form zurück, sodass die Information dann in jedem Fall wieder lesbar war. Um die Haltbarkeit der neu entwickelten Informationsträger gegenüber Umwelteinflüssen besser beurteilen zu können, wurden gefärbte Etiketten aus PEU künstlich bewittert. Hierfür wurden zwei Alterungsszenarien gewählt: die Degradation durch UVA-Strahlung und die Beständigkeit in wässrigem Medium. In beiden Fällen wurde die Bewitterung unterhalb und oberhalb der Schalttemperatur des Polymers durchgeführt. Die UV-Alterung führte zum Ausbleichen der Farben und somit zum Verlust der Lesbarkeit durch die Abnahme des QR Code Kontrastes. Während der Alterung in Wasser wurden die anfangs ungefärbten Domänen innerhalb des QR Codes nach und nach gefärbt, was ebenfalls zu einem Kontrastverlust führte. Das rührte daher, dass die organischen Farbstoffe wasserlöslich waren und somit in das gequollene Polymer hinein- und hinausdiffundieren konnten. Lagerung bei erhöhter Temperatur führte in beiden Fällen zu einer Beschleunigung der beobachteten Phänomene. Im Gegensatz dazu wurde während der untersuchten Alterungszenarien die Formgedächtnis-Funktionalität des Polymers kaum beeinflusst. Anschließend wurden die Informationsträger mit einem weiteren thermoresponsiven Sicherheitsmerkmal kombiniert. Die hierfür verwendeten thermochromen Pigmente (T-PIGs) waren im Vergleich zu den vorher verwendeten Farbstoffen jedoch zu groß, um in die Polymermatrix hineinzudiffundieren. Daher wurde eine weitere Methode zur oberflächenspezifischen Einfärbung von Polymeren entwickelt. Hierzu wurde zunächst eine viskose PEU-Lösung hergestellt, die im Anschluss mit den T-PIGs vermengt wurde. Die so erhaltene Paste wurde mittels der sogenannten „solvent cast“ Technik als dünner Film auf die Polymeroberfläche aufgebracht. Dabei konnte die Schichtdicke durch den Einsatz eines „doctor blades“ eingestellt werden. Nach dem vollständigen Abdampfen des Lösungsmittels wurden fest verbundene PEU/PEU-T-PIG Laminate erhalten. Die anschließende Lasergravur führte zu Informationsträgern, die bei Raumtemperatur lesbar waren. Oberhalb der Farbumschlagstemperatur der eingesetzten T-PIGs wurden diese jedoch aufgrund von Kontrastverlusten unlesbar. Die so erhaltenen multifunktionalen Informationsträger waren demzufolge neben ihren Formgedächtniseigenschaften durch einstellbare, temperaturabhängige Farbänderungen charakterisiert. Darüber hinaus war es möglich, Informationsträger mit mehreren Farbumschlägen zu erhalten, indem T-PIGs mit unterschiedlichen Farben und Farbumschlagstemperaturen während der Herstellung eingesetzt wurden. In einem weiteren Szenario wurden Informationsträger mit einer Schicht aus thermochromer Paste überdeckt. Als Folge war der Barcode bei Raumtemperatur unter dieser Schicht verborgen und wurde erst beim Erwärmen oberhalb der Schalttemperatur sichtbar und lesbar. T3 - BAM Dissertationsreihe - 132 KW - durability KW - smart materials KW - Shape memory polymers KW - QR codes KW - thermochromism PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5086 VL - 132 SP - 1 EP - 202 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR T1 - Amts- und Mitteilungsblatt, Band 45, Heft 2 T3 - Amts- und Mitteilungsblatt der BAM - 2/2015 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5091 SN - 0340-7551 VL - 45 IS - 2 SP - 1 EP - 65 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-509 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Seiffert, Franz T1 - Charakterisierung von Gesteinsbewuchs und -verwitterung durch einen Modellbiofilm N2 - Natürliche Gesteinsformationen und von Menschen aus Gesteinsmaterial erschaffene Gebäude oder Monumente werden bei genügend langer Inkubation von zahlreichen Mikroorganismen besiedelt, welche komplexe Ökosysteme bilden. Dies führt oft zu Verfärbungen der Gesteinsoberflächen durch Pigmente der Mikroorganismen. Zudem können die Organismen das Gestein angreifen und zusammen mit abiotischen Faktoren eine Auflösung herbeiführen, was von essenzieller Bedeutung für die Bildung von Böden und gleichzeitig kritisch für die Erhaltung von Kulturgütern ist. Ein profundes Verständnis der Primärbesiedlung auf Gesteinen ist eine Voraussetzung, um Prozesse der Sukzession und der Gesteinsverwitterung besser nachvollziehen und modellieren zu können. Mischkulturen, die aus dem phototrophen Cyanobakterium Nostoc punctiforme ATCC 29133 und dem mikrokolonialen Ascomycet Knufia petricola CBS 726.95 bestanden, wurden als Modell für die ersten Schritte der Gesteinsbesiedlung in Form von Biofilmen und hinsichtlich des biologischen Einflusses auf die Gesteinsverwitterung hin getestet. Dazu wurden unterschiedliche Gesteine als Substrate angeboten, unter verschiedenen Kultivierungs- und Witterungsbedingungen mit den Mischkulturen inkubiert und die sich bildenden Biofilme bzgl. ihrer Morphologie und Abundanz hin analysiert. Es zeigte sich, dass das Wachstum der Biofilme deutlich von den verwendeten Gesteinen und Witterungsbedingungen abhing und die Anordnung und Morphologie der Zellen und der aus diesen ausgeschiedenen polymeren Substanzen innerhalb der Biofilme sich je nach eingesetztem Gesteinssubstrat deutlich unterschieden. Der biologische Einfluss auf die Verwitterung von Gestein wurde in einem Durchfluss-System an einem Granit und in Batch-Kulturen an Calcit, Forsterit und Olivin getestet, indem nach Inkubation für 45-180 d in An- und Abwesenheit der Mikroorganismen die in der Flüssigphase angereicherten Elemente und die chemischen Veränderungen in der Mineralphase vergleichend gemessen wurden. Dabei zeigte sich, dass der Biofilm die Auflösung von Calcium, Natrium, Magnesium und Mangan aus Granit sowie von Magnesium aus Forsterit und Olivin verstärkte. Einzelkulturen von K. petricola und Mischkulturen führten zu verstärkter Magnesiumauflösung, Einzelkulturen von N. punctiforme zeigten die gleichen Effekte wie abiotische Kontrollen. Beide Mikroorganismen wuchsen deutlich besser in Mischkulturen, sodass ein indirekter biotischer Effekt auf die Mineralauflösung von N. punctiforme durch die Verstärkung des Wachstums von K. petricola innerhalb einer mutualistischen Gemeinschaft als plausibel erscheint. Der Mechanismus der biotisch induziert verstärkten Gesteinsverwitterung konnte aufgrund der hier vorliegenden Ergebnisse nicht eruiert werden. Die verwendeten Mischkulturen aus K. petricola und N. punctiforme konnten als nützliches Modell zur Untersuchung von Gesteinsbewuchs und –verwitterung etabliert werden. N2 - Natural rock formations and buildings or monuments constructed by mankind with rock materials are colonised by various microorganisms within complex ecosystems if incubated for sufficient periods of time. This often causes discolouration of rock surfaces by microbial pigments. Microorganisms can also attack the rocks and give rise to their decomposition in combination with abiotic factors being of essential importance for soil formation and critical to the conservation of cultural heritage. For the comprehension and modellizing of processes like succession and rock weathering, a profound understanding of primary colonisation is required. Mixed cultures consisting of the phototrophic cyanobacterium Nostoc punctiforme ATCC 29133 and the microcolonial ascomycete Knufia petricola CBS 726.95 were used as a model to study the first steps of rock colonisation by biofilms and the biotic influence on rock weathering. For that purpose different rocks were offered as substrates, incubation with mixed cultures was done under differing cultivation and atmospheric conditions and forming biofilms were analysed for their morphology and abundance. Results indicate that growth of the biofilms depended precisely on the offered rock substrates and atmospheric conditions. Arrangement and morphology of cells and their excreted polymeric substances within biofilms differed depending on the rock substrate. The biological influence on rock weathering was examined in a percolation system for granite and in batch cultures for calcite, forsterite and olivine. After incubation for 45-180 d with and without microorganisms accumulated elements within the liquid phase and chemical changes within the Mineral phase were measured comparatively. Results indicate that dissolution of calcium, sodium, magnesium and manganese from granite and magnesium from forsterite and olivine were enhanced in the presence of the biofilm. For some mineral experiments, biotic effects of mixed and single cultures were distinguished. K. petricola single cultures and mixed cultures enhanced magnesium dissolution, N. punctiforme single cultures showed effects comparable to the abiotic controls. Both microorganisms grew better within mixed cultures, suggesting an indirect biotic effect of N. punctiforme for mineral dissolution, acting as growth enhancing factor for K. petricola within mutualistic biofilms. The mechanism of biotically increased rock weathering could not be determined by the here presented results. Mixed cultures of K. petricola and N. punctiforme could be established as a useful model to study colonisation and weathering of rocks. T3 - BAM Dissertationsreihe - 135 KW - Gesteinsbewuchs KW - Mineralverwitterung KW - Granitverwitterung KW - Modellbiofilm KW - Gesteinsbiofilm PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5118 VL - 135 SP - 1 EP - 191 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-511 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lausch, Thomas T1 - Zum Einfluss der Wärmeführung auf die Rissbildung beim Spannungsarmglühen dickwandiger Bauteile aus 13CrMoV9-10 N2 - Wirtschaftliche und ökologische Aspekte führten in den letzten Jahren zu deutlich gesteigerten Anforderungen an die Effizienz und die Flexibilität petrochemischer Anlagen. Die heutzutage geforderten Prozesstemperaturen und -drücke lassen sich nur durch den Einsatz neuer warmfester Stahlgüten erreichen. Der mit Vanadium modifizierte Stahl 13CrMoV9-10 weist eine bessere Kriech und Druckwasserstoffbeständigkeit auf und wird seit Mitte der 90er Jahre im petrochemischen Reaktorbau eingesetzt. Aufgrund der niedrigen Zähigkeit und hohen Festigkeit des Schweißgutes im geschweißten, nicht spannungsarm geglühten Zustand sowie einer erhöhten Sensitivität gegenüber Spannungsrelaxationsrissen bedarf dieser Stahl allerdings einer äußerst sorgfältigen schweißtechnischen Verarbeitung. Bisherige Untersuchungen zur Rissentstehung in warmfesten Stählen konzentrierten sich vorrangig auf thermische und metallurgische Einflussfaktoren, bieten jedoch nur wenige Erkenntnisse zum Einfluss des Schweißprozesses auf die Rissbildung beim Spannungsarmglühen unter Berücksichtigung realitätsnaher Fertigungsbedingungen. Im ersten Teil wurde zunächst der Einfluss der Wärmeführung auf die mechanischen Eigenschaften anhand von frei schrumpfenden Laborproben untersucht. Während sich die Wärmeführung wesentlich auf die Schweißnahtstruktur auswirkte, war ein signifikanter Effekt auf die mechanischen Eigenschaften nicht nachweisbar. Auch traten infolge der Wärmenachbehandlung der frei schrumpfend geschweißten Proben keine Spannungsrelaxationsrisse auf. Der zweite Teil umfasste die realitätsnahe Abbildung der Fertigungsbedingungen im petrochemischen Reaktorbau. Zu diesem Zweck wurden die konstruktiven Randbedingungen während des Vorwärmens, Schweißens, des Wasserstoffarmglühens und der abschließenden Wärmenachbehandlung realitätsnah in einer speziellen 3-D-Prüfanlage zur Simulation von Bauteilschweißungen abgebildet. Unter konstruktiver Schrumpfbehinderung gelang der Nachweis der unterschiedlichen Wirkung von Vorwärm- / Zwischenlagentemperatur und Streckenenergie auf die resultierenden Kräfte, Momente und Spannungen. Die Gesamtreaktionsspannung nach dem Schweißen wurde innerhalb des untersuchten Parameterfeldes maßgeblich durch die Streckenenergie beeinflusst. Ein möglichst geringer Gesamtwärmeeintrag hat die niedrigste Bauteilbeanspruchung zur Folge. Während der Wärmenachbehandlung kam es in allen Versuchen zu Spannungsrelaxationsrissen. Deren kumulierte Länge korrelierte mit den ermittelten schweißbedingten Reaktionsspannungen. Die Detektion der Risse während der Wärmenachbehandlung im Bauteilversuch erfolgte erstmalig in-situ mittels Schallemissionsanalyse. Die Rissinitiierung fand nachweislich im Temperaturbereich von 300 °C bis 500 °C statt. Die Reaktionsspannungen nach der Wärmenachbehandlung lagen unabhängig von der Ausgangsbelastung auf einem vergleichbaren Niveau. Die Zähigkeit der Schweißverbindung nahm klar gegenüber den frei schrumpfend geschweißten Proben ab. Mittels REM- und TEM-Analysen an vergleichbaren belasteten und unbelasteten Proben wurde eine beschleunigte Alterung, durch das frühzeitige Ausscheiden von Sonderkarbiden während der Wärmenachbehandlung unter definierter Einspannung (d. h. unter Belastung), nachgewiesen. Die verstärkte Korngrenzensegregation korrelierte mit der signifikanten Abnahme der Kerbschlagarbeit der unter Einspannung geschweißten Proben. N2 - Over the past years economic and environmental considerations have led to a markedly increased demand for efficiency and flexibility in petrochemical plants. The operational temperatures and pressures required today can only be achieved by using new heat resistant grades of steel. The modified 13CrMoV9-10 vanadium steel shows a better resistance to creep and compressed hydrogen and has been in use for the construction of petrochemical reactors since the mid-1990s. However, processing of this type of steel requires extreme care during the welding procedure due to its low toughness and high strength in the welded state when not post weld heat treated, in Addition to its increased susceptibility to cracking during stress relaxation. Previous research into crack formation in heat resistant steel has largely focussed on thermal and metallurgical factors; however, little knowledge has been gathered regarding the influence of the welding procedure on crack formation during post weld heat treatment taking into account real-life manufacturing conditions. In the first part, the influence of heat control on the mechanical properties has been investigated using freely shrinking laboratory samples. Whereas heat control was clearly shown to have an impact on the structure of the weld, it had no significant effect on the mechanical properties. Furthermore, there was no stress relief cracking resulting from post weld heat treatment of the samples welded under conditions allowing free shrinkage. The second part concerns the reproduction of real-life manufacturing conditions prevailing during the construction of petrochemical reactors. To this end, the basic constructional conditions during pre-heating, welding, dehydrogenation heat treatment, and the final post weld heat treatment were realistically simulated in a special 3-D testing facility designed to prevent shrinkage during welding and subsequent heat treatments. Under conditions restricting shrinkage it was possible to show the different effects of pre-heating and interpass temperatures and heat input on the resulting forces, momentums and stresses. Within the range of parameters examined the total reaction stress applied after welding depended largely on the heat input. The lowest possible total heat input results in the lowest stress load on the building parts. In all experiments stress relief cracks were formed during post weld heat treatment. The summary length of the cracks correlated with the measured reaction stresses due to welding. In the test, detection of the cracks during post weld heat Treatment was for the first time performed in-situ using acoustic emission analysis. Crack formation was thus shown to start in the temperature range between 300 °C and 500 °C. The reaction stresses after post weld heat treatment reached a similar level regardless of the load initially applied. The toughness of the weld significantly decreased in comparison with the samples welded in conditions allowing free shrinkage. REM and TEM analyses of comparable samples with and without load showed accelerated aging as a result of early precipitation of special carbides during post weld heat treatment in defined clamping conditions. The increase in grain boundary segregation correlated with a significant decrease of the notched bar impact value of samples welded when clamped in. T3 - BAM Dissertationsreihe - 134 KW - PWHT KW - Spannungsarmglühen KW - Schrumpfbehinderung KW - Bauteilversuch KW - Stress Relief Cracking KW - 13CrMoV9-10 KW - Schweißen KW - Spannungsrelaxationsrisse PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5129 VL - 134 SP - 1 EP - 252 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-512 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Bleul, Regina T1 - Herstellung, Charakterisierung und Funktionalisierung polymerer Nanopartikel und Untersuchung der Wechselwirkungen mit biologischen Systemen N2 - Die Nanomedizin beschäftigt sich unter anderen mit der Frage, wie sich die Behandlung gefährlicher Krankheiten effizienter und sicherer gestalten lässt, deren konventionelle Therapie oftmals mit schweren Nebenwirkungen einhergeht. Die Vision ist, ein theranostisches Wirkstoffträgersystem zu schaffen, das seinen therapeutischen Cargo sicher an den Wirkort transportiert, dort freisetzt und gleichzeitig in Echtzeit verfolgt werden kann, um die Therapie individuell anzupassen. Die Grundlage für die erfolgreiche Entwicklung eines Wirkstoffträgersystems bilden Untersuchungen zum Verhalten von nanopartikulären Substanzen in physiologischer Umgebung. Im Rahmen der vorliegenden Arbeit wurden polymere Nanopartikel unterschiedlicher Morphologie durch die kontrollierte Selbstorganisation amphiphiler Blockcopolymere hergestellt, charakterisiert und auf ihre Wechselwirkungen mit menschlichen Zellen und Serumproteinen untersucht. Dazu wurde eine Studie zur Geometrie- und Größenabhängigkeit der Zytoxizität von nanoskaligen Kugel- und Zylindermizellen sowie Vesikelstrukturen durchgeführt. Des Weiteren wurde das Agglomerationsverhalten von verschiedenen polymeren Nanopartikeln in Anwesenheit von Serumproteinen untersucht. Mit Hilfe eines Mikromischer-basierenden Verfahrens gelang es, kontinuierlich sehr einheitliche Polymervesikel herzustellen und diese in situ mit unterschiedlichen Komponenten zu beladen - unter anderem mit dem Wirkstoff Camptothecin sowie einer hohen Dichte an hydrophoben Eisenoxid-Nanopartikeln. Diese wirkstoffbeladenen Hybridvesikel zeigten in vitro im Vergleich zum freien Wirkstoff eine erhöhte zytotoxische Wirksamkeit gegen die Krebszelllinie PC-3. Nach einer Funktionalisierung mit einem krebszellspezifischen Targeting-Peptid und einer zusätzlichen Fluoreszenzmarkierung wurde mit Hilfe der Durchflusszytometrie und konfokalen Laser-Scanning-Mikroskopie eine rezeptor-spezifische Zellaufnahme in PC-3-Krebszellen demonstriert. Messungen zur magnetischen Charakterisierung bestätigten zudem die potenzielle Anwendung magnetischer Polymervesikel als MRT-Kontrastmittel wie auch als Tracer für das Magnetic Particle Imaging (MPI). Kontinuierlich hergestellte, wirkstoffbeladene, magnetische Polymervesikel erfüllen somit viele Grundvoraussetzungen für ein theranostisches Wirkstoffträgersystem und bieten weitere Entwicklungsmöglichkeiten im Hinblick auf Magnetfluid-Hyperthermie, magnetisches Targeting oder eine durch ein Magnetfeld induzierte Wirkstofffreisetzung. N2 - One of the main goals of nanomedicine is to improve the treatment of hazardous diseases whose conventional therapy often has serious side effects. The vision is to create a theranostic drug delivery system which is capable of safely transporting therapeutic cargo through the body to a targeted site of disease at which point the drug is released. Furthermore, it is desirable to track the carrier in real time which would allow for a personal adjustment of the therapy. Studies on the behavior of nanoparticulate substances in a physiological environment form the basis for the possibility to successfully develop a drug carrier system. In the present work, polymeric nanoparticles with different morphologies were prepared by the controlled self-assembly of amphiphilic block copolymers. The nanoparticles were subsequently characterized and their interactions with human cells and serum proteins investigated. A cytotoxicity study with spherical and cylindrical micelles as well as vesicular structures was carried out and showed a dependency of cytotoxic effects on the geometry and size of the nanoparticles. The agglomeration behavior of various polymeric nanoparticles in the presence of serum proteins was also studied. Highly uniform polymeric vesicles were continuously manufactured in a micromixer based device and in situ loading with different components was performed. In this way, dual loaded vesicles with the anticancer drug camptothecin and a high amount of hydrophobic iron oxide nanoparticles were produced. When tested in vitro, these drug-loaded vesicles showed an increased cytotoxic activity against the cancer cell line PC-3 when compared to the free drug. Specific cellular uptake in PC-3 cancer cells was demonstrated with flow cytometry and confocal laser scanning microscopy after functionalization with a cancer cell specific targeting peptide and an additional fluorescent label. Magnetic characterization of the iron oxide-loaded vesicles also confirmed the potential application as MRI contrast agents and as tracers for magnetic particle imaging (MPI). Continuously manufactured, drug-loaded, magnetic polymeric vesicles thus fulfill many prerequisites for a theranostic drug carrier system and provide opportunities for further developments in the field of magnetic fluid hyperthermia, magnetic targeting or magnetic drug release. T3 - BAM Dissertationsreihe - 133 KW - Selbstorganisation KW - Nanomedizin KW - Wirkstoffträgersystem KW - Krebstherapie KW - Theranostik PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5134 VL - 133 SP - 1 EP - 238 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-513 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Rockland, Ulrike T1 - Jahresbericht 2014 T1 - Annual report 2014 T3 - BAM Reports/Jahresberichte - 2014 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5167 SN - 0934-9456 N1 - Volltext (PDF) in deutsch und englisch - Full text (PDF) in German and English VL - 2014 SP - 1 EP - 134 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-516 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Gollnow, Christian T1 - Beitrag zur Ermittlung vorrangig konstruktiver Einflussgrößen auf die Heißrissinitiierung an geschweißten Bauteilen N2 - Die bisherigen Forschungsergebnisse ermöglichen, ungeachtet der Vielzahl existenter experimenteller und numerischer Ergebnisse, keine allgemeingültige Heißrisscharakterisierung und speziell Erstarrungsrisscharakterisierung. Ursächlich hierfür ist vor allem die Vielzahl von Einflussgrößen und damit die komplexe Interaktion dieser Mechanismen, die eine generelle Beschreibung des Heißrissphänomens erschwert. Die Heißrissentstehung und somit die Erstarrungsrissinitiierung werden durch die Interaktion von Schweißprozess, Metallurgie und Design beschrieben. Die Literaturrecherche zeigt, dass bei der Erstarrungsrisscharakterisierung der konstruktive Aspekt vielfach unterschätzt wird. Hierbei werden u. a. die bauteil- und fertigungsspezifischen Vorbeanspruchungen durch diverse Umformprozesse hinsichtlich der Ausführung der Schweißnaht zu selten berücksichtigt. Ferner wird der Designeinfluss bei der Heißrissentstehung durch die eingeschränkte Übertragbarkeit verschiedener Beanspruchungen auf den Labormaßstab und somit auf die jeweiligen Heißrisstests limitiert. Daraus resultiert die Komplexität bei dem Transfer der Ergebnisse zwischen Laborproben und Bauteilen sowie der grundsätzlichen Heißrisscharakterisierung. Diese Arbeit hatte das Ziel, unterschiedliche bei Bauteilschweißungen auftretende Bean-spruchungen im Labor abzubilden sowie die experimentelle Quantifizierung erstarrungs-risskritischer Größen. Diesbezüglich wurden fremdbeanspruchte Heißrisstests unter An-wendung berührungsloser Messtechniken durchgeführt, um so den Schweißprozess hin-sichtlich verschiedener designspezifischer Einflussgrößen auf die Erstarrungsrissinitiierung bei hochlegierten Stählen zu analysieren. Die Untersuchungen erfolgten an austenitischen (1.4828) und ferritischen (1.4509) Werkstoffen mit unterschiedlichen mechanischen und technologischen Eigenschaften. Zur Berücksichtigung der praxisrelevanten Beanspruchungen wurden die Proben mit verschiedenen Zug- und Biegebeanspruchungen teils vor und während des WIG-Schweißprozesses beaufschlagt. Im Hinblick auf den jeweiligen Beanspruchungsfall erfolgten lokale und schweißnahtnahe Analysen erstarrungsrisskritischer Verschiebungen und Verschiebungsraten mit exakter Zeit- und Ortsauflösung. Zusätzlich wurden Fallanalysen an Bauteilen in industriellen Fertigungsprozessen durchgeführt, um besonders den gegenseitigen Einfluss von Design und Schweißprozess zu ermit-teln und zusätzlich die Ergebnisübertragbarkeit von Laborproben und Bauteilen aus dem Fertigungsprozess zu prüfen. Die durchgeführten Untersuchungen ergeben wesentliche Erkenntnisse zur Vermeidung von Bauteilschäden durch Erstarrungsrisse. Es wurde der designspezifische Einfluss auf das Erstarrungsverhalten der Schweißnaht nachgewiesen und als Erstarrungsrisskriterium dargestellt. Die Arbeit beschreibt für diverse Beanspruchungen die Mechanismen bei der Erstarrungsrissinitiierung. Ferner zeigen die Ergebnisse wesentliche erstarrungsrissspezifische Unterschiede zwischen Vorbeanspruchungen und Beanspruchungen während des Schweißprozesses. Zudem erfolgte die Darstellung der Interaktion von Design und Schweißprozess, werkstoffspezifisch anhand in-situ detektierter Verschiebungswerte. Es wurde gezeigt, dass die ermittelten Messdaten von Bedeutung für weiterführende numerische Simulationen sind, insbesondere zur Validierung numerischer Modelle, die erstarrungsrisskritische Bauteildeformationen abbilden. N2 - The previous research results do not allow a general hot crack characterisation although a variety of experimental and numerical knowledge is available. The reason for this is mainly the large number of influencing factors that complicate a complete description of the hot cracking phenomenon and especially solidification cracking. The hot crack formation and thus the solidification crack initiation can be described by the interaction of process, metal-lurgy and design. However, the literature examination shows that in the solidifaction crack characterisation the influence of the design aspect is often underestimated. The pre-stresses of the structural components is up to now not considered as an essential cause for the formation of solidification cracks. The evaluation of the influence of the vari-ous parameters is presented partly inconsistent. In addition, the targeted presentation of the design influence with respect to the solidification cracks in the weld is because the limited transferability of the various component-specific stresses on a laboratory scale and thus to the respective hot cracking tests restricted. Hence, the difficulty to transfer the results be-tween laboratory specimen and component as well as the general hot crack characterisa-tion is given. In this work the different types of stresses from the component welding in the laboratory and to quantify experimentally the solidification crack critical values, displacements and dis-placement rates were detected. In this regard external loaded hot cracking tests were car-ried out by using the advantages of contactless measurement techniques close to the weld and to analyse the welding process with respect to various local and global design-specific factors influencing the formation of solidification cracks in high alloyed steel. These investi-gations were performed on austenitic (1.4828) and ferritic (1.4509) materials with different mechanical and technological properties. To reflect the praxis relevant load conditions from production process the specimens were treated with various tensile and bending load partly before and during TIG-welding. With regard to the respective load cases the local and two-dimensional analyses of solidification crack critical parameters were carried out close to the weld, time and spatial resolved. Additionally, case analyses on components in the pro-duction process were done in order to evaluate the primary design-specific influence to solidification cracking. The general influence of the design to the process parameters was evaluated. Furthermore, the transferability of the laboratory test results on components was examined. The performed investigations yield significant knowledge to prevent solidification cracks, especially for component manufacturing. The design-specific influence on the solidification behavior and the weld microstructure was detected which was proved as a solidification crack criterion. This work describes feasible mechanisms of different stress conditions with respect to the initiation of solidification cracks. In addition, the results show substantial solidification specific differences between pre-load and load during the welding process. It was described the mutual influence of design and welding process, material-specific based on in-situ detected displacement values. The data obtained are of importance for further numerical simulations, especially for the validation of numerical models that represent the solidification crack-critical component deformations. T3 - BAM Dissertationsreihe - 139 KW - Digital-Image-Correlation-Technik (DIC) KW - Bauteilbeanspruchung KW - Heißrisse KW - Schweißtechnik KW - In-Situ-Analyse PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5353 SN - 978-3-9817502-0-1 VL - 139 SP - 1 EP - 183 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-535 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Klippel, Alexander T1 - Investigations into the influence of dustiness on the course of vented dust explosions N2 - A new safety characteristic named “dustiness” according to the German guideline VDI 2263 – part 9 is investigated. Dustiness describes the tendency of a powder to form airborne dust by a prescribed mechanical stimulus. Dusts often behave differently in a dust/air mixture or in the case of a dust explosion, even if they have comparable physical properties such as particle size and density. In order to look into the effects of dustiness on dust cloud Formation and explosion properties experiments and simulations in a 75 L vertical dust Dispersion glass tube apparatus were carried out. In a second step industrial-scale experiments were carried out in a 50 m³ silo. Experiments showed that particle size and density are not the only factors which influence dustiness, since the chosen dusts with comparable densities and particle size distributions showed very different behavior in the flow. Other dust properties such as particle shape, specific surface area, humidity and agglomeration processes have an influence which can outweigh size and density. Preliminary explosion experiments showed that dustiness has an influence on the reduced explosion pressure and pressure rise in a vented 75 L test apparatus. In order to verify the results for applications in the process industries further tests with different settings were carried out in industrial-scale experiments. First dust concentration measurements were done in order to evaluate the reproducibility of filling processes. Experiments showed that single tests differed by 30 % and more from the average depending on dust sample and filling method. First explosion experiments with a worst-case scenario in terms of high turbulence and homogenous dust distribution showed that the maximum reduced explosion pressures were well below the calculated values. Reduced explosion pressures and rates of pressure rise of the hree tested dust were as their Explosion characteristics pmax and KSt let suggest. The Euler/Lagrange and the Euler/Euler approaches were compared simulating dust/air mixtures. Especially sedimentation and the ability of the approaches to simulate the tendency of dust to stay airborne were investigated. The Euler/Lagrange approach is better suited for simulating local dust concentrations, particle size distributions and particle forces. With the Euler/Euler method it is possible to achieve fast solutions for one specified diameter. The computational fluid dynamics code ANSYS CFX R14 was used for all simulations. N2 - Eine neue sicherheitstechnische Kennzahl, das Staubungsverhalten gemäß VDI Richtlinie VDI 2263 – Blatt 9, wird hinsichtlich ihres Nutzens für den Staubexplosionsschutz untersucht. Unter Staubungsverhalten versteht man die Tendenz eines Staubes, Wolken aufgrund eines festgelegten mechanischen Stimulus zu bilden. Stäube können sich bei vergleichbareren physikalischen Eigenschaften wie Dichte oder Partikelgrößenverteilung, teilweise sehr unterschiedlich in einem Staub/Luft-Gemisch oder im Falle einer Staubexplosion verhalten. Um den Einfluss des Staubungsverhaltens auf die Staubwolkenbildung und den Ablauf von Explosionen zu untersuchen, wurden Experimente und Simulationen in einer vertikalen 75 L Rohrapparatur durchgeführt. Mit den Erkenntnissen aus diesen Laborversuchen wurden weitere Versuche im Realmaßstab in einem 50 m³ Silo durchgeführt. Versuche im Labormaßstab in einem druckentlasteten 75 L Behälter haben gezeigt, dass das Staubungsverhalten einen Einfluss auf die reduzierten Explosionsdrücke, die zeitlichen Druckanstiege und die Flammengeschwindigkeiten hat. Um die Versuchsergebnisse für den industriellen Maßstab zu belegen, wurden Versuche in einem 50 m³ Silo durchgeführt. Dabei wurde zunächst die Reproduzierbarkeit von Befüllungsvorgängen mit Staubkonzentrationsmessungen durch mehrere Wiederholungsversuche überprüft. Dabei ergaben sich Abweichungen von 30 % und mehr im Vergleich zum Mittelwert der Versuche. Erste Explosionsversuche eines Worst-Case-Szenarios mit hoher Turbulenz und möglichst homogenen Staubwolken ergaben deutlich niedrigere reduzierte Explosionsdrücke als die mit den empirischen Gleichungen berechneten. Der Explosionsverlauf war in Übereinstimmung mit den Kenngrößen pmax und KSt. Bei der Simulation von Staub/Luft-Gemischen wurden mit dem Euler/Lagrange- und dem Euler/Euler-Ansatz verwendet. Dabei wurde vor allem untersucht inwiefern das Sedimentations- und Staubungsverhalten modelliert werden können. Es zeigte sich, dass der Euler/Lagrange-Ansatz besser geeignet ist lokale Staubkonzentrationsverteilungen, Partikelgrößenverteilungen und -kräfte zu simulieren. Der Euler/Euler-Ansatz ermöglicht generelle Aussagen in kürzerer Rechenzeit für eine definierte Partikelgröße. Der numerische Strömungslöser ANSYS CFX V14 wurde für alle Simulationen benutzt. T3 - BAM Dissertationsreihe - 123 KW - dustiness KW - Euler/Lagrange approach KW - vented dust explosion KW - dust explosion protection KW - CFD PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-4635 SN - 978-3-9816668-2-3 VL - 123 SP - 1 EP - 207 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Liehr, Sascha T1 - Fibre Optic Sensing Techniques Based on Incoherent Optical Frequency Domain Reflectometry N2 - Diese Arbeit beschreibt einen alternativen Ansatz zur weit verbreiteten optischen Zeitbereichsreflektometrie, engl.: optical time domain reflectometry (OTDR). Die inkohärente optische Frequenzbereichsreflektometrie, engl.: incoherent optical frequency domain reflectometry (I-OFDR), wird grundlegend analysiert und hinsichtlich ihrer Möglichkeiten zur kontinuierlich ortsaufgelösten (verteilten) Rückstreumessung in optischen Fasern sowie faseroptischen Sensoranwendungen betrachtet. Im Gegensatz zum OTDR Ansatz wird hier die Übertragungsfunktion der optischen Faser gemessen, die über die inverse Fouriertransformation mit der äquivalenten Zeitbereichsantwort verknüpft ist. Das grundsätzliche Verfahren hat gewisse Vorteile und wird bereits zur Messung nichtlinearer optischer Effekte in optischen Fasern genutzt. Die allgemeine Rückstreumesstechnik unterscheidet sich jedoch bezüglich Anforderungen und Einschränkungen und wurde bisher nicht genau untersucht. Verteilte faseroptische Sensoranwendungen mit bemerkenswerter Messauflösung basierend auf Rayleigh-Rückstreuung und Reflexionsstellen in optischen Fasern werden erstmals vorgestellt. Im ersten Teil der Arbeit wird der Frequenzbereichsansatz theoretisch beschrieben. Notwendige Signalverarbeitung und deren Einfluss auf die Zeitbereichsantwort werden dargestellt. Abweichungen von der Linearität des I-OFDR Systems werden diskutiert und ein optimierter Messaufbau wird eingeführt; der entscheidende Einfluss der spektralen Eigenschaften der optischen Quelle wird im Detail betrachtet. Geeignete Parameter des I-OFDR Ansatzes, wie Dynamikbereich und Empfindlichkeit, werden definiert und für den Laboraufbau bestimmt. Ein möglicher Ansatz zur Unterdrückung starker Störsignale wird vorgestellt. Die Vorteile des I-OFDR Ansatzes gegenüber der OTDR Technik bezüglich der Umsetzung für hohe Ortsauflösungen sowie Messauflösung und Signalstabilität werden gezeigt. Diese Vorteile und dem Frequenzansatz eigene Messmöglichkeiten werden im zweiten Teil der Arbeit für ortsaufgelöste Sensoranwendungen demonstriert: Eine dämpfungsarme polymeroptische Faser (POF) wird erstmals auf ihre Sensoreigenschaften untersucht und zur verteilten Dehnungsmessung verwendet. Die Abhängigkeit der Rückstreuleistung von der aufgebrachten Dehnung kann genutzt werden, um gedehnte Faserstrecken zu lokalisieren. Weiterhin wird ein Korrelationsalgorithmus eingeführt, der es ermöglicht ortsaufgelöst Längenänderungen entlang der Faser mit mm-Auflösung zu messen indem die starken Streuzentren in der Faser mit einer Referenzmessung korreliert werden. Untersuchungen auf Querempfindlichkeiten der Sensorfaser bezüglich Temperatur, relativer Feuchte und Modenausbreitung zeigen vernachlässigbare bzw. beherrschbare Abhängigkeiten. In Kombination mit dem hochauflösenden I-OFDR Ansatz ermöglichen die vorgestellten Sensorverfahren vielversprechende neue Messanwendungen. Spezielles Interesse besteht in Bereichen der Bauwerksüberwachung, da die Faser nahezu verlustfrei auf über 100 % gedehnt werden kann. Ein weiteres Sensorverfahren, basierend auf dem Frequenzbereichsansatz zur dynamischen und quasi-verteilten Messung von Längenänderungen und Leistungsänderungen zwischen Reflexpunkten in der Faser wird präsentiert. Basierend auf der Messung weniger Frequenzpunkte der komplexen Frequenzantwort der Messfaser können mehrere Reflexe gleichzeitig und unabhängig voneinander bezüglich Position und reflektierter optischer Leistung ausgewertet werden. Messfrequenzen bis zu 2 kHz können erreicht werden und Längenänderungsauflösungen im μm-Bereich bei kleineren Messfrequenzen sind möglich. Das Messverfahren wird auf systematische Fehlereinflüsse untersucht und anhand von Demonstratormessungen validiert. Messungen der Deformation eines Gebäudes auf einem Erdbebenversuchsstand demonstrieren die Möglichkeit der Feldanwendung des Verfahrens. Das vorgestellte I-OFDR Verfahren demonstriert konkurrenzfähige Messparameter für allgemeine und hochauflösende optische Rückstreumessungen und die vorgestellten faseroptischen Sensorprinzipien zeigen vielversprechende Perspektiven für Anwendungen z.B. in der Bauwerksüberwachung. N2 - In this thesis, an alternative approach to the well-known optical time domain reflectometry (OTDR) technique is presented. A thorough analysis regarding distributed backscatter measurement in optical fibres is provided and its prospects for optical fibre sensing applications are demonstrated and discussed. The measurement approach is referred to as incoherent optical frequency domain reflectometry (I-OFDR): the frequency response of the fibre under test is measured and transferred into its time domain equivalent using inverse Fourier transform. This general technique has been studied and used for the measurement of nonlinear scattering effects in optical fibres. The requirements, limitations and prospects for general backscatter measurement, however, are different and have not been studied in detail prior to this work. Distributed sensing using Rayleigh scattering and reflective events in the fibre is first demonstrated using I-OFDR with remarkable measurement resolution. The incoherent detection technique allows for measuring singlemode fibres as well as multimode fibres. The first part of this work deals with the theoretical analysis and optimized implementation of the frequency domain approach. Necessary signal processing and its impact on the time domain response are presented. Sources of deviation from the linearity of the I-OFDR system are identified and an optimized laboratory setup is introduced; the crucial impact of the source coherence is thoroughly discussed. Suitable system parameters for the I-OFDR approach are defined: the system dynamic range and sensitivity are determined. A technique to suppress the dynamic range-limiting signal originating from strong reflections in the fibre is suggested. It is demonstrated that the I-OFDR technique has advantages over OTDR in terms of implementation for high-resolution measurement, measurement accuracy and signal stability. These advantages and measurement possibilities specific to the frequency domain approach are utilized for spatially resolved sensing applications in the second part of this work: A low optical loss polymer optical fibre (POF) is for the first time studied and analyzed for distributed strain sensing. The backscatter level dependence on strain in the fibre can be used to detect and locate strained fibre sections. Also, a correlation algorithm is proposed and demonstrated to measure length changes along the fibre with mm-resolution by correlating the typical backscatter signature of this fibre type. The fibre type is analyzed in detail regarding cross-sensitivities to temperature, relative humidity as well as mode propagation influences. The proposed sensing principles in combination with the highresolution I-OFDR allow for promising distributed sensing applications. Special interest is expressed by the structural health monitoring (SHM) sector since the fibre can measure strain values exceeding 100 %. Another sensing technique, specific to I-OFDR, is proposed for quasi-distributed and dynamic measurement of length changes and optical power changes at reflective events along the fibre. Precise calculation of the positions and reflected powers of multiple reflections can be conducted in parallel from the measurement of a few sampling points of the complex-valued frequency response. That allows for measuring with an increased repetition rate up to 2 kHz or at μm-scale length changes resolution at lower measurement frequencies. The approach is demonstrated in the laboratory and in a field application by measuring the deformation of a masonry building on a seismic shaking table. The I-OFDR exhibits competitive performance for general high-resolution backscatter measurement and the proposed optical fibre sensor principles may have promising prospects in the structural health monitoring (SHM) sector. T3 - BAM Dissertationsreihe - 125 KW - optical fiber sensor KW - OFDR KW - distributed backscatter measurement KW - polymer optical fiber (POF) sensor KW - structural health monitoring PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-4660 SN - 978-3-9816668-4-7 VL - 125 SP - 1 EP - 144 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Zur, Malte T1 - Numerische Modellierung der Kabinenluftströmung und des Stofftransports von Gefahrgut in Flugzeugfrachträumen N2 - Für den Transport flüssiger Gefahrguter im Luftverkehr werden unter anderem Kunststoffverpackungen verwendet, die Leckagen aufweisen oder Permeation unterliegen können. Aufgrund der vorhandenen Belüftungsbedingungen ist eine Ansammlung entzündlicher oder gesundheitsschädlicher Gase im Frachtraum von Flugzeugen denkbar. Die Überschreitung ausreichender Konzentrationen solcher Gase kann zu einer Gefährdung führen. Im Rahmen der vorliegenden Arbeit werden die Kabinenluftströmungen und der Stofftransport von Gefahrgut in Flugzeugfrachträumen mittels CFD untersucht. Zunächst erfolgt die Entwicklung eines geeigneten numerischen Modells auf der Grundlage eines generischen Frachtraums mit typischen Merkmalen. Die verwendeten realitätsnahen Randbedingungen entsprechen aktuellen Flugzeugmustern. Das numerische Modell wird mittels experimenteller Modellversuche im Maßstab 1/10 validiert. Das Strömungsfeld im Frachtraummodell wird mittels eines LDA-Systems vermessen. Das validierte numerische Modell wird sowohl für Simulationen im Maßstab 1/10 als auch im Maßstab 1/1 verwendet. Anhand der drei Validierungskriterien Symmetrie, Verlaufe und Beträge der betrachteten Strömungsgrößen und einer LDA-Spektralanalyse wird insgesamt eine gute qualitative und quantitative Übereinstimmung zwischen Experiment und Simulation ermittelt. Eine systematische Untersuchung zeigt den Einfluss relevanter Parameter auf das Strömungsfeld und den Stofftransport. Zunächst werden die Einlassreynoldszahl und der Einlassturbulenzgrad sowie die Wandrauigkeit und Wandunebenheit bewertet. Für kleine Reynoldszahlen werden hohe Konzentrationen und für größere Reynoldszahlen werden deutlich geringeren Konzentrationen von Gefahrgut ermittelt. Anhand einer Variation in vier Schritten wird der Einfluss des Einlassmassenstromverhältnisses aus Luft und Gefahrgut bewertet. Erst für Werte von <1000 lasst sich ein signifikanter Einfluss feststellen. Es werden die Stoffe Toluol und n-Hexan beispielhaft für brennbare Gefahrgüter der Klasse 3 verwendet. Der Einfluss der Position und Gestalt verschiedener Einlassquellen wird an vier realitätsnahen Quellentypen bewertet. Anhand vier verschiedener Transportszenarien wird die Ausbreitung von Gefahrgut im Modellmaßstab untersucht. Die Szenarien unterscheiden sich durch die Art der Belüftung und durch die Dauer des Gefahrgutaustritts. Szenarien mit aktiver Frachtraumbelüftung sind als eher unkritisch zu beurteilen. Die betrachteten Szenarien ohne aktive Frachtraumbelüftung sind als gefährlich einzustufen. Insbesondere das Szenario mit zeitlich unbegrenztem Gefahrgutmassenstrom erreicht kritische Konzentrationswerte und eine kritische Ausdehnung der Gefahrgutansammlung im Frachtraum. Diese Ergebnisse werden anhand zweier Szenarien im Maßstab 1/1 bestätigt. Die vorliegende Arbeit leistet einen Beitrag, das Verständnis der Strömungs- und Stofftransportvorgange im Flugzeugfrachtraum beim Transport von Gefahrgütern im Luftverkehr zu erweitern, um Risiken im Luftverkehr zu identifizieren. Die Allgemeingültigkeit und die Übertragbarkeit der Erkenntnisse auf Flugzeugmuster und Flugszenarien mit komplexeren Details sind zu prüfen. N2 - Liquid dangerous goods are regularly transported as air freight in commercial aircrafts. Using plastic jerrycans or plastic containers, liquids or gases can escape by leakage or permeation effects. The specific ventilation situation in the aircraft cargo compartment may lead to agglomerations of potentially flammable or harmful gas-air mixtures in the cargo compartment. Exceeding certain concentration limits of such gases may cause dangerous situations. This work presents a CFD study of the cabin air flow and the mass transport of dangerous goods in the cargo compartments of commercial airplanes. In a first step, an adequate numerical model is developed that utilizes a generic aircraft cargo compartment with typical characteristics. The realistic boundary conditions are based on modern types of aircrafts. The numerical model is validated by model experiments in 1/10 scale. As a second step, the flow field in the cargo compartment is determined using a LDA-system. The validated numerical model is employed for simulations in 1/10 and 1/1 scale. Using three validation criteria (the symmetry, the evolution and values of flow variables and a LDA spectral analysis) a good qualitative and quantitative agreement between experiment and simulation is found. As a next step, a systematic analysis of relevant parameters influencing the flow and the mass transport in the cargo compartment is conducted. The influence of the inlet Reynolds number and the inlet turbulence intensity as well as the wall roughness and geometric obstructions on the wall are evaluated. For low Reynolds numbers, high concentrations are found and for higher Reynolds numbers, significantly lower concentrations of dangerous goods are calculated. The influence of, the ratio of air and dangerous good flowing into the domain is evaluated using four different values of. Only values of <1000 show a significant influence on the concentration levels in the domain. The dangerous substances toluene and hexane are used as examples for class 3 flammable dangerous goods. The influence of the position and the shape of different inlet sources for dangerous goods are evaluated using four different types of sources. In a final step, four different transport scenarios are used to simulate and evaluate the expansion and propagation of dangerous goods in the generic cargo compartment in the model scale 1/10. The scenarios differ in the ventilation situation and the duration of the mass of dangerous goods entering the domain. Scenarios with an active cargo compartment ventilation are found to be noncritical. Scenarios without an active ventilation lead to critical concentrations of dangerous goods. In particular, a scenario with an indefinite mass inflow of a dangerous gas shows critical concentration levels and a critical expansion in the cargo compartment. These findings are confirmed by simulations of two different scenarios in a 1/1 scale. The presented work contributes to a better understanding of the cabin air flow and the mass transport of dangerous goods in aircraft cargo compartments in order to identify potential risks. The universal validity and the transferability of the findings to other, more complex aircraft cargo compartments and transportations scenarios are to be reviewed in further research. T3 - BAM Dissertationsreihe - 128 KW - CFD KW - Kabinenluftströmung KW - Stofftransport von Gasen KW - gefährliche Güter im Luftverkehr KW - LDA PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-4949 SN - 978-3-9816668-8-5 VL - 128 SP - 1 EP - 170 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-494 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -