TY - CONF A1 - Bresch, Sophie T1 - Pressure assisted sintering of tape cast calcium cobaltite N2 - Thermoelectric materials can convert waste heat directly into electrical power by utilizing the Seebeck effect. Calcium cobaltite Ca3Co4O9 is a promising p-type oxide thermoelectric material for applications between 600 °C and 900 °C in air. The properties and morphology of Ca3Co4O9 are strongly anisotropic because of its crystal structure of alternating layers of CoO2 and Ca2CoO3. The electrical conductivity is for example 13.5 times higher in a/b-direction than in c-direction. By aligning the plate-like grains, the anisotropic properties can be assigned to the component. Hot-pressing of tablets is a well-known technology for grain alignment of Ca3Co4O9 and increases the thermoelectric properties in a/b-direction remarkably. It also increases the relative density. However, hot-pressing of tablets is limited by the tablet size. An interesting alternative for larger components is the pressure assisted sintering of panels from tape casted layers. Tape casting already leads to a grain alignment during green body forming. By combining tape casting and pressure assisted sintering (50 kN maximum force) of Ca3Co4O9, high densities and high thermoelectric properties can be reached for large components up to 200 mm edge length. Ca3Co4O9 was successfully tape casted with the doctor blade technique (binder: polyvinyl butyral, organic solvent). Several layers of tape were stacked and laminated to 5 cm x 5 cm panels. These panels were sintered with different applied pressures in a LTCC sintering press with combined in-situ shrinkage measurement. Pressure-less sintered panels have a 2.5 times higher electrical conductivity at room temperature than test bars with randomly orientated particles. By applying a uniaxial pressure of 10 MPa during sintering, the electrical conductivity increases by the factor of 6 compared to the pressure-less sintered panels. About 40 % linear shrinkage are reached in pressing direction. The Seebeck coefficient (S25 °C=146 μV/K) and the electrical conductivity (σ25 °C=15100 S/m) are in good agreement with the values published in literature for hot-pressed tablets. T2 - 15th Conference & Exhibition of the European Ceramic Society CY - Budapest, Hungary DA - 09.07.2017 KW - Thermoelectrics KW - Pressure assisted sintering PY - 2017 AN - OPUS4-41026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Fedelich, Bernard A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Thermo-mechanical fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the thermo-mechanical fatigue and creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard LCF/TMF-tests as well as near-service loading tests with different hold times have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics (like e.g. pronounced softening) and the dominating damage mechanisms under different loads. The test programme is complemented by selected tests on service-aged material which demonstrate possible reactions of older components in existing plants to changes in operation profiles. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - LCF08 CY - Dresden, Germany DA - 27.06.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Thermo-Mechanical Fatigue PY - 2017 SN - 978-3-9814516-5-8 VL - 2017 SP - 101 EP - 105 PB - DVM CY - Berlin AN - OPUS4-42268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria T1 - Betriebsnahe LCF- und TMF-Untersuchungen an ferritsch-martensitischen Chromstählen N2 - Betriebsnahe LCF- und TMF-Untersuchungen an P92, Vorstellung erster Versuchsergebnisse T2 - DVM Arbeitskreis Bauteilverhalten bei thermomechanischer Ermüdung CY - Berlin, Germany DA - 06.04.2017 KW - P92 KW - TMF KW - LCF PY - 2017 AN - OPUS4-39831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria T1 - Creep fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard creep-tests as well as LCF/TMF tests with hold time have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics and the dominating damage mechanisms under different loads. The test programme is complemented by cyclic creep-tests (temperature change) and creep-tests under atmospheres. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - ECCC 2017 CY - Düsseldorf, Germany DA - 10.09.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Creep-Fatigue PY - 2017 AN - OPUS4-42269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Requirements for the use of elastomer seals in casks for final disposal of low and intermediate level waste N2 - Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period. In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits. Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to: - ensure full functionality until final container disposal, - maintain its function in case of a thermal or mechanical accident, - ensure encapsulation also at -20 °C. This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated. This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results. T2 - 13th International Symposium "Conditioning of Radioactive Operational & Decomissioning Wastes" CY - Dresden, Germany DA - 22.03.2017 KW - Disposal KW - Konrad repository KW - Seal KW - Ageing PY - 2017 AN - OPUS4-39868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stengel, Dominik A1 - Thiele, K. T1 - Measurements of downburst wind loading acting on an overhead transmission line in Northern Germany N2 - Along an overhead transmission line in Northern Germany, a unique instrumentation of anemometers and force measurements is installed. Details of this test line with wind measurements along a horizontal axis are given. A recent event of a presumable downburst wind event is analyzed by means of available data and precedent works on thunderstorm analysis. The measured response of the conductors at the suspension tower is investigated and compared with time domain simulation of a finite element model. T2 - X International Conference on Structural Dynamics, EURODYN 2017 CY - Rome, Italy DA - 10.09.2017 KW - Non-synoptic wind event KW - Downburst KW - Overhead transmission line KW - Finite element method PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-421239 DO - https://doi.org/10.1016/j.proeng.2017.09.578 SN - 1877-7058 VL - 199 IS - Supplement C SP - 3152 EP - 3157 PB - Elsevier AN - OPUS4-42123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mitzscherling, Steffen A1 - Barth, Enrico A1 - Götschel, S. A1 - Homann, Tobias A1 - Prager, Jens A1 - Weiser, M. T1 - Verbesserung und Qualifizierung der Ultraschallprüfung von Mischnähten im Primärkreis von KKW N2 - Die im Primärkreislauf von Kernkraftwerken anzutreffenden austenitischen Schweiß- und Mischnähte sind nicht nur extrem sicherheitsrelevant, sondern stellen auch sehr hohe Anforderungen an die Materialprüfung. Neben der eingeschränkten Zugänglichkeit ist das makroskopische Gefüge der Schweißnaht für die Prüfung mit Ultraschall von höchster Bedeutung. Um Materialfehler zuverlässig in Position und Größe bestimmen zu können, müssen die Kornorientierungen und die elastischen Konstanten des anisotropen Schweißnahtgefüges bekannt sein. Für die bildgebende Darstellung möglicher Materialfehler kommen folgende Arbeitsschritte zum Einsatz: Zunächst wird die Schweißnaht durchschallt, um mit einem inversen Verfahren wichtige Schweißnahtparameter wie beispielsweise die Kornorientierung bestimmen zu können. Auf der Basis dieser Parameter werden im nächsten Schritt die Schallwege mittels Raytracing (RT) simuliert. Zuletzt werden dieser RT-Simulation die Messdaten (A-Scans) von verschiedenen Sender- und Empfängerpositionen zugeordnet und nach der SAFT-Methode (Synthetic Aperature Focusing Technique) zeitaufgelöst überlagert. Die Kombination aus inversem Verfahren, RT und SAFT gewährleistet auch in anisotropen Werkstoffen eine ortsrichtige Visualisierung der Fehler. Wir erläutern diese drei Verfahren und stellen die Prüfanordnung von Prüfkörpern mit künstlichen Testfehlern vor. Messdaten sowie deren Auswertung werden mit den Ergebnissen einer CIVA-Simulation verglichen. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Zerstörungsfreie Prüfung KW - Ultraschall KW - SAFT KW - Schweißnaht KW - Austenit PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404329 SN - 978-3-940283-85-6 VL - DGZfP BB 162 SP - P16, 1 EP - 8 AN - OPUS4-40432 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stajanca, Pavol A1 - Krebber, Katerina T1 - Radiation-induced attenuation of perfluorinated polymer optical fibers for radiation monitoring N2 - Due to some of their unique properties, optical fiber dosimeters are attractive and extensively researched devices in several radiation-related areas. This work evaluates the Performance and potential of commercial perfluorinated polymer optical fibers (PF-POFs) for radiation Monitoring applications. Gamma radiation-induced attenuation (RIA) of two commercial PF-POFs is evaluated in the VIS spectral region. Influence of a dose rate and temperature on RIA measurement is investigated, along with defect stability and measurement repeatability. Co-extruded PF-POFs are identified as more suitable for radiation monitoring applications due to lower dose-rate dependence. With co-extruded PF-POF, RIA measurement holds potential for highly-sensitive radiation Monitoring with good reproducibility. The results show that operation in the blue part of the spectrum provides most favorable performance in terms of the largest nominal Radiation sensitivity, lower temperature, and dose-rate dependence as well as higher defect stability. We demonstrate for the first time to our knowledge, that PF-POFs can be used for distributed detection of radiation with doses down to tens of Grays. The off-the-shelf, user-friendly PF-POF could be of interest as a cheap, disposable sensor for various applications, especially of a more qualitative nature. KW - Perfluorinated polymer optical fiber KW - Cytop KW - Ionizing radiation KW - Radiation-induced attenuation KW - Gamma radiation monitoring PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-419504 DO - https://doi.org/10.3390/s17091959 SN - 1424-8220 VL - 17 IS - 9 SP - Article 1959, 1 EP - 12 PB - MDPI AN - OPUS4-41950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mosquera Feijoo, Maria T1 - Thermal-mechanical fatigue of oxide scales in cyclic water vapor oxidation of 9-12 % Cr steels N2 - Ferritic-martensitic steels with 9-12 % Cr-content are widely used as high temperature construction materials in power plant due to their high temperature properties such as creep resistance, strength, and favorable oxidation resistances. However, typical operating conditions include cyclic thermal/mechanical loading, and as a result the oxide scale might fail; cracks are formed and the oxide scale is spalled off. The oxide spalls can cause steam tube blocking and local thermal stresses, which might provoke shorter component service life. This work investigates the scale spallation behavior of ferritic-martensitic steels under cyclic load condition between 320°C and 620°C for up to 210 cycles in pure steam. All samples were isothermally pre-oxidized at 620°C for 500 h in water steam with 30 bar pressure to create an initial magnetite layer with low porosity. Different sample shapes, rectangular coupons, full rings and U-shape segments, are investigated to evaluate the impact of the geometry on these conditions. After oxidation experiments the oxidation kinetics in terms of mass change, metal loss and thickness scale is determined. In addition, the integrity of the oxide layer as well as its adherence to the matrix are characterized by modified hardness tests and scratch tests. Breakage of the layers at lower applied forces indicates a substantial loss of adhesion strength at intermediate cycle numbers. T2 - EUROCORR 2017 CY - Prague, Czech-Republic DA - 03.09.2017 KW - Geometry influence KW - Therma-mechanical fatigue KW - Oxide layer KW - Cyclic test KW - Scale adherence PY - 2017 AN - OPUS4-42635 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Wossidlo, Peter T1 - Experimental determination and analysis of dynamic fracture toughness data of ductile cast iron N2 - Ductile Cast Iron materials (DCI) have become important structural materials. Neverthe-less, to draw maximum benefit from DCIs property potential, tailored testing methods must be provided. The established dynamic Jd-R and CTOD 5d-R curve procedures are based on material specifically developed, independent experimental techniques but pro-vide almost matching results. This can be seen as additional validation of the Jd procedure which was mandatory. T2 - 14th International Conference on Fracture (ICF 14) CY - Rhodes, Greece DA - 18.07.2017 KW - Ductile cast iron KW - Fracture mechanics KW - Dynamic loading KW - Crack resistance curve KW - CTOD KW - J-integral PY - 2017 SP - Track 3, 1 EP - 2 AN - OPUS4-42721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Butz, Adam T1 - Experimental and analytical investigation of notched components of a Nickel based superalloy under high temperature cyclic loading N2 - While the increase in use of renewable energy sources is a necessity in times of climate change the use of gas turbines as back-up requires them to be run in a much more flexible manner in order to compensate for side effects like sudden fluctuations of energy generation. The significant changes of stress and temperature levels in turbine blades due to start-up and shut down can cause crack initiation and growth in the blades‘ alloy. The aim of this research project is to identify a model for lifetime prediction for gas turbine components made of a Nickel base superalloy under high temperature with a Focus on stress concentration points such as cooling holes. T2 - HIDA-7 Conference on Life/Crack Assessment & Failures in Industrial Structures, UK CY - Portsmouth, UK DA - 15.05.2017 KW - LCF KW - Gas turbine KW - Service life model PY - 2017 AN - OPUS4-42274 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Becker, Ben A1 - Duffner, Eric A1 - John, Sebastian T1 - Storage systems for CGH2- systematic improvement of RC&s composite storage systems for compressed hydrogen - systematic improvement of regulations for more attractive storage units N2 - Hydrogen is an attractive energy carrier that requires high effort for safe storage. For ensuring safety they have to undergo a challenging approval process. Relevant standards and regulations for composite cylinders used for the transport of for on-board storage of hydrogen are currently based on deterministic (e.g. ISO 11119-3) or semi-probabilistic (UN GTR No. 13) criteria. This paper analysis the properties of such methods in regards to the evaluation of load cycle strength. Their characteristics are compared with the probabilistic approach of the BAM. Based on Monte-Carlo simulations, the available design range (mean value and scatter of strength criteria) of current concepts were exemplarily estimated. The aspect of small sample sizes is analysed and discussed with respect to the evaluation procedures. T2 - 10th International Conference on Sustainable Energy and Environmental Protection CY - Bled, Slovenia DA - 27.06.2017 KW - Probabilistic KW - Hydrogen KW - Composite KW - Cylinder KW - Regulations KW - Load cycles KW - GTR 13 KW - ISO 11119 PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-416820 SN - 978-961-286-054-7 DO - https://doi.org/10.18690/978-961-286-054-7 SP - 1 EP - 10 PB - University of Maribor Press CY - Maribor, Slovenia AN - OPUS4-41682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Olejko, Lydia A1 - Bald, Ilko T1 - FRET efficiency and antenna effect in multi-color DNA origami-based light harvesting systems N2 - Artificial light harvesting complexes find applications in artificial photosynthesis, photovoltaics and light harvesting chemical sensors. They are used to enhance the absorption of light of a reaction center which is often represented by a single acceptor. Here, we present different light harvesting systems on DNA origami structures and analyze systematically the light harvesting efficiency. By changing the number and arrangement of different fluorophores (FAM as donor, Cy3 as transmitter and Cy5 as acceptor molecules) the light harvesting efficiency is optimized to create a broadband absorption and to improve the antenna effect 1 (including two energy transfer steps) from 0.02 to 1.58, and the antenna effect 2 (including a single energy transfer step) from 0.04 to 8.7, i.e. the fluorescence emission of the acceptor is significantly higher when the light-harvesting antenna is excited at lower wavelength compared to direct excitation of the acceptor. The channeling of photo energy to the acceptor proceeds by Förster Resonance Energy Transfer (FRET) and we carefully analyze also the FRET efficiency of the different light harvesting systems. Accordingly, the antenna effect can be tuned by modifying the stoichiometry of donor, transmitter and acceptor dyes, whereas the FRET efficiency is mainly governed by the spectroscopic properties of dyes and their distances. KW - DNA origami KW - Light-harvesting KW - FRET KW - Antenna effect PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-405867 UR - http://pubs.rsc.org/en/content/articlelanding/2017/ra/c7ra02114c#!divAbstract DO - https://doi.org/10.1039/C7RA02114C VL - 7 IS - 39 SP - 23924 EP - 23934 PB - The Royal Soc. of Chemistry AN - OPUS4-40586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuroiwa, T. A1 - Zhu, Y. A1 - Inagaki, K. A1 - Long, S. A1 - Christopher, S. A1 - Puelles, M. A1 - Porinsky, M. A1 - Hatamleh, N. A1 - Murby, J. A1 - Merrick, J. A1 - White, I. A1 - Saxby, D. A1 - Caciano de Sena, R. A1 - Dominguez de Almeida, M. A1 - Vogl, Jochen A1 - Phukphatthanachai, Pranee A1 - Fung, W.-H. A1 - Yau, H.-P. A1 - Okumu, T. O. A1 - Kang'iri, J. N. A1 - Tellez, J. A. S. A1 - Campos, E. Z. A1 - Galvan, E. C. A1 - Kaewkhomdee, N. A1 - Taebunpakul, S. A1 - Thiengmanee, U. A1 - Yafa, C. A1 - Tokman, N. A1 - Tunc, M. A1 - Can, S. Z. T1 - Report of the CCQM-K123: trace elements in biodiesel fuel N2 - The CCQM-K123 key comparison was organized by the Inorganic Analysis Working Group (IAWG) of CCQM to assess and document the capabilities of the national metrology institutes (NMIs) or the designated institutes (DIs) to measure the mass fractions of sodium, calcium, potassium, magnesium phosphorous and sulfur in biodiesel fuel (BDF). The National Metrology Institute of Japan (NMIJ) and National Institute of Standards and Technology (NIST) acted as the coordinating laboratories. Results were submitted by 11 NMIs and DIs. The participants used different measurement methods, though most of them used inductively coupled plasma-mass spectrometry (ICP-MS), isotope dilution technique with ICP-MS and inductively coupled plasma-optical emission spectrometry (ICP-OES) with microwave acid digestion. The material was quite challenging and a number of questions were raised at the IAWG meeting. Concerning S, the variation in S results between participants, particularly those using IDMS methods was discussed at the IAWG meeting. BAM, NIST and NMIJ reviewed their experimental conditions, results and/or uncertainty calculations for IDMS. According to the additional evaluation and investigation, the variances between the revised results became smaller than the original one, the revised results were overlapping between IDMS measurements of S content at the k=2 level. It is not possible to calculate a KCRV with values being modified after submission. It was concluded that this KC does not support S measurements. Accounting for relative expanded uncertainty, comparability of measurement results for each of Na, Ca, K, Mg and P was successfully demonstrated by the participating NMIs or DIs. It is expected that sodium, calcium, potassium, magnesium and phosphorus at mass fractions greater than approximately 0.1 mg/kg, 0.1 mg/kg, 0.05 mg/kg, 0.05 mg/kg and 0.1 mg/kg respectively in biodiesel fuel and similar matrices (fuels and oils etc.) can be determined by each participant using the same technique(s) employed for this key comparison to achieve similar uncertainties mentioned in the present report. Furthermore, the results of this key comparison can be utilized along with the IAWG core capability approach. KW - Biodiesel KW - Fuel KW - Sulphur KW - Reference measurement PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393941 UR - http://iopscience.iop.org/article/10.1088/0026-1394/54/1A/08008/meta DO - https://doi.org/10.1088/0026-1394/54/1A/08008 SN - 0026-1394 SN - 1681-7575 VL - 54 SP - Tech. Suppl. 2017, 08008, 1 EP - 47 PB - IOP Publishing CY - Bristol, UK AN - OPUS4-39394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Experimental determination and analysis of dynamic fracture toughness data of ductile cast iron N2 - Ductile Cast Iron materials (DCI) have become important structural materials. Neverthe-less, to draw maximum benefit from DCIs property potential, tailored testing methods must be provided. The established dynamic Jd-R and CTOD 5d-R curve procedures are based on material specifically developed, independent experimental techniques but pro-vide almost matching results. This can be seen as additional validation of the Jd procedure which was mandatory. T2 - 14th International Conference on Fracture (ICF 14) CY - Rhodes, Greece DA - 18.07.2017 KW - Ductile cast iron KW - Fracture mechanics KW - Dynamic loading KW - Crack resistance curve KW - CTOD KW - J-integral PY - 2017 AN - OPUS4-42727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ha, Q. L. M. A1 - Armbruster, U. A1 - Atia, Hanan A1 - Lund, H. A1 - Agostini, G. A1 - Radnik, Jörg A1 - Vuong, H. T. A1 - Martin, A. T1 - Development of active and stable low nickel content catalysts for dry reforming of methane N2 - Methane dry reforming (DRM) was investigated over highly active Ni catalysts with low metal content (2.5wt%) supported on Mg-Al mixed oxide. The aim was to minimize carbon Deposition and metal sites agglomeration on the working catalyst which are known to cause catalyst deactivation. The solids were characterized using N2 adsorption, X-ray diffraction, temperature-programmed reduction, X-ray photoelectron spectroscopy, and UV-Vis diffuse reflectance spectroscopy. The results showed that MgO-Al2O3 solid solution phases are obtained when calcining Mg-Al hydrotalcite precursor in the temperature range of 550–800 °C. Such phases contribute to the high activity of catalysts with low Ni content even at low temperature (500 °C). Modifying the catalyst preparation with citric acid significantly slows the coking rate and reduces the size of large octahedrally coordinated NiO-like domains, which may easily agglomerate on the surface during DRM. The most effective Ni catalyst shows a stable DRM course over 60 h at high weight hourly space velocity with very low coke deposition. This is a promising result for considering such catalyst systems for further development of an industrial DRM technology. KW - Dry reforming of methane KW - Carbon dioxide KW - Ni PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-402904 DO - https://doi.org/10.3390/catal7050157 SN - 2073-4344 VL - 7 IS - 5 SP - 157, 1 EP - 157, 17 PB - MDPI AN - OPUS4-40290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hesse, Almut T1 - Entwicklung immunchemischer Methoden zur Spurenanalytik der Sprengstoffe Nitropenta und Trinitrotoluol N2 - Pentaerythrityltetranitrat (PETN), ein in jüngster Vergangenheit häufig von Terroristen verwendeter Sprengstoff, ist äußerst schwer zu detektieren. Ein verbesserter Antikörper gegen PETN wurde durch Anwendung des Konzepts des bioisosteren Ersatzes entwickelt,indem ein Nitroester durch einen Carbonsäurediester ersetzt wurde. Biostere Moleküle haben eine ähnliche Struktur wie die Referenzsubstanz und zeigen eine vergleichbare biologische Wirkung. Dieser Ansatz führte zu polyklonalen Antikörpern mit extrem guter Selektivität und Sensitivität. Die Nachweisgrenze des Enzyme-Linked Immunosorbent Assays (ELISAs) beträgt 0,15 μg/L. Der Messbereich des Immunassays liegt zwischen 1 und 1000 μg/L. Die Antikörper sind sowohl hinreichend pH-stabil als auch robust gegen Lösungsmittelzusätze. Das Antiserum könnte auch für Schnelltests, Biosensoren, Mikro-Arrays und andere analytische Methoden verwendet werden. Für die Umweltanalytik von Trinitrotoluol (TNT) wurde eine Hochdruckflüssigkeitschromatographie (HPLC)-kompatible Affinitätssäule hergestellt. Druckbeständiges, poröses Glas hat sich als ein hervorragendes Trägermaterial herauskristallisiert. Um selektive anti-TNT-Antikörper für die Herstellung der Affinitätssäule aus den beiden verwendeten TNT-Seren zu isolieren, wurde eine Trennung an einer Dinitrophenyl-Affinitätssäule durchgeführt. Zur Optimierung der Immobilisierungsmethode wurden orangefarbene Dabsyl -Proteine synthetisiert und auf der Oberfläche gebunden. Die Färbung wurde als Indikator für die Immobilisierungsdichte verwendet. Wegen der hohen Affinitätskonstanten der polyklonalen anti-TNT-Antikörper der beiden Seren (5,1 bzw. 2,3∙109 L/mol) lässt sich TNT durch eine typische saure Elution der TNT-Affinitätssäule nur schwer eluieren. Aus diesem Grund wurde eine neuartige Elutionsmethode entwickelt, die irreversible, denaturierende, thermische Online -Elution. Diese eröffnet ein weites Anwendungsfeld, da so Affinitäten, die klass ischerweise aufgrund zu hoher Bindungskonstanten zwischen Ligand und Rezeptor nicht für die Affinitätschromatographie genutzt werden können, für die Analytik besser handhabbar werden. Die maximale Kapazität einer im Rahmen dieser Arbeit hergestellten Affinitätssäule (64,8 μL) betrug 650 ng TNT bzw. 10 μg/mL Säulenvolumen. Um die Immobilisierungsdichte der produzierten Affinitätssäulen zu bestimmen, wurde ein neues Verfahren entwickelt, da die üblichen spektroskopischen Proteinbestimmungsmethoden aufgrund der hohen unspezifischen Wechselwirkung mit dem Trägermaterial zur Proteinbestimmung nicht geeignet waren. Zur Quantifizierung von Proteinen oder Peptiden,die auf festen Trägern immobilisiert sind, wurde auf Grundlage einer HPLC-Trennung der aromatischen Aminosäuren Tyrosin (Tyr) und Phenylalanin (Phe) ohne vorherige Derivatisierung eine gegenüber der klassischen Aminosäureanalytik vereinfachte HPLC/UV-Methode entwickelt. Die Hydrolyse der Proteine und Peptide wurde durch Einsatz von Mikrowellentechnik beschleunigt, sodass nur 30 Minuten statt ca. 22 Stunden für das Standardprotokoll benötigt wurden, bei dem ein Hydrolyseröhrchen verwendet wird. Zur internen Kalibrierung wurden zwei Standardverbindungen, Homotyrosin (HTyr) und 4-Fluorphenylalanin (FPhe) verwendet. Die Nachweisgrenze (limit of detection, LOD) bei 215 nm ist sowohl für Tyr als auch für Phe 0,05 μM (~ 10 μg/L). Dieses neue Verfahren, das als Aromatische Aminosäureanalyse (Aromatic Amino Acid Analysis, AAAA) bezeichnet werden kann, wurde zur Proteinbestimmung von homogenen Proben mit Rinderserumalbumin (BSA) des Nationalen Instituts für Standards und Technologie der USA (NIST) validiert, wobei die Nachweisgrenze für Proteine mit 16 mg/L (~ 300 ng BSA) mit gängigen spektroskopischen Verfahren vergleichbar ist. Es liefert incl. der Hydrolysestufe eine verbesserte Genauigkeit mit einer relativen Standardabweichung von ca. 5%. T3 - BAM Dissertationsreihe - 158 KW - Affinitätschromatographie KW - Affinity chromatography KW - Polyklonale TNT-Antikörper KW - Immunassay KW - Aromatische Aminosäureanalyse KW - Polyclonal TNT-antibodies KW - Polyclonal PETN-antibodies KW - Immunoassay KW - Aromatic amino acid analysis KW - Polyklonale PETN-Antikörper PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-417566 SN - 1613-4249 VL - 158 SP - I EP - 234 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-41756 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -