TY - CONF A1 - Weltschev, Margit A1 - Hoffmann, Gabi T1 - Schadensursachen an Rohrleitungen N2 - Das Gefährdungspotential von Rohrleitungen hängt primär von den Eigenschaften des durchfließenden Stoffes, den Betriebsbedingungen und den äußeren Beanspruchungen ab. Zu den Hauptschadensursachen an Rohrleitungen zählen Korrosion, Druckstöße und Kavitationsschläge, Zeitstandbeanspruchung, struktur- und fluidmechanische Schwingungen, Fremdberührungen, elektrische Fremdbeeinflussung und geologische Besonderheiten im Bereich des Rohrleitungsverlaufes. T2 - Workshop:Anwendung der verteilten akustischen und faseroptischen Sensorik zur kontinuierlichen Überwachung von Rohrleitungen CY - Berlin DA - 01.03.2016 KW - Korrosion KW - Zeitstandbeanspruchung KW - Struktur- und fluidmechanische Schwingungen KW - Elektrische Fremdbeeinflussung PY - 2016 AN - OPUS4-35624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Planung und Betrieb von Trinkwasserinstallationen: Was uns das Regelwerk sagt N2 - Die gesetzlichen und technischen Regeln für Planung, Bau und Betrieb einer Trinkwasserinstallation werden dargestellt. Beispiele für einzelne Punkte werden gegeben. T2 - Der sichere Einsatz von Werkstoffen aus Kupfer und Kupferlegierungen in der Trinkwasserinstallation CY - Online meeting DA - 21.10.2020 KW - Trinkwasser KW - Werkstoffe KW - Korrosion KW - Hygiene PY - 2020 AN - OPUS4-51454 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Risikobewertung in der Trinkwasserinstallation N2 - Die Methode zur bewertung und Vermeidung von Risiken beim Betrieb der Trinkwasserinstallation wird dargestellt. Die vorgaben aus Gesetz, Regelwerk und anderen Vorschriften werden erläutert. Die grundsätzliche Philosophie der Vorgehensweise wird beschrieben. T2 - Drei-Länder-Korrosionstagung: Korrosion in der Infrastruktur CY - Online meeting DA - 28.10.2021 KW - Korrosion KW - Trinkwasser-Installation KW - Hygiene KW - Risikobewertung PY - 2021 AN - OPUS4-53655 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Planung und Betrieb von Trinkwasserinstallationen: Was uns das Regelwerk sagt N2 - Die gesetzlichen und technischen Regeln für Planung, Bau und Betrieb einer Trinkwasserinstallation werden dargestellt. Beispiele für einzelne Punkte werden gegeben. T2 - Der sichere Einsatz von Werkstoffen aus Kupfer und Kupferlegierungen in der Trinkwasserinstallation CY - Online meeting DA - 12.10.2021 KW - Hygiene KW - Korrosion KW - Trinkwasser KW - Werkstoffe PY - 2021 AN - OPUS4-53519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wagner, Adrian T1 - Auslagerung von nichtrostenden Stählen in Straßentunneln - Stand nach 3 Jahren N2 - Im Sinne einer mittel- bis langfristigen Reduktion wartungsbedingter Verkehrsbeeinflussungen in Tunnelbauwerken ist es von Bedeutung, die intensiven und aufwendigen Reinigungs- und Pflegearbeiten für Ein- und Anbauteile aus nichtrostendem Stahl in Straßentunneln zu reduzieren. Unter diesem Aspekt besteht großes Interesse die Einsatzmöglichkeiten alternativer nichtrostender Stähle, zu den bislang gebräuchlichen nichtrostenden austenitischen Stählen 1.4404 und 1.4571, zu eruieren. In dem Forschungsprojekt geht es um die Qualifizierung nichtrostender ferritisch austenitischer Stähle (Duplexstahl) in Straßentunneln. Diese verfügen im Vergleich zu austenitischen Stählen über eine doppelt so hohe Festigkeit bei gleichzeitig hoher Korrosionsbeständigkeit. In dieser Präsentation werden die Auslagerungsergebnisse nach 3 Jahren vorgestellt. T2 - Vorstellung der 3 Jahres Ergebnisse beim VDEh in Düsseldorf CY - Düsseldorf DA - 04.08.2021 KW - Duplex KW - Tunnelbauwerke KW - Korrosion KW - Korrosivität KW - Straßentunnel KW - Lean-Duplex PY - 2021 AN - OPUS4-53068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wagner, Adrian T1 - Korrosionsmonitoring bei der Instandsetzung von chloridbelasteten Stahlbetonwerken N2 - In der aktuellen RL-SIB (DAfStB) wie auch in der TR Instandsetzung (DIBt) ist bei Anwendung des Instandsetzungsprinzips W-CL der Erfolg der Maßnahme durch Einbau und Messung von Korrosionsstromsensoren gefordert. Art und Aufbau der Sensoren sowie Kriterien zur Bewertung der Ergebnisse gibt es nicht. Ziel ist die Ausarbeitung eines Regelwerks-Entwurfes für die Art und den Aufbau von Korrosionsmonitoring-Systemen sowie für Kriterien zur zuverlässigen Bewertung der Messergebnisse, mit denen der Erfolg bei verschiedenen Instandsetzungskonzepten überprüft werden kann. T2 - 3. PA Sitzung WIPANO Projekt KoMICS CY - Berlin, Germany DA - 17.11.2021 KW - Korrosion KW - Korrosionsmonitoring KW - Sensoren KW - Chloridhaltiger Beton KW - Instandhaltung PY - 2021 AN - OPUS4-53782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Update nach 10 Jahren Bewitterung - Langzeitkorrosionsverhalten nichtrostender Stähle in maritimer Atmosphäre N2 - Durch Fortführung der Untersuchungen aus einem Forschungsvorhaben wurden neun verschiedene Stahllegierungen unter maritimen Umgebungsbedingungen über zehn Jahre ausgelagert und deren Korrosionsverhalten untereinander verglichen und bewertet. Anhand der Ergebnisse der Auslagerungsprüfungen konnten Rückschlüsse auf die Einflüsse der Legierungszusammensetzung, der Oberfächenausführung und der Auslagerungszeit unter maritimen Auslagerungsbedingungen gewonnen werden. Die Proben der drei untersuchten Duplexwerkstoffe zeigten über den Auslagerungszeitraum von zehn Jahren sowohl mit als auch ohne Spaltgeometrie die beste Korrosionsbeständigkeit. Ebenso konnte der molybdänlegierte Ferrit 1.4521 eine vergleichbar gute Korrosonsbeständigkeit erzielen, wie die klassischen austenitischen Werkstoffe 1.4301 und 1.4404. T2 - Korrosionsschutz in der maritimen Technik 2022 CY - Online meeting DA - 27.01.2022 KW - Auslagerungsversuche KW - Korrosionsschutz KW - Korrosion KW - Nichtrostende Stähle PY - 2022 AN - OPUS4-54276 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf T1 - Kurzbericht aus den DIN Ausschüssen N2 - Der Vortrag gibt einen Überblick über die Tätigkeiten der DIN-Ausschüsse "Korrosionsprüfverfahren" sowie "Korrosion und Korrosionsschutz". Es werden neuste Informationen zum Stand verschiedener Normen aus den beiden Ausschüssen gegeben. T2 - Arbeitskreissitzung des GfKorr-Arbeitskreises Korrosionsuntersuchung und -überwachung CY - Leipzig, Germany DA - 21.03.2023 KW - Korrosion KW - Normung KW - Korrosionsprüfung KW - Korrosionsschutz PY - 2023 AN - OPUS4-57243 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens T1 - 1. Sitzung GfKORR AK "Atmosphärische Korrosion" N2 - Eine Übersicht zu den Zielen und Schwerpunktthemen des neu gegründeten Arbeitskreises Atmosphärische Korrosion. T2 - 1. Sitzung des GfKORR Arbeitskreises Atmosphärische Korrosion CY - Online meeting DA - 25.01.2023 KW - Korrosion KW - Atmosphäre KW - Luftqualität KW - Auslagerungsversuche PY - 2023 AN - OPUS4-57022 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wiederholt, Wilhelm A1 - Sonntag, J. T1 - Korrosion von Metallen im Bauwesen N2 - In Berührung mit Gips waren Blei, Aluminium und die Aluminiumlegierung AlMg genügend beständig, trotzdem versagte der galvanische Bleiüberzug als Schutz von Stahl, da der Überzug zu dünn und porenhaltig war, so daß die Korrosion durch Elementbildung Blei/Stahl nur gefördert wurde. Stahl und Zink werden von Gips stark angegriffen. Dementsprechend ist von Zinküberzügen auch nur solange eine Rostverhinderung zu erwarten, bis der Überzug aufgebraucht ist. Diese Schutzwirkung ist unabhängig von der Art des Aufbringens der Überzüge; sie gilt also sowohl für Zinküberzüge nach dem Schmelztauchverfahren als auch für solche nach Spritz- bzw. galvanischen Verfahren. Durch das Phosphatieren wurde der Angriff von Gips auf Zink nur verzögert, während schon durch Phosphatieren und Ölen ein beachtenswerter Schutz erreicht wurde. Besonders zweckmäßig erwies sich auch das Chromatieren von galvanisch verzinkten Stahlblechen, die nach 12monatiger Beanspruchung noch eine gute Schutzwirkung aufwiesen. Als Schutz gegen die Einwirkung von Gips haben sich ferner Anstriche bewährt, von denen Chlorkautschuk-, Alkydharz-, Rostschutzmennige-, Ölfarben- und Bitumenanstriche bereits auf den blanken Stahlblechen die Rostbildung verhinderten. Eine genügende Schutzwirkung war auch dann vorhanden, wenn der Deckanstrich beschädigt war. Rost wurde nur nach 50monatiger Versuchsdauer bei der Probe mit dem Chlorkautschukanstrich festgestellt. Im Verhalten der verschiedenartigen Werkstoffe in Berührung mit Gips einerseits und Gipssandmörtel andererseits konnten keine merklichen Unterschiede festgestellt werden. Das für Gips beschriebene Verhalten gilt demnach auch für das Verhalten der Proben in Gipssandmörtel. Von Kalkmörtel wurde Stahl nur verhältnismäßig wenig angegriffen. Noch günstiger verhielten sich Zink und Blei, während auf Aluminium und der Aluminiumlegierung AlMg starke, gleichmäßig ausgebildete Verkrustungen hervorgerufen wurden. Die Rostbeständigkeit von Stahl konnte durch Phosphatieren, durch Feuerverzinken, durch galvanisches Verzinken und Chromatieren sowie durch Spritzverzinken noch wesentlich verbessert werden. Diese Proben blieben bis zur 12monatigen Versuchsdauer rostfrei. Nach 50monatiger Versuchsdauer versagte jedoch die Schutzwirkung der eingeölten Phosphatschicht auf Stahl. Blanke Zinkbleche sowie solche, die phosphatiert bzw. phosphatiert und geölt waren, wurden 12 Monate lang nicht angegriffen. Erst dann konnten geringe Mengen von weißlichen Korrosionsprodukten aus Zinkverbindungen und eine leichte Verkrustung ihrer Oberflächen festgestellt werden. Der galvanische Bleiüberzug auf Stahl hatte nur eine etwas verzögernde rostverhindernde Wirkung. Als Rostschutz bewährten sich auch die bereits genannten Anstrichsysteme bis zu einer Versuchsdauer von 12 Monaten, dann traten insbesondere bei den nicht besonders vorbehandelten Stahlblechen Rosterscheinungen auf, die trotz Alkydharzlack und Bleimennigeanstrichs zu starken Zerstörungen der Oberfläche führten. Durch die Vorbehandlung vor dem Aufbringen der Anstriche durch Phosphatieren bzw. durch Reaktionsgrundierung konnte die Schutzwirkung auch bei diesen Anstrichen wesentlich verbessert werden. Bei den Aluminiumproben wurden durch die Anstriche die Verkrustungen der Oberfläche verhindert. Bei der Einwirkung von Kalkmörtel insbesondere auf die blanken Metalle konnte noch festgestellt werden, daß der Angriff an der Grenze Kalkmörtel/Luft begann. War die Einwirkung gering, so beschränkten sich die Veränderungen auf einen schmalen Streifen in dem Grenzgebiet. Mit fortschreitender Versuchsdauer breitete sich dieser Streifen, insbesondere bei Stahl, von der Oberfläche ausgehend gleichmäßig nach dem Inneren zu aus. Einzelheiten hierüber sind in der Tabelle aufgeführt. Auch an Lichtbildern kann das Fortschreiten des Angriffs mit der Zeitdauer deutlich verfolgt werden. Bei Kalkmörtel der verwendeten Mischung und Körnung ist somit damit zu rechnen, daß mit der Zeit Feuchtigkeit in die Grenzschicht zwischen Kalkmörtel und Metall eindringt. Zur Verhütung der Korrosion ist deshalb an den Übergangsstellen Kalkmörtel/Luft für eine dichte und sorgfältige Abdichtung zu sorgen. Durch Zusatz des Frostschutzmittels wurde die angreifende Wirkung des Kalkmörtels deutlich erhöht. Diese wirkte sich besonders bei den reinen Metallen aus. Im Beton verhielten sich im ungeschützten Zustand Stahl und Zink gut. Auf Aluminium und der Aluminiumlegierung AlMg wurden ähnlich wie in Kalkmörtel starke Verkrustungen festgestellt. Auf Blei bildete sich eine Schutzschicht. Nur am Übergang Beton/Luft konnte sich durch die speziellen Angriffsbedingungen die Schutzschicht nicht ausbilden, so daß hier die Oberfläche stärker angegriffen wurde. Zinküberzüge, die nach den verschiedenen Verfahren aufgebracht worden waren, und die galvanische Verbleiung erwiesen sich als Schutz gegen die Einwirkung von Beton nicht als vorteilhaft. Dagegen trat bei den phosphatierten Stahlblechen kein Rost auf. Durch das Phosphatieren von Zink wurde die Verkrustung begünstigt. Das Chromatieren bzw. Eloxieren von Aluminium und von der Aluminiumlegierung AlMg hatten auf die Verkrustung nur geringen Einfluß. Durch die Anstriche konnte die Krustenbildung auf Aluminium und der Aluminiumlegierung weitgehend verhindert werden. Auf eloxiertem Untergrund bewährte sich hier besonders der Chlorkautschukanstrich. Auch bei Beton wurde durch den Zusatz des Frostschutzmittels in den meisten Fällen der Angriff deutlich verstärkt. Ungünstig war die Wirkung vor allem dann, wenn statt des ebenmäßigen Angriffs die Korrosion punktförmig auftrat. Die ungünstige Wirkung des Zusatzes von Frostschutzmitteln konnte weitestgehend durch Anstriche ausgeschaltet werden, wenn die Bleche durch Phosphatieren vorbehandelt bzw. eine Reaktionsgrundierung erfolgt war. Besonders kraß machte sich die ungünstige Wirkung des Frostschutzmittelzusatzes bemerkbar bei den Stahlblechen, die verzinkt bzw. verbleit waren und auch bei den nicht vorbehandelten Blechen. Während Stahl in Kalkmörtel und Beton im allgemeinen beständig ist, können bei Gegenwart von Feuchtigkeit, die durch ausgelaugte Stoffe aus den Baumaterialien alkalisch reagiert, Anstriche zerstört und anorganische Schutzschichten angegriffen werden. Die bei den Versuchen verwendeten Anstriche, insbesondere der Chlorkautschuk- und der Alkydharzanstrich, waren deshalb gewählt, weil sie eine gewisse Alkalibeständigkeit aufweisen. Diese Alkalibeständigkeit wurde durch die Versuche bestätigt. Der Rostschutzmennigeanstrich und die weiße Ölfarbe bewährten sich unter diesen Beanspruchungen nicht ganz so gut. Aus den Untersuchungen folgt noch, daß die Stellen, an denen die Bleche aus dem Baustoff heraustreten, besonders korrosionsgefährdet sind. Von diesen Stellen aus kann die Korrosion nach dem Inneren des Bauwerkes hin vordringen. Außerdem wird die Korrosionsgefahr dann erhöht, wenn aus den Baustoffen alkalische Stoffe vollständig ausgelaugt werden, so daß bei erneutem Zutritt von Feuchtigkeit keine alkalische Wirkung und damit kein Schutz für Stahl vorhanden ist. Auch hierüber sind im Bericht Beispiele vorhanden. Zusammenfassend folgt aus den Untersuchungen, daß Konstruktionen aus Stahl und anderen Metallen, die von Gips, Kalkmörtel oder Beton umgeben sind und teilweise aus den Baustoffen herausragen, durch metallische oder organische Überzüge mit genügender Sicherheit vor Korrosion geschützt werden können. N2 - Lead, aluminium and the aluminium alloy AlMg were sufficiently corrosion-resistant in contact with gypsum plaster. The galvanically applied lead coating failed to function as a protection for steel as it was too thin and porous. Steel and zinc were strongly attacked by gypsum plaster. Phosphate treatment and oil-impregnation imparted a considerable protection. Chromate treatment of steel sheets with galvanically applied zinc coat proved to be particulary useful. In addition, applications of chlorcaoutchouc, alkydresin, red-lead, oil and bitumen paints have proved to impart adequate protection against gypsum plaster. The behaviour as described for gypsum plaster holds also for the behaviour for the samples in sand-plaster mortars. The reaction of lime mortar on steel was relatively mild. Zinc and lead fared yet better, whereas heavy and uniformly disposed incrustations were produced by lime mortar on aluminium and the aluminium alloy AlMg. The rust-resistance of steel could be substantially improved through phosphate-treatment, hot-dip galvanizing, electrogalvanizing and chromate treatment as well as through spray-galvanizing. Untreated zinc sheets, and those which were phosphate-treated only after 12 month, showed signs of a build-up of small amounts of whitish corrosion products and a light incrustation on the surface. The paints already mentioned, proved to be effective as rustresisting coats for up to a study period of 12 months. A preparation of the metal surface prior to the paint application through phosphate treatment or through the use of a wash-primer could substantially enhance the protective effect. Surface incrustation of aluminium samples was prevented through the application of paints. For non-protected metals placed in contact with lime mortar the attack began at the mortar-air boundary. With advancing test-age the corrosion extended uniformly toward the inner portions. For preventing corrosion therefore, the transition areas between lime mortar and air are to be carefully sealed. The corrosive effect of lime mortar was markedly enhanced with use of anti-frost additives. In concrete, untreated steel and zinc behaved satisfactorily. Heavy incrustation was noted on aluminium and on aluminium alloy AlMg in concrete, similar to the action of lime mortar. On lead, a protective layer was formed. Zinc-plating and aglvanically applied lead coating did not prove to be advantageous against the action of concrete. Phosphate treatment favoured the formation of corrosion scales on zinc. Chromate treatment and anodization hat very little effect on the scale formation. Application of paints prevented to a large extent the formation of corrosion scales on aluminium and the aluminium alloy. Also in concrete, the use of anti-frost additives caused in most of the cases an intensification of corrosive action. In many cases the corrosive attack was concentrated on several points. The unfavourable effect of the use of anti-frost additives could be to a great extent eliminated through the application of paints, when a surface preparation either through phosphate-treatment or through an application of a wash-primer was carried out beforehand. Particularly intense was the unfavourable effect of the anti-frost additives on galvanised or lead-plated steel sheets, and those which were not subjected to a pretreatment. The alcali-resistant properties of the chlorcaoutchouc and the alkyd-resin paints were proved by the experiments. The red-lead paints for rust-protection and the oil-paints did not prove to be so good under these conditions. A further conclusion, that can be drawn from the investigations, is, that those parts of the sheets which are not surrounded by the corrosion causing material, are particulary susceptible to corrosion. Further, the susceptibility to corrosion is increased when the building materials are completely freed or washed clean of their alcaline contents, so that no alcaline activisation by renewed entry of moisture, and as a result, no protection of steel is possible. Examples of this phenomenon have been included in this report. To sum up, it follows from the investigations, that structures of steel and other metals, which are encased in gypsum plaster, lime mortar or concrete with parts of them exposed, can be protected against corrosion by metallic or organic coatings with sufficient safety. KW - Korrosion KW - Metall KW - Bauwesen KW - Schutzüberzug KW - Gips KW - Mörtel KW - Beton PY - 1965 SN - 0409-1108 N1 - Untersuchungen über das Verhalten von Metallen ohne und mit Schutzüberzügen, die in Gips, Mörtel oder Beton ohne und mit Frostschutzmitteln eingebettet waren; durchgeführt im Auftrag des Bundesministers für Wohnungswesen, Städtebau und Raumordnung von der Bundesanstalt für Materialprüfung, Berlin-Dahlem. VL - 44 SP - 1 EP - 62 PB - Ernst CY - Berlin AN - OPUS4-60498 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas T1 - Korrosion und Korrosionsschutz metallener Werkstoffe- elektrochemische Grundlagen N2 - Ausgehend von den Grundlagen der Korrosion stellt der Vortrag die Möglichkeiten des Korrosionsschutzes mit Zink vor. Dabei wird sowohl auf den kathodische Korrosionsschutz mit aktiven Zink-Anoden, als auch auf den Korrosionsschutz durch Deckschichtbildung an Zink und Zinküberzügen eingegangen. Veränderte Umweltbedingungen in Europa in den letzten Jahrzehnten, ermöglichen mit Schichtdicken um 80 µm einen Korrosionsschutz von über 100 Jahren, wenn konstruktive Randbedingungen beachtet werden. T2 - Seminar VSVI-NRW: KKS-Kostensenkung und Kilmaschutz im konstruktiven Ingenieurbau CY - Bochum, Germany DA - 25.06.2024 KW - Korrosion KW - Korrosionsschutz KW - Zinküberzüge KW - Dauerhaftigkeit PY - 2024 AN - OPUS4-60483 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul T1 - Korrosionsbeständige Stähle II - Korrosionserscheinungen und Werkstoffklassen - N2 - Der Vortrag behandelt zunächst die wichtigsten lokalen Korrosionserscheinungen (Spaltkorrosion, Interkristalline Korrosion, Lochkorrosion und Spannungsrisskorrosion), die bei korrosionsbeständigen (nichtrostenden) Stählen auftretenden können und gibt wichtige Hinweise zu deren Vermeidung. Außerdem werden die verschiedenen Werkstoffklassen (Ferrite, Austenite, Martensite und Duplexstähle) im Bereich der nichtrostenden Stähle vorgestellt und auf die Eigenschaften und Besonderheiten eingegangen. T2 - Vortrag in der Vorlesung „Spezielle Werkstoffe“ an der Otto-von-Guericke-Universität CY - Magdeburg, Germany DA - 16.11.17 KW - Korrosion KW - Nichtrostender Stahl KW - KorroPad KW - Lochkorrosion KW - Interkristalline Korrosion KW - Spaltkorrosion KW - Korrosionsschutz KW - Werkstoffklassen PY - 2017 AN - OPUS4-43140 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul T1 - KorroPad-Prüfung - Anwendungen aus Industrie und Forschung - N2 - Mit der KorroPad-Prüfung kann die Lochkorrosionsbeständigkeit nichtrostender Stähle auf sehr einfache, schnelle und kostengünstige Weise eingeschätzt werden. Das Kor-roPad ist damit für Hersteller, Verarbeiter und Anwender nichtrostender Stähle eine interessante Alternative zu zeitintensiven Langzeitversuchen und komplexe elektrochemischer Untersuchungsmethoden. Die prinzipiellen Funktionsweise der KorroPad-Prüfung wird im Vortrag beschrieben, um anschließend verschiedene Anwendungen aus Industrie und Forschung vorzustellen. Exemplarisch werden dazu die Bewertung von Schleif- und Passivierungsprozessen, die Qualitätskontrolle der Wärmebehandlung und Oberflächenbearbeitung von Schneidwaren sowie die Optimierung der Schweißnaht-Nachbehandlung vorgestellt. Mit der KorroPad-Prüfung lassen sich aber auch werkstoff- und gefügebedingte Einflüsse auf die Lochkorrosionsbeständigkeit gezielt untersuchen. Dies wird an Beispielen aus aktuellen Forschungsprojekten dargestellt. Die abschließend dargestellte Charakterisierung vom Sensibilisierungsverhalten mit der KorroPad-Prüfung ist verdeutlicht das breite Anwendungsspektrum bei der Charakterisierung von nichtrostenden Stählen. T2 - Arbeitskreissitzung „Korrosionsuntersuchung und -überwachung“ des GfKORR e. V. CY - Magdeburg, Germany DA - 21.11.2017 KW - Korrosion KW - Nichtrostender Stahl KW - KorroPad KW - Schneidwaren KW - Oberflächenbehandlung KW - Lochkorrosion KW - Wärmebehandlung KW - Sensibilisierung KW - EPR PY - 2017 AN - OPUS4-43141 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul T1 - Referenzmaterialien für die Charakterisierung nichtrostender Stähle N2 - Im Vortrag wird ein innovativer Ansatz zur Herstellung von Referenzmaterialien für systematische Grundlagenuntersuchungen und Methodenentwicklungen vorgestellt. Dieser Ansatz basiert auf der Verwendung eines Lichtbogenschmelzofens (Arc-Melter), der zur Legierungsvariation bei nichtrostenden Stählen verwendet wurde. In Abhängigkeit vom Chromgehalt wurden zunächst Ergebnisse der elektrochemisch potentiodynamischen Reaktivierung (EPR) und der KorroPad-Prüfung vorgestellt, die neue Einblicke zur Nachweisgrenze beider Verfahren liefern. Anschließend wurde der Einfluss vom Schwefelgehalt auf die Lochkorrosionsbeständigkeit dargestellt und dabei gezeigt, dass die in den Normen festgeschriebenen Grenzwerte deutlich zu hoch sind. Darüber hinaus wurden zukünftig geplante Arbeiten vorgestellt, die mit diesem Ansatz möglich sind. T2 - Arbeitskreissitzung „Korrosionsuntersuchung und -überwachung“ des GfKORR e. V. CY - Magdeburg, Germany DA - 21.11.2017 KW - Referenzmaterialien KW - Lichtbogenschmelzofen KW - Nichtrostender Stahl KW - Korrosion KW - KorroPad KW - EPR KW - Nachweisgrenze KW - Lochkorrosion PY - 2017 AN - OPUS4-43142 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul T1 - Wärmebehandlung und Korrosionsbeständigkeit druckaufgestickter nichtrostender Stähle N2 - Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Insbesondere der Einfluss von Warmauslagerungsversuchen nach dem Abschrecken wird dabei charakterisiert. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden (EPR, KorroPad, Lochkorrosionspotentiale) ermittelt und interpretiert. T2 - Werkstoffwoche 2017 CY - Dresden, Germany DA - 27.09.2017 KW - Wärmebehandlung KW - Korrosion KW - Nichtrostender Stahl KW - EPR KW - KorroPad KW - Sensibilisierung KW - Stickstoff KW - ThermoCalc PY - 2017 AN - OPUS4-42831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, C. T1 - Wärmebehandlung und Korrosionsbeständigkeit druckaufgestickter nichtrostender Stähle N2 - Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden ermittelt und interpretiert. T2 - GfKORR-Jahrestagung 2017 CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Wärmebehandlung KW - Korrosion KW - Nichtrostender Stahl KW - EPR KW - KorroPad KW - Sensibilisierung KW - Stickstoff KW - ThermoCalc PY - 2017 AN - OPUS4-42833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kauss, N. A1 - Rosemann, Paul T1 - Sensibilisierungsverhalten vom nichtrostenden Lean-Duplexstahl 1.4062 N2 - Der nichtrostende Lean-Duplexstahl 1.4062 (X2CrNiN22-2) verbindet die hohe Festigkeit des Ferrits mit der Duktilität und Zähigkeit des Austenits in einem zweiphasigen Gefüge mit sehr hoher Korrosionsbeständigkeit. Die höchste Korrosionsbeständigkeit wird erreicht, wenn das ferritisch-austenitische Gefüge frei von weiteren Sekundärphasen ist. Dies wird durch ein gezieltes Lösungsglühen bei 1050 °C mit anschließender Abschreckung in Wasser erreicht. Durch thermische Beeinflussung (z.B. beim Schweißen) können Sekundärphasen ausgeschieden und die Korrosionsbeständigkeit des Werkstoffs gesenkt werden. Dies wurde durch eine isotherme Warmauslagerung bei 500 °C bis 900 °C für 0,1 h bis zu 72 h simuliert. Die Veränderung der Korrosionsbeständigkeit wurde mit dem DL-EPR-Verfahren und durch die angepasste KorroPad-Prüfung ermittelt. Die ermittelten Anfälligkeitsbereiche wurden miteinander Verglichen und in zwei Sensibilisierungsschaubildern zusammengefasst. T2 - GfKORR-Jahrestagung CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Duplexstahl KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - EPR KW - KorroPad KW - Sensibilisierung PY - 2017 AN - OPUS4-42834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Baumann, O. A1 - Müller, C. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials). T2 - Materials Science and Engineering 2018 (MSE) CY - Darmstadt, Germany DA - 26.09.2018 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - KorroPad PY - 2018 AN - OPUS4-46090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar T1 - Analyse von Schädigungsprozessen in Beton - Was leistet die CT? Teil 2: Analyse der CT-Daten N2 - Der rekonstruierte CT-Datensatz liefert Informationen über die Dichteverteilung im Untersuchungsobjekt in Form einer Grauwertedarstellung. Zur quantitativen Bestimmung der anhand der Grauwertunterschiede separierbaren Strukturen bedarf es einer genauen Determinierung der diese Strukturen abgrenzenden Übergänge. Am Beispiel der Oberflächenbestimmung an einer Stahlbetonprobe wird der Unterschied zwischen globalem und lokalem Schwellwert gezeigt. Die so erzeugten Oberflächen dienen dem dimensionellen Messen innerhalb des CT-Datensatzes, dem Fitten von Regelgeometrien oder der Durchführung automatischer Analysen (Poren, Wandstäken, Faserorientierung). Zur Reduzierung der Datenmenge und zur Verwendung in Simulationsprogrammen können die gefundenen Oberflächen auch in ein Netzmodell überführt werden. Gezeigt wird der Einsatz dieser Techniken an Untersuchungen von Betonproben in der BAM. T2 - Summer School im Rahmen des DFG Schwerpunktprogramms 2020 "Zyklische Schädigungsprozesse in Hochleistungsbetonen im Experimental-Virtual-Lab" CY - Hotel Park Soltau, 29614 Soltau, Germany DA - 25.06.2018 KW - Computertomographie KW - In-situ CT KW - Bildverarbeitung KW - Beton KW - Korrosion PY - 2018 AN - OPUS4-45431 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul T1 - Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit von nichtrostenden Duplexstählen N2 - Der Duplexstahl 1.4062 (X2CrNiN22-2) hat sich im Bauwesen als Werkstoffalternative zu den nichtrostenden Austeniten etabliert. Die Korrosionsbeständigkeit von Schweißverbindungen wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Oberflächennachbehandlung der Schweißnaht beeinflusst. Je nach zukünftigem Anwendungsbereich und geforderter Optik sowie Korrosionsbeständigkeit wird der Schweißnahtbereich anschließend geschliffen, gebeizt, elektropoliert, oder gestrahlt, um die beim Schweißen entstehenden Zunderschicht zu entfernen. Gestrahlte Oberfläche sind in der industriellen Praxis häufig anzutreffen, da sie deutlich einfacher und kostengünstiger herzustellen sind als gebeizte oder elektropolierte Oberflächen. Die Auswahl des Strahlmittels bestimmt auch die Prozesskosten, wobei das Strahlen mit Korund effektiver als das Strahlen mit Glasperlen ist. In den letzten Jahren wurden bei nichtrostenden Stählen korrosionsanfällige Oberflächen beobachtet, wenn diese mit Korund geschliffen wurden. Daher wird nun auch beim Strahlen kritisch hinterfragt, ob das Strahlmittel die Korrosionsbeständigkeit verändert. Diese Fragestellung wird beantwortet indem geschliffene, gebeizte, mit Korund gestrahlte und mit Glasperlen gestrahlte Schweißverbindungen vergleichend untersucht werden. Die Ergebnisse der REM-Untersuchungen von den Strahlmitteln und den gestrahlten Oberflächen werden dazu mit den Ergebnissen verschiedener Korrosionsuntersuchungen (KorroPad-Indikatortest, Potentialmessungen und Bestimmung der kritischen Lochkorrosionspotentiale) korreliert und vorgestellt. T2 - Werkstoffwoche 2017 CY - Dresden, Germany DA - 27.09.2017 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Oberflächenbearbeitung KW - Schweißen KW - Strahlen PY - 2017 AN - OPUS4-42830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens T1 - Forschungsbericht VH 7604 - Teil 2: Ergebnisse zum Korrosionsverhalten nichtrostender Stähle in den beprobten Straßentunneln N2 - In Straßentunneln sind nichtrostende Stähle weitverbreitete Werkstoffe, die für Konstruktionsteile verschiedenster Art verwendet werden. Straßentunnel sind aus Sicht des Korrosionsschutzes sehr speziell und zählen in Mitteleuropa zu den korrosivsten atmosphärischen Umgebungsbedingungen. Die hier vorgestellten Ergebnisse eines gemeinsamen Forschungsvorhabens von Straßen.NRW, der Bundesanstalt für Materialforschung und -prüfung (BAM), LSBG-Hamburg sowie weiteren Partnern, zeigen geeignete Duplexstähle für Straßentunnelanwendungen. Hierfür wurde eine breit angelegte Parameterstudie durchgeführt und seit 2017 die Korrosionsbedingungen in mehreren Tunneln umfassend untersucht. Die Korrosivität der Tunnelatmosphären wurden anhand normativer Regelwerke bewertet und dem Korrosionszustand von Prüfkörpern aus nichtrostenden Stählen gegenübergestellt. T2 - Infotag "Dauerhaftigkeit der Betriebs- und Sicherheitsausstattung im Straßentunnel" CY - Düsseldorf, Germany DA - 13.02.2025 KW - Korrosion KW - Tunnel KW - Atmosphärische Korrosion KW - Nichtrostender Stahl KW - Edelstahl rostfrei KW - ZTV-ING PY - 2025 AN - OPUS4-62551 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -