TY - CONF A1 - Radnik, Jörg T1 - Comparative chemical analysis of Ni-Fe oxide nanoparticles N2 - Ni-Fe oxide nanoparticles have gained a lot of interest because of their high activity in the oxygen evolution reaction (OER) which is crucial for water splitting. [1] Although there have been great efforts in the last years, the understanding of the synergistic effect between Fe and Ni is still under discussion. Therefore, we prepared different Ni-Fe oxide nanoparticles with different compositions from pure iron oxide to pure nickel oxide adapting a known procedure. [2,3] Size and morphology of the nanoparticles depend on the composition which was shown with Transmission Electron Microscopy (TEM). The compositions of the nanoparticles were measured with a comparative approach using X-ray Photoelectron Spectroscopy (XPS), Hard X-ray Photoelectron Spectroscopy (HAXPES), and Energy Dispersive X-Ray Spectroscopy (EDS) coupled with the TEM providing detailed chemical information of the nanoparticles in different sample regions. EDS reveals that the different sample regions are dominated by one of the components, Fe or Ni, but a slight mixing between the components can be found (see Figure 1), which was confirmed with X-ray Diffraction (XRD). XPS indicates the enrichment of Fe at the sample surface, while HAXPES and EDS data agree on the stoichiometry of the bulk. High-resolution XPS and HAXPES exhibit some differences in the valence states of Fe and Ni, whereas Ni seems to be easier to reduce than Fe. Further investigations combining these different techniques and additionally Secondary Ion Mass Spectrometry (ToF-SIMS) are ongoing by using in situ approaches and coupling cyclic voltammetry to the analytical techniques. T2 - ECASIA 2024 CY - Gothenburg, Sweden DA - 09.06.2024 KW - Oxygen evolution reaction KW - Transmission Electron Microscopy KW - (Hard) X-ray Photoelectron Spectroscopy KW - Synergistic effects PY - 2024 AN - OPUS4-60534 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Markötter, Henning T1 - In situ tomographic imaging with hard x rays at Bamline (BESSY II) N2 - The BAMline at the synchrotron X-ray source BESSY II (Berlin, Germany) is supporting researchers especially in materials science [1]. As a non-destructive characterization method, synchrotron X-ray imaging, especially tomography (SXCT) with hard X-Rays, plays an important role in structural 3D characterization. The imaging capabilities allow for in-situ and operando experiments. In this presentation the equipment, data handling pipeline as well as various examples from material science are presented. In series-connected lithium-ion cells are susceptible to an electrical safety hazard called over-discharge. Here the behavior of copper dissolution and deposition during over-discharge is presented, which leads to irreversible loss of capacity and internal short circuits. The concentration of dissolved and deposited copper is quantified. Also, a non-uniform distribution pattern of copper deposition on the cathode is shown. The second example deals with an Al alloy 7017 customized for a 3d-printing process by means of laser-based powder bed fusion (PBF-LB) technique. These advanced alloys have a significantly higher modulus of elasticity than conventional Al alloys, making them attractive for applications requiring high stiffness. SXCT during In-situ tensile tests confirmed that fracture initiation strongly depends on defects created during printing. However, the cracks are deflected from decohesion around inclusions/precipitates embedded in the Al matrix, increasing ductility. Low temperature cofired ceramic (LTCC) multilayer housings offer 3D-circuits for a wide range of applications in telecommunications, microsystems and sensor technology. Such housings are produced by combining structured and metallized ceramic layers using tape-casting and multilayer technology. The characterization of the integrity, deformation, defects, and positioning of the internal metal features was carried out using in-situ SXCT at up to 950°C. A high-precision nail penetration tool was developed to characterize the mechanically induced thermal runaway (TR) of lithium-ion battery (LIB) cells in a dynamic temperature range down to -190 °C. To investigate safety-specific low-temperature transport conditions, the damaged cells were tomographically imaged during thawing. T2 - ICTMS - International Conference on Materials and Structures 2024 CY - Cape Town, South Africa DA - 01.07.2024 KW - Synchrotron radiation KW - X-ray tomography KW - Li-ion battery PY - 2024 AN - OPUS4-60658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharpmann, Philippa T1 - Segregating the Degradation Mechanisms in Lithium-Ion Cells during Strongly Accelerated Ageing with Critically Extended Voltage Ranges N2 - Repurposing end-of-life (EOL) lithium-ion batteries from mobile applications, such as electric vehicles, is of utmost importance for a sustainable handling of scarce resources. For an economically and ecologically desirable reuse of aged batteries in second-life applications, a guarantee for safe and reliable operation is urgently required. However, the assessment of the state of safety (SOS) is not straightforward, as multiple abuse cases, variables and interactions need to be considered [1]. Therefore, defining safety parameters and test procedures, as well as determining the SOS requires a plethora of aged cells to be tested. In this study, a novel method of greatly accelerating the ageing process of lithium-ion batteries is proposed. Overcharging and overdischarging are embedded in cyclic ageing, continuously employing a depth of discharge larger than 100 %. Different electrical abuse conditions (overcharge, overdischarge, high current rates) are applied on lithium-ion NMC and LFP pouch cells in a preliminary test series. In this manner, the cells are stressed until a cell failure or a thermal runaway is induced. Thus, the critical state in proximity to a cell failure is spotted for individual and combined stress parameters. Based on this knowledge, a test protocol for strongly accelerated ageing with cell-specific, abusive electrical parameters is developed. The aging dynamics under these critical conditions are monitored by systematic capacity, open circuit voltage and electrochemical impedance spectroscopy (EIS) measurements. This enables an assessment of the degradation mechanisms induced by overdischarge and overcharge cycling. A special focus is set on the comparative assessment of the electrical behaviour, following conventional vs. greatly accelerated ageing. This novel method is suitable for providing cells with a defined SOH at a reasonable timescale. Furthermore, the results are of high relevance for the evaluation to which degree cyclic ageing can be accelerated without changing the characteristic degradation mechanisms of lithium-ion batteries. T2 - Advanced Battery Power Conference 2024 CY - Münster, Germany DA - 10.04.2024 KW - Lithium-Ion Battery KW - Safety KW - Ageing PY - 2024 AN - OPUS4-61492 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Overview of Battery Research Activities at BAM N2 - An overview on battery research activities of BAM was given using a seletion of activities of all work packages within the field of activity EES and selected activities of divsion 3.6. T2 - Boot Camp of the BAccara Graduate School on Batteries CY - Bad Sassendorf, Germany DA - 24.04.2024 KW - State of Safety KW - Compositional traceability KW - Sustainable energy materials KW - Sodium Ion Batteries PY - 2024 AN - OPUS4-61940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Chemie der Energiewende N2 - Es wurde ein Überblick über die BAM-Aktivitäten im Bereich Chemie der Energiewende gegeben. Dabei wurde ein Fokus auf Aktivitäten in Aktivitätsfeld EES und im Fachbereich 3.6 gelegt. T2 - 30 Jahre Naturwissenschaftliches Studium in Zittau CY - Zittau, Germany DA - 13.04.2024 KW - Chemie KW - Energiewende PY - 2024 AN - OPUS4-61941 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Sodium-Ion Battery Research and Testing at BAM N2 - An overview of activities at BAM on the topic of sodium ion batteries was given. Examples of the internal SIB-links project were given and a focus on novel synthetic anodes. T2 - Sodium Battery Sympoium-5 (2024) CY - Berlin, Germany DA - 23.09.2024 KW - Sodium ion batteries KW - Synthetic carbon anodes PY - 2024 AN - OPUS4-61944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick A1 - Krug von Nidda, Jonas T1 - Porous „Ionophoric“ Carbon Materials: Synthesis Routes and Electrochemical Applications N2 - Porous carbon materials play an important role for energy storage and conversion, e.g., as fuel cell catalysts, supercapacitor or battery electrodes. Tuning porosity features such as pore connectivity, specific surface area, maximum pore size and pore volume is one of the key strategies to improve the performance of those materials.[1] Moreover, the alteration of the chemistry allows further enhancement in performance, even leading to the applicability in new fields. In this context, nitrogen doped carbons (NDCs) are a very promising material class. Highly porous NDCs for example show interesting Na-storage features.[2] Moreover, the integration of iron ions in an NDC, forming FeN4-sites, can results in materials with very promising properties as fuel cell cathode catalysts.[3] However, to relate certain sites to specific performance indicators is still challenging as the variation of the present N-sites is very large in typically obtained NDCs. In the past, we were able to develop an ionothermal synthesis strategy which results in highly porous materials with specific, i.e., tetrapyrrolic, N4-sites.[4] Such N4 sites and there metal complexes are reminiscent of biomolecules like the heme molecule, which originally inspired the research on such materials.[5] The N4-sites are mainly occupied by Zn2+ as the synthesis is performed in a ZnCl2-containing salt melt. Moreover, the electrochemical performance of those materials can be rather easily altered upon removing/exchanging the Zn2+. Moreover, again looking at biomolecules, those kind of materials can be regarded as ionophoric carbons as they possess distinct, metal-binding N4-sites embedded in a carbon matrix. Herein, we will focus on the synthesis of zeolitic imidazolate framework (ZIF) based NDCs with high porosity. We will discuss different strategies to remove and/or exchange Zn2+ in the obtained ZnN4-containing materials. Different analytical methods, e.g., physisorption (N2, Ar, CO2), XPS, XAS, and NMR, will be used to understand the alteration of morphological and chemical features upon ion exchange (see Figure 1). Figure 1: A) Schematic illustration of the partial Zn-removal in a ZnN4-containing, ionophoric carbon. B) High resolution N 1s XPS-results of a ZIF-derived ionophoric carbon before and after metal leaching. Due to the ion exchange/removal, the chemistry of the NDCs is altered, however, typically preserving the porosity features as well as the general structure of the N-motifs. Thus, the influence of the occupancy of the N4-sites on the electrochemical performance can be studied in detail. Finally, structure-property-relations of the different ZIF-derived ionophoric NDCs regarding the performance as anodes in sodium ion batteries will be discussed. T2 - Deutsche Zeolith-Tagung 2024 CY - Jena, Germany DA - 28.02.2024 KW - Ionophoric carbon KW - Sodium ion battery KW - PGM-free catalysts PY - 2024 AN - OPUS4-61955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - DialySorb und Eigenschaften kommerzieller Zellen N2 - In dem Vortrag wurden zunächst die Eigenschaften erster kommerzieller Natrium-Ionen-Batterien vorgestellt, die an der BAM elektrotechnisch untersucht wurden und auf ihre Bestandteile hin analysiert wurden. Weiterhin wurden die aktuellen Projektergebnisse des BMBF-geförderten Verbundprojekts Dialysorb vorgestellt. T2 - KLiB-Gesprächsrunde zu Natrium-Ionen-Batterien und Festkörperbatterien CY - Frankfurt am Main, Germany DA - 09.07.2024 KW - Natrium-Ionen-Batterien PY - 2024 AN - OPUS4-61942 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Leveraging the Potential of Na-Ion-Batteries with Tailormade Anodes N2 - The concept of sodium-ion-batteries and their expected impact for the energy change is introduced, by explaining differences to lithium-ion-batteries. The challenge as well as the potential may be illustrated on the example of novel carbon anodes.While the general suitability is proven since the recent commercialization, limitations and detailed structure-performance relations remain topic to research. The progress in activities of BAM division 3.6 are illustrated further supporting the future impact of the technology. T2 - TechConnect Adlershof 2024: Sustainable Energy Future CY - Berlin, Germany DA - 09.11.2024 KW - Synthetic Carbon Anodes PY - 2024 AN - OPUS4-61947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Research on Synthetic Anodes for Na-Ion-Batteries N2 - Carbons with an amorphous structure are currently revisited as candidates for Li- and Na-ion batteries. High irreversible capacities (due to SEI formation) were considered an intrinsic problem of such hard carbons, rendering them irrelevant for practical use. Amorphous carbon anodes would present safety-related advantages such as lower heat dissipation throughout lithiation per mol of lithium, mechanical stability throughout cycling and a larger set of optional electrolytes. T2 - Advanced Automotive Battery Conference Europe 2024 CY - Strasbourg, France DA - 13.05.2024 KW - Synthetic Carbon Anodes PY - 2024 AN - OPUS4-61956 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -