TY - CONF A1 - Grimault de Freitas, Tomás T1 - Comprehensive Standardisation of the Hollow Specimen Technique for Tests in High-Pressure Hydrogen Gas N2 - The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations and complement the current techniques for qualifying metallic materials under highpressure hydrogen gas. In this technique, an axial hole is manufactured in a tensile specimen, which is then filled with hydrogen gas, sealed, and placed in a standard testing machine. This method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and does not require complex equipment or a specialised laboratory, unlike the conventional autoclave technique. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of the committee ISO/TC 164/SC 1/WG 9 to standardise the method, however, there are still open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions are being addressed in the H2HohlZug project, which is presented in this contribution. T2 - Oxford - EPRI Hydrogen Embrittlement Workshop CY - Oxford, United Kingdom DA - 23.06.2024 KW - Hollow Specimen Technique KW - High-pressure Gaseous Hydrogen KW - Hydrogen Embrittlement KW - Tensile Testing PY - 2024 AN - OPUS4-60501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Junias, Josua Kondja T1 - Prediction of Explosion Characteristics of Hydrogen Mixtures Using Machine Learning Models N2 - An understanding of Hydrogen-Oxygen/Air-Diluents gas mixtures combustion characteristics and their accurate prediction is crucial for ensuring the safety of hydrogen-related applications, reducing accidents risk, and protecting lives and property. Hydrogen detonation propagations are characterized by the detonation cell size, used to quantitatively predict for a mixture to detonate including, among others, the initiation energy, critical and minimum tube diameters. For the prediction of explosion limits, detonation run-up-distances and cell sizes, various empirical, semi-empirical and numerical models can be found in literature. These models are usually limited to a narrow range of explosion process or geometrical experimental parameters. Moreover, based on the limited availability of the detonation cell widths measurements, current estimation models are seemingly inaccurate. Machine learning models can be utilized to make justifiable prediction on the detonation cell sizes of hydrogen-air mixtures and other gaseous explosive mixtures cell sizes, explosion limits or run-up distance to detonation based on the mixture type, temperature, pressure, equivalence ratios as well as on geometrical parameters with consideration of highly diverse experimental data measurements uncertainties. Therefore, an up-to date database for explosion characteristics will be established and machine learning models will be developed, trained, tested, and validated using experimental data to predict explosion characteristics of hydrogen mixtures. The models predicted results will be validated against existing models. It will be tested whether machine learning models are able to predict the explosion characteristics of hydrogen mixtures with better accuracy and more comprehensively than conventional empirical and numerical models to be found in literature. T2 - Combustion Institute 40th International Symposium CY - Milano, Italy DA - 21.07. 2024 KW - Prediction, detonation KW - Machine Learning KW - Flammability limits PY - 2024 AN - OPUS4-60769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - Evolution of tensile testing methodologies for hydrogen embrittlement in austenitic steels: a comparative study N2 - The energy transition towards hydrogen utilisation has increased the demand for reliable testing methods to evaluate the susceptibility of metallic materials to hydrogen degradation. However, traditional electrochemical pre-charging techniques have limitations in represent-ing realistic gaseous hydrogen exposure conditions. This study presents three comparative analyses of tensile testing methodologies, focusing on the differences between electrochem-ical pre-charging, gaseous pre-charging, and in-situ testing using hollow specimens for aus-tenitic steels AISI 304L and 316L type austenitic steels. Based on the results obtained, the first comparison reveals that electrochemically pre-charged and gaseously pre-charged specimens exhibit different behaviours regarding the impact on the mechanical properties. This effect can be retraced to the varying distribution of hydrogen throughout the specimens. Although comparable embrittlement was observed for similar hydrogen concentrations, the relationship appears to be non-systematic. The second comparison evaluates the performance of pre-charged hollow specimens (300°C, 100 bar, 21 days) in comparison to hollow specimens tested in-situ under 200 bar hydrogen during slow strain rate tensile tests (SSRT). While pre-charged specimens show a slight de-crease in elongation at fracture and a noticeable decrease in reduction of area (RA), in-situ tested specimens exhibit significantly more pronounced embrittlement. This is in accord-ance with the results of Michler et. al. In the third comparison, geometry effects between pre-charged conventional and pre-charged hollow specimens are explored. In this case, the hydrogen effect appears to be of the same order of magnitude for both specimen types, although some differences are ob-served. The study's findings underscore the importance of considering differences between test methods when assessing materials’ compatibility with hydrogen. It specifically emphasises the need for in-situ testing with gaseous hydrogen to better represent real conditions in ap-plications within the hydrogen sector. Furthermore, the study provides an initial compari-son between conventional and hollow specimens, demonstrating their capability to reveal hydrogen effects. However, additional research is essential to enhance the comparability of results yielded by these testing methods. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Hollow Specimen Technique KW - Hydrogen KW - Austenitic Stainless Steel KW - Hydrogen Testing KW - AISI 316L PY - 2024 AN - OPUS4-60929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan T1 - The relationship between surface condition and the influence of hydrogen on the mechanical properties of additively manufactured 316L N2 - The following contribution presents the analyses of additively manufactured (AM) 316L using hollow specimens at 200 bar hydrogen and a strain rate of 1E-5 s-1. The work includes a comparison of three types of hollow specimens: mechanically extracted from fully additively manufactured cylinders, near-net-shape additively manufactured specimens, i.e. as printed, and specimens made of conventional 316L. AM specimens were manufactured via powder bed fusion with laser beam of metals (PBF-LB/M). For the near-net-shape specimens the inner hole remained without any mechanical processing. The inner holes of the cylindric specimens were manufactured by drilling with subsequent honing. The susceptibility to hydrogen embrittlement was found to be strongly dependent on the surface being in contact with hydrogen. While specimens with a clean surface had a relative reduction of area (RRA) of around 78 %, those with an as-printed surface showed a significantly larger RRA of around 90 %. One possible reason for this are oxide layers formed due to small amounts of oxygen during the AM-process. Further research is required to determine if the lower effect on the mechanical properties is permanently for as printed parts or e.g. time dependent. Additionally, further work with variation in the nominal strain rate is required. T2 - IIW 77th Annual Assembly 2024 CY - Rhodes, Greece DA - 07.07.2024 KW - Austenitic steel 316L KW - Additive manufacturing KW - PBF-LB/M KW - Hydrogen degradation KW - Hydrogen embrittlement KW - Hollow specimen technique PY - 2024 AN - OPUS4-60618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bock, Robert A1 - Mair, Georg W. T1 - Pilotprojekt "Verlässliche Wasserstofftechnologie" - Beispielanwendung für eine technische Anlage N2 - Kurzvorstellung des Pilotprojektes Verlässliche Wasserstofftechnologie in QI Digital. Anwendung der QI Digital Werkzeuge an einer technischen Anlage beispielhaft gezeigt anhand von sechs im Projekt entwickelten Demonstratoren. Unser erklärtes Ziel ist die Unterstützung des Markthochlaufs von Wasserstofftechnologien durch Digitalisierung der QI. Bei der Qualitätsinfrastruktur von technischen Anlagen geht es vor allem die Themen QI Dokumentation und Zugänglichkeit, Verfügbarkeit der Anlage und Informationen darüber, sowie Inspektionszyklen mit zeitaufwändigen und teuren manuellen Prüfungen. Mit dem Übergang zu einer digitalen QI streben wir hier an, eine kontinuierliche Überwachung des momentanen Gesundheitszustandes der Anlage und automatisierter Dokumentation hierüber, die fälschungssicher und vertraulich zugänglich gemacht werden kann, zu erreichen. Hierzu sollen die im Gesamtprojekt entwickelten QI Digital Werkzeuge zum Einsatz kommen. T2 - QI Forum 2024 CY - Berlin, Germany DA - 09.10.2024 KW - Wasserstoff KW - Qualitätsinfrastruktur KW - Digitalisierung PY - 2024 AN - OPUS4-61354 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hörmann, Anja Franziska T1 - (Grazing Incidence) Small-angle X-ray Scattering for STOP N2 - We remind project partners of the principles of SAXS, GISAXS and X-ray reflectivity and their applicability to the antimicrobial particles and coatings developed within the STOP project. T2 - M25 project meeting: Surface Transfer of Pathogens (STOP) CY - Bucharest, Romania DA - 19.09.2024 KW - X-ray Scattering KW - Nanomaterial PY - 2024 AN - OPUS4-62774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hajhariri, Aliasghar A1 - Eberwein, Robert A1 - Perrone, Luca Pakj A1 - Cozzani, Valerio A1 - Otremba, Frank A1 - Seidlitz, Holger T1 - Study the impact of spacer at thermal degradation process of MLI-based insulation in fire condition N2 - To reduce CO2 emissions, energy carriers such as hydrogen are considered to be a solution. Consumption of hydrogen as a fuel meets several limitations such as its low volumetric energy density in gas phase. To tackle this problem, storage as well as transportation in liquified phase is recommended. To be able to handle this component in liquid phase, an efficient thermal insulation e.g., MLI insulation is required. Different studies have been addressed the vulnerability of such insulation against high thermal loads e.g., in an accident engaging fire. Some of research works have highlighted the importance of considering the MLI thermal degradation focusing on its reflective layer. However, limited number of studies addressed the thermal degradation of spacer material and its effect on the overall heat flux. In this study, through systematic experimental measurements, the effect of thermal loads on glass fleece, glass paper as well as polyester spacers are investigated. The results are reported in various temperature and heat flux profiles. Interpreting the temperature profiles revealed that, as the number of spacers in the medium increases, the peak temperature detectable by the temperature sensor on the measurement plate decreases. Each individual spacer contributes to mitigating the radiative energy received by the measurement plate. Stacks of 20–50 spacers (this is the number of layers in commercial MLI systems applied for liquid hydrogen applications) can potentially reduce the thermal radiation by 1–2 orders of magnitude. An empirical correlation to predict a heat flux attenuation factor is proposed, which is useful for further numerical and analytical studies in the temperature range from ambient to 300 ◦C. KW - Cryogenic KW - Liquid Hydrogen KW - Multi-Layer Insultation KW - Heat Transfer KW - Hydrogen Storage Safety PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-614919 DO - https://doi.org/10.1016/j.jlp.2024.105461 SN - 0950-4230 VL - 92 SP - 1 EP - 7 PB - Elsevier Ltd. AN - OPUS4-61491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effect of temperature on the friction behaviour of rubber materials in hydrogen N2 - Safety and reliability are the major challenges to face for the development and acceptance of hydrogen technology. It is therefore crucial to study deeply material compatibility, in particular for tribological components that are directly in contact with hydrogen. Some of the most critical parts are sealing components that face high risk of damage due variation of pressure, temperature and mechanical stress. In this study, the friction and wear behaviour of several rubber materials was evaluated in hydrogen environment at ambient and low temperature. Tests were performed against 316L disks in a reciprocation motion. Results reveal that the hydrogen affects the friction and wear behaviour of most materials. The friction mechanism is dominated by deformation for most rubber materials at ambient temperature while sliding occurs at low temperature due to the increased hardness of the rubbers. T2 - Polytrib 2024 CY - Portorož, Slovenia DA - 03.10.2024 KW - Reciprocating sliding KW - Rubber materials KW - Hydrogen KW - Low temperature PY - 2024 AN - OPUS4-62019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Harmonised tribological testing of polymers in hydrogen N2 - The focus of this work is to study the tribological performance of polymers in hydrogen atmosphere. Additionally, tests were carried out with up to three different tribometers at two institutions. The challenge to compare and harmonise equipment, procedures, and methods is an important part of the study. T2 - PolyTrib 2024 CY - Portoroz, Slovenia DA - 03.10.2024 KW - Hydrogen KW - Tribometer KW - Comparability KW - Harmonisation KW - Oil-coupled compounds PY - 2024 AN - OPUS4-61224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Camplese, Davide A1 - Scarponi, Giordano Emrys A1 - Eberwein, Robert A1 - Hajhariri, Aliasghar A1 - Otremba, Frank A1 - Cozzani, Valerio T1 - Modelling Fire Response of Cryogenic Liquid Hydrogen Tanks Equipped with Multilayer Insulation (MLI) Systems N2 - In the context of the growing global interest in hydrogen-based green energy, cryogenic tanks equipped with multi-layer insulation (MLI) are emerging as a leading solution for storing hydrogen in vehicles. The integrity of these systems might be threatened during fire exposure. This can trigger the degradation of the MLI materials and induce rapid pressurization of the tank with a high risk of catastrophic failure. In this work, a novel lumped model to simulate the thermal response of MLI-equipped cryogenic liquid hydrogen tanks is presented. The model integrates the accurate database “Coolprop” for hydrogen thermodynamic properties and sub-models for detailed simulation of MLI degradation, providing a realistic simulation of the experimental data obtained under normal operating conditions. The application of the model to several case studies considering different numbers of MLI layers and tank geometries demonstrates that aluminum-based MLI offers scarce protection in case of exposure to a hydrocarbon poolfire. T2 - CISAP 11 CY - Neapel, Italy DA - 15.09.2024 KW - LH2 KW - LNG KW - Cryogenic storage tank KW - Insulation KW - MLI PY - 2024 DO - https://doi.org/10.3303/CET24111076 SN - 2283-9216 VL - 111 SP - 451 EP - 456 PB - AIDIC The Italian Association of Chemical Engineering AN - OPUS4-61384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Camplese, Davide T1 - Modelling Fire Response of Cryogenic Liquid Hydrogen Tanks Equipped with Multilayer Insulation (MLI) Systems N2 - In the context of the growing global interest in hydrogen-based green energy, cryogenic tanks equipped with multi-layer insulation (MLI) are emerging as a leading solution for storing hydrogen in vehicles. The integrity of these systems might be threatened during fire exposure. This can trigger the degradation of the MLI materials and induce rapid pressurization of the tank with a high risk of catastrophic failure. In this work, a novel lumped model to simulate the thermal response of MLI-equipped cryogenic liquid hydrogen tanks is presented. The model integrates the accurate database “Coolprop” for hydrogen thermodynamic properties and sub-models for detailed simulation of MLI degradation, providing a realistic simulation of the experimental data obtained under normal operating conditions. The application of the model to several case studies considering different numbers of MLI layers and tank geometries demonstrates that aluminum-based MLI offers scarce protection in case of exposure to a hydrocarbon poolfire. T2 - CISAP 11 CY - Neapel, Italy DA - 15.09.2024 KW - Liquefied hydrogen KW - LNG KW - Fire KW - Insulation KW - MLI PY - 2024 AN - OPUS4-61389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Harwege, Finn T1 - Characterisation of vacuum insulation panel based cryogenic insulation N2 - Current medium to large scale hydrogen storage tanks utilize a double walled tank with vacuum and a low thermal conductivity powder as bulk fill between the two tank walls. This approach offers poor failure resistance and is not economic to build at a large scale. In NICOLHy an alternative cryogenic insulation concept using vacuum insulation panels (VIP) targeted for tanks with capacities from 40 000 m³ to 100 000 m³ is in research. VIPs consist of a gas tight envelope that surrounds a low conductivity core material. Within the envelope, a vacuum is created, which supresses convective heat transfer. Since the core material is typically very low thermal conductivity, while the envelope material has a relatively high thermal conductivity, thermal bridges where two adjoining panels meet cannot be avoided. Modeling of the thermal behaviour of VIPs exists for the building industry, but not for cryogenic temperatures or applications with multiple layers of VIPs, both of which present a new challenge. Here, these challenges and goals for the thermal modeling within the project are presented, alongside an overview over the project itself. T2 - Themenvorstellung beim BTU Arbeitsgebiet Technische Akustik CY - Cottbus, Germany DA - 23.09.2024 KW - Liquefied Hydrogen PY - 2024 AN - OPUS4-61122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thünemann, Andreas T1 - Structure Analysis of Functional Hydrogels with Small-Angle X-ray Scattering (SAXS) N2 - Hydrogel properties are largely determined by their network structure. Here, we report on the capabilities of SAXS methods for characterizing polymer-network gels. SAXS provides rich insight into different types and levels of nanostructural inhomogeneities in these soft matter materials. The structure analysis of alginate hydrogels, typically utilized in tissue engineering applications, will be discussed in detail. T2 - Polydays 2024 CY - Berlin, Germany DA - 30.09.2024 KW - SAXS KW - Small-angle X-ray scattering KW - Polymer KW - Gel PY - 2024 AN - OPUS4-61184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai T1 - Sicherheit von Wasserstoff und Wasserstofftechnologien N2 - Der Nationale Wasserstoffrat (NWR) hat in einem Online-Seminar das Thema Sicherheit von Wasserstofftechnologien und aktueller Sachstand bzw. Herausforderungen in Deutschland aufgearbeitet. Dazu wurde ein Behördenvertreter (BAM), zwei Forschungsinstitutionen (FzJ und FhG IWM) sowie eine benannte Stelle (TÜV) eingeladen und die vorgestellten Themen in einem offenen Plenum diskutiert. T2 - Online-Seminar des Nationalen Wasserstoffrats CY - Online meeting DA - 07.06.2024 KW - Wasserstoff KW - Sicherheit KW - Herausforderungen KW - Elektrolyse KW - Dichtungswerkstoffe KW - Sicherheitsabstände KW - Reallabor BAM TTS KW - Nationale Allianz Wasserstoff-Sicherheit PY - 2024 AN - OPUS4-61483 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Anita T1 - Irrungen, Wirrungen und Lichtblicke - Überarbeitung des Gefahrguttransportrechts für Lithium- und Natrium-Ionen-Batterien N2 - Die Überarbeitung des Gefahrgutrechts hinsichtlich der Einstufung von Lithium- und Natrium - Ionen Batterien nach Gefährlichkeit trägt so einige Stilblüten - wie zuletzt den Vorschlag von 135 neuen UN Nummern für Lithiumbatterien. Die BAM trägt mit ihrer Kompetenz aus eigenen Untersuchungen und Forschung dazu bei, dass die deutsche Delegation bei den Vereinten Nationen, wo die Regelwerke weiterentwickelt werden, gezielte Vorschläge einbringen kann. Der Artikel beschreibt die aktuellen Entwicklungen. KW - Lithiumbatterien KW - Gefahrguttransport KW - Regelwerksentwicklung PY - 2024 VL - 2024 IS - 6 SP - 29 EP - 32 PB - Verkehrs-Verlag J. Fischer GmbH & Co. KG CY - Düsseldorf AN - OPUS4-62334 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mair, Georg W. A1 - Günzel, Stephan A1 - Saul, Herbert A1 - Bock, Robert T1 - Die volumenabhängige Druckbegrenzung als Maßnahme zur Konsequenzsteuerung im Wasserstofftransport N2 - Mit der technologischen Entwicklung werden auch die Transporteinheiten für Druckgase größer und die zu transportierenden Gase wie Wasserstoff deutlich über die lange als Standard geltenden 200 bar hinaus komprimiert. Damit steigt das Konsequenzpotenzial eines Zwischenfalls, das nun begrenzt werden soll, um die bisherige Praxis mit wenigen Zwischenfällen von den Maßnahmen für die neuen Entwicklungen extrem großer Transportdruckbehälter abgrenzen zu können. Hierzu wurde – ausgehend von einer technologisch und sicherheitstechnisch störenden Begrenzung des Volumens von Bergungsdruckgefäßen – das sogenannte Druck-Volumen-Produkt als Kenngröße und Konsequenzmaß vorgeschlagen. Um eine breit akzeptierte Abgrenzung der heute etablierten Druckgefäße gegenüber den zukünftigen Einheiten mit noch mehr Gasinhalt erarbeiten zu können, wurde eine Arbeitsgruppe bei den Vereinten Nationen eingerichtet, deren Weg zu ihrem Ergebnis „Einführung einer Obergrenze von 1.5 Mio. bar-Liter für das Druck-Volumen-Produkt von Druckgefäßen“ mit den Wasserstoff- spezifischen Einzelschritten „Grenze zwischen Großunfall und Katastrophe“, „Die Wirkung von Druckwellen auf den menschlichen Körper“, „Die Ausbreitung von Druckwellen“, „Der Referenzwert für die Bevölkerungsdichte“ und „Die Druckwellenberechnung“ hier dargestellt ist. Dieses Ergebnis der UN-Arbeitsgruppe wird bis 2027 zu einer verbindlichen Begrenzung des Druckvolumenproduktes in Druckgefäßen führen. KW - Risikosteuerung KW - Druck-Volumen-Produkt KW - Katastrophe KW - Bevölkerungsdichte KW - Druckwelle PY - 2024 SN - 2191-0073 VL - 14 IS - 05-06 SP - 8 EP - 17 PB - VDI Fachmedien GmbH & Co. KG CY - Düsseldorf AN - OPUS4-64309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Keßler, S. A1 - Gluth, Gregor ED - Lothenbach, B. ED - Wieland, E. ED - Altmaier, M. T1 - Influence of salt aggregate on the degradation of hybrid alkaline cement (HAC) concretes in magnesium chloride-rich saline solution simulating evaporite rock N2 - Concretes produced from salt aggregate and hybrid alkaline cements, an alkali-activated slag/fly ash blend, or a Portland cement were exposed to a magnesium chloride-rich saline solution ([Mg2+] = 3.6 m, [Cl−] = 8.3 m), representing a solution formed after contact of surface water with evaporite rock (rock salt) in a nuclear waste repository. The hydration and deterioration of the concretes were studied with X-ray diffraction, thermogravimetric analysis, pH mapping and permeability measurements. The results show that calcium silicate hydrate (C-S-H) or sodium-substituted calcium aluminium silicate hydrate (C-N-A-S-H) and Friedel's salt were the major reaction products in the concretes prior to exposure to the saline solution. During exposure to the saline solution, increasing amounts of C-S-H/C-N-A-S-H dissolved, and gypsum and a secondary AFm phase formed. The durability of the concretes improved with increasing amounts of Portland clinker in the cements, due to the associated differences in permeability and chemical resistance. Nevertheless, a massive increase of permeability occurred for all concretes, likely caused by crack formation due to the formation of gypsum from anhydrite in the salt aggregate. Thus, the behavior of the concretes differed from, and was more complex than, the behavior of plain cement pastes. T2 - Joint 6th International Workshop on Mechanisms and Modelling of Waste/Cement Interactions (JCCW 2023) CY - Prague, Czech Republic DA - 20.11.2023 KW - Nuclear waste repository KW - Evaporite rock KW - Magnesium chloride brine KW - Concrete KW - Hybrid alkaline cement PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599928 DO - https://doi.org/10.1016/j.apgeochem.2024.106027 SN - 0883-2927 SN - 1872-9134 VL - 168 SP - 1 EP - 14 PB - Elsevier AN - OPUS4-59992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hajhariri, Aliasghar A1 - Eberwein, Robert A1 - Camplese, Davide A1 - Scarponi, Giordano Emrys A1 - Cozzani, Valerio A1 - Otremba, Frank A1 - Seidlitz, Holger T1 - Non-combustible MLI based insulation behavior under fire condition - Experimental and numerical investigation N2 - The number of applications that demand zero-emission energy carriers, such as liquified hydrogen (LH2), is increasing worldwide. LH2 is typically transported or stored under cryogenic conditions. Storage in such conditions requires super thermal insulations which maintain very low boil-off for a prolonged time. Multi-Layer insulation (MLI) finds widespread use in cryogenic applications, designed to effectively restrict heat inleak towards cryogenic fluids. However, recent studies evidenced that exposure to high heat fluxes, such as in the event of a fire accident, can cause the thermal degradation of the insulation material, resulting in the severe collapse of its heat resistance performance. Therefore, the risk of rapid tank pressurization and its connection to the risk of BLEVE may be possible. This study proposes a numerical model to assess the performances of aluminum-based MLI materials under fire conditions. The model offers insights into the total heat transfer rate through the insulation, serving as a KW - Multi-Layer Insulation KW - Cryogenic KW - Liquid Hydrogen KW - CFD PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-617780 DO - https://doi.org/10.1016/j.psep.2024.11.037 VL - 193 SP - 603 EP - 620 PB - Elsevier B.V. AN - OPUS4-61778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert A1 - Scarponi, Giordano Emrys A1 - Cozzani, Valerio A1 - Otremba, Frank T1 - Lh2 Tanks In Fire Incidents - The Cryogenic High Temperature Thermal Vacuum Chamber Enables In-Depth Insights N2 - Liquefied Hydrogen (LH2) and Liquefied Natural Gas (LNG) establish themselves as important energy carriers in the transport sector. Their storage requires tanks with thermal super-insulations to keep them at cryogenic conditions for a long time. These insulation systems have proven itself in various applications over a long time. However, these insulations are still new in land transportation, where accidents involving collisions, fires, and their combination are to be expected. This study summarizes the results of the ongoing research program in which insulations commonly used in industry were analysed through experimental and numerical studies under fire-like conditions. It was found that there are strong differences among the various insulation systems. Several safety concerns and research gaps exists for layered insulations, which are typically used in land transport. To further analyse these insulation systems, a new test concept called Cryogenic High Temperature Thermal Vacuum Chamber (CHTTVC) was developed and manufactured. This concept enables the testing of large insulation samples under industrial conditions and the consideration of cryogenic conditions relevant for the investigation of various phenomena. The results are important for the evaluation of accident scenarios, the improvement of thermal super-insulations, and the development of emergency measures. T2 - IMECE 2024 CY - Oregon, Portland, USA DA - 17.11.2024 KW - LH2 KW - LNG KW - Fire KW - Insulation KW - Safety PY - 2024 SN - 978-0-7918-8869-8 SP - 1 EP - 7 PB - ASME AN - OPUS4-61751 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert T1 - Tanks For The Large-Scale Transport And Storage Of Liquefied Hydrogen N2 - Hydrogen is seen as a potential energy source that enables us to achieve our climate targets. Hydrogen can be well integrated into the electrical energy infrastructure, and its production and use is free of direct GHG emissions. However, tanks are needed for worldwide storage and transportation, which need to be further developed and up-scaled. In the EU-funded NICOLHy project, BAM investigates a novel insulation concept based on Vacuum Insulation Panels (VIP) that enables the safe, cost- and energy-efficient storage of large quantities of LH2. Such large-scale LH2 storage technology is necessary to build tanks with capacities of 40.000 m³ to more than 200.000 m³ of LH2, as it is in application for LNG today. However, new design concepts are needed because the currently available technologies used in small and medium storages today are not suitable for up-scaling. The main problems prohibiting up-scaling are the long production time due to the process chain, the low failure tolerance, and the spherical shape of the tank, which reduces the payload in technical applications by up to 50% compared to other shapes. The novel concept will change these conditions by a system which is modular, open-form, time-and cost-efficient during production, operation and service, multi-failure tolerant and applicable for onshore and offshore applications. The NICOLHy consortium is ideally suited for this ambitious project. It brings together experts from the fields of thermodynamics, cryogenics, marine, chemistry, process, and safety engineering. Thereby, NICOLHy will accelerate the integration of hydrogen into the European energy economy and industry, which is necessary to be in line with the European Green Deal and to build trust of society in the policy and the technology. T2 - BAM Akademie H2 Safety - Colloquium CY - Berlin, Germany DA - 06.11.2024 KW - LH2 KW - Insulation KW - Liquefied Hydrogen KW - Tank PY - 2024 AN - OPUS4-61540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert T1 - LH2 Tanks In Fire Incidents - The Cryogenic High Temperature Thermal Vacuum Chamber Enables In-Depth Insights N2 - Liquefied Hydrogen (LH2) and Liquefied Natural Gas (LNG) establish themselves as important energy carriers in the transport sector. Their storage requires tanks with thermal super-insulations to keep them at cryogenic conditions for a long time. These insulation systems have proven itself in various applications over a long time. However, these insulations are still new in land transportation, where accidents involving collisions, fires, and their combination are to be expected. This study summarizes the results of the ongoing research program in which insulations commonly used in industry were analysed through experimental and numerical studies under fire-like conditions. It was found that there are strong differences among the various insulation systems. Several safety concerns and research gaps exists for layered insulations, which are typically used in land transport. To further analyse these insulation systems, a new test concept called Cryogenic High Temperature Thermal Vacuum Chamber (CHTTVC) was developed and manufactured. This concept enables the testing of large insulation samples under industrial conditions and the consideration of cryogenic conditions relevant for the investigation of various phenomena. The results are important for the evaluation of accident scenarios, the improvement of thermal super-insulations, and the development of emergency measures. T2 - IMECE 2024 CY - Portland, OR, USA DA - 17.11.2024 KW - LH2 KW - LNG KW - Fire KW - Insulation KW - Safety PY - 2024 AN - OPUS4-61752 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai T1 - National Alliance for Hydrogen Safety N2 - Hydrogen as an energy carrier offers the possibility of establishing a global and local CO2-neutral energy economy. The Hydrogen Clusters4Future bundle already existing expertise in the field of hydrogen technologies in and around Aachen with actors from Industry, Science and Society. All while considering the entire hydrogen life cycle – from production to storage and distribution to use. Safety is also an important issue and independant analysis on a national level is actually not possible in Germany. Other countries like the US and Canada established national safety alliances to offer support to companies and authorities. BAM, together with other independant institutes in Germany started to establish the National Alliance for Hydrogen Safety and presented this alliance to the community of the Hydrogen Clusters4Future. T2 - Aachen Hydrogen Colloquium CY - Aachen, Germany DA - 14.05.2024 KW - Hydrogen Safety KW - National Alliance KW - Networking PY - 2024 AN - OPUS4-61403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - An overview of tribology in gaseous Hydrogen N2 - In this presentation, an overview in gaseous hydrogen is given along with examples related to metal, coatings, polymers and rubbers materials. T2 - International Seminar, Hydrogen & Materials 2024 CY - Espoo, Finland DA - 06.06.2024 KW - Hydrogen KW - Friction KW - Wear KW - Materials PY - 2024 AN - OPUS4-61408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai T1 - Trust in Hydrogen Technologies - Safety Issues in the Hydrogen Value Chain N2 - In June 2020, updated in July 2023, the German government presented the National Hydrogen Strategy (NHS), its first strategy for achieving the goals of its hydrogen policy. The NHS sets out a coherent framework for action for the future production, transportation and use of hydrogen and its derivatives, including the corresponding research, innovations and investments. Various measures have been defined to achieve goals such as the decarbonization of various sectors and the market introduction of hydrogen technologies. This will ultimately lead to the introduction of many “new” technologies in many areas of our daily lives, which will only be successful if decision-makers and the public are convinced that these technologies are safe. Therefore, the safety of hydrogen technologies is an important pillar in gaining and maintaining confidence in these new technologies. Safety must keep pace with, or better still anticipate, trends in technological development in order to avoid overly conservative and expensive s T2 - 10th World Energy Congress (WEC 2024) CY - Singapore DA - 12.11.2024 KW - Hydrogen Safety KW - Trustworthiness KW - Safety research KW - Accidents PY - 2024 AN - OPUS4-62174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Nils T1 - Nominal and Off-Nominal Battery / High Energy Storage Testing Off-Nominal cell and battery testing at BAM N2 - The abuse testing of electrochemical energy storage systems poses a major safety challenge. Thanks to its core competence in ensuring safety in technology and chemistry, BAM has the capabilities to carry out safety tests from small to large scale. Tests up to approx. 200Wh (lithium-ion batteries) can be carried out in the cell test center and abuse tests up to 20kWh are possible in the open field test on the TTS. T2 - Europe Energy Storage Safety Summit CY - Petten, Netherlands DA - 08.10.2024 KW - Battery Safety KW - Abuse testing KW - Lithium-ion batteries KW - Safety critical tests PY - 2024 AN - OPUS4-62321 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Anita T1 - Neues Klassifizierungssystem für Lithiumbatterien N2 - Um Lithiumbatterien sicherer aber gleichzeitig auch dem Gefährdungszustand angemessener und damit wirtschaftlich effizienter transportieren zu können, wird aktuell bei UN ein Klassifizierungssystem nach Gefährlichkeit ausgearbeitet. Als eine der intensiv mitarbeitenden zuständigen Behörden weltweit hat die BAM zahlreiche Untersuchungen selbst durchgeführt und arbeitet an Lösungsansätzen mit. T2 - Gefahrguttag des BMDV im Rahmen der IAA CY - Hannover, Germany DA - 19.09.2024 KW - Lithiumbatterien KW - Klassifizierung KW - Gefahrguttransport KW - Gefährlichkeit PY - 2024 AN - OPUS4-62326 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tiebe, Carlo T1 - Error Prevention, Damage Prevention, and Safety Management in Hydrogen Technologies N2 - In order to integrate the error prevention and damage prevention strategy into hydrogen technologies, it is important to proactively look out for potential weaknesses in the systems and processes. This includes the implementation of preventive measures as elements of safety management in order to identify and eliminate potential sources of error. In addition, training should be specifically focussed on avoiding errors and the safe use of hydrogen technologies. The principial approach of a gas sensor testing laboratory shows how to ensure reliable results, it is advisable to conduct sensor testing under controlled conditions, focusing on identifying specific properties and quantifying performance criteria. A well thought-out strategy for error prevention makes a significant contribution to preventing accidents and increasing overall safety when using hydrogen. T2 - 5th Germany-Korea Hydrogen Conference CY - Halle (Saale), Germany DA - 22.10.2024 KW - Hydrogen KW - Safety KW - Safety Management KW - Error Prevention KW - Reference Procedure PY - 2024 AN - OPUS4-62563 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tiebe, Carlo T1 - Hydrogen Sensing - Sensors for Safety and Process Control in Hydrogen Technologies N2 - The success of this energy transition and the efficient utilization of green hydrogen as a pristine energy carrier hinge upon the cultivation of hydrogen readiness, swift market expansion, and the establishment of crucial value chains within national and European contexts. Paramount to these objectives are reliable quality and safety standards, essential for ensuring supply safety, environmental compatibility, and instilling confidence in these technologies. In the realm of safety management systems, gas sensors emerge as vital components for detecting hydrogen. This presentation delves into the imperative role of hydrogen systems, emphasizing their capability to monitor and control operations, issue warnings, signal hazardous conditions, and sound alarms. It explores the intricate landscape of functional safety considerations and addresses the challenges associated with measurement uncertainty in sensor testing. A diverse array of sensors catering to hydrogen, pressure, temperature, and flow are available, each contributing significantly to the safety and efficiency of hydrogen technologies. Applications are envisaged to adhere meticulously to quality infrastructural regulations, codes, and standards, ensuring seamless integration and operation within the broader hydrogen ecosystem. This discussion underscores the ubiquitous presence of sensor systems across various fields within hydrogen technologies, illustrating their multifaceted contributions to safety, reliability, and overall success in realizing the transformative potential of green hydrogen. T2 - Joint European Summer School JESS 2024 CY - Vravrona, Greece DA - 16.09.2024 KW - H2Safety@BAM KW - Hydrogen KW - Sensor KW - Sensor technology KW - Safety KW - Process control PY - 2024 AN - OPUS4-61677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peters, Stefan A1 - Bartling, Stephan A1 - Parlinska-Wojtan, Magdalena A1 - Wotzka, Alexander A1 - de Oliveira Guilherme Buzanich, Ana A1 - Wohlrab, Sebastian A1 - Abdel-Mageed, Ali M. T1 - Stabilization of intermediate Mo oxidation states by Nb doping enhancing methane aromatization on Mo/HZSM-5 catalysts N2 - The dehydroaromatization of methane is a promising process to produce aromatics and ultra-pure hydrogen. Increased yields and stability of Mo/HZSM-5 against irreversible deactivation were achieved via a redox interaction by doping with otherwise inert Nb. KW - General Materials Science KW - Sustainability and the Environment KW - General Chemistry KW - Renewable Energy PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597670 DO - https://doi.org/10.1039/D3TA07532J SN - 2050-7488 SP - 1 EP - 16 PB - Royal Society of Chemistry (RSC) AN - OPUS4-59767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - On the assessment of dynamic fracture toughness of ferritic ductile cast iron using the master curve concept N2 - An established and validated method to determine and assess dynamic fracture toughness values of ferritic ductile cast iron (DCI) in the ductile-to-brittle transition regime is currently not available. Although the ASME-Code, Sect. III, Div. 3, WC-2330 explicitly requires safety assessment considerations for dynamic loading, sufficiently substantial information on the procedure is not given. Therefore, the applicability of the probabilistic Master Curve (MC) concept according to ASTM E1921 to DCI is being investigated in the joint German research project MCGUSS conducted by BAM Berlin and MPA Stuttgart. Using a tailored manufacturing specification, a DCI material of grade GJS-400 has been casted to provide a test material which is very homogeneous but typical for heavy-sections. The experimental test program covers test specimens of various geometries and sizes (Tensile, Charpy-V, Pellini, SE(B)10, SE(B)25, SE(B)140, DC(T)9, C(T)25 and C(T)50). In total about 500 specimens will be tested to investigate and validate the Master Curve concept and its background for DCI (e.g. size effects, weakest-link, Weibull distribution, microstructure-property correlation). While the whole project has not yet concluded, several work packages have already been completed. This presentation is focused on dynamic large-scale fracture mechanics test series using SE(B)140 specimens and instrumented Charpy impact testing using ISO-V specimens. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve concept PY - 2024 AN - OPUS4-61452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram T1 - Investigating the Applicability of the Master Curve Concept for Ductile Cast Iron – Early Results for 2 Different Test Temperatures N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. This paper outlines the research approach, the planned investigations and first results of the experimental program. T2 - 8th SEDS Workshop: Safety of Extended Dry Storage CY - Garching, Germany DA - 15.05.2024 KW - Dynamic fracture KW - Brittle fracture KW - Ductile cast iron KW - Master Curve PY - 2024 SP - 1 EP - 4 AN - OPUS4-60013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hörmann, Anja Franziska T1 - Next Level Grazing Incidence, Part I: Standardization of Calibration and Alignment for Grazing Incidence Small-Angle (X-ray) Scattering N2 - We present initial results of our survey on grazing incidence methods which focuses on hardware, software, sample alignment and instrument calibration. We illustrate both sample alignment and sample-to-detector distance calibration with data recorded at the MOUSE and conclude with promising results from our Bayesian beam optimization procedure based on Gaussian Process regression. T2 - XIX edition of the International Small-Angle Scattering Conference (SAS2024) CY - Taipei, Taiwan DA - 04.11.2024 KW - Standardisation KW - Grazing incidence KW - Sample alignment KW - Instrument calibration PY - 2024 AN - OPUS4-62775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Roy, Arkendu A1 - Kumar, Sourabh A1 - de Oliveira Guilherme Buzanich, Ana A1 - Prinz, Carsten A1 - Götz, Emilia A1 - Retzmann, Anika A1 - Hickel, Tilmann A1 - Bhattacharya, Biswajit A1 - Emmerling, Franziska T1 - Synergistic Catalytic Sites in High‐Entropy Metal Hydroxide Organic Framework for Oxygen Evolution Reaction N2 - AbstractThe integration of multiple elements in a high‐entropy state is crucial in the design of high‐performance, durable electrocatalysts. High‐entropy metal hydroxide organic frameworks (HE‐MHOFs) are synthesized under mild solvothermal conditions. This novel crystalline metal–organic framework (MOF) features a random, homogeneous distribution of cations within high‐entropy hydroxide layers. HE‐MHOF exhibits excellent electrocatalytic performance for the oxygen evolution reaction (OER), reaching a current density of 100 mA cm−2 at ≈1.64 VRHE, and demonstrates remarkable durability, maintaining a current density of 10 mA cm−2 for over 100 h. Notably, HE‐MHOF outperforms precious metal‐based electrocatalysts despite containing only ≈60% OER active metals. Ab initio calculations and operando X‐ray absorption spectroscopy (XAS) demonstrate that the high‐entropy catalyst contains active sites that facilitate a multifaceted OER mechanism. This study highlights the benefits of high‐entropy MOFs in developing noble metal‐free electrocatalysts, reducing reliance on precious metals, lowering metal loading (especially for Ni, Co, and Mn), and ultimately reducing costs for sustainable water electrolysis technologies. KW - Electrocatalysis KW - Green Hydrogen PY - 2024 DO - https://doi.org/10.1002/adma.202408114 SP - 1 EP - 14 PB - Wiley AN - OPUS4-61739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -