TY - THES A1 - Knieschewski, Arno T1 - Energy efficiency rating of cooking fume extractors based on captured and filtered oil mist N2 - The energy efficiency rating on the European Union energy label for cooking fume extractors is based on measurements of the flow rate and static pressure difference within the duct behind the cooking fume extractor according to standard EN 61591:1997/A12:2015 and regulation (EU) No 65/2014. These measurements do not enable a definite conclusion about the cooking fume extractor’s air purification performance.Measurements which evaluate the air purification performance directly would be more valuable for consumers. In this thesis, a test method was developed that enables the energy efficiency rating of cooking fume extractors based on a direct measurement of the air purification by measuring the captured and filtered oil mist. The test method also enables the rating of cooking fume extractors that operate in recirculation mode, which is not possible using the current standard EN 61591:1997/A12:2015. The performance rating based on removed oil mist requires a reproducible generation of oil mist. Furthermore, the generated oil mist should resemble the oil mist from common cooking scenarios to give meaningful performance ratings. The oil mist from the grease absorption test according to standard EN 61591:1997/A12:2015 was taken as a reference oil mist for common cooking scenarios. A round robin test revealed that the oil mist generation with the grease absorption test from the standard is not reproducible enough for performance tests. The oil mist generation with atomizer nozzles was found more suitable for the reproducible generation of an oil mist. Two different atomizers were analyzed by measuring the properties of generated oil mist and by applying them in performance tests on cooking fume extractors. One “mantled atomizer” was bought from the market and one “open atomizer” was developed specifically for the test of cooking fume extractors. It was found that an oil mist with similar properties compared to the reference oil mist can be generated with the design of the open atomizer. The proposed test method using the open atomizer led to a better repeatability compared to the grease absorption tests according to the current standard and has the potential to improve the reproducibility. The results suggest that the proposed test method could be used for standardized testing which would enable more meaningful energy efficiency ratings and the rating of cooking fume extractors that operate in recirculation mode. N2 - Die Energieverbrauchskennzeichnung der Europäischen Union von Dunstabzugshauben basiert auf den Messungen des Volumenstroms und der statischen Druckdifferenz im Abluftrohr hinter der Dunstabzugshaube gemäß der Norm EN 61591:1997/A12:2015 und Verordnung (EU) No 65/2014. Diese Messungen erlauben keine eindeutigen Rückschlüsse auf die Luftreinigungsfunktion der Dunstabzugshaube. Eine Energieeffizienzbewertung, welche auf Messungen beruht, die die Luftreinigungsfunktion direkt messen, hätte einen größeren Nutzen für die Verbraucher. In dieser Arbeit wird eine Prüfmethode vorgestellt, welche die Energieeffizienzbewertung von Dunstabzugshauben durch eine direkte Messung der Luftreinigungsfunktion ermöglicht, indem die Masse eines eingefangenen und gefilterten Ölnebels ausgewertet wird. The Prüfmethode erlaubt außerdem die Bewertung von Umlufthauben, was mit der jetzigen Prüfnorm EN 61591:1997/A12:2015 nicht möglich ist. Die Leistungsbewertung bezogen auf entfernte Öltropfen benötigt eine reproduzierbare Ölnebelproduktion. Des Weiteren soll der produzierte Ölnebel dem Ölnebel von typischen Kochvorgängen ähneln, um eine aussagekräftige Energieverbrauchskennzeichnung zu ermöglichen. Der Ölnebel vom Fettabscheidegradtest der Norm EN 61591:1997/A12:2015 wurde als Referenz für typische Kochvorgänge genommen. Ein Ringversuch hat ergeben, dass die Ölnebelproduktion vom Fettabscheidegradtest nicht reproduzierbar genug ist, um die Leistung von Dunstabzugshauben zu bewerten. Eine zuverlässigere Ölnebelproduktion konnte mit Zerstäuberdüsen erreicht werden. Zwei verschiedene Zerstäuber wurden analysiert, indem der produzierte Ölnebel vermessen wurde und die Zerstäuber in Leistungsprüfungen von Dunstabzugshauben eingesetzt wurden. Ein „verhüllter Zerstäuber“ wurde gekauft und ein „offener Zerstäuber“ wurde speziell für den Test von Dunstabzugshauben entwickelt. Der offene Zerstäuber konnte einen Ölnebel erzeugen, welcher ähnliche Eigenschaften hatte wie der Referenzölnebel. Die vorgeschlagene Prüfmethode zeigte mit dem offenen Zerstäuber eine bessere Wiederholbarkeit als der Fettabscheidegradtest der derzeitigen Prüfnorm. Die Ergebnisse zeigen, dass die vorgeschlagene Prüfmethode als Prüfnorm genutzt werden könnte, um die Aussagekraft der Energieverbrauchskennzeichnung zu erhöhen und die Bewertung von Umlufthauben zu ermöglichen. KW - Energy label KW - Cooking fume extractor KW - Range hood KW - Oil mist KW - Removal efficiency PY - 2020 SN - 978-3-8440-7498-7 SP - 1 EP - 132 PB - Shaker Verlag CY - Düren, Deutschland AN - OPUS4-51087 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Müller, Alexander T1 - Schädigungscharakterisierung an Faser-Kunststoff-Verbunden im Schwingversuch mittels Röntgenrefraktionstopographie unter Berücksichtigung der Matrixeigenschaften N2 - In der vorliegenden Arbeit wurden verschiedene Epoxidharzsysteme charakterisiert. Zwei Systeme mit großen bruchmechanischen Unterschieden wurden zur Fertigung äquivalenter GFK- und CFK-Laminate mit Faserausrichtungen in 0/90° und ±45° ausgewählt. In quasi-statischen Zugversuchen und Einstufenschwingversuchen mit einem Beanspruchungsverhältnis von R= 0,1 wurden diese Laminate hinsichtlich ihres Schädigungsbeginns und ihrer Schädigungsentwicklung untersucht. Die Detektion der Schädigungen sowie die Dokumentation der Schädigungsentwicklung wurde anhand der Lichtabsorptionsanalyse an GFK-Laminaten und anhand der Röntgenrefraktionsanalyse an CFK-Laminaten umgesetzt. Auf diese Weise konnten Einflüsse der bruchmechanischen Eigenschaften der Matrix auf die Schädigungsentwicklung im Verbund aufgezeigt werden. Zudem wurden für die untersuchten Laminate die Schädigungsgrenzen bei schwingender Beanspruchung ermittelt. Anhand durchgeführter Schwingversuche an CFK-Laminaten im Very High Cycle Fatigue-(VHCF)-Lastwechselbereich bis 108 konnten Rückschlüsse vom Schädigungsverhalten im High Cycle Fatigue-(HCF)-Lastwechselbereich bis 106 auf die Dauerfestigkeit im VHCF-Bereich gezogen werden und damit VHCF-Dauerfestigkeitsgrenzen bestimmt werden. Mit dem Ziel die Ermüdung der Laminate auf die Beanspruchung der Matrix zurückzuführen, wurden die Erweiterte Inverse Laminattheorie, mikromechanikbasierte Mischungsregeln sowie eine Vergleichsspannungshypothese auf die untersuchten Laminate angewendet. Die Schädigungsgrenzen konnten damit in Form der Matrixbeanspruchung wiedergegeben werden. Die Abbildung der Ermüdung verschiedener Laminate anhand einer matrixspezifischen normierten Masterschädigungslinie ist für die behandelten CFK- und GFK-Laminate gelungen. T3 - BAM Dissertationsreihe - 162 KW - CFK KW - GFK KW - Ermüdung KW - Epoxidharz KW - Masterschädigungslinie KW - Röntgenrefraktion KW - ZfP PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-467833 SN - 1613-4249 VL - 162 SP - 1 EP - 204 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-46783 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hille, Falk T1 - Unterraumbasierte Detektion von Strukturschäden an Jacket-Gründungen von Offshore-Windenergieanlagen N2 - Die vorliegende Arbeit beschreibt die Adaption eines globalen, schwingungsbasierten Verfahrens zur frühzeitigen Erkennung von Strukturschäden an Gründungsstrukturen offshore installierter Windenergieanlagen (OWEA). Damit soll es, Betreibern von Offshore-Windparks ermöglicht werden, im Rahmen periodisch durchgeführter messtechnischer Überwachungsmaßnahmen mit einem gegenüber wiederkehrender Inspektionen wesentlich geringen Aufwand auftretende Schäden an der Struktur zuverlässig zu delektieren. Das untersuchte und implementierte Verfahren basiert auf der Methode der stochastischen unterraumbasierten Schadensdetektion. Dabei erfolgt eine statistische Analyse des wiederkehrend messtechnisch aufgenommenen dynamischen Antwortverhaltens des mechanischen Systems. Mittels statistischem Test werden signifikante Änderungen in dessen Eigenstruktur und damit Schäden delektiert. Im Rahmen der vorliegenden Arbeit wurden umfangreiche experimentelle als auch numerische Untersuchungen zur Sensitivität und Robustheit des beschriebenen Schadensindikators durchgeführt. Dazu sind zunächst an einem Labormodell mittels künstlich und reversibel eingebrachter Schäden grundlegende Analysen zu den Einflüssen signal- und verfahrensinhärenter Kenngrößen durchgeführt worden. Auf der Basis dieser Ergebnisse wurde im Anschluss mittels numerischer Analysen das Antwortverhalten von OWEA simuliert und der entwickelte Algorithmus zur Schadensdetektion an den so realisierten Datensätzen angewendet. Anhand der Ergebnisse der Arbeit wird aufgezeigt, dass, vorausgesetzt die Windenergieanlage befindet sich in Parkposition, eine Detektion von schon geringen Schäden an Gründungs-strukturen mit dem beschriebenen Verfahren, auch unter Einsatz weniger Messaufnehmer, zuverlässig möglich ist. N2 - The present work describes the adaptation of a global, vibration-based procedure for an early detection of structural damage to foundation-structures of offshore wind turbines (OWT). It is intended to enable operators of offshore wind farms to reliably detect structural damage by periodic measurement with a once installed monitoring System. The analyzed and implemented procedure is based on the method of stochastic subspace- based damage detection. This involves a Statistical analysis of the of the periodically measured dynamic response behavior of the mechanical System. By means of a Statistical test, significant change in its eigenstructure and thus damage is detected. Within the present work extensive experimental as well as numerical investigations on the sensitivity and robustness of the described damage indicator were conducted. For this purpose, fundamental analyzes of the effects of signal- and process-inherent Parameters on the detection results has been performed at a laboratory model structure by means of artificially and reversibly applied damage. Based on these results, the response behavior of OWT structures was then simulated numerically and the developed algorithm for damage detection was finally applied to the thus achieved data sets. Based on the results of the work it is shown that, assuming the wind turbine Stands in parking position, a detection of already small damage at foundation structures is reliably possible with the described method, even using only a limited number of sensors. KW - Offshore-Windenergieanlagen KW - Structural Health Monitoring KW - Schwingungsbasierte Verfahren KW - Schadensdetektion KW - Unterraummethoden PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-470040 DO - https://doi.org/10.14279/depositonce-7567 SP - 1 EP - 219 PB - Technische Universität CY - Berlin AN - OPUS4-47004 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Nielow, Dustin T1 - Einfluss fertigungsbedingter Imperfektionen auf die Schwingfestigkeit von FKV-Schalenstrukturen in Sandwichbauweise N2 - Rotorblätter von Windenergieanlagen (WEA) weisen häufig nach wenigen Jahren, lange vor dem Erreichen der prognostizierten Lebensdauer von 20 bis 30 Jahren Risse in der Blattschale auf. Die Folge sind aufwendige Reparaturen am installierten und schwer zugänglichen Rotorblatt und der kostenintensive Nutzungsausfall durch den Stillstand der WEA. Als mögliche Initiatoren für die Schäden in der Blattschale der Rotorblätter gelten fertigungsbedingte Imperfektionen. Für die Untersuchung des Einflusses dieser Imperfektionen auf das Ermüdungsverhalten der Rotorblätter wurde an der BAM (Bundesanstalt für Mate-rialforschung und -prüfung) ein Prüfstand für statische und zyklische Versuche von Schalensegmenten im intermediate scale entwickelt und betrieben. Die untersuchten Schalensegmente in Sandwichbauweise sind der Rotorblattschale von WEA im Hinblick auf die Strukturmechanik, die eingesetzten Halbzeuge, den Laminataufbau und dem eingesetzten Fertigungsverfahren ähnlich. Als Imperfektionen wurden verschiedenen Variationen von Lagenstößen in die Hautlagen und Schaumstöße mit Breitenvariation in den Stützkern reproduzierbar eingebracht. Die Überwachung des Schädigungszustandes während der Schwingversuche unter realistischen Lastszenarien erfolgt über eine kombinierte in situ Schädigungsüberwachung mittels passiver Thermografie und Felddehnungsmessung. Mit den durchgeführten Schwingversuchen und der begleitenden Überwachung des Schädigungszustandes ließen sich die Schadensinitiation und die signifikante Herabsetzung der Lebensdauer durch die eingebrachten Imperfektionen zweifelsfrei nachweisen und entsprechende Konstruktionshinweise für die betriebssichere Auslegung von Sandwichstrukturen ableiten. N2 - Wind turbines often exhibit cracks in the blade shells after only a few years in service, significantly before their expected 20 to 30 year design lifespan. This leads to complicated repairs on difficult to reach rotor blades, and can cause a cost-intensive standstill of the turbine. A possible source of these defects in the rotor blade shells are the imperfections which occur during production. In order to investigate the effect of these imperfections on the fatigue behavior of rotor blades, a test rig was developed at the BAM (Bundesanstalt für Materialforschung und -prüfung) upon which intermediate scale static and cyclic-fatigue testing could be performed. The complementary sandwich shell specimens developed and investigated with the test rig are representative of the outer shell of wind turbine rotor blades in terms of materials and manufacturing processes, as well as structural mechanics. The specimens were built with reproducible imperfections, including laminate overlaps in the face sheets and gaps of varying size in the foam core. The damage condition was monitored during cyclic-fatigue testing under realistic load cases using a combination of in-situ passive thermography and strain field measurement. The cyclic testing and parallel non-destructive structural health monitoring of the shell specimens showed the imperfections to significantly influence the damage initiation and decrease the component service life. The results can be used accordingly as recommendations for operationally more reliable design of sandwich structures. T3 - BAM Dissertationsreihe - 170 KW - Erneuerbare Energien KW - Windenergie KW - Verbundwerkstoffe KW - Betriebsfestigkeit KW - Komponentenprüfung KW - Renewable ernergy KW - Wind energy KW - Intermediate scale KW - Composites KW - Fatigue PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546701 SN - 1613-4249 VL - 170 SP - 1 EP - 178 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-54670 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kraus, David T1 - Ermüdungsverhalten von Glasfaser-Kunststoff-Verbunden unter thermomechanischer Beanspruchung N2 - Die Werkstoffgruppe der Faser-Kunststoff-Verbunde (FKV) hat sich aufgrund ihrer hervorragenden Leichtbaueigenschaften unter anderem im Sportgerätebau, in der Luft- und Raumfahrt und in der Windenergieindustrie etabliert. Die so hergestellten Strukturen sind in der Regel nicht nur mechanischen Belastungen, sondern auch thermischen Lasten in einem breiten Temperaturspektrum ausgesetzt. Dennoch ist die Auswirkung des Temperatureinflusses bei einer Kombination von thermischer und mechanischer Last auf die Lebensdauer von Strukturen aus FKV bisher nur wenig untersucht. Im Rahmen dieser Arbeit wird der Einfluss von Temperaturen zwischen 213 K und 343 K auf einen Glasfaser-Epoxidharz-Verbund experimentell untersucht. Das Material wird in diesem Temperaturbereich eingehend charakterisiert: Es werden sowohl die thermomechanischen Eigenschaften von Faser- und Matrixwerkstoff als auch die des Verbundes ermittelt. In einem weiteren Schritt wird dann der Einfluss der Temperatur auf die Schädigungsentwicklung im quasi-statischen Lastfall sowie unter schwingender Ermüdungsbeanspruchung bei verschiedenen FKV-Mehrschichtverbunden analysiert. Basierend auf den experimentellen Daten wird ein Zusammenhang zwischen der Schädigung und der Anstrengung der Matrix innerhalb der Einzelschicht demonstriert. Die Matrixanstrengung wird mithilfe eines mikromechanischen Modells unter Berücksichtigung der thermomechanischen Eigenspannungen analytisch berechnet. Bei Querzugbeanspruchung kann gezeigt werden, dass eine Vorhersage der Schädigung in Abhängigkeit der Volumenänderungsenergie innerhalb der Matrix getroffen werden kann. Mithilfe des Konzepts der Matrixanstrengung ist eine Vorhersage der Lebensdauer des Werkstoffs unter schwingender Ermüdungsbeanspruchung in Abhängigkeit der Einsatztemperatur möglich. N2 - Due to their superior lightweight properties, fiber reinforced polymer (FRP) materials are well established in various fields, such as sports equipment, aerospace or wind energy structures. These structures are not only subjected to mechanical loads, but also to a broad spectrum of thermal environments. However, the impact of temperature on the fatigue life of thermomechanically loaded FRP structures is barely investigated to-date. In the scope of this work, the influence of temperatures in a range of 213 K to 343 K on a glass fiber reinforced epoxy polymer is experimentally examined. An extensive thermo-mechanical characterization of the static properties of the material is performed. The neat resin and Fiber material are investigated, as well as the composite. In addition, the impact of thermal loads on the damage evolution under quasi-static as well as cyclic fatigue loading is investigated for different multi-angle laminates. Based on the experimental data, a correlation is shown between damage and matrix effort of the unidirectional layer. The matrix effort is calculated according to a micromechanical model considering thermal residual stresses. Particularly under transverse loading, the damage Evolution can be predicted as a function of the dilatational strain energy of the matrix. Using the concept of the matrix effort presented in this work, a prediction of the fatigue life of the investigated material at different ambient temperature conditions can be performed. T3 - BAM Dissertationsreihe - 169 KW - Ermüdung KW - Faser-Kunststoff-Verbund KW - GFK KW - Schädigung KW - Thermomechanik KW - Fatigue KW - Composite KW - Glas fibre reinforced polymer KW - Damage KW - Thermomechanics PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-530253 SN - 1613-4249 VL - 169 SP - 1 EP - 164 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-53025 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Keller, Christian T1 - Beitrag zur numerischen Beanspruchungsanalyse an dünnwandigen Stahlblechcontainern im Fallversuch - Schädigungsmechanische Materialmodellierung duktiler Werkstoffe unter Berücksichtigung der Dehnratenabhängigkeit der plastischen Instabilität N2 - Gegenstand der vorliegenden Arbeit ist die Bereitstellung expliziter numerischer Simulationen von Fallversuchen mit dünnwandigen Stahlblechcontainern, die als Endlagerbehälter für radioaktive Abfälle mit vernachlässigbarer Wärmeentwicklung, d. h. schwach- und mittelradioaktive Abfälle, für die Verbringung in das Endlager Konrad vorgesehen sind. Die Betrachtung von potentiellen Absturzszenarien ist ein grundlegender und zentraler Bestandteil der Sicherheitsnachweise zur Auslegung der verschiedenen endlagergängigen Behälter- und Containertypen gegen mechanische Störfallbelastungen. Für dünnwandige Stahlblechcontainer existierten bislang keine sicherheitstechnischen Untersuchungen, die auf numerischen Bewertungsmethoden basieren und eine Bewertung der vorhandenen Sicherheitsreserven hinsichtlich der mechanischen Integrität ermöglichen. Daraus resultierte die Motivation, ein verifiziertes Finite-Elemente-Modell eines repräsentativen Referenzcontainers zu entwickeln, das das dynamische Verformungs- sowie duktile Schädigungs- und Versagensverhalten in numerischen Simulationen von dynamischen Lastfällen physikalisch mit der erforderlichen Güte beschreibt. Duktile Schädigungs- und Versagensvorgänge metallischer Werkstoffe gehen grundsätzlich mit großen plastischen Dehnungen einher und führen somit unweigerlich zu der Notwendigkeit der Diskussion von plastischer Instabilität und damit verknüpften Lokalisierungseffekten, die einen wesentlichen Einfluss auf die Entwicklung des lokalen Beanspruchungszustands haben. Für die schädigungsmechanische Materialmodellierung folgt hieraus das grundsätzliche Erfordernis der korrekten Berücksichtigung des Instabilitätsbeginns, der in der Regel dehnratenunabhängig angenommen wird. Für dynamische Randbedingungen ist der werkstoffspezifische Einfluss der Dehnrate auf das Einsetzen der Lokalisierung jedoch nicht uneingeschränkt vernachlässigbar, so dass im Rahmen dieser Arbeit ein theoretischer Ansatz ausgearbeitet wird, der die plastische Instabilität dehnratenabhängiger Werkstoffe anhand des zeit- und ortsabhängigen Dehnungsgradienten im einachsigen Zugversuch diskutiert. Darüber hinaus ist für eine hinreichend genaue Materialmodellierung neben der korrekten Prognose des Instabilitätsbeginns auch die korrekte Beschreibung des Verformungsverhaltens jenseits der Gleichmaßdehnung notwendig. Zu diesem Zweck wird in dieser Arbeit eine konstitutive Beziehung entwickelt, die sowohl unter Berücksichtigung der plastischen Instabilität als auch unter der Beachtung von ver- sowie entfestigenden Einflussfaktoren der dynamischen Plastizität formuliert werden kann. Insgesamt wird eine praxistaugliche Bewertungsmethode der mechanischen Integrität dünnwandiger Stahlblechcontainer unter Störfallbedingungen auf Basis expliziter dynamischer Simulationen erarbeitet, die die komplexen duktilen Schädigungs- und Versagensmechanismen dehnratenabhängiger Werkstoffe berücksichtigt. Mit der zur Simulation von Fallversuchen entwickelten numerischen Modellbildung und den zur Verifizierung entsprechend mit Testcontainern im Originalmaßstab durchgeführten Fallversuchen wird nachgewiesen, dass anhand des Finite-Elemente-Modells eines repräsentativen Referenzcontainers zum einen eine quantitativ belegte Bestimmung ungünstiger Fallorientierungen hinsichtlich maximaler Verformungen und zum anderen eine realistische Abbildung des duktilen Versagensverhaltens ermöglicht wird. Damit können tatsächlich vorhandene Sicherheitsreserven bei potentiell zu unterstellenden Behälterabstürzen quantitativ aufgezeigt und zukünftig eine verbesserte sicherheitstechnische Beurteilung von Stahlblechcontainern im Fallversuch bereitgestellt werden. Damit leistet die vorliegende Arbeit einen wichtigen Beitrag für die Bewertung von Sicherheitsnachweisen von Endlagerbehältern für radioaktive Abfälle und trägt dazu bei, den langfristigen Schutz von Mensch und Umwelt vor Schäden durch radioaktive Stoffe zu gewährleisten. N2 - The subject of the present work is the provision of explicit numerical simulations of drop tests with thin-walled sheet steel containers, which are intended as repository containers for radioactive waste with negligible heat generation, i.e. low and intermediate level waste, for shipment to the Konrad repository. The consideration of potential crash scenarios is a fundamental and central component of the safety analyses for the design of the various types of casks and containers suitable for final disposal against mechanical accident loads. For thin-walled sheet steel containers, no safety investigations based on numerical assessment methods existed so far that would allow an evaluation of the existing safety reserves with regard to mechanical integrity. This resulted in the motivation to develop a verified finite element model of a representative reference container that physically describes the dynamic deformation and ductile damage and failure behaviour in numerical simulations of dynamic load cases with the required quality. Ductile damage and failure processes of metallic materials are fundamentally accompanied by large plastic strains and thus inevitably lead to the need to discuss plastic instability and associated localisation effects, which have a significant influence on the development of the local stress state. For damage-mechanical material modelling this results in the fundamental requirement of correctly considering the onset of instability, which is usually assumed to be strain-rate independent. For dynamic boundary conditions, however, the material-specific influence of the strain rate on the onset of localisation cannot be neglected without restriction, so that a theoretical approach is elaborated within the scope of this work that discusses the plastic instability of strain-rate-dependent materials on the basis of the time- and location-dependent strain gradient in the uniaxial tensile test. Furthermore, for a sufficiently accurate material modelling, besides the correct prediction of the onset of instability, the correct description of the deformation behaviour in the postcritical region, i.e., beyond the uniform strain, is necessary. For this purpose, a constitutive relationship is developed in this work, which can be formulated both under consideration of the plastic instability as well as under consideration of hardening as well as softening influencing factors of the dynamic plasticity. Overall, a practical assessment method of the mechanical integrity of thin-walled sheet steel containers under accident conditions is developed based on explicit dynamic simulations, which takes into account the complex ductile damage and failure mechanisms of strain rate-dependent materials. With the numerical modelling developed for the simulation of drop tests and the drop tests carried out accordingly with full-scale test containers for verification, it is demonstrated that, on the basis of the finite element model of a representative reference container, on the one hand a quantitatively proven determination of unfavourable drop orientations with regard to maximum deformations and, on the other hand, a realistic representation of the ductile failure behaviour is made possible. This allows it to quantitatively demonstrate actually existing safety reserves in case of potential container crashes and to provide an improved safety assessment of sheet steel containers in drop tests in the future. This work thus makes an important contribution to the evaluation of safety verifications of final storage containers for radioactive waste and helps to ensure the long-term protection of humans and the environment from damage caused by radioactive substances. KW - FEM KW - Dynamische Plastizität KW - Plastische Instabilität KW - Duktile Schädigung KW - Endlager Konrad PY - 2024 DO - https://doi.org/10.14279/depositonce-21874 SP - 1 EP - 188 PB - DepositOnce CY - Berlin AN - OPUS4-61581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Pelkner, Matthias T1 - Entwicklung, Untersuchung und Anwendung von GMR-Sensorarrays für die Zerstörungsfreie Prüfung von ferromagnetischen Bauteilen N2 - Die Zerstörungsfreie Prüfung (ZfP) ist ein wichtiges Werkzeug zur Qualitätssicherung sowie zur Überwachung sicherheitsrelevanter Bauteile. In der industriellen ZfP ist das Interesse an innovativen, kostengünstigen und sicherheitssteigernden ZfP-Methoden sehr groß. Die klassische Streuflussmethode ist die Magnetpulverprüfung, die sehr sensitiv auf Mikrorisse ist. Eine zuverlässige, automatische Prüfung ist hier aber nur bedingt und mit großem Aufwand zu erreichen. Die Lösung liegt im Einsatz von Magnetfeldsensoren, die zudem eine Bewertung der Defektgeometrie aufgrund der gemessenen Rissstreufelder ermöglicht. Insbesondere GMR-Sensoren (giant magneto resistance) eignen sich hierfür aufgrund ihrer kleinen Sensorelemente, welche eine hohe Ortsauflösung ermöglichen, und der sehr guten Feldempfindlichkeit. Jedoch sind kommerzielle GMR-Sensoren nicht an die Bedürfnisse der ZfP angepasst. Daher wurden während dieser Arbeit GMR-Sensoren dahingehend optimiert, dass sie für eine automatisierte Prüfung infrage kommen. Neben dem Design und der Charakterisierung der angepassten Sensoren wurden Messungen zur Detektionswahrscheinlichkeit durchgeführt. Um die Praxistauglichkeit zu untermauern, erfolgte ein quantitativer Vergleich mit alternativen ZfP- Oberflächenmethoden, der Wirbelstrom-, Magnetpulver- und Thermografieprüfung. Zusätzlich konnte der erfolgreiche Einsatz der GMR-Streuflussprüfung in einer industriellen, automatisierten Prüfeinrichtung unter Beweis gestellt werden. N2 - Non-destructive testing is important for both Quality control and maintenance of safety-related components. Modern industry steadily undergoes competition and cost pressure. Therefore, new innovative testing methods are key to increase safety and cost effectiveness. The conventional magnetic flux leakage testing method (MFL) using magnetic particle inspection (MP) is a manual procedure which is very sensitive in terms of the detection of micrometer-scaled cracks. An automated reliable testing however calls for adapted magnetic field sensors. Additionally the quantification of stray fields allows an evaluation of defect geometry. GMR sensors (giant magneto resistance) are particularly well-suited for this purpose. Their low costs, excellent field sensitivity, and capacity to be miniaturized lead to high resolution test results. However, drawbacks exist for commercial GMR sensors which include nonadaption for NDT applications. To overcome this drawback one objective of this thesis was to optimize the geometry of the sensing elements for a GMR sensor array. After characterization, the new sensor arrays were used for validation and investigation of a probability of detection. In addition, by comparing GMR-MFL with other testing methods related to surface breaking defects (eddy current testing, MP, thermography), it was possible to classify in a first step GMR MFL testing in NDT. Finally, an automated GMR was tested successfully established for industrial purposes. T3 - BAM Dissertationsreihe - 122 KW - Zerstörungsfreie Prüfung KW - GMR KW - magnetischer Streufluss KW - Sensorarrays PY - 2014 SN - 978-3-9816668-0-9 SN - 1613-4249 VL - 122 SP - 1 EP - 232 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-36 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Quackatz, Lukas T1 - In situ Untersuchung der Phasenverteilung und der Schmelzbaderstarrung von Duplexstählen mittels laserinduzierter Plasmaspektroskopie (LIBS) N2 - Nichtrostende Duplexstähle (DSS) werden in allen Branchen eingesetzt, bei denen eine hohe Festigkeit in Verbindung mit einer hohen Korrosionsbeständigkeit in aggressiven Medien ge-fordert wird. Beispiele hierfür sind Kraftwerkskomponenten und maritime Strukturen. DSS ha-ben ein ausgewogenes Phasenverhältnis von Ferrit (α) und Austenit (γ). Im Gegensatz zu einphasigen nichtrostenden Stählen vereinen DSS die Vorteile dieser beiden Phasen und kön-nen daher viele Anforderungen der Industrie erfüllen, wie z. B. Gewichtseinsparung oder hohe mechanische Festigkeit. In vielen industriellen Anwendungen werden diese Stähle ge-schweißt. Die Schweißbarkeit wird weitgehend durch die chemische Zusammensetzung be-stimmt. Legierungen mit ferritischer oder ferritisch-austenitischer Erstarrung weisen die höchste Widerstandsfähigkeit gegen Heißrissbildung auf. Das resultierende Phasengleichge-wicht beeinflusst die endgültigen Eigenschaften des Bauteils. Daher kann es von Vorteil sein, den Ferritgehalt des Schweißguts vorherzusehen bzw. zu messen. Das neueste und präzi-seste Gefügediagramm ist das WRC-1992 Diagramm und basiert auf der chemischen Zusam-mensetzung der Grund- und Zusatzwerkstoffe. In diesem Diagramm kann vor dem Schweiß-prozess abgeschätzt werden, welche Volumenanteile von Ferrit und Austenit im resultierenden Schweißgut vorliegen werden. Genutzt wird es bei der schweißtechnischen Verarbeitung von nichtrostenden, austenitischen bzw. Duplex-Stählen. Verschiedene Quellen berichten, dass diverse Legierungselemente nicht berücksichtigt werden und Optimierungen nötig sind. Wei-terhin können Legierungselemente während des Schweißens abdampfen, was die Mikrostruk-tur zum Negativen beeinflusst. Diese Arbeit eruiert zunächst die theoretischen Grundlagen zur laserinduzierten Plasmaspekt-roskopie (LIBS, engl.: laser induced breakdown spectroscopy), die zur in situ Messung chemi-scher Konzentrationen während des Schweißens genutzt werden soll. Weiterhin werden die Grundlagen zur Erstarrung und zur Schweißbarkeit von DSS aufgezeigt. Mithilfe verschiede-ner Kalibriermodelle werden quantitative Messungen mittels LIBS ermöglicht. Um die Ergeb-nisse der LIBS-Analysen zu validieren, wurden Schweißproben angefertigt und LIBS-Messun-gen mit konventionellen Messmethoden, wie die Röntgenfluoreszenzanalyse (RFA) und die energiedispersive Röntgenspektroskopie (EDX) verglichen. Folglich wurden dann in situ LIBS-Versuche, während des Wolfram-Inertgas-Schweißens (WIG), mit und ohne Schweißzusatz-werkstoff durchgeführt. Hierbei konnten die chemischen Konzentrationen in der Schweißnaht mittels LIBS mit der gleichen Genauigkeit wie die konventionellen Verfahren gemessen wer-den. Ein weiteres Ziel dieser Arbeit ist es, die Gültigkeit und Vorhersagegenauigkeit des WRC-1992 Diagramms zu überprüfen. Hierfür wurde der Schweißzusatzwerkstoff mittels PVD-Be-schichtung mit den Legierungselementen Kohlenstoff, Nickel, Mangan, Silizium, Niob und Kup-fer beschichtet. Diese Elemente nehmen maßgeblich Einfluss auf das Phasengleichgewicht Austenit/Ferrit im Schweißgut der Duplexstähle, da sie entweder Ferrit- bzw. Austenitstabilisa-toren sind. Die Messung der ferritischen und austenitischen Phasenanteile im resultierenden Schweißgut wurde mit drei verschiedenen Methoden vergleichend durchgeführt. Mithilfe der Bildanalyse im Lichtmikroskop, einem Fischerscope® sowie der Röntgendiffraktion (XRD). Da-mit sollte auch geprüft werden, inwieweit die Verwendung der jeweiligen Messmethode die Aussagekraft des WRC-1992 Diagramms beeinflusst. Die Vorhersage anhand des WRC-1992 Diagramms war für Nickel, Silizium und Mangan akzeptabel, jedoch bei Niob, Kupfer und Koh-lenstoff waren deutliche Abweichungen zu beobachten. Anpassungen im WRC-1992 Dia-gramm sollten daher für die Elemente Niob, Kupfer und Kohlenstoff vorgenommen werden. Die geringste Genauigkeit und die größte Streuung wurden mit dem XRD-Verfahren erzielt. Daher kann dieses Verfahren für Ferritmessungen an Schweißnähten von Duplexstählen nicht empfohlen werden. KW - LIBS KW - Duplexstahl KW - Vorhersage Phasenanteile PY - 2025 SP - 1 EP - 118 AN - OPUS4-62622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Liehr, Sascha T1 - Fibre Optic Sensing Techniques Based on Incoherent Optical Frequency Domain Reflectometry N2 - Diese Arbeit beschreibt einen alternativen Ansatz zur weit verbreiteten optischen Zeitbereichsreflektometrie, engl.: optical time domain reflectometry (OTDR). Die inkohärente optische Frequenzbereichsreflektometrie, engl.: incoherent optical frequency domain reflectometry (I-OFDR), wird grundlegend analysiert und hinsichtlich ihrer Möglichkeiten zur kontinuierlich ortsaufgelösten (verteilten) Rückstreumessung in optischen Fasern sowie faseroptischen Sensoranwendungen betrachtet. Im Gegensatz zum OTDR Ansatz wird hier die Übertragungsfunktion der optischen Faser gemessen, die über die inverse Fouriertransformation mit der äquivalenten Zeitbereichsantwort verknüpft ist. Das grundsätzliche Verfahren hat gewisse Vorteile und wird bereits zur Messung nichtlinearer optischer Effekte in optischen Fasern genutzt. Die allgemeine Rückstreumesstechnik unterscheidet sich jedoch bezüglich Anforderungen und Einschränkungen und wurde bisher nicht genau untersucht. Verteilte faseroptische Sensoranwendungen mit bemerkenswerter Messauflösung basierend auf Rayleigh-Rückstreuung und Reflexionsstellen in optischen Fasern werden erstmals vorgestellt. Im ersten Teil der Arbeit wird der Frequenzbereichsansatz theoretisch beschrieben. Notwendige Signalverarbeitung und deren Einfluss auf die Zeitbereichsantwort werden dargestellt. Abweichungen von der Linearität des I-OFDR Systems werden diskutiert und ein optimierter Messaufbau wird eingeführt; der entscheidende Einfluss der spektralen Eigenschaften der optischen Quelle wird im Detail betrachtet. Geeignete Parameter des I-OFDR Ansatzes, wie Dynamikbereich und Empfindlichkeit, werden definiert und für den Laboraufbau bestimmt. Ein möglicher Ansatz zur Unterdrückung starker Störsignale wird vorgestellt. Die Vorteile des I-OFDR Ansatzes gegenüber der OTDR Technik bezüglich der Umsetzung für hohe Ortsauflösungen sowie Messauflösung und Signalstabilität werden gezeigt. Diese Vorteile und dem Frequenzansatz eigene Messmöglichkeiten werden im zweiten Teil der Arbeit für ortsaufgelöste Sensoranwendungen demonstriert: Eine dämpfungsarme polymeroptische Faser (POF) wird erstmals auf ihre Sensoreigenschaften untersucht und zur verteilten Dehnungsmessung verwendet. Die Abhängigkeit der Rückstreuleistung von der aufgebrachten Dehnung kann genutzt werden, um gedehnte Faserstrecken zu lokalisieren. Weiterhin wird ein Korrelationsalgorithmus eingeführt, der es ermöglicht ortsaufgelöst Längenänderungen entlang der Faser mit mm-Auflösung zu messen indem die starken Streuzentren in der Faser mit einer Referenzmessung korreliert werden. Untersuchungen auf Querempfindlichkeiten der Sensorfaser bezüglich Temperatur, relativer Feuchte und Modenausbreitung zeigen vernachlässigbare bzw. beherrschbare Abhängigkeiten. In Kombination mit dem hochauflösenden I-OFDR Ansatz ermöglichen die vorgestellten Sensorverfahren vielversprechende neue Messanwendungen. Spezielles Interesse besteht in Bereichen der Bauwerksüberwachung, da die Faser nahezu verlustfrei auf über 100 % gedehnt werden kann. Ein weiteres Sensorverfahren, basierend auf dem Frequenzbereichsansatz zur dynamischen und quasi-verteilten Messung von Längenänderungen und Leistungsänderungen zwischen Reflexpunkten in der Faser wird präsentiert. Basierend auf der Messung weniger Frequenzpunkte der komplexen Frequenzantwort der Messfaser können mehrere Reflexe gleichzeitig und unabhängig voneinander bezüglich Position und reflektierter optischer Leistung ausgewertet werden. Messfrequenzen bis zu 2 kHz können erreicht werden und Längenänderungsauflösungen im μm-Bereich bei kleineren Messfrequenzen sind möglich. Das Messverfahren wird auf systematische Fehlereinflüsse untersucht und anhand von Demonstratormessungen validiert. Messungen der Deformation eines Gebäudes auf einem Erdbebenversuchsstand demonstrieren die Möglichkeit der Feldanwendung des Verfahrens. Das vorgestellte I-OFDR Verfahren demonstriert konkurrenzfähige Messparameter für allgemeine und hochauflösende optische Rückstreumessungen und die vorgestellten faseroptischen Sensorprinzipien zeigen vielversprechende Perspektiven für Anwendungen z.B. in der Bauwerksüberwachung. N2 - In this thesis, an alternative approach to the well-known optical time domain reflectometry (OTDR) technique is presented. A thorough analysis regarding distributed backscatter measurement in optical fibres is provided and its prospects for optical fibre sensing applications are demonstrated and discussed. The measurement approach is referred to as incoherent optical frequency domain reflectometry (I-OFDR): the frequency response of the fibre under test is measured and transferred into its time domain equivalent using inverse Fourier transform. This general technique has been studied and used for the measurement of nonlinear scattering effects in optical fibres. The requirements, limitations and prospects for general backscatter measurement, however, are different and have not been studied in detail prior to this work. Distributed sensing using Rayleigh scattering and reflective events in the fibre is first demonstrated using I-OFDR with remarkable measurement resolution. The incoherent detection technique allows for measuring singlemode fibres as well as multimode fibres. The first part of this work deals with the theoretical analysis and optimized implementation of the frequency domain approach. Necessary signal processing and its impact on the time domain response are presented. Sources of deviation from the linearity of the I-OFDR system are identified and an optimized laboratory setup is introduced; the crucial impact of the source coherence is thoroughly discussed. Suitable system parameters for the I-OFDR approach are defined: the system dynamic range and sensitivity are determined. A technique to suppress the dynamic range-limiting signal originating from strong reflections in the fibre is suggested. It is demonstrated that the I-OFDR technique has advantages over OTDR in terms of implementation for high-resolution measurement, measurement accuracy and signal stability. These advantages and measurement possibilities specific to the frequency domain approach are utilized for spatially resolved sensing applications in the second part of this work: A low optical loss polymer optical fibre (POF) is for the first time studied and analyzed for distributed strain sensing. The backscatter level dependence on strain in the fibre can be used to detect and locate strained fibre sections. Also, a correlation algorithm is proposed and demonstrated to measure length changes along the fibre with mm-resolution by correlating the typical backscatter signature of this fibre type. The fibre type is analyzed in detail regarding cross-sensitivities to temperature, relative humidity as well as mode propagation influences. The proposed sensing principles in combination with the highresolution I-OFDR allow for promising distributed sensing applications. Special interest is expressed by the structural health monitoring (SHM) sector since the fibre can measure strain values exceeding 100 %. Another sensing technique, specific to I-OFDR, is proposed for quasi-distributed and dynamic measurement of length changes and optical power changes at reflective events along the fibre. Precise calculation of the positions and reflected powers of multiple reflections can be conducted in parallel from the measurement of a few sampling points of the complex-valued frequency response. That allows for measuring with an increased repetition rate up to 2 kHz or at μm-scale length changes resolution at lower measurement frequencies. The approach is demonstrated in the laboratory and in a field application by measuring the deformation of a masonry building on a seismic shaking table. The I-OFDR exhibits competitive performance for general high-resolution backscatter measurement and the proposed optical fibre sensor principles may have promising prospects in the structural health monitoring (SHM) sector. T3 - BAM Dissertationsreihe - 125 KW - optical fiber sensor KW - OFDR KW - distributed backscatter measurement KW - polymer optical fiber (POF) sensor KW - structural health monitoring PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-4660 SN - 978-3-9816668-4-7 VL - 125 SP - 1 EP - 144 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Zur, Malte T1 - Numerische Modellierung der Kabinenluftströmung und des Stofftransports von Gefahrgut in Flugzeugfrachträumen N2 - Für den Transport flüssiger Gefahrguter im Luftverkehr werden unter anderem Kunststoffverpackungen verwendet, die Leckagen aufweisen oder Permeation unterliegen können. Aufgrund der vorhandenen Belüftungsbedingungen ist eine Ansammlung entzündlicher oder gesundheitsschädlicher Gase im Frachtraum von Flugzeugen denkbar. Die Überschreitung ausreichender Konzentrationen solcher Gase kann zu einer Gefährdung führen. Im Rahmen der vorliegenden Arbeit werden die Kabinenluftströmungen und der Stofftransport von Gefahrgut in Flugzeugfrachträumen mittels CFD untersucht. Zunächst erfolgt die Entwicklung eines geeigneten numerischen Modells auf der Grundlage eines generischen Frachtraums mit typischen Merkmalen. Die verwendeten realitätsnahen Randbedingungen entsprechen aktuellen Flugzeugmustern. Das numerische Modell wird mittels experimenteller Modellversuche im Maßstab 1/10 validiert. Das Strömungsfeld im Frachtraummodell wird mittels eines LDA-Systems vermessen. Das validierte numerische Modell wird sowohl für Simulationen im Maßstab 1/10 als auch im Maßstab 1/1 verwendet. Anhand der drei Validierungskriterien Symmetrie, Verlaufe und Beträge der betrachteten Strömungsgrößen und einer LDA-Spektralanalyse wird insgesamt eine gute qualitative und quantitative Übereinstimmung zwischen Experiment und Simulation ermittelt. Eine systematische Untersuchung zeigt den Einfluss relevanter Parameter auf das Strömungsfeld und den Stofftransport. Zunächst werden die Einlassreynoldszahl und der Einlassturbulenzgrad sowie die Wandrauigkeit und Wandunebenheit bewertet. Für kleine Reynoldszahlen werden hohe Konzentrationen und für größere Reynoldszahlen werden deutlich geringeren Konzentrationen von Gefahrgut ermittelt. Anhand einer Variation in vier Schritten wird der Einfluss des Einlassmassenstromverhältnisses aus Luft und Gefahrgut bewertet. Erst für Werte von <1000 lasst sich ein signifikanter Einfluss feststellen. Es werden die Stoffe Toluol und n-Hexan beispielhaft für brennbare Gefahrgüter der Klasse 3 verwendet. Der Einfluss der Position und Gestalt verschiedener Einlassquellen wird an vier realitätsnahen Quellentypen bewertet. Anhand vier verschiedener Transportszenarien wird die Ausbreitung von Gefahrgut im Modellmaßstab untersucht. Die Szenarien unterscheiden sich durch die Art der Belüftung und durch die Dauer des Gefahrgutaustritts. Szenarien mit aktiver Frachtraumbelüftung sind als eher unkritisch zu beurteilen. Die betrachteten Szenarien ohne aktive Frachtraumbelüftung sind als gefährlich einzustufen. Insbesondere das Szenario mit zeitlich unbegrenztem Gefahrgutmassenstrom erreicht kritische Konzentrationswerte und eine kritische Ausdehnung der Gefahrgutansammlung im Frachtraum. Diese Ergebnisse werden anhand zweier Szenarien im Maßstab 1/1 bestätigt. Die vorliegende Arbeit leistet einen Beitrag, das Verständnis der Strömungs- und Stofftransportvorgange im Flugzeugfrachtraum beim Transport von Gefahrgütern im Luftverkehr zu erweitern, um Risiken im Luftverkehr zu identifizieren. Die Allgemeingültigkeit und die Übertragbarkeit der Erkenntnisse auf Flugzeugmuster und Flugszenarien mit komplexeren Details sind zu prüfen. N2 - Liquid dangerous goods are regularly transported as air freight in commercial aircrafts. Using plastic jerrycans or plastic containers, liquids or gases can escape by leakage or permeation effects. The specific ventilation situation in the aircraft cargo compartment may lead to agglomerations of potentially flammable or harmful gas-air mixtures in the cargo compartment. Exceeding certain concentration limits of such gases may cause dangerous situations. This work presents a CFD study of the cabin air flow and the mass transport of dangerous goods in the cargo compartments of commercial airplanes. In a first step, an adequate numerical model is developed that utilizes a generic aircraft cargo compartment with typical characteristics. The realistic boundary conditions are based on modern types of aircrafts. The numerical model is validated by model experiments in 1/10 scale. As a second step, the flow field in the cargo compartment is determined using a LDA-system. The validated numerical model is employed for simulations in 1/10 and 1/1 scale. Using three validation criteria (the symmetry, the evolution and values of flow variables and a LDA spectral analysis) a good qualitative and quantitative agreement between experiment and simulation is found. As a next step, a systematic analysis of relevant parameters influencing the flow and the mass transport in the cargo compartment is conducted. The influence of the inlet Reynolds number and the inlet turbulence intensity as well as the wall roughness and geometric obstructions on the wall are evaluated. For low Reynolds numbers, high concentrations are found and for higher Reynolds numbers, significantly lower concentrations of dangerous goods are calculated. The influence of, the ratio of air and dangerous good flowing into the domain is evaluated using four different values of. Only values of <1000 show a significant influence on the concentration levels in the domain. The dangerous substances toluene and hexane are used as examples for class 3 flammable dangerous goods. The influence of the position and the shape of different inlet sources for dangerous goods are evaluated using four different types of sources. In a final step, four different transport scenarios are used to simulate and evaluate the expansion and propagation of dangerous goods in the generic cargo compartment in the model scale 1/10. The scenarios differ in the ventilation situation and the duration of the mass of dangerous goods entering the domain. Scenarios with an active cargo compartment ventilation are found to be noncritical. Scenarios without an active ventilation lead to critical concentrations of dangerous goods. In particular, a scenario with an indefinite mass inflow of a dangerous gas shows critical concentration levels and a critical expansion in the cargo compartment. These findings are confirmed by simulations of two different scenarios in a 1/1 scale. The presented work contributes to a better understanding of the cabin air flow and the mass transport of dangerous goods in aircraft cargo compartments in order to identify potential risks. The universal validity and the transferability of the findings to other, more complex aircraft cargo compartments and transportations scenarios are to be reviewed in further research. T3 - BAM Dissertationsreihe - 128 KW - CFD KW - Kabinenluftströmung KW - Stofftransport von Gasen KW - gefährliche Güter im Luftverkehr KW - LDA PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-4949 SN - 978-3-9816668-8-5 VL - 128 SP - 1 EP - 170 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-494 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Steppan, Enrico T1 - Zur Analyse der Eigenschaftsdegradation und des Bindungsverhaltens von Wasserstoff in höherfesten Feinkornbaustählen N2 - Der Stahlbedarf in Deutschland wird maßgeblich neben dem Automobilsektor vom Maschinenbau und allgemeinen Bauwesen geprägt. In diesen Segmenten werden qualitativ hochwertige Stähle mit höchsten Ansprüchen an Festigkeit, Verformungsfähigkeit, schweißtechnische Verarbeitung und sicherheitsrelevante Aspekte gestellt. Wichtige Vertreter, welche diesen Ansprüchen gerecht werden, sind die heutigen modernen höherfesten FKB. Aus der Entwicklung dieser Stähle kristallisierten sich in den letzten Jahrzehnten verschiedene Legierungskonzepte und Herstellungsrouten heraus. Dem liegt neben essentiellen Eigenschaften, z.B. Streck- und Zugfestigkeit, noch weitere Anforderungen, bspw. Kaltumformbarkeit, Kerbschlagzähigkeit und Verschleißfestigkeit, zugrunde. Zunehmend werden im genormten Bereich mit Streckgrenzen bis 700 MPa neben den vergüteten Stählen (Q) auch thermomechanische Stähle (M) eingesetzt. Ein immerwährender paralleler Begleiter während der Stahlherstellung und -verarbeitung ist Wasserstoff. Wasserstoff wird in den nächsten Jahren als Schlüsselelement für eine nachhaltige Energiewirtschaft angesehen. Aus heutiger Sicht ist Wasserstoff ein Hoffnungsträger für eine klimafreundliche Energiewirtschaft und zukunftsfähige Industrie. Forschung und Industrie arbeiten intensiv an der Erschließung und Weiterentwicklung des enormen Potentials, um eine höhere Nutzbarkeit zu erreichen. Die Gründe liegen zum einen darin, dass Wasserstoff als Brennstoff unproblematisch (Umweltverträglichkeit und Verfügbarkeit) ist und zum anderen ein hervorragender Energieträger ist. Wasserstoff ist durch seine gebundene Form erst nach dem Lösen aus chemischen Verbindungen zugänglich. Dies geschieht für eine Nutzbarmachung in einer zukunftsfähigen Energiewirtschaft gezielt. Demgegenüber stehen Prozesse, wodurch Wasserstoff aus seiner chemischen Verbindung gelöst wird und aufgrund seiner Größe bzw. geringsten Atommasse von Werkstoffen aufgenommen wird. Damit verbunden interagiert der aufgenommene Wasserstoff mit dem Gefüge und kann zu einer negativen Beeinflussung der Eigenschaften des Werkstoffs führen. Wasserstoff kann Degradationsprozesse in Stählen verursachen, die sich insbesondere auf die mechanischen Eigenschaften auswirken. Diese Mechanismen können wasserstoffunterstützte Risse in höherfesten Stählen während der Herstellung oder im industriellen Einsatz verursachen. Elektrochemisch beladene Zugproben zeigen ein unterschiedliches Degradationsverhalten in ihren Eigenschaften. Die vorliegende Arbeit beschreibt die Wechselwirkungen zwischen Wasserstoff und Gitterdefekten in unterschiedlichen mikrolegierten Systemen und wärmebeeinflussten Zonen in den schweißbaren Feinkornbaustählen. Die Ergebnisse zeigen eine klare Abhängigkeit zwischen Mikrolegierung und Herstellungsprozess dieser Stahlsorten, respektive ihrer simulierten wärmebeeinflussten Bereiche. N2 - In addition to the automotive sector, demand for steel in Germany is dominated by mechanical engineering and general construction. These segments demand high-quality steels with the highest requirements in terms of strength, formability, welding processing and safety aspects. Important representatives that meet these requirements are today's more modern high-strength FKB. In the development of these steels, various alloying concepts and production routes have crystallized in recent decades. In addition to essential properties, e.g. yield and tensile strength, this is also based on other requirements, e.g. cold formability, notched impact strength and wear resistance. Increasingly, thermomechanical steels (M) are being used in addition to quenched and tempered steels (Q) in the standardized range with yield strengths up to 700 MPa. An ever-present parallel companion during steel production and processing is hydrogen. Hydrogen is seen as a key element for a sustainable energy economy in the coming years. From today's perspective, hydrogen is a beacon of hope for a climate-friendly energy economy and sustainable industry. Research and industry are working intensively on tapping and further developing the enormous potential in order to achieve greater usability. The reasons are, on the one hand, that hydrogen is unproblematic as a fuel (environmental compatibility and availability) and, on the other hand, that it is an excellent energy carrier. Due to its bonded form, hydrogen is only accessible after dissolution from chemical compounds. This is done in a targeted manner for utilization in a sustainable energy economy. In contrast, there are processes by which hydrogen is released from its chemical compound and absorbed by materials due to its size or lowest atomic mass. In connection with this, the absorbed hydrogen interacts with the microstructure and can lead to a negative influence on the properties of the material. Hydrogen can cause degradation processes in steels that affect mechanical properties in particular. These mechanisms can cause hydrogen-assisted cracking in higher strength steels during fabrication or in industrial use. Electrochemically loaded tensile specimens show different degradation behavior in their properties. The present work describes the interactions between hydrogen and lattice defects in different microalloyed systems and heat affected zones in the weldable fine grain structural steels. The results show a clear dependence between microalloying and manufacturing process of these steels, respectively their simulated heat affected zones. T3 - BAM Dissertationsreihe - 172 KW - Höherfeste Feinkornbaustähle KW - Wasserstoffdegradation KW - Wasserstoffdiffusion KW - Wasserstoffbindungsverhalten KW - Kaltriss und Schweißen KW - High strength fine grained structural steels KW - Hydrogen degradation KW - Hydrogen diffusion KW - Hydrogen trapping KW - Cold cracking and welding PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-579412 SN - 1613-4249 VL - 172 SP - 1 EP - 266 PB - Eigenverlag CY - Berlin AN - OPUS4-57941 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Popiela, Bartosz T1 - Einfluss fertigungsbedingter Eigenspannungen auf die Betriebssicherheit von nassgewickelten Composite-Druckbehältern mit einem nichttragenden Liner N2 - Im Hinblick auf die globale Herausforderung der Energietransformation steigt der Bedarf an Möglichkeiten zur Energiespeicherung. Eine Technologie, die zunehmend in den Fokus rückt, ist die Energiespeicherung mittels komprimiertem Wasserstoffgas. Insbesondere für mobile und Transport-Anwendungen ist eine geringe Masse des Speichers vorteilhaft, weshalb vollumwickelte Composite-Druckbehälter des Typs 4 zum Einsatz kommen. Diese werden überwiegend im Nasswickelverfahren gefertigt, das durch zahlreiche Prozessparameter und physikalische Effekte charakterisiert wird. Die Wahl der Wickelprozessparameter sowie Schwankungen der Materialkennwerte beeinflussen den Eigenspannungszustand in der Composite-Struktur eines Druckbehälters. Somit wirken sie sich auch auf den Spannungszustand im Betrieb aus. Die vorliegende Dissertation beinhaltet Untersuchungen des Einflusses von fertigungsbedingten Eigenspannungen auf die Sicherheit von Composite-Druckbehältern mit nichttragendem Kunststoff-Liner. Ziel ist es, das mechanische Verhalten von Composite-Druckbehältern besser zu verstehen und deren Sicherheitsniveau sowie Konkurrenzfähigkeit weiter zu steigern. Schwerpunkte der Arbeit sind experimentelle Untersuchungen der Eigenspannungsentstehung und -entwicklung sowie deren Einfluss auf die Behälter-Sicherheit. Im Fokus befindet sich die Exploration von Möglichkeiten zur Verbesserung der Zuverlässigkeit der Behälter durch Variation der Fertigungsparameter und eine Konditionierung nach der Fertigung. Der Eigenspannungszustand wird in numerischen Simulationen sowie mit dem zerstörenden Bohrlochverfahren charakterisiert. Die Überwachung der Spannungsumlagerung während einer Konditionierung unter Zeitstandbelastung erfolgt mit eingebetteten faseroptischen Sensoren, die später zur Dehnungsmessung in zerstörenden, langsamen Berstprüfungen eingesetzt werden. Zur Vertiefung des Verständnisses des Versagensverhaltens der verwendeten 6,8 l-Druckbehälter wird die Finite-Elemente-Methode eingesetzt. Darüber hinaus werden Qualitätsuntersuchungen der Composite-Struktur mittels Mikro-Computertomographie und Impuls-Echo-Verfahren beschrieben. Die Ergebnisse der Untersuchungen zeigen, dass eine Steigerung der Zuverlässigkeit durch eine gezielte Innendruckbeanspruchung der gewickelten Behälter nahezu kostenneutral möglich ist. Dies wird im Rahmen der Arbeit anhand eines Baumusters demonstriert. Darüber hinaus wird die Verbesserung der Zuverlässigkeit der Behälter im Rahmen einer Konditionierung unter Zeitstandbelastung vertieft diskutiert. Diese stellt eine weiterführende Möglichkeit dar, das Behälterverhalten positiv zu beeinflussen und das Sicherheitsniveau zu steigern. N2 - Considering the global challenge of energy transformation, the demand for energy storage solutions is increasing. One of the technologies, which is gaining attention, is the storage of hydrogen gas under high operating pressures. Particularly for on-board and transport applications, lightweight storage systems are advantageous. Therefore, fully wrapped composite pressure vessels of Type 4 are increasingly used. These are mostly manufactured using the wet filament winding process, which is characterized by numerous process parameters and physical effects. The choice of winding process parameters and variations in material properties influence the residual stress state in the finished component and thus also the stress state under operational loads. This dissertation includes insights into the impact of manufacturing-induced residual stresses on the safety of Type 4 pressure vessels, which contribute to a deeper understanding of the mechanical behavior of composite pressure vessels and support the further enhancement of safety levels and competitiveness. The work focuses on experimental investigations of the induction and development of residual stresses and their impact on the safety of the composite pressure vessels. A core of the dissertation is an exploration of the possibilities to improve pressure vessel performance through variation of manufacturing parameters and conditioning after manufacturing. The residual stress state is characterized in numerical simulations as well as with the destructive hole-drilling method. Embedded fiber optic sensors are used for the monitoring of stress redistribution during conditioning. The fiber optic sensors are later used for strain measurement in destructive, slow burst tests. Finite element analyses are performed to deepen the understanding of the failure behavior of the used 6.8-liter pressure vessels. Additionally, quality investigations of the composite structure using micro-computed tomography and impulse-echo ultrasonic propagation imaging are described. The results of the investigations show that an increase in performance is possible through targeted internal pressure regulation during the winding process pressure vessels. This is demonstrated almost cost-neutrally, i.e., without increasing process time and material usage. Furthermore, the improvement of vessel performance through conditioning under increased pressure and temperature is discussed in depth. This represents a further possibility to favorably influence vessel behavior and enhance safety levels. KW - Composite KW - Druckbehälter KW - Eigenspannung KW - Faserverstärkter Kunststoff KW - Nasswickelverfahren PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:co1-opus4-72383 DO - https://doi.org/10.26127/BTUOpen-7238 SP - 1 EP - 153 CY - Cottbus, Deutschland AN - OPUS4-65348 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Aristia, Gabriela T1 - Polyaniline/Silicon Dioxide Composite-Based Coating for Corrosion Protection in Geothermal Systems N2 - Geothermal energy is one of the cleanest renewable alternatives to reduce the dependency on fossil fuel [1, 2]. Despite its promising future, its implementation faces various challenges, one of them being corrosion processes. To implement this energy, hot fluids are pumped from a geothermal well. These hot fluids originate from deep within the earth, so consist of different ionic species and gases in a wide range of temperatures, which lead to their corrosive nature. In terms of geothermal energy resources, Indonesia is at the forefront, with the highest preserved geothermal energy in the world of about 29 GWe and 312 potential geothermal locations [3]. Geothermal wells in Sibayak (North Sumatera), Indonesia, belong to young stratovolcanoes and have operating temperatures varying from 36 °C at the near ground surface to 310 °C at the bottom of the well, which is liquid-dominated with acidic and saline properties [4, 5]. Therefore, this geothermal fluid creates an aggressive environment that is conducive to corrosion of the powerplant infrastructure. Parts of the geothermal powerplant infrastructure, such as pipelines and heat exchangers, are commonly made of metals, e.g. carbon steel and stainless steel. Consequently, they may undergo corrosion and scaling when exposed to the geothermal fluid, especially for carbon steel. To ensure the safety and longevity of a geothermal powerplant, the infrastructure is constructed of expensive corrosion resistant alloys [6–10], e.g., titanium and Ni-Cr based alloys, or carbon steel which needs to be protected by coatings or inhibitors. To address the corrosion of carbon steel in the geothermal environment, artificial geothermal water was used to simulate a geothermal well in Sibayak, Indonesia, with pH 4 and a saline composition of 1,500 mg/l Cl-, 20 mg/l SO42-, 15 mg/l HCO3-, 200 mg/l Ca2+, 250 mg/l K+, and 600 mg/l Na+. Carbon steel underwent the most severe corrosion at 150°C in an oxygen-containing solution with a corrosion rate of 0.34 mm/year, which is approximately ten times higher than that in the absence of dissolved oxygen. In all conditions, pitting corrosion was observed, which necessitate a protection strategy on carbon steel. In order to promote a cost effective and locally available option, this work focused on an easily applicable coating which utilized local resources. Toward developing such protective coating based on the locally available resources in Indonesia which can yield good corrosion resistance and thermal stability in geothermal environment, two additional components, i.e. polyaniline (PANI) and silicon dioxide, were used to modify an alkyd-based commercial coating. The selection of the alkyd-based coating as a matrix focused on the industrial convenience basis, where the coating application procedure should be simple and easy to apply within reasonable costs. The alkyd-based coating underwent severe blistering when exposed to the artificial geothermal water at 70 and 150°C due to the reaction between CaCO3 (as one of its components) and the artificial geothermal water, as well as a possible alkyd hydrolysis in the initial stage of exposure. In the oxygen-free solution, the degradation was controlled by chemical and thermal reactions, whereas in the aerated condition, oxidization at the coating surface further accelerated polymer degradation. PANI was chosen as one of the anticorrosion pigments which was widely developed over the past decades. To investigate the interaction between PANI and the artificial geothermal water, PANI film was electrochemically deposited on the carbon steel surface and exposed to the artificial geothermal water. Electrochemically synthesized oxalate-doped PANI was protective against corrosion of carbon steel in artificial geothermal water at room temperature. The mechanism involved an exchange of electroactive species within the coating layer, as confirmed by electrochemical impedance spectra. Interaction of ionic species, such as Cl-, Na+, Ca2+ from the artificial geothermal water, with the outer layer of PANI is suggested both at 25°C and 150°C, based on the EDX spectra of the coating surface after exposure to the artificial geothermal water. Thus, the protection mechanism of PANI is not solely based on the physical barrier layer properties, but rather associated with the redox mediated properties of PANI, which selectively allow ionic species intrusion from the electrolyte into the PANI layer. Although PANI is a promising candidate as an anticorrosion coating, its morphological characterization reveals that electrochemically deposited PANI is not stable for an application at 150°C. Therefore, another approach was used to promote better protective behavior of PANI by dispersing chemically synthesized PANI in the alkyd-based coating. To enhance the thermal stability of the coating, silicon dioxide (SiO2) was added, which was able to prolong the sustainability of coated metals until 28 days compared to the unmodified alkyd-based coating, which underwent a change in color to brown/orange only within 7 days of exposure. This improvement might be associated with the role of SiO2 to proportionate the thermal expansion coefficient of the coating system to be compatible with that of carbon steel. Although the coating is thermally enhanced, the electrolyte might still intrude through the coating resulting in the change of coating color after 28 days of exposure in the artificial geothermal water. When PANI was added, the coating system provided an active corrosion protection on the carbon steel surface. The chemical and morphological characterization of the PANI-alkyd and SiO2-alkyd coating system showed that coatings were improved, and no blisters were observed, albeit the degradation continued. Based on the results of exposure tests, the combined coating system was further investigated. The combinational coating of PANI/SiO2-alkyd was used with 2 wt% of PANI and 15 wt% of SiO2. Electrochemical tests indicated cathodic protection at 150°C, as the Ecorr of PANI/SiO2 remained approximately 400 mV lower than the carbon steel potential. The impedance spectra of the combinational coating of PANI/SiO2 showed a continuous decrease in the absolute impedance value over time. A significant decrease was observed within one day of exposure, followed by a slow gradual decrease, which might be associated with water absorption in the coating. FTIR spectra revealed that several peaks associated with the organic portion of the coatings were reduced after the specimens were exposed for 6 months. However, the absorption peaks related to the inorganic portion of the coatings remained stable until 6 months. Morphological characterization of the combinational coating of PANI/SiO2 showed that there were no blisters or significant discoloration of coatings after long-term exposure for 6 months in artificial geothermal water at 150°C, indicating that the chemical degradation does not significantly affect the functionality of the coating. This clearly shows the durability of PANI/SiO2 coating in the geothermal condition, suggesting that this coating can be used for such geothermal application. However, further testing of this coating should be conducted in a real geothermal environment on-site to ensure safety and viability. KW - Geothermal KW - Corrosion KW - Coating KW - Polyaniline KW - Electrochemical impedance spectroscopy PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-refubium-26704-6 UR - https://refubium.fu-berlin.de/handle/fub188/26704 DO - https://doi.org/10.17169/refubium-26461 SP - 1 EP - 175 CY - Berlin AN - OPUS4-51281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Mirtschin, Nikolaus T1 - Thermomechanisches Verhalten von semikristallinem Polyester-Urethan N2 - Formgedächtnispolymere werden durch thermomechanische Vorbehandlung, die Programmierung, in eine temporäre Form überführt. In die Ursprungsform kehren sie dann erst nach externer Stimulierung, durch Auslösen des Formgedächtniseffekts, wieder zurück. Um diesen Effekt zu optimieren, werden in dieser Arbeit thermomechanische Designoptionen analysiert und Stellschrauben der Programmierung diskutiert. Quantifiziert wird das Materialverhalten eines physikalisch vernetzten Polyurethans mit semikristalliner Polyester-Weichsegmentphase (PEU) in thermomechanischen Messungen, in denen das Polymer Dehnungen bis über 1000% fixiert. Deformationen im breiten Schmelzübergangsbereich der Weichsegmentphase ermöglichen die präzise Kontrolle über die Temperaturen der Dehnungs- und Spannungsrückstellung, den bekannten Temperaturgedächtniseffekt (TGE). Erst durch eine neuartige Programmierung wird jedoch der Beginn der Rückstellung einstellbar. Für diesen Onset-TGE wird das PEU direkt nach dem Recken entlastet und danach unter die Kristallisationstemperatur abgekühlt. In situ Röntgenstreuung zeigt, dass durch den frühen Entlastungszeitpunkt nur der Teil der kristallinen Weichsegmentphase zur Fixierung beiträgt, der auch beim Recken kristallin ist. Die Kristallinität bietet daher eine Stellschraube, um das thermomechanische Verhalten zu veredeln. Über die Optimierungsparameter Reckrate, Temperaturhaltezeit und maximale Dehnung erzielt das PEU hohe Fixierbarkeiten und Rückstellspannungen, ohne die Rückstellung und den Onset-TGE zu beeinträchtigen. Durch die Erweiterung der Programmierung des Onset-TGEs hin zu einer zweiten Deformation und Entlastung innerhalb des Schmelzübergangs zeigt das PEU einen bisher nicht berichteten zweistufigen Spannungsanstieg während der Rückstellung. Ein Temperaturlimit für den Onset-TGE stellt die Peak-Schmelztemperatur aus der dynamischen Differenzkalorimetrie dar. Durch die verbleibende Kristallinität oberhalb dieser Temperatur führt die Deformation und Entlastung direkt zur thermoreversiblen Aktuation mit Dehnungsänderungen bis zu 28%. Die Ergebnisse werden auf einen Miniaturisierungsansatz für schaltbare Informationsträger übertragen, mit denen eine maschinenlesbare Information von nichtlesbar nach lesbar geschaltet werden kann. In einer Machbarkeitsstudie wird der für Sensoranwendungen vielversprechende Onset-TGE genutzt, um die Lesbarkeit der Informationsträger bei einer vordefinierten Temperatur zu schalten. Das erweitert das potentielle Anwendungsfeld der Technologie vom Produkt- und Markenschutz zur Überwachung von Kühlketten. N2 - Shape memory polymers are able to change their shape upon application of an external stimulus. This behavior requires a thermomechanical treatment, so-called programming, to establish a temporary shape. To optimize the shape memory performance, thermomechanical design options will be analyzed and programming parameters discussed in the present thesis. The material behavior of a physically crosslinked polyurethane with semicrystalline polyester soft segments (PEU) is quantified by thermomechanical measurements, where the polymer fixes strains of above 1000%. The deformation within the broad melting transition of the soft segment phase enables the precise control over the temperatures of strain and stress recovery, also known as temperature-memory effect (TME). But only the herein introduced programming route, consisting in elongation and unloading prior to cooling below the crystallization transition, allows for fine-tuning the beginning of recovery. For the resulting onset-TME in situ X-ray scattering indicates that only soft segment crystals contribute to fixation, which are crystalline during deformation. Therefore, the crystallinity opens the door for gaining precisely control over the thermomechanical behavior. Optimization parameters for reaching high strain fixities and recovery stresses without compromising recovery nor the onset-TME are found in the strain rate, temperature holding time and maximum strain. When extending the programming route for onset-TMEs towards a second deformation and unloading step of PEU within the melting transition, an unreported two-step stress recovery is rendered possible. However, the peak melting temperature determined from differential scanning calorimetry represents a temperature limit for the onset control. Through the residual crystallinity above that temperature, deformation and unloading yield thermoreversible actuation with strain changes up to 28%. The findings are transferred to a miniaturization approach for switchable information carriers for switching encoded information from machine-unreadable to readable. In a proof-of-concept study the onset-TME – promising for sensor applications – can be exploited in order to predefine a temperature threshold value for readability of information carriers. This behavior widen their potential applicability from product and brand protection to cold chain supervision. T3 - BAM Dissertationsreihe - 156 KW - Formgedächtnispolymere KW - Temperaturgedächtnispolymere KW - Polyester-Urethan KW - Thermomechanische Eigenschaften KW - Programmierung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-399648 SN - 978-3-9818270-5-7 SN - 1613-4249 VL - 156 SP - iii EP - 150 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-39964 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kömmling, Anja T1 - Alterung und Lebensdauervorhersage von O-Ring-Dichtungen T1 - Aging and lifetime prediction of O-ring seals N2 - Für Anwendungen, bei denen Elastomerdichtungen ihre Dichtheit über sehr lange Zeiträume (z. B. Jahrzehnte) behalten müssen, ohne dass ein Austausch praktikabel wäre, ist es nötig, die Lebensdauer solcher Dichtungen zuverlässig bestimmen zu können. Aus diesem Grund wurden Alterungsversuche an O-Ring-Dichtungen sowie Flachproben auf Basis von hydriertem Acrylnitril-Butadien-Kautschuk (HNBR), Ethylen-Propylen-Dien-Kautschuk (EPDM) und Fluorkautschuk (FKM) über bis zu zwei Jahre bei mehreren Temperaturen durchgeführt. Zur Untersuchung der auftretenden Eigenschaftsveränderungen wurden u. a. Härtemessungen, Zugversuche, dynamisch-mechanische und thermogravimetrische Analysen durchgeführt. Zur Beurteilung des Relaxations- und Rückstellverhaltens der alternden Dichtungen wurden außerdem Druckspannungsrelaxations- und Druckverformungsrestmessungen durchgeführt. Darüber hinaus wurde die Leckagerate gemessen, um ein Versagen der Dichtung zu detektieren. Durch die Untersuchung der gealterten Proben wurden sowohl die auftretenden Eigenschaftsveränderungen charakterisiert wie auch die damit zusammenhängenden Alterungsmechanismen diskutiert. Anhand der großen Datenmenge aus Ergebnissen von verschiedenen Untersuchungsmethoden, die für mehrere Alterungszeiten und -temperaturen durchgeführt wurden, sollte zusätzlich die günstigste Vorgehensweise für Lebensdauervorhersagen ermittelt werden. Dies beinhaltete auch die Bestimmung eines Lebensdauerkriteriums, das mit dem Auftreten von Leckage und damit dem Versagen der Dichtung zusammenhängt. Hinsichtlich der Eigenschaftsänderungen und Alterungsmechanismen wurde beim HNBR eine starke Versprödung aufgrund dominanter Vernetzungsreaktionen während der Alterung festgestellt. Diese resultierten auch darin, dass die Sauerstoffpermeabilität abnahm, so dass der Sauerstofftransport ins Innere der Probe (hauptsächlich bei den dickeren O-Ringen) behindert wurde. Dies führte dazu, dass diffusionsbegrenzte Oxidationseffekte (DLO-Effekte) auftraten, d. h. dass das Probeninnere weniger stark alterte als oberflächennahe Bereiche. Während der Alterung von EPDM traten sowohl Kettenspaltungen wie auch Vernetzungsreaktionen auf, was sich vor allem in einer Verschlechterung der Zugeigenschaften und einer Abnahme der Druckkraft sowie in einem steigenden Druckverformungsrest äußerte. Bei sehr stark gealterten Proben dominierten ebenfalls Vernetzungsreaktionen, was sich auch in deutlichen DLO-Effekten äußerte. Aufgrund seiner ausgeprägten Oxidations- und Hochtemperaturbeständigkeit wies FKM vergleichsweise geringe Degradationserscheinungen auf. Nur mit Druckspannungsrelaxation und Druckverformungsrest waren nennenswerte Änderungen ersichtlich. Messungen der statischen Leckagerate ergaben, dass die O-Ringe erst bei sehr weit fortgeschrittener Degradation undicht wurden und bis zu diesem Zeitpunkt kein allmählicher Anstieg der Leckagerate beobachtet werden konnte. Aus diesem Grund wurden Leckagemessungen mit einem modifizierten Versuchsaufbau durchgeführt, bei dem die Dichtung während der Messung leicht entlastet wird. Da dieser Test eine dynamische Rückstellung der Dichtung erfordert und damit höhere Ansprüche an die Dichtung stellt, wurde am geprüften EPDM-O-Ring ein früheres Versagen beobachtet. Der entsprechende Alterungszeitpunkt wurde als Versagenszeitpunkt definiert. Dieser wurde anhand der Daten verschiedener Messmethoden mit dem Degradationszustand korreliert und entspricht beispielsweise einem Druckverformungsrest von 80 %. Auf der Grundlage dieses Kriteriums konnten Lebensdauern mittels Zeit-Temperatur-Verschiebung bestimmt werden. Im Rahmen dieser Arbeit wurden zahlreiche Erkenntnisse darüber gewonnen, worauf bei beschleunigten Alterungsversuchen und Lebensdauerprognosen von O-Ringen zu achten ist und welche Fehlerquellen vermieden werden sollten. Dies wird zusammen mit Empfehlungen für eine bestmögliche Versuchsdurchführung ausführlich diskutiert. N2 - In some applications, elastomer seals have to remain leak tight over extended time periods (up to several decades) as an exchange of the seals is not practical. Therefore, it is necessary to be able to predict the lifetime of such seals reliably. For this reason, ageing experiments with O-rings and sheets based on hydrogenated acrylonitrile butadiene rubber (HNBR), ethylene propylene diene rubber (EPDM) and fluorocarbon rubber (FKM) were performed over up to two years at different temperatures. For investigating the changes of material properties during ageing, measurements of i.a. hardness and tensile behaviour as well as dynamic-mechanical and thermogravimetric analyses were conducted. For assessing the relaxation and recovery behaviour of the ageing seals, compression stress relaxation and compression set experiments were performed. Furthermore, leakage rate was measured to detect seal failure. By examining the aged samples, both the property changes and the responsible degradation mechanisms were characterised. Additionally, the most suitable approach for lifetime predictions should be determined using the large database of results from different test methods performed at several ageing times and temperatures. This included identifying an end-of-lifetime criterion that correlates with leakage and thus seal failure. Regarding the property changes and degradation mechanisms of HNBR, a pronounced embrittlement was observed due to dominant crosslinking reactions during ageing. These also resulted in a decrease of oxygen permeability, leading to a reduction of the oxygen transport into the interior sample (mainly of the thicker O-rings). This resulted in diffusion-limited oxidation effects (DLO effects), meaning that the interior of the sample aged less strongly than regions close to the surface. During ageing of EPDM, both chain scission and crosslinking occurred, which became noticeable in deteriorated tensile properties and decreased compression force as well as an increase of compression set. For strongly aged samples, crosslinking dominated as well and also led to pronounced DLO effects. Due to its excellent heat and oxidative stability, FKM exhibited comparatively minor degradation effects. Only compression stress relaxation and compression set showed notable changes. Measurements of static leakage rate revealed that O-rings became untight only after advanced degradation and that no gradual increase of leakage rate could be observed before failure. For this reason, additional leakage measurements were performed using a modified experiment that enabled a small decompression of the seal during the measurement. As this test requires a dynamic recovery of the seal and is thus more demanding, the tested EPDM O-ring failed earlier compared to the purely static test. The corresponding ageing state was defined as the point of failure and correlated to data from other test methods, corresponding e.g. to a compression set of 80 %. Based on this criterion, the lifetimes could be determined using the time-temperature superposition approach. During this work, a number of findings regarding the best way to conduct accelerated ageing experiments and lifetime predictions of O-rings, and how to avoid possible error sources, were collected and are discussed in detail. KW - Elastomer KW - Gummi KW - Degradation KW - Leckage KW - Verpressung KW - Rubber KW - Aging KW - Lifetime prediction KW - Leakage PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-397374 DO - https://doi.org/10.14279/depositonce-5827 SP - 1 EP - 121 PB - Technische Universität CY - Berlin AN - OPUS4-39737 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schumacher, David T1 - Zerstörungsfreie Prüfung mit photonenzählenden und spektralauflösenden Röntgenmatrixdetektoren am Beispiel von Werkstoffverbunden N2 - Diese Arbeit beschäftigt sich mit den Eigenschaften der photonenzählenden und spektralauflösenden Detektortechnik und möglichen Anwendungsgebieten in der zerstörungsfreien Prüfung. Dabei wurden konventionelle und photonenzählende Detektortechniken hinsichtlich der Bildqualität und Anwendbarkeit bei unterschiedlichen Prüfaufgaben verglichen und untersucht, inwiefern sich die Energieschwellwertsetzung auf die erreichbare Bildqualität und eine Materialdiskriminierbarkeit bei verschiedenen radiographischen Verfahren auswirkt. Anhand von Anwendungsbeispielen wurden diese Eigenschaften und deren Auswirkung auf das Messergebnis analysiert. Neben der Radiographie wurden auch dreidimensionale Verfahren wie CT und Laminographie berücksichtigt. Als eine der wichtigsten Eigenschaften der photonenzählenden Detektortechnik wurden zunächst die Energieauflösung des photonenzählenden Detektors und die Homogenität der Energieantwort über größere Detektorbereiche bestimmt. Dabei stellte sich heraus, dass die Energieauflösung eines abgegrenzten Detektorbereichs ca. 32 % bei 60 keV beträgt und die Streuung in der Energieantwort der einzelnen Detektorbereiche ca. 12 % ausmacht, woraus sich eine Gesamtunsicherheit in der spektralen Detektorantwort von ca. 44 % ergibt. Die geringe Energieauflösung und das stark heterogene Verhalten der Detektorbereiche ergeben sich vor allem aus der Detektorelektronik, welche nur eine globale Energieschwellwertsetzung zulässt. Trotz dieser Einschränkungen konnte demonstriert werden, dass auch konventionelle radiographische Verfahren, wie Radiographie oder CT, vom Einsatz der photonenzählenden Technik profitieren. So ist es mit dieser Technik möglich, bei sehr geringen Dosisleistungen (z.B. aufgrund der Durchstrahlung großer Wandstärken von dichten Materialien) noch sehr gute Bildqualitäten zu erreichen. Die hohe Dynamik und Kontrastempfindlichkeit dieser Technik begünstigen die Inspektion von Leichtbauwerkstoffen wie Faserverbunde, was anhand von Vergleichen mit herkömmlicher Detektortechnik und anderen ZfP-Verfahren gezeigt werden konnte. Daneben konnte durch den Einsatz der Energieschwellwertsetzung der Einfluss von nicht bildzeichnender Streustrahlung im Röntgenbild um bis zu 20 % reduziert werden. Die Auswirkungen von Aufhärtungseffekten in der CT konnten sogar um bis zu Faktor 1 000 (in der mittleren quadratischen Abweichung), im Vergleich zu herkömmlicher Detektortechnik, reduziert werden. Der Einsatz von photonenzählender Detektortechnik mit Röntgenblitzröhren ist hingegen nicht sinnvoll, da aufgrund der hohen Photonendichte pro Puls und einer endlichen Totzeit des Detektors in der Größenordnung der Pulsbreite eines Blitzes nur ein geringes Signal detektiert werden kann. Im Hinblick auf eine Materialdiskriminierbarkeit konnte demonstriert werden, dass im Fall einer Radiographie anhand der Energieschwellwertsetzung im Detektor eine materialstärkenunabhängige Diskriminierung zwischen zwei Materialien (hier: Al und Fe) erzielt werden kann. Unter Einsatz mehrerer Energiefenster und eines Verfahrens der explorativen und multivariaten Datenanalyse konnte eine materialaufgelöste CT eines Multi-Material-Phantoms erreicht werden, wobei die Schwächungskoeffizienten der enthaltenen Materialien im relevanten Energieberiech teilweise sehr dicht beieinander lagen. Neben Radiographie und CT wurde auch die Möglichkeit einer materialaufgelösten Laminographie am Beispiel eines glasfaserverstärkten Rotorblatts untersucht. Anhand der Energieschwellwertsetzung war nicht nur eine eindeutige Trennung der Glasfasern von der Epoxidharzmatrix möglich, sondern auch eine signifikante Reduzierung der durch die Laminographie entstandenen Artefakte. Der damit verbundene Gewinn an Information führt zu einer verbesserten Aussagefähigkeit des Untersuchungsergebnisses, was letztendlich eine gesteigerte Betriebssicherheit zur Folge hat. N2 - This thesis investigates the properties of photon counting and energy discriminating digital detector arrays and possible applications in the field of non-destructive testing. Conventional integrating detector technology was compared with photon counting technology in terms of image quality and applicability in different inspection tasks. The impact of internal energy thresholding on material discriminability and achievable image quality was investigated for different radiological methods. The properties of photon counting detectors and their impact on the measurement result were analyzed for different applications including three-dimensional methods such as CT and laminography in addition to radiographic testing. Energy resolution is one of the most important properties of photon counting technology. Therefore, energy resolution was initially determined in addition to the homogeneity of the energy Response across the detector. It was found that the energy resolution amounts to approx. 32 % for a 60 keV monoenergetic spectrum (241Am). In combination with the variance in the response of single detector tiles of approx. 12 % the total uncertainty in the detector energy response appears to approx. 44 %. This low energy resolution and strongly heterogenous detector response result mainly from the detector electronics which only allow setting global energy thresholds. Despite these limitations it was demonstrated that even conventional single energy techniques, such as radiography or CT, benefit from photon counting technology. Thus, this technology allows to gain high quality images even at very low dose rates which might occur e.g. at high wall thickness Penetration of dense materials. The high dynamic range and high contrast sensitivity facilitate the inspection of lightweight materials such as fiber composites which was shown by comparison with integrating technology and other NDT methods. Furthermore, the use of energy thresholding enables to reduce the influence of non-imaging scattered radiation within the X-ray image by about 20 %. The impact of beam hardening artefacts in CT was reduced even up to a factor of 1 000, compared to conventional integrating detector technology. In contrast, the use of photon counting technology with x-ray flash tubes is not useful, since the high photon density within a single flash and a finite dead time of the detector only yield a very low signal. In terms of material discriminability, it was shown that due to energy thresholding a thickness Independent material separation between two materials (here: Al and Fe) can be achieved in the case of a radiography. By using more than two energy windows in combination with multivariate methods of data analysis, a material resolved CT of a multi-material phantom was performed in which six materials were separated distinctly despite very close attenuation coefficients in the relevant energy range. In addition to radiography and CT, the possibility of a material resolved laminography was investigated by means of a glass fiber reinforced wind turbine blade. In addition to a distinct separation between glass fibers and resin matrix, a significant reduction of cross artefacts that inherently arise from the laminography could be achieved. This gain in information yields a higher significance of the measurement and hence an increased reliability of the component or the whole system. T3 - BAM Dissertationsreihe - 165 KW - Zerstörungsfreie Prüfung KW - Photonenzählende Detektoren KW - Radiographie KW - Laminographie KW - Computer-Tomographie KW - Dual-Energy KW - Nondestructive testing KW - Photon counting detectors KW - Radiography KW - Laminography KW - Computed tomography KW - Dual energy PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-500327 SN - 1613-4249 VL - 165 SP - 1 EP - 172 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-50032 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Jürgens, Maria T1 - Verhalten des hochwarmfesten Stahles P92 unter zyklischen thermo-mechanischen Bedingungen in lastflexiblen Dampfkraftwerken N2 - Die Erzeugung von Erneuerbaren Energien unterliegt starken Schwankungen, die von konventionellen Kraftwerken ausgeglichen werden müssen, um das Stromnetz stabil zu halten. Für die konventionellen Kraftwerke bedeutet dies eine zunehmend zyklische Fahrweise, die zu häufigeren Last- und Temperaturwechseln führt. Von den eingesetzten Werkstoffen fehlen Daten zum Verhalten unter zyklischer Fahrweise. Ziel dieser Arbeit ist es daher, für P92, einen als Rohrleitungswerkstoff eingesetzten hochwarmfesten Stahl, zu untersuchen, welche Auswirkungen zyklische Fahrweisen auf die Schädigungsprozesse und Lebensdauern haben. Da durch den zyklischen Betrieb eine verstärkte Schädigung durch Ermüdungsprozesse zu erwarten ist, wurden dehnungskontrollierte isotherme (LCF) und nicht-isotherme (TMF) Ermüdungsversuche mit und ohne Haltezeit bei verschiedenen Temperaturen bzw. Temperaturintervallen durchgeführt. Mit den Haltezeitversuchen soll dabei das Kriech-Ermüdungs-Verhalten untersucht werden. Bei den TMF-Versuchen wurde zusätzlich die Temperaturrate variiert, um näher an den realen Lastwechselgeschwindigkeiten zu prüfen. Schließlich wurden auf Basis der durchgeführten LCF- und TMF-Versuche betriebsnahe Versuchsprozeduren entwickelt, um unterschiedliche Betriebsmodi in einem Versuch abzubilden. Die durchgeführten mechanischen Versuche stellen eine umfangreiche Basis zu Ermüdungsdaten an P92 dar. Neben der Abhängigkeit der Lebensdauer von Temperatur, Temperaturintervall und –rate, sowie Dehnung und Haltezeit, konnte auch das Entfestigungsverhalten genauer charakterisiert werden. Sowohl Haltezeiten als auch das Reduzieren der Temperaturrate können die Lebensdauer erheblich verringern. Dabei kommt es gerade bei vermeintlich kleinen Dehnungen, bei denen die Streckgrenze nur leicht überschritten wird, zu einer Lebensdauerreduzierung. Haltezeiten verstärken zudem die zyklische Entfestigung. Die fraktographische Analyse der Proben hat ergeben, dass es keinen direkten Zusammenhang zwischen der Entfestigung und der Bildung von Nebenrissen gibt. Stattdessen zeigen EBSD- und TEM-Untersuchungen, dass es zur Bildung einer Subkornstruktur kommt und die Entfestigung auf dem Verschwinden von Kleinwinkelkorngrenzen beruht. Während bei den LCF-Proben eine reine Ermüdungsschädigung vorliegt, konnte bei einigen TMF-Proben eine kriechdominierende Schädigung nachgewiesen werden. Die betriebsnahen Zyklen zeigen, dass sich mit den durchgeführten Versuchen das reale Betriebsverhalten gut abschätzen lässt. Da es jedoch auch Parameterkombinationen gibt, bei denen keine Änderung des Entfestigungs- und Lebensdauerverhaltens auftritt, sollte genau bekannt sein, welche Belastungen in einem Bauteil auftreten. KW - P92 KW - LCF KW - TMF KW - Energiewende KW - Kriechermüdung KW - Energy transition KW - Creep-fatigue PY - 2020 DO - https://doi.org/10.14279/depositonce-10538 SP - 1 EP - 144 CY - Berlin AN - OPUS4-51571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Stengel, Dominik T1 - Naturmessungen und numerische Simulationen zur Untersuchung von Freileitungsseilen im natürlichen Wind N2 - Für Tragmasten von Freileitungen ist meist die Windeinwirkung bemessungsrelevant. Mit den großen Spannweiten der Hochspannungsebene trägt dabei die Windeinwirkung auf die Leiterseile einen maßgebenden Anteil zur Gesamtbeanspruchung dieser Tragstrukturen bei. Daher ist es offensichtlich, dass das Tragverhalten der Freileitungsseile eine wichtige Rolle für die zuverlässige Bemessung bei Neubauten oder der Bewertung der Zuverlässigkeit des Bestands spielt. Hierfür sind insbesondere die Extremwindereignisse, das sog. 50-Jahres-Windereignis von Bedeutung. Bei diesen hohen Windgeschwindigkeiten treten vor allem windinduzierte Schwingungen der Leiterseile auf. Die für die Bemessung herangezogenen Konzepte basieren meist auf Übertragungsmodellen im Frequenzbereich. Diese setzen eine Linearisierung um den Arbeitspunkt der mittleren Verschiebung voraus, welche nur unter der Annahme von kleinen Schwingungsamplituden gerechtfertigt ist. Dabei kommt der Systemdämpfung eine wichtige Rolle zu. Zwar ist die Strukturdämpfung für Litzenseile vernachlässigbar gering, doch unter Windeinwirkung kann die aerodynamische Dämpfung aufgrund der Relativgeschwindigkeit zwischen Anströmung und Struktur zu beachtlicher Größe anwachsen. Die Beschreibung des Tragverhaltens im Zeitbereich erlaubt es, das nichtlineare Verhalten der Kraftübertragung, sowie der großen Verformungen zu berücksichtigen. Damit lassen sich für die Bemessung relevante Parameter identifizieren und notwendige Annahmen zur Windeinwirkung, sowie zur quasistationären Kraftübertragung überprüfen. Gerade das Verhalten von Freileitungsseilen unter Extremwindereignissen, auf das es zu Extrapolieren gilt, kann so im Rahmen der getroffenen Annahmen simuliert werden. Anhand von Naturmessungen werden die Übertragungsmodelle, sowie das Zeitbereichsmodell bei eher moderaten Windgeschwindigkeiten überprüft. Durch die Verteilung von Windsensoren entlang der Leitung kann die für die Belastung der Leiterseile maßgebende laterale Windverteilung annähernd erfasst werden. Bestehende Annahmen hierzu werden überprüft und erweitert. Für die Zeitbereichsrechnungen wird eine Methode zur Windfeldgenerierung dahingehend erweitert, dass die Windereignisse auch adäquat im Zeitbereich wiedergegeben werden können. Mit dem Ziel, eine zuverlässigere Bemessung von Freileitungen unter turbulenter Windbeanspruchung zu erreichen, werden sog. Spannweitenfaktoren abgeleitet und auf andere Leitungskonfigurationen übertragen, die die Mechanik der Leiterseile sowie die maßgebenden Eigenschaften der Windeinwirkung beinhalten. N2 - Regarding suspension towers of overhead transmission lines, wind is the most critical load case in design. Wind action on conductors significantly contributes to the overall loading of those supporting structures in case of wide spanning cables used in high voltage level. Hence it is inherent that loadbearing characteristic of conductor cables plays an important role for reliable design of new constructions or evaluation of reliability level of existing structures. Therefor extreme wind situations, a so-called 50-years wind event is of particular interest. Under such high wind velocities, mainly wind induced vibrations of conductor cables occur. Concepts employed for design purpose are mostly based on admittance functions in frequency domain. This implies linearization around the operating position of mean deflection, which is only valid for the assumption of small vibration amplitudes. Herein damping of the system becomes important. Structural damping of stranded wires is indeed negligible low, but in case of wind action aerodynamic damping increases significantly due to the relative velocity between acting wind flow and structure. The description of loadbearing characteristics in time domain allows considering nonlinear behavior of force admittance as well of large displacements. Relevant parameters for design can thereby be identified and necessary assumptions on wind action as well as quasi-steady force admittance can be validated. Just by that the behavior of overhead transmission line cables under extreme wind events which need to be extrapolated, can be simulated by means of the assumptions made. Models of admittance as well as a model in time domain are validated by means of field measurements at rather moderate wind speeds. Distributing wind sensors along an overhead transmission line, the lateral distribution of wind which is decisive for the loading of conductor cables can be captured. Existing assumptions for this are validated and extended. For calculations in time domain, a method for generation of a wind field will be extended in order to reproduce wind events adequately also in time domain. Aiming at a reliable design of overhead transmission lines under turbulent wind, so-called span reduction factors are derived and converted to other transmission line configurations which include the mechanics of overhead line conductors as well as the predominant characteristics of wind loading. T3 - BAM Dissertationsreihe - 150 KW - Hochspannungsleiter KW - Windbelastung KW - Naturmessungen KW - Windkanalversuche KW - Finite Element Methode PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-372171 SN - 978-3-9817853-7-1 SN - 1613-4249 VL - 150 SP - I EP - 126 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-37217 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Herbst, Tristan T1 - Konzept zur ganzheitlichen Nachhaltigkeitsbewertung des Abbruchs und der Aufbereitung von Mauerwerk N2 - Mit der vorliegenden Arbeit wurde ein methodisches Konzept zur ganzheitlichen Nachhaltigkeitsbewertung des Abbruchs und der Aufbereitung von Mauerwerk bereitgestellt. Das Bewertungskonzept ermöglicht einen ganzheitlichen Vergleich verschiedener Szenarien für den Abbruch und die Aufbereitung von Mauerwerk unter Berücksichtigung der Anwendung von Mauerwerkbruch und aussortierter Fremdstoffe zur Verwertung. Es kombiniert die Kosten-Wirksamkeitsanalyse, die Stoffflussanalyse, die Ökobilanzierung, die Betrachtung sozialer Aspekte und Wirtschaftlichkeitsbetrachtungen bei gleichzeitiger Berücksichtigung der Materialqualitäten. Das Bewertungskonzept basiert im Kern auf der Kosten-Wirksamkeitsanalyse (KWA) mit der Erweiterung um das Gesamtwirksamkeitswert-Kosten-Verhältnis. Hiermit können sowohl monetäre als auch nicht monetäre Effekte beurteilt werden. Ausgangspunkt der KWA ist ein klar definiertes Zielsystem. Im vorliegenden Fall wurden aus der EU-Abfallrahmenrichtlinie, dem Kreislaufwirtschaftsgesetz und der EU-Bauproduktenverordnung die vier Generalziele „Mensch und Umwelt“, „Ressourcenschonung“, „Ausreichende Materialqualität“ sowie „Wirtschaftlichkeit“ abgeleitet. Die Generalziele "Mensch und Umwelt" und "Ressourcenschonung" wurden weiter in Hauptziele, Ziele und Unterziele unterteilt. Die Quantifizierung und Beurteilung dieser beiden Generalziele erfolgt im Rahmen der Wirksamkeitsanalyse. Zur Quantifizierung der abstrakten Ziele wurden konkrete und messbare Zielkriterien ausgewählt, die üblicherweise bei der Ökobilanzierung und sozialorientierten Betrachtungen verwendet werden, z. B. Umweltauswirkungen, Material- und Energieverbrauch. Nach Ermittlung einer Gesamtwirksamkeit und den anfallenden Kosten für jedes Szenario wird das Gesamtwirksamkeit-Kosten-Verhältnis je Szenario errechnet. Dieses Verhältnis bildet die Grundlage für die abschließende Reihung der untersuchten Szenarien entsprechend ihrer nachhaltigkeitsbezogenen Wertigkeit im Sinne der europäischen und deutschen Kreislaufwirtschaft. Mit dem Konzept wird zukünftigen Nutzern eine strukturierte und methodische Bewertungsgrundlage als Planungsinstrument für Abbruchprojekte an die Hand gegeben. Gleichzeitig werden die Nutzer für bestehende Gestaltungsvarianten für den Abbruch und die Aufbereitung von Mauerwerk sowie für die vielfältigen Anwendungsmöglichkeiten von Mauerwerkbruch sensibilisiert. T3 - BAM Dissertationsreihe - 151 KW - Nachhaltigkeit KW - Kosten- und Wirksamkeitsanalyse KW - Mauerwerkbruch KW - Abbruch KW - Aufbereitung PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-384853 SN - 978-3-9817853-8-8 SN - 1613-4249 VL - 151 SP - 1 EP - 146 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-38485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Drzymala, Sarah T1 - Instrumental analysis, metabolism and toxicity of cis- and trans-zearalenone and their biotransformation products N2 - Trans-Zearalenone(ZEN)is a non-steroidal estrogenic mycotoxin which frequently contaminates cereal grains worldwide. Ingestion of food and feed containing ZEN causes numerous mycotoxicoses in animals and possibly humans with pronounced estrogenic effects. Due to the trans-configurated double bond, ZEN isomerizes to the cis-configuration upon the influence of light. This work investigates the instrumental analysis, metabolism and toxicity of ZEN and cis- ZEN. The first part focused on the determination of ZEN in edible oils. Due to a maximum level of 400 µg/kg ZEN in the European Union (EU), reliable analytical methods are needed. A comprehensive method comparison proved dynamic covalent hydrazine chemistry (DCHC) to be the most suitable approach. Thus, an automated solid phase extraction (SPE) coupled online to high performance liquid chromatography (HPLC) was developed with the novelty of a covalent SPE step comprising the DCHC principle. The automated online system allows an accurate, selective and reliable quantification of ZEN in edible oils in compliance with EU performance criteria while significantly reducing workload and thereby personnel costs. In contrast to ZEN, reference standards and analytical methods are missing for cis- ZEN which causes a lack of data on the occurrence, fate and risks of cis-ZEN. Therefore, a native and an isotopically labeled cis-ZEN standard were synthesized and implemented in an existing stable isotope dilution analysis HPLC tandem mass spectrometry (HPLC-MS/MS) method. Using this method, a large extent of cis-ZEN formation was observed for ZEN contaminated maize germ oils when exposed to daylight which confirms that cis-ZEN can be a relevant food contaminant and should be considered in the analysis of food and feed. Furthermore, this work investigated the in vitro phase I metabolism of ZEN and cis-ZEN in rat and human liver microsomes by using HPLC-MS and -MS/MS analyses. The metabolic pathways of cis-ZEN were found to be essentially similar to ZEN including reduction and oxidation reactions generating α- and β-cis- zearalenol as well as 13- and 15-OH-cis-ZEN. A previously unidentified oxidative metabolic pathway for both isomers of ZEN results in the formation of cis-ZEN-11,12-oxide and ZEN-11,12-oxide in human liver microsomes. The estrogenicity of cis-ZEN and its reductive metabolites was assessed using the E-Screen assay. cis-ZEN proved to be slightly more estrogenic than ZEN. Biotransformation of cis-ZEN to β-cis-ZEL corresponds to a detoxification, whereas metabolism to α-cis-ZEL resembles a metabolic activation as its estrogenicity considerably exceeds that of cis-ZEN. The catecholic metabolites can be expected to show a decreased estrogenicity as demonstrated for 15-OH- ZEN. Independent of the estrogenic effects, the catecholic and epoxidic metabolites identified in this work can be expected to act genotoxic and carcinogenic. The epoxides in particular could fundamentally change the widely accepted view of ZEN causing adverse effects exclusively through endocrine disrupting actions. T3 - BAM Dissertationsreihe - 152 KW - Hydrazinchemie KW - Isotopenstandard KW - SPE-HPLC Automatisierung KW - Zearalenon KW - Isomerisierung PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-386016 SN - 978-3-9817853-9-5 SN - 1613-4249 VL - 152 SP - 1 EP - 160 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-38601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Sobol, Oded T1 - Hydrogen assisted cracking and transport studied by ToF-SIMS and data fusion with HR-SEM N2 - For almost 150 years it is known that hydrogen has a deleterious effect on the mechanical properties of metallic components. Nowadays, the problem of hydrogen assisted degradation is highly relevant in energy related fields due to the massive use of steel as a structural component in these applications and its sensitivity to hydrogen. Since the discovery of hydrogen assisted cracking (HAC), researchers studied intensively and suggested possible explanations and mechanisms in order to define how hydrogen is affecting the material. In general, it is considered that hydrogen changes the mechanical properties more in terms of ductility (deformation capacities) than in strength (load capacities). Hydrogen concentration is one of three crucial factors in the degradation process, together with the microstructure of the material and the internal/external mechanical load. The relatively high concentration of hydrogen resulting in this loss of ductility can originate during production or before service (e.g. welding processes) and during service (i.e. catholically protected systems to eliminate corrosion processes in sour environments). In parallel to the theoretical work, tremendous efforts were, and are still, invested in searching for a proper method to elucidate, map and quantify the hydrogen in the microstructure, which is the basis for this work. For steels, the focus is mainly on the observations of diffusion processes and the interaction of hydrogen with the microstructure in regions with high local stresses/strains (for example around evolving cracks). The challenge for reaching this goal arises from the fact that accurate indication of hydrogen by means of position, unlike heavier atoms, can be made only by mass spectrometry or by interaction with another element (e.g. silver decoration, special coating and resonant nuclear reaction by nitrogen). In addition to this, the difficulty recording the hydrogen behavior while it rapidly diffuses through the material, leaving only the unpredicted failure, should be taken into account. Although using powerful characterization methods, models and computational simulations, the key to defining the mechanisms behind HAC is still under debate and not fully understood. The relationship between material and hydrogen is determined by three factors, i.e., the material structure and microstructure – determining the physical properties, the mechanical load applied on the material and the hydrogen concentration. It is well known that in order to have a complete definition of HAC these three factors must be examined locally with the minimal scale and the maximal resolution reachable. The major gap is the lack in such a characterization method or a technique by which one has the ability to detect and observe the hydrogen in the metallic microstructure. The commonly used techniques nowadays are capable of characterization of the microstructure without the ability to observe the hydrogen distribution. Global hydrogen concentration and localized hydrogen observation are possible by some techniques which are incapable of indicating a change in the structure or microstructure therefore a comprehensive overview can be gained only by combining several methods. In the presented research, secondary ion mass spectrometry (SIMS) was adopted as the main tool to detect and locally map the hydrogen distribution in two types of duplex stainless steel grades: EN 1.4462 (standard 2205 duplex stainless steel) and EN 1.4162 (2101 lean duplex stainless steel). The term duplex stainless steel (DSS) refers to the austenitic-ferritic microstructure of the steel where the combination of physical and mechanical properties of the two phases is achieved. The DSS was selected as a case study for this work due to the wide use of this grade in many energy and the lack of knowledge on hydrogen behavior in two-phase containing microstructures. ToFSIMS was exploited in-situ and ex-situ in three experimental approaches during or following an electrochemical charging procedure. This type of hydrogen charging was selected as it simulated a procedure of cathodic protection of most sub-water oil and gas extraction and delivery systems. The experimental procedures were: 1. Ex-situ charging followed by ToF-SIMS imaging for basic understanding of hydrogen distribution. 2. Ex-situ charging followed by in-situ mechanical loading to obtain information on hydrogen behavior around a propagating crack. 3. In-situ permeation of hydrogen through a steel membrane inside the ToF-SIMS to obtain information on diffusion behavior of hydrogen in a two-phase microstructure. The comprehensive view of the effect of hydrogen on steel was gained by using supplementary methods, such as high resolution scanning electron microscopy (HR-SEM), focused ion beam (FIB) and electron back-scattered diffraction (EBSD). The state of the art in this work lies in applying both: in-situ experimental approaches and data treatment of the ToF-SIMS raw data. The data treatment includes the combination of data from several sources (data fusion). The results for the ex-situ charging followed by static sample imaging and data fusion showed that when the analyzed surface is directly exposed to the electrolyte the degradation is pronounced differently in the ferrite, austenite and interface. The degradation mechanisms in the ferrite and austenite were reflected by the formation of cracks on the surface of both, where a high concentration of hydrogen was obtained. This result supports the assumption that hydrogen is attracted to highly deformed regions. The advantage of using in-situ charging/permeation in comparison to ex-situ charging is that the effect of hydrogen on the ferrite and austenite phases when the hydrogen is evolving from within the microstructure is realized, in comparison to when the analyzed surface is initially exposed directly to the electrolyte. In both experiments the ferrite was observed as a fast diffusion path for the hydrogen. The faster diffusion of hydrogen through the ferrite is expected due to the higher diffusion coefficient, however, a direct proof for the diffusion sequence in this scale was never shown. Most significant results were achieved by the ‘core’ experiments of this research. These experiments included the design of a novel dynamic mechanical loading device to apply an external load during SIMS imaging of a hydrogen precharged-notched sample. For the first time it was shown that plastic deformation induced by applying a mechanical load is resulting in a redistribution of hydrogen locally around the notch. T3 - BAM Dissertationsreihe - 160 KW - Duplex stainless steels KW - Hydrogen assisted cracking KW - Time-of-Flight secondary ion mass spectrometry KW - Data fusion PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-447331 SN - 1613-4249 VL - 160 SP - I EP - 180 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-44733 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schneider, Ronald T1 - Time-variant reliability of deteriorating structural systems conditional on inspection and monitoring data N2 - The current practice of operating and maintaining deteriorating structural systems ensures acceptable levels of structural reliability, but it is not clear how efficient it is. Changing the current prescriptive approach to a risk-based approach has great potential to enable a more efficient management of such systems. Risk-based optimization of operation and maintenance strategies identifies the strategy that optimally balances the cost for controlling deterioration in a structural system with the achieved risk reduction. Inspections and monitoring are essential parts of operation and maintenance strategies. They are typically performed to reduce the uncertainty in the structural condition and inform decisions on future operation and maintenance actions. In risk-based optimization of operation and maintenance strategies, Bayesian updating is used to include information contained in inspection and monitoring data in the prediction of the structural reliability. All computations need to be repeated many times for different potential inspection and monitoring outcomes. This motivates the development of robust and efficient approaches to this computationally challenging task. The reliability of deteriorating structural systems is time-variant because the loads on them and their capacities change with time. In most practical applications, the reliability analysis of deteriorating structural systems can be approached by dividing their lifetime into discrete time intervals. The time-variant reliability problem can then be represented by a series of time-invariant reliability problems. Using this methodology as a starting point, this thesis proposes a novel approach to compute the time-variant reliability of deteriorating structural systems for which inspection and monitoring data are available. The problem is formulated in a nested way in which the prediction of the structural condition is separated from the computation of the structural reliability conditional on the structural condition. Information on the structural condition provided by inspections and monitoring is included in the reliability assessment through Bayesian updating of the system deterioration model employed to predict the structural condition. The updated system reliability is obtained by coupling the updated deterioration model with a probabilistic structural model utilized to calculate the failure probability conditional on the structural condition. This approach is the first main outcome of this thesis and termed nested reliability analysis (NRA) approach. It is demonstrated in two numerical examples considering inspected and monitored steel structures subject to high-cycle fatigue. An alternative – recently developed – approach, which also follows the strategy of discretizing time, describes deteriorating structural systems with hierarchical dynamic Bayesian networks (DBN). DBN combined with approximate or exact inference algorithms also enable the computation of the time-variant reliability of deteriorating structural systems conditional on information provided by inspection and monitoring data. In this thesis – as a proof of concept – a software prototype is developed based on the DBN approach, which can be used to assess the reliability of a corroding concrete box girder for which half-cell potential measurements are available. This is the second main outcome of this thesis. Both approaches presented in this thesis enable an integral reliability analysis of inspected and monitored structures that accounts for system effects arising from (a) the correlation among deterioration states of different structural elements, (b) the interaction between element deterioration and system failure, and (c) the indirect information gained on the condition of all unobserved structural elements from inspecting or monitoring the condition of some structural elements. Thus, both approaches enable a systemwide risk-based optimization of operation and maintenance strategies for deteriorating structural systems. The NRA approach can be implemented relatively easily with subset simulation, which is a sequential Monte Carlo method suitable for estimating rare event probabilities. Subset simulation is robust and considerably more efficient than crude Monte Carlo simulation. It is, however, still sampling-based and its efficiency is thus a function of the number of inspection and monitoring outcomes, as well as the value of the simulated event probabilities. The current implementation of the NRA approach performs separate subset simulation runs to estimate the reliability at different points in time. The efficiency of the NRA approach with subset simulation can be significantly improved by exploiting the fact that failure events in different years are nested. The lifetime reliability of deteriorating structural systems can thus be computed in reverse chronological order in a single subset simulation run. The implementation of the DBN approach is much more demanding than the implementation of the NRA approach but it has two main advantages. Firstly, the graphical format of the DBN facilitates the presentation of the model and the underlying assumptions to stakeholders who are not experts in reliability analysis. Secondly, it can be combined with exact inference algorithms. In this case, its efficiency neither depends on the number of inspection and monitoring outcomes, nor on the value of the event probabilities to be calculated. However, in contrast to the NRA approach with subset simulation, the DBN approach with exact inference imposes restrictions on the number of random variables and the dependence structure that can be implemented in the model. T3 - BAM Dissertationsreihe - 168 KW - Reliability KW - Structural systems KW - Deterioration KW - Bayesian analysis KW - Inspection KW - Monitoring KW - Zuverlässigkeit KW - Tragstrukturen KW - Schädigungsprozesse KW - Bayes'sche Analyse KW - Inspektion KW - Monitoring PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512977 SN - 1613-4249 VL - 168 SP - 1 EP - 188 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-51297 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kanzler, Daniel T1 - Zuverlässigkeitsanalyse von digitalen Radiographie-Systemen bei der Prüfung von realen Materialdefekten N2 - Die zerstörungsfreie Prüfung (ZfP) ist aus solchen Bereichen unseres Lebens nicht mehr wegzudenken, in denen Schäden mit hohen Folgekosten oder Gefährdungen von Menschenleben entstehen können (Beispiele: Transportwesen, Energieerzeugung, Chemieindustrie). In der Praxis kann ein Prüfsystem an seine Grenzen geraten, z.B. bei kleinen Defekten. Defekte mit kritischer Größe werden möglicherweise nicht detektiert. Daher müssen probabilistische Bewertungsverfahren das Prüfsystem beschreiben. Es wird eine objektive Qualitätskennzahl gesucht, auf deren Basis die Anwendbarkeit der Prüfmethode definiert werden soll. Die Auffindwahrscheinlichkeit (engl. probability of detection - POD) erfüllt diese Anforderung. Die POD zeigt auf Basis des Zusammenhangs und der Streuung der Daten, ob das Verfahren für die Prüftätigkeit akzeptiert werden kann oder noch verbessert werden muss. Das ursprüngliche POD-Verfahren wurde für quasi eindimensionale Defekte in dünnen Luftfahrtbauteilen entwickelt. In der industriellen Realität ist diese Bewertung ein Balanceakt zwischen Statistik und Durchführbarkeit: Die Prüfung soll mit realen Defektdaten für die spätere Produktion des Bauteils (bzw. wiederkehrende Wartungsprüfung) bewertet werden. Doch die notwendige Gegenüberstellung zwischen Schliffdaten, für die Erfassung der wahren Defektgröße von räumlich ausgeprägten Defekten und dem Signal eines ZfP-Systems stellt sich als herausfordernde und kostenintensive Aufgabe heraus. Sowohl die Aufstellung eines gemeinsamen Koordiantensystems als auch die Beschreibung und Angleichung der Daten stellen eine notwendige Vorarbeit dar. In dieser Arbeit wird ein mögliches Vorgehen entwickelt, dass im Weiteren eingesetzt werden kann. Während in der Literatur zum Thema POD häufig die Begrenzung des Einsatzes einer eindimensionalen POD (POD mit einem Defektparameter) für reale Defekte bereits erkannt wurde, soll außerdem in dieser Arbeit das Verfahren auf der Signalseite umfassender erweitert werden, um die Einbeziehung realer Defekte in die POD-Bewertung zu ermöglichen. Hierfür werden mit Hilfe dieser Arbeit zwei wesentliche Neuerungen in der POD-Bewertung eingeführt: 1. Die Anzeigenfläche wird als wichtiges Indiz zur Detektion in die Bewertung eingeführt. Dabei zeigt der Ansatz einer Observer-POD, bei dem der Detektierbarkeit eines Defekts beschrieben wird, eine Möglichkeit in die Bewertung zu erweitern. Jedoch wird die notwendige Datenanzahl die für eine Observer-POD selten mit Experimenten erreicht. Daher schlagen wir die Einführung eines Glättungsalgorithmus vor, um auch auf der Basis von wenigen Daten die Flächenabhängigkeit zu erfassen. Der Algorithmus wird hierbei durch simulierte Daten auf seine Funktionsfähigkeit überprüft, bevor er auf reale Defekte angewendet wird. Gleichzeitig helfen die simulierten Daten einen Vergleich zu den vorhergegangenen Ansätzen zu ermöglichen. 2. Darüber hinaus reichen die Daten der realen Defekte häufig nicht aus, um die statistische Forderung zu gewährleisten, so dass es notwendig, wird künstliche Defekte mit einzubeziehen. Deshalb sollen die vorhanden künstlichen Defekte in Form von Referenzdefekten mit einbezogen werden, um die statistische Grundlage zu erhöhen. Für die Prüfung von Referenzdefekten sind jedoch wichtige Einflussgrößen (z.B. Oberflächenrauhigkeit) nicht vorhanden. Wegen der unterschiedlichen Aussagekraft der Daten und zur Vermeidung einer zu optimistischen Abschätzung, ist eine einfache Mischung der Daten ausgeschlossen. Um realen Defekten eine Möglichkeit dafür zu schaffen, dass die Eigenschaften der realen Defekte angemessen auf das Ergebnis der Bewertung des Verfahrens Einfluss nehmen können, wird eine gewichtete Kombination der Defektdaten für die Bewertung vorgestellt. Das Vorgehen wird am Beispiel der radiographischen Prüfung einer elektronenstrahlgeschweißten Naht durchgeführt. Die Schweißnaht verbindet den Deckel zur Außenwand eines Kupferbehältern, der für die spätere Endlagerung von verbrauchten Brennstäben aus Kernkraftwerken entwickelt wurde. Die Messergebnisse stammen aus von der Firma Posiva Oy, dem zuständigen Unternehmen für die Endlagerung von verbrauchten Brennstäben aus Kernkraftwerken in Finnland. Hierbei stellt die POD-Bewertung ein wichtiges Element in der Gesamtrisikobewertung für das Endlagersystem dar. T3 - BAM Dissertationsreihe - 153 KW - Radiographie KW - POD KW - Zuverlässigkeit KW - Zerstörungsfreie Prüfung (ZfP) KW - Probabilistische Bewertung PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388723 SN - 978-3-9818270-1-9 SN - 1613-4249 VL - 153 SP - iii EP - 134 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-38872 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Eberwein, Robert T1 - Untersuchung der Gefährdung von Personen und Bauwerken in Folge des Versagens von LNG-Kraftstoffspeichern für Fahrzeuge in Tunneln N2 - Liquefied Natural Gas (LNG) aus regenerativen Quellen, stellt einen potenziellen Kraftstoff für den Schwer- und Fernverkehr des Straßenverkehrs dar. Gegenüber seinen positiven Eigenschaften zu dem in diesem Verkehrssektor häufig verwendeten Kraftstoff Diesel birgt der Kraftstoff aber auch Gefahren für Personen und Bauwerke durch seine sehr niedrige Temperatur bei der Speicherung von ca. -160 °C und seine Explosionsfähigkeit in der Gas-Phase. In der Arbeit wurde sich mit der Gefährdung von Personen und Bauwerken hinsichtlich der von LNG ausgehenden Gefahren in Tunneln auseinandergesetzt. Tunnel stellen besonders schützenswerte Bauwerke dar, da aus vorhergehenden Störfällen in Tunneln bekannt ist, dass diese mit hohen Personen-, Bauwerks-, und Volkswirtschaftlichen-Schäden einhergehen können. Untersuchungsschwerpunkt bei der Bewertung von Gefährdungen durch LNG stellte eine Ereigniskaskade bestehend aus Freisetzung, Verdampfung, Stoffausbreitung und Zündung des sich gebildeten explosionsfähigen LNG-Gas/Luft-Gemisches dar. Mit dem Ziel eine solche Ereigniskaskade realitätsnah vorhersagen und zukünftig hierzu Risikoanalysen durchführen zu können wurden innerhalb der Arbeit Parameterstudien sowie Kalibrierungen und Validierungen gegenüber experimentellen Untersuchungen durchgeführt. Mit den Modellen wurden in der Arbeit exemplarische Fallbeispiele zu Störfällen untersucht. Ergebnisse dieser waren, dass Gefährdungen insbesondere von flüssigem LNG nach dessen Freisetzung und der Verbrennung von LNG-Gas/Luft-Gemischen ausgingen. N2 - Liquefied Natural Gas (LNG) from regenerative sources is a potential fuel for heavy and long-distance road traffic. In contrast to its positive properties compared to diesel, which is often used in this transport sector, the fuel also contains hazards from its very low storage temperature of approx. -160 °C and its explosiveness in the gas phase for personal and structural safety. The dissertation dealt with the dangers to persons and infrastructures according to the hazards by LNG in tunnels. Tunnels are especiallyworth protecting structures since it is known from previous incidents in tunnels that they can go hand in hand with high damage to the people, the structure, and the economy. The main focus of the investigation into the assessment of hazards from LNG was an event cascade consisting of release, evaporation, dispersion, and ignition of the explosive LNG-vapor/air-mixture formed. To realistically predict such an event cascade and being able to carry out risk analyzes for this purpose in the future, parameter studies such as calibrations and validations were carried out concerning experimental investigations. Exemplary case studies on incidents were examined in the thesis with the validated models. The results of this were that there were especially hazards in particular from liquid LNG after its release and the combustion of LNG-vapor/air-mixtures. KW - Verflüssigtes Erdgas KW - Erneuerbare Energien KW - Numerische Strömungsmechanik KW - Sicherheitstechnik KW - Liquefied Natural Gas KW - LNG KW - Renewable fuels KW - CFD KW - Safety engineering PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521145 DO - https://doi.org/10.14279/depositonce-11346 SP - 1 EP - 240 PB - TU Berlin CY - Berlin AN - OPUS4-52114 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hesse, Almut T1 - Entwicklung immunchemischer Methoden zur Spurenanalytik der Sprengstoffe Nitropenta und Trinitrotoluol N2 - Pentaerythrityltetranitrat (PETN), ein in jüngster Vergangenheit häufig von Terroristen verwendeter Sprengstoff, ist äußerst schwer zu detektieren. Ein verbesserter Antikörper gegen PETN wurde durch Anwendung des Konzepts des bioisosteren Ersatzes entwickelt,indem ein Nitroester durch einen Carbonsäurediester ersetzt wurde. Biostere Moleküle haben eine ähnliche Struktur wie die Referenzsubstanz und zeigen eine vergleichbare biologische Wirkung. Dieser Ansatz führte zu polyklonalen Antikörpern mit extrem guter Selektivität und Sensitivität. Die Nachweisgrenze des Enzyme-Linked Immunosorbent Assays (ELISAs) beträgt 0,15 μg/L. Der Messbereich des Immunassays liegt zwischen 1 und 1000 μg/L. Die Antikörper sind sowohl hinreichend pH-stabil als auch robust gegen Lösungsmittelzusätze. Das Antiserum könnte auch für Schnelltests, Biosensoren, Mikro-Arrays und andere analytische Methoden verwendet werden. Für die Umweltanalytik von Trinitrotoluol (TNT) wurde eine Hochdruckflüssigkeitschromatographie (HPLC)-kompatible Affinitätssäule hergestellt. Druckbeständiges, poröses Glas hat sich als ein hervorragendes Trägermaterial herauskristallisiert. Um selektive anti-TNT-Antikörper für die Herstellung der Affinitätssäule aus den beiden verwendeten TNT-Seren zu isolieren, wurde eine Trennung an einer Dinitrophenyl-Affinitätssäule durchgeführt. Zur Optimierung der Immobilisierungsmethode wurden orangefarbene Dabsyl -Proteine synthetisiert und auf der Oberfläche gebunden. Die Färbung wurde als Indikator für die Immobilisierungsdichte verwendet. Wegen der hohen Affinitätskonstanten der polyklonalen anti-TNT-Antikörper der beiden Seren (5,1 bzw. 2,3∙109 L/mol) lässt sich TNT durch eine typische saure Elution der TNT-Affinitätssäule nur schwer eluieren. Aus diesem Grund wurde eine neuartige Elutionsmethode entwickelt, die irreversible, denaturierende, thermische Online -Elution. Diese eröffnet ein weites Anwendungsfeld, da so Affinitäten, die klass ischerweise aufgrund zu hoher Bindungskonstanten zwischen Ligand und Rezeptor nicht für die Affinitätschromatographie genutzt werden können, für die Analytik besser handhabbar werden. Die maximale Kapazität einer im Rahmen dieser Arbeit hergestellten Affinitätssäule (64,8 μL) betrug 650 ng TNT bzw. 10 μg/mL Säulenvolumen. Um die Immobilisierungsdichte der produzierten Affinitätssäulen zu bestimmen, wurde ein neues Verfahren entwickelt, da die üblichen spektroskopischen Proteinbestimmungsmethoden aufgrund der hohen unspezifischen Wechselwirkung mit dem Trägermaterial zur Proteinbestimmung nicht geeignet waren. Zur Quantifizierung von Proteinen oder Peptiden,die auf festen Trägern immobilisiert sind, wurde auf Grundlage einer HPLC-Trennung der aromatischen Aminosäuren Tyrosin (Tyr) und Phenylalanin (Phe) ohne vorherige Derivatisierung eine gegenüber der klassischen Aminosäureanalytik vereinfachte HPLC/UV-Methode entwickelt. Die Hydrolyse der Proteine und Peptide wurde durch Einsatz von Mikrowellentechnik beschleunigt, sodass nur 30 Minuten statt ca. 22 Stunden für das Standardprotokoll benötigt wurden, bei dem ein Hydrolyseröhrchen verwendet wird. Zur internen Kalibrierung wurden zwei Standardverbindungen, Homotyrosin (HTyr) und 4-Fluorphenylalanin (FPhe) verwendet. Die Nachweisgrenze (limit of detection, LOD) bei 215 nm ist sowohl für Tyr als auch für Phe 0,05 μM (~ 10 μg/L). Dieses neue Verfahren, das als Aromatische Aminosäureanalyse (Aromatic Amino Acid Analysis, AAAA) bezeichnet werden kann, wurde zur Proteinbestimmung von homogenen Proben mit Rinderserumalbumin (BSA) des Nationalen Instituts für Standards und Technologie der USA (NIST) validiert, wobei die Nachweisgrenze für Proteine mit 16 mg/L (~ 300 ng BSA) mit gängigen spektroskopischen Verfahren vergleichbar ist. Es liefert incl. der Hydrolysestufe eine verbesserte Genauigkeit mit einer relativen Standardabweichung von ca. 5%. T3 - BAM Dissertationsreihe - 158 KW - Affinitätschromatographie KW - Affinity chromatography KW - Polyklonale TNT-Antikörper KW - Immunassay KW - Aromatische Aminosäureanalyse KW - Polyclonal TNT-antibodies KW - Polyclonal PETN-antibodies KW - Immunoassay KW - Aromatic amino acid analysis KW - Polyklonale PETN-Antikörper PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-417566 SN - 1613-4249 VL - 158 SP - I EP - 234 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-41756 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Oberleitner, Lidia T1 - Immunochemical determination of caffeine and carbamazepine in complex matrices using fluorescence polarization N2 - Pharmacologically active compounds are omnipresent in contemporary daily life, in our food and in our environment. The fast and easy quantification of those substances is becoming a subject of global importance. The fluorescence polarization immunoassay (FPIA) is a homogeneous mix-and-read format and a suitable tool for this purpose that offers a high sample throughput. Yet, the applicability to complex matrices can be limited by possible interaction of matrix compounds with antibodies or tracer. Caffeine is one of the most frequently consumed pharmacologically active compounds and is present in a large variety of consumer products, including beverages and cosmetics. Adverse health effects of high caffeine concentrations especially for pregnant women are under discussion. Therefore, and due to legal regulations, caffeine should be monitored. Automated FPIA measurements enabled the precise and accurate quantification of caffeine in beverages and cosmetics within 2 min. Samples could be highly diluted before analysis due to high assay sensitivity in the low μg/L range. Therefore, no matrix effects were observed. The antiepileptic drug carbamazepine (CBZ) is discussed as a marker for the elimination efficiency of wastewater treatment plants and the dispersion of their respective effluents in surface water. The development of a FPIA for CBZ included the synthesis and evaluation of different tracers. Using the optimum tracer CBZ-triglycine-5-(aminoacetamido) fluorescein, CBZ concentrations in surface waters could be measured on different platforms: one sample within 4 min in tubes or 24 samples within 20 min on microtiter plates (MTPs). For this study, a commercially available antibody was used, which led to overestimations with recovery rates up to 140% due to high cross-reactivities towards CBZ metabolites and other pharmaceuticals. For more accurate CBZ determination, a new monoclonal antibody was produced. In this attempt, methods for improving the monitoring during the production process were successfully applied, including feces screening and cell culture supernatant screening with FPIA. The new monoclonal antibody is highly specific for CBZ and showed mostly negligible cross-reactivities towards environmentally relevant compounds. Measurements at non-equilibrium state improved the sensitivity and selectivity of the developed FPIA due to slow binding kinetics of the new antibody. Additionally, this measure enables for CBZ determination over a measurement range of almost three orders of magnitude. The comprehensively characterized antibody was successfully applied for the development of sensitive homogeneous and heterogeneous immunoassays. The new antibody made the development of an on-site measurement system for the determination of CBZ in wastewater possible. After comprehensive optimization, this automated FPIA platform allows the precise quantification of CBZ in wastewater samples only pre-treated by filtration within 16 min. Recovery rates of 61 to 104% were observed. Measurements in the low μg/L range are possible without the application of tedious sample preparation techniques. Different FPIA platforms including MTPs, cuvettes and tubes were successfully applied. For the choice of the right format, the application field should be considered, e.g. desired sample throughput, usage for optimization or characterization of antibodies or if a set-up for routine measurements is sought for. For high sample throughput and optimization, FPIA performance on MTPs is advantageous. The best results for the application to real samples were obtained using kinetic FP measurements in cuvettes. T3 - BAM Dissertationsreihe - 154 KW - Antibody KW - Coffee KW - ELISA KW - Fluorophore tracer KW - Wastewater PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-392506 SN - 978-3-9818270-2-6 SN - 1613-4249 VL - 154 SP - 1 EP - 124 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-39250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -