TY - CONF A1 - Arndt, Ralf A1 - Helmerich, Rosemarie A1 - Maierhofer, Christiane A1 - Röllig, Mathias T1 - Quantitative pulse-phase-thermography for composites and concrete structures T2 - Structural Faults & Repair 2006 CY - Edinburgh, Scotland DA - 2006-06-13 PY - 2006 AN - OPUS4-12441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Arndt, Ralf A1 - Röllig, Mathias T1 - Aktive Thermografie zur zerstörungsfreien Ortung von Ablösungen und Fehlstellen in Beton und Mauerwerk T2 - Bauwerksdiagnose 2006 CY - Berlin, Germany DA - 2006-02-23 PY - 2006 AN - OPUS4-14083 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, Ralf A1 - Maierhofer, Christiane A1 - Röllig, Mathias T1 - Quantitative pulse-phase-thermography for masonry and concrete structures T2 - 9th European Conference on NDT CY - Berlin, Germany DA - 2006-09-25 PY - 2006 AN - OPUS4-13193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, Ralf A1 - Helmerich, Rosemarie A1 - Maierhofer, Christiane A1 - Röllig, Mathias ED - Forde, M. T1 - Quantitative Pulse-Phase-Thermography for Composites and Concrete Structures N2 - The active approach for non-destructive-testing in Civil Engineering (NDT-CE) with infraredthermography (IR), developed at the Federal Institute for Materials Research and Testing (BAM), is described in part one of this contribution. The active IR-approach is based on the principles of impulse- (IT) and pulse-phase-thermography (PPT). The concept is a direct result of a research project at the BAM in cooperation with the Technical University of Berlin (TUB) and was funded by the Deutsche Forschungsgemeinschaft (DFG). In the second part results of the new thermography-scanning system (thermo-scanner) of BAM on debonding of multi-layered structures, especially carbon fibre reinforced plates (CFRP) on concrete are presented. Both, the thermo-scanner developed at BAM, and the investigations carried out, are part of the EU-Project Sustainable Bridges. In the third part of the paper the characteristic frequency of the optimum phase-contrast as a means for the characterization of defects’ depth in CE by means of PPT is introduced. A new quantitative approach is tested and discussed on concrete structures with defects of polystyrene and gas concrete. T2 - 11th International Conference and Exhibiton "Structural Faults and Repair - 2006" CY - Edinburgh, Scotland, UK DA - 2006-06-13 KW - Quantitative NDT KW - Impulse-thermography KW - Pulse-phase-thermography KW - Blind / characteristic frequency KW - Concrete KW - Thermo-scanner KW - CFRP-laminates KW - Debonding KW - Voids PY - 2006 SN - 0-947644-59-8 SP - 1(?) EP - 17(?) PB - Engineering Technics Pr., CY - Edingburgh AN - OPUS4-13794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maierhofer, Christiane A1 - Arndt, Ralf A1 - Röllig, Mathias A1 - Rieck, C. A1 - Walther, A. A1 - Scheel, H. A1 - Hillemeier, B. T1 - Application of impulse-thermography for non-destructive assessment of concrete structures N2 - Impulse-thermography is an active method for quantitative investigations of the near surface region of various structures. It has recently been applied and optimised to applications in civil engineering. By using either an internal or external heat source, parts of the structure under investigation are heated up and the transient heat flux is observed by recording the temperature change at the surface as a function of time. This method is very well suited for the detection of voids and honeycombing in concrete, up to concrete covers of 10 cm as well as for the location of delaminations in multi-layered systems (e.g. plaster on concrete, CFRP-laminates on concrete, asphalt on concrete). Also safety relevant defects like voids in tendon ducts and cracks in concrete could be recognised. KW - Non-destructive testing KW - Impulse-thermography KW - Concrete KW - CFRP-laminates KW - Delamination KW - Tendon duct KW - Voids KW - Compaction faults PY - 2006 DO - https://doi.org/10.1016/j.cemconcomp.2006.02.011 SN - 0958-9465 SN - 1873-393X VL - 28 IS - 4 SP - 393 EP - 401 PB - Elsevier CY - Barking, Essex AN - OPUS4-12359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kley, Gerd A1 - Brenneis, Rudolf A1 - Adamczyk, Burkart A1 - Simon, Franz-Georg T1 - Thermochemical treatment - Technologies for recovery and utilisation of materials KW - Thermochemical treatment KW - Materials separation KW - Refractories KW - Stainless steel PY - 2006 SN - 1009-606X VL - 6 IS - 2 SP - 231 EP - 236 CY - Beijing AN - OPUS4-12346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Adamczyk, Burkart T1 - RECARC - Verwertung von Rückständen aus der Metallurgie mit der Lichtbogenofentechnologie N2 - The project RECARC is to demonstrate the complete recycling of slag gained from the stainless steel production after the AOD-process. Due to the high content of chromium, this slag is only usable in qualitative inferior applications. Thermochemical treatment by arc furnace enables the separation of chromium from the mineral fraction. The recovered chromium can be returned as raw material into the stainless steel production. Furthermore, the processing turns the slag into a useful building material. The investigations focused mainly on nearly complete reduction and removal of the chromium from the mineral fraction. The process parameters were optimised and different reducing agents (carbon, aluminium, FeSi and SiC) were tested. The chromium content of an AOD-slag was successfully significant decreased to >0.1% by resistance melting in addition of petroleum coke as reducing agent. By adding adequate additives and a granulation of the slag the mineral fraction can be simply improved to a phase, which is similar to typical cement components. Furthermore, EOF-slag, which consist much more chromium compounds, was tested. In this slag 80% of the chromium was successfully removed. Totally 30 melting experiments with a total conversion of 5.5 tons of stainless steel slag had been carried out. Thus, totally 220 melting products were gained. Although the characterisation of the products was affected by technical reasons, appearing problems could be solved by choosing alternative characterisation methods. The project results were published more than 20 times (presentations in journals and on international conferences, press releases, poster presentations, internet page).------------------------------------------------------------------------------------------------------------------------------------ Im Projekt RECARC wird eine Möglichkeit für die vollständige Wiederverwertung einer bei der Herstellung von Edelstahl nach dem AOD-Verfahren anfallenden Schlacke demonstriert. Die Schlacke enthält erhebliche Mengen Chrom in Form metallischer Einschlüsse (2-5%) und mineralisch gebunden (3-4%) und wird daher gegenwärtig nur minderwertig bzw. nicht genutzt. Durch eine thermochemische Behandlung im Lichtbogenofen wird das Chrom von der mineralischen Fraktion getrennt, so dass es als Rohstoff bei der Edelstahlherstellung wiederverwendet werden kann. Die schwermetallfreie Schlacke wird durch geeignete Maßnahmen so konditioniert, dass sie als Baustoff uneingeschränkt verwendet werden kann. Die Effektivität der Reduktion und der Chromabscheidung wurde für unterschiedliche Betriebsparameter und die Reduktionsmittel Koks, Aluminium, FeSi und SiC mit dem Ziel der Optimierung des Verfahrens bestimmt. Optimal für das angestrebte Ziel ist der Betrieb im Widerstand mit Petrolkoks als zusätzlichem Reduktionsmittel. Unter diesen Bedingungen kann der Cr-Gehalt einer AOD-Schlacke auf > 0,1% gesenkt werden. Durch entsprechende Zusätze und eine Schlackegranulation beim Abguss lässt sich die Schlackequalität so einstellen, dass sie den Anforderungen eines Zementzumahlstoffes genügt. Neben AOD-Schlacken wurde auch eine EOF-Schlacke mit wesentlich höheren Chromgehalten untersucht, der um ca. 80% durch die thermochemische Behandlung gesenkt wurde. Es wurden 30 Schmelzversuche durchgeführt, in denen ca. 5,5 t AOD bzw. EOF-Schlacke umgesetzt wurden. Die Gesamtzahl an unterschiedlichen Schmelzprodukten beläuft sich auf ca. 220. Die Charakterisierung der erhaltenen Produkte wurde wegen zeitweiser Geräteausfälle erschwert, konnte aber durch Einsatz alternativer Charakterisierungsmethoden immer duchgeführt werden. Inhalt und Ergebnisse des Projektes wurden durch über 20 Publikationen (Präsentationen in Fachzeitschriften und auf internationalen Tagungen, Pressemitteilungen, Posterpräsentationen und nicht zuletzt durch die Internetseite) der Öffentlichkeit zugänglich gemacht. PY - 2006 IS - Technischer Abschlussbericht (LIFE03 ENV/D/043 SP - 1 EP - 60 AN - OPUS4-26528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Kalbe, Ute A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Weimann, Karin T1 - Recovery of non-renewable resources from waste T2 - 7th International Conference on EcoBalance CY - Tsukuba, Japan DA - 2006-11-14 KW - Natural resources KW - Thermo-chemical treatment KW - Waste management KW - Sewage sludge KW - Aggregetes PY - 2006 IS - E2-4 SP - 499 EP - 502 PB - The Society of Non-Traditional Technology CY - Tsukuba, Japan AN - OPUS4-14115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Peplinski, Burkhard A1 - Adamczyk, Burkart A1 - Adam, Karin A1 - Emmerling, Franziska A1 - Simon, Franz-Georg T1 - New horizons for the structural characterization of stainless steel slags by X-ray powder diffraction T2 - 10. European Powder Diffraction Conference (EPDIC-10) CY - Geneva, Switzerland DA - 2006-09-01 PY - 2006 AN - OPUS4-13787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -