TY - CONF A1 - Trappe, Volker T1 - Infinite life of CFRP evaluated non-destructively with X-ray-refraction topography in-situ mechanical loading N2 - Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying X-ray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP-samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - CFRP KW - NDT KW - Fatigue KW - Damage evolution PY - 2016 AN - OPUS4-37567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holstein, R. A1 - Müller, Christina T1 - Analyzing the reliability of non-destructive tests using the modular modell - a practical approach N2 - Non-destructive testing is an important tool to guarantee the safety of railway traffic. The infrastructure with tracks, switches and sleepers is regularly tested, the locomotives and wagons with their wheels, bogies and axles as well. Many years of experience and some events lead in Germany to a good practice in testing the railway components. Now, European authorities are drafting a system of common requirements and standards for the European Railway Market. The German practice combines an intensive training of the NDT-personnel including sufficient time for practical exercises with organizational measures of the companies, responsible for rolling stock and infrastructure. Through the example of UT-testing of railway axles it will be shown, how training and organizational measures influence the reliability of such testing. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - Modular model KW - Railway KW - Human factors PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375712 UR - http://www.ndt.net/article/wcndt2016/papers/mo1d4.pdf SP - id 19519, 1 EP - 6 AN - OPUS4-37571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, D. A1 - Müller, Christina T1 - Evaluating RT systems with a new POD approach N2 - The usefulness and purpose of evaluating nondestructive testing (NDT) systems and their capabilities has changed in the last decade. The conventional method of simply applying a familiar statistical algorithm to say whether the system is usable for the tasks is history. Nowadays, multiple parameter methods which describe the probabilities of detection (POD) of different systems or real defects need new characteristics and a broader variety of statistical models to describe the true system behaviour. The appraisal of the NDT system involves diverse departments within a company (engineering, NDT-operators, and statisticians), but is, at the same time, more needed and requested than in the past. In this article, an approach is discussed in which professionals from different fields worked well together, accomplishing cost-intensive metallographic studies in correlation with well-understood physical behaviour of NDT-methods as well as deep-discussed mathematical methods to create a holistic evaluation of the technical reliability for a specific radiographic testing (RT) equipment. The first part of the publication will show the comparison between metallographic grinding and the RT indications. An essential innovation over past evaluation methods was the use of a multi-scale smoothing algorithm, which describes physical parameters, which were not used in evaluation like the POD in this way in the past. In the second part the statistical requirements for the POD take the focus. It can often be hard to make significant statements; especially in the case where only a small amount of data is available. The combination of data and the use of knowledge from simulations are essential. One possible solution will be shown for the RT evaluation. The methodology is used for evaluating the digital RT system for the inspection of electron-beam welds, which was method considered to seal the Finnish copper canisters for the final deposit of spent nuclear fuel. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - POD KW - RT PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375732 UR - http://www.ndt.net/article/wcndt2016/papers/we1d4.pdf SP - id 19535, 1 EP - 8 AN - OPUS4-37573 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pelkner, Matthias T1 - Evaluation of high spatial resolution imaging of magnetic stray fields for early damage detection N2 - Metal magnetic memory (MMM) technique with associated ISO 24497-1:3 is gaining considerable interest in the magnetic NDT community. In contrast to traditional Magnetic Flux Leakage (MFL) testing, the inspection objects are not intentionally magnetized by an external magnetic field. Due to the physical coupling between mechanical stress and magnetization of ferromagnetic materials, it is assumed that the distribution of the residual MFL correspond to the internal stress of the specimen, or in the most general sense, to a degradation of the material. Usually, MMM measurements are performed by relatively bulky magnetic inspection sensors. The evaluation of local magnetic field distribution is limited thereby. Highprecision GMR (Giant Magneto Resistance) measurements in the micrometer regime can provide a higher degree of information due to better spatial resolution. We present a concise summary of studies on the correlation of magnetic structure and microstructure of steels. In particular, we compare residual stress measurements in S235JRC steel welds by means of neutron diffraction with high resolution magnetic field mappings. Results indicate a qualitative correlation between residual stresses and local stray field variation. In addition, stray field measurements of plastically deformed specimens for quasi-static and cyclic loading cases are discussed. The present study concludes that GMR sensors can detect inhomogeneous plastic deformations of S235JR steel in a very early stage, without specific signal processing according to the ISO 24497-1:3. T2 - QNDE - Review of Progress in Quantitative Nondestructive Evaluation CY - Atlanta, Georgia, USA DA - 18.07.2016 KW - NDT KW - MMM KW - GMR PY - 2016 AN - OPUS4-37101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pavlovic, Mato A1 - Müller, Christina A1 - Ronneteg, U. T1 - Reliability Analysis of the Phased-Array Ultrasonic System used for the Inspection of Friction Stir Welds N2 - The canister for the permanent storage of spent nuclear fuel used by SKB in Sweden consists of a cast iron insert surrounded by a five centimetre thick shell of copper. It is a safety critical component and in order to secure long-term structural integrity non-destructive methods are used to inspect 100% of the volume of each canister, before it is disposed of in the repository. One of the critical components that requires inspection is a sealing weld, joining the copper tube and the lid. The friction stir weld is inspected using an ultrasonic phased array system. The area of the weld is inspected with several inspection channels with different angles and varying coverage. To make sure that no defects that might occur in the weld are overseen, the reliability of the inspection must be quantified. The reliability of NDT is usually quantified with the probability of detection curves. The influence of the parameters that might influence the POD of the flaws in the weld is investigated analysing the experimental results, as well as with a help of a numerical simulation of the inspection. T2 - 19th Wolrd Conference on Nondestructive Testing CY - Munich, Germany DA - 13.06.2016 KW - NDT KW - Ultrasonic KW - Reliability KW - POD KW - Copper KW - FSW KW - JLH PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366982 VL - 2016/158 SP - We.4.E.5 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-36698 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zoёga, Andreas A1 - Kurz, J. H. A1 - Oelschlägel, T. A1 - Rohrschneider, A. A1 - Müller, Christina A1 - Pavlovic, Mato A1 - Hintze, H. A1 - Kanzler, D. T1 - Investigations to introduce the probability of detection method for ultrasonic inspection of hollow axles at Deutsche Bahn N2 - Currently at Deutsche Bahn (DB) ultrasonic inspections in maintenance procedures for wheelset axles with a bore hole are, to the greatest possible extent, carried out using automated ultrasonic inspection system. Although the acceptance levels are in accordance with DIN 27201 part 7, the testing results have shown in recent years that in the case of true indications, the effective defect sizes were far below the level of acceptance. Due to this experience it can be assumed that the automated ultrasonic inspection systems are testing substantially more sensitively than required. This increased sensitivity leads to an increase in false indications, generally resulting in the unnecessary demounting of wheelsets. In Research cooperation between Federal Institute for Materials Research and Testing (BAM) and DB the effective flaw detection sensitivity of existing automated ultrasonic inspection system will be determined and the true/false indication ratio optimised. Through systematic investigations with the Probability of Detection method on the existing automated ultrasonic inspection system the results could be directly applied to the optimisation of existing ultrasonic inspections of wheelset axles with a bore hole in maintenance procedures and the level of reliability can be considerably increased. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - POD KW - Railway KW - Axles KW - UT PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375813 UR - http://www.ndt.net/article/wcndt2016/papers/we2g4.pdf SP - id 19515, 1 EP - 8 AN - OPUS4-37581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Müller, Alexander A1 - Hickmann, Stefan T1 - Infinite life of CFRP evaluated non-destructively with X-ray-refraction topography in-situ mechanical loading N2 - Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying Xray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - CFRP KW - NDT KW - Fatigue KW - Damage evolution PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375015 UR - https://www.ndt.net/?id=19360 SN - 978-3-940283-78-8 VL - 2016 SP - 1 EP - 9 PB - DGZFP CY - Berlin AN - OPUS4-37501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ronneteg, U. A1 - Grybäck, T. A1 - Bertovic, Marija A1 - Müller, Christina A1 - Pavlovic, Mato T1 - Safe for 1 million years – NDT matters! N2 - The General Guidance in the Swedish regulations state that the safety assessment for a final repository for spent nuclear fuel should be 1 million years after closure. SKB developed the KBS-3 method, according to which the spent nuclear fuel is protected by three barriers. It is encapsulated in canisters with a diameter of 1 metre and a length of 5 metres. The canister consists of a cast iron insert surrounded by a 5 centimetre thick shell of copper. The canisters are disposed in the bedrock at a depth of about 500 meters surrounded by bentonite clay. In order to assess the safety over this extremely long period, an extensive quality control programme is applied to the canisters before deposit. In this programme, the use of non-destructive testing (NDT) is vital. The safety assessment of the canister in turn places high demands on the coverage, detectability, and reliability of the applied NDT inspections of the canister parts, i.e. cast iron insert, copper base, tube and lid, and the copper friction stir welds (FSW). This paper presents the extensive full-scale inspection development programme that runs at the Canister Laboratory in Oskarshamn (Sweden). In order to fulfil the high demands, phased array ultrasonic inspection techniques are developed using practical trials aided by ultrasonic modelling. The techniques apply, for example, different frequencies, inspection angles, focus depths, and both longitudinal and shear waves. Increased inspection reliability of the FSW is achieved by applying digital X-ray technique using a 9 MeV linear accelerator and a line detector. To complete the coverage, complementary surface inspections methods, i.e. eddy current array, magnetic flux sensor techniques and magnetic particle inspection, are applied. The canister safety assessment was the driving force to include reliability studies during the NDT development. Initially, the technical reliability was considered, resulting in development of advanced POD models (probability of detection). In combination with human factors studies, these models were implemented as tools in the development of the NDT techniques. Human factors studies were also applied to improve the inspection procedures to be more user-friendly enabling reliable inspections. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - Spent nuclear fuel PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375785 UR - http://www.ndt.net/article/wcndt2016/papers/we4e4.pdf SP - id 19464, 1 EP - 9 AN - OPUS4-37578 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - McGrath, B. A1 - Holstein, R. A1 - Bertovic, Marija T1 - How NDT companies can benefit from human factors knowledge N2 - Ultrasonic phased array is, currently, the technology which is being applied as the solution to a lot of inspection problems. The perceived benefits are seen to be worth the outlay on equipment and specialised personnel. Yet, there is a source of knowledge, freely available, which can also deliver immediate benefits, through more reliable inspection results, and consequently increased client confidence, but which is largely ignored by the greater part of the NDT community. This talk will review the latest Human Factors knowledge and provide practical illustrations of how companies can use it to improve their competitive edge. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - Human factors PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375742 UR - http://www.ndt.net/article/wcndt2016/papers/tu4d3.pdf SP - id 19532, 1 EP - 8 AN - OPUS4-37574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan T1 - Elastic wave propagation of ultrasound in bituminous road surfaces – simulations and measurements N2 - Maintenance costs of road infrastructure are increasing steadily. Adverse environmental impacts on infrastructure get more and more important as well. Therefore, it is important to determine how limited financial resources can be directed with an optimum pay-out. The present study takes first steps towards the usage of low-frequency ultrasound as a tool to evaluate the road condition. T2 - International Symposium Non-Destructive Testing in Civil Engineering 2015 CY - Berlin, Germany DA - 15.09.2015 KW - Wave propagation KW - Ultrasonic KW - NDT KW - Simulation PY - 2015 AN - OPUS4-38837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -