TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_4/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_4 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Automation KW - Procedure KW - Synthesis KW - Traceability PY - 2024 DO - https://doi.org/10.5281/zenodo.11237899 PB - Zenodo CY - Geneva AN - OPUS4-61343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_1/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_1 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Synthesis KW - Automation KW - Traceability KW - Procedure PY - 2024 DO - https://doi.org/10.5281/zenodo.11236031 PB - Zenodo CY - Geneva AN - OPUS4-60243 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Hörmann, Anja A1 - Moeez, Abdul A1 - Breßler, Ingo T1 - BAMresearch/HDF5Translator: A Framework for translating and transforming data between HDF5 files N2 - HDF5Translator is a Python framework for translating and transforming data between HDF5 files. It supports operations like unit conversion, dimensionality adjustments, and subtree copying, making it suitable for managing and manipulating a wide range of scientific datasets. KW - Measurement data conversion KW - Data conversion KW - HDF5 KW - NeXus KW - NXsas KW - Framework KW - Python KW - Methodology PY - 2024 DO - https://doi.org/10.5281/zenodo.10927639 PB - Zenodo CY - Geneva AN - OPUS4-59797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Laskina, Sofya A1 - Naik, Aakash A1 - Smales, Glen Jacob A1 - George, Janine A1 - Breßler, Ingo A1 - Benner, Philipp T1 - Jupyter notebook and VASP calculation details accompanying the manuscript: "Ultima Ratio: Simulating wide-range X-ray scattering and diffraction" N2 - Summary: This notebook and associated datasets (including VASP details) accompany a manuscript available on the ArXiv (https://doi.org/10.48550/arXiv.2303.13435) and hopefully soon in a journal as short communication as well. Most of the details needed to understand this notebook are explained in that paper with the same title as above. For convenience, the abstract is repeated here: Paper abstract: We demonstrate a strategy for simulating wide-range X-ray scattering patterns, which spans the small- and wide scattering angles as well as the scattering angles typically used for Pair Distribution Function (PDF) analysis. Such simulated patterns can be used to test holistic analysis models, and, since the diffraction intensity is presented coupled to the scattering intensity, may offer a novel pathway for determining the degree of crystallinity. The "Ultima Ratio" strategy is demonstrated on a 64-nm Metal Organic Framework (MOF) particle, calculated from $Q<0.01$\,$\mathrm{nm}^{-1}$ up to $Q\approx150$\,$\mathrm{nm}^{-1}$, with a resolution of 0.16\,\AA. The computations exploit a modified 3D Fast Fourier Transform (3D-FFT), whose modifications enable the transformations of matrices at least up to $8000^3$ voxels in size. Multiple of these modified 3D-FFTs are combined to improve the low-$Q$ behaviour. The resulting curve is compared to a wide-range scattering pattern measured on a polydisperse MOF powder. While computationally intensive, the approach is expected to be useful for simulating scattering from a wide range of realistic, complex structures, from (poly-)crystalline particles to hierarchical, multicomponent structures such as viruses and catalysts. KW - X-ray KW - Simulation KW - Scattering KW - MOUSE KW - Nanomaterials KW - XRD KW - SAXS KW - PDF KW - Total scattering KW - 3D Fourier transform KW - High resolution KW - FFT PY - 2023 DO - https://doi.org/10.5281/zenodo.7764044 PB - Zenodo CY - Geneva AN - OPUS4-57207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mehri Sofiani, F. A1 - Chaudhuri, Somsubhro A1 - Elahi, S. A. A1 - Wallaert, E. A1 - Depover, T. A1 - De Waele, W. T1 - Accelerated laboratory simulation of corrosion pit evolution in low-carbon steel using phase-field guided overpotential application N2 - This study is performed to replicate field data of pit geometry evolution in the laboratory by accelerating pit evolution through the application of relatively high overpotential on low-carbon steel. A phase-field model is used to reduce the number of trials and errors in the laboratory. The effect of overpotential on pitting corrosion is studied in low-carbon steel in the electrolyte representative of the North Sea. Based on the results obtained through the numerical model, potentiostatic polarisation tests are performed, and a comparison is made between such accelerated tests and steel coupons collected from the field. The results of this comparison suggest that the pitting corrosion acceleration mechanism effectively produces surface conditions closely resembling those of naturally pitted steel. Additionally, it enables the investigation of the electrochemical characteristics of a stable pit over long-term exposure, where direct probing is challenging. This framework strives to mitigate the excessive costs of time-consuming coupon experiments by correlating accelerated pitting corrosion in short periods of time with actual pitting corrosion observed over the long term. KW - Pitting corrosion KW - Corrosion acceleration KW - Potentiodynamic tests KW - Phase-field KW - S355 PY - 2025 DO - https://doi.org/10.1016/j.engfailanal.2025.110352 SN - 1350-6307 VL - 184 SP - 1 EP - 20 PB - Elsevier CY - Oxford AN - OPUS4-64805 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - R&D insights into sustainable additive manufacturing for high-temperature applications (HTA) N2 - Im Rahmen des AM Forums Berlin 2026 wird durch diesen Vortrag ein Einblick in FuE-Aktivitäten der BAM auf dem Gebiet der additiven Fertigung für Hochtemperaturanwendungen gegeben. Es werden dabei insbesondere Aspekte der nachhaltigen Verwendung von Pulverausgangswerkstoff und der Einfluss von Sauerstoff im Pulverwerkstoff auf die Degradation resultierender mechanischer Eigenschaften von Probekörpern beleuchtet. Die präsentierten Arbeiten sind im Rahmen des Pro FIT Projektes HTA2.0 entstanden. T2 - 10. AM Forum 2026 CY - Berlin, Germany DA - 10.03.2026 KW - Additive Manufacturing KW - Sustainability KW - Powder recycling KW - Powder degradation PY - 2026 AN - OPUS4-65725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hülagü, Deniz A1 - Hertwig, Andreas T1 - Correlative analysis of graphene: Advancing ellipsometry as a fast routine method N2 - Graphene (G) and graphene oxide (GO) are key materials for various applications, yet their structural and thickness inhomogeneities calls for rapid, reliable characterization. In this work, we performed a correlative analysis, combining spectroscopic (SE) and imaging ellipsometry (IE) with complementary microscopy techniques to investigate monolayer graphene and GO flakes on SiO₂/Si substrates. SEM, owing to its high resolution and excellent contrast, delivered a comprehensive overview of the monolayer graphene (Figure 1a) and enabled the clear identification of individual GO flakes (c). However, SEM does not provide layer-thickness information. In this case, SE served as a fast and non-destructive method capable of quantitative thickness determination through optical modeling, revealing a graphene layer thickness of 0.7 nm (b), corresponding to a monolayer. The GO flake identified by SEM was subsequently analyzed by AFM, a well-established technique providing nanoscale height profiles with high accuracy (d–f). AFM results further revealed flake thicknesses of a few monolayers. However, AFM is time-consuming, restricted to small scan areas, and does not offer a full overview of the sample. WLIM complemented these results by providing large-area imaging, enabling the visualization of multiple flakes simultaneously. Nevertheless, it is not able to quantify the exact thickness (e). In contrast, IE enabled non-destructive, substrate-independent thickness of GO flakes with single-atomic-layer precision and improved sensitivity, once the ellipsometer settings were optimized for material and thickness contrast and fixed during imaging, bridging the gap between overview imaging and quantitative nanoscale analysis (g–h). While SE provides non-destructive, quantitative thickness information for homogeneous monolayer graphene, GO flakes require imaging-based methods. Therefore, IE represents an attractive alternative, offering large-area maps of GO flakes together with local layer-thickness information. This correlative approach establishes a foundation for standardized, large-area quality assessment of such 2D materials. T2 - 13th Workshop on Spectroscopic Ellipsometry WSE 2026 CY - Genova, Italy DA - 09.02.2026 KW - Monolayer graphene KW - Graphene oxide KW - Correlative Analysis KW - SEM KW - Spectroscopic ellipsometry KW - Imaging ellipsometry KW - AFM PY - 2026 AN - OPUS4-65708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miliute, Aiste T1 - How experimental and computational methods allow us to design negative thermal expansion materials N2 - Combined experimental and computational methods allow a comprehensive understanding, design, and tailoring of material properties. We focus on a well-known negative thermal expansion (NTE) material, zirconium vanadate (ZrV2O7), and address its synthesis, characterisation, and computational validation of results. Experimental and computational X-ray diffraction and Raman spectroscopy data highlighted differences between phase-pure and multiphase ceramics. The total-scattering method enabled us to distinguish subtle differences in the material's structure. Based on ab initio simulated phonon data, we could interpret the Raman spectra, visualise Raman-active atomic vibrations, and gain deeper insight into the local structure. Computational models provided deeper insight and enabled further experimental improvements, while high-quality experimental data validated and improved the computational simulation strategy. T2 - CATS Special Guests III CY - Urcuqui, Ecuador DA - 06.03.2026 KW - NTE KW - Ab initio KW - PDF KW - Raman KW - XRD PY - 2026 AN - OPUS4-65714 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröder, Nina A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Hydrogen-assisted cracking in GMA welding of high-strength structural steel - A new look into this issue at narrow groove N2 - Modern arc processes, such as the modified spray arc (Mod. SA), have been developed for gas metal arc welding of high-strength structural steels with which even narrow weld seams can be welded. High-strength joints are subjected to increasingly stringent requirements in terms of welding processing and the resulting component performance. In the present work, this challenge is to be met by clarifying the influences on hydrogen-assisted cracking (HAC) in a high-strength structural steel S960QL. Adapted samples analogous to the self-restraint TEKKEN test are used and analyzed with respect to crack formation, microstructure, diffusible hydrogen concentration and residual stresses. The variation of the seam opening angle of the test seams is between 30° and 60°. To prevent HAC, the effectiveness of a dehydrogenation heat treatment (DHT) from the welding heat is investigated. As a result, the weld metals produced at reduced weld opening angle show slightly higher hydrogen concentrations on average. In addition, increased micro- as well as macro-crack formation can be observed on these weld metal samples. On all samples without DHT, cracks in the root notch occur due to HAC, which can be prevented by DHT immediately after welding. KW - High-strength structural steel KW - Gas metal arc welding KW - Diffusible hydrogen KW - Hydrogen-assisted cracking KW - TEKKEN KW - Residual stresses KW - Weld metal cracking PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527260 DO - https://doi.org/10.3390/met11060904 VL - 11 IS - 6 SP - 1 EP - 18 PB - MDPI CY - Basel AN - OPUS4-52726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Engelking, Lorenz A1 - Madia, Mauro A1 - Schröpfer, Dirk A1 - Kruse, Julius A1 - Saliwan Neumann, Romeo A1 - Kannengießer, Thomas T1 - Influence of Ultrasonic-Assisted Milling on Surface Integrity and Fatigue Strength of a Low Alloy Steel N2 - The milling process significantly influences the surface integrity of metallic components through machining induced near surface residual stresses. Modern hybrid machining processes, such as ultrasonic-assisted milling (USAM), offer the potential to induce beneficial near-surface compressive residual stresses compared to the near-surface tensile residual stresses typically resulting from conventional milling (CM). This study investigates the effects of USAM compared to CM on the near-surface residual stress state and fatigue performance of a S355J2C low-alloy steel. Milling experiments and subsequent rotating bending tests revealed that USAM significantly reduces cutting force by approximately 45% and induces near-surface compressive re sidual stresses as low as −733MPa. This leads to a significant improvement in fatigue strength estimated in approximately 34% compared to polished specimens and 11% compared to the CM. These findings highlight the potential of USAM to enhance the fatigue performance of components made of steel. KW - Fatigue strength KW - Residual stress KW - Surface integrity KW - Surface roughness KW - Ultrasonic-assisted milling PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-657358 DO - https://doi.org/10.1111/ffe.70259 SP - 1 EP - 11 PB - Wiley AN - OPUS4-65735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - George, Janine T1 - Robust Data Generation, Heuristics and Machine Learning for Materials Design N2 - Despite significant progress, computational materials design still faces major challenges—particularly when simulating advanced and chemically complex materials with the accuracy of density functional theory (DFT) or beyond.[1] To overcome these limitations, machine learning (ML) methods have gained considerable traction in recent years. We have developed robust data-generation strategies to support the creation and benchmarking of new ML models.[2] In this talk, I will highlight methods for large-scale quantum-chemical bonding analysis and workflows for ML interatomic potentials. Our work demonstrates that quantum-chemical bonding properties can be incorporated into ML models to predict phononic properties.[3] This approach enables large-scale validation of expected correlations—such as the link between bonding strength and force constants or thermal conductivities. Furthermore, we have built an automated training framework for machine-learned interatomic potentials (autoplex).[4] Initial workflows include random structure searches, suitable for general-purpose potentials, as well as specialized workflows targeting ML potentials with accurate phonon properties. While atomistic simulations are highly effective for certain material properties, others—such as magnetism or synthesizability—remain challenging. In these cases, promising strategies include benchmarking established ab initio methods against chemical heuristics or developing new ML models primarily based on experimental data.[5,6] T2 - MATSUS Spring 2026 CY - Barcelona, Spain DA - 24.03.2026 KW - Materials Design KW - High-througput KW - Bonding properties KW - Thermal conductivity KW - Amorphous materials KW - Crystallisation PY - 2026 AN - OPUS4-65734 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suarez Ocano, Patricia T1 - Effect of the powder composition on the microstructure and mechanical properties of 316L stainless steel fabricated by laser powder bed fusion N2 - Additive manufacturing (AM) has seen rapid growth in recent decades, with Laser Powder Bed Fusion (PBF-LB/M) emerging as the leading technique for producing high-density, geometrically complex metal parts. Austenitic stainless steel 316L is one of the most studied alloys for PBF-LB/M due to its excellent strength, ductility, and corrosion resistance [1]. The microstructure formed during PBF-LB/M processing can improve certain mechanical properties compared to conventionally manufactured 316L [2]. However, the current 316L standards allow broad ranges for key alloying elements, particularly Cr and Ni. While such variations have little effect on conventionally produced alloys, emerging evidence shows that they can markedly alter the microstructure and mechanical properties in PBF-LB/316L—even within specification limits [3]. This study investigates through microstructural and thermodynamical assessment, how two powders of nominally standard 316L composition (Alloys A and B) respond to identical PBF-LB/M processing parameters. Despite identical printing conditions, Alloy A exhibited twice the grain size and five times higher low-angle grain boundary (LAGB) density compared to Alloy B . Conversely, Alloy B showed a significantly higher density of Σ3 twin boundaries, nearly absent in Alloy A. These microstructural differences are attributed primarily to variations in Cr and Ni content in the liquid, which may influence icosahedral short-range ordering (ISRO) mechanism [4]. ISRO potentially facilitates twin boundary formation, ultimately refining grain structure [5]. This work highlights the critical impact of compositional control on final part microstructures and consequent mechanical properties and emphasizes the need to reassess compositional tolerances for AM-specific applications. T2 - 5th Symposium on Materials and Additive Manufacturing (Additive 2026) CY - Kassel, Germany DA - 24.03.2026 KW - Additive manufacturing KW - 316L stainless steel KW - Chemical composition KW - Lcosahedral short-range ordering mechanism KW - Grain size PY - 2026 AN - OPUS4-65738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans A1 - Weidner, Steffen A1 - Scheliga, Felix T1 - Ring-Expansion Polymerization (REP) of L-lactide with cyclic Tin(II) Bisphenoxides N2 - Five new cyclic catalysts were prepared by a new synthetic method from tin(II)-2-ethyhexanoate and silylated catechols, silylated 2,2´dihydroxybiphenyl or silylated 1,1´-bisnaphthol. These catalysts were compared with regard to their usefulness as catalysts for the ring expansion polymerization (REP) of L-lactide in bulk at 160 °C, and with two different tin(IV) derivatives of 1,1´binaphthol. Best results were obtained using seven-membered cyclic tin(II)bisphenoxides, which yielded colorless cyclic poly(l-lactide)s free of racemization with weight average molecular weights (Mw) up to 305 000 g mol-1. Furthermore, these catalysts were active even at a lactide/catalyst ratio of 20 000/1. Our new results were superior to those obtained from all other previously published catalysts yielding cyclic poly(L-lactide). The seven-membered cycles also proved to be more active than tin(II) 2-ethylhexanoate with and without the addition of alcohol. KW - Lactide KW - Cyclization KW - Ring-expansion polymerization KW - Tin(II)octanoate KW - MALDI-TOF MS PY - 2019 DO - https://doi.org/10.1016/j.eurpolymj.2019.04.024 SN - 0014-3057 SN - 1873-1945 VL - 116 SP - 256 EP - 264 PB - Elsevier Ltd. AN - OPUS4-47794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Meyer, A. A1 - Weidner, Steffen T1 - High Tm Poly(l-lactide)s by Means of Bismuth Catalysts? N2 - One series of BiSub-catalyzed ring-opening polymerizations (ROPs) is per-formed at 160 °C for 3 days with addition of difunctional cocatalysts to find out, if poly(l-lactide) crystallizes directly from the reaction mixture. An analogous series is performed with monofunctional cocatalysts. High Tm crystal-lites (Tm > 190 °C) are obtained from all bifunctional cocatalysts, but not from all monofunctional ones. It is shown by means of SAXS measurements that the high Tm values are mainly a consequence of a transesterification–homogenization process across the lamellar surfaces resulting in thickness and smoothing of the surfaces. An unusual enthalpy-driven modification of the molecular weight distribution is found for samples that have crystallized during the polymerization. A third series of ROPs is performed at 170 °C for 2 h followed by annealing at 120 °C (2 h) to induce crystallization. Complete transformation of the resulting low Tm crystallites (Tm < 180 °C) into the high Tm crystallites by annealing at 170 °C for 1 d is not achieved, despite variation of the cocatalyst. KW - Polylactide KW - MALDI-TOF MS KW - Crystallization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522777 DO - https://doi.org/10.1002/macp.202100019 SN - 1022-1352 VL - 222 IS - 8 SP - 19 PB - Wiley AN - OPUS4-52277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Meyer, A. T1 - About the Influence of (Non-)Solvents on the Ring Expansion Polymerization of l-Lactide and the Formation of Extended Ring Crystals N2 - Ring-expansion polymerizations (REPs) catalyzed by two cyclic tin catalysts(2-stanna-1.3-dioxa-4,5,6,7-dibenzazepine [SnBiph] and 2,2-dibutyl-2-stanna-1,3-dithiolane [DSTL) are performed at 140 °C in bulk. Small amounts (4 vol%) of chlorobenzene or other solvents are added to facilitate transesterification reactions (ring–ring equilibration) in the solid poly(l-lactide)s. In the mass range up to m/z 13 000 crystalline PLAs displaying a so-called saw-tooth pattern in the MALDI-TOF mass spectra are obtained indicating the formation of extended-ring crystals. The characteristics of extended-ring crystallites and folded-ring crystallites are discussed. Furthermore, extremely high melting temperatures (Tm’s up to 201.2 °C) and melting enthalpies (𝚫Hm’s up to 106 J g−1)) are found confirming that 𝚫Hmmax, the 𝚫Hm of a perfect crystal, is around or above 115 J g−1 in contrast to literature data. KW - Polylactide KW - MALDI-TOF MS KW - Ring-expansion polymerization KW - Crystals PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-565038 DO - https://doi.org/10.1002/macp.202200385 SN - 1022-1352 SP - 1 EP - 8 PB - Wiley VHC-Verlag AN - OPUS4-56503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H. R. T1 - SnOct2-catalyzed ROPs of L-lactide initiated by acidic OH- compounds: Switching from ROP to polycondensation and cyclization N2 - Ring-opening polymerizations (ROPs) of L-lactide are performed in bulk at 130°C with tin(II) 2-ethylhexanoate as catalyst and various phenols of differentacidity as initiators. Crystalline polylactides having phenyl ester end groups are isolated, which are almost free of cyclics. The dispersities and molecular weights are higher than those obtained from alcohol-initiated ROPs under identical conditions. Polymerizations at 160°C yield higher molecular weights than expected from the monomer/initiator ratio and a considerable fraction of cycles. The fraction of cycles increases with higher reactivity of the ester end group indicating that the cycles are formed by end-to-end cyclization. KW - Polylactide KW - MALDI-TOF MS KW - Polymerization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540250 DO - https://doi.org/10.1002/pol.20210823 SN - 2642-4150 VL - 60 IS - 5 SP - 785 EP - 793 PB - Wiley AN - OPUS4-54025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Musl, O. A1 - Sulaeva, I. A1 - Sumerskii, I. A1 - Mahler, A.K. A1 - Rosenau, T. A1 - Falkenhagen, Jana A1 - Potthast, A. T1 - Mapping of the Hydrophobic Composition of Lignosulfonates N2 - Lignosulfonates are industrial biorefinery products that are characterized by significant variability and heterogeneity in their structural composition. Typically, they exhibit high dispersities in molar mass (molar mass distribution-MMD) and in functionalities (functionality-type distribution - FTD), which crucially affect their material usage. In terms of FTD, state-of-the-art Lignin analytics still rely mainly on the determination of functional group contents, which are statistical averages with limited explanatory power. In contrast, our online hydrophobic interaction chromatography−size-exclusion chromatography 2D-LC approach combines the determination of both MMD and FTD in a single measurement to provide a comprehensive picture of the characteristic composition of industrial lignosulfonates information hitherto inaccessible by state-of-the-art lignin analytics. In this way, the complex inter - relationships between these two important structural parameters can be studied in an unprecedented manner. In this study, we reveal the considerable differences in terms of hydrophobic composition and its dispersity present in a range of different industrial lignosulfonates - data desperately needed in tailoring and refining of lignosulfonate composition for material usage. KW - Lignosulfonates KW - Amphiphilicity KW - Hydrophobic interaction chromatography KW - Two-dimensional chromatography (2D-LC) KW - Charge-to-size-ratio PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-538612 DO - https://doi.org/10.1021/acssuschemeng.1c06469 VL - 9 IS - 49 SP - 16786 EP - 16795 PB - ASC Publications AN - OPUS4-53861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Meyer, A. T1 - Poly(L-lactide): Optimization of Melting Temperature and Melting Enthalpy N2 - Twice recrystallized L-lactide was polymerized with a dozen of different tin or bismuth catalysts in bulk at 160°C for 24 h and was annealed at 150°C afterwards. In two cases Tm values above 197.0°C were obtained. The parameters causing a scattering of the DSC data were studied and discussed. The samples prepared with SnCl2, 2,2-dibutyl-2-stanna-1,3-ditholane (DSTL) or cyclic tin(II) bisphenyldioxide (SnBiph) were subject to annealing programs with variation of time and temperatures, revealing that the Tm´s did not increase. However, an increase of Hm was achieved with maximum values in the range of 93-96 J g-1 corresponding to crystallinities off around 90%. Further studies were performed with once recrystallized L-lactide. Again, those samples directly crystallized from the polymerization process showed the highest Tm values. These data were compared with the equilibrium Tm0 and Hm0 data calculated by several research groups for perfect crystallites. A Tm0 of 213+/-2°C and a Hm0 of 106 J g-1 show the best agreement with the experimental data. The consequences of annealing for the thickness growth of crystallites are discussed on the basis of SAXS measurements. Finally, a comparison of cyclic and linear poly L-lactide)s is discussed. KW - Polylactide KW - MALDI-TOF MS KW - Transesterification PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-538656 DO - https://doi.org/10.1039/D1MA00957E SP - 1 EP - 10 PB - Royal Society for Chemistry AN - OPUS4-53865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fink, Friedrich A1 - Emmerling, Franziska A1 - Falkenhagen, Jana T1 - Identification and Classification of Technical Lignins by means of Principle Component Analysis and k-Nearest Neighbor Algorithm N2 - The characterization of technical lignins is a key step for the efficient use and processing of this material into valuable chemicals and for quality control. In this study 31 lignin samples were prepared from different biomass sources (hardwood, softwood, straw, grass) and different pulping processes (sulfite, Kraft, organosolv). Each lignin was analysed by attenuated total reflectance Fourier transform infrared (ATR-FT-IR) spectroscopy. Statistical analysis of the ATR-FT-IR spectra by means of principal component analysis (PCA) showed significant differences between the lignins. Hence, the samples can be separated by PCA according to the original biomass. The differences observed in the ATR-FT-IR spectra result primarily from the relative ratios of the p-hydroxyphenyl, guaiacyl and syringyl units. Only limited influence of the pulping process is reflected by the spectral data. The spectra do not differ between samples processed by Kraft or organosolv processes. Lignosulfonates are clearly distinguishable by ATR-FT-IR from the other samples. For the classification a model was created using the k-nearest neighbor (k NN) algorithm. Different data pretreatment steps were compared for k=1…20. For validation purposes, a 5-fold cross-validation was chosen and the different quality criteria Accuracy (Acc), Error Rate (Err), Sensitivity (TPR) and specificity (TNR) were introduced. The optimized model for k=4 gives values for Acc = 98.9 %, Err = 1.1 %, TPR = 99.2 % and TNR = 99.6 %. KW - Classification KW - PCA KW - K-nearest neighbor KW - FT-IR KW - Technical lignin PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-533855 DO - https://doi.org/10.1002/cmtd.202100028 VL - 1 IS - 8 SP - 350 EP - 396 PB - Wiley-VCH GmbH AN - OPUS4-53385 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Meyer, A. T1 - High Tm linear poly(L-lactide)s prepared via alcohol-initiated ROPs of L-lactide N2 - Alcohol-initiated ROPs of L-lactide were performed in bulk at 160 °C for 72 h with variation of the catalyst or with variation of the initiator (aliphatic alcohols). Spontaneous crystallization was only observed when cyclic Sn(II) compounds were used as a catalyst. Regardless of initiator, high melting crystallites with melting temperatures (Tm) of 189–193 °C were obtained in almost all experiments with Sn(II) 2,2′-dioxybiphenyl (SnBiph) as catalyst, even when the time was shortened to 24 h. These HTm poly(lactide)s represent the thermodynamically most stable form of poly(L-lactide). Regardless of the reaction conditions, such high melting crystallites were never obtained when Sn(II) 2-ethylhexanoate (SnOct2) was used as catalyst. SAXS measurements evidenced that formation of HTm poly(L-lactide) involves growth of the crystallite thickness, but chemical modification of the crystallite surface (smoothing) seems to be of greater importance. A hypothesis, why the “surface smoothing” is more effective for crystallites of linear chains than for crystallites composed of cycles is discussed. KW - Polylactide KW - MALDI-TOF MS KW - Ring-opening polymerization PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524330 DO - https://doi.org/10.1039/d1ra01990b VL - 11 IS - 23 SP - 14093 EP - 14102 PB - Royal Society of Chemistry AN - OPUS4-52433 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - ROP of L-lactide and ε-caprolactone catalyzed by tin(ii) andtin(iv) acetates–switching from COOH terminated linear chains to cycles N2 - The catalytic potential of tin(II)acetate, tin(IV)acetate, dibutyltin-bis-acetate and dioctyl tin-bis-acetate was compared based on polymerizations of L-lactide conducted in bulk at 160 or 130°C. With SnAc2 low-Lac/Cat ratios (15/1–50/1) were studied and linear chains having one acetate and one carboxyl end group almost free of cyclics were obtained. Higher monomer/catalyst ratios and lower temperatures favored formation of cycles that reached weight average molecular weights (Mw's) between 100,000 and 2,500,000. SnAc4 yielded mixtures of cycles and linear species under all reaction conditions. Dibutyltin- and dioctyl tin bis-acetate yielded cyclic polylactides under most reaction conditions with Mw's in the range of 20,000–80,000. Ring-opening polymerizations performed with ε-caprolactone showed similar trends, but the formation of COOH-terminated linear chains was significantly more favored compared to analogous experiments with lactide. The reactivity of the acetate catalysts decreased in the following order: SnAc2> SnAc4>Bu2SnAc2~Oct2SnAc2 KW - Polylactide KW - MALDI-TOF MS KW - Catalyst KW - Ring-opening polymerization KW - Tin acetates PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521923 DO - https://doi.org/10.1002/pol.20200866 VL - 59 IS - 5 SP - 439 EP - 450 PB - Wiley Online Library AN - OPUS4-52192 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Scheliga, F. A1 - Weidner, Steffen T1 - What does conversion mean in polymer science? N2 - The definition of the term “conversion” is discussed for a variety of polymer syntheses. It is demonstrated that in contrast to organic and inorganic chemistry several different definitions are needed in polymer science. The influence of increasing conversion on structure and topology of homo- and Copolymers is illustrated. Chain-growth polymerizations, such as radical polymerization or living anionic polymerizations of vinyl monomers, condensative chain polymerization, two and three-dimensional step-growth polymerizations, ring–ring or chain–chain equilibration and chemical modification of polymers are considered. KW - Polymers KW - Polymerization KW - Conversion KW - Polycondensation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-523597 DO - https://doi.org/10.1002/macp.202100010 VL - 222 IS - 8 SP - 10 PB - Wiley VCH AN - OPUS4-52359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Falkenhagen, Jana T1 - The role of transesterifications in reversible polycondensations and a reinvestigation of the Jacobson-Beckmann-Stockmayer experiments N2 - The polycondensations of adipic acid and 1,10-decanediol catalyzed by toluene sulfonic acid (TSA) were reinvestigated using MALDI TOF mass spectrometry and NMR spectroscopy. Unexpected reactions of TSA were detected along with incomplete conversion of the monomers. Furthermore, transesterification reactions of end-capped poly(1,10-decanediol adipate) and end-capped poly(ε-caprolactone) catalyzed by TSA were studied. Despite the quite different (ionic) reaction mechanisms, it was found that for polycondensations performed in bulk intermolecular transesterification is more efficient than the intramolecular “back-biting”; this scenario was not considered in the Jacobson–Stockmayer theory of reversible polycondensations. These results also confirm that the Jacobson–Stockmayer explanation of reversible polycondensations solely on the basis of ring chain equilibration is not only devoid of any experimental evidence, but also in contradiction to the results elaborated in this work. KW - Polylactide KW - MALDI-TOF MS KW - Polycondensation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543402 DO - https://doi.org/10.1039/d1py01679b SN - 1759-9962 SP - 1 EP - 9 PB - RSC Publ. CY - Cambridge AN - OPUS4-54340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -