TY - CONF A1 - Fey, Gero T1 - Dilatometer-based welding simulation: CCT-Diagram and investigation of heat-affected zones in pipeline steels N2 - Presentation of the research project “Hydrogen-dependent mechanical properties of the weld microstructure of low-alloy steels for long-distance gas pipelines” and the present results at the Young Professionals International Conference (YPIC) of the International Institute of Welding (IIW) T2 - 2nd Online Young Welding Professional International Conference - YPIC2025 CY - Online meeting DA - 06.02.2025 KW - Pipeline steel KW - CCT KW - Dilatometry KW - Heat-affected zone PY - 2025 AN - OPUS4-62583 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fey, Gero T1 - Dilatometerbasierte Schweißsimulation: ZTU-Diagramme und Untersuchung der Wärmeeinflusszonen in Pipelinestählen N2 - Präsentation des Forschungsprojekts "Wasserstoffabhängige mechanische Eigenschaften der Schweißnahtgefüge niedriglegierter Stähle für Ferngasleitungen" und der bisherigen Ergebnisse auf der 28. Konferenz aller Werkstofftechnischen und Materialwissenschaftlichen Studiengänge (KaWuM) an der TU Ilmenau. T2 - 28. Konferenz aller Werkstofftechnischen und Materialwissenschaftlichen Studiengänge CY - Ilmenau, Germany DA - 07.11.2024 KW - ZTU-Diagramm KW - Wärmeeinflusszone KW - WEZ KW - Dilatometer KW - Pipelinestahl PY - 2024 AN - OPUS4-62418 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Fügetechnik für Wasserstofftechnologien: Ausgewählte Themen und Herausforderungen N2 - Die Präsentation fasst die Bedeutung der Fügetechnik für Wasserstofftechnologien im Rahmen der Arbeiten für einer Studie (DVS-Berichte Nr. 373) mit besonderer Berücksichtigung der Normung und Regelwerkssetzung zusammen. T2 - Sitzung des DIN-Gemeinschaftsarbeitsausschusses NA 092 00 05 GA, NAS/NMP: Zerstörende Prüfung von Schweißverbindungen CY - Online meeting DA - 10.03.2022 KW - Wasserstoff KW - Fügetechnik KW - Schweißen KW - Wasserstofftechnologien KW - Bedeutung PY - 2022 AN - OPUS4-54447 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Reliable hydrogen determination in metallic materials and their weld joints: Parameters and challenges N2 - In the course of tomorrow's hydrogen-based energy transition, the construction of the corresponding infrastructure will play a central role. The majority of materials used to date are typically welded for component fabrication. In that context, steels are widely applied and can be prone to hydrogen embrittlement. This includes the classical delayed cold cracking during welding processing as well as embrittlement phenomena during operation. For the evaluation of any hydrogen effect on, for example, the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. In the case of welds, for example, according to ISO 3690, this is the isothermal carrier gas hot extraction (CGHE). CGHE is based on accelerated hydrogen degassing due to thermal activation of hydrogen at elevated temperatures. In addition to the pure quantification of hydrogen, thermal desorption analysis (TDA) with varied heating rates can be used to determine and evaluate the bonding state at microstructural defects in the material. For both techniques, experimental and measurement influences have to be considered, which have a great effect on the result. For CGHE, for example, ISO 3690 suggests different sample geometries as well as minimum extraction times. The present study summarizes results and experiences of numerous investigations with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding: the influence of the sample surface (polished/welded), measurement accuracies depending on the sample volume as well as the insufficient monitoring of the effect of the PI controller on the extraction temperature. In particular, a deviating extraction temperature to the set temperature, can significantly falsify the measurement results. Based on the results, methods are shown to quickly reach the desired extraction temperature without having to physically interfere with the measurement equipment. This serves to substantially improve the reliability of hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples for the selected heating procedure is advisable to exclude possible unwanted temperature influences already before the measurement. In addition (and way more important), the methods described can be transferred directly to industrial applications. T2 - 47th MPA-Seminar CY - Stuttgart, Germany DA - 10.10.2023 KW - Hydrogen assisted cracking KW - Carrier gas hot extraction KW - Welding KW - ISO 3690 KW - Metals PY - 2023 AN - OPUS4-58677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz T1 - Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten N2 - In vielen Anwendungen werden aufgrund zunehmender Anforderungen an den Widerstand gegenüber hohen, kombinierten mechanischen, tribologischen, thermischen und korrosiven Beanspruchungen Hochleistungsle¬gierungen eingesetzt. Den vielfach komplexen Bauteilstrukturen, herausfordernden Fertigungseigenschaften und der Erhöhung der Ressourceneffizienz lässt sich heute mit der additiven Fertigung (AM) begegnen, dem oftmals noch unzureichende Kenntnisse über die resultierende Homogenität und Anisotropie der speziellen Gefüge und den damit verbundenen Eigenschaften entgegensteht. Viele Anwendungen benötigen zudem definierte Oberflächen mit hohen Anforderungen an die Oberflächenintegrität, dem durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten Rechnung getragen wird. Hochleistungslegierungen auf der Basis von Nickel oder Kobalt sind infolge der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ein Vorhaben (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF befasst sich mit der Lösung dieser Problemstellung durch gezielte Beeinflussung des Gefüges mittels Modifikation der Schweißzusatzwerkstoffe und den Einsatz des ultraschallunterstützten Fräsens (US), bei gleichzeitiger Sicherstellung der geforderten Eigenschaften der untersuchten Werkstoffe. Es werden die Ergebnisse der Mikrostruktur und der Zerspanbarkeit der Modifikationen der MSG-Schweißung der FeNi36-Referenzlegierung mit 0,4 Gew.-% Zr und der Modifikationen der MSG-Schweißung der CoCr-Referenzlegierung mit 1 Gew.-% Zr sowie Hf vorgestellt. Abschließend werden aus den Ergebnissen Handlungsempfehlungen abgeleitet. T2 - Sitzung der Arbeitsgruppe (AG) V 12 „Additive Fertigung“ CY - Online meeting DA - 15.11.2023 KW - Legierungsmodifikation KW - Ultraschallunterstütztes Fräsen KW - Additive Fertigung KW - Oberflächenintegrität PY - 2023 AN - OPUS4-58859 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Hybrider Einsatz von LTT-Schweißzusatzwerkstoffen N2 - LTT (Low Transformation Temperature) - Schweißzusätze stellen eine Alternative zur Verfügung, um die Schwingfestigkeit in Schweißnähten zu erhöhen. Ziel dieses Vortages ist es zum einem die Thematik der LTT - Schweißzusätze, insbesondere in hybrider Ausführung zu erläutern, Zum anderen werden die Ergebnisse der Vorversuche präsentiert. T2 - BMDK CY - Magdeburg, Germany DA - 25.10.2023 KW - LTT (Low Transformation Temperature) KW - Martensitstarttemperatur KW - Baustähle KW - Eigenspannungen KW - Aufmischung PY - 2023 AN - OPUS4-58690 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Fügetechnik in Wasserstofftechnologien - Forschungsbedarf für die Branche (Kurzversion) N2 - Die Studie gibt einen kurzen Überblick über die jetzige Bedeutung der Fügetechnik in Wasserstofftechnologien und über zukünftige Forschungsbedarfe für die Branche in den einzelnen Technologiefeldern Wasserstofferzeugung, -speicherung, -transport und -nutzung. Fügetechnologien haben dabei wesentliche Bedeutung für die erfolgreiche Umsetzung von technischen Komponenten der Wasserstofftechnologien. Die Schwerpunkte bzw. Forschungsbedarfe ergeben sich bspw. durch die Erstellung neuer Infrastruktur für Wasserstoffspeicherung und -transport sowie durch Umnutzung der bestehenden Erdgasinfrastruktur. Bei der Wasserstofferzeugung und -anwendung wird z.B. die Entwicklung effiziente Massenproduktionsmethoden von Elektrolyseuren und Brennstoffzellen einen wichtigen Meilenstein bilden und laserbasierte Fügetechnologien sind hier zum Teil schon etabliert. Die additive Fertigung nimmt dabei eine Querschnittsposition ein und besitzt hohes Anwendungspotential für die Zukunft z.B. für die Fertigung von Komponenten in Gasturbinen. Aus den technischen Fragestellungen und Forschungsbedarfen ergeben sich zudem Herausforderungen für die notwendige Neu- und Weiterentwicklung von technischen Regelwerken und Normen und den Eingang in die Aus- und Weiterbildung von fügetechnischem Fachpersonal. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - Wasserstoff KW - Fügetechnik KW - Forschung KW - Werkstoff KW - Bedarf PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 612 EP - 624 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53370 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Experimentelle Bestimmung und thermodynamische Modellierung des Ausscheidungsverhaltens in der WEZ eines S690QL bei unterschiedlichen Mikrolegierungsrouten N2 - Für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Normstreckgrenze > 690 MPa, ist die Zugabe von Mikrolegierungselementen, wie Nb und Ti, unerlässlich. Die Normvorgaben zur chemischen Zusammensetzung dieser Stähle (bspw. in DIN EN 10025-6) geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Legierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Zuzüglich können moderne Schweißprozesse, wie MSG mit modifiziertem Sprühlichtbogen (mod. SLB) durch ihre hohe Wärmeeinwirkung die Phasenumwandlung in der Wärmeeinflusszone negativ beeinflussen. Eine unerwünschte Eigenschaft ist dabei die Erweichung (engl.: softening) der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung (engl.: hardening). Vor diesem Hintergrund werden im Rahmen eines DFG-Vorhabens systematisch Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten des hochfesten und vergüteten Feinkornbaustahls S690QL untersucht. Dazu wird das MAGSchweißen mit mod. SLB verwendet, welches durch hohe Abschmelzleistung gekennzeichnet ist und schmalere Fugenöffnungswinkel (α = 30°) ermöglicht. An diesen Schweißungen wird der Effekt der metallurgischen Zusammensetzung in Kombination mit hoher Wärmeeinwirkung auf die Ausbildung einer kritischen WEZ-Gefügezone mit Erweichung und/oder exzessiver Aufhärtung untersucht. Ein besonderes Augenmerk wird auf die Phasenumwandlungen und das Ausscheidungsverhalten im Gefüge der Wärmeeinflusszone gelegt. Neben umfangreichen metallographischen Untersuchungen einzelner WEZ-Bereiche wurden, unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels ThermoCalc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation und Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. Das Ziel ist es, mittels erster Untersuchungen den Einfluss der Wärmeeinwirkung auf die Gefügeausbildung in der WEZ zu zeigen. Insbesondere wird hier auf die Auswirkung der unterschiedlichen Mikrolegierungskonzepte (Ti oder Nb) geachtet. T2 - DVS CONGRESS 2022 - Große Schweißtechnische Tagung CY - Koblenz, Germany DA - 19.09.2022 KW - WEZ-Erweichung KW - Hochfester Feinkornbaustahl KW - ThermoCalc KW - Thermodynamische Simulation KW - Mikrolegierungselemente KW - Modifizierter Sprühlichtbogen PY - 2022 SN - 978-3-96144-189-1 SN - 978-3-96144-190-7 VL - 382 SP - 131 EP - 137 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-55834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neumann, Martin A1 - Gleim, Tobias A1 - Gradt, Thomas T1 - Friction coefficients for wood-wood and wood-steel high pressure contact under temperatures between -40 °C and 90 °C N2 - Wood is widely used in impact limiters of Transport casks for radioactive material. Encapsulated by an outer and inner Steel structure, spruce wood is offen applied in layers of altemating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard component. In order to get detailed Information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature ränge between -40 °C and 90 °C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40 °C to 0.22 for 90 °C for wood-steel combinations and from 0.3 at -40 °C to 0.24 at 90 °C to for a wood-wood combination. KW - Wood KW - Friction KW - Transport cask KW - Radioactive material PY - 2023 DO - https://doi.org/10.24053/TuS-2023-0007 SN - 0724-3472 VL - 70 IS - 2 SP - 5 EP - 12 PB - expert verlag AN - OPUS4-57787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas T1 - Measurement of hydrogen concentration in steel using Laser-induced Breakdown spectroscopy (LIBS) N2 - Currently, the ISO 3690 standard requires a thermal activation of the diffusible hydrogen in weld metal for the subsequent ex situ concentration measurement by TDS. Laser-induced breakdown spectroscopy (LIBS) would offer a time and spatially resolved, almost non-destructive, measurement of hydrogen at surfaces. We could already show that this analysis technique allows for highly accurate in situ measurements of chemical compositions of e.g. Mn, Cr and Ni during welding e.g. in the melt pool, the weld metal or the heat affected zone. For quantitative LIBS measurements of hydrogen in steel, certified reference materials with different hydrogen concentrations were used for calibration. There is a significant problem in welding steels: A critical combination of diffusible hydrogen, hardness microstructure and weld residual stresses can cause cold cracks to form in the weld microstructure. We investigated hydrogen in steels, which was loaded either electrochemically or with high-pressure hydrogen gas. Subsequently, various experiments were conducted to verify the feasibility of hydrogen measurements with LIBS. For example, depth profiles of hydrogen distribution could be obtained. Furthermore, samples were water jet cut and a line scan was made over the cross section to obtain a spatially resolved representation of the hydrogen. Total hydrogen concentrations were determined using carrier gas hot extraction. Our results show that LIBS is a promising technique for time and spatially resolved measurement of hydrogen in steels. T2 - IIW Annual Assembly 2023 CY - Singapore DA - 16.07.2023 KW - LIBS KW - Hydrogen measurement KW - Welding KW - Stainless steel PY - 2023 AN - OPUS4-57989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - The contribution describes a newly developed software tool for crack identification and selection in Modified Varestraint Transvarestraint (MVT) testing. From the digital crack information, in addition to the classical results, such as Total Crack Length (TCL) and Maximum Crack Length (MCL), advanced evaluations can be applied, taking into account the loading and welding parameters. A numerical parameter study is conducted to demonstrate how the isolated variation of individual welding and loading parameters, affects the crack lengths that can potentially be expected based on the machine specifics. An alternative crack criterion is presented that evaluates the crack formation in relation to the machine behavior. Some examples demonstrate the possibilities and limitations of the approach. The criterion can be used to compare and transfer the results of different varestraint test variants. T2 - IIW Annual Assembly, Comission II-C CY - Singapore DA - 17.07.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Local strain behaviour by digital image correlation of cross weld tensile specimens of high strength steel with two different Ti microalloying routes N2 - Microalloying elements such as Nb and Ti play a decisive function in achieving the desired mechanical strength of quenched and tempered, high-strength fine-grain structural steels with a nominal yield strength ≥ 690 MPa. The current specifications for the chemical composition only provide manufacturers with upper limits. However, even minor deviations in the alloy concept can have a significant impact on the mechanical properties. Consequently, accurate prediction of weldability and the integrity of welded joints becomes difficult or even impossible due to differences in composition and the resulting microstructures. Undesirable consequences include a possible softening of the heat-affected zone (HAZ) or, conversely, hardening effects. In view of these challenges, various microalloying strategies with different Ti and Nb contents are being systematically investigated for the first time using specially developed laboratory casting alloys. Each alloying route is based on the common S690QL, maintaining both the chemical composition and the heat treatment parameters. To analyse the weldability, three-layer welds were performed using gas metal arc welding (GMAW) and critical microstructures, such as areas of the heat-affected zone (HAZ) that exhibit significant softening or hardening, were identified. The effect of the softened HAZ region on failure was evaluated using transverse tensile specimens. Digital image correlation (DIC) is used to image changes in local strains in different HAZ regions in situ. Using a specially developed mirror system, the local strains of the microstructure zones on the top and bottom of the weld are recorded simultaneously. This makes it possible to analyse how the weld seam geometry (e.g., V-seam) influences the strain gradients. In addition, the analysis of the local deformation helps to understand the effects of the softened HAZ on the global strain, the fracture constriction, the fracture position, and the overall fracture behavior T2 - The 77th IIW Annual Assembly and International Conference on Welding and Joining CY - Rhodos, Greece DA - 07.07.2024 KW - HSLA KW - Digital Image Correlation KW - Microalloy KW - GMAW KW - HAZ KW - Cross-weld tensile test PY - 2024 AN - OPUS4-60794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Westin, Elin T1 - Assessing ferrite content in duplex stainless weld metal: WRC '92 predictions vs. practical measurements N2 - The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to assess the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was evaluated using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While predictions from the WRC ’92 diagram were deemed acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, albeit with slightly higher FN values, wider scatter, and the conversion factor from FN to vol.-% is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds. These findings underscore the need for improved prediction tools and appropriate measurement methods for assessing ferrite content in duplex weld metals. T2 - Annual Assembly and International Conference CY - Rhodes, Greece DA - 07.07.2024 KW - Duplex steel KW - Ratio austenite / ferrite KW - WRC diagram PY - 2024 AN - OPUS4-60771 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp T1 - Einfluss des Einspanngrades auf die Bildung von Erstarrungsrissen in Überlappverbindungen hochfester Stähle N2 - Im Vortrag werden Ergebnisse aus Versuchen mit dem Controlled Thermal Severity (CTS)-Test vorgestellt, der für sehr stark eingespannte Kehlnähte bekannt ist. Niedriglegierte Schweißungen an hochfesten Stählen sind nicht anfällig für Erstarrungsrissbildung. Unter dem besonderen Einfluss eines hohen Einspanngrades wurde die Erstarrungsrissneigung durch Abmessen der Rissflächen als Funktion der Schweißparameter und des Einspanngrades für vier hochfeste Schweißzusätze im MAG-Schweißen untersucht. Die Tests zeigen, dass sowohl eine Erhöhung des Einspanngrades als auch eine Änderung der Schweißparameter (hinsichtlich Streckenenergie und Geschwindigkeit) zu mehr Erstarrungsrissfläche führen. Besonders die Kombination aus sehr hohem Einspanngrad und hoher Streckenenergie plus hoher Schweißgeschwindigkeit sollte im Sinne der Erstarrungsrissminimierung vermieden werden. T2 - DVS-Congress CY - Erfurt, Germany DA - 16.09.2024 KW - CTS KW - Kehlnähte KW - Erstarrungsrisse PY - 2024 AN - OPUS4-61068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp T1 - Investigation of Solidification cracking susceptibility via Modified Varestraint Transvarestraint testing of high-strength filler material N2 - The Modified Varestraint Transvarestraint test is a local variant of the globally used Varestraint test. With these tests, measuring solidification cracking susceptibility as a function of welding parameters is possible. A wide range of welding parameters for four high-strength steel filler wires, including three solid wires and one-flux cored metal wire, were tested. All wires do show a very low solidification cracking susceptibility, regardless of the paramaters. On a low level, it could be shown that solidification cracking susceptibility increases with heat input and welding speed. T2 - IIW Annual Assembly CY - Rhodos, Greece DA - 07.07.2024 KW - MVT KW - Varestraint KW - Transvarestraint KW - Solidification cracking PY - 2024 AN - OPUS4-60684 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp T1 - Investigation of restraint intensity influence on solidification cracking of high-strength filler materials in fillet welds via CTS testing N2 - Testing of highly restraint high-strength fillet welds with regards to solidification cracking susceptibility. The Controlled Thermal Severity test was used to apply a high amount of strain to solidifying welds. Test welds were cut and observed under an optical light microscope. A clear positive correlation between restraint intensity and measured crack sizes, as well as heat input and measured crack sized could be observed. T2 - IIW Annual Assembly CY - Rhodos, Greece DA - 07.07.2024 KW - CTS KW - Solidification cracking KW - Hot cracking KW - High-strength steel PY - 2024 AN - OPUS4-60682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Residual stress reduction using LTT welding consumables with focus on the weld geometry N2 - Low Transformation Temperature (LTT) welding consumables represent an innovative approach to realize compressive residual stress in weld and HAZ. LTT welding consumables use the volume-expanding martensitic phase transformation near room temperature to generate compressive residual stress during cooling. This article focusses on the weld geometry of LTT welding consumables and their influence on residual stress reduction. For this purpose, LTT layers were additionally applied to the front sides of conventionally welded longitudinal stiffeners. By varying parameters such as offset and welding speed, different weld geometries could be realized. These were analyzed for geometric parameters, chemical composition and residual stress using X-ray diffraction and fatigue testing. While the chemical composition was only slightly influenced by parameters changes, a clear influence was observed regarding to weld geometry and residual stress. The conventionally weld was characterized by tensile residual stress of ≈350 MPa at the weld toe, the additional LTT weld bead exhibits compressive and tensile residual stress of ≈-150MPa to ≈+150MPa depending to the parameter variation. T2 - International Institut of Welding 2024 CY - Rhodos, Greece DA - 07.07.2024 KW - LTT (Low Transformation Temperature) KW - Residual stress KW - Fatigue strength KW - High-strength steels PY - 2024 AN - OPUS4-60825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fey, Gero T1 - Nachbildung der Schweißgefüge von Pipelinestählen durch Dilatometerversuche: ZTU-Diagramme und Wärmeeinflusszonen im Fokus N2 - This study investigates the suitability of low-alloy pipeline steels for hydrogen transportation, focusing on the development of weld microstructures. Previous research has been limited by a deficiency in the understanding of how different microstructural components respond to trapped hydrogen. By developing Continuous Cooling Transformation (CCT) diagrams through dilatometry analysis, this study explores the impact of t8/5-cooling times (the time between 800 °C and 500 °C) on the microstructure and mechanical properties of the HAZ compared to the base material. The findings provide valuable insights into how cooling times influence transformation temperatures and microstructure development, which, in turn, affect hydrogen diffusion and absorption. These findings establish a foundation for future investigations into hydrogen's impact on weld microstructures, including experimental studies, with the aim of optimizing welding practices and enhancing resistance to hydrogen-assisted cracking. Ultimately, this research contributes to improving the safety and reliability of hydrogen transportation systems in commonly used industrial pipeline steels. T2 - Forschungsseminar am Institut für Werkstoff- und Fügetechnik der Otto-von-Guericke-Universität Magdeburg CY - Magdeburg, Germany DA - 18.06.2025 KW - Pipelinestahl KW - ZTU KW - WEZ KW - L555ME KW - X80M KW - Dilatometrie PY - 2025 AN - OPUS4-63751 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fey, Gero T1 - Thermophysically Simulated Weld HAZ and CCT Diagram of High Strength Low Alloy Pipeline Steel N2 - This study investigates the suitability of low-alloy pipeline steels for hydrogen transportation, focusing on the development of weld microstructures. Previous research has been limited by a deficiency in the understanding of how different microstructural components respond to trapped hydrogen. By developing Continuous Cooling Transformation (CCT) diagrams through dilatometry analysis, this study explores the impact of t8/5-cooling times (the time between 800 °C and 500 °C) on the microstructure and mechanical properties of the HAZ compared to the base material. The findings provide valuable insights into how cooling times influence transformation temperatures and microstructure development, which, in turn, affect hydrogen diffusion and absorption. These findings establish a foundation for future investigations into hydrogen's impact on weld microstructures, including experimental studies, with the aim of optimizing welding practices and enhancing resistance to hydrogen-assisted cracking. Ultimately, this research contributes to improving the safety and reliability of hydrogen transportation systems in commonly used industrial pipeline steels. T2 - 78th IIW Annual Assembly & International Conference on Welding and Joining CY - Genoa, Italy DA - 22.06.2025 KW - Pipeline steel KW - CCT KW - HAZ KW - Dilatometry KW - Welding KW - L485ME KW - X70M PY - 2025 AN - OPUS4-63752 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fey, Gero T1 - Unter Druck gesetzt: Die unterschätzte Bedeutung des In-Service-Schweißen an druckführenden, in Betrieb befindlicher H2-Ferngasleitungen N2 - Wasserstoff gilt als Energieträger für die Erreichung der Klimaziele und einer nachhaltigen zukünftigen Energieversorgung. Für den notwendigen Transport des Wasserstoffs in großem Maßstab und über weite Entfernungen ist eine zuverlässige Pipeline-Infrastruktur erforderlich. Umfassende weltweite Forschungsprojekte deuten auf die allgemeine Kompatibilität der verwendeten überwiegend ferritischen Stähle für die vorgesehenen Betriebsbedingungen von bis zu 60 °C bei 100 bar Wasserstoff hin. Dies ist jedoch nicht direkt übertragbar auf schweißtechnische Reparatur- und Wartungsarbeiten an im Betrieb befindlichen Pipelines. Ein im Erdgasnetz etabliertes Verfahren stellt das „Hot-Tapping“ dar, bei dem eine unter Druck stehende Pipeline im Betrieb angebohrt wird. Hierfür kommt ein an die Rohrleitung geschweißtes Formstück zum Einsatz, das die Montage der Bohr-/Lochschneidemaschine ermöglicht. In den Richtlinien EIGA 121/14 bzw. AIGA 033/14 wird darauf hingewiesen, dass das Anbohren von Wasserstoffleitungen kein Routineverfahren darstellt: “[…] a hydrogen hot-tap shall not be considered a routine procedure […]“. Dieser Aussage liegt unter anderem zugrunde, dass das Anschweißen des Formstücks an das Rohr und alle zu erwartenden Wärmebehandlungen vor und nach dem Schweißen eine lokale Temperaturerhöhung verursachen. Insbesondere auch an der Rohrinnenfläche, die dem Wasserstoff ausgesetzt ist. Diese erhöhten Temperaturen begünstigen die Absorption und Diffusion von Wasserstoff in das Material. Besonders zu beachten ist außerdem die lokal auftretende kurzzeitige Austenitisierung des Materials, die eine lokal stark erhöhte Wasserstoffkonzentration verursachen kann. Aus den genannten Gründen gibt diese Studie einen kurzen Überblick über die derzeit weltweit verfügbaren Forschungsprojekte zum Schweißen von Wasserstoff-Pipelines im Betrieb. Vorgestellt werden unter anderem erste Ergebnisse des Kooperationsforschungsprojektes H2SuD, das derzeit an der BAM bearbeitet wird. T2 - DVM-Workshop "Werkstoffe für die Wasserstoffinfrastruktur – von der Werkstoffentwicklung bis zum Einsatz im Bauteil" CY - Berlin, Germany DA - 21.05.2025 KW - Pipeline KW - Schweißen KW - Wasserstoff KW - In-Service Welding KW - Reparaturschweißen PY - 2025 AN - OPUS4-63749 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -