TY - CONF A1 - Schröpfer, Dirk T1 - Residual stress evaluation using the contour method of an additive manufactured high-strength steel solid cuboid N2 - Direct Energy Deposition with Arc (DED-Arc) enables the weight-optimized and near-net-shape manufacturing of complex structures. Lightweight construction principles allow a reduction of CO2 emissions by saving time, costs, and resources. Further optimisations can be achieved by using high-strength steel. This allows for a reduction in wall thickness and optimisation of weight. However, manufacturing intricate geometries using high-strength steels poses challenges in managing residual stresses (RS), which are essential for ensuring the structural integrity of welded components. High residual stresses can increase the risk of cold cracking, arising from the complex interactions between material properties, process conditions, and component design. Despite the availability of suitable filler metals, the lack of comprehensive knowledge and guidelines on residual stress formation limits the industrial application. Therefore, in the present study, the contour method (CM) was used to analyse the full field longitudinal residual stresses in an solid cuboid component (dimensions: 120 × 50 × 35 mm³) manufactured by DED-Arc. The CM enables the analysis of the two-dimensional map of residual stresses normal to a cutting plane using a finite element model. For this purpose, a solid cuboid component was welded fully automatically with a high-strength solid wire specially adapted for DED-Arc (yield strength > 790 MPa) onto conventionally manufactured substrates made of S690QL. The residual stresses from CM in the volume are compared with residual stress analyses using X-Ray diffraction on the surface. Additionally, comparative data from previous studies on hollow cuboid structures was included in order to identify similarities and differences in the resulting stress state, and to complement and validate the CM results. These results demonstrate the significant influence of the geometry on the residual stress profiles within the solid cuboid in relation to the open hollow. T2 - 4th International Conference on Advanced Joining Processes 2026 CY - Coimbra, Portugal DA - 16.10.2025 KW - Residual stress KW - Contour method KW - DED-Arc/M KW - High-strength steel KW - Filler metals KW - Neutron diffraction PY - 2025 AN - OPUS4-65209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas A1 - Fabry, Cagtay A1 - Thiele, Marc A1 - Artinov, Antoni A1 - Rethmeier, Michael T1 - Automated Arc Welding and Sensor Based Quality Assessment for Enhancing Fatigue Strength and Structural Reliability of Offshore Wind Turbine Supports N2 - Offshore wind energy plays a crucial role in achieving a carbon dioxide free industrial sector in the coming decades. However, foundation systems for offshore wind turbines significantly impact the overall installation process, posing technical and regulatory challenges. Adopting lightweight design principles in steel construction such as dissolved load bearing structures in jacket foundations offers substantial potential for reducing resource consumption, particularly steel usage. This presentation explores the complete digitalization of welding manufacturing and testing processes, enabling fully automated production and data driven quality assessment of tubular nodes, which are vital components of jacket foundations. The study also investigates the relationship between seam geometry and fatigue strength inspired by bionic design principles. The results demonstrate that tubular nodes can be welded entirely automatically, accommodating geometric tolerances, and that seam geometries ca n be precisely manufactured according to suggestions from e.g. numerical models or other sources . These advancements significantly enhance the fatigue strength and service life of offshore wind turbine support structures. T2 - IIW Annual Assembly 2025 CY - Genova, Italy DA - 23.06.2025 KW - Automated gas metal arc welding KW - Quality assessment and control KW - Support structures KW - Fatigue PY - 2025 AN - OPUS4-65232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Graebner, Maraike A1 - Giese, Marcel A1 - Lorenz, Svenja A1 - Treutler, Kai A1 - Schröpfer, Dirk A1 - Wesling, Volker A1 - Kannengießer, Thomas T1 - Wear resistance of modified NiMoCrSi claddings in relation to the resulting surface machinability via ultrasonic-assisted milling N2 - In the field of plastics processing, extruder screws are subjected to significant wear stresses. The extruder screw is the main wear component in those production machines and is usually coated with intermetallic wear protection alloys composed of Ni-based alloys, specifically Colmonoy C56 PTA (NiMoCrSi). There is a growing demand for providing an economic machinability of these alloys to achieve defined contours with a sufficient surface integrity. Recent investigations exhibit promising results applying ultrasonic milling for such hard-to-cut materials. The Colmonoy C56 is modified by various alloying additions Ti, Nb, Mo, Hf, and Al, and then cladded on a steel S355 via Plasma Transferred Arc process. The effect of alloying additions on the microstructure is analyzed regarding their resistance to abrasive and adhesive wear. With Miller test ASTM G75 the influence of alloying elements on resistance to abrasive wear for two abrasive materials is investigated (high-grade corundum F220 and quartz powder). The wear loss is not increased for additions of Nb and Ti compared to the base material C56. Modifications with Hf or Al reduces the resistance to abrasive wear and significantly increases material loss. The extruder screw is also subject to adhesive wear, which can be quantified by means of the pin-roll test. It is demonstrated that the addition of Hf, for example, contributes to a reduction in wear loss. Aim of the investigations is to find suitable modifications for the wear claddings of C56 for a sufficient machineability, without compemising the wear resistant. The machinability is considerably affected by the alloy additions, and is determined using ultrasonic-assisted milling. The addition of hafnium reduces machinability, i.e. significantly increases cutting forces. The incorporation of Nb exhibits a significant reduction of cutting forces, and results in reduced tool wear and an enhanced of surface integrity (roughness, density of defects, residual stresses). KW - Colmonoy C56 KW - PTA welding KW - Adhesive wear KW - Abrasive wear KW - Ultrasonic-assisted milling process KW - Surface integrity KW - Service life and efficiency KW - Substitution of critical raw materials PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651530 DO - https://doi.org/10.1016/j.wear.2025.205830 SN - 0043-1648 VL - 571 SP - 1 EP - 10 PB - Elsevier B.V. AN - OPUS4-65153 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Röhsler, Andreas A1 - Sobol, Oded A1 - Hänninen, H. A1 - Böllinghaus, Thomas T1 - In-situ ToF-SIMS analyses of deuterium re-distribution in austenitic steel AISI 304L under mechanical load N2 - Hydrocarbons fuel our economy. Furthermore, intermediate goods and consumer products are often hydrocarbon-based. Beside all the progress they made possible, hydrogen-containing substances can have severe detrimental effects on materials exposed to them. Hydrogen-assisted failure of iron alloys has been recognised more than a century ago. The present study aims to providing further insight into the degradation of the austenitic stainless steel AISI 304L (EN 1.4307) exposed to hydrogen. To this end, samples were electrochemically charged with the hydrogen isotope deuterium (2H, D) and analysed by scanning electron microscopy (SEM), electron back-scatter diffraction (EBSD) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). It was found that deuterium caused a phase transformation from the original γ austenite into ε- and α’-martensite. Despite their low solubility for hydrogen, viz. deuterium, the newly formed phases showed high deuterium concentration which was attributed to the increased density of traps. Information about the behaviour of deuterium in the material subjected to external mechanical load was gathered. A four-point-bending device was developed for this purpose. This allowed to analyse in-situ pre-charged samples in the ToF-SIMS during the application of external mechanical load. The results indicate a movement of deuterium towards the regions of highest stress. KW - ToF-SIMS KW - Hydrogen KW - Deuterium KW - AISI 304L KW - EBSD PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505142 DO - https://doi.org/10.1038/s41598-020-60370-2 VL - 10 IS - 1 SP - 3611 PB - Nature AN - OPUS4-50514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konert, Florian A1 - Campari, Alessandro A1 - Nietzke, Jonathan A1 - Sobol, Oded A1 - Paltrinieri, Nicola A1 - Alvaro, Antonio T1 - Evaluation of the tensile properties of X65 pipeline steel in compressed gaseous hydrogen using hollow specimens N2 - Hydrogen has great potential on the path towards decarbonization of the energy and transport sectors and can mitigate the urgent issue of global warming. It can be sustainably produced through water electrolysis with potentially zero emissions, and efficiently used (e.g., in fuel cell systems). Despite its environmental advantages, hydrogen-metal interactions could result in the degradation of the mechanical properties of several structural materials. In order to determine the magnitude of the material degradation in relation to hydrogen exposure, extensive material testing is required. The standardized procedure for in-situ testing for the quantification of the impact of compressed gaseous hydrogen (CGH2) relies on the utilization of an autoclave around the tested specimen. Such test set-up is complex, expensive, time-consuming and requires special equipment, trained personnel, and strict safety procedures. A relatively recent method to circumvent these issues and provide affordable results consists of using hollow specimens, thus applying the hydrogen pressure inside rather than outside the specimen. It allows to reduce the volume of hydrogen by several orders of magnitude and to perform the tests more efficiently and in a safer manner. This study focuses on evaluating the tensile properties of X65 vintage pipeline steel tested in a high-pressure hydrogen environment using hollow specimens. Tests are performed in 6 MPa H2 and Ar at the nominal strain rate of 10−6 s−1 to evaluate the reduced area at fracture and the elongation loss. The effect of surface finishing on crack initiation and propagation is investigated by comparing two different manufacturing techniques. In this way, this study provides insights into the applicability of a novel, reliable, and safe testing method which can be used to assess the hydrogen-assisted ductility loss in metallic materials. KW - Mechanical Engineering KW - Hydrogen Embrittlement KW - SSRT KW - Hollow specimen KW - Pipeline steel KW - In-situ tensile test PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595887 DO - https://doi.org/10.1016/j.prostr.2024.01.074 SN - 2452-3216 VL - 54 SP - 1 EP - 8 PB - Elsevier B.V. AN - OPUS4-59588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konert, Florian A1 - Wieder, Frank A1 - Nietzke, Jonathan A1 - Meinel, Dietmar A1 - Böllinghaus, Thomas A1 - Sobol, Oded T1 - Evaluation of the impact of gaseous hydrogen on pipeline steels utilizing hollow specimen technique and μCT N2 - The high potential of hydrogen as a key factor on the pathway towards a climate neutral economy, leads to rising demand in technical applications, where gaseous hydrogen is used. For several metals, hydrogen-metal interactions could cause a degradation of the material properties. This is especially valid for low carbon and highstrength structural steels, as they are commonly used in natural gas pipelines and analyzed in this work. This work provides an insight to the impact of hydrogen on the mechanical properties of an API 5L X65 pipeline steel tested in 60 bar gaseous hydrogen atmosphere. The analyses were performed using the hollow specimen technique with slow strain rate testing (SSRT). The nature of the crack was visualized thereafter utilizing μCT imaging of the sample pressurized with gaseous hydrogen in comparison to one tested in an inert atmosphere. The combination of the results from non-conventional mechanical testing procedures and nondestructive imaging techniques has shown unambiguously how the exposure to hydrogen under realistic service pressure influences the mechanical properties of the material and the appearance of failure. KW - Energy Engineering and Power Technology KW - Condensed Matter Physics KW - Fuel Technology KW - Renewable Energy, Sustainability and the Environment KW - µCT KW - Hollow Specimen Technique KW - Hydrogen Embrittlement PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595077 DO - https://doi.org/10.1016/j.ijhydene.2024.02.005 SN - 0360-3199 VL - 59 SP - 874 EP - 879 PB - Elsevier B.V. AN - OPUS4-59507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leo, Reinhold T1 - Duplex stainless steels - Compatibility for high-pressure hydrogen applications N2 - Duplex Stainless Steels (DSS) are an essential component used in the construction of transportation pipelines because of their many distinctive qualities. The choice of DSS for a particular hydrogen application mainly depends on its susceptibility level to Hydrogen Assisted Cracking (HAC). Several mechanisms have been proposed to describe the occurring microscale processes behind HAC, and these include metastable phase transformation, Hydrogen Enhanced Localized Plasticity (HELP), and Hydrogen Enhanced Decohesion (HEDE). This contribution describes the path to ascertain if DSS is suitable for high-pressure gaseous hydrogen applications. The interplay between several critical factors that result in HAC was examined using high-pressure gaseous hydrogen charging, Electron Backscatter Diffraction (EBSD), tensile testing and hydrogen concentration measurements using Carrier Gas Hot Extraction (CGHE). T2 - Third German-African Green Hydrogen Forum 2025 CY - Bernburg (Saale), Germany DA - 23.09.2025 KW - Hydrogen Assisted Cracking KW - High Pressure Hydrogen KW - Duplex Stainless Steels KW - Hollow Specimen Technique PY - 2025 AN - OPUS4-64302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Holzwarth, Marcel A1 - Mayer, Uwe ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Versuchswerkstoff und erste Ergebnisse an SE(B)140-Großproben N2 - In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt. Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und -60 °C präsentiert. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2024 DO - https://doi.org/10.48447/BR-2024-BB SP - 49 EP - 58 PB - DVM-Verlag CY - Berlin AN - OPUS4-59518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Kritische Belastungsrate und erste Ergebnisse an C(T)-Proben N2 - Im laufenden Verbundprojekt MCGUSS untersuchen dieProjektpartner MPA Stuttgart und BAM Berlin das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI). Ziel des Projektes ist die Entwicklung einer Methode zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag werden die Eigenschaften des verwendeten Werkstoffs der Festigkeitsklasse GJS-400 vorgestellt und die sich daraus ergebenden Probenentnahmestellen näher erläutert. Weiterhin werden erste Ergebnisse der C(T)25-Versuchsserien vorgestellt, die bei Belastungsraten von ca. 5∙103 MPa√ms-1, 5∙104 MPa√ms-1 und 5∙105 MPa√ms-1 und einer Temperatur von -40 °C durchgeführt wurden. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Belastung KW - Master Curve KW - Gusseisen KW - C(T)-Proben PY - 2024 SP - 37 EP - 47 PB - DVM Verlag CY - Berlin AN - OPUS4-59519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Untersuchung des Master Curve-Konzepts für Ferritisches Gusseisen mit Kugelgraphit: Versuchswerkstoff und erste Ergebnisse von SE(B)140-Grossproben N2 - In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestim-mung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbe-reich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt. Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und 60 °C präsentiert. T2 - Jahrestagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Bruchzähigkeit KW - Sprödbruch KW - Master Curve KW - Gusseisen mit Kugelgraphit KW - ASTM E1921 PY - 2024 AN - OPUS4-59860 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mayer, Uwe T1 - Untersuchung des Master Curve-Konzeptes für ferritisches Gusseisen mit Kugelgraphit N2 - In dem Poster werden der Forschungsansatz, die Ziele, das Untersuchungsprogramm und die erwarteten Ergebnisse des BMUV-Forschungsvorhabens MCGUSS "Untersuchung des Master Curve-Konzeptes für ferritisches Gusseisen mit Kugelgraphit" vorgestellt. Mit Blick auf bruchmechanische Sicherheitsbewertungen in der Kerntechnik werden Stähle momentan mit dem deterministischen ASME-Referenzkurvenkonzept, ergänzt durch das probabilistische Master Curve-Konzept nach ASTM E1921, bewertet. Das Master Curve-Konzept wird bereits für die Bewertung von ferritischen Schmiedestahlbehältern verwendet. Bewertungsmethoden für ferritisches Gusseisen mit Kugelgraphit sind im Moment unvollständig. Normen wie die nationale BDG-Richtlinie P300 oder der internationale ASME-Code, Sect. III, Div. 3, WC-2330 decken Sprödbruch nicht ausreichend ab. Die Verwendung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit würde eine bruchmechanische Bewertung via einer KJc,d Verteilung erlauben und gleichzeitig Größeneffekte und einen Temperaturbereich von 100 K berücksichtigen. T2 - GRS-Projektstatusgespräch 2023 CY - Karlsruhe, Germany DA - 06.11.2023 KW - Dynamische Bruchzähigkeit KW - Sprödbruch KW - Gusseisen mit Kugelgraphit KW - Master Curve PY - 2023 AN - OPUS4-59060 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mayer, Uwe T1 - Untersuchung des Master Curve-Konzeptes für ferritisches Gusseisen mit Kugelgraphit N2 - In dem Vortrag werden der Forschungsansatz, die Ziele, das Untersuchungsprogramm und die erwarteten Ergebnisse des BMUVForschungsvorhabens MCGUSS "Untersuchung des Master Curve-Konzeptes für ferritisches Gusseisen mit Kugelgraphit" vorgestellt. Mit Blick auf bruchmechanische Sicherheitsbewertungen in der Kerntechnik werden Stähle momentan mit dem deterministischen ASME Referenzkurvenkonzept, ergänzt durch das probabilistische Master Curve-Konzept nach ASTM E1921, bewertet. Das Master Curve-Konzept wird bereits für die Bewertung von ferritischen Schmiedestahlbehältern verwendet. Bewertungsmethoden für ferritisches Gusseisen mit Kugelgraphit sind im Moment unvollständig. Normen wie die nationale BDG-Richtlinie P300 oder der internationale ASME-Code, Sect. III, Div. 3, WC-2330 decken Sprödbruch nicht ausreichend ab. Die Verwendung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit würde eine bruchmechanische Bewertung via einer KJc,d Verteilung erlauben und gleichzeitig Größeneffekte und einen Temperaturbereich von 100 K berücksichtigen. T2 - GRS-Projektstatusgespräch 2023 CY - Karlsruhe, Germany DA - 06.11.2023 KW - Dynamische Bruchzähigkeit KW - Master Curve KW - Gusseisen mit Kugelgraphit KW - Sprödbruch PY - 2023 AN - OPUS4-59061 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, M. T1 - First results for the modification of the master curve concept for ferritic ductile cast iron N2 - Within the scope of fracture mechanics safety, ferritic ductile cast iron (DCI) does currently not have an established and validated method to determine and assess dynamic fracture toughness values in the ductile-to-brittle transition regime. For this reason, the applicability of the fracture mechanics Master Curve concept according to ASTM E1921 to DCI is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. To investigate the applicability of the Master Curve concept for DCI, a DCI material of grade GJS-400 has been procured via a detailed manufacturing specification. From this material test specimens of various geometries and sizes (Tensile, Charpy-V, Pellini, SE(B)10, SE(B)25, SE(B)140, DC(T)9, C(T)25 and C(T)50) were produced. In total, about 500 test specimens will be tested to investigate and validate the Master Curve Concept as well as other assumptions (e.g. size effects, Weakest-Link, Weibull distribution) for DCI. While the whole project has not yet concluded, several work packages have yet been completed. Selected test results using C(T)25 specimens are presented. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve PY - 2024 AN - OPUS4-61451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Ohm, Katrin A1 - Holzwarth, Marcel A1 - Mayer, Uwe T1 - Master Curve-Auswertungen und fraktographische Analysen zum Bruchmechanismus – neue Ergebnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung (Projekt MCGUSS) N2 - In diesem Beitrag werden erste Master Curve (MC)-Auswertungen und fraktographische Analysen zum Bruchmechanismus aus dem laufenden Kooperationsprojekt MCGUSS zwischen der BAM Berlin und der MPA Stuttgart diskutiert. Für zwei SE(B)140-Großprobenversuchsserien mit je 6-8 Versuchen bei -40 °C bzw. -60 °C und Belastungsraten von 5-8x10^4 MPa√m/s wurden Referenztemperaturen T0 bestimmt. Ergänzt wird dies für erste Versuchsreihen an SE(B)25-Kleinproben, die bei -60 °C und Belastungsraten von ca. 2x10^5 MPa√m/s geprüft wurden. An ausgewählten Bruchflächen dieser Versuche wurden detaillierte fraktographische REM-Analysen vorgenommen. Im Vordergrund stand die Charakterisierung des Bruchmechanismus in Abhängigkeit von den Einflussfaktoren Temperatur und Probengröße. In Richtung der Zähigkeitstieflage werden die Analysen komplettiert durch die Ergebnisse von zwei SE(B)140-Großprobenversuchen bei -100 °C bzw. -140 °C und Belastungsraten von ca. 5-8x10^4 MPa√m/s. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2025 DO - https://doi.org/10.48447/BR-2025-467 SP - 113 EP - 122 PB - DVM-Verlag CY - Berlin AN - OPUS4-62554 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stephan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary. T2 - 21st International Symposium ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Washington, D.C., USA DA - 08.11.2023 KW - Dynamic Fracture Toughness KW - Cleavage fracture KW - Master Curve Concept KW - Ductile Cast Iron PY - 2023 AN - OPUS4-59063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ferritic ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the research project is on brittle fracture. The goal is the establishment of a methodology to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. The experimental program uses a DCI material of grade GJS-400, which is generally used for transport and storage containers of radioactive materials. Firstly, a basic mechanical-technological material characterization will be performed consisting of tensile, Charpy and Pellini tests. Following the material characterization, the loading rate relevant for brittle fracture will be determined using instrumented C(T)25-fracture tests at a temperature of -40°C. To be able to transfer the relevant loading rate to other specimen geometries or sizes, the time-dependent course of the Weibull stress is assessed via numerical analyses. With this information an extensive experimental program consisting of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25 and SE(B)140 specimens is performed. These experimental results will be further supported by numerical and fractographic analyses. The empirical experimental database developed for DCI materials will be used to assess the applicability of the MC concept for DCI materials under dynamic loading. At the current time manufacturing and precracking of test specimens is ongoing. The authors provide first results concerning the mechanical-technological material characterization, the relevant loading rate for brittle fracture determined via C(T)25 tests, and some early results of other specimen types. These experimental results are also supported by preliminary numerical and statistical analyses. T2 - Conference SMiRT27 CY - Yokohama, Japan DA - 04.03.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - ASTM E1921 KW - Master curve KW - Brittle fracture PY - 2024 AN - OPUS4-59859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram A1 - Weihe, Stefan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to Hojo et al. (2008) the MC concept is already in use for the brittle fracture safety assessment of ferritic forged steel containers, which would suggest an extension to ductile cast iron containers. In compliance with IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general exclusion of crack initiation. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using only a low number of small fracture mechanics test specimens extracted from a component. For the experimental program, a DCI material of grade GJS-400 (GGG-40) has been produced as it is generally used for transport and storage containers for nuclear material. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests has been planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens at various loading rates and temperatures. The specimen testing is divided between the project partners based on specimen geometry. MPA Stuttgart has been tasked with the testing of the C(T), DC(T) and Pellini specimens, while BAM Berlin was assigned the SE(B), Charpy and tensile tests. These tests allow for the determination of the loading rate relevant for brittle fracture via C(T)25 specimens and an assessment of size effects by transferring the relevant loading rate to other specimen geometries and sizes. Numerical analyses of different specimen geometries and test setups are planned to investigate the influence of stress triaxiality and loading rate. Furthermore, the time-dependent course of the Weibull stress is assessed via these numerical analyses. Throughout the experimental program, the microstructure-property relationship will also be investigated based on quantitative metallographic and fractographic analyses like scanning electron microscope images and metallographic sections. With the acquired experimental database fundamental assumptions of the MC concept, like the weakest link model and the Weibull distribution, will be assessed for the application to DCI. In the end, the applicability of the MC concept will be evaluated and if necessary, modifications to the MC concept for DCI will be proposed. This paper will present the preliminary results of the GJS400 material characterization and the related selection of test specimen extraction points. First results of the C(T)25 and SE(B)140 specimen testing will also be discussed supported by first metallographic analyses. T2 - SMiRT27 Conference CY - Yokohama, Japan DA - 03.03.2024 KW - Ductile Cast iron KW - Dynamic Fracture Toughness KW - Safety Assessment KW - Master Curve Concept PY - 2024 SP - 1 EP - 10 AN - OPUS4-59302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan T1 - On the Applicability of the Master Curve Concept for Ductile Cast Iron based on experimental and microstructural results N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project (MCGUSS) between BAM Berlin and MPA Stuttgart. The experimental program included a basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests. To determine the relevant loading rate for brittle fracture, instrumented C(T)25 fracture tests were performed at different loading rates at a temperature of -40°C. The relevant loading rates are 5x10^3 MPa√ms-1 and 5x10^4 MPa√ms-1. A series of dynamic fracture tests consisting of DC(T)9, C(T)25 and C(T)50 specimens were performed at MPA. BAM performed corresponding test series with SE(B)10 (pre-cracked Charpy), SE(B)25 and SE(B)140 specimens to cover the influence of specimen geometry. In total about 400 tests were performed during this project. The experimental program is complemented by extensive fractographic and metallographic studies using scanning electron microscopy and cross sectioning, as well as characterizations of the chemical composition of the material and of the morphology and distribution of the graphite particles. KJcd values were evaluated for all C(T)25 specimens and some C(T)50 and DC(T)9 specimens. First Master Curve analyses suggest that modifications on the Master Curve setup will be neccessary for instance changing the coefficient from 0.019 to 0.045. This modification requires further validation and is only one of many possible modifications. The SE(B) specimen results clearly show an inverse size effect. This does not correlate with the weakest link effect attributed to steels which dictates lower fracture toughness values for larger specimens. Due to the presence of graphite particles in the DCI material, it is currently assumed that these particles play a significant role in the failure behavior of DCI materials and the following fracture mechanism is proposed: “Specimen size-dependent arrest of local brittle fracures before global brittle failure by weakest link”. T2 - 9th SEDS Workshop: Safety of Extended Dry Storage, 20.-22. Mai 2025 CY - Garching, Germany DA - 20.05.2025 KW - Statistics KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve KW - Safety assessment PY - 2025 SP - 1 EP - 3 AN - OPUS4-63566 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Comprehensive Standardisation of the Hollow Specimen Technique for Tests in High-Pressure Hydrogen Gas N2 - The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations and complement the current techniques for qualifying metallic materials under highpressure hydrogen gas. In this technique, an axial hole is manufactured in a tensile specimen, which is then filled with hydrogen gas, sealed, and placed in a standard testing machine. This method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and does not require complex equipment or a specialised laboratory, unlike the conventional autoclave technique. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of the committee ISO/TC 164/SC 1/WG 9 to standardise the method, however, there are still open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions are being addressed in the H2HohlZug project, which is presented in this contribution. T2 - Oxford - EPRI Hydrogen Embrittlement Workshop CY - Oxford, United Kingdom DA - 23.06.2024 KW - Hollow Specimen Technique KW - High-pressure Gaseous Hydrogen KW - Hydrogen Embrittlement KW - Tensile Testing PY - 2024 AN - OPUS4-60501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - Evolution of tensile testing methodologies for hydrogen embrittlement in austenitic steels: a comparative study N2 - The energy transition towards hydrogen utilisation has increased the demand for reliable testing methods to evaluate the susceptibility of metallic materials to hydrogen degradation. However, traditional electrochemical pre-charging techniques have limitations in represent-ing realistic gaseous hydrogen exposure conditions. This study presents three comparative analyses of tensile testing methodologies, focusing on the differences between electrochem-ical pre-charging, gaseous pre-charging, and in-situ testing using hollow specimens for aus-tenitic steels AISI 304L and 316L type austenitic steels. Based on the results obtained, the first comparison reveals that electrochemically pre-charged and gaseously pre-charged specimens exhibit different behaviours regarding the impact on the mechanical properties. This effect can be retraced to the varying distribution of hydrogen throughout the specimens. Although comparable embrittlement was observed for similar hydrogen concentrations, the relationship appears to be non-systematic. The second comparison evaluates the performance of pre-charged hollow specimens (300°C, 100 bar, 21 days) in comparison to hollow specimens tested in-situ under 200 bar hydrogen during slow strain rate tensile tests (SSRT). While pre-charged specimens show a slight de-crease in elongation at fracture and a noticeable decrease in reduction of area (RA), in-situ tested specimens exhibit significantly more pronounced embrittlement. This is in accord-ance with the results of Michler et. al. In the third comparison, geometry effects between pre-charged conventional and pre-charged hollow specimens are explored. In this case, the hydrogen effect appears to be of the same order of magnitude for both specimen types, although some differences are ob-served. The study's findings underscore the importance of considering differences between test methods when assessing materials’ compatibility with hydrogen. It specifically emphasises the need for in-situ testing with gaseous hydrogen to better represent real conditions in ap-plications within the hydrogen sector. Furthermore, the study provides an initial compari-son between conventional and hollow specimens, demonstrating their capability to reveal hydrogen effects. However, additional research is essential to enhance the comparability of results yielded by these testing methods. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Hollow Specimen Technique KW - Hydrogen KW - Austenitic Stainless Steel KW - Hydrogen Testing KW - AISI 316L PY - 2024 AN - OPUS4-60929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - The relationship between surface condition and the influence of hydrogen on the mechanical properties of additively manufactured 316L N2 - The following contribution presents the analyses of additively manufactured (AM) 316L using hollow specimens at 200 bar hydrogen and a strain rate of 1E-5 s-1. The work includes a comparison of three types of hollow specimens: mechanically extracted from fully additively manufactured cylinders, near-net-shape additively manufactured specimens, i.e. as printed, and specimens made of conventional 316L. AM specimens were manufactured via powder bed fusion with laser beam of metals (PBF-LB/M). For the near-net-shape specimens the inner hole remained without any mechanical processing. The inner holes of the cylindric specimens were manufactured by drilling with subsequent honing. The susceptibility to hydrogen embrittlement was found to be strongly dependent on the surface being in contact with hydrogen. While specimens with a clean surface had a relative reduction of area (RRA) of around 78 %, those with an as-printed surface showed a significantly larger RRA of around 90 %. One possible reason for this are oxide layers formed due to small amounts of oxygen during the AM-process. Further research is required to determine if the lower effect on the mechanical properties is permanently for as printed parts or e.g. time dependent. Additionally, further work with variation in the nominal strain rate is required. T2 - IIW 77th Annual Assembly 2024 CY - Rhodes, Greece DA - 07.07.2024 KW - Austenitic steel 316L KW - Additive manufacturing KW - PBF-LB/M KW - Hydrogen degradation KW - Hydrogen embrittlement KW - Hollow specimen technique PY - 2024 AN - OPUS4-60618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - Stainless Steels and Hydrogen Applications N2 - The contribution was presented at the Stainless Steel World Conference 2022. The presentation shows the influence of hydrogen on the mechanical properties of steel. Some test methods are shown and selected results are presented. T2 - Stainless Steel World Conference 2022 CY - Maastricht, Netherlands DA - 27.09.2022 KW - Gaseous hydrogen KW - Hydrogen Embrittlement KW - Hydrogen assisted cracking KW - SSRT PY - 2022 AN - OPUS4-55913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Technique for Tests in High-Pressure Hydrogen Gas: The Path Towards Standardisation and the Case Study of a Pipeline Steel and its Weld N2 - The hollow specimen technique is a simple method that has the potential to make material qualification with gaseous pressurized hydrogen widely applicable for the hydrogen industry at low cost. The feasibility of this method has been demonstrated in several studies, leading to the establishment of an ISO committee for its standardization. Questions have emerged during this process, that currently prevent the method from being standardized for hydrogen testing. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. The aim is to close the identified gaps towards the standardization of this method for hydrogen testing. This contribution presents the structure and milestones of the project, followed by the results regarding the influence of specimen production and its response to hydrogen effects. Depending on the production method, different roughness and residual stresses can be expected on the inner hole surface of the specimens. This is of importance since an increase in stress concentration sites have been found to be associated to a higher severity of hydrogen effects. This influence has been investigated after applying the following machining processes: a) drilled only; b) drilled and reamed; c) drilled and honed; d) electro-discharge machining (EDM) and honed; e) EDM and reamed. Roughness measurements using a profilometer, electron back-scatter diffraction (EBSD) analysis and microhardness tests have been performed previous to mechanical testing to infer on the effect of the different production methods on the surface of the inner hole. Next, the specimens were mechanically tested via slow strain rate tensile tests in a argon and in hydrogen, both at 150 bar and room temperature. Here, a strain-rate sensibility analysis was also performed to identify an optimal strain-rate for the mechanical tests. Based on the results an optimal production method is identified and proposed. T2 - ASTM Conference on Hydrogen Materials CY - La Rochelle, France DA - 03.06.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - Austenitic Stainless Steel KW - H2HohlZug KW - TransHyDE KW - Tensile Test KW - Pipeline Steel PY - 2025 AN - OPUS4-63329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobol, Oded T1 - Challenges with metallic materials in hydrogen technologies N2 - The contribution was presented in the Joint European Summer School in Athens as part of several contributions from BAM in the field of hydrogen safety. These presentations are given in order to provide an overview about the activities of BAM as part of the competence center H2Safety@BAM T2 - JOINT EUROPEAN SUMMER SCHOOL (JESS) CY - Athens, Greece DA - 12.09.2022 KW - Gaseous hydrogen KW - Hydrogen Embrittlement KW - Hydrogen assisted cracking PY - 2022 AN - OPUS4-55822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Harmonising Tribotests of Polymers in Hydrogen N2 - This talk harmonised methods to investigate friction and wear of commercial and experimental polymer compounds in hydrogen using several tribometers. T2 - Surface Ventures - Symposium on Hydrogen Tribology CY - Online meeting DA - 31.07.2025 KW - Hydrogen KW - Polymers KW - Tribometer KW - Wear KW - Coefficient of Friction KW - Interlaboratory comparison KW - Comparability KW - Harmonisation KW - Standardisation KW - Tribology KW - Oil-coupled compounds KW - FAIR data KW - Database KW - i-TRIBOMAT PY - 2025 AN - OPUS4-63838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effect of temperature on the friction behaviour of rubber materials in hydrogen N2 - Safety and reliability are the major challenges to face for the development and acceptance of hydrogen technology. It is therefore crucial to study deeply material compatibility, in particular for tribological components that are directly in contact with hydrogen. Some of the most critical parts are sealing components that face high risk of damage due variation of pressure, temperature and mechanical stress. In this study, the friction and wear behaviour of several rubber materials was evaluated in hydrogen environment at ambient and low temperature. Tests were performed against 316L disks in a reciprocation motion. Results reveal that the hydrogen affects the friction and wear behaviour of most materials. The friction mechanism is dominated by deformation for most rubber materials at ambient temperature while sliding occurs at low temperature due to the increased hardness of the rubbers. T2 - Polytrib 2024 CY - Portorož, Slovenia DA - 03.10.2024 KW - Reciprocating sliding KW - Rubber materials KW - Hydrogen KW - Low temperature PY - 2024 AN - OPUS4-62019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effect of high-pressure hydrogen environment on the physical and mechanical properties of elastomers N2 - This presentation deals with the exposure of HNBR rubbers to high pressure hydrogen (100 MPa) at 120 °C for 7 and 21 days under static conditions followed by characterization of their physical and mechanical properties.The core areas include swelling, rapid gas decompression, dynamic mechanical analysis (DMA), tensile strength and compression set properties. This study will assist in expanding the knowledge base of elastomer compatibility with hydrogen and therefore contribute significantly to the selection and development of polymer materials deploying hydrogen as a future energy carrier. T2 - EHEC European Hydrogen Energy Conferecne 2022 CY - Madrid, Spain DA - 18.05.2022 KW - Rubbers KW - Hydrogen KW - Characterization PY - 2022 AN - OPUS4-62084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Harmonised tribological testing of polymers in hydrogen N2 - The focus of this work is to study the tribological performance of polymers in hydrogen atmosphere. Additionally, tests were carried out with up to three different tribometers at two institutions. The challenge to compare and harmonise equipment, procedures, and methods is an important part of the study. T2 - PolyTrib 2024 CY - Portoroz, Slovenia DA - 03.10.2024 KW - Hydrogen KW - Tribometer KW - Comparability KW - Harmonisation KW - Oil-coupled compounds PY - 2024 AN - OPUS4-61224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Tribological performance of polymer compounds in gaseous hydrogen N2 - In this study, friction and wear of conventional and alternative high performance polymer compounds, typically used for components of compressors, were investigated in gaseous hydrogen and nitrogen up to 80 bar of gas pressure. The compounds used were a commercial PEEK matrix with 10 wt.% each of PTFE, graphite, and short carbon fibres, a PPS matrix with 10 wt.% each of PTFE and graphite, and an experimental PA12 matrix with PTFE chemically coupled with an oleyl alcohol. Due to the cylindrical shape of the polymer samples, the contact area and pressure change if wear occurs. Therefore, experimental results of pre-screening tests have been used as input for FEM and an analytical model to determine the decreasing contact pressure over time. Afterwards, the outcome of the models was used to determine the duration of the experiments to reach typical contact pressures of seals in hydrogen compressors. T2 - ASMET TriboCorrosion International Conference 2025 CY - Vienna, Austria DA - 23.10.2025 KW - Hydrogen KW - Polymer KW - Tribometer KW - Comparability KW - Harmonisation KW - Oil-coupled compounds KW - Coefficient of Friction KW - Wear KW - FAIR data KW - Standardisation KW - Tribology KW - Database KW - i-TRIBOMAT PY - 2025 AN - OPUS4-64473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Comparison of the sliding behavior of several polymers in gaseous and liquid hydrogen N2 - The development of hydrogen technologies entails high safety requirements in distribution and dispensing infrastructure. Therefore, it is necessary to pursue research on material compatibility in hydrogen, especially for critical parts with tribological issues. The focus of this study is to evaluate the influence of hydrogen on a wider range of commercially available polymer materials. Thereby, the friction and wear behavior of different grades of TPE, POM, PA66, PA12, PPA, PEEK, PPS, PTFE, PAI, PI and PBI were investigated against a rotating steel disk (AISI 304). Filled and unfilled polymers from different suppliers were evaluated at room temperature in air, vacuum and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2). The sliding behavior of the polymer materials is discussed by means of surface analyses, whereby special attention is paid to the formation of a transfer film. According to the results at ambient temperature, the effect of hydrogen environment on the tribological behavior of neat polymers may be related to lack of moisture, but also to saturated hydrocarbons in gaseous hydrogen. In liquid hydrogen, the best tribological performances were achieved with neat PA polymers as well as PPS and PI composites. KW - Polymers KW - Composites KW - Sliding wear KW - Hydrogen KW - Cryogenic temperature PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597123 DO - https://doi.org/10.2474/trol.18.217 SN - 1881-2198 VL - 18 IS - 5 SP - 217 EP - 231 PB - Japanese Society of Tribologists AN - OPUS4-59712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Comparison of the sliding behaviour of several polymers in hydrogen N2 - The work presented here deals with the friction and wear behaviour of polymer materials in hydrogen. Commercially available grades of PEEK, PA, PPA, PAI, PI and PBI were investigated at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -253°C (LH2). T2 - 7th World Tribology Congress, WTC 2022 CY - Lyon, France DA - 10.07.2022 KW - Friction KW - Wear KW - Polymers KW - Hydrogen KW - Cryogenic PY - 2021 SP - 1 AN - OPUS4-62089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Polymer materials in hydrogen N2 - This presentation provides an overview of the applications and challenges related to polymer materials in hydrogen. The effects of hydrogen on polymers are described and test methods to evaluate the interactions between polymers and hydrogen are presented along with case studies. T2 - Masterstudiengang Wasserstofftechnologien DIU CY - Online meeting DA - 25.08.2023 KW - Hydrogen KW - Polymers PY - 2023 AN - OPUS4-61964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cano Murillo, Natalia T1 - Effect of high-pressure hydrogen environment on the physical and mechanical properties of different kinds of carbon black filled elastomers. N2 - As the transition towards the usage of renewable energy is getting urgent, the fluctuations of clean energy production require efficient storage alternatives. Hydrogen offers not only the possibility of energy storage but also, acts as an energy carrier. It is then important to study the effect of highly pressurized hydrogen atmosphere on the materials destinated for its storage and transport, in order to assure the reliable performance of the sealing materials containing hydrogen. In this study, a set of carbon black (CB) filled rubbers comprising hydrogenated acrylonitrile butadiene rubber (HNBR), acrylonitrile butadiene rubber (NBR) and ethylene propylene diene monomer rubber (EPDM) was tested under high pressure hydrogen atmosphere (1000 bar) and at different temperature conditions: 120°C for HNBR, room temperature and 85°C for NBR and EPDM. The influence of hydrogen on the materials properties was measured after 7 days of exposure under hydrogen and evaluated again after 48h. Density and volume change, as well as hardness, tensile tests, compression set, dynamic mechanical measurements and infrared spectroscopy evaluations were conducted to estimate the impact of high-pressure hydrogen on the rubber grades. Our study reveals, an effect on the physical and mechanical properties, possibly related to small changes in the matrix-filler interaction after the hydrogen exposure. All materials, however, show a trend to recover most of their properties 48h after hydrogen exposure. T2 - RubberCon 2023 CY - Edinburgh, Scotland DA - 09.05.2023 KW - Elastomers KW - Hydrogen exposure KW - Mechanical properties PY - 2023 AN - OPUS4-62007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Comparison of the sliding behaviour of several polymers in hydrogen N2 - The work presented here deals with the friction and wear behaviour of polymer materials in hydrogen. Commercially available grades of PEEK, PA, PPA, PAI, PI and PBI were investigated at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2). T2 - 7th World Tribology Congress, WTC 2022 CY - Lyon, France DA - 10.07.2022 KW - Friction KW - Wear KW - Polymers KW - Hydrogen KW - Cryogenic PY - 2022 AN - OPUS4-62087 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Denora, Isabella A1 - Clute, Clara A1 - Murillo, Natalia Cano A1 - Theiler, Geraldine A1 - Balasooriya, Winoj A1 - Kaiser, Andreas A1 - Fasching, Michael A1 - Schwarz, Thomas A1 - Marano, Claudia T1 - A study on the mechanical behaviour of carbon black and Struktosil-filled NBR compounds for hydrogen applications N2 - This study investigates the effect of the addition of a 2D filler (Struktosil) to a carbon black-filled acrylonitrile butadiene rubber, developed for seals in hydrogen applications. Several characterization methods have been adopted. The addition of Struktosil increases the stiffness of the material up to a strain of about 100%, to a lesser extent in presence of a plasticizer. The dissipative response of the material is increased by Struktosil addition and decreased in presence of the plasticizer. Concerning fracture behaviour, the crack initiation and Rapid Gas Decompression (RGD) resistance were not affected by the addition of Struktosil but decreased in presence of plasticizer. Furthermore, the addition of Struktosil had a positive effect on crack propagation resistance. The effects of pressurized hydrogen exposure on physical-mechanical properties were also evaluated and correlated with the results. A correlation between fracture toughness and RGD resistance has been also attempted. KW - Acrylonitrile Butadiene rubber KW - Fracture mechanics KW - 2D filler KW - High-pressure hydrogen KW - Rapid gas decompression PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-648285 DO - https://doi.org/10.1016/j.ijhydene.2025.03.122 SN - 0360-3199 VL - 118 SP - 407 EP - 416 PB - Elsevier Ltd. AN - OPUS4-64828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Sawae, Y. A1 - Shinmori, H. A1 - Hashimoto, H. A1 - Aoyagi, A. A1 - Dobbelaar, E. T1 - Towards sustainable and hydrogen compatible sealing materials N2 - Materialien auf PTFE-Basis werden in der Regel als Kolbenringe in Hochdruck- und/oder kryogenem Wasserstoff verwendet. In diesem Projekt werden neu formulierte und nachhaltigere Polymerwerkstoffe mit herkömmlichen Materialien verglichen. Auf Grundlage der tribologischen Ergebnisse werden vielversprechende Kandidaten zusammen mit Reibungsmechanismen sowohl bei Hochdruck- als auch bei Niedrigtemperatur-Wasserstoff vorgeschlagen. T2 - 66. GfT Tribologie-Fachtagung 2025 CY - Wernigerode, Germany DA - 29.09.2025 KW - Wasserstoff KW - Reibung KW - Verschleiß KW - Kolbenring KW - Dynamische Dichtung PY - 2025 VL - 09 SP - 1 EP - 4 AN - OPUS4-64314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - An overview of tribology in gaseous Hydrogen N2 - In this presentation, an overview in gaseous hydrogen is given along with examples related to metal, coatings, polymers and rubbers materials. T2 - International Seminar, Hydrogen & Materials 2024 CY - Espoo, Finland DA - 06.06.2024 KW - Hydrogen KW - Friction KW - Wear KW - Materials PY - 2024 AN - OPUS4-61408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Halder, Karabi A1 - Balasooriya, Winoj T1 - Effect of high-pressure hydrogen environment on the physical and mechanical properties of elastomers N2 - This paper deals with the exposure of HBNR rubbers to high pressure hydrogen (100 MPa) at 120 °C for 7 and 21 days under static conditions followed by characterization of their physical and mechanical properties. T2 - EHEC European Hydrogen Energy Conference 2022 CY - Madrid, Spain DA - 18.05.2022 KW - Rubbers KW - Hydrogen KW - Characterization PY - 2022 SP - 1 EP - 2 AN - OPUS4-62085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effect of hydrogen pressure on the fretting behavior of elastomers N2 - In this study, the fretting behavior of several elastomer materials against 316L were evaluated in air and hydrogen environment up to 10 MPa. Furthermore, aging experiments were conducted for 7 days under static conditions in 100 MPa hydrogen and the physical and mechanical properties of the rubber materials were examined before and after hydrogen exposure. Fretting tests revealed that the wear of these compounds is significantly affected by the hydrogen environment compared to air, especially with NBR grades. After aging experiment, the friction response of HNBR grades is characterized by increased adhesion due to elastic deformation, leading to partial slip. T2 - 4th Int. Conf. on Polymer Tribology, PolyTrib 2022 CY - Stockholm, Sweden DA - 05.12.2022 KW - Hydrogen KW - Fretting KW - Elastomers PY - 2022 AN - OPUS4-62006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Toward sustainable and hydrogen compatible sealing materials N2 - As sealing components, polymeric materials are used in a wide range of applications e.g. as O-rings and piston rings in high-pressure and/or cryogenic hydrogen. For these extreme demanding application, PTFE or PPS based materials are often used as high-performance polymer matrix. This project aims to provide a safe and sustainable sealing solutions for hydrogen applications. New materials with improved sustainability were investigated and compared with conventional grades. Tests were performed in hydrogen over a wide range of temperature and pressure (0.1 MPa to 40 MPa, and 100°C down to -150°C) at Kyushu University and BAM using a pin-on-disk apparatus in a continuous sliding motion. Polymer samples ran against 316L disk at 0.5 m/s and 3 MPa contact pressure. Based on the tribological results and surface analyses, promising candidates are suggested along with friction mechanisms in both high-pressure and low temperature hydrogen. T2 - STLE Meeting CY - Atlanta, Georgia, USA DA - 18.05.2025 KW - Hydrogen KW - Friction KW - Wear KW - Piston ring KW - Reciprocating seals PY - 2025 AN - OPUS4-63809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Comparative evaluation of the sliding performance of polymers materials in gaseous and liquid hydrogen N2 - The focus of this study is to evaluate the influence of hydrogen on the friction and wear behavior of a wide range of commercially available polymer materials. Thereby, Filled and unfilled polymers from different suppliers were evaluated at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2). T2 - 2023 Hydrogenius & I2CNER Tribology Symposium CY - Fukuoka, Japan DA - 03.02.2023 KW - Hydrogen KW - Tribology KW - Cryogenic KW - LH2 KW - Polymers PY - 2023 AN - OPUS4-61961 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - On the assessment of dynamic fracture toughness of ferritic ductile cast iron using the master curve concept N2 - An established and validated method to determine and assess dynamic fracture toughness values of ferritic ductile cast iron (DCI) in the ductile-to-brittle transition regime is currently not available. Although the ASME-Code, Sect. III, Div. 3, WC-2330 explicitly requires safety assessment considerations for dynamic loading, sufficiently substantial information on the procedure is not given. Therefore, the applicability of the probabilistic Master Curve (MC) concept according to ASTM E1921 to DCI is being investigated in the joint German research project MCGUSS conducted by BAM Berlin and MPA Stuttgart. Using a tailored manufacturing specification, a DCI material of grade GJS-400 has been casted to provide a test material which is very homogeneous but typical for heavy-sections. The experimental test program covers test specimens of various geometries and sizes (Tensile, Charpy-V, Pellini, SE(B)10, SE(B)25, SE(B)140, DC(T)9, C(T)25 and C(T)50). In total about 500 specimens will be tested to investigate and validate the Master Curve concept and its background for DCI (e.g. size effects, weakest-link, Weibull distribution, microstructure-property correlation). While the whole project has not yet concluded, several work packages have already been completed. This presentation is focused on dynamic large-scale fracture mechanics test series using SE(B)140 specimens and instrumented Charpy impact testing using ISO-V specimens. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve concept PY - 2024 AN - OPUS4-61452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Recent Results on the Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within the current framework for safety assessment of ferritic ductile cast iron (DCI) containers for transport as well as interim and final storage of radioactive materials, the IAEA guidelines SSG 26 apply fracture mechanics principles. Crack initiation in either, stable or unstable modes is generally forbidden. Additionally, for DCI, the ASME-Code, Sect. III, Div. 3, WC-2330, explicitly requires a safety proof regarding dynamic loading conditions. Nevertheless, corresponding information given in the ASME Code does not seem to be sufficient to appropriately perform a dynamic fracture mechanics safety assessment for DCI. To address and improve this status of the dynamic brittle fracture safety assessment framework for DCI, the application of the fracture mechanics master curve (MC) concept to DCI is being investigated in an ongoing joint research project (acronym MCGUSS) between BAM Berlin and MPA Stuttgart. For ferritic DCI, the MCGUSS project addresses the currently lacking systematic review of applicability and potential modifications to the assumptions and the procedure according to ASTM E1921. The aim is to establish a methodology to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime using small samples extracted from a component. The research approach and the planned investigations were outlined in more detail earlier. This paper is focused on the discussion of recent experimental results to establish the dynamic fracture mechanics toughness data base and its MC analyses. MCGUSS fracture mechanics test setups and the dynamic fracture toughness data base achieved at the time of abstract submission is discussed (covering 128 specimens). Current application limits of ASTM E1921 MC to DCI are discussed, and planned investigations to further investigate and modify the MC procedure for DCI are outlined. T2 - ASTM 23rd International ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Atlanta, GA, USA DA - 12.11.2025 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Safety assessment KW - Master curve KW - Statistics PY - 2025 AN - OPUS4-64746 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - The current framework for safety assessment of ferritic ductile cast iron (DCI) containers for transport and storage of radioactive materials applies fracture mechanics principles. As established by the IAEA safety standard SSG 26, prevention of crack initiation is the governing criterion and no reliance in design should be placed on any predicted ductile tearing resistance. Similarly, the ASME-Code, Sect. III, Div. 3 explicitly deals with DCI and requires a safety proof for dynamic loading conditions. However, information given in the guidelines does not seem to be sufficient to appropriately perform such dynamic fracture mechanics safety assessments. The ongoing German research project MCGUSS is tailored to tackle this status. In MCGUSS, the application potential of the probabilistic fracture mechanics master curve (MC) concept according to ASTM E1921 is being systematically investigated and potential modifications specific for dynamic brittle fracture of DCI will be identified. While MCGUSS covers testing of a high number of SE(B)- and C(T)-type specimens, this poster focuses on preliminary C(T) results. The obtained data was statistically analyzed, and current results of MC analyses are discussed. Special emphasis of MCGUSS is on using optical and scanning electron microscopy to link microstructural damage and failure processes to the fracture toughness data gained. A fracture mechanism called "specimen size-dependent arrest of local brittle fractures before global brittle failure by weakest link" is proposed to describe the established dynamic toughness data. Concerning the MC concept, it was shown that the ASTM E1921 procedure cannot simply be adopted to dynamic DCI toughness data on a one-to-one basis. Material specific modifications are being investigated and the DCI dynamic fracture toughness data base is to be expanded. T2 - MPA Conference 2025 CY - Stuttgart, Germany DA - 06.10.2025 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Safety assessment KW - Master curve KW - Statistics PY - 2025 AN - OPUS4-64367 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stephan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary. T2 - 21st International Symposium ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Washington, DC, USA DA - 08.11.2023 KW - Ductile Cast Iron KW - Dynamic Fracture Toughness KW - Cleavage Fracture KW - Master Curve Concept PY - 2023 SP - 1 EP - 5 PB - ASTM International CY - West Conshohocken, PA AN - OPUS4-59064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan T1 - Master Curve-Auswertungen und Untersuchung des Größeneffekts für c(t)-proben - Aktuelle Erkenntnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung N2 - Ausgehend vom Stand des Regelwerkes und der Forschung wird in einem BMUV-Verbundprojekt zwischen der MPA Stuttgart und der BAM Berlin die Anwendung des Master Curve (MC)-Konzepts auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Ziel des Verbundprojekts ist die Anwendbarkeit des MC-Konzepts näher zu untersuchen und ggf. Modifikationen vorzunehmen, um eine Bewertungsmethode für die dynamische Bruchzähigkeit von DCI im Übergangsbereich zu erarbeiten. Auf den Jahrestagungen 2023 und 2024 des DVM-AK Bruchmechanik und Bauteilsicherheit wurden bereits der Forschungsansatz sowie erste Ergebnisse des Projekts MCGUSS präsentiert. Der Beitrag für die diesjährige Tagung soll nun MC-Auswertungen und den Größeneffekt für C(T)-Proben aus DCI diskutieren. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Versuche KW - Master Curve KW - Bruchmechanik KW - Dynamische Beanspruchung KW - Gusseisen mit Kugelgraphit PY - 2025 DO - https://doi.org/10.48447/BR-2025-495 SP - 123 EP - 129 PB - DVM-Verlag CY - Berlin AN - OPUS4-62555 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram T1 - Investigating the Applicability of the Master Curve Concept for Ductile Cast Iron – Early Results for 2 Different Test Temperatures N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. This paper outlines the research approach, the planned investigations and first results of the experimental program. T2 - 8th SEDS Workshop: Safety of Extended Dry Storage CY - Garching, Germany DA - 15.05.2024 KW - Dynamic fracture KW - Brittle fracture KW - Ductile cast iron KW - Master Curve PY - 2024 SP - 1 EP - 4 AN - OPUS4-60013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Statistische Auswertung der SE(B)-Bruchzähigkeitsdatenbasis und Untersuchungen zum Bruchmechanismus - Neue Ergebnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung (Projekt MCGUSS) N2 - Die Zielstellung des laufenden Kooperationsprojektes MCGUSS zwischen der BAM Berlin und der MPA Stuttgart ist es, das probabilistische Master Curve (MC)-Konzept hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) zu untersuchen. Über Teilergebnisse der Arbeiten wurde bereits auf den Jahrestagungen 2023 bis 2025 des DVM-AK Bruchmechanik und Bauteilsicherheit berichtet. Der vorliegende Beitrag hat zwei Schwerpunkte. Zum einen wurde die Datenbasis der dynamischen Bruchzähigkeit für SE(B)-Proben der Dicken 10 mm, 25 mm und 140 mm auf insgesamt 101 Versuche bei Temperaturen von -40 °C bis -140 °C erweitert, statistisch ausgewertet sowie MC-Analysen unterzogen. Die Ergebnisse zeigen, dass die Daten sich zwar mit einer Weibullverteilung gut beschreiben lassen, die MC-Methode nach ASTM E1921 jedoch nicht ohne Weiteres anwendbar ist, sondern Modifikationen erforderlich sind. Des Weiteren werden neue Ergebnisse zum werkstoffspezifischen Bruchmechanismus bei dynamischer Belastung im unteren Übergangsbereich der Zähigkeit diskutiert. Die fraktographische Datenbank wurde durch REM-Analysen weiterer Bruchflächen von SE(B)25-Proben bei -40 °C, -60 °C und -80 °C ergänzt. Die Ergebnisse unterstreichen die prägende Rolle, die Rissarrestereignissen im Verlauf des dynamischen Sprödbruchversagens bei DCI zukommt. Der in MCGUSS zur Erklärung eines gegenüber Stahl inversen Probengrößeneinflusses vorgeschlagene Mechanismus „Specimen size-dependent arrest of local brittle fractures before global brittle failure by weakest link“ wird dadurch weiter unterstützt. T2 - DVM-Jahrestagung 2026 des Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Stuttgart, Germany DA - 24.02.2026 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Safety assessment KW - Master curve KW - Statistics PY - 2026 AN - OPUS4-65593 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Ohm, Katrin A1 - Holzwarth, Marcel T1 - Statistische Auswertung der SE(B)-Bruchzähigkeitsdatenbasis und Untersuchungen zum Bruchmechanismus – neue Ergebnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung (Projekt MCGUSS) N2 - Die Zielstellung des laufenden Kooperationsprojektes MCGUSS zwischen der BAM Berlin und der MPA Stuttgart ist es, das probabilistische Master Curve (MC)-Konzept hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) zu untersuchen. Über Teilergebnisse der Arbeiten wurde bereits auf den Jahrestagungen 2023 bis 2025 des DVM-AK Bruchmechanik und Bauteilsicherheit berichtet. Der vorliegende Beitrag hat zwei Schwerpunkte. Zum einen wurde die Datenbasis der dynamischen Bruchzähigkeit für SE(B)-Proben der Dicken 10 mm, 25 mm und 140 mm auf insgesamt 101 Versuche bei Temperaturen von -40 °C bis -140 °C erweitert, statistisch ausgewertet sowie MC-Analysen unterzogen. Die Ergebnisse zeigen, dass die Daten sich zwar mit einer Weibullverteilung gut beschreiben lassen, die MC-Methode nach ASTM E1921 jedoch nicht ohne Weiteres anwendbar ist, sondern Modifikationen erforderlich sind. Des Weiteren werden neue Ergebnisse zum werkstoffspezifischen Bruchmechanismus bei dynamischer Belastung im unteren Übergangsbereich der Zähigkeit diskutiert. Die fraktographische Datenbank wurde durch REM-Analysen weiterer Bruchflächen von SE(B)25-Proben bei -40 °C, -60 °C und -80 °C ergänzt. Die Ergebnisse unterstreichen die prägende Rolle, die Rissarrestereignissen im Verlauf des dynamischen Sprödbruchversagens bei DCI zukommt. Der in MCGUSS zur Erklärung eines gegenüber Stahl inversen Probengrößeneinflusses vorgeschlagene Mechanismus „Specimen size-dependent arrest of local brittle fractures before global brittle failure by weakest link“ wird dadurch weiter unterstützt. T2 - DVM-Jahrestagung 2026 des Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Stuttgart, Germany DA - 24.02.2026 KW - Statistics KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve KW - Safety assessment PY - 2026 SP - 1 EP - 12 PB - DVM-Verlag CY - Berlin AN - OPUS4-65591 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Czeskleba, Denis A1 - Rhode, Michael A1 - Wandtke, Karsten A1 - Irfan, Muhammad Dary A1 - Kannengiesser, Thomas T1 - Hydrogen diffusion in thick-walled S690 saw joints: part 1—experimental determination of microstructure-dependent diffusion coefficients N2 - High-strength low-alloyed steel S690 is widely used in heavy-duty applications, such as structural components, mobile cranes, and industrial plant construction, owing to their high strength and weldability. However, thick-plate submerged arc welding (SAW) can introduce elevated hydrogen levels and residual stresses that promote time-delayed hydrogen-assisted cold cracking (HACC). Accurate, microstructure-specific diffusion data are scarce, limiting predictive HACC assessments. This study presents an experimental determination of hydrogen diffusion coefficients (DH) in two S690 variants: thermomechanically rolled (S690MC) and quenched and tempered (S690Q). Multi-layer SAW welds were produced from 30 mm thick plate material at three heat input levels, and diffusion membranes were extracted from weld metal (WM), heat-affected zone (HAZ), and base material (BM). Hydrogen permeation tests, conducted in accordance with DIN En ISO 17081, yielded flux curves normalized in time from which DH was derived using the inflection-point method. At room temperature, DH values ranged from 6 × 10−5 mm2/s to 9 × 10−5 mm2/s across all regions and heat inputs, with no significant difference between S690MC and S690Q. Weld metal exhibited marginally lower DH, attributed to enhanced hydrogen trapping, while base material measurements showed greater variability. These microstructure-resolved diffusion coefficients add quantitative data for modern S690 SAW welds and provide internally consistent input parameters for the numerical simulations presented in part 2. The results support improved parameterization for subsequent assessments of HACC risk through the optimization of welding parameters. KW - Hydrogen assisted cracking KW - Submerged arc welding KW - Diffusion KW - Electrochemical permeation KW - Microstructure PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655711 DO - https://doi.org/10.1007/s40194-026-02400-7 SN - 0043-2288 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-65571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Czeskleba, Denis A1 - Rhode, Michael A1 - Wandtke, Karsten A1 - Irfan, Muhammad Dary A1 - Kannengiesser, Thomas T1 - Hydrogen diffusion in thick-walled S690 SAW joints: part 2 – predictive modeling of heat input and microstructure influence N2 - High-strength low-alloy (HSLA) steels such as S690 are widely employed in thick-walled welded structures, where hydrogen-assisted cold cracking (HACC) remains a persistent concern. While microstructure-specific hydrogen diffusion coefficients (DH) for weld metal (WM), heat-affected zone (HAZ), and base material (BM) were experimentally established in Part 1 of this study, their quantitative influence on hydrogen accumulation and effusion has not yet been fully clarified. This work presents a transient, spatially resolved numerical model for simulating hydrogen transport in multi-pass submerged arc welds. The model integrates experimentally determined DH values with realistic thermal cycles and temperature-dependent boundary conditions. Developed in Python, the simulation tool is purpose-built for hydrogen diffusion in welded joints. It offers a focused, transparent alternative. It offers a focused, transparent alternative to general-purpose finite element platforms. Parametric analyses demonstrate that, although the diffusion coefficients vary by up to 50%, their impact on overall hydrogen retention is minor. In contrast, plate thickness, bead geometry, cooling time (t₈/₅), and interpass temperature exert a dominant influence on hydrogen distribution. Despite clear microstructural differences between the thermomechanically rolled (S690MC) and quenched and tempered (S690Q) variants, including opposite HAZ hardness responses (softening in S690MC, hardening in S690Q) in the (pen)ultimate weld bead, the simulations confirm that their diffusion behavior and hydrogen solubility are closely aligned. Consequently, differences in DH and solubility exert only a minor influence on hydrogen retention compared to thermal exposure and joint geometry. These findings support the interchangeable use of both steel grades in terms of HACC risk due to hydrogen diffusion kinetics under comparable welding conditions. KW - Hydrogen assisted cracking KW - Numerical simulation KW - Diffusion KW - Submerged arc welding PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655721 DO - https://doi.org/10.1007/s40194-026-02395-1 SN - 0043-2288 SP - 1 EP - 16 PB - Springer Science and Business Media LLC AN - OPUS4-65572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -