TY - CONF A1 - Scholz, Philipp A1 - Panne, Ulrich A1 - Wachtendorf, Volker A1 - Weidner, Steffen T1 - Degradation of polyurethanes in various environments – Effects on molecular mass and crosslinking N2 - The increasing application of polyurethanes (PU) in safety relevant sectors (fire protection, insulation, medicine technique) requires detailed knowledge of the stability and reliability of these materials. Different climate factors are supposed to induce diverse and overlapping degradation reactions. The knowledge of these degradation mechanisms is necessary for an estimation of the period of application depending on usage of the material. An essential property of a polymeric system is represented by the molecular weight. Since a change of the molecular weight is a measure for the chemical stability of a polymer, size-exclusion chromatography (SEC) was used to monitor changes of the molecular weight of thermoplastic polyether- and polyester urethane (TPU) exposed to thermal, hydrolytic and photo-oxidative (UV) degradation conditions for several days. Thermal treatments were performed at elevated temperatures (100 - 200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥ 175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤ 150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks, which was already known from FTIR spectroscopy[1]. In contrast to that, UV treatment at 25 °C at less than 10 % rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than during the thermal treatments. The depth of penetration of the UV radiation was determined using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤ 80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that ester-based PU in general exhibits a significant higher stability compared to ether-based materials. T2 - ANAKON 2019 CY - Münster, Germany DA - 25.03.2019 KW - Polyurethane KW - Thermal degradation KW - UV degradation KW - Molecular masses KW - Crosslinking PY - 2019 AN - OPUS4-47957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duwe, M. A1 - Fischer, Daniel A1 - Quast, J.-H. A1 - Schneider, S. A1 - Beck, Uwe T1 - Curved-surface metrology by imaging Mueller-matrix ellipsometry N2 - Outline - maging ellipsometry: oncept and setup - Basic theory: ellipsometry on tilted/curved surfaces - Geometric considerations - Tilt-induced cross-polarization - Application: coating analysis on microlensarray - Mueller-Matrix Imaging - Conversion to Delta-Psi Image - Layer-thickness of ITO coating T2 - 8th International conference on spectroscopic CY - Barcelona, Spain DA - 26.05.2019 KW - Spectroscopic Imaging KW - Mueller-Matrix Ellipsometry KW - Curved surfaces PY - 2019 AN - OPUS4-48366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Özcan Sandikcioglu, Özlem A1 - Witt, Julia A1 - Schenderlein, Matthias A1 - Hampel, Marco A1 - Almalla, Ahed T1 - Coupled electrochemical, microscopic and spectroscopic techniques for the analysis of local corrosion and mic processes N2 - Summary of the research topics of the division 6.2 and recent results T2 - HZDR-IRE Institutscolloquium CY - Dresden, Germany DA - 24.09.2019 KW - MIC KW - Localised corrosion KW - Corrosion monitoring KW - Biofilmbildung KW - Atomic Force Microscopy (AFM) PY - 2019 AN - OPUS4-50295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Szymoniak, Paulina A1 - Qu, Xintong A1 - Schönhals, Andreas T1 - Competition of mobilization and Immobilization Effects in Epox-Based Nanocomposites N2 - Two epoxy-based nanocomposites with different nanofillers (layered double hydroxide and boehmite) were investigated employing temperature modulated DSC, flash DSC and broadband dielectric spectroscopy. Detailed investigation on the molecular mobility of the two systems showed the effect of the fillers on the structure of the bulk epoxy matrix and the interface formed at the polymer/particle interface T2 - FOR 2021: Acting principles of Nano-Scaled Matrix Additives for Composite Structures CY - Berlin, Germany DA - 11.10.2019 KW - TMDSC KW - Nanocomposites KW - Rigid amorphous fraction KW - Boehmite KW - BDS PY - 2019 AN - OPUS4-49287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghasem Zadeh Khorasani, Media A1 - Silbernagl, Dorothee A1 - Elert, Anna Maria T1 - Combination of advanced atomic force microscopy methods to investigate mechanical and chemical interphases in epoxy-boehmite nanocomposites N2 - Formation of interphases between inorganic nanofillers and thermoplastic matrices are usually correlated to short-range interactions which does not exceed more than tens of nanometers away from the surface of the filler. Nevertheless, in nanocomposites with thermosetting matrices, the effect of nanofillers on the properties of the matrix is not limited to the immediate vicinities, but a long-range property alteration of the bulk polymer may be observed. The interaction between nanofillers and the polymer can disturb the curing reaction and alters the chemical, physical and mechanical properties of the polymer network in the matrix phase. In our studies, we aim to investigate short and long-range interphases of a nanocomposite system consisting of a thermosetting matrix (DGEBA) filled with an inorganic nanoparticle (boehmite). For this purpose, a combination of atomic force microscopy (AFM)-based approaches is implemented. Scanning kelvin probe microscopy (SKPM) was used to map the compositional contrast and the interphase with different electrical properties than the bulk. The mechanical properties of the interphase were probed by high resolution intermodulation AFM. (ImAFM). Furthermore, infrared spectroscopy AFM (AFM-IR) is used to investigate the chemical structure of the matrix at different distances from the nanoparticle. SKPM and (AFM-IR) measurements both show a long-range (to 10 µm) effect of boehmite on the chemical structure and surface potential of the bulk epoxy, respectively, whereas ImAFM force measurements reveals a short-range mechanical interphase between the filler and the matrix. The AFM-IR demonstrated the existence of unreacted anhydride hardener at the interphase. This indicates the preferential absorption of anhydride on the surface of boehmite. The consequence of such a selective interaction between the inorganic filler and the epoxy components is disturbance of the epoxy-hardener stoichiometric ratio, the curing mechanism. and the alteration of bulk properties of the matrix. T2 - EUROMAT CY - Stockholm, Sweden DA - 01.09.2019 KW - AFM KW - SKPM KW - AFM-IR KW - ImAFM KW - Boehmite PY - 2019 AN - OPUS4-50693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn A1 - Kirner, Sabrina V. A1 - Wirth, Thomas A1 - Florian, Camilo A1 - Sturm, Heinz A1 - Spaltmann, Dirk A1 - Krüger, Jörg T1 - Chemical effects during the formation of femtosecond laser-induced periodic surface structures N2 - The processing of laser-induced periodic surface structures (LIPSS, ripples) on metals and semiconductors in ambient air is usually accompanied by superficial oxidation effects – a fact that is widely neglected in the current literature. In this contribution, chemical, structural, and mechanical alterations in the formation of femtosecond LIPSS are characterized by a variety of surface analytical techniques, including energy dispersive X-ray analyses (EDX), X-ray photoelectron spectroscopy (XPS), micro Raman spectroscopy (µ-RS), and depth-profiling Auger electron microscopy (AEM). Alternative routes of electrochemical and thermal oxidation allow to qualify the relevance of superficial oxidation effects on the tribological performance in oil lubricated reciprocating sliding tribological tests (RSTT). It is revealed that the fs-laser processing of near-wavelength sized LIPSS on metals leads to the formation of a few hundreds of nanometers thick graded oxide layers, consisting mainly of amorphous oxides. Regardless of reduced hardness and limited thickness, this nanostructured surface layer efficiently prevents a direct metal-to-metal contact in the RSTT and may also act as an anchor layer for specific wear-reducing additives contained in the used engine oil. T2 - EMRS Spring Meeting 2019, Symposium V “Laser interactions with materials: from fundamentals to applications" CY - Nice, France DA - 27.05.2019 KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser KW - Oxidation KW - Tribology PY - 2019 AN - OPUS4-48127 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Yin, Huajie A1 - Schönhals, Andreas T1 - Characterization of high-performance membrane polymers for gas separation using broadband dielectric spectroscopy N2 - In recent years superglassy polymers exhibiting intrinsic microporosity established a new perspective for a number of applications, especially for gas separation membranes as These polymers Combine extremely high permeabilities with attractive selectivities. The essential factor governing the structure Formation in the solid film or layer is either a contorted rigid Backbone (polymers of intrinsic microporosity - PIMs) or extremely bulky side groups (polynorbornenes and polytricyclonenenes). For a deeper understanding of both types of such high-Performance polymers for gas separation membranes and their further development broadband dielectric spectroscopy (BDS) can provide a substantial contribution. BDS addresses molecular relaxations characterizing the dynamics of the solid polymer as a major factor determining the gas transport properties but also the physical aging behavior which is an essential issue for such polymers. BDS is applied on PIMs where fluctuations of molecular dipoles connected to the backbone can be directly monitored. Furthermore, also polynorbornenes were investigated which carry no dipole moment in their repeat unit - the high resolution of modern equipment allows for the detailed analysis also for very small dielectric losses originating from partially oxidized moieties or marginal catalyst residues. Additionally, from interfacial polarization phenomena, such as Maxwell-Wagner-Sillars (MWS) polarization due to blocking of charge carriers at internal interfacial boundaries on a mesoscopic length scale, valuable information on the intrinsic microporosity and its changes induced by physical aging can be obtained. Finally, also conductivity can be characterized in detail in such polymeric systems revealing contributions of interactions of aromatic moieties (π-π-stacking) or the drift motion of charge carriers. These features also determine the structure formation in the solid state. T2 - 257th ACS National Meeting - Symposium "Transport in Polymer Membranes" CY - Orlando, FL, USA DA - 31.03.2019 KW - polymers KW - gas separation membranes KW - polynorbornenes KW - polymers of intrinsic microporosity KW - dielectric spectroscopy KW - molecular mobility PY - 2019 AN - OPUS4-48142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana T1 - Characterization of co (polyamide)s N2 - Characterization problems of technically relevant copolyamides applying size exclusion chromatography, interaction chromatography and their combination with MALDI-TOF-MS will be discussed. T2 - 23. Kolloquium Massenspektrometrie und synthetische Polymere CY - Berlin, Germany DA - 14.05.2019 KW - LCCC KW - Mass spectrometry of polymers KW - SEC KW - LC / MALDI-TOF-MS coupling PY - 2019 AN - OPUS4-48221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Mansfeld, Ulrich A1 - Hörenz, Christoph A1 - Pellegrino, F. A1 - Maurino, V. A1 - Marguet, S. A1 - Testard, F. A1 - Tache, O. A1 - Bartczak, D. A1 - Goenaga-Infante, H. T1 - Challenges in Traceable Size Measurement of Non-Spherical, Non-Monodisperse Nanoparticles - nPSize N2 - Size measurement of nanoparticles (NP) becomes a challenging analytical problem when non-spherical shapes must be traceably measured. However, most industrial NPs have irregular shapes and broad size distribution making it often more complex to follow European regulatory to identify a material as a nanomaterial according to which accurate measurement of the smallest dimension and its size Distribution is necessary. The European research project nPSize - Improved traceability chain of nanoparticle size measurements aims to fill this gap by developing potential non-spherical reference nanoparticles, measurement procedures and physical modelling to improve the traceability chain, comparability and compatibility for NP size measurements between different methods. Therefore, new model NP with well-controlled shape has been synthesized and are supposed to be systematically characterized using the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering. Following NP candidates are under investigation with respect to their homogeneity and stability: (i) titania nanoplatelets (10-15 nm thickness x 50-100 nm lateral), (ii) titania bipyramides (~60 nm length x 40 nm width), (iii) titania acicular particles (100 nm length x 15-20 nm width; aspect ratio 5.5/6), (iv) gold nanorods (~10 nm width x 30 nm length), and (v) gold nanocubes (~55 nm x 55 nm x 55 nm). In addition, sample preparation procedures as well as measurement analysis procedures with evaluation of appropriate measurands and descriptors for each material class and method are being developed to support standardization. To underpin the traceability of the size measurement of nonspherical NP, physical modelling of the signals in e.g. electron microscopy techniques will be used and in combination, the implementation of machine learning is aimed to facilitate measurement Analysis procedures, especially regarding the accurate thresholding/segmentation of the NPs.zeige mehr T2 - Nanoparticle Reference Materials - Production and Cerification Training Course CY - London, UK DA - 10.12.2019 KW - Nanoparticles KW - Traceability KW - Particle size distribution KW - Electron microscopy KW - Reference materials KW - Non-spherical shape PY - 2019 AN - OPUS4-50040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher-Hofinger, Stefan A1 - Lange, Thorid A1 - Stockmann, Jörg M. A1 - Weise, Matthias A1 - Rietz, U. A1 - Lerche, D. T1 - Centrifugal force meets materials testing – analytical centrifuge as multipurpose tool for tensile and compressive stress testing N2 - Up until several years ago, tensile and compressive tests have been exclusively carried out as single-sample tests within a tensile, hardness or universal testing machine. The availability of centrifuge technology changed this situation in 2013 in several ways because centrifugal force is used as testing force within a rotational reference frame. Firstly, multiple-sample strength testing became feasible for both tensile load condi-tions, e.g. determination of composite, bonding or adhesive strength, and compressive load conditions, e.g. hardness, compressibility and compactibility. Secondly, there is no need for a two-sided sample clamping and double-cardanic suspensions as samples are simply inserted using a one-sided sample support. Thirdly, shear forces can be avoided by means of guiding sleeves which steer test stamps acting as mass bodies for either tensile or compressive testing. Fourthly, up to eight samples can be tested under identical conditions within a very short period of time, typically within 15 minutes including sample loading and unloading. Hence, either a reliable statistics (of identical samples) or a ranking (of different samples) can be derived from one test run. The bench-top test system is described in detail and demonstrated that centrifugal force acts as testing force in an appropriate way because Euler and Coriolis force do not affect the testing results. Examples for both tensile strength testing, i.e. bonding strength of adhesives-bonded joints and adhesive strength of coatings, and compres-sive strength testing, i.e. Vickers-, Brinell- and ball indentation hardness and deter-mination of spring constants, are presented, discussed and compared with conven-tional tests within tensile, hardness or universal testing machines. At present, a maximum testing force of 6.5 kN can be realized which results at test stamp diameters of 5 mm, 7 mm, and 10 mm in tensile or compressive stress values of 80 MPa, 160 MPa, and 320 MPa. For tensile strength, this is already beyond bonding strength of cold- and warm-curing adhesives. Moreover, centrifuge technology is compliant to standards such as EN 15870, EN ISO 4624, EN ISO 6506/6507 and VDI/VDE 2616. Programmable test cycles allow both short-term stress and log-term fatigue tests. Based on a variety of examples of surface and bonding technology, applications in both fields R&D and QC are presented. Meanwhile, centrifuge technology is also accredited according to DIN EN ISO/IEC 17025. T2 - Intermationa Conference Dispersion Analysis & Materials Testing CY - Berlin, Germany DA - 22.05.2019 KW - Centrifugal Force KW - Compressive Stress KW - Tensile Stress PY - 2019 AN - OPUS4-48310 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher-Hofinger, Stefan A1 - Lange, Thorid A1 - Hidde, Gundula A1 - Lerche, D. A1 - Rietz, U. T1 - CAT-Technologie zur Bestimmung der Klebfestigkeit N2 - Der Vortrag widmet sich der „ CAT-TECHNOLOGIE ZUR BESTIMMUNG DER KLEBFESTIGKEIT“ und beschreibt die Punkte „Motivation –CAT-Technologie (Centrifugal Adhesion Testing), Klebfestigkeit ( Materialscreening verschiedener Werkstoffklassen, Klebstoffscreening fürV2A gegenV2A als Referenz, Klebstoffscreening für Niedrigenergie-Polymere und Oberfächenmodifizierung von Niedrigenergie-Polymeren) und Verbundfestigkeit (“Stirnabzug vs. Zug-Scher-Prüfung an CFK) im Einzelnen. T2 - 17. Praxisseminar KLEBEN CY - IWF Jena, Germany DA - 30.01.2019 KW - CAT-Technologie KW - Klebfestigkeit KW - Verbundfestigkeit KW - Niedrigenergie-Polymeren PY - 2019 AN - OPUS4-47466 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher-Hofinger, Stefan A1 - Lange, Thorid A1 - Weise, Matthias A1 - Lerche, D. A1 - Rietz, U. T1 - CAT-Technologie zur Bestimmung der Haftfestigkeit Dünner Schichten N2 - Der Vortrag widmet sich der „CAT-TECHNOLOGIE ZUR BESTIMMUNG DER HAFTFESTIGKEIT DÜNNER SCHICHTEN“ und beschreibt die Punkte „Motivation –CAT-Technologie“ (CAT: Centrifugal Adhesion Testing) und die „Haftfestigkeit von Schichten“, (Ag-Schichten auf N-BK7 Glas, Cr- und Al-Schichten auf Borofloat 33 Glas, Au-Schichten auf N-BK7 Glas und SiO2-Schichten auf CR39 Polymer) im Einzelnen. T2 - EFDS, Workshop: Haft- und Antihaftschichten CY - Dresden, Germany DA - 31.01.2019 KW - CAT-Technologie KW - Centrifugal Adhesion Testing KW - Dünne Schichten KW - Haftfestigkeit PY - 2019 AN - OPUS4-47489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Szymoniak, Paulina A1 - Schönhals, Andreas A1 - Madkour, Sherif T1 - Broadband dielectric spectroscopy on miscible polymer blends in the bulk and in nanometer thick films - Comparison of the different confinement situations N2 - Broadband dielectric spectroscopy in the frequency range from 10-1 to 109 Hz is employed to revisit the segmental dynamics of the miscible blend system poly(vinyl methyl ether)/polystyrene (PVME/PS) in dependence on the composition firstly in the bulk state. Here especially the case of high polystyrene concentrations is considered. It is important to note that only the molecular dynamics of PVME segments as affected by PS is observed because the dipole moment of polystyrene is negligible. Three relaxation processes are found which are due to fluctuations of differently constrained or confined PVME segments. The degree of the confinement of PVME segments due to PS is discussed in dependence on the composition. Further a spatial confinement is considered by investigating thin films of the PVME/PS blend where the film thickness was varied from 100 nm down to 5 nm. Two concentrations of PVME/PS (50/50 wt% and 25/75 wt%) are investigated. To measure nanometer thick films a novel electrode system based on nanostructured electrodes was employed. Nanostructured electrodes can be considered as a cut-edge technology in dielectric spectroscopy. The relaxation spectra of the films showed multiple processes which are discussed in dependence on the film thickness. T2 - Spring Meeting of the American Physical Scociety CY - Boston, Ma, USA DA - 03.03.2019 KW - Polymer blends PY - 2019 AN - OPUS4-47518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griepentrog, Michael T1 - Bestimmung der Messunsicherheit bei der instrumentierten Eindringprüfung N2 - In der DIN EN ISO 14577 Metallische Werkstoffe – Instrumentierte Eindringprüfung zur Bestimmung der Härte und anderer Werkstoffparameter sind die Durchführung und Auswertung des Verfahrens, sowie die Kalibrierung der zu verwendenden Prüfmaschine genormt. In dieser Norm werden auch grundsätzliche Aussagen zur Bestimmung der Messunsicherheit gemacht. An Beispielen aus der täglichen Prüfpraxis werden verschiedene Möglichkeiten, aber auch die Grenzen der Bestimmung der Messunsicherheitbei der Instrumentierten Eindringprüfung beschrieben und kritisch diskutiert. T2 - 3. Zwick Roell Symposium –Nanoindentation CY - Ulm, Germany DA - 04.07.2019 KW - ISO 14577 KW - Instrumentierte Eindringprüfung KW - Bestimmung der Messunsicherheit PY - 2019 AN - OPUS4-48431 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yusenko, Kirill A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - Emmerling, Franziska T1 - BAMline 2.0 – further technical developments for a broader multipurpose hard X-ray beamline at BESSY II N2 - We show further development of our beamline in the contexst of further itermational collaboration. T2 - PACC and AfSC CY - Accra, Ghana DA - 28.01.2019 KW - Synchrotron radiation PY - 2019 AN - OPUS4-47317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Griepentrog, Michael A1 - Hertwig, Andreas A1 - Hielscher, Stefan A1 - Weise, Matthias T1 - Auf dem Weg zu Industrie 4.0: Bestimmung von Messunsicherheitsbudgets in der Oberflächentechnik N2 - Vorgestellt wurde die Bestimmung von Messunsicherheitsbudgets für sehr unterschiedliche physikalische Größen, die in der Oberflächentechnik von hoher Relevanz sind: Stufenhöhe h, Schichtdicke d, Eindringhärte HIT und Haftfestigkeit. Die Unterschiede betreffen die Art der Prüfmethodik (optisch zerstörungsfrei vs. mechanisch invasiv/zer-störend), die laterale Größe des Integrationsgebietes der Messung (lokal:nano bis sub-mikro vs. global: mikro bis makro) und die Art der Bestimmung von Messunsicherheitsbudgets (physikalische Größen: direkt rückführbar; Werkstoffkenngröße: genormt; Systemkenngröße: genormt). Im Rahmen von Industrie 4.0 werden ausgehend der geforderten Spezifikation des beschichteten Produkts (Mittelwert mit Vertrauensbereich oder Mindestwert) durchgehende Toleranzbänder zur Oberflächenmodifizierung/Beschichtung des Substrats, einhergehend mit Prozessfenstern, die diese Toleranzbänder garantieren, erforderlich, die zuverlässig erfasst werden müssen. Die Frage der anzuwendenden Mess- und Prüftechnik und die damit notwendige Betrachtung von Messunsicherheitsbudgets ist für die Digitalisierung von Konditionierungs-, Zustands-, Regel- und Steuergrößen unverzichtbar. Mit Blick auf die Einhaltung von Prozessfenstern und die dafür notwendige Prozessführung wird technologisches Kern-Know-how digitalisiert, das es unbedingt zu schützen gilt. Nur lokale Netze können diese Sicherheit garantieren, in globalen Netzen ist die Datensicherheit bestenfalls maximierbar. T2 - 14. ThGOT Thementage Grenz- und Oberflächentechnik CY - Zeulenroda, Germany DA - 12.03.2019 KW - Oberflächentechnik KW - Messunsicherheit KW - Messtechnik KW - Prüftechnik KW - Haftfestigkeit PY - 2019 AN - OPUS4-47612 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Camilo A1 - Kirner, Sabrina V. A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Applications on Surface Functionalization by Laser-Induced Periodic Surface Structures (LIPSS) N2 - In recent years, the understanding on the formation of laser-induced periodic surface structures (LIPSS) has led to an emerging variety of applications that modify the optical, mechanical and chemical properties of many materials. Such structures strongly depend on the used polarization and are formed usually after irradiation with ultrashort linearly polarized laser pulses. Some specific formation mechanisms to explain every situation are still to be uncovered, but the most accepted explanation relies on the interference of the incident laser beam with electromagnetic surface waves that propagate or scatter at the surface of the irradiated materials. This leads to an intensity modulation that is finally responsible for the selective ablation in the form of parallel structures with periodicities ranging from hundreds of nanometers up to some micrometers. The versatility when forming such structures is based on the high reproducibility with different wavelength, pulse duration and repetition rate laser sources, customized micro- and nanometric spatial resolutions and compatibility with industrially relevant processing speeds when combined with fast scanning devices. In this contribution, we review the latest applications in the rapidly emerging field of surface functionalization through LIPSS, including biomimetic functionalities on fluid transport, control of the wetting properties, specific optical responses in technical materials, improvement of tribological performance on metallic surfaces and bacterial and cell growth for medical devices among many others. T2 - 38th International Congress on Applications of Lasers and Electro Optics (ICALEO 2019) CY - Orlando, FL, USA DA - 07.10.2019 KW - Laser-induced periodic surface structures, LIPSS KW - Femtosecond laser ablation KW - Surface functionalization KW - Applications PY - 2019 AN - OPUS4-49473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Özcan Sandikcioglu, Özlem A1 - Witt, Julia A1 - Almalla, Ahed T1 - Application of atomic force microscopy (AFM) for in situ corrosion studies of thin film covered AA2024 T3 aluminium alloy surface N2 - The performance of functional coatings and adhesively joined hybrid components relies strongly on the stability of the polymer-metal interface. With the increasing utilization of multi-material structures in the automotive and aerospace industry, it is of great scientific and technical interest to understand the processes leading to interface degradation and to develop novel strategies to increase corrosion and delamination resistance. The aim of this project is to develop thin epoxy-based films and their carbon nanofiller loaded composites on aluminium alloy AA2024-T3 as a model system and to investigate their interfacial stability under corrosive and coupled corrosive-mechanical load. Spin coating was used for the layer-by-layer deposition of poly[(o-cresyl glycidyl ether)-co-formaldehyde] and poly-(ethylenimine) bi-layers. Atomic force microscopy (AFM) results indicate a very homogeneous and dense film with low surface roughness. Carbon nanofillers were introduced either by mixing into the coating components or in between individual layers to control the separation between the carbon nanofillers and alloy surface. The film chemistry and barrier properties were characterized by means of spectroscopic and electrochemical methods, respectively. The degradation and delamination behavior of the epoxy-based films was characterized by means of in situ AFM corrosion experiments. The quantitative imaging (QI) mode allowed the observation of hydrogen-generation induced blister formation during exposure to corrosive electrolyte and how the local corrosion processes evolved with exposure time. Complementary energy dispersive X-ray spectroscopy (EDX) analysis was performed to correlate the corrosion behavior with the different intermetallic particle chemistries and distributions. The presentation will summarize our results on the effect of interface chemistry and carbon nanofiller – alloy separation on the initiation of local corrosion processes on thin film covered AA2024-T3 aluminium alloys. T2 - EuroCorr2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Corrosion KW - Atomic Force Microscopy (AFM) PY - 2019 AN - OPUS4-50293 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Bannick, C.G. T1 - Analytik von Mikroplastik in komplexen Umweltproben N2 - Der Sachstand zur Analytik von Mikroplastik in Umweltproben wird dargestellt. T2 - Fachausstellung Kunststoffanalytik CY - Lüdenscheid, Germany DA - 04.12.2019 KW - TED-GC-MS KW - Mikroplastik KW - Analytik PY - 2019 AN - OPUS4-50005 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Bannick, C.G. T1 - Analytik von Mikroplastik - Verfahren-Ergebnisse-Harmonisierung N2 - Die zunehmenden Nachweise von Kunststoffen in verschiedenen Umweltmedien erfahren in den letzten Jahren weltweit ein zunehmendes wissenschaftliches, gesellschaftliches und politisches Interesse. Besondere Aufmerksamkeit erfahren Kunststoffpartikel von 1-1.000 µm sogenanntes Mikroplastik. Es wurde mittlerweile in Wasser, Böden, Luft und Biota nachgewiesen. Obwohl die Wirkungen auf die natürlichen Umweltfunktionen noch unklar sind und kontrovers diskutiert werden, ist allein durch die ubiquitäre Präsenz eine systematische Erfassung von Eintragsquellen und Verbleib der Partikel über alle Umweltmedien notwendig, um Maßnahmen zur Reduktion der Einträge zu veranlassen. Für eine zuverlässige Erfassung sind medienübergreifende Verfahren zu entwickeln, welche die drei analytischen Schritte, Probennahme, Probenaufbereitung und Detektion beinhalten. Die Verfahren adressieren unterschiedliche Zielgruppen, welche verschiedene analytische Informationen fordern. Für die akademische Bewertung werden Verfahren mit hohem analytischen Aufwand favorisiert, welche möglichst detaillierte Information über Partikelsorte, -größe, -zahl und -oberflächenbeschaffenheit geben. Im Gegensatz dazu, fordern Anwender aus der Praxis schnelle und einfache Monitoring Verfahren, welche die Bestimmung eines Massengehaltes, bzw. eines Grenzwertes zulassen. Allen ist gemeinsam, dass ein hoher interdisziplinärer Anspruch besteht, der sowohl technische Voraussetzungen zur repräsentativen Probennahme und die Limitationen von Detektionsverfahren berücksichtigt, als auch die Fachkompetenz von Biologen, Umweltwissenschaften, Analytiker und Polymerwissenschaftler einschließt. Verfahren zum Mikroplastiknachweis müssen auch verschieden Proben mit sehr unterschiedlichen Gehalten an natürlicher Matrix gerecht werden. So müssen allein für Wasser Verfahren entwickelt werden, die Mikroplastik verschiedener Form (sphärische Partikel, komplexe Bruchstücke, Fasern) aus Medien mit sehr variablen Partikelanteil (u.a. Trinkwasser, Oberflächenwasser, Abwasser) repräsentativ erfassen sowie schnell und kostengünstig sind – einschließlich der notwendigen Probenaufbereitung. Die jeweiligen Detektionsverfahren müssen z.B. einzelne Partikel oder integrale Gehalte über drei Dekadenklassen für thermoplastische und insbesondere auch elastomere Partikelsorten erfassen können. T2 - GDCh Wissenschaftsforum Chemie CY - Aachen, Germany DA - 15.09.2019 KW - TED-GC-MS KW - Mikroplastik KW - Analytik PY - 2019 AN - OPUS4-49995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -