TY - CONF A1 - Jaunich, Matthias T1 - Low temperature properties of rubber seals N2 - Understanding the failure mechanisms that lead to leakage of rubber seals at low temperatures is important. Rubber properties are highly temperature dependent. Changes in behaviour at low temperatures can result from the rubber-glass transition and for some rubbers by partial crystallisation. Experimental results on the low temperature behaviour of different rubber seals were discussed to help understand seal failure processes. T2 - Rubber in Engineering Group (RIEG) webinar an Elastomers at Low Temperatures CY - Online meeting DA - 11.09.2020 KW - Low temperature KW - Rubber seal KW - Compression set KW - Glass transition PY - 2020 UR - https://www.iom3.org/rubber-engineering-group/event/elastomers-low-temperatures AN - OPUS4-51306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sagradov, Ilja T1 - Long-term tests on metal seals using continuous force measurement in compressed state N2 - In Germany, spent fuel and heat generating radioactive waste is stored in casks for transport and storage (DPCs). The storage licenses were granted for up to 40 years. Due to the delay in identifying a final repository site for such radioactive waste, the storage periods are to be extended significantly. The objective of our research work is to collect additional material data for metal seals in order to be able to better assess the long-term safety of the sealing system of the casks for a period of up to 100 years. A principal safety consideration for the DPCs is the long-term performance of bolted lid sealing systems utilizing metal seals to ensure the safe enclosure of the radioactive inventory during interim storage. To assess the sealing behavior, it is necessary to examine the aging-dependent residual restoring force for the metal seals and the usable resilience. By investigating the change in these values as a function of time and temperature, further insight can be gained into the assessment of long-term safety for extended interim storage. In the present study, the restoring force of metal seals with an outer aluminum jacket and a torus diameter of 9.9 mm was measured continuously. For this purpose, a specially designed device equipped with a load cell was used under isothermal conditions. As part of the investigation, the level and rate of decrease of the restoring seal force were recorded over test periods of one and two months. The seal temperature was set to 35 °C, 75 °C, 100 °C, 125 °C, and 150 °C, respectively. A direct correlation was observed between the temperature of the seal, the level of the restoring force after compressing and heating the seal, and the drop-off characteristics of the restoring force. It was found that in our test device the force level immediately after reaching the respective temperature is lower for higher seal temperatures, while the drop rate of the restoring force is higher. This paper describes the experimental setting and discusses first results in comparison with our long-term discontinuous measurements. T2 - 21st International Symposium on the Packaging and Transportation of Radioactive Materials - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - Long-Term Safety Assessment KW - Extended Interim Storage KW - Metal Seal Aging KW - Restoring Force Degradation KW - Temperature-Dependent Performance PY - 2025 VL - 2025 SP - 1 EP - 10 CY - Indianapolis, IN, USA AN - OPUS4-63881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liu, Yung A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Jaunich, Matthias T1 - Cooperation in Advanced Technologies Associated with the Back End of Nuclear Fuel Cycle N2 - A Memorandum of Understanding (MOU) between Argonne National Laboratory (Argonne) and the German Bundesanstalt für Materialforschung und -prüfung (BAM) was signed in October 2014. Its objectives are to promote cooperation among scientists and specialists at Argonne and BAM and establish a framework for collaboration in advanced technologies associated with the back end of the nuclear fuel cycle. Collaborative activities involving Argonne and BAM may be implemented through the promotion of joint research activities and scientific workshops and conferences; exchange of technical information; and visits by scientists, specialists, and graduate, postgraduate, and Ph.D. students. The MOU was renewed in January 2020 for another five years. Highlights of the progress and achievements are provided in identified topical areas for collaboration on ageing management guidance, storage, transportation and disposal R&D, joint conference activities, and conclude with the benefits of the MOU in fostering Argonne and BAM collaboration. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Nuclear fuel cycle KW - Back end KW - Spent fuel performance KW - Storage KW - Transportation PY - 2022 SP - 1 EP - 10 AN - OPUS4-55861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Ageing under Hydrogen: effects on O-ring seals N2 - In this work we present results for three typical sealing materials (EPDM, HNBR, FKM) after up to 100 days ageing at high temperature under hydrogen. To allow for a better evaluation of the occurring changes the results are compared with effects of ageing in air on the material properties. Despite the common assumption that ageing under hydrogen atmosphere is expected to be less severe for the material in com-parison to air ageing, this is not seen for every material. T2 - Technomer 2023 CY - Chemnitz, Germany DA - 09.11.2023 KW - Hydrogen KW - Ageing KW - Seal KW - Compression set PY - 2023 AN - OPUS4-58818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Comparison of Ageing Behavior of O-Ring Seals Under Hydrogen and Air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 AN - OPUS4-63888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Elastomerdichtungen für Wasserstoffanwendungen - Vergleich des Alterungsverhaltens in Luft und Wasserstoff N2 - In diesem Beitrag soll ein Fokus auf das Alterungsverhalten von Elastomerdichtungen unter Wasserstoff gelegt werden. Hierfür wurden Untersuchungen bei einem mittleren Wasserstoffdruck über Alterungszeiten von bis zu 100 Tagen durchgeführt. Das Alterungsverhalten wird im Vergleich der Alterungseffekte unter thermooxidativen Bedingungen betrachtet und bewertet. Die Annahme, dass der Alterungseffekt unter Wasserstoff stets weniger ausgeprägt ist als an Luft bestätigt sich nicht durch die Ergebnisse. T2 - 4. O-Ring-Forum der Firma ISGATEC CY - Bad Schönborn, Germany DA - 15.05.2025 KW - Wasserstoff KW - Dichtung KW - Thermische Alterung KW - Elastomer PY - 2025 AN - OPUS4-63135 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ammerman, D. J. A1 - Bignell, J. L. A1 - Bjorkman, G. S. A1 - Breach, M. R. A1 - Broz, V. A. A1 - Jordan, J. A1 - Kuehner, S. A1 - Molitoris, D. P. A1 - Reinhardt, W. A1 - Rigato, A. B. A1 - Rosvall, E. S. A1 - Sakalaukus Jr., P. J. A1 - Shih, P. Y.-K. A1 - Siromani, D. A1 - Snow, S. D. A1 - Tso, C.-F. A1 - Yaksh, M. C. A1 - Zencker, Uwe A1 - Zhang, X. T1 - Guidance document - Use of explicit finite element analysis for the evaluation of radioactive material transport packages and storge casks in energy-limited impact events N2 - The purpose of this document is to provide guidance for developing quality finite element models to ensure, with reasonable certainty, that the model produces accurate results for comparison with the strain-based or stress-based acceptance criteria of Section III, Division 3 of the ASME Boiler and Pressure Vessel Code, but could be applicable to other Sections of the Code or other codes. Models developed following the guidance provided in this document meet the definition of a "Quality Model," as described in Paragraph EE 1240 of the Nonmandatory Appendix EE (Strain-Based Acceptance Criteria Definitions and Background Information). It cannot be emphasized enough, however, that the guidance supplied here does not constitute requirements. Rather, the intent of the guidance is to give practical direction to analysts (i.e., this is not a set of regulatory requirements). This guidance document is an "evolving" document. It will undergo revision as computing capability and FEA techniques progress, and as example problems are developed. KW - Computational modeling KW - Explicit dynamics PY - 2025 SN - 978-0-7918-7749-4 VL - NTB-6 SP - 1 EP - 153 PB - Americal Society of Mechanical Engineers (ASME) CY - New York, NY ET - 2025 AN - OPUS4-65759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -