TY - CONF A1 - Bresch, Sophie T1 - Pressure-assisted sintering of tape cast calcium cobaltite for thermoelectric applications N2 - Thermoelectric materials can convert waste heat directly into electrical power by using the Seebeck effect. Calcium cobaltite Ca3Co4O9 is a promising p-type oxide thermoelectric material for applications between 600 °C and 900 °C in air. The properties and morphology of Ca3Co4O9 are strongly anisotropic because of its crystal structure of alternating layers of CoO2 and Ca2CoO3. By aligning the plate-like grains, the anisotropic properties can be assigned to the component. Pressure-assisted sintering (PAS), as known from large-scale production of low temperature co-fired ceramics, was used to sinter multilayers of Ca3Co4O9 green tape at 900 °C with different pressures and dwell times. In-situ shrinkage measurements, microstructural investigations and electric measurements were performed. Pressure-less sintered multilayers have a 2.5 times higher electrical conductivity at room temperature than dry pressed test bars with randomly oriented particles. The combination of tape casting and PAS induces a pronounced alignment of the anisotropic grains. Relative density increases from 57 % after free sintering for 24 h to 94 % after 2 h of PAS with 10 MPa axial load. By applying a uniaxial pressure of 10 MPa during sintering, the electrical conductivity (at 25°C) improves by a factor of 15 compared to test bars with randomly oriented particles. The high temperature thermoelectric properties show the same dependencies. The smaller the applied axial load, the lower the relative densities, and the lower the electrical conductivity. Longer dwell times may increase the density and the electrical conductivity significantly if the microstructure is less densified as in the case of a small axial load like 2 MPa. At higher applied pressures the dwell time has no significant influence on the thermoelectric properties. This study shows that PAS is a proper technique to produce dense Ca3Co4O9 panels with good thermoelectric properties similar to hot-pressed tablets, even in large-scale production. T2 - Electroceramics XVI CY - Hasselt, Belgium DA - 09.07.2018 KW - Texturation KW - Hot Press KW - Calcination KW - Multilayer PY - 2018 AN - OPUS4-45491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bresch, Sophie A1 - Mieller, Björn A1 - Selleng, Christian A1 - Stöcker, T. A1 - Moos, R. A1 - Rabe, Torsten T1 - Influence of the calcination procedure on the thermoelectric properties of calcium cobaltite Ca3Co4O9 N2 - Calcium cobaltite is one of the most promising oxide p-type thermoelectric materials. The solid-state reaction (or calcination, respectively), which is well known for large-scale powder synthesis of functional materials, can also be used for the synthesis of thermoelectric oxides. There are various calcination routines in literature for Ca3Co4O9 powder synthesis, but no systematic study has been done on the influence of calcination procedure on thermoelectric properties. Therefore, the influence of calcination conditions on the Seebeck coefficient and the electrical conductivity was studied by modifying calcination temperature, dwell time, particle size of raw materials and number of calcination cycles. This study shows that elevated temperatures, longer dwell times, or repeated calcinations during powder synthesis do not improve but deteriorate the thermoelectric properties of calcium cobaltite. Diffusion during calcination leads to idiomorphic grain growth, which lowers the driving force for sintering of the calcined powder. A lower driving force for sintering reduces the densification. The electrical conductivity increases linearly with densification. The calcination procedure barely influences the Seebeck coefficient. The calcination procedure has no influence on the phase formation of the sintered specimens. KW - Thermoelectrics KW - Calcination KW - Calcium Cobaltite KW - Solid-State-Synthesis KW - Reaction-sintering PY - 2018 DO - https://doi.org/10.1007/s10832-018-0124-3 SN - 1385-3449 SN - 1573-8663 VL - 40 IS - 3 SP - 225 EP - 234 PB - Springer AN - OPUS4-44336 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kardjilov, N. T1 - Quantification of hydrogen in metals applying neutron imaging techniques N2 - Hydrogen interaction with metals is well known to have severe detrimental effects on their mechanical properties. The use of modern high-strength steels, which are attractive to improve fuel economy by reducing weight as well as candidates for H storage cylinders and other components, is currently being severely limited by the fact that the presence of H can cause embrittlement of the material. In addition to steel, several other metals and alloys used in the nuclear industry, like Ti and Zr, are susceptible to H degradation through hydride formation and subsequent cracking. Microstructure-specific H mapping has been recognized as the most important challenge on the pathway towards a better understanding of the nature of H embrittlement in metallic alloys as well as the development of H storage solutions based on metal hydrides. Unfortunately, the characterization of H interactions with metals is an extremely challenging task and neutron-based techniques are of exceptional importance in this matter because – contrary to X-rays and electrons – thermal and cold neutrons interact strongly with the H nuclei, while the neutron beam is only weakly attenuated by the relevant metallic materials. Therefore, hydrogen distributions can be measured and quantified even in 3D by tomographic methods. Here we present several neutron imaging investigations of embrittlement and cracking in Fe and Zr based metal alloys and optimization studies of hydrogen storage systems containing metal hydrides as an active substance. The advantages and the limitations of the experimental methods as well as the attempts for hydrogen quantification will be discussed in detail. T2 - M&M 2022 Annual Meeting (Microscopy & Microanalysis) CY - Portland, Oregon, USA DA - 31.07.2022 KW - Neutron imaging techniques KW - Hydrogen in metals PY - 2022 DO - https://doi.org/10.1017/S1431927622006638 AN - OPUS4-55716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mieller, Björn T1 - Synthesis and testing of beta aluminate sodium electrolyte (BASE) for sodium ion battery development N2 - Sodium beta aluminate, or beta aluminate solid electrolyte (BASE), is an established material for tubular electrolytes in NaNiCl2 and NaS batteries, and a promising candidate for planar electrolytes in safe all solid-state batteries. The synthesis of BASE with high ionic conductivity is still challenging due to process dependent formation of different phases in the sintered material. However, to drive forward the development of active materials for all solid-state sodium ion batteries, the fabrication of solid electrolyte specimens with reproducible performance is required. With respect to the various testing scenarios in the field, for example cell assembly for cycling, electrolyte parts are needed in various shapes, sizes, and thicknesses in the lab. Different ceramic shaping technologies can be applied to produce such geometries, including pressing combined with green or hard machining, or tape casting combined with punching. Typically, different shaping technologies require adapted pre-treatment of the powder which might affect the resulting properties and thus need to be investigated. In this contribution, starting from the raw materials mixture, aspects of milling, drying, aqueous slurry preparation for tape casting, and firing are discussed with respect to particle size distribution, stability, energy consumption and resulting material properties. Finally, the fabrication and cyclic testing of Na/electrolyte/Na coin cells is presented. T2 - XIXth Conference of the European Ceramic Society / SBS6 International Sodium Battery Symposium CY - Dresden, Germany DA - 01.09.2025 KW - Ceramics KW - Beta aluminate solid electrolyte KW - Sodium ion battery PY - 2025 AN - OPUS4-64054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zheng, Y. A1 - Zhang, S. A1 - Ma, J. A1 - Sun, F. A1 - Osenberg, M. A1 - Hilger, A. A1 - Markötter, Henning A1 - Wilde, F. A1 - Manke, I. A1 - Hu, Z. A1 - Cui, G. T1 - Codependent failure mechanisms between cathode and anode in solid state lithium metal batteries: mediated by uneven ion flux N2 - An in-depth understanding of the degradation mechanisms is a prerequisite for developing the nextgeneration all solid-state lithium metal battery (ASSLMB) technology. Herein, synchrotron X-ray computed tomography (SXCT) together with other probing tools and simulation method were employed to rediscover the decaying mechanisms of LiNi0.8Co0.1Mn0.1O2 (NCM)|Li6PS5Cl (LPSCl)|Li ASSLMB. It reveals that the detachment and isolation of NCM particles cause the current focusing on the remaining active regions of cathode. The extent of Li stripping and the likelihood of Li+ plating into LPSCl facing the active NCM particles becomes higher. Besides, the homogeneity of Li stripping/plating is improved by homogenizing the electrochemical reactions at the cathode side by LiZr2(PO4)3 (LZP) coating. These results suggest a codependent failure mechanism between cathode and anode that is mediated by uneven Li ion flux. This work contributes to establish a holistic understanding of the degradation mechanisms in ASSLMBs and opens new opportunities for their further optimization and evelopment. KW - Current density distribution KW - Lithium ion flux KW - Solid-state lithium metal batteries KW - Codependent failure mechanism KW - Cathode deactivation PY - 2023 DO - https://doi.org/10.1016/j.scib.2023.03.021 SN - 2095-9273 VL - 68 IS - 8 SP - 813 EP - 825 PB - Elsevier B.V. AN - OPUS4-57309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tötzke, C. A1 - Gaiselmann, G. A1 - Osenberg, M. A1 - Arlt, Tobias A1 - Markötter, Henning A1 - Hilger, A. A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Schmidt, V. A1 - Lehnert, W. A1 - Manke, I. T1 - Influence of hydrophobic treatment on the structure of compressed gas diffusion layers N2 - Carbon fiber based felt materials are widely used as gas diffusion layer (GDL) in fuel cells. Their transport properties can be adjusted by adding hydrophobic agents such as polytetrafluoroethylene (PTFE). We present a synchrotron X-ray tomographic study on the felt material Freudenberg H2315 with different PTFE finishing. In this study, we analyze changes in microstructure and shape of GDLs at increasing degree of compression which are related to their specific PTFE load. A dedicated compression device mimicking the channel-land pattern of the flowfield is used to reproduce the inhomogeneous compression found in a fuel cell. Transport relevant geometrical parameters such as porosity, pore size distribution and geometric tortuosity are calculated and consequences for media transport discussed. PTFE finishing results in a marked change of shape of compressed GDLs: surface is smoothed and the invasion of GDL fibers into the flow field channel strongly mitigated. Furthermore, the PTFE impacts the microstructure of the compressed GDL. The number of available wide transport paths is significantly increased as compared to the untreated material. These changes improve the transport capacity liquid water through the GDL and promote the discharge of liquid water droplets from the cell. KW - Gas diffusion layer KW - Synchrotron Tomography KW - Compression KW - Hydrophobic treatment KW - Water transport PY - 2016 DO - https://doi.org/10.1016/j.jpowsour.2016.05.118 SN - 0378-7753 VL - 324 SP - 625 EP - 636 PB - Elsevier CY - Amsterdam AN - OPUS4-36918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, T. A1 - Reimann, T. A1 - Bochmann, A. A1 - Vogel, A. A1 - Capraro, B. A1 - Mieller, Björn A1 - Teichert, S. A1 - Töpfer, J. T1 - Sintering behavior, microstructure and thermoelectric properties of calcium cobaltite thickfilms for transversal thermoelectric multilayer generators N2 - The sintering behavior and the thermoelectric performance of Ca3Co4O9 multilayer laminates were studied, and a multilayer thermoelectric generator was fabricated. Compacts and multilayer samples with anisotropic microstructure and residual porosity were obtained after conventional sintering at 920 °C, whereas dense and isotropic multilayer samples were prepared by firing at 1200 °C and reoxidation at 900 °C. A hot-pressed sample has a dense and anisotropic microstructure. Samples sintered at 920 °C exhibit low electrical conductivity due to the low density, whereas the Seebeck coefficient is not sensitive to preparation conditions. However, thermal conductivity of multilayers is very low, and, hence acceptable ZT values are obtained. A ransversal multilayer thermoelectric generator (TMLTEG) was fabricated by stacking layers of Ca3Co4O9 green tapes, AgPd conductor printing, and co-firing at 920 °C. The TMLTEG has a power output of 3 mW at ΔT =200 K in the temperature interval of 25 °C to 300 °C. KW - Thermoelectric oxide KW - Calcium cobaltite KW - Pressure-assisted sintering KW - Multilayer PY - 2018 DO - https://doi.org/10.1016/j.jeurceramsoc.2017.11.017 SN - 0955-2219 SN - 1873-619X VL - 38 IS - 4 SP - 1600 EP - 1607 PB - Elsevier Ltd. AN - OPUS4-43983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Widjaja, Martinus Putra A1 - Alves, M. A1 - Mavrogordato, M. A1 - Joannes, S. A1 - Bunsell, A. A1 - Mair, Georg W. A1 - Thionnet, A. T1 - Effect of the Time Dependent Loading of Type IV Cylinders Using a Multiscale Model N2 - The Reduced Volume Method (RVM) has been used to evaluate the multiscale fibre break model developed at Mines ParisTech. It allows the model to be assigned only at certain part of the structures without necessarily compromising the final prediction. An attempt to model a simple unidirectional composite structure has also been carried out and gave a satisfying result. This paper deals with the application of the RVM to real scale type IV composite cylinders, where its stacking sequence was evaluated through micro-CT scans conducted with the collaboration of the University of Southampton. Two modelling geometries were evaluated and compared with the corresponding experimental results. T2 - 8th International Conference on Hydrogen Safety (ICHS) CY - Adelaide, Australia DA - 24.09.2019 KW - Fibre break KW - Multiscale modelling KW - Type IV pressure vessel KW - Time dependent loading PY - 2019 SP - ID131 AN - OPUS4-49273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Widjaja, Martinus Putra T1 - General update of the PhD work for mid_term consortium meeting N2 - Before the multiscale model is used to calculate real scale composite structures, a study to improve the effectiveness is required, especially the computation time. The reduced volume method has been studied and proved to be useful for the multiscale model of Mines ParisTech. T2 - Mid_Term Consortium Meeting of FiBreMoD CY - Imperial College London, United Kingdom DA - 11.09.2018 KW - Reduced volume method KW - Integral range KW - Composite pressure vessels KW - Multiscale model KW - Fibre breaks PY - 2018 AN - OPUS4-48570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bresch, Sophie T1 - Material development for oxide multilayer generators N2 - Thermoelectric generators can be used for energy harvesting by directly transforming a temperature gradient into a voltage. Multilayer generators based on low-temperature co-fired ceramics technology (LTCC) are an interesting alternative to conventional π-type generators. They exhibit several advantages like high filling factor, possibility of texturing, co-firing of all materials in one single-step, and reduction of production costs due to the high possible degree of automation. Pressure-assisted sintering enables the theoretical possibility of co-firing two promising oxide thermoelectric materials: Ca3Co4O9 (p-type) and CaMnO3 (n-type). Due to the large difference in sintering temperature (300 K) the process is very challenging. In this work we show the material development of Ca3Co4O9, CaMnO3, insulation and metallization for multilayer generators co-fired under pressure at 900 °C. The materials are tailored regarding their sintering behavior, electrical performance and coefficients of thermal expansion. Different generator designs (unileg and pn-type) were fabricated and analyzed regarding crack formation, interaction layers and thermoelectric performance. Simulated stresses during cooling in the multilayers are compared with actual crack formation for different sintering conditions. This study shows that a lower pressure level and a lower level of complexity are beneficial for co-firing and performance. T2 - 45th International Conference and Expo on Advanced Ceramics and Composites (ICACC 2021 Virtual) CY - Online meeting DA - 08.02.2021 KW - Thermoelectrics KW - Multilayer PY - 2021 AN - OPUS4-52462 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Spitzer, Stefan A1 - Adamus, Wojciech A1 - Askar, Enis A1 - Benke, Alexander A1 - D’Hyon, Sebastian A1 - Dyduch, Zdzislaw A1 - Dufaud, Olivier A1 - Flemming, Friederike A1 - Gehle, Nicole A1 - Hohenberger, Michael A1 - Jankuj, Vojtech A1 - Jian, Wang A1 - Krietsch, Arne A1 - Kuracina, Richard A1 - Mynarz, Miroslav A1 - Norman, Frederik A1 - Osborne, David A1 - Prodan, Maria A1 - Sandsta, Nelly A1 - Toman, Adrian A1 - Skjold, Trygve A1 - Skrinsky, Jan A1 - Szabova, Zuzana A1 - Vignes, Alexis A1 - Wingerden, Mattheus van A1 - Zhong, Shenjung T1 - Validation of a new standard for safety characteristics of hybrid mixtures: HYBRID II N2 - Safety characteristics are used for the safe operation of processes. Designing protection measures requires explosion characteristics to be determined, namely the maximum explosion pressure and the maximum rate of pressure rise. Safety characteristics of single-phase components (solid, liquid or gas) can be determined according to standards that were developed 40 years ago and are continuously improved. For hybrid mixtures containing a flammable gas and a combustible dust there has been an approach in the 80s but it has never been improved nor applied ever since (ISO 6184-3). A new approach by four German research facilities and the German Institute for standardization (DIN) with the aim of developing a new standard was launched in 2019. In 2022 the key findings led to a first international round robin test with eleven participating facilities from seven countries. The dust component was corn starch and methane was chosen as gas component. In order to strengthen the data foundation before finalizing and publishing the new standard, a second round robin test was initiated with hydrogen as gas component and lycopodium as dust. The paper will summarize the findings and their influence on the new standard. KW - Explosionsschutz KW - Anlagensicherheit KW - Konstruktiver Explosionsschutz KW - Hybride Gemische KW - Round robin tests KW - Hybrid mixtures KW - Industrial explosions KW - Safety characteristics PY - 2025 DO - https://doi.org/10.1016/j.jlp.2025.105560 SN - 1873-3352 VL - 94 SP - 1 EP - 6 PB - Elsevier Ltd. AN - OPUS4-62486 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Martínez, E. A1 - Lejeune, N. A1 - Frechilla, J. A1 - Porta-Velilla, L. A1 - Forneau, E. A1 - Angurel, L. A. A1 - de la Fuente, G. F. A1 - Bonse, Jörn A1 - Silhanek, A. V. A1 - Badía-Majós, A. T1 - Laser engineered architectures for magnetic flux manipulation on superconducting Nb thin films N2 - Custom shaped magnetic flux guiding channels have been fabricated on superconducting Nb thin films by laser nanopatterning of their surface. Preferential pathways are defined by suitable combination of imprinted anisotropic pinning domains through laser-induced periodic surface structures (LIPSS). Generated by the selective energy deposition of femtosecond UV laser pulses, quasi-parallel ripple structures are formed under optimized irradiation conditions. On average, each domain is formed by grooves with a lateral period of 260–270 nm and a depth about 80 nm. By combination of scanning and transmission electron microscopy, magneto-optical imaging, and conductive atomic force microscopy techniques, we conclude that the boundaries of the LIPSS-covered domains play a prominent role in the magnetic flux diversion process within the film. This is confirmed by dedicated modeling of the flux dynamics, combined with the inversion of the magneto-optical signal. The created metasurfaces enable control of the flux penetration process at the microscale. KW - Laser-induced periodic surface structures (LIPSS) KW - Magnetic flux KW - Magneto-optical imaging (MOI) KW - Critical current density PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611243 UR - https://www.sciencedirect.com/science/article/pii/S0169433224019287 DO - https://doi.org/10.1016/j.apsusc.2024.161214 SN - 1873-5584 (Online) SN - 0169-4332 (Print) VL - 679 SP - 1 EP - 12 PB - Elsevier AN - OPUS4-61124 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Averin, Anton T1 - Automated thermographic inspection of radioactive waste drums N2 - In Germany, more than 130,000 cubic meters of low- and medium-level radioactive waste, comprising approximately 90% of the nation’s total radioactive waste, are stored in 200-liter drums. These waste drums, housed in interim storage facilities, are subject to human visual inspections for outer corrosion, while the final disposal site, the Konrad mine, is scheduled for completion in 2030. Manual inspections introduce the risk of human error, making the process less reliable and less safe. The proposed study aims to automate these inspections by implementing remote and non-destructive testing (NDT) methods. The part of project specifically focuses on the application of infrared thermography to detect inner defects in the metallic drums, which could not have been detected so far using visual inspection alone. However, several challenges affect the accuracy of thermographic inspections, such as the presence of surface contaminants (scratches, dirt, stickers), multiple paint layers with low thermal conductivity, and barrel curvature, which disrupt heat distribution and obscure defect signals. This study explores the effectiveness of various thermographic heat sources—flash lamps and laser—as well as techniques including conventional pulse thermography (PT), lock-in thermography. It explores various thermal data processing methods as principal component thermography (PCT), pulse-phase thermography (PPT) and thermal signal reconstruction (TSR). Additionally, machine learning models were estimated to process thermographic images, effectively filtering artifacts (e.g. surface contaminants). The findings suggest that combining advanced thermography techniques with machine learning improves defect detection, ensuring more reliable and automated inspection processes for radioactive waste storage. T2 - SPIE Defense + Commercial Sensing - Thermosense: Thermal Infrared Applications XLVII CY - Orlando, FL, USA DA - 13.04.2025 KW - Automated inspection KW - Defect detection KW - Infrared thermography KW - Laser thermography KW - Machine Learning KW - Principal component thermography KW - Pulse-phase thermography KW - Thermal Data Processing PY - 2025 UR - https://www.spiedigitallibrary.org/conference-proceedings-of-spie/13470/3052732/Automated-thermographic-inspection-of-radioactive-waste-drums/10.1117/12.3052732.short DO - https://doi.org/10.1117/12.3052732 SP - 1 EP - 19 PB - SPIE AN - OPUS4-63285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Saegusa, T. ED - Sert, G. ED - Völzke, Holger ED - Wille, Frank T1 - Basics of Transport and Storage of Radioactive Materials N2 - Transport and storage of radioactive materials are performed in countries with policy of either closed or open nuclear fuel cycle. The related technologies have been established by accumulation of experiences and researches including demonstrative tests using full scale or scale models and analyses. Those are essential before commercialization, but are often costly and time consuming. Such demonstrative works should not be repeated meaninglessly, but can be shared through this kind of book and used by readers and the future generations to advance the technology effectively. This book systematically provides findings from lots of valuable researches on safety of transport and storage of radioactive materials under normal and accident conditions that have an impact on basis of safe regulations, designs, and operations. KW - Drop testing KW - Metal seals KW - Transport safety KW - Aging management KW - Package PY - 2018 SN - 978-981-323-405-5 SN - 978-981-323-404-8 SN - 978-981-323-403-1 DO - https://doi.org/10.1142/10820 SP - 1 EP - 376 PB - Worlds Scientific Publishing Co Pte Ltd CY - Singapore AN - OPUS4-44867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jankuj, V. A1 - Spitzer, Stefan A1 - Krietsch, Arne A1 - Bernatik, A. T1 - Safety of Alternative Energy Sources: a Review N2 - The article summarizes a short review of the literature focused on safety in the field of alternative energy sources. With an increasing orientation towards sustainable and renewable energy sources, new technologies will come to the fore. These facts must be demonstrated in occupational health and safety. Several studies focused on alternative energy sources are mentioned and show the trends for the future. Especially in the area of hydrogen and battery technologies, systems should pay attention to acquisitions as a normal part of our lives. Safety research is essential for the acceptance of cleaner, efficient, and sustainable future. T2 - Loss Prevention CY - Prag, Czechia DA - 06.06.2022 KW - Safety KW - Alternative Energy Sources PY - 2022 DO - https://doi.org/10.3303/CET2290020 SN - 2283-9216 VL - 90 SP - 115 EP - 120 PB - AIDIC CY - Milano AN - OPUS4-55030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn T1 - Laser Nanotexturierung von Metalloberflächen zur Reduktion von Reibung und Verschleiß N2 - Die Reduktion von Reibung und Verschleiß in technischen Systemen bietet ein großes Potenzial zur Reduktion von CO2-Emissionen. Dieser Beitrag diskutiert die Erzeugung und tribologische Charakterisierung von Ultrakurzpuls-generierten Nanostrukturen auf Metallen (Stahl, Titan). Besonderes Augenmerk wird dabei auf die Rolle der laserinduzierten Oxidschicht im Zusammenspiel mit verschleißreduzierenden Additiven in ölbasierten Schmiermitteln gerichtet. T2 - Internationale Bodensee Fachtagung „Wärmebehandlung und Oberflächentechnik zur Verbesserung von Tribologie und Verschleissbeständigkeit" CY - Feldkirch, Austria DA - 20.03.2025 KW - Additive KW - Laser-induzierte periodische Nanostrukturen KW - Reibungsreduktion KW - Verschleißreduktion PY - 2025 AN - OPUS4-62757 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lucaßen, J. T1 - Bottom-up grown CISe micro absorber arrays: microstructure analysis and solar cell integration N2 - A reduction of critical raw materials like indium and gallium in chalcopyrite thin-film solar cells is aimed for the micro-concentrator concept. Bottom-up grown micro absorbers for operation under light concentration on the micrometer scale allow improved heat dissipation. T2 - 41st European Photovoltaic Solar Energy Conference and Exhibition (EU PVSEC 2024) CY - Vienna, Austria DA - 23.09.2024 KW - Laser-assisted MO-CVD KW - CISe micro-absorber KW - Micro solar cell arrays KW - Solar cell efficiency PY - 2024 AN - OPUS4-62075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Claudia T1 - Ensuring Quality Smarter with a digital Quality Infrastructure (Mexican-German Technical Exchange) N2 - The presentation introduces the initiative QI‑Digital, which aims to holistically transform quality infrastructure across all its elements. To this end, a digital QI ecosystem is being developed that integrates digital QI tools with advanced methods for testing, inspection, and monitoring, and embeds them into the broader digital industrial ecosystem. Sovereign and secure data sharing and management are enabled through technologies such as data spaces, the Asset Administration Shell, verifiable credentials, and the Digital Product Passport (DPP). Particular emphasis is placed on the role of artificial intelligence in quality assurance: Several use cases and ongoing projects from BAM are presented togetehr with the business benefits they enable. Ongoing activities on the use of AI for manageing quality-related documentation are also presentated that aim at establishing an agentic AI framework for QI. The talk concludes with key lessons learned so far within the initiative. T2 - Mexican-German Technical Exchange on QI Digital CY - Mexico City, Mexico DA - 23.01.2026 KW - Quality infrastructure KW - Agentic AI KW - Digital Ecosystem PY - 2025 AN - OPUS4-65411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kulkarni, Kajol A1 - Kemmler, Samuel A1 - Schwartz, Anna A1 - Gedik, Gülçin A1 - Chen, Yanxiang A1 - Papageorgiou, Dimitrios A1 - Kavroulakis, Ioannis A1 - Iakymchuk, Roman T1 - Harvesting energy consumption on European HPC systems: Sharing Experience from the CEEC project N2 - Energy efficiency has emerged as a central challenge for modern high-performance computing (HPC) systems, where escalating computational demands and architectural complexity have led to significant energy footprints. This paper presents the collective experience of the EuroHPC JU Center of Excellence in Exascale CFD (CEEC) in measuring, analyzing, and optimizing energy consumption across major European HPC systems. We briefly review key methodologies and tools for energy measurement as well as define metrics for reporting results. Through case studies using representative CFD applications (waLBerla, FLEXI/GALÆXI, Neko, and NekRS), we evaluate energy-to-solution and time-to-solution on diverse architectures, including CPU- and GPU-based partitions of LUMI, MareNostrum5, MeluXina, and JUWELS Booster. Our results highlight the advantages of accelerators and mixed-precision techniques for reducing energy consumption while maintaining computational accuracy. Finally, we advocate the need to facilitate energy measurements on HPC systems in order to raise awareness, teach the community, and take actions toward more sustainable exascale computing. T2 - SCA/HPCAsiaWS 2026: SCA/HPCAsia 2026 Workshops: Supercomputing Asia and International Conference on High Performance Computing in Asia Pacific Region Workshops CY - Osaka , Japan DA - 26.01.2026 KW - Energy consumption KW - eEergy measurement KW - Energy-to-solution KW - Mixed-precision KW - HPC KW - CFD PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654175 DO - https://doi.org/10.1145/3784828.3785161 SP - 40 EP - 49 PB - ACM CY - New York, NY, USA AN - OPUS4-65417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bresch, Sophie T1 - Pressure assisted sintering of tape cast calcium cobaltite N2 - Thermoelectric materials can convert waste heat directly into electrical power by utilizing the Seebeck effect. Calcium cobaltite Ca3Co4O9 is a promising p-type oxide thermoelectric material for applications between 600 °C and 900 °C in air. The properties and morphology of Ca3Co4O9 are strongly anisotropic because of its crystal structure of alternating layers of CoO2 and Ca2CoO3. The electrical conductivity is for example 13.5 times higher in a/b-direction than in c-direction. By aligning the plate-like grains, the anisotropic properties can be assigned to the component. Hot-pressing of tablets is a well-known technology for grain alignment of Ca3Co4O9 and increases the thermoelectric properties in a/b-direction remarkably. It also increases the relative density. However, hot-pressing of tablets is limited by the tablet size. An interesting alternative for larger components is the pressure assisted sintering of panels from tape casted layers. Tape casting already leads to a grain alignment during green body forming. By combining tape casting and pressure assisted sintering (50 kN maximum force) of Ca3Co4O9, high densities and high thermoelectric properties can be reached for large components up to 200 mm edge length. Ca3Co4O9 was successfully tape casted with the doctor blade technique (binder: polyvinyl butyral, organic solvent). Several layers of tape were stacked and laminated to 5 cm x 5 cm panels. These panels were sintered with different applied pressures in a LTCC sintering press with combined in-situ shrinkage measurement. Pressure-less sintered panels have a 2.5 times higher electrical conductivity at room temperature than test bars with randomly orientated particles. By applying a uniaxial pressure of 10 MPa during sintering, the electrical conductivity increases by the factor of 6 compared to the pressure-less sintered panels. About 40 % linear shrinkage are reached in pressing direction. The Seebeck coefficient (S25 °C=146 μV/K) and the electrical conductivity (σ25 °C=15100 S/m) are in good agreement with the values published in literature for hot-pressed tablets. T2 - 15th Conference & Exhibition of the European Ceramic Society CY - Budapest, Hungary DA - 09.07.2017 KW - Thermoelectrics KW - Pressure assisted sintering PY - 2017 AN - OPUS4-41026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -