TY - GEN A1 - Durlo Tambara, Luís Urbano A1 - Dehn, F. A1 - Gluth, Gregor ED - D’Erme, C. ED - Paglia, C. ED - Cordero, E. G. T1 - The importance of leaching for the carbonation resistance of alkali-activated slag and calcined clay concretes N2 - This study investigates the impact of leaching on the carbonation resistance of alkali-activated materials with varying calcium content. Six binder compositions were tested, combining ground blast furnace slag and calcined clay, with CaO content ranging from ~0% to ~40%. Samples underwent three conditions: no leaching, two weeks of leaching (2Le), and five leaching-carbonation cycles (5LCC). Carbonation tests were performed under natural conditions and 1% CO2 for reference and 2Le samples, while 5LCC samples were exposed solely to accelerated carbonation. Under natural carbonation, the typical relationship between carbonation resistance and the water/(CaO+MgOeq+Na2Oeq+K2Oeq) ratio was observed for both the reference and 2Le samples, with an increase in carbonation rate in compositions containing more than 40% calcined clay. In accelerated carbonation conditions, 2Le and 5LCC conditions showed slightly improved carbonation resistance compared to the reference samples, except for the mixtures containing only calcined clay (C100) and the mix with 40% calcined clay (C40S60). The poor performance of C100 was attributed to its low reactivity after 28 days, which resulted in significant sodium leaching and reduced activation of the calcined clay. Although C40S60 outperformed non-leached samples, its carbonation resistance slightly decreased in leached and accelerated carbonation samples due to reduced gel phase formation; however, this reduction was significantly less than that of C100. These findings suggest that while leaching can enhance carbonation resistance by reducing excess alkalis, low-reactivity systems, e.g. based solely on calcined clay, are more susceptible to degradation. KW - Carbonation KW - Alkali-activated materials KW - Leaching KW - Durability KW - Calcined clay PY - 2026 SN - 978-3-032-14170-5 DO - https://doi.org/10.1007/978-3-032-14170-5_16 SP - 148 EP - 157 PB - Springer CY - Cham AN - OPUS4-65355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hlavacek, Petr A1 - Gluth, Gregor A1 - Lüchtenborg, Jörg A1 - Sturm, Patrick A1 - Mühler, T. A1 - Kühne, Hans-Carsten A1 - Günster, Jens T1 - A Novel Approach to Additive Manufacturing of Alkali-activated Materials: Laser-induced Slip Casting (LIS) of Lithium Aluminate/Silica Slurries N2 - Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles. KW - Laser-induced slip casting KW - Alkali-activated materials KW - Additive manufacturing PY - 2019 DO - https://doi.org/10.29272/cmt.2018.0011 SN - 2612-4882 VL - 1 IS - 2 SP - 138 EP - 144 PB - Techna Group AN - OPUS4-49142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Durlo Tambara, Luís Urbano A1 - Nikoonasab, Ali A1 - Radtke, Martin A1 - de Oliveira Guilherme Buzanich, Ana A1 - Gluth, Gregor T1 - Determination of the oxidation depths of ground granulated blast furnace slag-containing cement pastes using Mn K-edge X-ray absorption near-edge structure spectroscopy N2 - The redox potential of the pore solution of hardened cements containing ground granulated blast furnace slag (GGBFS) affects reinforcement corrosion and immobilization of radioactive waste. Here, Mn K-edge X-ray absorption near-edge structure (XANES) spectroscopy was applied to determine the depth profile of the oxidation state of manganese in hardened GGBFS-containing cement pastes. Manganese was oxidized in the outer regions of some of the pastes, but the depth to which this occurred was not identical with the ‘blue-green/white color change front’, usually interpreted as indicating oxidation of sulfur species. For CEM III/B, the color change of the material was gradual and thus unsuitable for a precise determination of the oxidation depth, while for the alkali-activated slag, a distinct color change front was found, but full oxidation of manganese and sulfur had not occurred in the brighter region. Mn K-edge XANES spectroscopy is thus a more reliable method than the determination of the visual color change front to follow the ingress of the oxidation front. KW - Manganese KW - Oxidation KW - Sulfide KW - Alkali-activated materials KW - Redox conditions PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651469 DO - https://doi.org/10.1111/jace.70445 SN - 0002-7820 SN - 1551-2916 VL - 109 IS - 1 SP - 1 EP - 11 PB - Wiley CY - Oxford AN - OPUS4-65146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - Additive manufacturing of geopolymers by selective laser curing N2 - Additive manufacturing (3D printing) of ceramics and other materials offers significant advantages compared to conventional production processes for several applications. While ceramics have been extensively investigated in this regard, additive manufacturing of geopolymers have received much less attention to date. In the present contribution we study a ‘standard’ metakaolin-based geopolymer, a fly ash-based geopolymer and a silica-based one-part geopolymer regarding their suitability for additive manufacturing via selective laser curing. Model geometries such as bars and cuboids could be produced by this route. After selective laser curing the specimens were additionally cured at 80 °C for 24 h. The specimens were studied by means of scanning electron microscopy (SEM) and powder X-ray diffraction (XRD). SEM showed that the precursors in all geopolymers had reacted partially and geopolymeric gel had formed. XRD confirmed these results and additionally revealed that the crystalline byproducts (zeolites) in the one-part geopolymer differed from the byproducts observed in conventionally produced samples. This indicates that also the geopolymerization reactions differ between the two synthesis routes. The mechanical strength after selective laser curing and 80 °C-curing appeared to be highest for the metakaolin-based geopolymer. However, SEM also showed that a significant volume of macropores remained in most regions of all specimens, while some regions in the metakaolin-based geopolymer appeared to be significantly denser. These preliminary results demonstrate that selective laser curing offers potential for the production of geopolymers, but more research has to be undertaken to optimize the process. T2 - 92. DKG Jahrestagung CY - Berlin, Germany DA - 19.03.2017 KW - Geopolymers KW - Inorganic polymers KW - Additive manufacturing KW - 3D printing KW - Selective laser curing PY - 2017 AN - OPUS4-39514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - Shrinkage and bond behaviour of one-part alkali-activated mortars N2 - Mortars for application on concrete, e.g. repair mortars or protective coatings, need to have a durable bond to the substrate. This bond is determined by the adhesion between the two materials and by the differential deformations of the mortar and the substrate. In the present contribution, the hygric deformations (shrinkage/expansion) of novel one-part alkali-activated mortars and their bond to concrete substrates are studied. Shrinkage of the mortars was studied at 50 % r.H., while expansion was studied on mortars stored over an open water surface (> 99% r.H.). The bond behaviour was studied by pull-off tests according to DIN EN 1542 and by optical microscopy. The alkali-activated mortars exhibit hygric deformations much lower than the deformations of an established, commercial mortar for sewer maintenance that was tested as reference in parallel with the alkali-activated mortars. The bond behaviour of the alkali-activated mortars depends strongly on their mix-design and curing. Optical microscopy showed that in the mortars with lower bond strength, cracks developed in the mortar during curing. Mortars with appropriate mix-design and curing did not exhibit cracking, and their pull-off strength (up to > 3 MPa) conformed to the requirements of relevant standards. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Bond strength KW - Hygric deformations KW - Repair mortars KW - Sewer repair PY - 2019 AN - OPUS4-47618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Carabba, L. A1 - Pirskawetz, Stephan A1 - Krüger, Simone A1 - Gluth, Gregor A1 - Bignozzi, M.C. T1 - Acoustic emission study of heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars N2 - Alkali-activated fly ashes have been proposed for various applications where resistance against high temperatures is required, yet several details regarding the response of these materials to heat-exposure need to be clarified. In the present study, heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars was analyzed by in-situ acoustic emission (AE) detection during complete heating-cooling cycles (up to ∼1100 °C), augmented by thermogravimetry and ex-situ SEM and XRD analyses. The applicability of the lightweight mortars as passive fire protection coatings was assessed by recording temperature-time curves of mortar-coated steel plates. Cracking during heating was limited and associated exclusively with the dehydration of the materials in the temperature range ∼90–360 °C. However, samples heated to temperatures above ∼600 °C exhibited intense cracking on cooling. This was attributed to differential deformations caused by local sintering and partial melting at the glass transition temperature, and subsequent quenching on cooling. KW - Alkali-activated materials KW - Acoustic emission KW - Fire proofing KW - Heat resistance KW - Cracking PY - 2019 DO - https://doi.org/10.1016/j.cemconcomp.2019.04.013 SN - 0958-9465 SN - 1873-393X VL - 102 SP - 145 EP - 156 PB - Elsevier AN - OPUS4-47904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Carabba, L. A1 - Masi, G. A1 - Pirskawetz, Stephan A1 - Krüger, Simone A1 - Gluth, Gregor A1 - Bignozzi, M.C. ED - Serdar, M. ED - Stirmer, N. ED - Provis, J. T1 - Thermal properties and steel corrosion in light-weight alkali-activated mortars N2 - This study aims at investigating the use of coal fly ash-based alkali activated mortars as passive fire protection system for steel structures. These systems are used to slow down the temperature rise of the steel substrate in case of fire. In addition, the protective system should guarantee the ability to prevent and/or mitigate steel corrosion phenomena. The behavior of a light-weight mortar was compared to that of a normal-weight mortar. Density and porosity were measured to better characterize the physical properties of the mortars. The degree of protection in case of fire was assessed by performing medium-scale fire tests. Acoustic emission measurements were conducted to analyze cracking phenomena during the high temperature exposure. The corrosion process was evaluated using an electrochemical approach in order to monitor the durability of the developed material. Preliminary results show that a 20 mm-thick layer of light-weight mortar is able to protect the steel substrate from reaching the critical temperature of 500 °C for 38 minutes in case of cellulosic fire. In addition, alkali activated mortars provide protection for carbon steel in presence of aggressive environment (i.e. presence of chlorides). The corrosion resistance is strictly related to the physical properties of the developed mortars. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Fire resistance KW - Steel corrosion KW - Acoustic emission KW - Alkali-activated materials PY - 2019 SN - 978-2-35158-223-7 VL - 1 SP - 125 EP - 132 PB - RILEM Publications CY - Paris AN - OPUS4-47584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Priebe, Nsesheye Susan A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Simon, Sebastian A1 - Kühne, Hans-Carsten ED - Serdar, M. ED - Stirmer, N. ED - Provis, J. T1 - Investigation of calcined brick clays from Central Germany for use as a sustainable pozzolan N2 - The production of Portland cement causes a substantial environmental impact, since the calcination of limestone results in high emissions of carbon dioxide. The use of supplementary cementitious materials such as calcined clays as partial replacement for Portland cement offers a solution to limit this environmental impact. This paper investigates four clays from deposits in central Germany with the aim of obtaining pozzolans for the production of Portland-pozzolana cement. The results obtained show that the calcined clays possess pozzolanic properties, which differ depending on calcination temperature and the relative amounts of Kaolinite and 2:1 clay minerals. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Supplementary cementitious materials KW - Calcined clays KW - Blended cements KW - Brick clays KW - Illitic clays PY - 2019 SN - 978-2-35158-223-7 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 1 SP - 462 EP - 469 PB - RILEM Publications CY - Paris AN - OPUS4-47586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten ED - Barcevic, A. ED - Rukavina, M.J. ED - Damjanovic, D. ED - Guadagnini, M. T1 - Shrinkage and bond behaviour of one-part alkali-activated mortars N2 - Mortars for application on concrete, e.g. repair mortars or protective coatings, need to have a durable bond to the substrate. This bond is determined by the adhesion between the two materials and by the differential deformations of the mortar and the substrate. In the present contribution, the hygric deformations (shrinkage/expansion) of novel one-part alkali-activated mortars and their bond to concrete substrates are studied. Shrinkage of the mortars was studied at 50 % r.H., while expansion was studied on mortars stored over an open water surface (> 99% r.H.). The bond behaviour was studied by pull-off tests according to DIN EN 1542 and by optical microscopy. The alkali-activated mortars exhibit hygric deformations much lower than the deformations of an established, commercial mortar for sewer maintenance that was tested as reference in parallel with the alkali-activated mortars. The bond behaviour of the alkali-activated mortars depends strongly on their mix-design and curing. Optical microscopy showed that in the mortars with lower bond strength, cracks developed in the mortar during curing. Mortars with appropriate mix-design and curing did not exhibit cracking, and their pull-off strength (up to >3 MPa) conformed to the requirements of relevant standards. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Repair mortars KW - Sewer repair KW - Hygric deformations KW - Bond strength PY - 2019 SN - 978-2-35158-225-1 VL - 3 SP - 103 EP - 110 PB - RILEM Publications CY - Paris AN - OPUS4-47587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Serdar, M. ED - Stirmer, N. ED - Provis, J. T1 - Behaviour of reinforced alkali-activated fly ash mortars under leaching conditions N2 - Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching PY - 2019 SN - 978-2-35158-223-7 VL - 1 SP - 118 EP - 124 PB - RILEM Publications CY - Paris AN - OPUS4-47585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - Investigation of calcined brick clays from Central Germany for use as SCM N2 - The production of Portland cement causes a substantial environmental impact, since the calcination of limestone results in high emissions of carbon dioxide. The use of supplementary cementitious materials such as calcined clays as partial replacement for Portland cement offers a solution to limit this environmental impact. This paper investigates four clays from deposits in central Germany with the aim of obtaining pozzolans for the production of Portland-pozzolana cement. The results obtained show that the calcined clays possess pozzolanic proper¬ties, which differ depending on calcination temperature and the relative amounts of kaolinite and 2:1 clay minerals. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Blended cements KW - Calcined clays KW - Brick clays KW - Supplementary cementititous materials PY - 2019 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. AN - OPUS4-47617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Priebe, Nsesheye Susan A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Vogler, Nico A1 - Kühne, Hans-Carsten T1 - Comparison of calcined illitic clays (brick clays) and low-grade kaolinitic clays as supplementary cementitious materials N2 - The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose. KW - Blended cement KW - Calcined clay KW - Brick clay KW - Illite KW - Kaolinite PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488195 DO - https://doi.org/10.1617/s11527-019-1393-2 SN - 1359-5997 SN - 1871-6873 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 52 IS - 5 SP - Article Number 94 PB - Springer Nature AN - OPUS4-48819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - One-part alkali-activated materials with high sulfuric acid resistance N2 - Materials with a high acid resistance are required in different important infrastructures. Examples include repair systems for sewer structures, where biogenic sulfuric acid corrosion is the major degradation mechanism. Low-calcium alkali-activated materials (AAMs) have been repeatedly observed to exhibit high acid resistance. However, the reasons for the high acid resistance of these materials were not fully under¬stood until recently, and the use of highly alkaline activator solutions to produce AAMs appears to hamper their commercial uptake. These issues have been tackled by characterising one-part AAMs and studying their alteration when exposed to sulfuric acid. One-part AAMs were synthesized by mixing blends of solid silica and sodium aluminate with water, and subsequent curing at 60–80 °C. Acid resistance testing was performed according to DIN 19573, i.e. exposure to sulfuric acid at pH = 1 for 70 days. Characterisation of the cured and the acid-exposed materials was done by XRD, ATR-FTIR, SEM as well as 29Si, 27Al and 1H MAS NMR spectroscopy, including cross-polarisation and double-resonance methods. Materials synthesized from industrial silicas were gel-zeolite composites, containing a substantial amount of unreacted ‘excess’ silica, while materials synthesized from rice husk ash were fully amorphous, containing ‘excess’ hydrous alumina. The sulfuric acid resistance of mortars based on these binders conformed to the requirements of DIN 19573 for sewer repair applications. The high acid resistance was caused by precipitation of silica gel at the mortar–solution interface, inhibiting further degradation. The presence of alumina gel may inhibit bacterial activity, potentially further improving performance in sewer environments. The phase assemblage of silica/sodium aluminate-based one-part AAMs can be adjusted via choice of the silica starting material. Properly designed materials exhibit excellent acid resistance, caused by precipi¬tation of silica gel which protects subjacent regions, and they may also inhibit bacterial activity. T2 - XVI ECerS Conference CY - Turin, Italy DA - 16.06.2019 KW - Alkali-activated materials KW - One-part mix KW - Acid resistance PY - 2019 AN - OPUS4-48236 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Provis, J. L. A1 - Arbi, K. A1 - Bernal, S. A. A1 - Bondar, D. A1 - Buchwald, A. A1 - Castel, A. A1 - Chithiraputhiran, S. A1 - Cyr, M. A1 - Dehghan, A. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Gluth, Gregor A1 - Nanukuttan, S. A1 - Peterson, K. A1 - Puertas, F. A1 - van Riessen, A. A1 - Torres-Carrasco, M. A1 - Ye, G. A1 - Zuo, Y. T1 - RILEM TC 247-DTA round robin test: mix design and reproducibility of compressive strength of alkali-activated concretes N2 - The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories. KW - Alkali-activated materials KW - Alkali-activated slag KW - Compressive strength KW - Concrete KW - Mix-design PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489131 DO - https://doi.org/10.1617/s11527-019-1396-z SN - 1359-5997 SN - 1871-6873 VL - 52 IS - 5 SP - Article Number 99 PB - Springer Nature AN - OPUS4-48913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hlavacek, Petr A1 - Ebell, Gino A1 - Gluth, Gregor A1 - Reinemann, Stefi A1 - Mietz, Jürgen A1 - Kühne, Hans-Carsten T1 - Betonstahlkorrosion in Geopolymerbetonen bei Angriff von Kohlenstoffdioxid und Chlorid N2 - Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt. KW - Korrosion KW - Geopolymer PY - 2019 SP - 1 EP - 83 AN - OPUS4-49752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - Einkomponentige alkaliaktivierte Bindemittel und Mörtel mit hohem Schwefelsäure-Widerstand N2 - Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere»). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird. T2 - Tagung Bauchemie der GDCh-Fachgruppe Bauchemie CY - Aachen, Germany DA - 30.09.2019 KW - Alkaliaktivierte Bindemittel KW - Biogene Schwefelsäurekorrosion KW - Abwasserinfrastruktur KW - Reparatursysteme PY - 2019 AN - OPUS4-49269 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten T1 - Einkomponentige alkaliaktivierte Bindemittel und Mörtel mit hohem Widerstand gegen Schwefelsäureangriff N2 - Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird. T2 - Tagung Bauchemie der GDCh-Fachgruppe Bauchemie CY - Aachen, Germany DA - 30.09.2019 KW - Alkaliaktivierte Bindemittel KW - Biogene Schwefelsäurekorrosion KW - Abwasserinfrastruktur KW - Reparatursysteme PY - 2019 SP - 107 EP - 113 PB - Gesellschaft Deutscher Chemiker CY - Frankfurt am Main AN - OPUS4-49264 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Kühne, Hans-Carsten ED - Wang, J. ED - Kriven, W. ED - Fey, T. ED - Colombo, P. ED - Weber, W.J. ED - Amoroso, J. ED - Fahrenholtz, W.G. ED - Shimamura, K. ED - Halbig, M. ED - Kirihara, S. ED - Wu, Y. ED - Shurgart, K. T1 - One-part geopolymers and aluminosilicate gel-zeolite composites: factors influencing microstructure and engineering properties N2 - Mixing and curing of geopolymers and related alkali-activated materials without storage and handling of highly alkaline solutions possesses advantages regarding safety and economic viability. One possible approach is to produce these materials from solid silica feedstocks and solid sodium aluminate, and subsequent mixing with water. We present a comparison between geopolymers and aluminosilicate gel-zeolite composites synthesized by this route from different silica feedstocks (by-product silica from chlorosilane production, microsilica, rice husk ash) and with different SiO2/Al2O3 ratios, using results from XRD, NMR, SEM, thermal analysis, mechanical and acid resistance testing. The use of rice husk ash favors formation of a fully amorphous geopolymer with high strength. Utilization of the other silica feedstocks leads to formation of aluminosilicate gel-zeolite composites, the amount and kind of zeolites depending on the feedstock and the SiO2/Al2O3 ratio. These composites show beneficial dehydration behavior, viz. no distinct dehydration step of thermal strain, with the phase assemblage after heating to 1000°C controlled by the starting composition. Mortars produced from both, the geopolymers as well as the composites, exhibit high resistance to sulfuric acid attack, making them promising materials for the construction and the repair of industrial and sewer structures. T2 - 42nd International Conference on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 21.01.2018 KW - Alkali-activated materials KW - One-part geopolymers KW - Sulfuric acid resistance KW - High-temperature resistance PY - 2019 DO - https://doi.org/10.1002/9781119543381.ch17 VL - 39 IS - 3 SP - 183 EP - 196 PB - John Wiley & Sons AN - OPUS4-47282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - Nachhaltige Betone: Calcinierte Tone als Zementhauptbestandteil N2 - Der Einsatz von calcinierten Tonen als Zementhauptbestandteil ist ein vielversprechender Weg, die mit der Zementherstellung und -verwendung verbundenen CO2-Emissionen zu senken. Im Vortrag werden die Randbedingungen hierfür sowie Ergebnisse eines aktuellen Vorhabens zur Calcinierung von illitreichen Tonen (Ziegeltonen) und anderen Tonen vorgestellt. T2 - Kolloquium Angewandte Geowissenschaften, Technische Universität Berlin CY - Berlin, Germany DA - 14.01.2019 KW - Calcinierte Tone KW - Dreischichtminerale KW - Metakaolin KW - Puzzolane KW - Metatone PY - 2019 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. AN - OPUS4-47198 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Sittner, Jonathan A1 - Hoffmann, T. A1 - Bertmer, M. A1 - Neubert, M. A1 - Schuster, T. A1 - Gluth, Gregor ED - D’Erme, C. ED - Paglia, C. ED - Cordero, E. G. T1 - Influence of the calcination method on the transformations and the reactivity of calcined low-kaolinitic clays N2 - This study investigates the calcination of low-grade kaolinitic clays containing high proportions of 2:1 clay minerals using two different methods: rotary kiln and fluidized bed calcination. The objective was to evaluate their potential as supplementary cementitious materials. The results demonstrate that even clays with low kaolinite content, when processed in a rotary kiln, exhibit pozzolanic properties suitable for cement replacement. Furthermore, fluidized bed calcination proved to be an energy-efficient alternative, achieving considerable dehydroxylation within just 30 min of calcination. This indicates the potential for substantial energy savings compared to conventional calcination techniques. However, further optimization of the process conditions is required to maximize reactivity and industrial applicability. The findings contribute to the ongoing development of sustainable cementitious materials by utilizing widely available, 2:1 clay mineral-dominated resources. KW - Calcined clay KW - Supplementary cementitous materials KW - Blended cement KW - Fluidized bed PY - 2026 SN - 978-3-032-14166-8 DO - https://doi.org/10.1007/978-3-032-14166-8_28 VL - 2 SP - 280 EP - 289 PB - Springer CY - Cham AN - OPUS4-65377 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor ED - Wittke, W. T1 - Alkalisch aktivierter Beton (Geopolymer-Beton) N2 - Alkalisch aktivierte Bindemittel (AAB) sind Zemente, deren Erhärtung auf der alkalischen Anregung von reaktiven Aluminiumsilicaten beruht. AAB sind nach gegenwärtigem Stand die vielversprechendste Option, die mit der Herstellung und dem Einsatz von Zementen verbundenen CO2-Emissionen mittel- bis langfristig signifikant zu senken. Die Erhärtungsreaktionen und die Einflüsse auf die Mikrostruktur von AAB sind durch jahrzehntelange Forschung gut verstanden, und zahlreiche Beispiele belegen, dass AAB grundsätzlich als Betonbindemittel geeignet sind. Offene Fragen bestehen aber immer noch hinsichtlich der Dauerhaftigkeit von mit AAB hergestellten Betonen. Der vorliegende Beitrag gibt eine kurze Einführung in die Nomenklatur und die Geschichte von AAB. Die wichtigsten Reaktionen und Reaktionsprodukte, die zur Bildung der Mikrostruktur von AAB führen, werden beschrieben. Der Hauptteil des Beitrags diskutiert aktuelle Forschungsergebnisse und offene Fragen zur Dauerhaftigkeit von Betonen auf Basis von AAB. Wichtige Fortschritte auf diesem Gebiet konnten in den letzten Jahren insbesondere zum Einfluss von Sulfiden auf die Bewehrungskorrosion, zum Carbonatisierungswiderstand und zum Säurewiderstand erzielt werden. T2 - 10. Felsmechanik- und Tunnelbautag CY - Weinheim, Germany DA - 22.05.2025 KW - Alkali-activated materials KW - Carbonation KW - Reinforcement corrosion KW - MIC KW - Microbially induced corrosion PY - 2025 SN - 978-3-00-083562-9 SP - 73 EP - 84 PB - WBI GmbH CY - Weinheim AN - OPUS4-64266 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -