TY - CONF A1 - Kaiser, Sebastian T1 - Component-like demonstrator for determination of temperature field and inner surface temperatures during in-service welding of hydrogen pipelines N2 - Hydrogen is considered as one of the most important energy carriers in the future. The necessary large-scale transport over long distances requires a suitable pipeline infrastructure. Current plannings encompass a dual-way strategy of repurposing existing natural gas (NG) pipelines, supplemented by the construction of new hydrogen pipelines. In some cases, such as necessary grid extensions or installation of bypasses in case of repair work, techniques like “hot tapping” are applied. These techniques include so-called in-service welding on pressurized pipelines and are state-of-the-art for NG grids and oil pipelines. The existing NG pipeline grid consists of a wide range of materials with different strengths, diameters, and wall thicknesses. In this context, the material compatibility is crucial. The main difference between hydrogen and NG is that hydrogen can both penetrate the material and cause hydrogen embrittlement. In that connection, in-service welding encompasses elevated temperatures for a certain time during the typically multi-layer welding process. Locally even austenitization temperature can be reached or surpassed. Austenite has a higher hydrogen solubility at a significantly lower diffusion rate, which could lead to a critical hydrogen accumulation. Especially the inner pipe surface temperature is from utmost interest, as this interface is exposed to the pressurized hydrogen (up to 100 bar). However, direct measurement of the locally occurring temperatures is very challenging. For this reason, a component-like geometry was developed. The geometry consists of a pipeline segment with a metal sheet joined to the pipe segment, representing similar heat dissipation conditions as in the field. In addition, typical welding parameters were applied that are currently used in the NG grid. This allows the welding of realistic multi-layer fillet welds on the outer pipe wall with simultaneous temperature measurement using manifold thermocouples at defined positions: (1) adjacent to the weld seam on the outer pipe surface, (2) on the inner pipe surface and (3) on the welded metal sheet. To ensure realistic conditions, manual shielded metal arc welding (SMAW) and gas tungsten arc welding (GTAW) was investigated. The effects of different wall thicknesses and welding heat inputs on the temperature distribution and peak temperatures achieved on the inner pipe surface during welding vary depending on the chosen method. Peak temperatures above austenitization temperature up to 1078 °C have been measured on L245 pipes with wall thickness of 3.6 mm. For pipes made from higher strength materials, such as L485, with a wall thickness of 8 mm, peak temperatures between 607 °C and 755 °C were recorded. Temperature and austenitization directly affects hydrogen diffusivity and solubility, showing the importance of the findings. The temperature profile and cooling conditions influence the mechanical properties of the material as well. For this reason, metallurgical investigations are carried out to assess the hardness and microstructure of the welds. Hardening up to 248 HV10 was detected in the heat-affected zone (HAZ) of the top layer, which could lead to a locally increased susceptibility to hydrogen assisted cracking. Meanwhile, the minimum hardness found in the HAZ of the root layer was as low as 144 HV10, indicating a softening. The results of this study provide valuable insights into the suitability of existing materials and geometries for hydrogen transport. Secondly, the data collected will serve as a basis for planned numerical simulations to further improve knowledge and optimize welding processes to ensure the integrity and safety of hydrogen pipelines. T2 - 78th IIW Annual Assembly and International Conference, Meeting of Commission II-C: "Testing and Measurement of Welds" CY - Genoa, Italy DA - 22.06.2025 KW - Pipeline KW - Welding KW - Inner-surface temperature KW - Temperature measurement KW - Hydrogen PY - 2025 AN - OPUS4-63637 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaiser, Sebastian T1 - Assessment of in service welding conditions for pressurized hydrogen pipelines via component test N2 - Hydrogen is the energy carrier of tomorrow for a fossil-free future. This requires a reliable transport infrastructure with the ability to carry large amounts of hydrogen e.g. for steel industry or chemical industry. The conversion of existing natural gas (NG) grids is an essential part of the worldwide hydrogen strategies, in addition to the construction of new pipelines. In this context, the transportation of hydrogen is fundamental different from NG as hydrogen can be absorbed into the pipeline material. Given the well-known effects of hydrogen embrittlement, the compatibility of the materials for the intended pipelines must be investigated (typically low alloy steels in a wide range of strengths and thicknesses). However, pipelines require frequent maintenance, repair or the need for installation for further outlets. In some cases, it is necessary to perform welding on or onto the pipelines while they are still in service, i.e. with active gas flow under high pressure, e.g. such as the well-known “hot tapping”. This in-service welding causes challenges for hydrogen operations in terms of additional hydrogen absorption during welding and the material compatibility. The challenge can be roughly divided into the possible austenitization of the inner pipe material exposed to hydrogen, which can lead to sufficient hydrogen absorption, and the welding itself, which causes an increased temperature range. Both lead to a significant increase in hydrogen solubility and diffusivity of the respective materials compared to room temperature. In this context, knowledge about hot tapping on hydrogen pipelines is scarce due to the lack of operating experience. Fundamental experimental investigations are required to investigate the transferability from NG to hydrogen pipeline grids. For this reason, the present study introduces a specially designed mock-up / demonstrator concept for the realistic assessment of the welding processing conditions. The mock-up was designed to enable in-situ temperature measurement during welding as well as ex-post extraction of samples for the quantification of the absorbed hydrogen concentration. For safety measures, the necessary pressurized hydrogen volume was limited by the insertion of a solid cylinder ensuring a 1 cm hydrogen gas layer. Welding experiments on the pressurized mock-ups with the diameters DN60 and DN200 have shown that the austenitization temperature can be reached on the inner surface of the pipeline, especially on thinner walled pipelines, using current welding practices. This corresponds to an increased hydrogen uptake in the welded area of several ppm. T2 - 78th IIW Annual Assembly and International Conference, IC-Session "Hydrogen Applications and Energy Transition" CY - Genoa, Italy DA - 22.06.2025 KW - Pipeline KW - Welding KW - Hydrogen KW - In-Service KW - Component-testing PY - 2025 AN - OPUS4-63638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Determination of inner pipe surface temperatures during in-service welding on hydrogen pipelines by means of component-like mock up experiments N2 - Hydrogen is considered as one of the most important energy carriers in the future. The necessary large-scale transport over long distances requires a suitable pipeline infrastructure. Current plannings encompass a dual-way strategy of repurposing existing natural gas (NG) pipelines, supplemented by the construction of new hydrogen pipelines. In some cases, such as necessary grid extensions or installation of bypasses in case of repair work, techniques like “hot tapping” are applied. These techniques include so-called in-service welding on pressurized pipelines and are state-of-the-art for NG grids and oil pipelines. The existing NG pipeline grid consists of a wide range of materials with different strengths, diameters, and wall thicknesses. In this context, the material compatibility is crucial. The main difference between hydrogen and NG is that hydrogen can both penetrate the material and cause hydrogen embrittlement. In that connection, in-service welding encompasses elevated temperatures for a certain time during the typically multi-layer welding process. Locally even austenitization temperature can be reached or surpassed. Austenite has a higher hydrogen solubility at a significantly lower diffusion rate, which could lead to a critical hydrogen accumulation. Especially the inner pipe surface temperature is from utmost interest, as this interface is exposed to the pressurized hydrogen (up to 100 bar). However, direct measurement of the locally occurring temperatures is very challenging. For this reason, a component-like geometry was developed. The geometry consists of a pipeline segment with a metal sheet joined to the pipe segment, representing similar heat dissipation conditions as in the field. In addition, typical welding parameters were applied that are currently used in the NG grid. This allows the welding of realistic multi-layer fillet welds on the outer pipe wall with simultaneous temperature measurement using manifold thermocouples at defined positions: (1) adjacent to the weld seam on the outer pipe surface, (2) on the inner pipe surface and (3) on the welded metal sheet. To ensure realistic conditions, manual shielded metal arc welding (SMAW) and gas tungsten arc welding (GTAW) was investigated. The effects of different wall thicknesses and welding heat inputs on the temperature distribution and peak temperatures achieved on the inner pipe surface during welding vary depending on the chosen method. Peak temperatures above austenitization temperature up to 1078 °C have been measured on L245 pipes with wall thickness of 3.6 mm. For pipes made from higher strength materials, such as L485, with a wall thickness of 8 mm, peak temperatures between 607 °C and 755 °C were recorded. Temperature and austenitization directly affects hydrogen diffusivity and solubility, showing the importance of the findings. The temperature profile and cooling conditions influence the mechanical properties of the material as well. For this reason, metallurgical investigations are carried out to assess the hardness and microstructure of the welds. Hardening up to 248 HV10 was detected in the heat-affected zone (HAZ) of the top layer, which could lead to a locally increased susceptibility to hydrogen assisted cracking. Meanwhile, the minimum hardness found in the HAZ of the root layer was as low as 144 HV10, indicating a softening. The results of this study provide valuable insights into the suitability of existing materials and geometries for hydrogen transport. Secondly, the data collected will serve as a basis for planned numerical simulations to further improve knowledge and optimize welding processes to ensure the integrity and safety of hydrogen pipelines. T2 - IIW Intermediate Meeting, Com. II-A CY - Trollhättan, Sweden DA - 10.03.2025 KW - Testing KW - In-service welding KW - Hydrogen KW - Pipelines PY - 2025 AN - OPUS4-62690 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas T1 - Measurement of hydrogen concentration in steels by laser-induced breakdown spectroscopy (LIBS) N2 - Current efforts to achieve lightweight construction and the required reduction in CO2 emissions and an increase in energy and resource efficiency call for the increasing use of high-strength fine-grain structural steels. However, as the strength of higher-strength fine-grain structural steels increases, so do the associated joining challenges. Particular attention must be paid to hydrogen-assisted cold cracking. The influence of hydrogen reveals itself less in the strength but has a significant effect on the deformability [1, 2]. The degradation of the material properties can lead to zero ductility, where the values of the yield strengths coincide with the tensile strengths. Laser-induced breakdown spectroscopy (LIBS) is a spectroscopic technique that can be used to determine elemental compositions without pre-treatment of the samples. Short, high-energy laser pulses ablate a small volume (< 0.1 mm3) of the examined material and ionize it to form a plasma. The decaying plasma emits element-specific light. This light is spectroscopically analysed and allows to detect qualitatively the present elements and to quantify them with help of a standardization routine. The simple experimental set-up and the fast, nearly non-destructive analysis procedure characterize the LIBS analysis. The LIBS method allows a time and spatially resolved in situ measurement of steel components in use. Even low hydrogen concentrations (~ 1 wt.-ppm) in steel can be measured with the LIBS method and can be quantified with help of certified reference materials. The results are compared with results gained with the well-established carrier gas hot extraction method. T2 - MaterialsWeek 2021 CY - Online Meeting DA - 07.09.2021 KW - LIBS KW - Hydrogen KW - Stainless steel KW - Diffusion PY - 2021 AN - OPUS4-53234 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karapanagiotis, Christos A1 - Heimann, Jan A1 - Duffner, Eric A1 - Charmi, Amir A1 - Schukar, Marcus A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Towards predictive maintenance of hydrogen pressure vessels based on multi-sensor data N2 - In this paper, we report on a sensor network for structural health monitoring (SHM) of Type IV composite overwrapped pressure vessels (COPVs) designed for hydrogen storage. The sensor network consists of three different SHM sensing technologies: ultrasonic guided waves (GW), acoustic emission (AE) testing, and distributed fiber optic sensors (DFOS). We present an experimental setup for a lifetime test, where a COPV is subjected to cyclic loading. Data from all sensors are collected and centrally evaluated. The COPV failed after approximately 60,000 load cycles, and the sensor network proved capable of detecting and localizing the damage even before the failure of the COPV. This multi-sensor approach offers significantly more channels of information and could therefore enable a transition from costly and time-consuming periodic inspections to more efficient and modern predictive maintenance strategies, including artificial intelligence (AI)-based evaluation. This not only has a positive effect on operational c KW - Ffiber optic sensors KW - Acoustic emission KW - Guided waves KW - Hydrogen KW - Digital twin KW - Structural health monitoring PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618948 DO - https://doi.org/10.58286/30513 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-61894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - Hydrogen permeability of glass measured by VHE-MS powder methods N2 - Glasses are can serve as exceptionally tight hydrogen barriers e.g. used for hydrogen storage in micro glass containers or cover glasses in micro electronic systems. Respective glass development, however, requires precise measurements of minimal hydrogen permeability, PH2. Recent studies showed that PH2 can be measured down to 2 10-21 mol s-1 Pa-1m-1 by means of Vacuum Hot Extraction (VHE) powder methods [1]. In this respect the isothermal gas release from glass powder particles is fitted in terms of classical diffusion models assuming spherical particles of uniform size thus obtaining the hydrogen diffusion coefficient, DH2. PH2 is then given by D H2 × S H2, where hydrogen solubility, SH2, is obtained from VHE studies of glass powders exposed to hydrogen atmosphere for different exposure time and hydrogen pressure. Measurements of minimal values of hydrogen permeability, however, require a careful evaluation and error discussion of this method. Against that background, we modeled hydrogen degassing during heating and subsequent isothermal annealing of glass powder particles of different shape and particle size distribution by means of COMSOL Multiphysics® [2] and verified related effects on DH2 obtained by the VHE powder method. T2 - SGT Centenary Conference, & ESG 2016 CY - Sheffield, UK DA - 4.9.2016 KW - Glass KW - Hydrogen KW - Permeability KW - Storage PY - 2016 AN - OPUS4-38307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Update on "Call for interested people to contribute to series of comprehensive papers on welding and joining of components for sustainable energy systems" N2 - Based on the initial call in March 2024, an update time-frame is introduced on the working plan for a comprehensive review paper series on joining and welding technologies for the manufacturing of components and parts used in sustainable energy generation, conversion, and transport with focus on hydrogen and wind energy. T2 - 77th IIW Annual Assembly and International Conference, Meeting of Commission II-A CY - Ixia, Rhodes, Greece DA - 07.07.2024 KW - Review paper KW - Research study KW - Hydrogen KW - Joining KW - Welding PY - 2024 AN - OPUS4-60674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim T1 - Characterization of Hydrogen Diffusion in a Thick-walled Submerged Arc Multi-Layer Weld Joint N2 - The energy production of the future will be dominated by CO2-emission free techniques like wind turbines and become essential in scope of the planned hydrogen economy. As onshore installation capacity is limited, the in-crease of the number of offshore wind turbines (OWT) is a major goal. In that connection, the OWTs continuously increase in size and weight and demand adequate foundations concepts like monopiles or tripods. These compo-nents are typically manufactured from welded mild steel plates with thickness up to 200 mm. The predominant welding technique is submerged arc welding (SAW) with up to five wires. In accordance with the standards, the occurrence of delayed hydrogen assisted cracking is anticipated by either a hydrogen removal heat treatment (HRHT) or a so-called minimum waiting time (MWT) before non-destructive testing (NDT) of the respective weld joint is allowed. The reason for the MWT is the necessary time for the hydrogen diffusion at ambient temperature due the high plate thickness. Both the effectiveness of a HRHT at elevated temperatures or the MWT at ambient temperature can be estimated by calculation of the diffusion time. This time depends on reliable hydrogen diffu-sion coefficients and these are rare in literature. For that reason, this study presents the hydrogen diffusion coef-ficients obtained from a multi-layer SAW joint of an offshore steel grade. Two different experimental techniques were used to identify the respective diffusion behavior: (1) hydrogen desorption experiments with a carrier gas hot extraction analyzer at elevated temperatures for the characterization of a HRHT and (2) the electrochemical permeation technique at ambient temperature for the characterization of an MWT. From both experiments, the respective diffusion coefficients were calculated. The obtained DCs are different from those reported in literature, i.e., the duration or applicability of a HRHT or MWT must be critically discussed. T2 - European Congress and Exhibition on Advanced Materials and Process - Euromat 2021 CY - Online meeting DA - 13.09.2021 KW - Welding KW - Offshore KW - Wind turbine KW - Hydrogen KW - Cracking PY - 2021 AN - OPUS4-53296 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Joining Processes in Hydrogen Technologies - Current need and future R&D activites, a review N2 - This study gives an overview on the important field of joining processes for component fabrication in hydrogen technologies. For that reason, the current need and future research and developement activites are highlighted for the different technological field of hydrogen generation, storage, transport and use. In addition, the emerging field of additive manufacturing is included. Finally, some remarks are given for necessary changes in the standardization and its challenges. T2 - 46th Seminar - Additive Manufacturing, Hydrogen, Energy, Integrity CY - Online meeting DA - 12.10.2021 KW - Hydrogen KW - Joining process KW - Welding KW - Review KW - Research and Development PY - 2021 AN - OPUS4-53554 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Joining processes for components in hydrogen technologies: Current need and future importance N2 - This presentation gives an overview on the importance of joining processes for component fabrication in hydrogen technologies. For that reason, the current need and future research and developement activites are highlighted for the three technological fields: hydrogen storage, transport and use (in terms of the emerging field of additive manufacturing). Finally, some remarks are given for necessary changes in the standardization. T2 - IIW Intermediate Meeting, Comm. II-A "Welding Metallurgy" CY - Online meeting DA - 17.03.2022 KW - Hydrogen KW - Welding KW - Research KW - Review KW - Additive manufacturing PY - 2022 AN - OPUS4-54488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Residual stresses and hydrogen assisted cracking in thick walled submerged arc weld joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods or jackets. These components are typically submerged arc welded (SAW) high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicate the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam / layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with 22 passes and a seam length of 1,000 mm. Additional welded stiffeners simulated the effect of a high restraint, to stimulate critical HAC conditions. The residual stresses were determined by a robot XRD goniometer. A least square regression analysis of the sin²ψ-law by using multiple ψ- and φ-tilts was applied. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modelling allowed the qualitative estimation of the hydrogen diffusion in the weld, enabling the determination of critical conditions for the formation of HAC. In a future step, a structural simulation will allow the assessment of the welding residual stresses and the comparison to the XRD-values. T2 - International Conference on Residual Stresses ICRS-11 CY - Nancy, France DA - 27.03.2022 KW - Welding KW - X-ray diffraction KW - Hydrogen KW - Cracking KW - Offshore steel PY - 2022 AN - OPUS4-54576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kaiser, Sebastian T1 - Repair welding of pressurized in-service hydrogen pipelines: A review on current challenges and strategies N2 - As energy carrier of the future, green hydrogen can make a decisive contribution to a sustainable energy supply. In Europe concrete plans for a hydrogen pipeline grid already exist, as the so called “European Hydrogen backbone”. As building a completely new pipeline grid is economically not justifiable, a dual-way strategy of repurposing natural gas (NG) pipelines and newly built pipelines is intended. Long distance pipeline grids require regular maintenance and repairs. In that conection, for natural gas (NG) pipelines in-service welding is state of the art. Concepts such as hot-tapping (drilling into pressurized pipelines) and “stoppling” (sealing off pipeline sections after installing bypasses or pressure relieves) allow the repair of damaged pipeline sections or the installation of new branches without shutting the pipeline down. The EIGA 121/14 guideline already pointed out in 2014 that “a hydrogen hot-tap shall not be considered a routine procedure”. This shows that the determination of the transferability of these repair concepts to hydrogen pipelines is of utmost importance. Due to the degrading effects of hydrogen on mechanical proper-ties, commonly referred to as “hydrogen embrittlement” it is necessary to understand and investigate the occurring effects. In the special case of repair welding on in-service hydrogen pipelines an increased hydro-gen uptake due to a large heat input and microstructural changes in the material needs to be considered. For this reason, this paper gives an overview on existing weld repair concepts and its risks and limitations in terms of hydrogen absorption and possible embrittlement effects when transferred to hydrogen pipelines. The complexity lies in a large variety of materials (low alloyed steels), pipeline diameters and corresponding welded joints. The material compatibility of materials in used (repurposed NG-pipelines) and new condition must be investigated. Particularly for repurposed/used pipelines the effect of a pre-matured/corroded inner surface and sometimes insufficient documentation of the material “history” needs to be considered. An overview on ongoing and completed R&D-projects with respect to repair concepts for hydrogen pipelines and hydrogen effects on pipeline materials is given. T2 - 77th IIW Annual Assembly and International Conference, Meeting of Commission XI "Pressure Vessels and Piping" CY - Ixia, Rhodes, Greece DA - 07.07.2024 KW - Hydrogen KW - Repair welding KW - Pipelines KW - Study PY - 2024 AN - OPUS4-60673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heimann, Jan T1 - Innovative Real-Time Monitoring of H2 Pressure Vessels for Enhanced Safety and Reliability N2 - The significantly increased number of pressure vessels for storage and transport of H2 makes periodic manual inspections virtually impossible. Structural health monitoring enables proactive maintenance, extends the vessel’s lifespan, and ensures compliance with regulations, all while minimizing operational risks and downtime. T2 - QI-Digital Forum 2024 CY - Berlin, Germany DA - 09.10.2024 KW - Structural Health Monitoring KW - Pressure Vessel KW - Hydrogen KW - Reliability KW - Quality Infrastructure KW - Demonstrator PY - 2024 AN - OPUS4-61485 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos A1 - Heimann, Jan A1 - Duffner, Eric A1 - Charmi, Amir A1 - Schukar, Marcus A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Towards predictive maintenance of hydrogen pressure vessels based on multi-sensor data fusion and digital twin modeling N2 - Hydrogen pressure vessels are among the most essential components for reliable hydrogen technology. Under current regulations, a mostly conservative strategy is employed, restricting the usage time of hydrogen pressure vessels without providing information on the real remaining lifetime. During the service life, pressure vessels are inspected periodically. However, no established method that can provide continuous monitoring or information on the remaining safe service life of the vessel. In this paper, we propose a sensor network for Structural Health Monitoring (SHM) of hydrogen pressure vessels where data from all sensors are collected and centrally evaluated. Specifically, we integrate three different SHM sensing technologies namely Guided Wave ultrasonics (GW), Acoustic Emission testing (AT), and distributed Fiber Optic Sensing (FOS). This integrated approach offers significantly more information and could therefore enable a transition from costly and time-consuming periodic inspections to more efficient and modern predictive maintenance strategies, including Artificial Intelligence (AI)-based evaluation. This does not only have a positive effect on the operational costs but enhances safety through early identification of critical conditions in the overall system in real-time. We demonstrate an experimental set-up of a lifetime test where a Type IV Composite Overwrapped Pressure Vessel (COPV) is investigated under cyclic loading instrumented with AT, FOS, and GW methods. We acquired data from the sensor network until the pressure vessel failed due to material degradation. The data collected using the three different SHM sensor technologies is planned to be evaluated individually, using data fusion, and AI. In the future, we aim to integrate the measurement setup into a hydrogen refueling station with the data stream implemented into a digital signal processing chain and a digital twin. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Acoustic emission KW - Ultrasonic guided waves KW - Fiber optic sensors KW - Hydrogen KW - Pressure vessels KW - Structural health monitoring KW - Machine learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602764 UR - https://www.ndt.net/search/docs.php3?id=29702 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karapanagiotis, Christos A1 - Breithaupt, Mathias A1 - Duffner, Eric A1 - Schukar, Marcus T1 - Real-time monitoring of hydrogen composite pressure vessels using surface-applied distributed fiber optic sensors N2 - In this paper, we report to the best of our knowledge for the first time on continuous real-time monitoring of composite overwrapped pressure vessels (COPVs) designed for hydrogen storage using surface-applied distributed fiber optic sensors (DFOS). We conducted continuous and real-time DFOS measurements during pressure cycling tests consisting of periodic pressure fluctuations between 20 bar and 875 bar, with a rate of 5 cycles min−1. During pressure cycling, the DFOS system measured strain changes, that under normal operating conditions were linearly correlated to changes in pressure. To detect and quantify damage-related anomalies, we trained a simple regression model to predict strain from pressure data and used the difference between predicted and measured values as a damage indicator. With our approach, the DFOS system not only detected and localized the damage but also continuously tracked its evolution in real time under dynamic pressure conditions. Furthermore, unlike previous studies where optical fibers were embedded within the composite structure, we applied them on the COPV surface, reducing both implementation cost and time while eliminating the need to modify the COPV manufacturing process. Based on our results, we are confident that DFOS can enhance safety and facilitate the transition from time-consuming periodic inspections to more efficient, machine learning-based predictive maintenance. KW - Fiber optic sensors KW - Hydrogen KW - Structural health monitoring KW - Pressure vessels KW - Predictive maintenance PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-627644 DO - https://doi.org/10.1088/2515-7647/adb9ac SN - 2515-7647 VL - 7 IS - 2 SP - 2 EP - 10 PB - IOP Publishing Ltd CY - Bristol, UK AN - OPUS4-62764 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Welding (and joining) technologies for the hydrogen economy - a short overview N2 - This study gives an overview on the important field of joining processes for component fabrication in hydrogen technologies. The current main issues and future perspectives are highlighted for the different technological field of hydrogen generation, storage, transport and use. In addition, the emerging field of additive manufacturing is included. Some remarks are given for standardization and regulations. T2 - Meeting of the European Welding Association (EWA), Executive Committee (EC) 1 CY - Frankfurt am Main, Germany DA - 22.03.2023 KW - Hydrogen KW - Welding KW - Research KW - Study PY - 2023 AN - OPUS4-57222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Assessment of in-service welding conditions for pressurized hydrogen pipelines via component test N2 - Hydrogen is the energy carrier of tomorrow for a fossil-free future. This requires a reliable transport infrastructure capable of transporting large quantities of hydrogen. In addition to the construction of new pipelines, the conversion of existing natural gas (NG) networks is an essential part of global hydrogen strategies. The transport of hydrogen is fundamentally different from that of NG, as hydrogen can be absorbed into the pipeline material. Given the known effects of hydrogen embrittlement, the compatibility of the materials for the proposed pipelines (typically low alloy steels in a wide range of strengths and thicknesses) must be investigated. However, pipelines require frequent maintenance, repair, or the need to install additional outlets. In some cases, it is necessary to perform welding on or to the pipelines while they are in-service, i.e. with active gas flow under high pressure. This in-service welding poses challenges for hydrogen operations in terms of additional hydrogen absorption during welding and material compatibility. The challenge can be roughly divided into the possible austenitization of the inner pipe material exposed to hydrogen, which can lead to sufficient hydrogen absorption, and the welding itself, which causes an increased temperature range. Both lead to a significant increase in hydrogen solubility of the respective materials compared to room temperature. In this context, knowledge about welding on hydrogen pipelines is scarce due to the lack of operational experience. Fundamental experimental investigations are required to investigate the transferability from natural gas to hydrogen pipeline networks. For this reason, the present study presents a specially designed demonstrator concept for the realistic assessment of the welding process conditions. The demonstrator was designed ex-post sample extraction for quantification of the absorbed hydrogen concentration. For safety reasons, the required volume of pressurized hydrogen was limited by inserting a solid cylinder. Welding experiments on the DN50 and DN200 pressurized demonstrators showed an increased hydrogen uptake in the welded area of several ppm. T2 - Materials Week/Steel Innovation CY - Frankfurt am Main, Germany DA - 02.04.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - Component test PY - 2025 AN - OPUS4-62941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Masoud Nia, Niloufar A1 - Nietzke, Jonathen A1 - Kannengiesser, Thomas T1 - Ti and Nb microalloying of HSLA steels and its effect on hydrogen diffusion and trapping N2 - Fine-grain, high-strength, low-alloy (HSLA) structural steels with yield strengths > 600 MPa are now the state of the art in construction applications such as mobile cranes and civil engineering. HSLA grades derive their strength from a combination of specific heat treatment and the underlying chemical composition. In this context, Ti or Nb are essential to obtain a fine-grained microstructure as well as the necessary carbides or nitrides for precipitation strengthening. In this context, the specific effect of Ti or Nb-rich compounds on hydrogen trapping and diffusion is well known for special laboratory cast alloys, but unknown for realistic steel compositions. For this reason, a series of S690Q-based alloys were synthesized, close to a real steel composition, but with well controlled Ti or Nb additions in different amounts. Specimens were obtained from these alloys by electrochemical discharge machining (EDM). The specimens were tested using the well-established electrochemical permeation technique. From the experimental results, the hydrogen diffusion coefficients and the analytical subsurface hydrogen concentration were calculated. In addition, the hydrogen trapping behavior at elevated temperatures was interpreted by thermal desorption analysis (TDA) using different heating rates of hydrogen charged samples. The results showed that in contrast to metallurgically "pure" laboratory cast alloys, realistic chemical compositions were similar in their hydrogen trapping behavior, despite some small differences. All investigated steel grades exhibited shallow and reversible hydrogen trapping, regardless of their chemical composition. Of course, the experiments only allowed the calculation of effective diffusion coefficients and trapping energies, which represent an average of the entire microstructure. Nevertheless, HSLA steels are typically joined by arc welding, which includes the risk of delayed hydrogen assisted cracking. From the point of view of welding practice, however, a more or less identical hydrogen diffusion behavior means that no special "metallurgically specific", justifiable measures need to be considered, despite the well-established processes such as "soaking" or dehydrogenation heat treatment. T2 - MPAC 2025 CY - Stuttgart, Germany DA - 06.10.2025 KW - HACC KW - Hydrogen KW - HSLA PY - 2025 AN - OPUS4-64337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Component test for simulation of in-service welding on hydrogen pipelines N2 - Hydrogen is set as the energy carrier of tomorrow and most countries will achieve large-scale hydrogen transport through the conversion of the natural gas (NG) grid and the construction of new pipelines. The interaction between hydrogen and the pipeline materials differs fundamentally from that of NG, as hydrogen is readily absorbed into the material. Considering the possible hydrogen embrittlement (HE), the compatibility of the pipeline materials (low-alloyed steels with a wide strength/thickness range) must be investigated. However, pipelines require intervention for maintenance, repair, or grid expansion with welding on/onto the pipelines while in service, i.e. the well-known "hot tapping" and "stoppling". The challenges compared to NG can be broadly divided into the possible austenitization of the inner pipe material exposed to hydrogen and the welding itself. Both result in a significant increase in hydrogen solubility and could potentially pose challenges in terms of HE. Emphasis is placed on the word "could" because knowledge of "hot tapping" on hydrogen pipelines is scarce due a lack of service experience. To this end, this study proposes a concept for a component-like demonstrator with the objectives: (1) safe feasibility of "hot tapping" on pressurized model hydrogen pipeline sections, (2) facilitate ex-post sample extraction for the purpose of quantifying the absorbed hydrogen concentrations, and (3) ensure in-situ temperature measurement during welding to monitor the pipeline surface temperature. For safety reasons in the event of an unintentional "burn-through", a solid cylinder was inserted in the demonstrator to restrict the hydrogen gas volume to a small, pressurized layer. Reference pipeline surface temperature measurements were ensured on comparable, unpressurized geometries. The investigated range of welding conditions was investigated for representative material/thickness combinations (DN60 to DN300), suggesting the feasibility of the demonstrator for the determination of reliable in-service welding conditions for both installed and new pipelines for hydrogen service. T2 - 49th MPA Conference CY - Stuttgart, Germany DA - 06.10.2025 KW - Hydrogen KW - Pipeline KW - In-service welding KW - Component test PY - 2025 AN - OPUS4-64317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Widjaja, Martinus Putra A1 - Moosavi, Robabeh A1 - John, Sebastian A1 - Schumacher, David A1 - Grunwald, Marcel A1 - Auster, Jürgen A1 - Szczepaniak, Marius A1 - Mair, Georg W. A1 - Waske, Anja T1 - Impact damage evaluation of hydrogen composite pressure vessels by analysing computed tomography images N2 - The objective of this work is to find a method that describes the degree of damage from an impact experiment. This experiment was performed on Composite Pressure Vessels (CPV) in order to find the correlation of impact damage to the residual burst pressure. Computed Tomography (CT) approach was used to capture the before and after impact condition of the CPVs. The Wasserstein function was used to calculate how much the after impact image has differed from the original one. In the end, a good correlation was obtained to the residual burst pressure. T2 - HyFiSyn Conference CY - Online meeting DA - 15.09.2021 KW - Hydrogen KW - Composite pressure vessel KW - Carbon fibre KW - Burst test KW - Image analysis KW - Computed tomography (CT) PY - 2021 SP - 31 EP - 32 AN - OPUS4-53494 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Widjaja, Martinus Putra T1 - Impact damage evaluation of hydrogen composite pressure vessels by analysing computed tomography images N2 - The objective of this work is to find a method that describes the degree of damage from an impact experiment. This experiment was performed on Composite Pressure Vessels (CPV) in order to find the correlation of impact damage to the residual burst pressure. Computed Tomography (CT) approach was used to capture the before and after impact condition of the CPVs. The Wasserstein function was used to calculate how much the after impact image has differed from the original one. In the end, a good correlation was obtained to the residual burst pressure. The smaller the Wasserstein distance is, the higher the residual burst pressure would be and vice versa. T2 - HyFiSyn Conference CY - Online meeting DA - 15.09.2021 KW - Hydrogen KW - Composite pressure vessel KW - Carbon fibre KW - Burst test KW - Image analysis KW - Computed tomography (CT) PY - 2021 AN - OPUS4-53496 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhao, H. A1 - Chakraborty, Poulami A1 - Ponge, D. A1 - Hickel, Tilmann A1 - Sun, B. A1 - Wu, C.-H. A1 - Gault, B. A1 - Raabe, D. T1 - Hydrogen trapping and embrittlement in high-strength Al alloys N2 - Ever more stringent regulations on greenhouse gas emissions from transportation motivate efforts to revisit materials used for vehicles. High-strength aluminium alloys often used in aircrafts could help reduce the weight of automobiles, but are susceptible to environmental degradation. Hydrogen ‘embrittlement’ is often indicated as the main culprit; however, the exact mechanisms underpinning failure are not precisely known: atomic-scale analysis of H inside an alloy remains a challenge, and this prevents deploying alloy design strategies to enhance the durability of the materials. Here we performed near-atomic-scale analysis of H trapped in second-phase particles and at grain boundaries in a high-strength 7xxx Al alloy. We used these observations to guide atomistic ab initio calculations, which show that the co-segregation of alloying elements and H favours grain boundary decohesion, and the strong partitioning of H into the second-phase particles removes solute H from the matrix, hence preventing H embrittlement. Our insights further advance the mechanistic understanding of H-assisted embrittlement in Al alloys, emphasizing the role of H traps in minimizing cracking and guiding new alloy design. KW - Atomistic models KW - Hydrogen KW - Metals and alloys KW - Mechanical properties PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543631 DO - https://doi.org/10.1038/s41586-021-04343-z SN - 1476-4687 VL - 602 IS - 7897 SP - 437 EP - 441 PB - Nature Publ. Group CY - London AN - OPUS4-54363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tiebe, Carlo A1 - Bayat, Mehmet E. T1 - Measurement and Testing Methods for Sensors in Hydrogen Technologies N2 - To ensure accurate results, it is advisable to conduct sensor testing under controlled conditions, focusing on identifying specific properties and quantifying performance criteria. The necessity of these evaluations lies in determining if a potentially beneficial sensor is a good fit for a specific application. Devices are typically factory-calibrated in according to ISO/IEC 17025, followed by testing/validation prior to intended use. Subsequent inspections/validations performance tests and long-term stability should be repeated in appropriate intervals. We present the testing and calibration validation of a hydrogen sensor intended for safety applications, using dynamic dilution of hydrogen into clean, dry air. • Sensor testing for the determination of non-explosive gas mixture composition, response time and characteristic curves of gas sensors, gas measuring devices. • Hydrogen mole fraction: 100 μmol/mol to > 4.0 cmol/mol – (approximately equal to 0.1 Vol-% to > 4.0 Vol-%) • Humidity: frost-point temperatures in the range of -85 °C to 15 °C (equal to 0.2 μmol/mol to 17000 μmol/mol humidity mole fraction) at ambient pressure • Sensor output provided directly in hydrogen volume percent, as defined by the factory calibration. The results obtained from the device under test demonstrate the effectiveness of the evaluated gas sensor in detecting and quantifying hydrogen. Its responses to different amounts of hydrogen in air and reliably returns to zero. To quantify the generated hydrogen mole fractions in situ and in operando, a process-GC-TCD-TCD system calibrated against our primary gas standards was used, ensuring the highest accuracy as a designated institute for primary gas standards. This procedure provides a foundation for modern and efficient quality assurance of gas sensors. T2 - 2025 IARIA Annual Congress on Frontiers in Science, Technology, Services, and Applications CY - Venice, Italy DA - 06.07.2025 KW - Hydrogen KW - Sensor KW - Quality KW - Validation KW - Data analysis KW - Reference procedure PY - 2025 AN - OPUS4-64047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effect of hydrogen pressure on the fretting behavior of elastomers N2 - In this study, the fretting behavior of several elastomer materials against 316L were evaluated in air and hydrogen environment up to 10 MPa. Furthermore, aging experiments were conducted for 7 days under static conditions in 100 MPa hydrogen and the physical and mechanical properties of the rubber materials were examined before and after hydrogen exposure. Fretting tests revealed that the wear of these compounds is significantly affected by the hydrogen environment compared to air, especially with NBR grades. After aging experiment, the friction response of HNBR grades is characterized by increased adhesion due to elastic deformation, leading to partial slip. T2 - ITC 2023: 9th International Tribology Conference 2023 CY - Fukuoka, Japan DA - 26.09.2023 KW - Hydrogen KW - Fretting KW - Elastomers PY - 2023 AN - OPUS4-61962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Halder, Karabi A1 - Balasooriya, Winoj A1 - Hausberger, Andreas A1 - Kaiser, Andreas T1 - Effect of high-pressure hydrogen environment on the physical and mechanical properties of elastomers N2 - This study presents the influence of high-pressure hydrogen environment on the physical and mechanical properties of two types of cross-linked hydrogenated acrylonitrile butadiene rubbers. Based on the CSA/ANSI standard, static exposures in hydrogen experiments were performed up to 100 MPa at 120 °C. Characterization before and after exposure was conducted by means of density and hardness measurements, dynamic mechanical analysis (DMA), tensile tests, compression set, FT-IR and AFM analyses to assess effects after decompression. While the effect of high-pressure exposure is significant immediately after exposure, most of the physical and mechanical properties recover after 48 hours. FT-IR, AFM, SEM and compression set results indicate, however, permanent effects. KW - Hydrogen KW - Mechanical properties KW - Elastomers KW - High-pressure hydrogen environment PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597102 DO - https://doi.org/10.1016/j.ijhydene.2024.01.148 SN - 0360-3199 VL - 58 SP - 389 EP - 399 PB - Elsevier Ltd. AN - OPUS4-59710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Hausberger, Andreas T1 - Effect of hydrogen pressure on the fretting behavior of rubber materials N2 - Safety and reliability are the major challenges to face for the development and acceptance of hydrogen technology. It is therefore crucial to deeply study material compatibility, in particular for tribological components that are directly in contact with hydrogen. Some of the most critical parts are sealing materials that need increased safety requirements. In this study, the fretting behavior of several elastomer materials were evaluated against 316L stainless steel in an air and hydrogen environment up to 10 MPa. Several grades of cross-linked hydrogenated acrylonitrile butadiene (HNBR), acrylonitrile butadiene (NBR) and ethylene propylene diene monomer rubbers (EPDM) were investigated. Furthermore, aging experiments were conducted for 7 days under static contions in 100 MPa of hydrogen followed by rapid gas decompression. Fretting tests revealed that the wear of these compounds is significantly affected by the hydrogen environment compared to air, especially with NBR grades. After the aging experiment, the friction response of the HBNR grades is characterized by increased adhesion due to elastic deformation, leading to partial slip. KW - Fretting wear KW - Rubbers KW - Hydrogen KW - High-pressure PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608462 DO - https://doi.org/10.3390/lubricants12070233 VL - 12 IS - 7 SP - 1 EP - 17 PB - MDPI AN - OPUS4-60846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Harmonized tribological testing of polymers in hydrogen N2 - To investigate typical polymer compounds and a potential alternative to be used in hydrogen compressors, tribological tests have been performed with several tribometers in hydrogen atmosphere. The compounds used were a commercially available PEEK matrix with 10 wt-% PTFE, graphite, and short carbon fibers each (supplied by company Polytron), a PPS matrix with 10 wt-% PTFE and graphite (supplied by company MOCOM) and an experimental PA12 matrix with PTFE, chemically coupled with an oleyl alcohol, as additive (supplied by the polymer research institute IPF). For all compounds a steel counter disc (type 316L / 1.4404) with a lapped surface was used in a cylinder on disc setup. The focus of this work is to study the tribological performance of the polymers in hydrogen atmosphere. Additionally, tests were carried out with up to three different tribometers at two institutions. The challenge to compare and harmonize equipment, procedures, and methods is an important part of the study. This naturally includes the determination of the wear volumes of the polymeric cylinders. Furthermore, selected results of the wear and the resulting change in the contact geometry were compared by FEM simulations and an analytical model. T2 - Colloquium H2Safety@BAM, Materials properties and compatibility CY - Online meeting DA - 14.05.2025 KW - Hydrogen KW - Polymers KW - Tribometer KW - Wear KW - Coefficient of Friction KW - Interlaboratory comparison KW - Comparability KW - Harmonisation KW - Standardisation KW - Tribology KW - Oil-coupled compounds PY - 2025 AN - OPUS4-63103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Fretting behavior of elastomer materials in hydrogen N2 - This presentation deals with the fretting wear behavior of elastomer materials (two types of cross-linked hydrogenated acrylonitrile butadiene rubbers) against 316L steel ball in hydrogen environment. Furthermore, aging experiments were conducted for 7 days under static conditions in 100 MPa hydrogen. Fretting tests revealed the wear of the polymer decreases with increasing hydrogen pressure. After high pressure hydrogen exposure, the fretting process is characterized by increased adhesion due to elastic deformation, leading to partial slip. T2 - 63rd German Tribology Conference 2022 CY - Göttingen, Germany DA - 26.09.2022 KW - Fretting KW - Rubbers KW - Hydrogen PY - 2022 AN - OPUS4-62082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Harmonized testing in hydrogen N2 - In this study, the tribological performance of conventional and alternative polymer compounds for compressors was investigated in gaseous hydrogen using several tribometers. The compounds used were a commercial PEEK matrix with 10 wt.% each of PTFE, graphite, and short carbon fibres (Polytron), a PPS matrix with 10 wt.% each of PTFE and graphite (MOCOM), and an experimental PA12 matrix with PTFE, chamically coupled with an oleyl alcohol, as additive (supplied by the polymer research institute IPF). For all compounds a steel counter disc (type 316L / 1.4404) with a lapped surface finish was used in a cylinder-on-disc setup. Next to the tribological performance of the polymer compounds in hydrogen atmosphere, a strong focus of the work was to compare the results obtained with different tribometer setups. The tests were carried out with three different tribometers at two institutions. The challenge to compare and harmonise equipment, procedures, test and evaluation methods was an important part of the study. This includes the determination of the wear volumes of the polymeric cylinders with different wear analysis workflows. Furthermore, selected results of the wear and the resulting change in the contact geometry were compared with an FEM simulation and an analytical model. T2 - 25th International Conference of Wear of Materials CY - Sitges, Spain DA - 14.04.2025 KW - Standardisation KW - Harmonisation KW - Hydrogen KW - Polymers KW - Wear KW - Coefficient of Friction KW - Interlaboratory comparison KW - Tribometer PY - 2025 AN - OPUS4-62992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - On the way to sustainable and hydrogen compatible sealing materials N2 - In this contribution, the sliding performance of newly formulated polymer materials with improved sustainability are investigated and compared with conventional materials. Tribological tests were performed in hydrogen at ambient temperature as well as cryogenic medium. The samples were arranged in a pin-on-disk configuration with a flat pin sliding against a rotating austenitic steel disk. The friction and wear mechanisms are described and discussed by means of surface analyses. T2 - PolyTrib 2024 CY - Portoroz, Slowenia DA - 03.10.2024 KW - High-performance polymers KW - Sliding wear KW - Hydrogen KW - Cryogenic PY - 2024 AN - OPUS4-61419 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Hashimoto, H. A1 - Aoyagi, A. A1 - Dobbelaar, E. T1 - On the way to sustainable and hydrogen compatible sealing materials N2 - In this contribution, the sliding performance of newly formulated polymer materials with improved sustainability are investigated and compared with conventional materials. Tribological tests were performed in hydrogen at ambient temperature as well as cryogenic medium. The samples were arranged in a pin-on-disk configuration with a flat pin sliding against a rotating austenitic steel disk. The friction and wear mechanisms are described and discussed by means of surface analyses. T2 - PolyTrib 2024 CY - Portoroz, Slowenia DA - 03.10.2024 KW - High-performance polymers KW - Sliding wear KW - Hydrogen KW - Cryogenic PY - 2024 SP - 1 EP - 2 AN - OPUS4-61421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis T1 - Competence centre h2safety@bam N2 - In this presentation the current focus areas of the competence centre H2Safety@BAM are shown. The fields of competence include “Material properties and compatibility”, “Process and plant safety”, “Component testing, component safety and approval” as well as “Sensors, analytics and certified reference Materials. Moreover, the cross-cutting activities regarding “Education and training” and the testing possibilities and planed test facilities at the Test Site for Technical Safety (BAM TTS) are presented. T2 - VDMA P2X4A: P2X Technik-Treffen CY - Online meeting DA - 14.09.2023 KW - Hydrogen KW - Test area hydrogen safety KW - ModuH2Pipe PY - 2023 AN - OPUS4-58333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El Harrab, Hayat A1 - Askar, Enis A1 - Franken, T. A1 - Mauss, F. T1 - Experimental and reaction kinetic study of hydrogen ignition behavior at ignition limits N2 - The paper presents the results of an experimental and reaction kinetic investigation of hydrogen ignition at different pressures in a closed vessel, highlighting its non-linear behavior and the effects of radical wall termination. The reaction kinetic simulation predicts the three characteristic ignition limits of hydrogen caused by radical and thermal auto-ignition and is in close agreement with the experimental measurements. The first ignition limit is determined by the chain branching reaction H+O_2→O+ OH. This limit shows strong sensitivity towards the wall termination of O, H and OH radicals. The second ignition limit is influenced by the wall termination of O, H, OH, HO2 and H2O2 radicals. The third ignition limit is dominated by the reaction paths HO_2+HO_2→H_2 O_2+O_2 and H_2 O_2+M→2 OH+M, which is why it shows strong sensitivity towards wall termination of HO₂ and H₂O₂ radicals. Increasing the radical wall termination rate by increasing the sticking coefficient of the radicals at the wall or the surface-to-volume-ratio leads to an increase of the auto-ignition temperature at the same pressure. The introduction of radical wall termination reactions improved the prediction of ignition limits and highlighted the profound effect of the autoclave wall and vessel size on the hydrogen ignition behavior. KW - Radical Wall Termination Reaction KW - Hydrogen KW - Auto-ignition Temperature KW - Ignition Limit PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-647609 DO - https://doi.org/10.1016/j.proci.2025.105980 SN - 1540-7489 VL - 41 SP - 1 EP - 7 PB - Elsevier Inc. AN - OPUS4-64760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Namwoonde, Andreas Sheuyange T1 - Polymer Composites Under Continuous and Reciprocating Sliding Conditions In Hydrogen N2 - The implementation of hydrogen as an alternative energy source to fossil fuels necessitates the use of compatible materials for safety purposes, and thermoplastics are widely utilized in this context. The application of polymers in gaseous and liquid hydrogen environments requires careful consideration of their tribological performance, as the operating environment is dramatically different from ambient conditions. Friction, wear, and lubrication are crucial factors to consider in this regard. Researchers have investigated various strategies to enhance the tribological performance of polymers in hydrogen environments, including modifying the composition and structure of polymers by incorporating fillers to improve their friction and wear resistance. The tribological properties of polymer composites based on matrices of PEEK, PPS, and PI have been mostly investigated using the continuous sliding test method, and the results indicate that these materials are suitable candidates for tribological applications in both gaseous and liquid hydrogen. This project explores the tribological properties of related polymer composites in hydrogen using continuous and reciprocating motion with a pin-on-disc testing method. T2 - Polytrib2024 CY - Portorož, Slovenia DA - 03.10.2024 KW - Polymers KW - Friction KW - Wear KW - Tribological behaviour KW - Hydrogen PY - 2024 AN - OPUS4-61378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - From Research to a Standard: The Hollow Specimen Technique for High-Pressure Hydrogen Gas Testing N2 - As the world moves towards a decarbonised economy, the demand for sustainable and low-carbon alternatives is growing rapidly. Hydrogen has an important role to play in this transition, but in order to make the most of hydrogen as an energy carrier, a comprehensive understanding of its impact on the integrity of structural materials is necessary. Metallic materials, mainly steels, are the most commonly used structural materials in various components throughout the hydrogen supply chain. Ensuring their sustainable and safe use in hydrogen technologies is a crucial factor in the development of the hydrogen economy. This is particularly important since hydrogen can promote crack formation and ultimately lead to premature failure in these materials when combined with mechanical load. This process is commonly known as Hydrogen Embrittlement and can occur in almost all the steels used for the hydrogen technologies. Extensive materials qualification is required for the rapid implementation of hydrogen technologies, however, most accepted, and standardised test methods for determining the effect of gaseous hydrogen on metallic materials describe complex and costly procedures that are only available to a very limited extent worldwide. The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations of the current methods and complement them for qualifying metallic materials under high-pressure hydrogen gas. Unlike the conventional autoclave technique, this method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and no need for complex equipment or a specialised laboratory. The technique's low investment and testing costs, simple operation, and shorter testing time make it an optimal for widespread use around the world, thereby increasing the output of results. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of an ISO committee to standardise the method. However, there are open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions relate to specimen geometry, inner hole surface and gas quality and are being addressed in the H2HohlZug project, of which the overall aim is to systematically close the gaps towards a standard. This contribution presents the structure and milestones of the project, followed by initial results. T2 - CETIM Workshop Technique H2 CY - Nantes, France DA - 11.12.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - TransHyDE KW - H2HohlZug KW - Standardisation PY - 2025 AN - OPUS4-65103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The Role of Geometry, Surface Quality and Gas Purity N2 - The hollow specimen technique is a simple and cost-effective method that has the potential to make materials qualification with pressurised gaseous hydrogen widely accessible to academia and industry. The feasibility of this method for slow strain tensile tests has been demonstrated in several studies, leading to the establishment of the ISO/TC 164/SC 1/WG 9 ISO committee for its standardisation. Questions have emerged during this process, that currently prevent the method from being standardised for hydrogen testing. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. The first results are presented in this poster. T2 - TransHyDE Vollversammlung 2024 CY - Leipzig, Germany DA - 27.11.2024 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - Austenitic Stainless Steel KW - TransHyDE KW - H2HohlZug PY - 2024 AN - OPUS4-61847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai T1 - Hydrogen - Trust through safety N2 - In den Virtual Talks der DECHEMA wurden allgemeine Aspekte der Sicherheit und Akzeptanz von Wasserstofftechnologien vorgestellt. Wie kann Vertrauen in neue Technologien geschaffen werden, wenn Unfälle aus der Vergangenheit zu Mythen und Märchen führten? Der Vortrag räumt mit allgemeinen Vorurteilen auf und zeigt, dass der Umgang mit Wasserstoff weder unsicherer, noch sicherer ist als der Umgang mit anderen Brenngasen. Basis für den sicheren Umgang mit Wasserstoff ist immer eine Risikoanalyse. N2 - In the DECHEMA Virtual Talks, general aspects of the safety and acceptance of hydrogen technologies were presented. How can trust in new technologies be built when past accidents led to myths and fairy tales? The presentation does away with general prejudices and shows that handling hydrogen is neither more unsafe nor safer than handling other fuel gases. The basis for the safe handling of hydrogen is always a risk analysis. T2 - DECHEMA Virtual Talks CY - Online meeting DA - 23.11.2020 KW - Hydrogen KW - Wasserstoff KW - Safety KW - Sicherer Umgang KW - Sicherheit PY - 2020 AN - OPUS4-52082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - Performance of Conventional and Additive Manufactured Austenitic Stainless Steels under Gaseous Hydrogen Environment using in-situ Hollow Specimen Technique N2 - Hydrogen and its derivatives (e.g. ammonia) are considered as a suitable energy carrier in the future supply of renewable energy. Hydrogen transportation systems require pipes, valves and fittings, among other components. In this sense, austenitic stainless steels are commonly used structural materials for pure hydrogen applications. Stable austenitic alloys, like AISI 316L, are often assumed to be practically unsusceptible to hydrogen embrittlement. At the same time, a number of studies show the influence of hydrogen even in 316L under some circumstances. Some other studies state that this embrittlement could be avoided by using steel grades with a higher nickel equivalent which contributes to a more stable austenitic phase. Nonetheless, 316L is widely used in hydrogen atmospheres since many years because of lower costs and positive practical experience. For these reasons, not only 316L but also 304 could be further utilized by identifying the exact constraints. With increasing demand for components regarding hydrogen applications, additive manufacturing technologies are getting increasingly important complementary to conventional manufacturing. In the context of additive manufacturing, 316L is a common material as well. The manufacturing process offers great advantages due to higher freedoms in design and the possibility for customized components in small batches. For example, valves with improved flow characteristics and reduced component weight can be produced. Nevertheless, there is still lack of experience and experimental results concerning additively manufactured parts under hydrogen service. Therefore, the influence on the material properties for additively manufactured parts in hydrogen environments needs to be further investigated. In the present work, slow strain rate testing (SSRT) has been applied using hollow specimens. This testing procedure allows to perform practicable and faster in-situ tests in comparison to tests in autoclaves and investigate the influence of hydrogen on the mechanical properties. Conventional AISI 304 and 316L specimens as well as additively manufactured 316L specimens were tested at room temperature and a pressure of 200 bar. Elongation at fracture and relative reduction of area (RRA) have been used to evaluate the influence of hydrogen. It is shown that the influence of hydrogen is more pronounced in 304 than in 316L. Furthermore, potentially influencing factors such as surface roughness, microstructure and porosity are discussed. T2 - International Hydrogen Conference CY - Park City, Utah, USA DA - 17.09.2023 KW - Hydrogen KW - Hollow Specimen Technique KW - Additive Manufacturing KW - Austenitic Steels PY - 2023 AN - OPUS4-58776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Konert, Florian T1 - Investigation of the resistance of X65 pipeline steel and weld to gaseous hydrogen using the hollow specimen technique N2 - The constantly increasing demand for renewable energy sources lead to the necessity of transporting large amounts of hydrogen. Since pipelines enable a cost-effective way for the distribution of gaseous hydrogen, the interaction of hydrogen and the pipeline materials must be carefully investigated as hydrogen can cause a degradation of the mechanical properties under certain conditions. Especially welds, which are assumed to be more susceptible to the degradation enhanced by hydrogen, are of great interest. The aim of this study is to investigate the effect of gaseous hydrogen on the mechanical properties of an X65 pipeline, and the longitudinal submerged arc welding (SAW) welded joint. The tests are conducted using the hollow specimen technique on two types of specimens: one extracted from the base material (BM) and the other extracted as a cross-weld (CW) specimen consisting of base material and weld seam. The specimens are charged in-situ under a pressure of 60 bar and tested using slow strain rate (SSR) tensile tests with a nominal strain rate of 10-5 s-1. The performed tests showed a decrease of the reduction of area (RA) from 72% in inert atmosphere to 52% in hydrogen atmosphere for the CW-specimen and a decrease from 73% in inert atmosphere to 51% for the BM. Metallographic analyses showed the crack initiation between fine grain heat affected zone (FGHAZ) and BM for the specimens tested in hydrogen atmosphere as well as for the reference specimens. This leads to the conclusion that the location of the crack initiation does not change due to the presence of gaseous hydrogen. T2 - 77th IIW Annual Assembly and International Conference 2024 CY - Rhodes, Greece DA - 07.07.2024 KW - Hydrogen KW - Hollow-specimen KW - Pipeline steel KW - SSRT KW - Hydrogen embrittlement PY - 2024 AN - OPUS4-60617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The TransHyDE - H2HohlZug Project N2 - The feasibility of the method for slow strain tensile tests has been demonstrated in several studies, leading to the establishment of the ISO/TC 164/SC 1/WG 9 ISO committee for its standardisation. Questions have emerged during this process, that currently prevent the method from being standardised for hydrogen testing. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. T2 - TrasnsHyDE Abschlusskonferenz CY - Berlin, Germany DA - 25.03.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - TransHyDE PY - 2025 AN - OPUS4-62807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Konert, Florian A1 - Nietzke, Jonathan T1 - Application of an in-situ H2Test Method N2 - The degradation effect of hydrogen on the mechanical properties of steels is well known, but still not sufficiently understood. The fast and safe market ramp up of hydrogen technologies makes it evident to evaluate a wider understanding of this topic. In general it is often described as hydrogen embrittlement. Therefore it is desirable to achieve a test method which is able to provide material properties under hydrogen atmosphere in an easy way. Currently mechanical tests under hydrogen atmosphere are executed in autoclaves. For this technique complex hardware is needed, therefore tests are expensive and test capacities are only available in a small scale. The shown test method promises a trendsetting approach for reducing costs and machine time by using hollow specimen. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - Hollow specimen KW - In-situ KW - Test procedure PY - 2022 AN - OPUS4-56032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The Role of Strain-Rate and Surface Quality N2 - As the world moves towards a decarbonised economy, the demand for sustainable and low-carbon alternatives is growing rapidly. Hydrogen has an important role to play in this transition, but in order to make the most of hydrogen as an energy carrier, a comprehensive understanding of its impact on the integrity of structural materials is necessary. Metallic materials, mainly steels, are the most commonly used structural materials in various components throughout the hydrogen supply chain. Ensuring their sustainable and safe use in hydrogen technologies is a crucial factor in the development of the hydrogen economy. This is particularly important since hydrogen can promote crack formation and ultimately lead to premature failure in these materials when combined with mechanical load. This process is commonly known as Hydrogen Embrittlement and can occur in almost all the steels used for the hydrogen technologies. Extensive materials qualification is required for the rapid implementation of hydrogen technologies, however, most accepted, and standardised test methods for determining the effect of gaseous hydrogen on metallic materials describe complex and costly procedures that are only available to a very limited extent worldwide. The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations of the current methods and complement them for qualifying metallic materials under high-pressure hydrogen gas. Unlike the conventional autoclave technique, this method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and no need for complex equipment or a specialised laboratory. The technique's low investment and testing costs, simple operation, and shorter testing time make it an optimal for widespread use around the world, thereby increasing the output of results. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of an ISO committee to standardise the method. However, there are open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions relate to specimen geometry, inner hole surface and gas quality and are being addressed in the H2HohlZug project, of which the overall aim is to systematically close the gaps towards a standard. This contribution presents the structure and milestones of the project, followed by initial results. T2 - HyLab | HyTalks CY - Online meeting DA - 12.11.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - TransHyDE KW - H2HohlZug PY - 2025 AN - OPUS4-64749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Richter, Tim A1 - Mayr, P. A1 - Nitsche, A. A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - Hydrogen diffusion in creep-resistant 9% Cr P91 multi-layer weld metal N2 - Welded components of P91 9% Cr steel demand for careful welding fabrication with necessary post weld heat treatment (PWHT). Before the PWHT, a hydrogen removal heat treatment is necessary for avoidance of hydrogen assisted cracking (HAC). In this context, the microstructure and temperature-dependent hydrogen diffusion is important, and reliable diffusion coefficients of P91 weld metal are rare. For that reason, the diffusion behavior of P91 multi-layer weld metal was investigated for as-welded (AW) and PWHT condition by electrochemical permeation experiments at room temperature and carrier gas hot extraction (CGHE) from 100 to 400 °C. Hydrogen diffusion coefficients were calculated, and the corresponding hydrogen concentration was measured. It was ascertained that both heat treatment conditions show significant differences. At room temperature the AW condition showed significant hydrogen trapping expressed by to seven times lower diffusion coefficients. A preferred diffusion direction was found in perpendicular direction expressed by high permeability. The CGHE experiments revealed lower diffusion coefficients for the AW condition up to 400 °C. In this context, a hydrogen concentration of approximately 21 ml/100 g was still trapped at 100 °C. For that reason, a certain HAC susceptibility of as-welded P91 weld metal cannot be excluded, and hydrogen removal should be done before PWHT. KW - Creep resisting materials KW - Diffusion KW - Hydrogen KW - Weld metal KW - Post weld heat treatment KW - Microstructure PY - 2020 DO - https://doi.org/10.1007/s40194-019-00828-8 SN - 0043-2288 VL - 64 IS - 2 SP - 267 EP - 281 PB - Springer AN - OPUS4-50471 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Konert, Florian T1 - The applicability of the hollow specimen technique for testing various metals under high pressure hydrogen atmosphere N2 - The transition to a decarbonised economy will require large amounts of hydrogen over a broad variety of applications. The use of hydrogen poses high safety requirements as hydrogen can be absorbed by metallic materials and result in hydrogen embrittlement under certain condi-tions. For this reason, interactions of gaseous hydrogen and metallic materials are of high sci-entific and industrial interest. Slow strain rate tensile (SSRT) tests are commonly used to evaluate the hydrogen-induced ductility loss of alloys. However, the current standardised test method describes a complex and expensive procedure with limited availability worldwide. The hollow specimen technique promises huge potential for scaling suitable in-situ testing infra-structure and is currently under intensive development in several institutes around the world. As this method has only gained significant attention in the last decade, there are varying interpretations, particularly when testing materials with vastly different mechanical properties. Most available literature focuses on common steels used in hydrogen and natural gas piping systems. The present work provides an overview of the widespread applicability of hollow specimens in evaluating the effect of high-pressure hydrogen on the tensile properties of vari-ous metallic materials. The research presented includes Near-Net shape produced additively manufactured (AM) AISI 316 L, ferritic X65 steel, its weld seam, and solution annealed and hardened 100Cr6 steel. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Hydrogen KW - Hollow specimen technique KW - SSRT PY - 2024 AN - OPUS4-60912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ekici, Nilsah T1 - SHIMMER project: safe hydrogen injection modelling and management for european gas network resilience N2 - To accelerate the transition to a low-carbon economy while exploiting existing infrastructure, hydrogen can be injected to the natural gas network. However, many technical and regulatory gaps should be closed, and adaptations and investments made to ensure that multi-gas networks across Europe will be able to operate in a reliable and safe way while providing a highly controllable gas quality and required energy demand. The SHIMMER project aims to enable a higher integration and safer hydrogen injection management in multi-gas networks by contributing to the knowledge and better understanding of hydrogen projects, their risks, and opportunities. T2 - EGATEC 2024 CY - Hamburg, Germany DA - 18.06.2024 KW - Hydrogen KW - Gas grid KW - Database KW - Low-carbon PY - 2024 AN - OPUS4-60519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El Harrab, Hayat A1 - Askar, Enis A1 - Franken, T. A1 - Mauss, F. T1 - Experimental and Reaction Kinetic Study of Hydrogen Ignition Behavior at Ignition Limits N2 - The paper presents the results of the experimental and reaction kinetic investigation of hydrogen ignition at different pressures, highlighting its non-linear behaviour and effects of radical wall termination. The reaction kinetic simulation predicts the three characteristic ignition limits caused by radical and thermal auto-ignition and is in close agreement with the experimental measurements. The introduction of radical wall termination in the reaction mechanism allowed us to investigate the effect of the autoclave wall and vessel size on the hydrogen ignition behaviour. The first ignition limit is determined by the chain initiation reaction H_2+O_2→2 OH and shows a strong sensitivity towards wall termination of O, H and OH radicals. The third ignition limit is dominated by the reaction paths HO_2+HO_2→H_2 O_2+O_2 and H_2 O_2+M→2 OH+M which is why it shows a strong sensitivity towards wall termination of HO₂ and H₂O₂ radicals. The second ignition limit is influenced by the wall termination of O, H, OH, HO2 and H2O2 radicals. Increasing the radical wall termination rate by increasing the adsorption rate of the radicals at the wall leads to an increase of the auto-ignition temperature at the same pressure. T2 - 13th Mediterranean Combustion Symposium CY - Corfu, Greece DA - 01.06.2025 KW - Hydrogen KW - Auto-ignition Temperature KW - Radical Wall Termination Reaction KW - Ignition Limit PY - 2025 AN - OPUS4-64762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El Harrab, Hayat T1 - Evaluation of the Impact of Lubricating Oil on Pre-Ignition of Hydrogen for Engine Relevant Conditions N2 - A successful transition to clean energy depends on ensuring that the world's growing energy needs are met while reducing greenhouse gas emissions. Achieving this goal requires the use of carbon-free energy sources. Many utilities have already begun the shift from conventional carbon-based fuels to cleaner alternatives, such as hydrogen. However, numerous challenges persist regarding the use of hydrogen in internal combustion engines. The use of hydrogen in engines, which have extremely lower ignition energy, has raised concerns about the risk of pre-ignition due to the undesirable presence of lubricating oil during combustion. Due to its low auto-ignition temperature, lubricating oil is widely regarded as the main cause of abnormal combustion. To verify and understand the potential influence of lubricating oil on hydrogen reactivity, the auto-ignition temperature was measured using a constant volume reactor. Auto-ignition was identified by a sudden increase in pressure combined with a rapid rise in temperature. The experimental results verified that the addition of 0.2 ml lubricating oil to stoichiometric hydrogen-air mixtures at 20 bar reduced the auto-ignition temperature from 460°C to 270°C, reducing the ignition temperature by 190K. Moreover, the auto-ignition temperature of oil showed a decreasing trend as the initial amount of oil increased, indicating that the ignition process mainly occurs by vaporization. T2 - CI’s 40th International Symposium - Emphasizing Energy Transition CY - Milan, Italy DA - 24.07.2024 KW - Hydrogen KW - Lubricating oil KW - Auto-ignition temperature KW - Internal combustion engines and pre-ignition PY - 2024 AN - OPUS4-61373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Comprehensive standardization of the hollow specimen method for tests in high pressure hydrogen gas N2 - As the world moves towards a decarbonised economy, the demand for sustainable and low-carbon alternatives is rapidly increasing. Hydrogen plays an important role in this transition, but in order to make the most of hydrogen as an energy carrier, a comprehensive understanding of its impact on the integrity of structural materials is necessary. Metallic materials, mostly steels, are the most regularly used structural materials in various components throughout the hydrogen supply chain. Ensuring their sustainable and safe use in hydrogen technologies is a crucial factor in the development of the hydrogen economy. This is particularly important since hydrogen can promote crack formation and ultimately lead to premature failure in these materials when combined with mechanical load. This process is commonly known as Hydrogen Embrittlement and can occur in almost all the steels used for the hydrogen technologies. Extensive materials qualification is needed for the rapid implementation of hydrogen technologies, however, most accepted, and standardised test methods for determining the effect of gaseous hydrogen on metallic materials describe complex and costly procedures that are only available to a very limited extent worldwide. The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations of the current methods and complement them for qualifying metallic materials under high-pressure hydrogen gas. In this method, an axial hole is drilled in a tensile specimen, which is then filled with hydrogen gas, sealed, and placed in a standard testing machine. This method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and no need for complex equipment or a specialised laboratory, unlike the conventional autoclave technique. The technique's low investment and testing costs, simple operation, and shorter testing time make it optimal for widespread use around the world, thereby increasing the output of results. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of the committee ISO/TC 164/SC 1/WG 9 “Tensile testing, method in high-pressure hydrogen environment“ to standardise the method, however, there are open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions relate to specimen geometry, inner hole surface and gas quality and are being addressed in the H2HohlZug project. Here, the aim is to systematically address and close the gaps towards the standardisation of this technique for tests with hydrogen. This contribution presents the structure and milestones of the project, followed by initial results regarding the optimisation of the specimen geometry, as well as the influence of different manufacturing and finishing processes on the inner hole surface of the hollow specimen and its response to hydrogen effects. T2 - TestXpo | 32nd International Expo for Materials Testing CY - Ulm, Germany DA - 21.10.2024 KW - Hydrogen KW - Hydrogen Embrittlement KW - High-Pressure Gaseous Gas KW - Hollow Specimen Technique KW - H2HohlZug KW - TransHyDE KW - Standardisation KW - Tensile Test PY - 2024 AN - OPUS4-61453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás A1 - Konert, Florian A1 - Nietzke, Jonathan A1 - Krzysch, Zephanja A1 - Böllinghaus, Thomas A1 - Michler, Thorsten A1 - Wackermann, Ken A1 - Oesterlin, Heiner A1 - Tlili, Mohamed A1 - Puthur, Alen A1 - Elsen-Humberg, Stephan A1 - Koenigs, Timo A1 - Ruchti, Peter A1 - Systermans, Thomas A1 - Sobol, Oded T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The Role of Strain-Rate and Surface Quality N2 - The feasibility of the method for slow strain tensile tests has been demonstrated in several studies, leading to the establishment of the ISO/TC 164/SC 1/WG 9 ISO committee for its standardisation. Questions have emerged during this process, that currently prevent the method from being standardised for hydrogen testing. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. The first results addressing the questions regarding specimen manufacturing are presented in this poster. T2 - TrasnsHyDE Abschlusskonferenz CY - Berlin, Germany DA - 25.03.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - TransHyDE KW - H2HohlZug PY - 2025 AN - OPUS4-62809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ekici, Nilsah T1 - Introduction of The SHIMMER Database for Safe Hydrogen Injection in The European Natural Gas Infrastructure N2 - An important step in the transportation strategy for hydrogen is its injection into the existing natural gas grid, which allows accelerating the transition to a low-carbon economy, in other words, hydrogen economy. The European Commission has established hydrogen roadmaps and strategies that emphasize the safe and efficient integration of hydrogen into the natural gas network to support this transition. In line with the objectives of the road map, several funded projects have been established, among others – the Safe Hydrogen Injection Modelling and Management for European Gas Network Resilience (SHIMMER) project. One of the main goals of this project is establishing a database containing a comprehensive repository of information regarding materials, standards, European pilot projects, and operational conditions parameters for the European gas network gathered from open sources as well as transmission and distribution system operators participating in the project. The SHIMMER database has an extensive structure consisting of 262 pipeline entries, each with details such as length, design pressure, inner diameter, and installation year and more. The following contribution elaborates on how the SHIMMER database was established as reliable source of information to be available for the public. The database allows consistent assessments of hydrogen compatibility across different countries, offering a structured framework to help overcome the challenges inherent to the assessments of the components for the injection of hydrogen across Europe. Further, the SHIMMER database provides a valuable information source for future research on the European gas networks. T2 - ICHS 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Database KW - Hydrogen KW - Gas Grid KW - Low-carbon KW - Pipeline Steel PY - 2025 AN - OPUS4-64288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -