TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Prestressed concrete structures with concentrated tendons - Structural damage due to hydrogen-induced stress corrosion cracking N2 - Hydrogen-induced stress corrosion cracking (HSCC) is well known, and highly sensitive pre-stressing steels are normally not available on the market. But in the case of existing structures, it could be necessary to ensure their safety through special kinds of investigations. Those kinds of investigations are often not applicable in a non-destructive way. Therefore, a once in a lifetime project was initiated. In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks could obtained. The initial observation to do several investigations at this bridge are several meters long longitudinal cracks in the concrete web of the box girder above and below the tension duct. The BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions. One of the major results is, the wire breaks observed at this bridge can be attributed to cracking as a result of HSCC and subsequent crack growth until breakage, due to cyclic loading from traffic and alternating restraint stresses. The probable trigger here was crevice corrosion processes at the contact points of the wires to the spacer plates in superposition with high tensile stresses due to prestressing after or with in grouting the duct. Tension wire breaks, which may have occurred before grouting and during prestressing, were not detected. The unfavorable gap situation at the spacer plates occurs over the entire cross-section of the prestressing channel and can thus affect each individual prestressing wire. Losses in the load-bearing capacity of the prestressed concrete structure can then be the result. A disadvantage of the prestressing block method in this respect is that a large number of individual wires can be affected at the same time (theoretically all wires), which can reduce the prestressing effect of the concentrated tendon accordingly. With the usual use of only one tendon per web, the possibility of load transfer to other tendons is thus not given (lack of redundancy). T2 - 4rd International Congress on Materials & Structural Stability CY - Rabat, Morocco DA - 08.03.2023 KW - Corrosion KW - HSCC KW - Wasserstoff KW - Spannungsrisskorrosion PY - 2023 AN - OPUS4-57158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialfeldmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. T2 - Vorlesung TU Berlin CY - Online meeting DA - 10.06.2020 KW - Korrosion KW - Corrosion KW - Potentialfeldmessung PY - 2020 AN - OPUS4-50905 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit. T2 - ICCRRR 2022 CY - Capetown, South Africa DA - 03.10.2022 KW - Korrosion KW - Corrosion KW - LIBS KW - Zinc PY - 2022 AN - OPUS4-55948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Prestressed Concrete Structures with Concentrated Tendons - Structural Damage due to Hydrogen-Induced Stress Corrosion Cracking N2 - In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks was obtained. BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions. T2 - Eurocorr 2022 CY - Berlin, Gemany DA - 29.08.2022 KW - Korrosion KW - Corrosion KW - Hydrogen KW - Stress Cracking PY - 2022 AN - OPUS4-55613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potential Mapping - What could we measure and what should we able to detect – guideline B03 of DGZfP N2 - “Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. Areas of corroding reinforcement steel can be located in a non-destructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose, determining the carbonation depth and the concrete cover appears more appropriate. The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.” T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Half-cell potential KW - Potential mapping PY - 2022 AN - OPUS4-55524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - Weathring camopaigns to determine corrosivity on offshore wind turbines N2 - ISO 9223 standard for the classification of corrosivity in atmospheres is based on the mass loss of standard samples. We are concerned with the question of which corrosivity categories for Fe-sheets can be found at an offshore wind turbine and where they are comparable with our offshore locations. The preliminary results indicate that the extreme corrosivity of class CX is only given in splash water-affected exposure, which is not a real atmospheric exposure condition. The results of the exposure at the SP show that the corrosivity category changes into C4, only a few meters above the splash water zone. Compared to the marine environments at Helgoland or OSS-Platform, the corrosivity is higher. The offshore environment is not as corrosive as originally expected, no atmospheric corrosion attack could be determined that would form the corrosivity category C5. T2 - Eurocorr 2024 CY - Paris, France DA - 01.09.2024 KW - Korrosion KW - Corrosion PY - 2024 AN - OPUS4-60973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan T1 - Testing to reasses - Corrosion activity assessment based on NDT using a prestressed concrete bridge as case study N2 - Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of reinforced concrete structures significantly. The challenge of detecting corrosion is that the corrosion process in its various forms is not immediately visible, especially in the corrosion initiation phase inside the concrete. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually, but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforcement. This, in turn, can cause sudden structural collapses without prior notice. Therefore, it is important to investigate whether there is protection against corrosion of the reinforcement in the concrete and to detect active corrosion in the structure at an early stage. In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-promoting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen (Germany) is used as a case-study to demonstrate how the information obtained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing (Torrent tester) and the electrical resistance measurement (Wenner probe) are considered, as well as active corrosion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrating radar (GPR). The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy (LIBS) was applied to obtain information about possible ion transport in the concrete. T2 - EUROSTRUCT 2021 - 1st Conference of the European Association on Quality Control of Bridges and Structures - EUROSTRUCT CY - Padova, Italy DA - 30.08.2021 KW - Nondestructive testing KW - Corrosion KW - Bridge KW - Durability assessment KW - Civil engineering PY - 2021 AN - OPUS4-53222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Befestigungsmittels im Bauwesen - Der richtige Werkstoff??? N2 - Die Anforderungen in verschiedenen Fachgebieten des Bauwesens an metallene Befestigungsmittels hinsichtlich des Korrosionsschutzes sind zum einen Abhängig von den verwendeten Werkstoffen und zum anderen von der Korrosivität in der jeweiligen Exposition. Hier wird ein Überblick über die gängigen Werkstoffe als auch Anwendung und Fehlerquellen verschaff T2 - TU-Berlin Vorleseung CY - Berlin, Germany DA - 05.06.2024 KW - Korrosion KW - Corrosion PY - 2024 AN - OPUS4-60974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Achenbach, R. A1 - Harnisch, J. T1 - The dgzfp Subcommittee „Corrosion Detection in Reinforced Concrete“ N2 - The subcommittee “Corrosion Detection in Reinforced Concrete” is a technical committee within the scope of the German Society for Non-Destructive Testing (DGZfP). The international working group consists of engineers and scientists from Germany, Austria and Switzerland who work at research institutes or engineering firms and aims for the practical implementation of non-destructive testing in civil engineering (NDT-CE) methods to assess the corrosion condition of reinforced concrete (RC) structures. Therefore, the group works on technical specifications that explain the necessary theoretical background of the presented techniques but mainly provide helpful instructions for the application on-site and in the laboratory. Based on the corrosion process of steel in concrete the specifications focus on selected topics where the field engineer is getting into contact with the phenomenon. Therefore, specification B 12 highlights corrosion monitoring in reinforced and prestressed concrete structures and presents different approaches to monitor the initiation and propagation phase of corrosion and shows case studies of where these techniques were applied successfully. Specification B 03 deals with the potential-mapping technique. In addition to this specification, practical training courses and certification in this method have been developed and are offered by the working group members and are organized by the DGZfP. Both specifications, B 03 as well as B 12, are available in English. In the case of specification B 03, the current version is still in the translation process and will be available soon. Currently, the group is working on a new specification for measuring the electrical resistivity of cementitious materials, for example, to evaluate the suitability of mortars for cathodic protection applications and to validate the influence of the concrete resistivity with regard to corrosion processes of steel in concrete. Given the increasing impact of corrosion damages on infrastructural structures, the working group would like to introduce the use of the mentioned specifications to an interested international audience and thus offer the possibility to reliably detect corrosion damages at an early stage to prevent significant damages or high repair costs on RC structures. T2 - ICCRRR 2024 CY - Cape Town, South Africa DA - 03.11.2024 KW - Corrosion KW - Monitoring PY - 2024 AN - OPUS4-61603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Detection of reinforcement corrosion in reinforced concrete structures by potential mapping: Theory and practice N2 - Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Nondestructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from, e.g., stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. Therefore, in a training concept firstly the theoretical basics of the test method should be imparted. Then, frequently occurring practical situations of various influencing factors will be made accessible to the participants by a model object specially designed for this purpose. The aim is to impart profound knowledge concerning the characteristics of potential mapping for detecting corrosion of reinforcing steel in order to apply this technique in practice as reliable and economical test method. KW - Corrosion KW - Potential mapping KW - Korrosion KW - Potentialfeldmessung PY - 2018 DO - https://doi.org/10.1155/2018/3027825 SN - 1687-9333 SN - 1687-9325 VL - 2018 SP - Article 3027825, 1 EP - 6 PB - Hindawi AN - OPUS4-46206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seifert, Lando T1 - The Development of a new Test Method for assessing the Susceptibility of Prestressing Steels to HiSCC N2 - This EUROCORR 2021 talk gives current results of the WIPANO research project "safety of prestressing steels." The project targets improving DIN EN ISO 15630-3 according to the reproducibility and scattering of constant load tests to assess the susceptibility of prestressing steels to stress corrosion cracking. Essential questions which we answered in the talk was: Are test practical on surfaces in delivery condition? What are the hydrogen activities of test solutions A and B during free corrosion and cathodic polarization? Can the test be improved by a modification of the test cell dimensions? T2 - Virtual EUROCORR 2021 CY - Online meeting DA - 20.09.2021 KW - Prestressing steels KW - Corrosion KW - Test electrolytes KW - DIN EN ISO 15630-3 KW - Stress corrosion cracking KW - Hydrogen charging KW - Permeation measurements PY - 2021 AN - OPUS4-53325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Corrosivity of Atmospheres and the Resulting Corrosion Protection of Galvanized Steel N2 - The investigation of the corrosivity of atmospheres are major target to ensure the durability of metallic structures. Therefore the corrosivity has to be determined and finally, the right material or corrosion protection system has to be chosen. T2 - Intergavla CY - Brussels, Belgium DA - 10.06.2024 KW - Corrosion KW - Potentialfeldmessung KW - Atmospheric corrosion PY - 2024 AN - OPUS4-60591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Poltavtseva, M. A1 - Mietz, Jürgen ED - Ottosen, L. T1 - Electrochemical investigation of carbon-based conductive coatings for application as anodes in ICCP system of reinforced concrete structures N2 - Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. T2 - International RILEM Conference on Materials, Systems and Structures in Civil Engineering 2016 CY - Lyngby, Denmark DA - 21.08.2016 KW - ICCP KW - Coating KW - Cunductive KW - Corrosion KW - reinforcement KW - Concrete KW - Cathodic protection PY - 2016 SN - 978-2-35158-176-6 SN - 978-2-35158-177-3 VL - Proceedings PRO 111 SP - 43 EP - 46 PB - RILEM Publications S.A.R.L. CY - Paris, France AN - OPUS4-37216 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Electrochemical investigation of carbon-based conductive coatings for application as anodes in ICCP system of reinforced concrete structures N2 - Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. T2 - MSSCE Materials, Systems and Structures in Civil Engineering 2016 CY - Lyngby, Denmark DA - 21.08.2016 KW - ICCP KW - Cathodic protection KW - Corrosion KW - Concrete KW - Reinforcement PY - 2016 AN - OPUS4-37215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Corrosion of galvanized reinforcement in carbonated concrete N2 - Corrosion of galvanized steel in carbonated concrete is different from the corrosion of reinforcement made of carbon steel. This is based on the corrosion mechanism of galvanized steel in dependence of the pH-value of carbonated concrete. To describe the influence of a lower pHvalue on the corrosion activity of galvanized reinforcement, different electrochemical measurements were made. The anodic and cathodic partial reaction were investigated by galvanostatic pulse measurements and potentiodynamic measurements. Especially the galvanostatic pulse measurements can describe the influence of the lower pH-value by the anodic polarization resistance with pt = 20 sec. (polarization time). Additionally, corrosion current measurements were performed, coupled with potential measurements, between galvanized steel in carbonated and non-carbonated concrete. Normally, the potential measurements are an indicator to localize the anodic and cathodic parts of a macro system. In this case the cathode was more negative than the anode before they were coupled. After the coupling of the two specimens the mixed potential was much more positive than the single potential of the galvanized steel in carbonated concrete. It increased up to the potential range of the non-carbonated specimens. This means that in case of carbonated outer areas, the embedded galvanized steel forms the cathodic part of a macro element. T2 - Eurocorr 2016 CY - Montpellier, France DA - 11.09.2016 KW - Galvanized KW - Rebar KW - Concrete KW - Corrosion PY - 2016 AN - OPUS4-37432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Electrochemical Investigations on the Corrosion Behaviour of Galvanized Reinforcing Steels in Chloride Containing Mortar N2 - Corrosion of galvanized steel in chloride containing mortar is different from the corrosion of reinforcement made of carbon steel. This is based on the corrosion behavior of galvanized steel in chloride containing mortar. To describe the influence of a chloride containing zinc-hydroxide layer at the phase boundary against a zinc-hydroxide layer in chloride free mortar, different electrochemical measurements were made. The anodic and cathodic partial reaction were investigated by galvanostatic pulse measurements and potentiodynamic measurements. Especially the galvanostatic pulse measurements can describe the influence of the chloride content by the polarization resistance with pt = 20 sec. (polarization time). Additionally, corrosion current measurements were performed, coupled with potential measurements, between galvanized steel in chloride containing and chloride free concrete. Normally, the potential measurements are an indicator to localize the anodic and cathodic parts of a macro system. In this case the results show that there is no formation of a significant macro element cell between chloride containing and chloride free mortar. After 1500 h of potential and current measurement the results show a more positive corrosion potential with increasing chloride content. The results of the potential/current curves show a significant different free corrosion current depending on the chloride content, the free corrosion current increase with increasing chloride contents; reasons for this behavior are discussed. T2 - Eurocorr 2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - Corrosion KW - Galvanized KW - Reinforcement PY - 2017 AN - OPUS4-41856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Large scale reinforced concrete test specimen for potential mapping under practical conditions N2 - Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from e.g. stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. To investigate these influencing factors under practical conditions it requires a specimen with similar damage patterns, dimensions and more factors e.g. metallic mounting parts. Recently the BAM realized such a large scale test specimen for this purpose. T2 - NDE 2017 CY - Chennai, TN, India DA - 14.12.2017 KW - Potential mapping KW - Corrosion KW - Reinforcement PY - 2017 AN - OPUS4-43472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialmessung im Stahlbetonbau N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz T2 - KKS-Schulung CY - TAE Esslingen, Germany DA - 23.04.2018 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion PY - 2018 AN - OPUS4-44770 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialfeldmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu wird Stahl im Beton durch Ausbildung einer Deck-schicht vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisie-rung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich durch Volumenexpansion der Korrosionsprodukte korrosi-onsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwen-dige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte In-formationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeu-tung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beur-teilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korro-sion zum Einsatz. T2 - 3-Länder-Korrosionstagung CY - Zürich, Switzerland DA - 12.04.2018 KW - Korrosion KW - Corrosion KW - Potentialfeldmessung PY - 2018 AN - OPUS4-44698 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. T2 - Vorlesung TU-Berlin CY - TU-Berlin, Germany DA - 30.05.2018 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion PY - 2018 AN - OPUS4-45047 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino T1 - Potentialfeldmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. KW - Korrosion KW - Potentialfeldmessung KW - Corrosion PY - 2018 SP - 1 EP - 21 CY - Berlin AN - OPUS4-45048 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar N2 - Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt T2 - Intergalva 2018 - 25th International Galvanizing Conference CY - Berlin, Germany DA - 17.06.2018 KW - Corrosion KW - Korrosion KW - Verzinkt KW - Betonstahl PY - 2018 SP - 301 EP - 309 AN - OPUS4-45240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Seifert, Lando A1 - Burkert, Andreas T1 - Innovative Korrosionsprüfung für Beton- und Spannstähle T1 - Test methods for corrosion testing of reinforcing and prestressing steels N2 - Korrosion ist einer der maßgeblichen Schädigungsmechanis-men im Stahlbetonbau und limitiert die Nutzungsdauer vonInfrastrukturbauwerken zum Teil erheblich. Dabei differenziertman zwischen verschiedenen Korrosionsvarianten, Korrosioninfolge Karbonatisierung des Betons, chloridinduzierte Korro-sion an Meerwasserbauwerken oder durch Tausalzbelastungund im Fall von Spannstahlbauwerken kann zusätzlich was-serstoffinduzierte Spannungsrisskorrosion (SpRK) auftreten.Für den Einsatz alternativer Betonstähle wie nichtrostenderBetonstahl gilt es, die Höhe des kritischen korrosionsaus-lösenden Chloridgehalts zu bestimmen. Um diesen für diejeweiligen Betonstähle zu ermitteln, fehlen bislang jedochnormativ geregelte Prüfverfahren. Die Empfindlichkeit vonSpannstählen gegenüber SpRK bedarf gemäß aktueller Nor-mung Langzeit-Auslagerungstests, die eine werkseigeneProduktionskontrolle aufgrund der langen Prüfzeiten nahezuunmöglich machen. Ein neu entwickeltes Prüfverfahren unterAnwendung kathodischer Polarisation, das inzwischen imneusten Entwurf der DIN EN ISO 15630–3 aufgenommenwurde, ermöglicht eine Bewertung der SpRK-Empfindlichkeitfür Spanndrähte innerhalb von 24 Stunden. Die Ergebnissetragen zur Verbesserung der Lebensdauerabschätzung undzur Weiterentwicklung von Normen für korrosionsbeständigeBetonstähle und der Robustheitsbewertung von Spannstählenbei. N2 - Corrosion is a primary damage mechanism in reinforced concrete construction, significantly reducing the service life of infrastructure. A categorisation of corrosion is imperative for the comprehension of the subject. The corrosion of concrete can be attributed to the carbonation process, whilst chloride-induced corrosion is prevalent in structures exposed to seawater or by de-icing salt. Additionaly to the former corrosion processe, prestressing steel structures could be also highly susceptible to hydrogen-induced stress corrosion cracking (SCC). In order to utilise alternative reinforcing steels, such as stainless reinforcing steel, it is necessary to ascertain the level of critical chloride threshold that can induce corrosion. Nevertheless, there is an absence of standardised test methods for determining this for the respective reinforcing steels to date. Acc. to current standardization, the sensitivity of prestressing steels to chromium content necessitates long-term ageing tests, which impede in-house production control due to the extended testing times. However, a newly developed test method using cathodic polarization, which has now been included in the latest draft of DIN EN ISO 15630–3, makes it possible to assess the susceptibility of prestressing steels to corrosion cracking within 24 hours. The results of this study will contribute to the improvement of service life estimation and the further development of standards for corrosion-resistant reinforcing steels and the robustness assessment of prestressing steels. KW - Korrosion KW - Spannstahl KW - Nichtrostender Betonstahl KW - Corrosion KW - Prestressing steel KW - Stainless reinforcing steel KW - Wasserstoff KW - Spannungsrisskorrosion KW - Lochkorrosion KW - Hydrogen KW - Stress corrosion cracking KW - Pitting corrosion PY - 2025 DO - https://doi.org/10.1002/best.202500025 SN - 0005-9900 SN - 1437-1006 SP - 1 EP - 8 PB - Ernst CY - Berlin AN - OPUS4-63305 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialfeldmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu wird Stahl im Beton durch Ausbildung einer Deck-schicht vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisie-rung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich durch Volumenexpansion der Korrosionsprodukte korrosi-onsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwen-dige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte In-formationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeu-tung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beur-teilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korro-sion zum Einsatz. T2 - 3-Länder-Korrosionstagung CY - Zürich, Switzerland DA - 12.04.2018 KW - Korrosion KW - Corrosion KW - Potentialfeldmessung PY - 2018 SN - 978-3-935406-66-6 SP - 123 EP - 128 AN - OPUS4-44697 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Poptential Mapping at Concrete Structures N2 - Die Potentialfeldmessung dient der Lokalisierung aktiv korrodierender Betonstähle in Bauwerken. N2 - Potentialmapping is an electrochemical measurement for the detection of active corroding reinforcement at concrete structures. T2 - NDT&E Advanced Training Workshop 2017 CY - Berlin, Germany DA - 05.07.2017 KW - Corrosion KW - Poptential Mapping PY - 2017 AN - OPUS4-40941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Performance & Failure Mechanisms of Galvanic Anodes N2 - Galvanic anodes could be used in concrete structures to prevent new anode formation surrounding patch-repaired areas. Therefore so-called galvanic anodes need to be embedded into the fresh concrete with an electroconductive connection to the reinforcement. This anodic area will protect the surrounding reinforcement against forming other anodic areas. T2 - Pre-Consec Workshop 2024 CY - Chennai, India DA - 24.09.2024 KW - Corrosion KW - Galvanic anodes KW - Reinforcement KW - Pitting corrosion PY - 2024 AN - OPUS4-61307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Breit, W. T1 - Investigation of corrosion product layers in chloride containing mortars - "galvanized reinforcement" N2 - In the case of galvanised steel in mortar or concrete, the corrosion behaviour depends on the ion distribution of the pore solution and the pH value. Therefore, a new approach has been developed to determine the corrosion behaviour by single frequency AC measurements and to determine the B-values to calculate the corrosion current density using the Stern-Geary equation. T2 - ICCRRR 2024 CY - Cape Town, South Africa DA - 03.11.2024 KW - Corrosion KW - Galvanized steel PY - 2024 AN - OPUS4-61517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialmessung im Stahlbetonbau N2 - Durch das alkalische Porenwassermilieu wird Stahl im Beton durch Ausbildung einer Deckschicht vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich durch Volumenexpansion der Korrosionsprodukte korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. T2 - KKS-Messtechnik CY - Online meeting DA - 26.04.2021 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion PY - 2021 AN - OPUS4-52529 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Ermittlung kritischer Chloridgehalte in Beton mittels LIBS N2 - Es wurden elektrochemische und LIBS Untersuchungen verwendet um den kritischen Korrosion auslösenden Chloridgehalt in alkalischen und karbonatisierten Mörteln zu ermitteln. Ein deutliche Abhängikeit zwischen pH-Wert und Ccrit konnte dabei festgestellt werden. T2 - AK Prüf- und Untersuchungsverfahren CY - Online meeting DA - 18.06.2020 KW - Korrosion KW - Corrosion KW - Ccrit KW - LIBS PY - 2020 AN - OPUS4-50911 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas ED - Isecke, B. ED - Krieger, J. T1 - Detektion korrosionsaktiver Bereiche an Brückenbauwerken aus Stahlbeton mittels Potentialfeldmessung N2 - Durch das alkalische Porenwassermilieu wird Stahl im Beton durch Ausbildung einer Deckschicht vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich durch Volumenexpansion der Korrosionsprodukte korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaß-nahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. T2 - 4. Brückenkolloquium CY - Online meeting DA - 08.09.2020 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion PY - 2020 SN - 978-3-8169-3518-6 SN - 978-3-8169-8518-1 SP - 583 EP - 588 PB - expert CY - Tübingen AN - OPUS4-51218 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Seifert, Lando A1 - Müller, Thoralf T1 - Stress corrosion test in thiocyanate solution with galvanostatic current N2 - Prüfung von Spannstählen hinsichtlich ihrer Anfälligkeit gegenüber wasserstoffinduzierter Spannungsrisskorrosion in kürzeren Zeiträumen. Gewährleistung der Dauerhaftigkeit mittels neuartiger elektrochemischer Prüfverfahren und galvanostatischer Kontrolle und Wasserstoffbeladung T2 - Meeting ISO TC17 SC16 WG8 CY - Online meeting DA - 11.01.2023 KW - Hydrogen KW - Corrosion PY - 2023 AN - OPUS4-56854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Corrosion of Steel in Concrete and Corrosion Behavior of Stainless Steel N2 - In order to obtain a statement on the corrosion resistance of stainless steel against pitting corrosion, a well-tested measuring arrangement is required. For this purpose, the so-called ECISS test can be used to determine the critical chloride content. This makes it possible to assess the corrosion resistance of various stainless steels that have different chromium contents. T2 - ISO-TC17-SC16-WG13 Expertensitzung CY - Online meeting DA - 11.01.2022 KW - Corrosion KW - Lochkorrosion KW - Chloride induced corrosion KW - Concrete KW - Stainless steel PY - 2022 AN - OPUS4-54239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boschmann Käthler, C. A1 - Angst, U. A1 - Ebell, Gino A1 - Elsener, B. T1 - Chloride-induced reinforcement corrosion in cracked concrete: the influence of time of wetness on corrosion propagation N2 - Literature data on the influence of concrete cracks on corrosion propagation of reinforcing steel are contradictory. This might be due to very different exposure and test conditions but also to a lack of time-resolved data in cyclic wetting–drying exposure. Here, the influence of the environmental conditions on the corrosion rates in cracked concrete is studied experimentally. The results show that the corrosion rate in cracked concrete depends on the duration of wetting and drying phases and the relative humidity (RH) during the drying phase. The lower the ambient RH in the drying phase, the faster the cracks dry, which depresses the corrosion rate in the periods between the wetting events. A model is proposed to estimate corrosion rates in cracked concrete cyclic wetting/drying exposure. KW - Korrosion KW - Corrosion KW - Concrete PY - 2020 DO - https://doi.org/10.1080/1478422X.2020.1789371 SP - 1 EP - 11 PB - Taylor Francis Online CY - London AN - OPUS4-50986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite. T2 - ICCRRR 2022 CY - Capetown, South Africa KW - Corrosion KW - LIBS KW - Zinc KW - Anode PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560576 DO - https://doi.org/10.1051/matecconf/202236404023 SN - 2261-236X VL - 364 SP - 1 EP - 7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-56057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heyn, A. A1 - Meist, M. A1 - Michael, O. A1 - Babutzka, M. A1 - Valet, Svenja A1 - Ebell, Gino T1 - Electrochemical characterization of surfaces of galvanized steels under different exposure conditions using gel electrolytes N2 - The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values. KW - Materials Chemistry KW - Metals and Alloys KW - Surfaces, Coatings and Films KW - Mechanical Engineering KW - Mechanics of Materials KW - Environmental Chemistry KW - Corrosion KW - Znc PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599234 DO - https://doi.org/10.1002/maco.202414389 SP - 1 EP - 16 PB - Wiley VHC-Verlag AN - OPUS4-59923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Corrosivity of Atmospheres and the Resulting Corrosion Protection of Galvanized Steel N2 - The investigation of the corrosivity of atmospheres are major target to ensure the durability of metallic structures. Therefore the corrosivity has to be determined and finally, the right material or corrosion protection system has to be chosen. T2 - Forschungsbeiratssitzung des GAV CY - Darmstadt, Germany DA - 06.06.2024 KW - Corrosion KW - Potentialfeldmessung KW - Atmospheric corrosion PY - 2024 AN - OPUS4-60589 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Brem, M. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. T1 - Elektrochmische Potentialmessung zur Detektion von Bewehrungsstahlkorrosion N2 - Die Potentialmessung kann zum Auffinden korrosionsaktiver Bereiche neben Stahlbetonbauwerken auch bei Spannbetonbauwerken angewandt werden, die mit Spannstählen im direkten Verbund hergestellt werden. Bei Vorspannsystemen mit metallischen Hüllrohren im nachträglichen Verbund ist eine Aussage über den Korrosionszustand des Hüllrohrs, nicht aber des Spannstahls möglich. Messungen an Spannbetonbauteilen erfordern grundsätzlich die besonderen Kenntnisse eines Spezialisten. KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Concrete PY - 2021 SN - 978-3-947971-16-9 VL - Merkblatt B 03 SP - 1 EP - 22 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-53091 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Post-Treatment of galvanized reinforcement as prevention of hydrogen evolution in fresh concrete N2 - The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. It is important to investigate the critical conditions in the first hours following the pouring of the concrete. T2 - Eurocorr 2018 CY - Cracow, Poland DA - 09.09.2019 KW - Corrosion KW - Korrosion KW - Verzinkt KW - Betonstahl PY - 2018 AN - OPUS4-45944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Large scale reinforced concrete test specimen for potential mapping under practical conditions N2 - Electrochemical potential mapping according to guideline B3 of DGZfP German Society for Non- Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from e.g. stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. To investigate these influencing factors under practical conditions it requires a specimen with similar damage patterns, dimensions and more factors e.g. metallic mounting parts. Recently the BAM realized such a large scale test specimen for this purpose. T2 - NDE 2017 CY - Chennai, TN, India DA - 14.12.2017 KW - Potential mapping KW - Corrosion PY - 2017 UR - http://thehashtag.in/NDE17/chennai/wp-content/uploads/2017/12/Ebell-NDE-2017.pdf SP - 1 EP - 1 AN - OPUS4-43469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potential mapping at concrete structures N2 - Potentialmapping is an electrochemical measurement for the detection of active corroding reinforcement at concrete structures. T2 - NDT&E Workshop 2023 CY - Berlin, Germany DA - 23.06.2023 KW - Corrosion KW - Potentialfeldmessung PY - 2023 AN - OPUS4-57884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Zur Deckschichtbildung an feuerverzinkten Betonstählen in chloridhaltigen Mörteln N2 - Die Deckschichtbildung an feuerverzinkten Betonstählen in chloridhaltigen Mörteln oder Betonen unterscheidet sich hinsichtlich der Korrosionseigenschaften signifikant von chloridfreien Systemen. Diese Unterschiede wurden in der dargestellten Arbeit dezidiert untersucht und dargestellt, als auch die Wechselwirkung mit dem Mörtel bei direkter Chloridzugabe. T2 - GAV-Forschungbeiratssitzung CY - Aachen, Germany DA - 02.12.2024 KW - Corrosion KW - Galvanized steel KW - Korrosion PY - 2024 AN - OPUS4-62009 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Kosalla, M. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. A1 - Sodeikat, C. T1 - Specification B 12 - Corrosion monitoring in reinforced and prestressed concrete structures N2 - This specification describes how corrosion monitoring is used to check the condition of reinforced and prestressed concrete members. In this specification, the term "corrosion monitoring" covers all methods in which it is possible to continuously track corrosion-relevant variables in the area of stationary, built-in sensors. This specification does not cover other possible methods, such as potential field measurements, involving the use of mobile, portable sensors that are placed temporarily on the membersurface to take measurements. KW - Korrosion KW - Corrosion KW - Monitoring PY - 2021 SN - 978-3-947971-14-5 SP - 1 EP - 55 PB - DGZfP CY - Berlin AN - OPUS4-53092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Formation of Corrosion Product Layers on Galvanized Reinforcement in Chloride Containing Mortar N2 - To study a corrosion system such as galvanized steel in chloride containing mortars, more than just some electrochemical studies are required. The addition of chlorides by direct addition to the water will have an influence on the hardening process and consequently on the pore structure, and the investigation of these influences is necessary. Furthermore, a new approach has been investigated which is able to determine the corrosion rate in less than 30 seconds without influencing the corrosion system by intense polarization. T2 - Eurocorr 2024 CY - Paris, France DA - 01.09.2024 KW - Corrosion KW - Galvanized Steel KW - Verzinkt KW - Feuerverzinkt KW - Betonstahl KW - Korrosion PY - 2024 AN - OPUS4-60968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potential Mapping at Concrete Structures N2 - Potentialmapping is an electrochemical measurement for the detection of active corroding reinforcement at concrete structures. T2 - NDT&E Advanced Training Workshop 2018 CY - Berlin, Germany DA - 27.06.2018 KW - Corrosion KW - Potential mapping PY - 2018 AN - OPUS4-45356 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Lehmann, Jens A1 - Müller, Thoralf A1 - Meinel, Dietmar A1 - Paetsch, O. T1 - Investigation of chloride-induced pitting corrosion of steel in concrete with innovative methods N2 - The combination of electrochemical and 3D computed tomography (CT) investigations offers the possibility of verifying electrochemical measurements non-destructively. Determining the steel surfaces damaged by pitting corrosion allows developing specimens having damage pattern corresponding to practice. Corrosion phenomena like decoupled pitting corrosion cannot be verified by electrochemical measurements only, but with the combination of those two kinds of investigations it is possible. Another advantage is the minimization of the number of samples. The classical experimental procedure requires the destruction of samples after each damage step.This can be avoided by the use of 3D computed tomography. As long as the corrosion phenomena are completely within the examination zone shown by the 3D computed tomography, the electrochemical measurements can be calculated on an area basis to get the specific corrosion rate or polarization resistance. KW - Corrosion KW - Concrete KW - 3D x-ray KW - Corrosion rate PY - 2016 DO - https://doi.org/10.1002/maco.201608969 SN - 1521-4176 SN - 0947-5117 SN - 0043-2822 VL - 67 IS - 6 SP - 583 EP - 590 PB - Wiley-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-36341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stoljarova, A. A1 - Regenspurg, S. A1 - Bäßler, Ralph A1 - Mathiesen, T. A1 - Braüner Nielsen, J. T1 - Effect of lead and copper containing brine on steel materials for geothermal applications – A corrosion study N2 - Geothermal brines often contain high amounts of lead and copper ions that can precipitate as native Cu and Pb as consequence of galvanic corrosion when brines react with carbon steel materials. This contribution evaluates which materials could overcome the problem of galvanic corrosion at geothermal environment. The behavior of these materials in water containing high chloride concentration (> 100 g/L NaCl) as well as various amounts of dissolved bCl2 and/or CuCl2 was characterized by electrochemical and exposure measurements. Both methods reveal carbon steel suffers corrosion susceptibility, accompanied by Cu◦ and/or Pb◦ precipitation on the surface. Electrochemical measurements on stainless steels result in significant difference in corrosion and repassivation potentials (Ecorr = -189 mV, Erep = 70 mV), indicating a good corrosion resistance. KW - Copper KW - Lead KW - Corrosion KW - Steel KW - Geothermal energy PY - 2021 DO - https://doi.org/10.1016/j.geothermics.2020.102024 SN - 0375-6505 VL - 91 SP - NIL_75 EP - NIL_85 PB - Elsevier CY - Amsterdam AN - OPUS4-51976 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Faes, W. A1 - Lecompte, S. A1 - van Bael, J. A1 - Salenbien, R. A1 - Bäßler, Ralph A1 - Bellemans, I. A1 - Cools, P. A1 - de Geyter, N. A1 - Morent, R. A1 - Verbeken, K. A1 - de Paepe, M. T1 - Corrosion behaviour of different steel types in artificial geothermal fluids N2 - Geothermal energy is an interesting alternative to polluting fossil energy sources. Therefore, in Belgium, two wells have been drilled for a deep geothermal power plant. However, the environment to which the installations are exposed is challenging. The geothermal brine has 165 g/l total dissolved solids (of which 90% are sodium and chlorine) and the production temperature can be up to 130 °C. To assess their suitability to be used in a geothermal power plant, the corrosivity of the artificial brine to three common construction materials was investigated with exposure and electrochemical tests. The metals under consideration are a low-alloyed carbon steel (S235JR), an austenitic stainless steel (UNS S31603) and a duplex stainless steel (UNS S31803). The carbon steel, that was found to corrode uniformly, could be considered as a constructional material if a sufficient wall thickness is chosen. The austenitic stainless steel and the duplex stainless steel demonstrate very low uniform corrosion rates. They are however susceptible to pitting and crevice corrosion. To guarantee safe operation of the geothermal power plant, the susceptibility of the alloys to stress corrosion cracking should be tested and in situ experiments should be performed. KW - Geothermal energy KW - Corrosion KW - Carbon dioxide KW - Carbon steel KW - Stainless steel PY - 2019 DO - https://doi.org/10.1016/j.geothermics.2019.05.018 SN - 0375-6505 VL - 82 IS - 11 SP - 182 EP - 189 PB - Elsevier Ltd. AN - OPUS4-48759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Suitability of Metallic Materials in CC(U)S Applications N2 - Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited. (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv). Corrosion rates increase with increasing water content. (0.2 – 20 mm/a). Condensation of acids and therefore droplet formation is always possible, even at low water contents. A low SO2 content within the CO2-stream might be more important than a low water content. Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications. Low alloyed steels showed better corrosion behavior. � (predictable uniform corrosion) For direct contact with saline aquifer fluids only high alloyed steels shall be used. T2 - EUROCORR 2021 CY - Budapest, Hungary DA - 20.09.2021 KW - Carbon capture storage KW - Corrosion KW - Steel KW - CCS KW - CCU KW - CO2 PY - 2021 AN - OPUS4-53461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Electrochemical deposition of polyaniline on carbon steel for corrosion study in geothermal solution N2 - Polyaniline has been widely developed for many applications, e.g. sensor, supercapacitor components, electrochromic devices, and anticorrosion pigments. Although the addition of polyaniline pigment in organic coatings has been an alternative for corrosion protection in industrial applications, the protection mechanism is still not fully understood. Herein in this study, as a part of the development of polyaniline/silicon dioxide coating for geothermal application, polyaniline has been deposited electrochemically on carbon steel surface in oxalic acid medium and tested in geothermal solution to understand the contribution of polyaniline to the corrosion protection of a polyaniline-based composite in the geothermal system. To observe the surface/interface reaction between the electrolyte and electrode surface during the electrochemical polymerization, electrochemical impedance spectroscopy (EIS) was applied after each cycle. For corrosion study in the geothermal application, an artificial geothermal solution was used with the composition of 1,500 mg/l Cl⁻, 20 mg/l SO₄²⁻, 15 mg/l HCO₃⁻, 200 mg/l Ca²⁺, 250 mg/l K⁺, and 600 mg/l Na⁺, and pH 4 to simulate a geothermal brine found in Sibayak, Indonesia. An electrochemical measurement was performed by monitoring the open circuit potential over seven days, with the interruption by EIS every 22 hours. The experiments were performed at room temperature and 150 °C (1 MPa) in an oxygen-free environment. Impedance spectra showed a reduction of the total impedance value of approximately 10 times for specimens measured at 150 °C compared to the specimens measured at room temperature, suggesting a less stable layer at high temperature. KW - Corrosion KW - Electrochemical deposition KW - Polyaniline PY - 2019 DO - https://doi.org/10.4028/www.scientific.net/MSF.966.107 SN - 1662-9752 VL - 966 SP - 107 EP - 115 PB - Trans Tech Publications Ltd CY - Zürich AN - OPUS4-48776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Bäßler, Ralph T1 - Study of Al2O3 Sol-Gel Coatings on X20Cr13 in Artificial North German Basin Geothermal Water at 150 °C N2 - Al2O3 has been widely used as a coating in industrial applications due to its excellent chemical and thermal resistance. Considering high temperatures and aggressive mediums exist in geothermal systems, Al2O3 can be a potential coating candidate to protect steels in geothermal applications. In this study, γ-Al2O3 was used as a coating on martensitic steels by applying AlOOH sol followed by a heat treatment at 600 °C. To evaluate the coating application process, one-, two-, and three-layer coatings were tested in the artificial North German Basin (NGB), containing 166 g/L Cl−, at 150 °C and 1 MPa for 168 h. To reveal the stability of the Al2O3 coating in NGB solution, three-layer coatings were used in exposure tests for 24, 168, 672, and 1296 h, followed by surface and cross-section characterization. SEM images show that the Al2O3 coating was stable up to 1296 h of exposure, where the outer layer mostly transformed into boehmite AlOOH with needle-like crystals dominating the surface. Closer analysis of cross-sections showed that the interface between each layer was affected in long-term exposure tests, which caused local delamination after 168 h of exposure. In separate experiments, electrochemical impedance spectroscopy (EIS) was performed at 150 °C to evaluate the changes of coatings within the first 24 h. Results showed that the most significant decrease in the impedance is within 6 h, which can be associated with the electrolyte penetration through the coating, followed by the formation of AlOOH. Here, results of both short-term EIS measurements (up to 24 h) and long-term exposure tests (up to 1296 h) are discussed. KW - Al2O3 KW - Geothermal KW - Martensitic steels KW - Behmite KW - Corrosion PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-525551 DO - https://doi.org/10.3390/coatings11050526 SN - 2079-6412 VL - 11 IS - 5 SP - 526 PB - MDPI CY - Basel AN - OPUS4-52555 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -