TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - It was found that there is a systematic dependence of the crack growth on the welding parameters as well as on the load. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate. Based on the results, a new crack criterion was finally selected which allows an extended assessment of the material behavior during the MVT-test. The threshold introduced can quantify the dependencies of the crack formation on the welding and testing parameters, which could not be comprehensively described with the conventional evaluation. In principle, the evaluation routine can also be transferred to other Varestraint or externally loaded hot cracking tests. T2 - IIW Intermediate Meeting Comission II-c CY - Garching, Germany DA - 06.03.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57131 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk T1 - Residual stress formation in DED-arc manufactured high strength steel components N2 - Additive manufacturing (AM) processes enable the efficient production of advanced constructions. New developments in topology optimization are leading to weight-optimized designs of increasing complexity. Direct energy deposition processes (DED) such as wire and arc-based additive manufacturing are an important method of additive manufacturing. The wire filler metals enable a wide range of materials, while the arc process provides a high deposition rate compared to laser and powder-based processes. Combined with the use of high-strength steels, the thickness of walls or components can be significantly reduced in the context of lightweight construction, which results in significant savings in energy, costs, time and resources. Suitable high-strength steel filler metals are commercially available for DED-arc AM processes. However, guidelines and quantitative knowledge about welding stresses and cold cracking issues during component production and service are lacking. This limits the industrial application considerably. In a joint project of BAM and Chemnitz University of Technology, the main influences and complex interactions of material, production process, design and processing steps on the residual stress level are investigated. The aim is to develop processing recommendations and a cold cracking test for economical processing and stress-related design of high-strength steels with DED-arc. This study focuses on residual stress analysis by neutron diffraction (ND) and X-ray diffraction (XRD) on defined test specimens. The ND analysis were performed at the Paul Scherrer Institute- Villigen, Switzerland (PSI) and the XRD analysis at BAM. The study shows a quantitative and qualitative comparison of the residual stress magnitudes and distribution between the component bulk (ND) and surface (XRD) analyses. The ND analysis reveals that in DED-arc AM walls the residual stresses dominate in the direction of welding and are negligibly small in each case transverse to the direction of welding. The topology of the analyzed residual stresses shows almost identical residual stress maps compared to XRD. In addition, the residual stresses are significantly influenced by the solid phase transformation of the material due to low cooling times and less post heat treatment cycles of following AM layers in the area of the top layer. T2 - IIW Intermediate Meeting C-II/CIX CY - Munich, Germany DA - 06.03.2023 KW - Additive manufacturing KW - High strength steel KW - Residual stress PY - 2023 AN - OPUS4-59307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eissel, A. A1 - Engelking, Lorenz A1 - Gustus, R. A1 - Treutler, K. A1 - Wesling, V. A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Alloy modification for additive manufactured Ni alloy components—part I: effect on microstructure and hardness of Invar alloy N2 - Alloy 36 (1.3912), also known as “Invar,” is an alloy with 36% nickel. The alloy has a remarkably low thermal expansion coefficient in certain temperature ranges. This peculiarity is called the invar effect, which was discovered in 1896 by the Swiss physicist Charles Édouard Guillaume. Therefore, it is used in applications in which dimensional stability is critical, such as molding tools for composite materials in aerospace, automotive applications, or liquified natural gas (LNG) cargo tanks. Moreover, increasingly complex structures and the optimization of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In addition, the manufactured components require subsequent machining surface finishing, like finish milling, to achieve their final contour. Nickel iron alloys are difficult to machine. Additionally, inhomogeneous microstructure may lead to unstable cutting forces and conditions. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr, and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Furthermore, one modification is applied to metal arc welding process and investigated. Part II focuses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components. T2 - 75th IIW Annual Assembly CY - Tokyo, Japan DA - 17.07.2022 KW - Alloy modification KW - Alloy 36 KW - Plasma-transferred arc welding PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571777 DO - https://doi.org/10.1007/s40194-023-01510-w SN - 0043-2288 SP - 1 EP - 9 PB - Springer CY - Heidelberg AN - OPUS4-57177 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Engelking, Lorenz A1 - Eissel, A. A1 - Schröpfer, Dirk A1 - Treutler, K. A1 - Kannengießer, Thomas A1 - Wesling, V. T1 - Optimisation of surface residual stresses using ultrasonic‑assisted milling for wire‑arc additive manufactured Ni alloy components N2 - Nickel alloys are cost intensive materials and generally classified as difficult-to-cut material. However, machining of these materials is needed especially in case of alloy 36 (1.3912), which is commonly used in mould construction for the production of fibre-reinforced composites. With regard to repair, modification and manufacturing of such components, additive manufacturing offers significant economic advantages. Nevertheless, subsequent machining steps are needed to achieve the final component contour and defined surface conditions. Dependent on the material and machining process conditions, detrimental tensile residual stresses may be the result on the machined surface, having negative impact on the component performance and safety. In this investigation, machining experiments were carried out on wire arc additive manufactured components made of alloy 36, varying the cutting speed and the feed rate. In addition, the conventional milling process (CM) was compared with a modern, hybrid machining process, the ultrasonic-assisted milling (US). The cutting forces and the surface-near residual stresses were analysed using X-ray diffraction. A significant improvement of the machinability as well as the surface integrity by using the ultrasonic assistance was observed, especially at low cutting speeds. The CM induced mainly tensile residual stresses, the US mainly compressive residual stresses. KW - Surface integrity KW - Ultrasonic-assisted milling KW - Additive manufacturing KW - Ni alloy KW - Alloy 36 PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575246 DO - https://doi.org/10.1007/s00170-023-11326-z SN - 1433-3015 VL - 126 IS - 9 SP - 4191 EP - 4198 PB - Springer Nature AN - OPUS4-57524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Brackrock, Daniel A1 - Czeskleba, Denis A1 - Kannengießer, Thomas T1 - Component test for the assessment of delayed hydrogen-assisted cracking in thick-walled SAW joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed. KW - Hydrogen KW - Cold cracking KW - Minimum Waiting Time KW - Offshore steel grade KW - Component test PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591981 DO - https://doi.org/10.1007/s40194-023-01658-5 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-59198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Thermodynamic prediction of precipitations behaviour in HAZ of a gas metal arc welded S690QL with varying Ti and Nb content N2 - For a significant increase in the strength of high-strength fine-grained structural steels with a nominal yield strength ≥690 MPa, the addition of microalloying elements such as Nb and Ti is required. The standard specifications for the chemical composition of these steels (e.g., in EN 10025-6) often only give the manufacturer limit contents to achieve the defined properties. The effect of the alloying elements in the heat affected zone (HAZ) is sometimes completely contrary. This makes it difficult to adequately predict the batch dependency regarding weldability and the load-bearing behaviour of the welded joint. Three different micro-alloyed steels of the grade S690QL were produced on a laboratory scale, focusing on different Nb and Ti contents. To investigate the tempering effect, these were gas metal arc welded in three layers. In addition to metallographic investigations of individual HAZ areas, thermodynamic phase calculations were carried out using Thermo-Calc, following variations in the chemical composition. This provides an understanding of phase transformation, precipitation growth, and dissolution during welding as a function of temperature and cooling conditions. The results show a divergent metallurgical behaviour in the HAZ of the three different micro-alloyed steels. Thereby, the Ti micro-alloyed grade showed a strong softening of the HAZ in contrast to the Nb micro-alloyed grade. This can be attributed to a contrary precipitation behaviour during welding. KW - High-strength structural steel KW - Gas metal arc welding KW - HAZ-softening KW - Microalloying influences KW - Thermodynamic simulation PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-579988 DO - https://doi.org/10.1007/s40194-023-01550-2 SN - 0043-2288 SP - 1 EP - 10 PB - Springer AN - OPUS4-57998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Hensel, J. T1 - Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen - Kurzdarstellung der Projektergebnisse, FOSTA P1380 N2 - Die Verwendung hochfester Feinkornbaustähle hat für viele Anwendungen des Stahlbaus ein großes Potenzial für gewichtsoptimierte, effiziente Strukturen mit ho-her mechanischer Beanspruchbarkeit. Weitere Zugewinne an Effizienz sind durch generative Fertigungsschritte sowie bionische Bauweisen erzielbar. Hierzu stehen bereits kommerzielle hochfeste drahtförmige Zusatzwerkstoffe für formgebendes MSG-Schweißen zur Verfügung. Dem Einsatz stehen noch fehlende quantitative Aussagen zu den fertigungsbedingten Beanspruchungen und der Bauteilsicherheit während Herstellung und Betrieb im Wege. Dies betrifft insbesondere prozess- sowie materialbedingte Einflüsse und die konstruktive Schrumpfbehinderung verbunden mit der Ausbildung hoher Zugeigenspannungen und damit zusammenhängenden Kaltrissbildung. Hierfür wurden im Projekt detaillierte und anwenderbezogene Kenntnisse zu den komplexen Wechselwirkungen zwischen Schweißprozess und Wärmeführung während der Fertigung, der metallurgischen Vorgänge und insbesondere der vorliegenden konstruktiven Einflüsse auf die entstehenden Eigenspannungen erarbeitet, um ein frühzeitiges Bauteilversagen aufgrund eines hohen fertigungsbedingten Beanspruchungsniveaus bis hin zu einer Rissbildung während der Fertigung sicher zu vermeiden. Gleichzeitig wurden die Einflüsse auf die mechanisch-technologischen Gütewerte systematisch analysiert. Zudem wurden die Auswirkungen trennender Verfahren durch Entfernen der Substratplatte sowie durch die spanende Bearbeitung der Vorformlinge zu Endbauteilgeometrien geklärt, da diese unmittelbar den Eigenspannungszustand beeinflussen und deutlichen Verzug der Bauteile auslösen. Für das generative Schweißen konnten Verarbeitungsempfehlungen sowie Normenvorgaben erarbeitet werden. Dies hilft insbesondere KMU eine wirtschaftliche, beanspruchungsgerechte und risssichere generative Fertigung von Bauteilen aus hochfesten Feinkornbaustählen zu ermöglichen. KW - MAG-Schweißen KW - Additive Fertigung KW - Eigenspannungen KW - Kaltrisssicherheit KW - Hochfester Stahl PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582198 N1 - Das IGF-Vorhaben IGF-Nr. 21162 BG (P 1380) "Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen" der Forschungsvereinigung Stahlanwendung e. V. wurde über die AiF im Rahmen des Programms zur Förderung der Industriellen Gemeinschaftsforschung (IGF) vom Bundesministerium für Wirtschaft und Klimaschutz aufgrund eines Beschlusses des Deutschen Bundestages gefördert. SP - 1 EP - 2 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-58219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Hybrid use of LTT welding filler N2 - Through a hybrid use of Low Transforamtion Temperature welding filler, fatigue strength of welds should be increased. Through the hybrid use of LTT welding filler the Integrity of a weld will be less affected. By creating several variants of LTT weld geometries an idea of the optimum residual stress reduction is given. T2 - European Academy of Wind Energy (EAWE) CY - Hannover, Germany DA - 06.09.2023 KW - Welding KW - LTT (Low Transformation Temperature) KW - Fatigue strength KW - High-strength steels KW - Residual stress PY - 2023 AN - OPUS4-58362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp T1 - Anwendung von Convolutional Neural Networks (CNNs) bei der Erkennung von Rissen im Modifizierten Varestraint-Transvarestraint-Heißrisstest (MVT-Test) N2 - Der MVT-Test ist die an der BAM entwickelte und genutzte Version des Varestraint-Tests der weltweit für die Charakterisierung der Erstarrungsrissanfälligkeit von Schweißzusätzen und Legierungen eingesetzt wird. Die Auswertung solcher Tests erfolgt klassisch unter dem Lichtmikroskop. Durch Automatisierung des Auswerteprozesses mit KI kann der Informationsgehalt des Tests besser ausgeschöpft und eine höhere Vergleichbarkeit zwischen Testergebnissen gewährleistet werden. T2 - DVS-Congress CY - Essen, Germany DA - 10.09.2023 KW - MVT KW - Varestraint KW - KI KW - Neuronales Netzwerk KW - Semantic Segmentation PY - 2023 AN - OPUS4-58313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Eissel, A. A1 - Treutler, K. A1 - Wesling, V. T1 - Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten N2 - Die additive Fertigung (AM) durch schweißtechnische Verfahren eröffnet vielfach ökonomische Vorteile für eine ressour-ceneffiziente Bauteilherstellung. Gerade hinsichtlich der Homogenität und Anisotropie der resultierenden Schweißgefüge und den damit verbundenen Eigenschaften gibt es noch offene Fragestellungen. Die Einstellung der finalen Bauteilgeo-metrie und Oberflächengüte erfordert den komplementären Einsatz abtragender Fertigungsschritte. Hochleistungslegie-rungen auf der Basis von Nickel oder Kobalt sind aufgrund ihrer niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit schwer spanbar. Eine gezielte Gefügebeeinflussung mittels Modifikation der AM-Schweißzusatz-werkstoffe und der Einsatz des ultraschallunterstützten Fräsens (US) bietet das Potential insgesamt die Zerspanungssi-tuation zu verbessern. Dieser Lösungsansatz unter Gewährleistung des Erhalts der geforderten Werkstoff- bzw. Bauteileigenschaften ist Untersuchungsgegenstand eines Gemeinschaftsvorhabens (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF. Der vorliegende Beitrag stellt Ergebnisse für die beiden untersuchten FeNi- und CoCr-Legierungen sowie wesentliche Zusammenhänge zwischen Legierungsmodifikation, entstehender Gefügemorphologie und Zerspanungseigenschaften der mittels MAG additiv gefertigter Proben vor. Das größte Potential für die Modifikation zeigten Zr und Hf. Die Zulegierung in das Schweißgut erfolgte durch Beschichtung von Massivdrähten sowie durch Her-stellung von Fülldrähten. T2 - DVS Congress - GST CY - Essen, Germany DA - 11.09.2023 KW - Legierungsmodifikation KW - Ultraschallunterstütztes Fräsen KW - Additive Fertigung KW - Oberflächenintegrität PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 697 EP - 703 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58380 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Mente, Tobias T1 - Zuverlässige Wasserstoff Bestimmung in Metallen und ihren Schweißverbindungen: Parameter, Einflüsse, Grenzen N2 - Im Zuge der wasserstoffbasierten Energiewirtschaft von morgen, kommt der Errichtung der dementsprechenden Infrastruktur die zentrale Rolle zu. Der überwiegende Teil bisher eingesetzter und meist geschweißter Werkstoffe, wie Stähle, kann unter bestimmten Bedingungen zur Wasserstoffversprödung neigen. Dies umfasst die klassische verzögerte Kaltrissbildung während der Schweißverarbeitung als auch Versprödungsphänomene während des Betriebs. Für die Bewertung eines jeden Wasserstoffeffektes auf bspw. die mechanischen Eigenschaften eines geschweißten metallischen Werkstoffes, muss der Wasserstoffgehalt präzise bestimmt werden, Im Fall von Schweißnähten ist die beispielsweise nach der ISO 3690, die klassische isotherme Trägergas-Heißextraktion (TGHE). Die TGHE basiert dabei auf der beschleunigten Wasserstoffentgasung aufgrund der thermischen Aktivierung des Wasserstoffs bei erhöhten Temperaturen. Neben der reinen Quantifizierung des Wasserstoffs, kann über die thermische Desorptionsanalyse (TDA) mit variierten Heizraten, der Bindungszustand an mikrostrukturellen Defekten im Material festgestellt und bewertet werden. Für beide Techniken sind experimentelle und messtechnische Einflüsse zu beachten, die großen Effekt auf das Ergebnis haben. Für die TGHE schlägt die ISO 3690 schlägt beispielswiese verschiedene Probengeometrien sowie Mindestextraktionszeiten vor. Die vorliegende Studie fasst Ergebnisse und Erfahrungen zahlreicher Untersuchungen an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit unterschiedlichen Probentemperaturen und Geometrien (ISO 3690 Typ B und zylindrische TDA-Proben) zusammen hinsichtlich: Einfluss der Probenoberfläche (poliert/geschweißt), Messgenauigkeiten in Abhängigkeit des Probenvolumens sowie die unzureichende Überwachung des Effektes des PI-Reglers auf die Extraktionstemperatur. Insbesondere eine abweichende Extraktionstemperatur zur eingestellten Temperatur, kann die Messergebnisse wesentlich verfälschen. Basierend auf den Ergebnissen werden Methoden aufgezeigt, um schnell die gewünschte Extraktionstemperatur zu erreichen, ohne physisch in das Messequipment eingreifen zu müssen. Dies dient der wesentlichen Verbesserung der Zuverlässigkeit der Wasserstoffmessung durch erhöhte Signalstabilität und beschleunigte Wasserstoffdesorption. Im Allgemeinen ist eine unabhängige Temperaturmessung mit Dummy-Proben für die gewählte Heizprozedur angeraten, um mögliche unerwünschte Temperatureinflüsse bereits vor der Messung auszuschließen. Die beschriebenen Methoden können ohne großen Aufwand direkt in die industrielle Anwendung überführt werden. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Wasserstoff KW - Schweißen KW - Forschung KW - ISO 3690 PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 435 EP - 442 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, O. A1 - Neumann, Martin T1 - System of Quality Assurance Measures in Manufacturing and Operation of Dual Purpose Casks for Spent Nuclear Fuel and High Level Waste in Germany N2 - German spent nuclear fuel and high level waste is stored in dry conditions in interim storage facilities until a final repository will be ready for operation in the future. Dual purpose casks are used for the packaging of the materials to ensure transportability at any time during long-term interim storage and fulfilling both requirements from interim storage as well as transport. Germany’s 2011 decision to phase out utilization of nuclear energy has led to a high demand for casks for decommissioning power plants as quickly as possible. Cask serial production will continue at a high level for the next few years. In the process, a system of quality assurance measures ensures that every cask reliably complies with design specification according the transport approval certificate and storage license. When the first casks were manufactured in Germany about 40 years ago, quality assurance was oriented towards pressure vessel and general nuclear manufacturing. The system was continuously adapted to the state of the art. In particular serial production, globalization of manufacturing and deep supplier chains had to be taken into account. The system of quality assurance measures applied today for cask manufacturing shall be presented here. The quality assurance measures can be categorized as system-related and design-related. With respect to transport regulations for example, they are independently approved and monitored by the competent authority BAM and its authorized inspection experts. The qualification of the applicant is reviewed first in the context of the design approval procedure and then periodically. The qualification of component and cask manufacturers is also checked at the start of manufacturing and then periodically. Before the start of manufacturing documents such as quality plans are pre-assessed. Manufacturing and inspection are then performed according to the pre-assessed documents. Cask manufacturing is completed by a final inspection before commissioning. Periodic inspections during operation ensure preservation of the properties specified in the approval certificate over package life time. The type and the time interval of periodic inspections depend on the use of the package. For transport after interim storage a system of specific tests and inspections is prescribed. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 22) CY - Juan-les-Pins, France DA - 11.06.2023 KW - Radioactive material KW - Quality Assurance Measures KW - Dual Purpose Casks KW - Independent Surveillance PY - 2023 AN - OPUS4-57705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of Residual Stresses on Stress Relief Cracking of Thick-Walled Creep-Resistant Steel Welds N2 - Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT. T2 - AJP 2023 3rd International Conference on Advanced Joining Processes CY - Braga, Portugal DA - 19.10.2023 KW - Residual stress KW - Creep-resistant steel KW - Stress relief cracking KW - Neutron diffraction PY - 2023 AN - OPUS4-58646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Large scale hydrogen assisted cracking test for thick walled SAW joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods or jackets. These components are typically submerged arc welded (SAW) high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicate the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam / layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with 22 passes and a seam length of 1,000 mm. Additional welded stiffeners simu-lated the effect of a high restraint, to stimulate critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of 48 h after welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modelling allowed the qualitative estimation of the hydrogen diffusion in the weld. A remarkable HAC occurrence was not identified and proves both, a certain resistance of the weld joint to HAC and the (questionable) duration of the MWT. T2 - IIW Annual Assembly, Meeting of Commission II-C CY - Singapore DA - 19.07.2023 KW - Mock-up KW - Hydrogen assisted cracking KW - Submerged arc welding KW - Offshore KW - Steel PY - 2023 AN - OPUS4-57977 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe N2 - Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unterschiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium in Analogie zu Prokhorovs Heißrissmodell. Die neue Auswertung wird anhand einer Studie hochfester Schweißzusatzwerkstoffe vorgestellt, deren Rissverhalten in Abhängigkeit der chemischen Zusammensetzung und der Schweißparameter bewertet wird. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Heißrisse KW - Varestraint-Test KW - Materialprüfung PY - 2023 AN - OPUS4-57070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Hensel, J. T1 - Influence of the WAAM process and design aspects on residual stresses in high-strength structural steels N2 - Wire arc additive manufacturing (WAAM) enables the efficient production of weight-optimized modern engineering structures. Further increases in efficiency can be achieved by using high-strength structural steels. Commercial welding consumables for WAAM are already available on the market. Lack of knowledge and guidelines regarding welding residual stress and component safety during production and operation leads to severely limited use for industry applications. The sensitive microstructure of high-strength steels carries a high risk of cold cracking; therefore, residual stresses play a crucial role. For this reason, the influences of the material, the WAAM process, and the design on the formation of residual stresses and the risk of cold cracking are being investigated. The material used has a yield strength of over 800 MPa. This strength is adjusted via solid solution strengthening and a martensitic phase transformation. The volume expansion associated with martensite formation has a significant influence on the residual stresses. The focus of the present investigation is on the additive welding parameters and component design on their influence on hardness and residual stresses, which are analyzed by means of X-ray diffraction (XRD). Reference specimens (hollow cuboids) are welded fully automated with a systematic variation of heat control and design. Welding parameters and AM geometry are correlated with the resulting microstructure, hardness, and residual stress state. Increased heat input leads to lower tensile residual stresses which causes unfavorable microstructure and mechanical properties. The component design affects heat dissipation conditions and the intensity of restraint during welding and has a significant influence on the residual stress. KW - DED-arc KW - Additive manufacturing KW - High-strength steel filler metal KW - Residual stress PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572698 DO - https://doi.org/10.1007/s40194-023-01503-9 SN - 1878-6669 VL - 67 IS - 4 SP - 987 EP - 996 PB - Springer CY - Berlin AN - OPUS4-57269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Einfluss unterschiedlicher Mikrolegierungsrouten eines S690QL auf das Ausscheidungsverhalten in der Wärmeeinflusszone N2 - Mikrolegierungselementen, wie Nb und Ti sind für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung dieser Stähle geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Mikrolegierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Eine unerwünschte Eigenschaft ist dabei die Erweichung der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden im Rahmen eines DFG-Vorhabens systematisch Mikrolegierungs-routen mit variierenden Ti- und Nb-Gehalten des hochfesten und vergüteten Feinkornbaustahls S690QL untersucht. Dazu wird das MAG-Schweißen mit modifizierten Sprühlichtbogen verwendet, welches durch hohe Abschmelzleistung gekennzeichnet ist und schmalere Nahtöffnungswinkel (α = 30°) ermöglicht. An Dreilagen-Schweißungen wird der Effekt der metallurgischen Zusammensetzung in Kombination mit hoher Wärmeeinwirkung auf die Ausbildung einer kritischen WEZ-Gefügezone mit Erweichung und/oder exzessiver Aufhärtung untersucht. Ein besonderes Augenmerk wird auf die Phasenumwandlungen und das Ausscheidungsverhalten im Gefüge der Wärmeeinflusszone gelegt. Neben umfangreichen metallographischen Untersuchungen einzelner WEZ-Bereiche wurden, unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels Thermo-Calc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation und Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. Das Ziel ist es, den Einfluss der Wärmeeinwirkung auf die Gefügeausbildung in der WEZ und dessen mechanischer Eigenschaften zu analysieren. Insbesondere wird hier auf die Auswirkung der unterschiedlichen Mikrolegierungskonzepte (Ti oder Nb) geachtet. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - WEZ Erweichung KW - Thermodynamische Simulation KW - Mikrolegierungseinfluss KW - Schweißen von hochfesten FKB PY - 2023 SN - 978-3-8440-9105-2 VL - 12 SP - 332 EP - 343 PB - Shaker Verlag AN - OPUS4-58006 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Schweißen von hochfesten Feinkornbaustählen N2 - Das Schweißen von hochfesten Feinkornbaustählen erfordert aufgrund der Sicherstellung der Gütewerte des Grundwerkstoffes (Zähigkeit, Festigkeit) auch in der Schweißverbindung, die Einhaltung von engen Grenzen bei der Auswahl von Schweißparametern. Die Reproduzierbarkeit von beanspruchungsgerechten hochfesten Schweißverbindungen hängt vom Schweißverfahren und der damit einhergehenden komplexen Gefügeausbildung ab. Hierbei müssen hochfeste Schweißverbindungen mindestens die gleichen Festigkeitsanforderungen erfüllen wie der eingesetzte Grundwerkstoff. In diesem Vortrag werden speziell die Herausforderungen wie der Empfindlichkeit gegenüber der wasserstoffunterstützen Kaltrissbildung beim Schweißen von hochfesten Feinkornbaustählen und dem Mikrolegierungseinfluss auf die divergente Ausbildung der Wärmeeinflusszone thematisiert. T2 - Jahresmitgliederversammlung DVS BV Berlin CY - Berlin, Germany DA - 03.05.2023 KW - Herausforderungen beim Schweißen hochfester FKB KW - Wasserstoffunterstütze Kaltrissbildung KW - TEKKEN Test KW - Mikrolegierungseinfluss KW - Wärmeeinflusszone PY - 2023 AN - OPUS4-57995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Mikrolegierungseinfluss beim Schweißen hochfester Feinkornbaustähle N2 - Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusam-mensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abwei-chungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adä-quate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikro-gefüge erschwert bis unmöglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung. T2 - DVS BV Potsdam, Mitglieder Weiterbildungsveranstaltung CY - Groß Kreutz (Havel), Germany DA - 31.05.2023 KW - WEZ Erweichung KW - WEZ Aufhärtung KW - Mikrolegierungseinfluss KW - Schweißen von hochfesten FKB PY - 2023 AN - OPUS4-57996 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Witte, Julien A1 - Hübler, Daniela A1 - Schröpfer, Dirk A1 - Börner, Andreas A1 - Kannengießer, Thomas ED - Hanke, S. T1 - Wear behavior of innovative niobium carbide cutting tools in ultrasonic-assisted finishing milling N2 - The resources of niobium exceed the ones of tungsten by an order of magnitude. With 92%, Brazil is today the main global producer of niobium. Hence, niobium carbides (NbC) are a sustainable and economic alternative to conventionally used cutting materials, especially tungsten carbides (WC). Moreover, NbC can be used in Ni alloy matrix and thus offer significant advantages by substituting WC in Co matrix as cutting materials in terms of health risks and raw material price and supply risk. Based on recent studies which found an increased performance of NbC compared to WC cutting tools in machining higher strength steels, the composition NbC12Ni4Mo4VC was chosen for finish machining of a high-strength steel S960QL in this study. The experiments were carried out on an ultrasonic-assisted 5-axis milling machine using NbC tools specially made to benchmark them with commercially available coated WC cutting inserts. In addition, the influence of a coating system for the NbC inserts is tested and evaluated for its performance in the cutting process. Tool wear and cutting force analyses are implied to identify optimal parameter combinations as well as tool properties for the novel NbC tool. Together with the oscillation of ultrasonic-assisted milling, the loads on the component surface and the tool can be reduced and the wear behavior of the novel NbC tool can be refined. These milling tests are accompanied by standardized wear tests, i.e., pin-on-disc, between the aforementioned material combinations, and the results are correlated with each other. Finally, the behavior when using hard-to-cut materials such as Ni alloys, or innovative materials such as iron aluminide is also being tested, as these are constantly in the focus of machining optimization. With this strategy, comprehensive knowledge is achievable for future efficient application of NbC for milling tools, which have already been researched for decades using WC. T2 - 24th International Conference on Wear of Materials CY - Banff, Canada DA - 16.04.2023 KW - Niobium carbide KW - Cutting tool KW - Ultrasonic-assisted milling KW - Tool wear PY - 2023 DO - https://doi.org/10.1016/j.wear.2023.204722 SN - 0043-1648 VL - 522 SP - 1 EP - 7 PB - Elsevier B.V. AN - OPUS4-57561 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Influence of Microalloying on Precipitation Behavior and Notched Impact Strength of Welded High Strength Structural Steels N2 - Microalloying elements, such as Nb and Ti, are essential for significantly increasing the strength of quenched and tempered, high-strength structural steels with a nominal yield strength ≥ 690 MPa and their welded joints. The standard specifications (e.g., EN 10025-6) for the chemical composition are only tolerated limit contents within which the steel manufacturers operate. The standard composition, however, says nothing per se about the properties of the material. Even small deviations in the alloy route can have a drastic effect on the mechanical properties. This makes it difficult or even impossible to adequately predict the weldability and integrity of the welded joint. An undesirable side effect is the possible softening of the heat-affected zone (HAZ), as well as the opposite hardening.Mechanical-technological investigations of the notched impact strength confirm the results of the simulation regarding the development of different microalloy routes in the welded state. From this, the influence of the heat effect of welding on the microstructure formation in the HAZ and the corresponding mechanical properties can be described qualitatively. T2 - 76th IIW Annual Assembly and International Conference on Welding and Joining CY - Singapore DA - 16.07.2023 KW - High-strength structural steel KW - Notched impact strength KW - HAZ-softening KW - Microalloying influences PY - 2023 AN - OPUS4-57997 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Mikrolegierungseinfluss auf das Ausscheidungsverhalten und die mechanischen Eigenschaften geschweißter hochfester Baustähle N2 - Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrogefüge erschwert bis unmöglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden erstmals systematisch die unterschiedlichen Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten an Versuchsschmelzen untersucht. Die Stahlgüte S690QL bildet dabei die Grundlage der chemischen Zusammensetzung sowie der entsprechenden Wärmebehandlung. Zur Untersuchung der jeweiligen Schweißeignung wurden Dreilagen-Schweißungen mittels moderner MAG-Hochleistungsschweißprozesse durchgeführt und kritische Gefügebereiche mit hoher Erweichung/Aufhärtung identifiziert. Mechanisch-technologische Untersuchungen zur Kerbschlagzähigkeit mittels Kerbschlagbiegeversuchen durchgeführt wurden, bestätigen dabei die Ergebnisse der thermodynamischen Simulation bezüglich des Ausscheidungsverhaltens während der Temperatur-Zeit Schweißzyklen. Daraus lässt sich der Einfluss der Wärmeeinwirkung beim Schweißen auf die Gefügeausbildung in der WEZ und der korrespondierenden mechanischen Eigenschaften qualitativ beschreiben. T2 - DVS CONGRESS 2023 CY - Essen, Germany DA - 11.09.2023 KW - WEZ-Erweichung KW - Digital Image Correlation KW - Mikrolegierungseinfluss KW - Hochfester Feinkornbaustahl KW - Kerbschlagzähigkeit PY - 2023 AN - OPUS4-58354 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Kadoke, Daniel A1 - Kruse, Julius T1 - Investigation of the local strain behavior by digital image correlation and transverse tensile tests on welded differently microalloyed high strength structural steel N2 - Der Einsatz von hochfesten niedriglegierten Stählen (HSLA) ist in vielen Industriesektoren, wie dem allgemeinen Bauwesen, Offshore Strukturen, Mobilkranbau usw. unumgänglich geworden. Die steigende Nachfrage an Stählen mit einer hohen Festigkeit und gleichzeitig hervorragenden Zähigkeit stellt ein ökonomisches und ökologisches Potential dieser Stähle in Vordergrund. Aktuell gültige Normvorgaben (EN ISO 10025-6) geben den Stahlherstellern Vorgaben bezüglich der chemischen Zusammensetzung, um die geforderten mechanischen Eigenschaften erreichen zu können. Die Legierungsrouten variieren jedoch von Hersteller zu Hersteller. In Betracht der Schweißeignung dieser Stähle zeigt sich das Problem, dass diese bereits bei geringen Nb- und Ti-Mikrolegierungsunterschieden im Grundwerkstoff ein divergentes metallurgisches Verhalten in der Wärmeeinflusszone (WEZ) aufweisen. In diesem Vortrag werden die schweiß-metallurgischen Unterschiede zwischen verschieden mikrolegiertem hochfestem Feinkornbaustahl S690QL thematisiert. Zur Prüfung der Schweißnahtfestigkeit wurden mittels eines instrumentierten DIC (ARAMIS) Systems Querzugversuche an Schweiß-Querflachzugproben durchgeführt. T2 - AJP 2023 3rd International Conference on Advanced Joining Processes CY - Braga, Portugal DA - 19.10.2023 KW - WEZ-Erweichung KW - Hochfester Feinkornbaustahl KW - Digital Image Correlation KW - Querzugversuch KW - Mikrolegierungseinfluss PY - 2023 AN - OPUS4-58721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel T1 - Investigation of the influence of PWHT heating rate and global stress conditions on the stress relief cracking mechanism of CrMoV steel SAW joints N2 - This presentation summarizes the latest research results of the influence of the post weld heat treatment (PWHT) rate and the global mechanical stress conditions on the stress relief cracking (SRC) susceptibility of low-alloyed and creep-resistant CrMoV steel submerged arc weld joints. It was found that a certain effect of very low heating rates could be confirmed. In addition, the interlinking of SRC susceptibility increasing effects during the PWHT and the ex-post indentification in metallographic cross-section via microstructure characterization is very complex. T2 - IIW Intermediate meeting of Commission II-A CY - Garching, Germany DA - 06.03.2023 KW - Creep-resistant steel KW - Submerged arc welding KW - Stress relief cracking KW - Heating rate KW - Microstructure characterization PY - 2023 AN - OPUS4-57116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas T1 - Full-scale drop testing with a heavy-weight package for radioactive waste N2 - Packages for the transport of radioactive materials shall fulfil the requirements of the IAEA regulations for the safe transport. The requirements define mechanical and thermal test conditions including criteria ensuring the package design’s ability to withstand severe accidents and provide a high level of technical safety. Different methods can be used for safety demonstration showing compliance with the regulations. The central part of a safety demonstration which is presented in this paper was a comprehensive drop test program with a full-scale model of a transport package accompanied by pre- and post-test FE analyses. Using full-scale drop test models allow the benefit that similarity and scaling issues become a significant smaller issue, additional material investigations can be limited and analyses for transferring test results to the original package design are reduced. Additionally, experience for the future serial packaging manufacturing and handling procedures can be collected in a very early state of the design approval process. The pre-test finite element analyses derived and justified the drop test program consisting of several drop sequences with different drop orientations of the specimen. The performance and the results of the drop test sequences shows the manageability and the advantage e.g., in view of the direct availability of test results for the package licensing. On the other hand, the drop test performance shows the difficulties during handling and the need for additional equipment during preparation of the specimen. The package presented was intended for the transport and storage of compacted radioactive waste from reprocessing of spent nuclear fuel assemblies - designed and applied for approval by the AGC consortium. The project ended in 2021. The package design was characterized by a cask body made of a forged thick stainless-steel shell, a bolted double lid system with metallic gaskets and wood filled shock absorbers at both ends. The total mass of the entire transport package including content was 120,000 kg, the total length was about 7000 mm and the diameter approximately 3000 mm, both measures include the shock absorbers. The paper provides an insight into the performance of a full-scale drop testing campaign within the package safety evaluation and shows some selected test results. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 22) CY - Juan-Les-Pins, France DA - 11.06.2023 KW - Full-scale KW - Drop testing KW - Package KW - Radioactive waste PY - 2023 AN - OPUS4-57731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Component test for the assessment of hydrogen assisted cracking susceptibility of thick-walled submerged arc welded offshore steels N2 - Offshore wind turbines (OWT) are a key factor of the sustainable energy generation of tomorrow. The continuously increasing installation depths and weight of the OWTs require suitable foundation concepts like monopiles or tripods. Typically, mild steels like the S420ML are used with plate thicknesses up to several hundreds of mm causing high restraints in the weld joints. Due to the large plate thickness, submerged arc welding (SAW) with multiple wires is the state-of-the-art welding procedure. As a result of the very high stiffness of the construction, a certain susceptibility for time-delayed hydrogen-assisted cracking (HAC) may occur. The evaluation of crack susceptibility is very complex due to the component size and stiffness of real offshore structures. For this purpose, a near-component test geometry was developed to transfer the real stiffness conditions to laboratory (i.e., workshop) scale. The investigated mock-up, weighing 350 kg, comprised heavy plates (thickness 50 mm, seam length 1,000 m) joined by a 22-pass submerged arc weld. Additional stiffeners simulated the effect of high restraint or shrinkage restraint of the weld. Extreme scenarios of hydrogen absorption during welding were simulated via the use of welding fluxes in dry (HD < 5 ml/100g Fe) and moisture condition (HD > 15 ml/100g Fe). The residual stresses were determined by a robot X-ray diffractometer. Areas of critical tensile residual stress (at the level of the yield strength) were found in the weld metal and heat affected zone. To identify possible delayed cracking, the welds were tested by phased array ultrasonic testing (PAUT) after 48 h. Summarized, no significant occurrence of HAC was detected, indicating the high crack resistance of the welded joint, i.e., a suitable combination of base material, welding consumable and welding parameters. T2 - AJP 2023: 3rd International Conference on Advanced Joining Processes 2023 CY - Braga, Portugal DA - 19.10.2023 KW - Hydrogen assisted cracking KW - Submerged arc welding KW - Component test KW - NDT KW - Waiting time PY - 2023 AN - OPUS4-58672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popiela, Bartosz T1 - Influence of manufacturing process related residual stresses in wound composite material on the operational safety of H2 pressure vessels: PhD Topic Introduction N2 - Short introduction of the PhD Topic 5 in the BTU-BAM Graduate School "Trustworthy Hydrogen". Description of the objectives, deliverables and expected added value of the thesis. T2 - Introduction Week - BTU-BAM Graduate School "Trustworthy Hydrogen" CY - Berlin, Germany DA - 16.01.2023 KW - Residual stress KW - Composite KW - Pressure vessel KW - Hydrogen PY - 2023 AN - OPUS4-56882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chierici, Andrea A1 - Ciolini, Riccardo A1 - Lo Frano, Rosa A1 - D’Onofrio, Antonio A1 - Sabbarese, Carlo A1 - Pandalone, Antonio A1 - Romoli, Mauro A1 - di Meo, Paolo A1 - Finocchiaro, Paolo A1 - Conti, Enrico A1 - Gonella, Franco A1 - Andreetto, Paolo A1 - Checchia, Paolo A1 - Niederleithinger, Ernst A1 - d’Errico, Francesco T1 - Innovative Non-Destructive Techniques for Radioactive Waste Packages Monitoring N2 - A monitoring and surveillance system is a mandatory element to ensure that a radioactive waste disposal facility provides and meets the required level of safety during both its operational and closure periods. In this study an innovative approach for the identification and monitoring of the structural integrity of stored radioactive drums is presented. The activities were carried out in the context of the European Project PREDIS, whose goal is the development of a robust and reliable sensing technology for monitoring and long-term storage of radioactive waste packaging systems. Specifically, the focus was set on the development of innovative and smart sensor technologies, non-destructive examination tools, and/or devices capable to improve the safety of the storage by minimizing the number of interventions of cemented waste packages. Both conventional and innovative techniques, such as muon-tomography, SiLiF neutron and SciFi gamma detection, or contactless and smart radio transceiver technology provided with radiation monitoring sensors, have been considered and adapted for the use under repository conditions. Indeed, gamma and neutron detection techniques exploit the radiological information coming from inside the drums, while imaging techniques proved to be effective in spotting high density objects embedded inside the concrete: together, they allow to improve safety and security and can provide an early alert on behavioral changes hinting at anomalies in the drums. T2 - ASME 2023 International Conference on Environmental Remediation and Radioactive Waste Management CY - Stuttgart, Germany DA - 03.10.2023 KW - Radioactive waste KW - Waste packages KW - Radiation monitoring KW - Muon tomography KW - Integrity testing PY - 2023 SN - 978-0-7918-8753-0 DO - https://doi.org/10.1115/ICEM2023-110990 SP - 1 EP - 10 PB - American Society of Mechanical Engineers AN - OPUS4-60218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Günzel, Stephan T1 - Der sichere Wasserstofftransport - Eine Rechtsänderung in der Vorschau N2 - Das Bundesverkehrsministerium hat seit 2008 in drei Stufen jeweils auf Vorschlag der BAM einen Antrag zur Einführung bzw. Regulierung von Bergungsdruckgefäßen bei den Vereinten Nationen eingebracht. Die Anträge führten jeweils nach der Delegation in eine Arbeitsgruppe unter der Leitung des Vortragenden zu neuen Vorschriften im internationalen Gefahrguttransportrecht. Zuletzt hat das UN-Subcommittee der Experten für den Transport gefährlicher Güter der Einführung einer Druck-Volumen-Begrenzung für Druckgefäße zugestimmt. Mit dieser Begrenzung wurde die bisherige Volumenbegrenzung für Bergungsdruckgefäße ersetzt, wodurch nun das Spektrum der Bergungsdruckgefäße gestaltet werden kann, das notwendig wäre, um defekte Druckgefäße transportieren zu können. Das zentrale Kriterium für die Begrenzung des Druck-Volumen-Produktes (pV) fand bereits in den Landverkehrsvorschriften ADR/RID bis zu ihrer Neustrukturierung auch als Konsequenzmaß Verwendung. Damit soll sichergestellt werden, dass sich aus Wasserstofftransporten in Druckgefäßen keine Konsequenz entwickeln kann, die nach den Kriterien für stationäre Anlagen, einer Katastrophe gleichkommen würde. Hierzu hatte eine Arbeitsgruppe der Vereinten Nationen seit 2020 auf Vorschlag der BAM eine Kette aufeinander aufbauende Kriterien diskutiert, die im Vortrag vorgestellt werden: Einfluss der Druckwellen auf den menschlichen Körper (ohne Splitterwirkung oder Umsetzung der chemischen Energie) – Zusammenhang von Druckwelle und Fläche – Druckwellenberechnung – Bevölkerungsdichte – Grenzwerte für eine Katastrophe – resultierendes pV-Produkt. Das Ergebnis wurde mit herausragenden Großunfällen und Katastrophen aus dem Gefahrguttransport und Gefahrstoffbereich verglichen. Außerdem wurden noch die Effekte des Temperatureinflusses auf den maximalen Betriebsdruck diskutiert. Zuletzt wurde bei den UN darauf hingewiesen, dass mit Blick auf die Auswirkungsbetrachtung der Wassersoff das Gas mit den geringsten Konsequenzen bei gegeben Druk-Volumen-Produkt ist, was zu restriktiveren Obergrenzen für z.B. Erdgas führen könnte. Als letzter Punkt im Vortrag wird erläutert, dass in den kommenden UN-Sitzungen über nachfolgende Änderungen im Recht, wie z.B. der Kennzeichnung des pV-Produktes, diskutiert werden wird. Außerdem muss ein neuer Einstieg für die bei ISO in der Normung befindliche Umschließungen mit einem größeren pV-Produkt gefunden werden, wozu aber Transportland-spezifische Risikoanalysen in Verbindung mit massiven Fahrwegsbeschränkungen zu erwarten sind. T2 - 32. Erfahrungsaustausch für Gefahrgutbeauftragte (ERFA-T) des IGV CY - Berlin, Germany DA - 08.11.2023 KW - pV-Produkt KW - Quantitative Risikoanalyse KW - Konsequenzbegrenzung KW - Katastrophe KW - Druckgefäße PY - 2023 AN - OPUS4-58832 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maiwald, Michael T1 - Metrology for Advanced Hydrogen Storage Solutions (MefHySto) – Overviewand Tangible Results N2 - The European project MefHySto addresses the need of large-scale energy storage, which is required for a shift to renewable energy supply. The project is funded by the European Metrology Programme on Innovation and Research (EMPIR) and consists of 14 consortium partners from all over Europe (www.mefhysto.eu). It is demonstrated, how MefHySto is contributing to the EMN for Energy Gases aiming at prioritisation of the measurement gaps and challenges interacting with the EMN stakeholders. T2 - European Metrology Network Energy Gases “Measurement Solutions for Energy Gases” Workshop CY - Lisbon, Portugal DA - 21.03.2023 KW - MefHySto KW - EMPIR KW - Hydrogen Storage KW - Hydrogen Metrology KW - Hydrogen Purity KW - Geological Storage PY - 2023 AN - OPUS4-57193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich T1 - Introduction to Metrology in Chemistry N2 - Measurements are an important fundament of natural science in general and of chemical analysis in particular. Metrology is the science (and art) of performing measurements. The basic concepts and terms of metrology and their practical implementation are introduced. The very special peculiarities of chemical measurements that are absent in physical measurements are discussed. T2 - 7th PhD Seminar of the German Working Group for Analytical Spectroscopy (DAAS) in the GDCh Division of Analytical Chemistry CY - Berlin, Germany DA - 15.11.2023 KW - Metrology KW - Chemical Analysis PY - 2023 AN - OPUS4-58868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winckelmann, Alexander T1 - How does solid microanalysis profit from innovations in EUV research N2 - Research into new sources for EUV lithography is driving advancements in experimental methods tailored for this short wavelength range. This progress enables the exploration of spectroscopic techniques aimed at monitoring electronic transitions within this energy spectrum. Laser-induced breakdown spectroscopy (LIBS) serves as a rapid tool for elemental analysis, primarily established in the UV-vis range. However, LIBS encounters challenges such as limited repeatability precision and elevated background noise resulting from continuum radiation. In parallel, laser-induced extreme UV spectroscopy (LIXS) delves into the initial stages of plasma evolution, characterized by the emergence of soft X-ray and extreme UV radiation. The method benefits from a fast timeframe and constrained plasma confinement, leading to better precision. Nevertheless, LIXS encounters convoluted spectra arising from unresolved transition arrays (UTA), particularly pronounced for heavier elements. This complexity renders conventional univariate data analysis impractical, demanding the adoption of a multivariate data analysis approach. Multiple cathode samples, each coated with varying stoichiometries of lithium nickel manganese cobalt oxide (NMC), were prepared and used for calibration purposes. Through the application of Partial Least Squares (PLS) regression, a robust correlation with an R2 value exceeding 0.97 was achieved. The LIXS technique underwent a comparative evaluation against UV-vis LIBS. Furthermore, a comparison between univariate and multivariate analysis approaches was conducted, incorporating validation through y-randomization to mitigate overfitting risks. The viability of this approach was confirmed through the testing of an NMC reference material. The results showed metrological compatibility with reference values, underscoring the potential capability of the proposed methodology. T2 - 322. PTB Seminar 2023 - VUV and EUV Metrology CY - Berlin, Germany DA - 14.11.2023 KW - Laser induced XUV spectroscopy KW - Lithium-ion batteries KW - Solid microanalysis PY - 2023 UR - https://www.euv2023.ptb.de/ AN - OPUS4-58834 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich T1 - MefHySto - Metrology for Advanced Hydrogen Storage Solutions N2 - An overview on the almost completed EMPIR-MefHySto-Project is given. T2 - Workshop on Green Hydrogen CY - Montevideo, Uruguay DA - 12.10.2023 KW - MefHySto KW - Hydrogen storage KW - Metrology PY - 2023 AN - OPUS4-58650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ziel, Ruben P. A1 - Zalewska, Ewelina A1 - van der Veen, Adriaan M. H. A1 - Kipphardt, Heinrich A1 - Tuma, Dirk A1 - Esteban, Andres Rojo A1 - Fernandez Vicente, Teresa Esperanza A1 - Mace, Tatiana A1 - Sutour, Christophe A1 - Marioni, Fabrice A1 - Fükö, Judit A1 - Szücs, László A1 - Büki, Tamás A1 - Szilágyi Nagyné, Zsófia A1 - Cieciora, Dariusz A1 - Ochman, Grzegorz A1 - Romanowski, Przemysław A1 - Lis, Anna A1 - Garnuszek, Magdalena A1 - Valkova, Miroslava A1 - Ackermann, Andreas A1 - Pascale, Celine A1 - Niederhauser, Bernhard A1 - Tarhan, Tanil A1 - Boztepe, Aylin A1 - Beránek, Jan A1 - Bárta, Miroslav T1 - International comparison EURAMET.QM-K3.2019 - Automotive exhaust gases N2 - EURAMET.QM-K3.2019 was a repeat of the key comparison EURAMET.QM-K3 on the composition of automotive exhaust gases. New in EURAMET.QM-K3.2019 was the addition of the amount fraction oxygen to the programme. The key comparison reference values were obtained independently, using static gravimetry and appropriate corrections from purity analysis and are linked to those of CCQM-K3.2019. The key comparison results show equivalence between the measurement standards maintained by the participating national metrology institutes. The demonstrated equivalence can be used to underpin services related to automotive exhaust gases as well as generically through the flexible scheme ("track A"). KW - CCQM KW - Automotive gases PY - 2023 DO - https://doi.org/10.1088/0026-1394/60/1A/08030 SN - 1681-7575 VL - 60 IS - 1A SP - 1 EP - 63 PB - IOP Publishing CY - Bristol AN - OPUS4-58904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lozano-Martín, D. A1 - Tuma, Dirk A1 - Kipphardt, Heinrich A1 - Khanipour, Peyman A1 - Chamorro, C. R. T1 - Thermodynamic characterization of the (H2 + C3H8) system significant for the hydrogen economy: Experimental (p, rho, T) determination and equation-of-state modelling N2 - For the gradual introduction of hydrogen in the energy market, the study of the properties of mixtures of hydrogen with typical components of natural gas (NG) and liquefied petroleum gas (LPG) is of great importance. This work aims to provide accurate experimental (p, rho, T) data for three hydrogen-propane mixtures with nominal compositions (amount of substance, mol/mol) of (0.95 H2 + 0.05 C3H8), (0.90 H2 + 0.10 C3H8), and (0.83 H2 + 0.17 C3H8), at temperatures of 250, 275, 300, 325, 350, and 375 K, and pressures up to 20 MPa. A single-sinker densimeter was used to determine the density of the mixtures. Experimental density data were compared to the densities calculated from two reference equations of state: the GERG-2008 and the AGA8-DC92. Relative deviations from the GERG-2008 EoS are systematically larger than those from the AGA8-DC92. They are within the ±0.5% band for the mixture with 5% of propane, but deviations are higher than 0.5% for the mixtures with 10% and 17% of propane, especially at low temperatures and high pressures. Finally, the sets of new experimental data have been processed by the application of two different statistical equations of state: the virial equation of state, through the second and third virial coefficients, B(T, x) and C(T, x), and the PC-SAFT equation of state. KW - Hydrogen-containing gas mixture KW - Density data KW - Equation of state KW - Virial coefficients PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-570056 DO - https://doi.org/10.1016/j.ijhydene.2022.11.170 SN - 0360-3199 VL - 48 IS - 23 SP - 8645 EP - 8667 PB - Elsevier B. V. CY - Amsterdam AN - OPUS4-57005 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eiben, Mario T1 - Die Aufgaben der BAM als zuständige Behörde im Gefahrgutbereich in Deutschland N2 - Die BAM ist zuständige Behörde in Deutschland für bestimmte Aufgaben im Gefahrgutbereich, die u. a. in § 8 der Gefahrgutverordnung Straße, Eisenbahn und Binnenschifffahrt (GGVSEB) und § 12 der Gefahrgutverordnung See (GGVSee) aufgeführt sind und hauptsächlich von den Abteilungen 2 und 3 wahrgenommen werden. So ist die BAM bspw. die in Deutschland für die Zulassung von Verpackungen und Tanks oder auch die Einstufung bestimmter gefährlicher Güter zuständige Stelle. Die BAM arbeitet des Weiteren als Kompetenzbehörde national und international in den entsprechenden Gremien mit und berät das BMDV in der Rechtsfortentwicklung der internationalen Vorschriften für den Gefahrguttransport. Dies geschieht u. a. durch die Mitarbeit im Ständigen Ausschuss Gefahrgutbeförderung (AGGB) des Gefahrgut-Verkehrs-Beirats beim BMDV und den zugehörigen Arbeitsgruppen, oder auch das Erstellen von Anträgen für Rechtsänderungen in den internationalen Vorschriften der Vereinten Nationen (UN) bzw. der Wirtschaftskommission für Europa der UN (UNECE) im Auftrag des BMDV. Die Beratung der betroffenen Wirtschaft und die Normungsarbeit sind weitere wichtige Themen. Die Expertise der BAM wird insbesondere durch Forschung im Gefahrgutbereich erhalten und weiter ausgebaut. Im Rahmen des Vortrags werden drei Forschungsbereiche vorgestellt, von denen zwei für die Energiewende von großer Bedeutung sind. T2 - 10. Deutsche Gefahrgut-Sicherheitstage CY - Nürburg, Germany DA - 13.09.2023 KW - Gefahrgut KW - Zuständige Behörde KW - Transport gefährlicher Güter KW - Gremienarbeit KW - Normung KW - Forschung KW - Gesetzliche Aufgaben PY - 2023 AN - OPUS4-58350 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - Entwicklungen rings um Gase als Energieträger N2 - Dr. Mair erläutert, welcher Anwuchs an H2-Bedarf zu erwarten ist, wo er weltweit erzeugt werden könnte und in welcher Form auf grünem Wasserstoff basierende Energieträger transportiert werden können. Es wird deutlich, dass das Transportaufkommen von H2 erheblich anwachsen wird und dass sich alle Seiten, die Regelsetzer und die Industrie darauf vorbereiten müssen. Danach wird mit Blick auf die Normungsroadmap H2 des DIN der probabilistische Ansatz mit seinem Potenzial, Normen und Vorschriften in ihrer Wirkung zu simulieren und zu bewerten kurz vorgestellt. Der dritte Block des Vortrages beginnt mit der Definition von Sicherheit, zeigt kurz das mikromechanische Prinzip der Alterung von Composite und greift dann ein Thema auf, dass Dr. Mair bereits 2018 und 2019 in dieser Runde dargelegt hat: Der Aufwand für die klassische Wiederkehrende Prüfung ist enorm und bringt nur wenig Erkenntnis. Es werden graphisch das 5-Jahres 100%-Prooftesting, der Ansatz nach GGR 022 mit seiner zerstörend geprüften Stichprobe und der mögliche Ansatz für eine ergebnisgesteuerte Stichprobenprüfung auf ZfP-Basis miteinander verglichen. Die Unterschiede im Aufwand-zu-Nutzen-Verhältnis sind enorm. Dabei ist der aufwändigste Ansatz zudem der mit der geringsten Erkenntnistiefe. Jeder Ansatz, der von einer 100%-Prüfung in einem maximalen Zeitrahmen von 10 Jahren abweicht, also z.B. der Verzicht auf eine 100%-Prüfung während des Betriebes, würde eine Änderung des Regelwerkes erfordern, die zeitnah angestoßen werden müsste. Da es sich hierbei primär um eine Ressourcenoptimierung und nicht um eine Verbesserung der Sicherheit handelt, liegt der Ball bei den Verbänden. Als eine Idee für das Herangehen mit einer Begrenzung auf Druckgefäße, die nach der EN 17339 zulassungsfähig sind (fest montiert, H2 und nur CFK), verweist Dr. Mair auf die SV 674 in Verbindung mit 6.2.3.5.3/.4 ADR/RID. Bei dem absehbaren Anwachsen des Bestandes an H2-Batteriefahrzeugen, ist hier nicht nur ein Optimierungsaspekt, sondern auch ein Kapazitätsproblem in der wiederkehrenden Prüfung zu lösen. Es würde aber auch ein Mehrwert für die Sicherheit entstehen. T2 - 30. BAM-DIN-IGV-DVFG Treffen CY - Berlin, Germany DA - 22.02.2023 KW - Wasserstoffspeicher KW - Markthochlauf KW - Sicherheit KW - Wiederkehrende Prüfung KW - Schallemissionsanalyse PY - 2023 AN - OPUS4-57041 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Duffner, Eric A1 - Günzel, Stephan T1 - Die Zukunft der Betriebsüberwachung von Gasspeichern aus Composite N2 - Im Vortrag wird zunächst erläutert, dass auch im Fall der Wasserstoffversorgung die Schadensanalyse, -vermeidung und die wiederkehrende Prüfung von Speichern in engem Zusammenhang stehen. Der Wasserstofftransport in Deutschland hat bereits deutlich zugenommen und wird in den nächsten Jahren weiter erheblich zunehmen. Dies führt zu einem stärkeren Fokus auf die wirtschaftlichen Aspekte im Transport und der wiederkehrenden Prüfung. Letztere droht, ohne neue technische Ansätze zum Flaschenhals in der Verfügbarkeit vorhandener Transportkapazitäten zu werden. Das gegenwärtige System der Wasserdruckprüfung bis zum sog. Prüfdruck mit Innen- und Außenbesichtigung etc., die im Normalfall alle 5 Jahre durchzuführen ist, führt zu jeweils etwa 8 Wochen Stillstand. Das Aufwendige dabei sind die Trocknungs- und Spülprozesse, die notwendig sind, um wieder entsprechend reinen Wasserstoff abfüllen zu können. Auf Basis der BAM GGR‘n 021 und 022 lässt sich beim Nachweis entsprechender, probabilistischer Restzuverlässigkeiten diese Frist in Deutschland auf 10 Jahre ausdehnen. Diesen Weg sind in den letzten Jahren viele Betreiber gegangen. Mit Blick auf die derzeit fast exponentielle Zunahme von Transporteinheiten kann auch diese Verlängerung der Prüffristen das Problem nicht lösen. Auch das Umschwenken von hydraulischer, auf die heute bereits genehmigungsfähige Gasdruckprüfung bis zum Prüfdruck bringt zwar eine Verkürzung der Stillstandzeiten, erfordert aber erhebliches Investment in Schutzmaßnahmen. Als hinreichend zielführendes Konzept für Transporteinheiten mit vielen Elementen wird im Vortrag eine Mischung aus probabilistischem Ansatz und zerstörungsfreien Prüfungen erläutert und bzgl. Aufwand und Nutzen im Vergleich zu den üblichen Verfahren visualisiert. Voraussetzung für diesen vorgestellten Ansatz sind die Weiterentwicklung und Qualifizierung der Schallemissionsanalyse als Ersatz für die derzeitig zerstörenden Prüfungen und auch eine durchgängig digitale Lebenslaufakte, die eine lückenlose Zuordnung von Baumusterprüfung, Herstellungslos, Betreiber und Betriebsdaten erlaubt. Für Transporteinheiten mit wenigen, sehr großen Elementen wird dagegen das sog. Online-Monitoring mit fest installierter und permanent messender Technik gesehen. Für die Anwendung beider Lösungsansätze sind umfangreiche Änderungen im Recht erforderlich. T2 - 49. VDI-Jahrestagung Schadensanalyse 2023: Schadensprävention bei Druckwasserstoff und Schadensprävention für Kunststoff- und Elastomerprodukte CY - Würzburg, Germany DA - 18.10.2023 KW - ATR Anerkanntes Technisches Regelwerk KW - Probabilistik KW - Zerstörungsfreie Prüfung KW - Online-Monitoring KW - Schallemissionsanalyse KW - Gasdruckprüfung PY - 2023 AN - OPUS4-58838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günzel, Stephan T1 - Safety assessment of hydrogen gas storage systems N2 - In this lecture, the safety assessment of hydrogen gas storage systems is presented using the example of composite pressure vessels. The main element is a probabilistic approval approach based on five steps. Firstly, the testing and evaluation of properties at the beginning of life are shown. Secondly, methods for artificial aging and the effect on the residual strength are presented. Thirdly, testing against dedicated accidents is introduced. Fourthly, effects on the surveillance of production quality are discussed. Finally, degradation and the end of life are estimated. Background information and examples are given for each step. The assessment presented is a method applicable for many safety-related systems. T2 - Masterstudiengang Wasserstofftechnologie - Modul 8: Safety and Public Acceptance – Sicherheitsaspekte, Akzeptanz und werkstofftechnische Herausforderungen des Wasserstoffs CY - Online meeting DA - 25.08.2023 KW - Safety KW - Hydrogen KW - Wasserstoff KW - Bewertung KW - Assessment PY - 2023 AN - OPUS4-59899 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günzel, Stephan T1 - Safety assessment of hydrogen gas storage systems N2 - In this lecture, the safety assessment of hydrogen gas storage systems is presented using the example of composite pressure vessels. The main element is a probabilistic approval approach based on five steps. Firstly, the testing and evaluation of properties at the beginning of life are shown. Secondly, methods for artificial aging and the effect on the residual strength are presented. Thirdly, testing against dedicated accidents is introduced. Fourthly, effects on the surveillance of production quality are discussed. Finally, degradation and the end of life are estimated. Background information and examples are given for each step. The assessment presented is a method applicable for many safety-related systems. T2 - Joint European Summer School 2023, Hydrogen Safety CY - Online meeting DA - 17.09.2023 KW - Safety KW - Hydrogen KW - Wasserstoff KW - Bewertung KW - Assessment PY - 2023 AN - OPUS4-59903 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Balderas-Xicohtencatl, R. A1 - Villajos Collado, José Antonio A1 - Casabán, J. A1 - Wong, D. A1 - Maiwald, Michael A1 - Hirscher, M. T1 - ZIF‑8 Pellets as a Robust Material for Hydrogen Cryo-Adsorption Tanks N2 - Cryoadsorption on the inner surface of porous materials is a promising solution for safe, fast, and reversible hydrogen storage. Within the class of highly porous metal−organic frameworks, zeolitic imidazolate frameworks (ZIFs) show high thermal, chemical, and mechanical stability. In this study, we selected ZIF-8 synthesized mechanochemically by twin-screw extrusion as powder and pellets. The hydrogen storage capacity at 77 K and up to 100 bar has been analyzed in two laboratories applying three different measurement setups showing a high reproducibility. Pelletizing ZIF-8 increases the packing density close to the corresponding value for a single crystal without loss of porosity, resulting in an improved volumetric hydrogen storage capacity close to the upper limit for a single crystal. The high volumetric uptake combined with a low and constant heat of adsorption provides ca. 31 g of usable hydrogen per liter of pellet assuming a temperature−pressure swing adsorption process between 77 K − 100 bar and 117 K − 5 bar. Cycling experiments do not indicate any degradation in storage capacity. The excellent stability during preparation, handling, and operation of ZIF-8 pellets demonstrates its potential as a robust adsorbent material for technical application in pilot- and full-scale adsorption vessel prototypes. KW - Hydrogen adsorption storage KW - Metal−organic frameworks KW - ZIF-8 KW - Cryoadsorption KW - Hydrogen Storage KW - MefHySto PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569473 DO - https://doi.org/10.1021/acsaem.2c03719 SN - 2574-0962 SP - 1 EP - 8 PB - ACS Publications CY - Washington DC AN - OPUS4-56947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT ED - Tuma, Dirk ED - Weide, T. ED - Rasmusson, H. T1 - MefHySto - Metrology for advanced hydrogen storage solutions N2 - The “Metrology for Advanced Hydrogen Storage Solutions” (MefHySto) project is a European initiative addressing the need for large-scale energy storage solutions, that is crucial for the successful transition to renewable energy sources. The main objective of this project was to develop and provide metrological standards and validated techniques for the storage and utilization of hydrogen. Hydrogen is increasingly recognized as an important component in the future energy system due to its ability to store and supply energy during peak demand periods when renewable sources, such as solar and wind, are not generating power. KW - Water electrolysis KW - Thermophysical properties KW - Fuel cell KW - Hydrogen storage PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625952 DO - https://doi.org/10.5281/zenodo.12684898 SP - 1 EP - 40 PB - ERIG European Research Institute for Gas and Energy Innovation a.i.s.b.l. CY - Bruxelles AN - OPUS4-62595 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera T1 - Material research and multi-sensory monitoring for concrete sealing structure in rock salt underground repositories N2 - Within the project SealWasteSafe, we advance construction materials and non-destructive monitoring concepts of sealing structures applied for underground disposal of nuclear waste. As these engineered barriers have high demands regarding structural integrity, an innovative alkali-activated material (AAM) that is highly suitable for the application in salt as a host rock is improved and tested on two laboratory scales. This AAM has a low heat evolution due to the reaction mechanism in comparison to common salt concretes based on Portland cement or magnesium oxychloride binders. Hence, crack formation due to thermally induced stress during the hardening process is reduced. After successful laboratory tests with small specimens (height ~5 cm), comparably manufactured large cubic (edge length 70 cm) and cylindrical specimens (height 120 cm, diameter 40 cm) are equipped with sensing technologies to demonstrate the sensors´ technical capabilities. A comprehensive multi-sensory monitoring scheme is developed and investigated to characterize and compare the different material behaviour during the setting and hardening process of two materials: (1) the newly developed AAM-based mortars with salt aggregate, and (2) a blended Portland cement-based salt concrete as reference. The analysed parameters include temperature and humidity of the material, acoustic emissions, and strain variations recorded by fiber optic cables. Passive sensor systems based on radiofrequency identification technology (RFID) embedded in the concrete provide an interface for the wireless readout of various sensors. In parallel to the embedded RFID sensors, conventional cabled systems to read out the temperature and humidity measurements are installed for comparison. Additionally, a detailed inspection of the two large cubic specimens after a monitoring period of more than six months has been undertaken. Active thermography and ultrasonic echo measurements are used to reveal potentially occurring inner cracks from the surface. To verify the non-invasive results, a core sample (diameter 2 cm) was extracted from each of the investigated cubic specimens and analysed in detail with X-ray computed tomography. Furthermore, ultrasonic methods are used for quality assurance to detect obstacles, cracks, and delamination at in-situ scale sealing structures. Experimental layout and applied imaging techniques are optimised to enhance the image quality for measurements from the front side of the engineered barrier. To characterize the inside of the test sealing structure and to improve the detection of potentially existing cracks, an ultrasonic borehole probe using the phased array technique is developed. First analyses at a half-spherical specimen coincide with modelling results and prove the reliability of the directional response caused by the phased array technique of the newly constructed ultrasonic borehole probe. Overall, the project SealWasteSafe helps to characterize construction materials and improves multi-sensory monitoring concepts and ultrasonic equipment for the sake of quality assurance. Particularly for salt as a host rock, this will help to design safe sealing structures for nuclear waste disposal. T2 - EGU General Assembly 2023 CY - Vienna, Austria DA - 23.04.2023 KW - SealWasteSafe KW - Engineered barriers KW - Salt concrete KW - Quality assurance KW - Ultrasound KW - CT KW - Thermography PY - 2023 DO - https://doi.org/10.5194/egusphere-egu23-11582 AN - OPUS4-57500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera T1 - Untersuchung eines Spritzbeton-Probekörpers unter Tage mit Ultraschall N2 - Für die sichere Endlagerung nuklearer Abfälle sind im Salzgestein Verschlussbauwerke aus Salzbeton als geotechnischen Barrieren vorgesehen. Um die Integrität der Bauwerke im Rahmen einer Qualitätssicherung nachzuweisen, eignet sich eine zerstörungsfreie Prüfung (ZfP) mit Ultraschall-Verfahren. Potenziell auftretende Risse oder Ablösungen sowie Einbauteile können detektiert werden. Um die Möglichkeiten und Grenzen der Ultraschall-Echo-Messungen sowie der Auswertemethoden zu untersuchen, wurden in einem aus Spritzbeton hergestellten Testbauwerk in der Grube Teutschenthal (bei Halle, Deutschland) verschiedene Störkörper während der Betonage eingebettet. Die Störkörper (Breite 3 cm bis ~8 cm) liegen in Tiefen von etwa 30 cm bis 80 cm und repräsentieren Hohlräume, Risse oder Inhomogenitäten des Betons. Von der Oberfläche führten wir Ultraschall-Echo-Messungen auf einer Fläche von etwa 100x150 cm² in einem 3D Modus durch. Die Auswertung erfolgte zunächst mithilfe der in der ZfP etablierten Synthetic-Aperture-Focusing Technique (SAFT), die der Kirchhoff Migration ähnelt. Insgesamt wird eine Vielzahl von Reflektoren im Bauwerk abgebildet, die jedoch nur in wenigen Fällen den eingebauten Störkörpern zugeordnet werden konnten, so dass auch die Grenzen des Verfahrens bei dieser Bauweise deutlich werden. Allerdings konnte eine ungeplante großflächige (>30 cm) Ablösung nachgewiesen und durch anschließende Bohrungen verifiziert werden. Um das strukturelle Abbild des Bauwerksinneren trotz des stark streuenden Spritzbetons zu verbessern, wenden wir fokussierende Migrationsverfahren an. Erste Ergebnisse zeigen, dass eine klarere Abbildung einzelner Reflektoren erreicht werden kann. Dies erleichtert die Detektion einzelner Objekte. Das hier präsentierte Experiment mit bekannten Reflektoren unter realen Bedingungen mit Spritzbeton unter Tage bietet hervorragende Möglichkeiten zur Überprüfung von methodischen Weiterentwicklungen im Bereich der Ultraschallanalyse. Durch die Verbesserung der Auswertemethodik und der darauf basierenden ultraschallbasierten Qualitätssicherungskonzepte werden insgesamt sicherere Verschlussbauwerke für nukleare Endlager ermöglicht. T2 - 83. Jahrestagung der Deutschen Geophysikalischen Gesellschaft (DGG) CY - Bremen, Germany DA - 06.03.2023 KW - Ultraschall KW - Spritzbeton KW - Qualitätssicherung KW - Abbildungsverfahren PY - 2023 AN - OPUS4-57136 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera T1 - Multi-sensory monitoring and ultrasound for quality assurance at underground sealing structures N2 - Within the safety concepts of underground disposal sites of nuclear waste, engineered barriers play an important role. As these sealing structures have high demands concerning integrity, we aim at advancing the available construction materials, monitoring and inspection techniques within the project SealWasteSafe. After successful laboratory analysis on the cm-scale, cylindrical and cuboid specimens on the m-scale are produced from classical salt concrete and a specifically developed alkali-activated material. A comprehensive multi-sensory monitoring scheme is applied to compare the setting process of both materials and to demonstrate the sensors’ resistance to highly alkaline environments. Besides temperature and humidity of the materials, strain variations using fibre optic sensors and acoustic emissions are recorded over periods of at least 28 days, partly for more than 8 months. Passive sensor systems based on radiofrequency identification technology (RFID) embedded in the concrete allow for wireless access to temperature and humidity measurements and are compared to conventional cabled systems. After hardening and removal of the outer casings of the specimens, further non-destructive evaluations using ultrasonic echo and thermographic measurements are conducted. Preliminary results clearly highlight differences between the tested materials, particularly showing lower acoustic emission activity for the newly developed alkali-activated material potentially indicating less phase changes or cracks. Complementary, ultrasonic methods are improved to be used for quality assurance to detect obstacles, potential cracks and delamination at in-situ sealing structure scale. A unique large aperture ultrasonic system (LAUS) with depth penetration as large as 9 m has already successfully been applied at the test site in Morsleben, Germany, of the federal company for radioactive waste disposal (BGE). Modelling studies help to further optimize the measurement layout. Advanced imaging techniques applied to the modelled and measured data will further improve the obtained images of internal structures. Additionally, an ultrasonic borehole probe is developed and constructed using phased arrays to further enhance the detection of potential cracks. Modelling and preliminary results from laboratory specimens prove the feasibility and potential of the directional response even in heterogeneous material such as concrete. Final investigations under in-situ conditions at the test site of the sealing structure are planned. Overall, the project SealWasteSafe improves the construction material, multi-sensory monitoring, and ultrasound for quality assurance to allow for the development of safe nuclear sealing structures. Although the techniques are tailored for sealing structures within salt as a host rock, they are transferrable to a wider field of applications and alternative disposal conditions. T2 - NDE NucCon CY - Espoo, Finland DA - 25.01.2023 KW - SealWasteSafe KW - Engineered barriers KW - Monitoring KW - Embedded sensors KW - Ultrasonic imaging PY - 2023 AN - OPUS4-56927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst T1 - Nuclear concrete, and how to live with it more easy using NDE N2 - This keynote presentation compiles the specialities of civil engineering compared to other disciplines, of NDT in civil engineering compared to other filds of NDT and the specific challenges of applications in the nuclear energy and disposal sector. T2 - NucCon 2023 CY - Espoo, Finland DA - 25.01.2023 KW - NDT KW - Concrete KW - Nuclear PY - 2023 AN - OPUS4-56912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Fügetechnik in Wasserstofftechnologien: Erzeugung, Transport, Speicherung, Nutzung N2 - Der Vortrag gibt einen kurzen Überblick über die Bedeutung der Fügetechnik in Wasserstofftechnologien und über zukünftige FuE-Bereiche. Fügetechnologien haben dabei wesentliche Bedeutung für die Umsetzung von technischen Komponenten der Wasserstofftechnologien. Forschungsschwerpunkte ergeben sich insbesondere für die Erzeugung und den Transport des Wasserstoffs. T2 - Vortragsreihe des DVS Bezirksverbandes Berlin CY - Berlin, Germany DA - 22.02.2023 KW - Wasserstoff KW - Fügetechnik KW - Forschung KW - Review PY - 2023 AN - OPUS4-57040 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Babutzka, Martin A1 - Zekhnini, Khalid A1 - Seifert, Lando A1 - Le, Quynh Hoa A1 - Grabowski, Sven T1 - Schlussbericht zum Forschungsvorhaben „Verbundvorhaben: "KKS-Gründung" - Korrosionsmonitoring und aktiver kathodischer Korrosionsschutz von Offshore-Gründungsstrukturen - Teilvorhaben: Korrosionsprüfungen im Laborcontainer“ in der Fördermaßnahme „Anwendungsorientierte nichtnukleare FuE im 6. Energieforschungsprogramm“ im Förderbereich „Windenergie“ N2 - Das Ziel des Verbundforschungsvorhabens KKS-Gründung war die Entwicklung eines Monitoringsystems zur Erfassung von Korrosion an Gründungsstrukturen im Labormaßstab. Dafür war eine umfassende Bewertung und Beschreibung korrosionsbeeinflussender Faktoren und der Korrosionssysteme notwendig. Im Vorhaben KKS-Gründung wurde die Gründungsstruktur unterhalb der Wasserlinie betrachtet bis hin zum anaeroben Bereich im Sediment. Insbesondere der Sedimentbereich wurde bisher nur unzureichend betrachtet. Da die komplexen Mechanismen in der Sedimentzone noch nicht ausreichend wissenschaftlich untersucht wurden, mussten Möglichkeiten entwickelt werden, um diese zu bewerten. Im Verbundforschungsvorhaben KKS-Gründung agierte die Bundesanstalt für Materialforschung und -prüfung (BAM) als Forschungsstelle. Die Hauptziele des Teilvorhabens der BAM waren die Bereitstellung einer Messumgebung für das von den Partnern entwickelte Monitoringsystem, die umfassende wissenschaftliche Beschreibung der Korrosionssysteme im Unterwasserbereich und Sediment sowie die Gewinnung von Messdaten zur Verifizierung und Überführung in die Simulation. Als Forschungsstelle war die BAM der Ansprechpartner für die Verbundpartner bei wissenschaftlichen Fragestellungen. Die Hauptziele des Vorhabens wurden erreicht und es wurden grundlegende Erkenntnisse zum Korrosionsverhalten von Offshore-Stahl im Unterwasser und Sedimentbereich gewonnen. Darüber hinaus wurden wichtige Erkenntnisse zum Betrieb eines Laborcontainers und zur Nachstellung von Korrosionssystemen in Meerwasserbecken bei Verwendung von künstlichem Meerwasser und Sand als Sediment gewonnen. Eine Beschreibung und Bewertung der Korrosivität und ablaufender Reaktionen in den einzelnen Belastungszonen wurde mittels elektrochemischer und gravimetrischer Verfahren vorgenommen. KW - Korrosionsschutz KW - KKS KW - Korrosionsmonitoring KW - Offshore-Windenergieanlagen KW - Meerwasser KW - Sediment PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569252 SP - 1 EP - 74 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-56925 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten T1 - Residual stress formation in DED-arc manufactured high strength steel components N2 - Additive manufacturing (AM) processes enable the efficient production of advanced constructions. New developments in topology optimization are leading to weight-optimized designs of increasing complexity. Direct energy deposition processes (DED) such as wire and arc-based additive manufacturing are an important method of additive manufacturing. The wire filler metals enable a wide range of materials, while the arc process provides a high deposition rate compared to laser and powder-based processes. Combined with the use of high-strength steels, the thickness of walls or components can be significantly reduced in the context of lightweight construction, which results in significant savings in energy, costs, time and resources. Suitable high-strength steel filler metals are commercially available for DED-arc AM processes. However, guidelines and quantitative knowledge about welding stresses and cold cracking issues during component production and service are lacking. This limits the industrial application considerably. In a joint project of BAM and Chemnitz University of Technology, the main influences and complex interactions of material, production process, design and processing steps on the residual stress level are investigated. The aim is to develop processing recommendations and a cold cracking test for economical processing and stress-related design of high-strength steels with DED-arc. This study focuses on residual stress analysis by neutron diffraction (ND) and X-ray diffraction (XRD) on defined test specimens. The ND analysis were performed at the Paul Scherrer Institute- Villigen, Switzerland (PSI) and the XRD analysis at BAM. The study shows a quantitative and qualitative comparison of the residual stress magnitudes and distribution between the component bulk (ND) and surface (XRD) analyses. The ND analysis reveals that in DED-arc AM walls the residual stresses dominate in the direction of welding and are negligibly small in each case transverse to the direction of welding. The topology of the analyzed residual stresses shows almost identical residual stress maps compared to XRD. In addition, the residual stresses are significantly influenced by the solid phase transformation of the material due to low cooling times and less post heat treatment cycles of following AM layers in the area of the top layer. T2 - IIW Intermediate Meeting C-XIII CY - Online meeting DA - 20.04.2023 KW - Additive Manufacturing KW - High strength steel KW - Residual Stress PY - 2023 AN - OPUS4-59308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Konert, Florian T1 - Evaluation of the tensile properties of X65 pipeline steel in compressed gaseous hydrogen using hollow specimens N2 - Hydrogen has great potential into the decarbonization process of the energy and transport sectors, thus helping to mitigate the urgent issue of global warming. It can be sustainably produced through water electrolysis with potentially zero emissions, and efficiently used in fuel cell systems. Despite its environmental advantages, hydrogen is an extremely flammable substance and its interaction with most metallic materials could result in their mechanical properties degradation to an extent that could make them inherently unsafe. Extensive material testing under realistic operating conditions is required to determine the criteria under which hydrogen-induced damage is to be expected. In-situ slow strain rate tensile (SSRT) test is an option that allow the quantification of the behavior of metals in hydrogenated environments. The standardized procedure for testing in-situ the pressurized gaseous hydrogen effect on metals consists of the utilization of an autoclave as a containment volume. Testing inside an autoclave is difficult, expensive, and time-consuming, and requires specialized equipment and trained personnel. A relatively recent method to circumvent these issues and provide affordable and reliable test results consists in using hollow specimens as the gas containment volume, thus applying the hydrogen pressure inside rather than outside the specimen. This experimental setup allows us to minimize the volume of hydrogen and perform the tests safely and effectively. This study focuses on the evaluation of tensile properties of X65 pipeline steel, which was in vervice for natural gas transport, tested in a high-pressure hydrogen environment using hollow specimens. A constant nominal strain rate of 1ꞏ10-6 s-1 is applied. Tests are performed with different manufacturing techniques for the drilling process, which results in difeerent surface conditions. The effect of the roughness on the HE was investigated. For the evaluation the effect on the reduced area at fracture (RA) and the elongation loss were determined. Further fractographic analysis were performed. In this way, this study provides insights on the applicability of novel, reliable, and safer testing method which can be used to assess HE, particularly in relation with hydrogen-induced loss of ductility in metallic material. T2 - ICSI 2023 | 5th International Conference on Structural Integrity CY - Funchal, Portugal DA - 29.8.2023 KW - Hydrogen KW - Hollow-specimen KW - SSRT KW - Ferritic steel KW - Hydrogen embrittlement PY - 2023 AN - OPUS4-58141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -