TY - CONF A1 - Feldkamp, Martin T1 - Fire reference package - Results of large-scale fire tests N2 - Packages for the transport of high-level radioactive material are designed to withstand severe accidents. Hypothetical severe accident conditions are defined in the IAEA Regulations for the Safe Transport of Radioactive Materials. One of these accident conditions is the thermal test, mainly consisting of a 30 minute fully engulfing 800°C pool fire or an equally severe fire test. The heat fluxes into the package depend substantially on the fire characteristics and the surface temperature of the package. Fire tests can be performed at BAM on a propane gas fire test facility. In order to investigate the heat fluxes over a wide range of surface temperatures in this test facility a fire reference package was designed for multiple use. The package represented the outer geometry of a specific transport cask for radioactive waste. The fire reference package is a closed steel sheet cylinder with a wall thickness of 10 mm, a length of 1500 mm and a diameter of 1050 mm. The package was instrumented with thermocouples and filled with heat resistant insulation material. Three open-air fire tests were performed in the BAM propane gas fire test facility. The flames exposure time period varied slightly for the fire tests. The wind direction as well as the wind speed were measured and changed between and during the tests. Test stand parameters such as wind shield location and propane gas volume flow were chosen constant for the three tests. The locally measured fire reference package steel sheet temperatures were used for the calculation of heat fluxes as function of time and surface temperature. The measured temperatures allowed further calculations. In a first approach effective fire characteristics of the propane gas fire, including the flame temperature, the fire convection coefficient and a radiation exchange coefficient mathematically describing the determined average heat flux over the surface temperature were calculated. T2 - IRSN-BAM Symposium - Safety of Transport and Storage Packages CY - Online meeting DA - 19.11.2020 KW - Fire reference KW - Calorimetric test KW - Propane KW - Heat flux KW - Propane gas fire test facility PY - 2020 AN - OPUS4-51686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger T1 - Update on the German Spent Fuel Management Strategy N2 - The presentation provides an update on the German spent fuel Management strategy in the areas of transportation, dry interim storage and deep geological disposal. T2 - IAEA 18th TWG-NFCO CY - Online meeting DA - 07.09.2020 KW - Spent nuclear fuel KW - Final disposal KW - Safety KW - Transport and storage cask PY - 2020 AN - OPUS4-51616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Amano, K.O.A. A1 - Hahn, S.-K. A1 - Tschirschwitz, Rico A1 - Rappsilber, Tim A1 - Krause, U. T1 - Experimental Investigation on Explosion Pressure Characteristics of Lithium-based (NMC) Pouch Batteries during Thermal Runaway N2 - Lithium ion batteries (LIBs) are prone to spontaneous and subsequent fire or explosion resulting from thermal runaway. The vented gases are not only toxic and flammable, their emission can also raise the surrounding pressure rapidly. In this study, characteristic variations of explosion pressure rise, rate of explosion pressure rise and 𝐾(sT)-value have been evaluated. The characteristic 𝐾(𝑠𝑇)-values were determined to evaluate the explosive behavior of LIBs during thermal runaway. The estimated values were compared to that of other explosive substances. T2 - Batterieforum Deutschland 2021 CY - Online meeting DA - 20.01.2021 KW - Pressure KW - Lithium KW - Thermal Runaway KW - Battery KW - Pouch PY - 2021 AN - OPUS4-52033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias A1 - Chen, Hefeng T1 - Numerical Analysis for an Electro‐Magneto‐Mechanical Phenomenon with High‐Order Accurate Methods N2 - This paper establishes an axisymmetric model for a levitation device. Therein, the Maxwell equations are combined with the balance of linear momentum. Different possible formulations to describe the MAXWELL equations are presented and compared and discussed in the example. A high order finite element discretization using GALERKIN's method in space and the generalized NEWMARK‐α method in time are developed for the electro‐magneto‐mechanical approach. Several studies on spatial and temporal discretization with respect to convergence will be investigated. In addition, the boundary influences and the domain size with respect to the levitation device are also examined. T2 - International Association for Applied Mathematics and Mechanics CY - Kassel, Germany DA - 16.03.2020 KW - High-Order Methods KW - Electro-Magneto-Mechanical KW - Levitation Device PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520720 DO - https://doi.org/10.1002/pamm.202000018 VL - 20 IS - 1 SP - e202000018 PB - Wiley‐VCH GmbH CY - Online AN - OPUS4-52072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Asna Ashari, Parsa T1 - An Analysis of the Three Knowledge and Technology Transfer Channels: Publications, Patents, Standards – The Case of Hydrogen Technology N2 - Climate change and the need to reduce greenhouse gas emissions pose tremendous challenges to policymakers, the economy, and society. In this context, the development of clean, low-emission technologies plays a crucial role in mitigating the negative impact of fossil fuels on the climate. Hydrogen is a promising energy carrier and fuel that, thanks to its versatility, can be used in many applications. However, the adoption of hydrogen technology requires sufficient trust in its safety. To proxy the development of hydrogen safety innovations, we provide an analysis along the three knowledge and technology transfer channels of publications, patents, and standards. Our results show that research on hydrogen safety has increased significantly in the last decades, with hydrogen safety patents experiencing a general upward trend between 1980 and 2020, just recently decreasing. However, an analysis of almost 100 international hydrogen and fuel cell standards shows only a small number of references to scientific publications. This apparently limited transfer of knowledge from publications points to the need to optimize the coordination of the three knowledge and technology transfer channels for the future development of hydrogen technology. Based on the exploration of this gap, we recommend that research on the three channels for hydrogen be intensified and that the impact of hydrogen safety technology research and development on their diffusion be investigated. T2 - 25th EURAS Annual Standardisation Conference – Standardisation and Innovation CY - Online meeting DA - 06.09.2021 KW - Hydrogen Standards KW - Fuel Cells KW - Knowledge and Technology Transfer KW - Publications KW - Patents KW - Standards KW - Safety PY - 2021 AN - OPUS4-53215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin T1 - Fire Testing - Current Activities N2 - The presentation gives an overview over three current fire testing activities for testing transport packages for the transport of high-level radioactive material. Packages for the transport of high-level radioactive material must withstand severe hypothetical accidents. Regulatory test conditions shall cover these severe accident conditions and consist of mechanical tests and a following thermal test. To withstand the mechanical tests heavy weight packages are often designed with impact limiters consisting of wood encapsulated in steel sheets. The thermal test is defined precisely in the IAEA-regulations as a 30 minute fully engulfing 800 °C fire. After the fire phase a pre-damaged impact limiter might continue burning or smoldering and influence the cask thermal behavior with its energy release. The energy transferred from the impact limiter to the cask is of importance for the safety of transport packages. A full-scale fire test with an impact limiter of 2.3 m in diameter and filled with spruce wood was designed and performed. The impact limiter continued burning for 3 days. Energy transfer and temperature measurements were performed. A new test is designed to examine pressure build up and possible mechanical failures in an undamaged impact limiter with a diameter of 1.9 m. The test is designed to measure heat flux from the impact limiter in case of its ignition and burning. To furthermore examine the burning behavior of steel encapsulated wood piles, tests are prepared with wood fire containers and an infrared ignition source. A fire reference package for calorimetric tests was designed. The fire reference package design consists of a closed steel sheet cylinder with a length of 1,500 mm, an exterior diameter of 1,050 mm, and a wall thickness of 10 mm. The cylinder was filled with refractory insulation material and instrumented with thermocouples distributed all over the cylinder. The measured local steel sheet temperatures allow the determination of local as well as overall integral heat fluxes versus time and versus surface temperature. Currently, tests are planned with a new and relatively small fire reference package design. The new design will have a steel sheet cylinder with a length of 182 mm, an exterior diameter of 120 mm. Additionally heat flux sensors will be used in the new fire reference package test design. The propane gas fire will be adjusted with respect to the outcome of the fire tests to meet the requirements of the IAEA-fire. T2 - Technical Exchange IRSN – BAM Transport & Storage of Packages for Radioactive Material CY - Berlin, Germany DA - 08.09.2021 KW - Heat flux sensor KW - Propane gas fire KW - Wood fire PY - 2021 AN - OPUS4-53242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad T1 - Prestressed bolt connections under lateral displacements N2 - The containment system of transport packages for spent nuclear fuel and high-level waste usually includes bolted lids with metal gaskets. The specified transport condition imply high loading on the lids and the bolt connections of the package. The response of the lid systems on these load conditions is generally investigated by drop tests or numerically. BAM has started a research project to get a better understanding about the behavior of prestressed bolt connection under loadings typical for drop tests. T2 - BAM-IRSN-Workshop 2021 CY - Berlin, Germany DA - 08.09.2021 KW - Transport packages KW - Bolt connections KW - Finite element analysis KW - Experimental investigation PY - 2021 AN - OPUS4-53251 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seher, Julia A1 - Fröba, M. T1 - Shape matters: The effect of particle morphology on the fast-charging performance of LiFePO4/C nanoparticle composite electrodes N2 - For the successful use of lithium-ion batteries in automotive applications, reliable availability of high storage capacity and very short recharging times are essential. In order to develop the perfect battery for a certain application, structure–property relationships of each active material must be fully understood. LiFePO4 is of great interest due to its fast-charging capability and high stability regarding its thermal resistance and chemical reactivity. The anisotropic lithium-ion diffusion through the LiFePO4 crystal structure indicates a strong dependence of the electrochemical performance of a nanostructured active material on particle morphology. In this paper, the relationship of the particle morphology and fast-charging capability of LiFePO4/C core/shell nanoparticles in half-cells was studied. For this purpose, a new multistep synthesis strategy was developed. It involves the combination of a solvothermal synthesis followed by an in situ polymer coating and thermal calcination step. Monodisperse rodlike LiFePO4 nanoparticles with comparable elongation along the b-axis (30–50 nm) and a varying aspect ratio c/a (2.4–6.9) were obtained. A strong correlation of the fast-charging capability with the aspect ratio c/a was observed. When using LiFePO4 nanoparticles with the smallest aspect ratio c/a, the best electrochemical performance was received regarding the specific capacity at high C-rates and the cycling stability. A reduction of the aspect ratio c/a by 30% (3.6 to 2.4) was found to enhance the charge capacity at 10 C up to an order of magnitude (7.4–73 mA h·g–1). KW - LiFePO4 KW - Schnellladung KW - Nanoparticles KW - Carbon KW - Chemical synthesis KW - Electrochemical cells KW - Materials PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-533004 DO - https://doi.org/10.1021/acsomega.1c03432 SN - 2470-1343 VL - 6 IS - 37 SP - 24062 EP - 24069 PB - American Chemical Society CY - Washington, DC AN - OPUS4-53300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Polyurethane Foam in Impact Limiters - Experimental and Numerical Analysis N2 - Transport containers with radioactive material are usually shipped in Germany with wooden-filled impact limiters. Alternative energy-absorbing materials for this purpose can be polyurethane foam, for example. In order to perform adequate simulations with PU foam, experimental and numerical investigations must be carried out. With the help of a series of experimental test runs, a material model is developed, tested and compared in LS-Dyna. T2 - Technical Exchange IRSN – BAM: Transport & Storage of Packages for Radioactive Material CY - Berlin, Germany DA - 08.09.2021 KW - Polyurethane Foam, Impact Limiters, PU-Foam PY - 2021 AN - OPUS4-53261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Polyurethane Foam for Impact Limiters - Theory and Experimental Data N2 - Transport containers with radioactive material are usually shipped in Germany with wooden-filled impact limiters. Alternative energy-absorbing materials for this purpose can be polyurethane foam, for example. In order to adequately determine the characteristics for a selected PU foam, various experimental investigations must be carried out. Classically, PU foam specimens are tested under uniaxial compression, confined compression and a tensile test. Using the experimental data and selected material models from the literature, the parameters can be determined to describe and apply material models. T2 - Technical Exchange Sandia – BAM: Transport & Storage of Packages for Radioactive Material CY - Online meeting DA - 31.08.2021 KW - Polyurethane Foam KW - Impact Limiters KW - PU-Foam PY - 2021 AN - OPUS4-53262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -