TY - CONF A1 - Nietzke, Jonathan T1 - Influence of strain rate on the effect of hydrogen in pre-charged 316L stainless steel: A comparison of conventional and hollow specimen testing N2 - The growing demand for hydrogen requires an expansion of testing capabilities to assess the performance of metallic materials under hydrogen exposure. Considering only gaseous atmospheres, there is a variety of in-situ and ex-situ methods used to investigate the material behavior while or after exposed to hydrogen, respectively. Among these methods, a more conservative one is the in-situ testing at slow strain rates (SSRT) using conventional tensile specimens. While results obtained by a conservative procedure may be more applicable in many cases than those of ex-situ experiments, the tests are quite demanding, leading to limited testing capacities and high costs, especially for very slow strain rates. A possible solution that can enable in-situ testing at relatively low cost is the hollow specimen technique which gained increasing interest in the last decade. The main reasons are the minimal volume of hydrogen required and the elimination of a high-pressure hydrogen autoclave leading to significantly lower costs and enabling more laboratories worldwide to perform these tests. However, interpreting results from hollow specimens, especially when compared to conventional ones, remains a significant challenge. To address this, an experimental study was conducted using conventional and hollow specimens, both uncharged and pre-charged. Pre-charging was achieved using pure hydrogen (5.0, i.e. 99.999 %) at 100 bar and 300 °C for around 21 days. In order to obtain suitable reference specimens, other specimens were stored in argon at 100 bar and 300 °C for the same period of time. The tests were performed at various strain rates, down to 1E-6 1/s. While these ex-situ experiments are not directly comparable to in-situ tests with both types of specimens, they do provide some insights into the differences between the results of hollow and conventional specimens. Therefore, the elongation at fracture and reduction of area (RA) were compared, among other aspects. In addition, fractographical analyses were carried out using SEM images. Elongation at fracture was not significantly affected by hydrogen in conventional specimens, but it was slightly reduced in hollow specimens. RA, on the other hand, was lower for tests with hydrogen in both types of specimens across all strain rates. Moreover, the strain rate did not appear to influence hydrogen embrittlement in conventional specimens whereas in hollow specimens, tests conducted at higher strain rates (1E-4 1/s) showed a greater impact of hydrogen on elongation at fracture than those at lower strain rates (1E-6 1/s), which is contrary to the typical expectation. These findings suggest that the influence of hydrogen differs between conventional and hollow specimens, possibly due to factors such as surface roughness and differing stress states. However, further experiments are needed to fully understand these differences, including in-situ experiments to understand potential differences in hydrogen absorption between the two specimen types. T2 - EPRI Workshop on Hydrogen Embrittlement CY - Oxford, England, United Kingdom DA - 23.06.2024 KW - Stainless steel KW - Hollow specimen KW - Pre-charging KW - Hydrogen PY - 2024 AN - OPUS4-60494 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis T1 - Ignition Behaviour and Challenges for Hydrogen Safety N2 - The presentation is divided in two parts. In the first part the significance of mechanical impacts as ignition source for hydrogen containing atmospheres is shown and recent results of a research project evaluating ignition probabilities under different conditions is presented. In the second part future challenges in the field of hydrogen safety are discussed. Finally, the German National Hydrogen Safety Alliance is introduced. T2 - Hydrogen Online Workshop 2024 CY - Online meeting DA - 05.06.2024 KW - Explosion protection KW - Mechanical impacts KW - Ignition source KW - German National Alliance for Hydrogen Safety PY - 2024 AN - OPUS4-60288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konert, Florian A1 - Campari, Alessandro A1 - Nietzke, Jonathan A1 - Sobol, Oded A1 - Paltrinieri, Nicola A1 - Alvaro, Antonio T1 - Evaluation of the tensile properties of X65 pipeline steel in compressed gaseous hydrogen using hollow specimens N2 - Hydrogen has great potential on the path towards decarbonization of the energy and transport sectors and can mitigate the urgent issue of global warming. It can be sustainably produced through water electrolysis with potentially zero emissions, and efficiently used (e.g., in fuel cell systems). Despite its environmental advantages, hydrogen-metal interactions could result in the degradation of the mechanical properties of several structural materials. In order to determine the magnitude of the material degradation in relation to hydrogen exposure, extensive material testing is required. The standardized procedure for in-situ testing for the quantification of the impact of compressed gaseous hydrogen (CGH2) relies on the utilization of an autoclave around the tested specimen. Such test set-up is complex, expensive, time-consuming and requires special equipment, trained personnel, and strict safety procedures. A relatively recent method to circumvent these issues and provide affordable results consists of using hollow specimens, thus applying the hydrogen pressure inside rather than outside the specimen. It allows to reduce the volume of hydrogen by several orders of magnitude and to perform the tests more efficiently and in a safer manner. This study focuses on evaluating the tensile properties of X65 vintage pipeline steel tested in a high-pressure hydrogen environment using hollow specimens. Tests are performed in 6 MPa H2 and Ar at the nominal strain rate of 10−6 s−1 to evaluate the reduced area at fracture and the elongation loss. The effect of surface finishing on crack initiation and propagation is investigated by comparing two different manufacturing techniques. In this way, this study provides insights into the applicability of a novel, reliable, and safe testing method which can be used to assess the hydrogen-assisted ductility loss in metallic materials. KW - Mechanical Engineering KW - Hydrogen Embrittlement KW - SSRT KW - Hollow specimen KW - Pipeline steel KW - In-situ tensile test PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595887 DO - https://doi.org/10.1016/j.prostr.2024.01.074 SN - 2452-3216 VL - 54 SP - 1 EP - 8 PB - Elsevier B.V. AN - OPUS4-59588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konert, Florian A1 - Wieder, Frank A1 - Nietzke, Jonathan A1 - Meinel, Dietmar A1 - Böllinghaus, Thomas A1 - Sobol, Oded T1 - Evaluation of the impact of gaseous hydrogen on pipeline steels utilizing hollow specimen technique and μCT N2 - The high potential of hydrogen as a key factor on the pathway towards a climate neutral economy, leads to rising demand in technical applications, where gaseous hydrogen is used. For several metals, hydrogen-metal interactions could cause a degradation of the material properties. This is especially valid for low carbon and highstrength structural steels, as they are commonly used in natural gas pipelines and analyzed in this work. This work provides an insight to the impact of hydrogen on the mechanical properties of an API 5L X65 pipeline steel tested in 60 bar gaseous hydrogen atmosphere. The analyses were performed using the hollow specimen technique with slow strain rate testing (SSRT). The nature of the crack was visualized thereafter utilizing μCT imaging of the sample pressurized with gaseous hydrogen in comparison to one tested in an inert atmosphere. The combination of the results from non-conventional mechanical testing procedures and nondestructive imaging techniques has shown unambiguously how the exposure to hydrogen under realistic service pressure influences the mechanical properties of the material and the appearance of failure. KW - Energy Engineering and Power Technology KW - Condensed Matter Physics KW - Fuel Technology KW - Renewable Energy, Sustainability and the Environment KW - µCT KW - Hollow Specimen Technique KW - Hydrogen Embrittlement PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595077 DO - https://doi.org/10.1016/j.ijhydene.2024.02.005 SN - 0360-3199 VL - 59 SP - 874 EP - 879 PB - Elsevier B.V. AN - OPUS4-59507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Holzwarth, Marcel A1 - Mayer, Uwe ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Versuchswerkstoff und erste Ergebnisse an SE(B)140-Großproben N2 - In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt. Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und -60 °C präsentiert. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2024 DO - https://doi.org/10.48447/BR-2024-BB SP - 49 EP - 58 PB - DVM-Verlag CY - Berlin AN - OPUS4-59518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Kritische Belastungsrate und erste Ergebnisse an C(T)-Proben N2 - Im laufenden Verbundprojekt MCGUSS untersuchen dieProjektpartner MPA Stuttgart und BAM Berlin das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI). Ziel des Projektes ist die Entwicklung einer Methode zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag werden die Eigenschaften des verwendeten Werkstoffs der Festigkeitsklasse GJS-400 vorgestellt und die sich daraus ergebenden Probenentnahmestellen näher erläutert. Weiterhin werden erste Ergebnisse der C(T)25-Versuchsserien vorgestellt, die bei Belastungsraten von ca. 5∙103 MPa√ms-1, 5∙104 MPa√ms-1 und 5∙105 MPa√ms-1 und einer Temperatur von -40 °C durchgeführt wurden. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Belastung KW - Master Curve KW - Gusseisen KW - C(T)-Proben PY - 2024 SP - 37 EP - 47 PB - DVM Verlag CY - Berlin AN - OPUS4-59519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Untersuchung des Master Curve-Konzepts für Ferritisches Gusseisen mit Kugelgraphit: Versuchswerkstoff und erste Ergebnisse von SE(B)140-Grossproben N2 - In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestim-mung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbe-reich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt. Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und 60 °C präsentiert. T2 - Jahrestagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Bruchzähigkeit KW - Sprödbruch KW - Master Curve KW - Gusseisen mit Kugelgraphit KW - ASTM E1921 PY - 2024 AN - OPUS4-59860 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, M. T1 - First results for the modification of the master curve concept for ferritic ductile cast iron N2 - Within the scope of fracture mechanics safety, ferritic ductile cast iron (DCI) does currently not have an established and validated method to determine and assess dynamic fracture toughness values in the ductile-to-brittle transition regime. For this reason, the applicability of the fracture mechanics Master Curve concept according to ASTM E1921 to DCI is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. To investigate the applicability of the Master Curve concept for DCI, a DCI material of grade GJS-400 has been procured via a detailed manufacturing specification. From this material test specimens of various geometries and sizes (Tensile, Charpy-V, Pellini, SE(B)10, SE(B)25, SE(B)140, DC(T)9, C(T)25 and C(T)50) were produced. In total, about 500 test specimens will be tested to investigate and validate the Master Curve Concept as well as other assumptions (e.g. size effects, Weakest-Link, Weibull distribution) for DCI. While the whole project has not yet concluded, several work packages have yet been completed. Selected test results using C(T)25 specimens are presented. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve PY - 2024 AN - OPUS4-61451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ferritic ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the research project is on brittle fracture. The goal is the establishment of a methodology to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. The experimental program uses a DCI material of grade GJS-400, which is generally used for transport and storage containers of radioactive materials. Firstly, a basic mechanical-technological material characterization will be performed consisting of tensile, Charpy and Pellini tests. Following the material characterization, the loading rate relevant for brittle fracture will be determined using instrumented C(T)25-fracture tests at a temperature of -40°C. To be able to transfer the relevant loading rate to other specimen geometries or sizes, the time-dependent course of the Weibull stress is assessed via numerical analyses. With this information an extensive experimental program consisting of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25 and SE(B)140 specimens is performed. These experimental results will be further supported by numerical and fractographic analyses. The empirical experimental database developed for DCI materials will be used to assess the applicability of the MC concept for DCI materials under dynamic loading. At the current time manufacturing and precracking of test specimens is ongoing. The authors provide first results concerning the mechanical-technological material characterization, the relevant loading rate for brittle fracture determined via C(T)25 tests, and some early results of other specimen types. These experimental results are also supported by preliminary numerical and statistical analyses. T2 - Conference SMiRT27 CY - Yokohama, Japan DA - 04.03.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - ASTM E1921 KW - Master curve KW - Brittle fracture PY - 2024 AN - OPUS4-59859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram A1 - Weihe, Stefan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to Hojo et al. (2008) the MC concept is already in use for the brittle fracture safety assessment of ferritic forged steel containers, which would suggest an extension to ductile cast iron containers. In compliance with IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general exclusion of crack initiation. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using only a low number of small fracture mechanics test specimens extracted from a component. For the experimental program, a DCI material of grade GJS-400 (GGG-40) has been produced as it is generally used for transport and storage containers for nuclear material. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests has been planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens at various loading rates and temperatures. The specimen testing is divided between the project partners based on specimen geometry. MPA Stuttgart has been tasked with the testing of the C(T), DC(T) and Pellini specimens, while BAM Berlin was assigned the SE(B), Charpy and tensile tests. These tests allow for the determination of the loading rate relevant for brittle fracture via C(T)25 specimens and an assessment of size effects by transferring the relevant loading rate to other specimen geometries and sizes. Numerical analyses of different specimen geometries and test setups are planned to investigate the influence of stress triaxiality and loading rate. Furthermore, the time-dependent course of the Weibull stress is assessed via these numerical analyses. Throughout the experimental program, the microstructure-property relationship will also be investigated based on quantitative metallographic and fractographic analyses like scanning electron microscope images and metallographic sections. With the acquired experimental database fundamental assumptions of the MC concept, like the weakest link model and the Weibull distribution, will be assessed for the application to DCI. In the end, the applicability of the MC concept will be evaluated and if necessary, modifications to the MC concept for DCI will be proposed. This paper will present the preliminary results of the GJS400 material characterization and the related selection of test specimen extraction points. First results of the C(T)25 and SE(B)140 specimen testing will also be discussed supported by first metallographic analyses. T2 - SMiRT27 Conference CY - Yokohama, Japan DA - 03.03.2024 KW - Ductile Cast iron KW - Dynamic Fracture Toughness KW - Safety Assessment KW - Master Curve Concept PY - 2024 SP - 1 EP - 10 AN - OPUS4-59302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Comprehensive Standardisation of the Hollow Specimen Technique for Tests in High-Pressure Hydrogen Gas N2 - The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations and complement the current techniques for qualifying metallic materials under highpressure hydrogen gas. In this technique, an axial hole is manufactured in a tensile specimen, which is then filled with hydrogen gas, sealed, and placed in a standard testing machine. This method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and does not require complex equipment or a specialised laboratory, unlike the conventional autoclave technique. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of the committee ISO/TC 164/SC 1/WG 9 to standardise the method, however, there are still open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions are being addressed in the H2HohlZug project, which is presented in this contribution. T2 - Oxford - EPRI Hydrogen Embrittlement Workshop CY - Oxford, United Kingdom DA - 23.06.2024 KW - Hollow Specimen Technique KW - High-pressure Gaseous Hydrogen KW - Hydrogen Embrittlement KW - Tensile Testing PY - 2024 AN - OPUS4-60501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Junias, Josua Kondja T1 - Prediction of Explosion Characteristics of Hydrogen Mixtures Using Machine Learning Models N2 - An understanding of Hydrogen-Oxygen/Air-Diluents gas mixtures combustion characteristics and their accurate prediction is crucial for ensuring the safety of hydrogen-related applications, reducing accidents risk, and protecting lives and property. Hydrogen detonation propagations are characterized by the detonation cell size, used to quantitatively predict for a mixture to detonate including, among others, the initiation energy, critical and minimum tube diameters. For the prediction of explosion limits, detonation run-up-distances and cell sizes, various empirical, semi-empirical and numerical models can be found in literature. These models are usually limited to a narrow range of explosion process or geometrical experimental parameters. Moreover, based on the limited availability of the detonation cell widths measurements, current estimation models are seemingly inaccurate. Machine learning models can be utilized to make justifiable prediction on the detonation cell sizes of hydrogen-air mixtures and other gaseous explosive mixtures cell sizes, explosion limits or run-up distance to detonation based on the mixture type, temperature, pressure, equivalence ratios as well as on geometrical parameters with consideration of highly diverse experimental data measurements uncertainties. Therefore, an up-to date database for explosion characteristics will be established and machine learning models will be developed, trained, tested, and validated using experimental data to predict explosion characteristics of hydrogen mixtures. The models predicted results will be validated against existing models. It will be tested whether machine learning models are able to predict the explosion characteristics of hydrogen mixtures with better accuracy and more comprehensively than conventional empirical and numerical models to be found in literature. T2 - Combustion Institute 40th International Symposium CY - Milano, Italy DA - 21.07. 2024 KW - Prediction, detonation KW - Machine Learning KW - Flammability limits PY - 2024 AN - OPUS4-60769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - Evolution of tensile testing methodologies for hydrogen embrittlement in austenitic steels: a comparative study N2 - The energy transition towards hydrogen utilisation has increased the demand for reliable testing methods to evaluate the susceptibility of metallic materials to hydrogen degradation. However, traditional electrochemical pre-charging techniques have limitations in represent-ing realistic gaseous hydrogen exposure conditions. This study presents three comparative analyses of tensile testing methodologies, focusing on the differences between electrochem-ical pre-charging, gaseous pre-charging, and in-situ testing using hollow specimens for aus-tenitic steels AISI 304L and 316L type austenitic steels. Based on the results obtained, the first comparison reveals that electrochemically pre-charged and gaseously pre-charged specimens exhibit different behaviours regarding the impact on the mechanical properties. This effect can be retraced to the varying distribution of hydrogen throughout the specimens. Although comparable embrittlement was observed for similar hydrogen concentrations, the relationship appears to be non-systematic. The second comparison evaluates the performance of pre-charged hollow specimens (300°C, 100 bar, 21 days) in comparison to hollow specimens tested in-situ under 200 bar hydrogen during slow strain rate tensile tests (SSRT). While pre-charged specimens show a slight de-crease in elongation at fracture and a noticeable decrease in reduction of area (RA), in-situ tested specimens exhibit significantly more pronounced embrittlement. This is in accord-ance with the results of Michler et. al. In the third comparison, geometry effects between pre-charged conventional and pre-charged hollow specimens are explored. In this case, the hydrogen effect appears to be of the same order of magnitude for both specimen types, although some differences are ob-served. The study's findings underscore the importance of considering differences between test methods when assessing materials’ compatibility with hydrogen. It specifically emphasises the need for in-situ testing with gaseous hydrogen to better represent real conditions in ap-plications within the hydrogen sector. Furthermore, the study provides an initial compari-son between conventional and hollow specimens, demonstrating their capability to reveal hydrogen effects. However, additional research is essential to enhance the comparability of results yielded by these testing methods. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Hollow Specimen Technique KW - Hydrogen KW - Austenitic Stainless Steel KW - Hydrogen Testing KW - AISI 316L PY - 2024 AN - OPUS4-60929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - The relationship between surface condition and the influence of hydrogen on the mechanical properties of additively manufactured 316L N2 - The following contribution presents the analyses of additively manufactured (AM) 316L using hollow specimens at 200 bar hydrogen and a strain rate of 1E-5 s-1. The work includes a comparison of three types of hollow specimens: mechanically extracted from fully additively manufactured cylinders, near-net-shape additively manufactured specimens, i.e. as printed, and specimens made of conventional 316L. AM specimens were manufactured via powder bed fusion with laser beam of metals (PBF-LB/M). For the near-net-shape specimens the inner hole remained without any mechanical processing. The inner holes of the cylindric specimens were manufactured by drilling with subsequent honing. The susceptibility to hydrogen embrittlement was found to be strongly dependent on the surface being in contact with hydrogen. While specimens with a clean surface had a relative reduction of area (RRA) of around 78 %, those with an as-printed surface showed a significantly larger RRA of around 90 %. One possible reason for this are oxide layers formed due to small amounts of oxygen during the AM-process. Further research is required to determine if the lower effect on the mechanical properties is permanently for as printed parts or e.g. time dependent. Additionally, further work with variation in the nominal strain rate is required. T2 - IIW 77th Annual Assembly 2024 CY - Rhodes, Greece DA - 07.07.2024 KW - Austenitic steel 316L KW - Additive manufacturing KW - PBF-LB/M KW - Hydrogen degradation KW - Hydrogen embrittlement KW - Hollow specimen technique PY - 2024 AN - OPUS4-60618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bock, Robert A1 - Mair, Georg W. T1 - Pilotprojekt "Verlässliche Wasserstofftechnologie" - Beispielanwendung für eine technische Anlage N2 - Kurzvorstellung des Pilotprojektes Verlässliche Wasserstofftechnologie in QI Digital. Anwendung der QI Digital Werkzeuge an einer technischen Anlage beispielhaft gezeigt anhand von sechs im Projekt entwickelten Demonstratoren. Unser erklärtes Ziel ist die Unterstützung des Markthochlaufs von Wasserstofftechnologien durch Digitalisierung der QI. Bei der Qualitätsinfrastruktur von technischen Anlagen geht es vor allem die Themen QI Dokumentation und Zugänglichkeit, Verfügbarkeit der Anlage und Informationen darüber, sowie Inspektionszyklen mit zeitaufwändigen und teuren manuellen Prüfungen. Mit dem Übergang zu einer digitalen QI streben wir hier an, eine kontinuierliche Überwachung des momentanen Gesundheitszustandes der Anlage und automatisierter Dokumentation hierüber, die fälschungssicher und vertraulich zugänglich gemacht werden kann, zu erreichen. Hierzu sollen die im Gesamtprojekt entwickelten QI Digital Werkzeuge zum Einsatz kommen. T2 - QI Forum 2024 CY - Berlin, Germany DA - 09.10.2024 KW - Wasserstoff KW - Qualitätsinfrastruktur KW - Digitalisierung PY - 2024 AN - OPUS4-61354 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hörmann, Anja Franziska T1 - (Grazing Incidence) Small-angle X-ray Scattering for STOP N2 - We remind project partners of the principles of SAXS, GISAXS and X-ray reflectivity and their applicability to the antimicrobial particles and coatings developed within the STOP project. T2 - M25 project meeting: Surface Transfer of Pathogens (STOP) CY - Bucharest, Romania DA - 19.09.2024 KW - X-ray Scattering KW - Nanomaterial PY - 2024 AN - OPUS4-62774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hajhariri, Aliasghar A1 - Eberwein, Robert A1 - Perrone, Luca Pakj A1 - Cozzani, Valerio A1 - Otremba, Frank A1 - Seidlitz, Holger T1 - Study the impact of spacer at thermal degradation process of MLI-based insulation in fire condition N2 - To reduce CO2 emissions, energy carriers such as hydrogen are considered to be a solution. Consumption of hydrogen as a fuel meets several limitations such as its low volumetric energy density in gas phase. To tackle this problem, storage as well as transportation in liquified phase is recommended. To be able to handle this component in liquid phase, an efficient thermal insulation e.g., MLI insulation is required. Different studies have been addressed the vulnerability of such insulation against high thermal loads e.g., in an accident engaging fire. Some of research works have highlighted the importance of considering the MLI thermal degradation focusing on its reflective layer. However, limited number of studies addressed the thermal degradation of spacer material and its effect on the overall heat flux. In this study, through systematic experimental measurements, the effect of thermal loads on glass fleece, glass paper as well as polyester spacers are investigated. The results are reported in various temperature and heat flux profiles. Interpreting the temperature profiles revealed that, as the number of spacers in the medium increases, the peak temperature detectable by the temperature sensor on the measurement plate decreases. Each individual spacer contributes to mitigating the radiative energy received by the measurement plate. Stacks of 20–50 spacers (this is the number of layers in commercial MLI systems applied for liquid hydrogen applications) can potentially reduce the thermal radiation by 1–2 orders of magnitude. An empirical correlation to predict a heat flux attenuation factor is proposed, which is useful for further numerical and analytical studies in the temperature range from ambient to 300 ◦C. KW - Cryogenic KW - Liquid Hydrogen KW - Multi-Layer Insultation KW - Heat Transfer KW - Hydrogen Storage Safety PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-614919 DO - https://doi.org/10.1016/j.jlp.2024.105461 SN - 0950-4230 VL - 92 SP - 1 EP - 7 PB - Elsevier Ltd. AN - OPUS4-61491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effect of temperature on the friction behaviour of rubber materials in hydrogen N2 - Safety and reliability are the major challenges to face for the development and acceptance of hydrogen technology. It is therefore crucial to study deeply material compatibility, in particular for tribological components that are directly in contact with hydrogen. Some of the most critical parts are sealing components that face high risk of damage due variation of pressure, temperature and mechanical stress. In this study, the friction and wear behaviour of several rubber materials was evaluated in hydrogen environment at ambient and low temperature. Tests were performed against 316L disks in a reciprocation motion. Results reveal that the hydrogen affects the friction and wear behaviour of most materials. The friction mechanism is dominated by deformation for most rubber materials at ambient temperature while sliding occurs at low temperature due to the increased hardness of the rubbers. T2 - Polytrib 2024 CY - Portorož, Slovenia DA - 03.10.2024 KW - Reciprocating sliding KW - Rubber materials KW - Hydrogen KW - Low temperature PY - 2024 AN - OPUS4-62019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Harmonised tribological testing of polymers in hydrogen N2 - The focus of this work is to study the tribological performance of polymers in hydrogen atmosphere. Additionally, tests were carried out with up to three different tribometers at two institutions. The challenge to compare and harmonise equipment, procedures, and methods is an important part of the study. T2 - PolyTrib 2024 CY - Portoroz, Slovenia DA - 03.10.2024 KW - Hydrogen KW - Tribometer KW - Comparability KW - Harmonisation KW - Oil-coupled compounds PY - 2024 AN - OPUS4-61224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Camplese, Davide A1 - Scarponi, Giordano Emrys A1 - Eberwein, Robert A1 - Hajhariri, Aliasghar A1 - Otremba, Frank A1 - Cozzani, Valerio T1 - Modelling Fire Response of Cryogenic Liquid Hydrogen Tanks Equipped with Multilayer Insulation (MLI) Systems N2 - In the context of the growing global interest in hydrogen-based green energy, cryogenic tanks equipped with multi-layer insulation (MLI) are emerging as a leading solution for storing hydrogen in vehicles. The integrity of these systems might be threatened during fire exposure. This can trigger the degradation of the MLI materials and induce rapid pressurization of the tank with a high risk of catastrophic failure. In this work, a novel lumped model to simulate the thermal response of MLI-equipped cryogenic liquid hydrogen tanks is presented. The model integrates the accurate database “Coolprop” for hydrogen thermodynamic properties and sub-models for detailed simulation of MLI degradation, providing a realistic simulation of the experimental data obtained under normal operating conditions. The application of the model to several case studies considering different numbers of MLI layers and tank geometries demonstrates that aluminum-based MLI offers scarce protection in case of exposure to a hydrocarbon poolfire. T2 - CISAP 11 CY - Neapel, Italy DA - 15.09.2024 KW - LH2 KW - LNG KW - Cryogenic storage tank KW - Insulation KW - MLI PY - 2024 DO - https://doi.org/10.3303/CET24111076 SN - 2283-9216 VL - 111 SP - 451 EP - 456 PB - AIDIC The Italian Association of Chemical Engineering AN - OPUS4-61384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -