TY - CONF A1 - Winckelmann, Alexander T1 - Investigation of degradation of the aluminum current collector in lithium-ion batteries by glow-discharge optical emission spectroscopy N2 - Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs. T2 - Adlershofer Forschungsforum 2022 CY - Berlin, Germany DA - 11.11.2022 KW - Lithium Ion Batteries KW - GD-OES KW - FIB KW - SEM KW - EDX PY - 2022 AN - OPUS4-56246 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Nils T1 - Sicherheit von Lithium-und Natrium-Batterien - Brandprüfungen und Sicherheitsmaßnahmen N2 - Die Präsentation gibt einen ganzheitlichen Überblick im sicheren Umgang mit elektrochemischen Energiespeichertechnologien. Ferner enthält diese Präsentation einen Überblick über die aktuell an der BAM durchgeführten Forschungsprojekte und hoheitlichen Aufgaben mit Bezug diesen Energiespeichern T2 - Lehrgang "Moderne elektrochemische Energiespeicher" (905350) CY - Mannheim, Germany DA - 16.09.2024 KW - Lithiumbatterien KW - Thermal Runaway KW - Sicherheit KW - Natriumbatterien PY - 2024 AN - OPUS4-62302 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tichter, Tim T1 - Electroanalytical experiments at macroporous electrodes for redox-flow batteries N2 - Macroporous carbon felts (CFs) are the prevalently used electrode material for redox-flow batteris. Owing to their large internal surface area, these structures can efficiently drive the Faradaic reactions in a RFB. However, the electrochemical characterization of novel CFs, or modified CF-materials is a cumbersome task. This is essentially related to the complex mass-transport phenomena which are convoluted with the electrode kinetics. This talk will focus on ex-situ cyclic voltammetry and operando electrochemical impedance spectroscopy as electroanalytical techniques for porous RFB electrodes. Common pitfalls in the voltammetric analysis of CFs are elucidated and recent strategies for modeling and evaluating CV experiments on porous structures are introduced. Finally, a method based on electrochemical impedance spectroscopy is introduced which allows for an operando fingerprinting of electrochemical reactions in a vanadium-based RFB. T2 - Flow4U-Event CY - Eindhoven, Netherlands DA - 08.04.2024 KW - Porous Electrodes KW - Redox-Flow Batteries KW - Digital Simulation KW - Convolutive modeling KW - Impedance Spectroscopy KW - Distribution of Relaxation Times PY - 2024 AN - OPUS4-62304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tichter, Tim T1 - The DSDC Algorithm - A Universal Strategy for Simulating Voltammetry of Rough and Porous Electrodes N2 - Porous electrodes or electrodes with rough surfaces offer a multitude of tailored applications. The theoretical treatment of such structures is, however, challenging since their voltammetric profile is a convolution of the time-dependent current with an inherently random mass-transfer function. Since the latter quantity has no analytical solution, the classical convolutive techniques cannot be applied. Therefore, simulations have been based on severe simplifications of the diffusion space [1,2] or were performed by means of digital simulation. Unfortunately, the latter approach becomes computationally prohibitive when a large and/or highly resolved, three-dimensional diffusion space needs to be considered. To mitigate these problems, we introduce the digital simulation, deconvolution, convolution (DSDC) algorithm, consisting of four successive steps [3]. Firstly, the three-dimensional image of the electrode under investigation is extracted via micro X-ray computed tomography (µ-CT) or atomic-force microscopy (AFM). Subsequently, the purely mass-transfer controlled current of this spatial template is generated by means of digital simulation. In the third and fourth steps, the mass-transfer function is extracted for a set of discrete points in time by numerical deconvolution and finally used for classical convolutive simulations. In this manner, any simplification of the diffusion domain becomes obsolete and the advantages of digital simulation and convolutive modelling are most favourably combined. Finally, this DSDC-algorithm provides an interdisciplinary connection of ex-situ imaging and in-situ electrochemistry which results in excellent agreement of simulated and experimentally acquired data. T2 - Bunsentagung 2024 CY - Aachen, Germany DA - 25.03.2024 KW - Porous Electrodes KW - Convolutive Modeling KW - Digital Simulation KW - Diffusion KW - Redox-Flow Batteries PY - 2024 AN - OPUS4-62303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leonhardt, Robert T1 - Impedance-based characterization of the overstress-related degradationin alkali metal-ion cells N2 - The successful repurposing of degraded alkali metal-ion batteries in second-life applications is a vital step towards achieving a circular economy. While reusing aged cells is a promising way of mitigating their overall environmental footprint, it is crucial to anticipate their future safety and performance characteristics. Unfortunately, predicting these properties is a cumbersome task, essentially caused by limited knowledge of the interference of different degradation modes in the cells’ first life. To still enable estimating of these parameters from a current state, the present study systematically investigates the impact of abusive conditions in an early phase of the cells’ life on their subsequent degradation behavior. For this purpose, individual lithium-ion and sodium-ion cells are initially stressed by different measures such as deep-discharging, high-temperature conditions, and deliberate combinations of the aforementioned methods. Electrochemical performance indicators are monitored during subsequent cycling of the cells, which provides insights into the interdependencies of different degradation modes induced by specific stress conditions. In this manner, it is clarified whether or not the total degradation can be determined by a convolution or a superposition of individual deterioration effects and thus, be described as a multidimensional state function. This knowledge will finally contribute to a better understanding of the performance and safety behavior of degraded batteries which can help to successfully implement them into second-life applications. T2 - Doktorandenseminar der Technischen Universität Berlin CY - Berlin, Germany DA - 30.09.2025 KW - Alkali metal-ion batteries KW - Electrochemical performance indicators PY - 2025 AN - OPUS4-65068 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Nils T1 - Lithiumbatterien, Natrium-Ionen Batterien, Festkörperbatterien - Wohin geht die Regelwerksentwicklung? N2 - Der Markt für Energiespeicher befindet sich in einer Phase intensiver technologischer Diversifizierung. Neben etablierten Lithium-Ionen-Batterien gewinnen neue Systeme wie Natrium-Ionen-Batterien und künftige Technologien wie Festkörperbatterien zunehmend an Bedeutung. Dies stellt jedoch neue Anforderungen an die Handhabung und Logistik respektiver Systeme und rückt die Klassifizierung von Batterien nach Gefährlichkeit stärker in den Fokus. In diesem Kontext gilt es Transportprozesse zu vereinfachen und simultan die Sicherheit zu erhöhen. Im Rahmen dieses Vortrags werden aktuelle und kommende Batterietechnologien vorgestellt, die essenziellen Hürden bei deren Handhabung, Transport und Lagerung zusammenfassend dargestellt und ein umfassender Ausblick auf die Regelwerksentwicklung gegeben. Schwerpunkte liegen dabei auf I) der Entwicklung dedizierter Methoden für die Einordnung in Kategorien defekte und kritisch defekte Batteriesysteme, II) Passivierende Verfahren (thermisch und/oder elektrisch) für einen sicheren Transport und III) der Optimierung der Wertschöpfungskette des Gesamtsystems „Batterie“ durch effizientere Batteriekreisläufe und Recyclingverfahren. T2 - Zweite Fachkonferenz Transport und Lagerung von Lithiumbatterien 2025 CY - Augsburg, Germany DA - 03.07.2025 KW - Batteriesicherheit KW - Gekühlter Transport von Batterien KW - Tieftemperaturpassivierung KW - Regelwerksentwicklung KW - Wertschöpfungskette und Batterierecycling PY - 2025 AN - OPUS4-65078 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Nils T1 - „Batterien“ Gefahrgutrechtliche Entwicklung für die Anwendung N2 - Der Markt für Energiespeicher bietet eine kontinuierlich wachsende, technologische Vielfalt. Neben etablierten Lithium-Ionen-Batterien gewinnen alternative Systeme wie Natrium-Ionen-Batterien zunehmend an Bedeutung. Jene Entwicklung steigert aktuell die Anforderungen an Regularien für Logistik und Handhabung ebendieser Systeme und bedarf einer dedizierten jedoch gleichwohl praktikablem Klassifizierung unterschiedlicher Batterien nach deren Gefährlichkeit. Genau dies ist der Schwerpunkt der vorliegenden Präsentation. Ein besonderer Fokus liegt dabei auf dem sicheren Transport kritisch defekter Batteriesysteme durch thermische Passivierung und/oder gezieltes Tiefentladen. Explizit werden aktuelle und zukünftige Batterietechnologien vorgestellt, die wesentlichen Herausforderungen bei Handhabung, Transport und Lagerung zusammengefasst und ein umfassender Ausblick auf die Weiterentwicklung der relevanten Regelwerke gegeben. T2 - 35. Münchner Gefahrgut-Tage CY - Munich, Germany DA - 26.05.2025 KW - Batteriesicherheit KW - Thermisches Durchgehen KW - Tieftemperaturpassivierung KW - Initiale Reaktionstemperatur KW - Gekühlter Transport von (kritisch) defekten Batterien PY - 2025 AN - OPUS4-65077 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winckelmann, Alexander T1 - Investigation of degradation of the aluminum current collector in lithium-ion batteries by glow-discharge optical emission spectroscopy N2 - Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs.[1] Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs. T2 - European Winter Conference on Plasma Spectrochemistry (EWCPS 2023) CY - Ljubljana, Slovenia DA - 29.01.2023 KW - Lithium-ion batteries KW - Aging mechanisms KW - Depth-profiling PY - 2023 AN - OPUS4-56992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winckelmann, Alexander T1 - Investigation of degradation of the aluminum current collector in lithium-ion batteries by GD-OES N2 - Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs. T2 - Empa Group Meeting CY - Dübendorf, Switzerland DA - 22.11.2022 KW - Lithium Ion Batteries KW - GD-OES KW - FIB KW - SEM KW - EDX PY - 2022 AN - OPUS4-56584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Nils T1 - A Journey From Formula Student to Research at BAM N2 - In this presentation, the battery and cell test center of BAM is introduced to the Berlin Motion Lab. Points of intersection are identified, and interested students are familiarized with BAM’s research priorities in the field of batteries. The aim is to foster interaction and to inspire young researchers to engage with technologically relevant topics. T2 - Berlin Deep Tech Nexus Meetup CY - Berlin, Germany DA - 26.02.2025 KW - Battery safety KW - BAM-academy KW - Qualification programme for PhD students at BAM KW - Advanced (battery) safety topics PY - 2025 AN - OPUS4-65079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Hajhariri, Aliasghar A1 - Sklorz, Christian A1 - Kriegsmann, Andreas A1 - Müller, Karsten T1 - A modular concept for protection against debris flight - Design, properties and usage N2 - With advances in technological development, stationary and mobile storage units for compressed hydrogen are becoming larger and larger. Their number is also increasing. At the same time, their design has evolved from steel and aluminium to pressure vessels made of composite materials. For safety reasons the design approval of those composite cylinders requires fire engulfment tests, which are mainly organised as open-air tests always needs dedicated protection measures. Under some conditions those protections measures even reduce the effort for organisational safety measures if e.g. the emission of splinters can get totally prevented. Another aspect is the improved reproducibility of fire tests by reducing the influence of wind. Between 2017 and 2019, BAM developed a stackable protective frame made of steel to safely capture splinters for the safe execution of high-energy impact tests. However, this frame was not flexible enough for the follow-up project, which led to a completely new protection concept for (potentially) destructive tests on gas-filled pressure vessels. This concept is based on very robust building blocks made from welded steel. Despite their considerable weight of around 500 kg p.p., they can be combined and stacked very easily like ‘Lego bricks’. The presentation will show the flexibility of the concept, some results of tests on the robustness against pressure waves and the effectiveness in wind attenuation. Finally, the interaction with a new, also modular burner concept for localised fires and full engulfment fires will be presented. T2 - 11th International conference on hydrogen safety (ICHS 2025) CY - Seoul, Republic of Korea DA - 22.09.2025 KW - Splinter protection KW - Pressure vessel testing KW - Fire engulfment KW - Destructive tests KW - Rupture KW - Gaseous tests KW - Pressure wave KW - Test equipment KW - Precaution measures PY - 2025 SN - 979-1-2243-0274-2 VL - 2025 SP - 1428 EP - 1439 AN - OPUS4-65100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - Welcome to BAM and the Competence Centre H2Safety@BAM N2 - The presentation starts with general slides on BAM, its mission and focus areas. It provides the fields of activity in the focus area “Energy” and explains the structure of the competence Centre and its focus on building trust in hydrogen. The next part shows the H2Safety@BAM’s Products“ in a nutshell and explains the main items with deep dives on the Living Lab “Hydrogen Networks”, the Living Lab „Hydrogen Refuelling Station“, on Reference Materials and Procedures, Storage of Liquid Hydrogen, Storage Systems for Compressed Gases and Material Compatibility. T2 - Information Tour at the Invitation of the Federal Foreign Office The Hydrogen Economy in Germany CY - Berlin, Germany DA - 05.11.2025 KW - Living Lab “Hydrogen Networks” KW - Living Lab „Hydrogen Refueling Station“ KW - Reference Materials and Procedures KW - Storage of Liquid Hydrogen KW - Storage Systems for Compressed Gases KW - Material Compatibility PY - 2025 AN - OPUS4-65101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sterr, Andrea A1 - Schwarz, Irina T1 - Valorization of Carbon Dioxide by Electrocatalytic Reduction Coupled to Acetogens via Multiple Electron Carriers (Ecat-Acetogens II) N2 - A Bioelectrochemical approach for reducing CO2 to fuels or value-added chemicals allows overcoming the limitations of a pure biochemical or electrochemical approach. A Bioelectrochemical system (BES) for this application has been developed in cooperation with TUM in the first project phase. BAM's contribution to the research focuses on the electrochemical side of the setup, mainly on the development of a suitable CO2RR catalyst for reducing CO2 to CO, which is then consumed by actogenic bacteria to produce further products. Single-metal-atom catalysts in a nitrogen-doped carbon matrix (M-N-Cs) are a promising, sustainable alternative to expensive rare-metal catalysts like Ag and Au. In this work, the first-generation catalyst, a ZIF-8-based Co-N-C is compared to a Mg salt mix templated Ni-N-C. In the new catalysts, the activity for CO2RR as well as the stability during BES operation could be enhanced. T2 - E-Biocat Statusupdate 2025 CY - Karlsruhe, Germany DA - 01.04.2025 KW - CO2RR KW - M-N-Cs KW - Bioelectrochemical System PY - 2025 AN - OPUS4-65143 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - DE-JP Hydrogen Safety Cooperation - Contribution of H2Safety@BAM N2 - The presentation starts with general slides on BAM, its location, mission, tasks and focus areas. It provides the fields of activity in the focus area “Energy” and explains the structure of the competence Centre and its focus on building trust in hydrogen. The test sides at TTS on hydrogen are explained in combination with the H2Safety@BAM’s products in a nutshell. Then the major H2-applications of H2Safety@BAM are explained by deep dives on the Living Lab “Hydrogen Networks”, the Living Lab „Hydrogen Refuelling Station“, on Explosion Protection, on Reference Materials and Procedures, on Material Compatibility, on Storage Systems for Compressed Gases and Storage of Liquid Hydrogen as well as on the Training and Further Education. The presentation ends with an overview about our international work on H2Safe-Collaboration. T2 - KICK-OFF WORKSHOP: JAPANESE-GERMAN COOPERATION ON H2 SAFETY CY - Online meeting DA - 15.12.2025 KW - Living Lab KW - Hydrogen Networks KW - Hydrogen Refuelling Station KW - Explosion Protection KW - Material Compatibility KW - Liquid Hydrogen KW - Compressed Gases PY - 2025 AN - OPUS4-65151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghaznavi, Ali T1 - Machine Learning Approach for Robust Acoustic Emission-Based Damage Classification in Pressure Vessels N2 - Accurate damage classification of Composite Pressure Vessels (CPVs) is crucial for understanding failure behaviour of hydrogen storage systems. Acoustic Emission (AE) monitoring is a non-destructive testing technique capable of detecting signals from different failure mechanisms such as fiber breakage and matrix cracking, supporting durability assessment of CPVs. Therefore, the main objective of this study is to combine AE and advanced deep learning techniques to develop a robust framework for automatic and accurate identification and classification of damage mechanisms across various CPVs. The evolutionary Genetic Algorithms (GA) was used for feature selection, followed by unsupervised clustering to generate automatic labels for model training. Two different FCNN and CNN-LSTM architectures were used to train individual models based on different AE datasets. Later, Adaptive Transfer Learning (ATL) and Meta Ensemble Learning (MEL) techniques were applied to handle data variability and train predictive generalized model over varied AE datasets. The ATL fine-tunes a pre-trained models to leverage their knowledge, while MEL uses pre-trained models' predictions as meta features to train a meta model. Experimental results demonstrate that while both generalized ATL and MEL trained models perform well across different AE datasets, the MEL framework outperforms ATL method in terms of evaluation metrics. The Mean-Accuracy score reaches 0.9026, and 0.9900 for ATL, and MEL, respectively. The most accurate multi-class classification results was achieved using MEL method in terms of the Mean-Accuracy and Recall metrics. The proposed framework provides a scalable, adaptive approach for automated damage classification using AE signals across diverse CPVs in real-world settings. T2 - BAM Colloquium Abteilung 3 CY - Berlin, Germany DA - 14.10.2025 KW - Acoustic Emission KW - Machine Learning KW - Sequential Neural Network KW - Deep Learning KW - Deep Neural Network PY - 2025 AN - OPUS4-65184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popiela, Bartosz A1 - Günzel, Stephan A1 - Mair, Georg W. T1 - Discussion of creep phenomena during initial loading of type 4 composite pressure vessels N2 - To maintain the highest safety standards for compressed gas storage in composite pressure vessels, a deeper understanding of their ageing mechanism is required. In this study, two designs of type 4 cylinders were manufactured the only difference being the internal pressure function used during the filament winding process. Hence, their residual stress state and the quality of the composite layers varied. Ten pressure vessels were initially loaded under sustained pressure and increased temperature and later subjected to slow burst tests. Comparing the results with cylinders tested in a pristine state underlines a significant improvement in the performance of initially loaded cylinders of one of the designs. This phenomenon was caused by a significant decrease of the scattering of burst pressures within a sample. At the same time, a slight decrease of the burst pressures could be observed. An explanation of this behavior could be supported by strain measurements with fiber optic sensors, which were embedded in the composite material. The strains measured during the initial loading indicate a stress redistribution, which has an impact on the strength of the pressure vessel. Moreover, an increased stiffness during the slow burst tests after initial loading was observed that indicates a better exploitation of the individual layers of the composite structure. The study supports previous observations on the increased performance after initial loading and provides new insights into the strain development in creep effects in type 4 pressure vessels. T2 - Pressure Vessels & Piping Conference PVP2025 CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Type 4 pressure vessel KW - Creep KW - Fiber optic sensors KW - Slow burst test KW - Mechanics of composites PY - 2025 SN - 978-0-7918-8907-7 VL - 2025 SP - 1 EP - 7 PB - ASME AN - OPUS4-63897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Castells-Gil, Javier A1 - Zhu, Jinjie A1 - Itskou, Ioanna A1 - Wolpert, Emma H. A1 - Hunter, Robert D. A1 - Tidey, Jeremiah P. A1 - Pedersen, Angus A1 - Solvay, Elisa A1 - Tyrrell, Helen A1 - Petit, Camille A1 - Barrio, Jesús T1 - Impact of N-heterocyclic amine modulators on the structure and thermal conversion of a zeolitic imidazole framework N2 - The zeolitic imidazole framework-8 (ZIF-8) is a crystalline porous material that has been widely employed as template to fabricate porous nitrogen-doped carbons with high microporosity via thermal treatment at high temperatures. The properties of the carbon scaffold are influenced by the pore structure and chemical composition of the parent ZIF. However, the narrow pore size distribution and microporous nature from ZIF-8 often results in low mesopore volume, which is crucial for applications such as energy storage and conversion. Here we show that insertion of N-heterocyclic amines can disrupt the structure of ZIF-8 and dramatically impact the chemical composition and pore structure of the nitrogen-doped carbon frameworks obtained after high-temperature pyrolysis. Melamine and 2,4,6-triaminopyrimidine were chosen to modify the ZIF-8 structure owing to their capability to both coordinate metal ions and establish supramolecular interactions. Employing a wide variety of physical characterization techniques we observed that melamine results in the formation of a mixed-phase material comprising ZIF-8, Zn(Ac)6(Mel)2 and crystallized melamine, while 2,4,6-triaminopyrimidine induces the formation of defects, altering the pore structure. Furthermore, the absence of heterocyclic amine in the ZIF-8 synthesis leads to a new crystalline phase, unreported to date. The thermal conversion of the modified ZIFs at 1000 °C leads to nitrogen-doped carbons bearing Zn moieties with increased surface area, mesopore volume and varying degree of defects compared to ZIF-8 derived carbon. This work therefore highlights both the versatility of heterocyclic amines to modify the structure of framework materials as well as their role in tuning pore structure in nitrogen-doped carbons, paving the way to targeted design of high-performance electrodes for energy storage and conversion. KW - Zeolitic imidazole framework KW - Heterocyclic amine KW - Triaminopyrimidine PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-639177 DO - https://doi.org/10.1039/D5TA04831A SN - 2050-7488 SP - 1 EP - 13 PB - Royal Society of Chemistry (RSC) AN - OPUS4-63917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braga, Daniel S. A1 - Pedersen, Angus A1 - Riyaz, Mohd A1 - Barrio, Jesús A1 - Bagger, Alexander A1 - Neckel, Itamar T. A1 - Mariano, Thiago M. A1 - Winkler, Manuel E. G. A1 - Stephens, Ifan E. L. A1 - Titirici, Maria‐Magdalena A1 - Nagao, Raphael T1 - In situ structural evolution and activity descriptor of atomically dispersed catalysts during nitrate electroreduction N2 - Single‐Atom Catalysts (SAC) have emerged as a promising class of materials for various catalytic applications, including the electrochemical nitrate reduction reaction (eNO3RR) and consequently ammonia production. While the efficiency and selectivity of these materials have been extensively highlighted for the eNO3RR, the in situ evolution to their structure and composition during electrocatalysis is largely unexplored and lacks catalyst design principles. To solve this, we investigated a series of high utilization metal‐nitrogen‐carbon (MNC) SACs (M = Cr, Fe, Co, Ni, and Cu) for eNO3RR. Except for CuNC, which selectively produced nitrite, all catalysts exhibited Faradaic efficiencies (FE) for ammonia exceeding 50%. NiNC demonstrated the highest performance (FE of 78.0 ± 2.9% at −0.4 V versus reversible hydrogen electrode (RHE) at pH 13 and maximum ammonia production rate of 615.7 ± 176.5 µmol·h−1·, corresponding to an energy efficiency of 15.1 ± 1.4% at −0.6 VRHE), followed by CoNC. In situ Synchrotron X‐ray fluorescence (SXRF) mapping at various cathodic potentials (from open circuit potential to 0.0 VRHE and then −0.6 VRHE at 100 mV steps) revealed significant mobility of Ni within the carbon matrix, leading to the formation of metallic clusters from 0.0 VRHE. Similar in situ metal clustering is observed for CoNC. Structure‐activity plots are generated from both MNC literature and results obtained here, finding a clear trend between OH binding energy and turnover frequency, with the high activity of NiNC and CoNC in this work explained by their stronger OH binding in the metallic structure compared to their SAC coordination. This work therefore, reveals the structure‐activity‐stability of MNCs for eNO3RR and provides a simple descriptor for identifying highly active eNO3RR catalysts and their in situ structural evolution. KW - Single atom KW - Nitrate reduction KW - Structure-activity-selectivity KW - In situ PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640353 DO - https://doi.org/10.1002/advs.202510282 SN - 2198-3844 VL - 12 IS - 39 SP - 1 EP - 14 PB - Wiley-VCH CY - Weinheim AN - OPUS4-64035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Kriegsmann, Andreas T1 - Distributed Fibre Optic Monitoring of Hydrogen Storage Composite Pressure Vessels for Automotive Use N2 - We present our research work on the condition monitoring of hydrogen storage composite pressure vessels using distributed fibre optic sensors. The sensing fibres are integrated into the composite structure by wrapping them over the polymer liner in the helical and circumferential direction during the manufacturing process of the carbon fibre reinforced polymer. The following use of optical backscatter reflectometry allows for continuous condition monitoring and precise detection and localization of structural damages during the entire service life. To account for the time-dependent strength degradation of the composite pressure vessels, both slow burst and ambient hydraulic cycling tests, respectively, were conducted on five 70 MPa pressure vessels with integrated fibre optic sensors. The results achieved via distributed fibre optic strain sensing demonstrate a near linear strain response to pressure suitable for sensitive condition monitoring and confirm the required robustness of the selected sensor solution. T2 - DGZfP-Jahrestagung 2025 CY - Berlin, Germany DA - 26.05.2025 KW - Distributed fibre optic sensor (DFOS) KW - Composite pressure vessel KW - Optical backscatter reflectometry KW - Slow burst test KW - Ambient hydraulic cycling test PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653067 DO - https://doi.org/10.58286/32344 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-65306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sauermoser-Yri, M. A1 - Veldurthi, N. A1 - Wölfle, C. H. A1 - Svartvatn, P. J. A1 - Flo Hoem, S. O. A1 - Lid, M. J. A1 - Bock, Robert A1 - Palko, J. A1 - Torgersen, J. T1 - On the porosity-dependent permeability and conductivity of triply periodic minimal surface based porous media N2 - With the fast development in the field of additive manufacturing, triply periodic minimal surface (TPMS) based porous media have recently found many uses in mechanical property tuning. However, there is still a lack of understanding in their porosity-dependent permeability and electrical as well as thermal conductivity. Here, we perform finite volume simulations on the solid and void domains of the Schoen gyroid (SG), Schwarz primitive (SP) and Schwarz primitive beam (SPB) TPMS with porosities between 63% and 88% in Ansys Fluent. A simple cubic lattice (CL) of equivalent porosity served as reference. The SPB and CL showed up to one order of magnitude higher permeabilities than the SG and SP. However, SG and SP have about 1.3 and 2.6 times the electrical and thermal conductivity of SPB and CL, respectively. Furthermore, the properties of SPB and CL are largely affected by the surface area density, whereas tortuosity variation does not impact permeability and conductivity to a major extent. Finally, empirical relations are adapted to describe the presented data and thus, they may enable future designers of TPMS based porous structures to fine-tune the geometries according to the requirements on permeability and electrical as well as thermal conductivity. KW - Metals and Alloys KW - Surfaces, Coatings and Films KW - Biomaterials KW - Ceramics and Composites PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-585250 DO - https://doi.org/10.1016/j.jmrt.2023.09.242 SN - 2238-7854 VL - 27 SP - 585 EP - 599 PB - Elsevier B.V. AN - OPUS4-58525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -