TY - JOUR A1 - Suárez Ocaño, Patricia A1 - Ávila Calderón, Luis A1 - Agudo Jácome, Leonardo A1 - Rehmer, Birgit A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Effect of 700–900 °C heat treatments and room and high temperature tensile deformation on the microstructure of laser powder bed fused 316L stainless steel N2 - The effect of post-processing heat treatments on the hierarchical microstructure evolution and mechanical strength of the austenitic stainless steel 316L produced by laser powder bed fusion has been investigated. Heat treatments between 700 and 900 ◦C and 0.5 to 3 h, were applied to samples treated at 450 ◦C for 4 h. The results showed a stable microstructure at all studied temperatures and times in terms of grain size, morphology, aspect ratio, density of low-angle grain boundaries, and texture. However, temperature and time promoted the diffusion of segregated elements together with a reduction in dislocation density and disappearance of the cellular structure. This was associated with a reduction in hardness and tensile proof strength at both room and high temperature. In addition, microstructural characterization coupled with thermodynamic CALPHAD-based equilibrium calculations showed that the formation of carbides and intermetallic phases was already visible after annealing at 800 ◦C for 3 hours, although these intermetallics did not affect the tensile properties at this level. Analysis of the microstructure evolution after tensile deformation showed differences in the deformation mechanisms at room and high temperature, with twinning and martensitic transformation occurring at room temperature, the latter not widely reported for additively manufactured 316L. Finally, comparisons with similar materials produced under comparable conditions showed differences in the tensile properties, attributed to differences in chemical composition and the associated presence of stacking faults in the undeformed state. KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Tensile properties KW - Microstructure PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632471 DO - https://doi.org/10.1016/j.msea.2025.148469 SN - 0921-5093 VL - 939 SP - 1 EP - 24 PB - Elsevier CY - Amsterdam AN - OPUS4-63247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rockenhäuser, Christian A1 - Rowolt, C. A1 - Milkereit, B. A1 - Darvishi Kamachali, Reza A1 - Kessler, O. A1 - Skrotzki, Birgit T1 - On the long-term aging of S-phase in aluminum alloy 2618A N2 - The aluminum alloy 2618A is applied for engine components such as radial compressor wheels which operate for long time at elevated temperatures. This results in coarsening of the hardening precipitates and degradation in mechanical properties during the long-term operation, which is not taken into account in the current lifetime prediction models due to the lack of quantitative microstructural and mechanical data. To address this issue, a quantitative investigation on the evolution of precipitates during long-term aging at 190 °C for up to 25,000 h was conducted. Detailed transmission electron microscopy (TEM) was combined with Brinell hardness measurements and thorough differential scanning calorimetry (DSC) experiments. The results showthat GPB zones and S-phase Al2CuMg grow up to < 1,000 h during which the GPB zones dissolve and S-phase precipitates form. For longer aging times, only S-phase precipitates coarsen, which can be well described using the Lifshitz–Slyozov Wagner theory of ripening. A thorough understanding of the underlying microstructural processes is a prerequisite to enable the integration of aging behavior into the established lifetime models for components manufactured from alloy 2618A. KW - Long-term aging KW - Transmission electron microscopy (TEM) KW - Differential scanning calorimetry (DSC) KW - Microstructure KW - S-phase KW - Ostwald ripening PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519899 DO - https://doi.org/10.1007/s10853-020-05740-x SN - 0022-2461 VL - 56 IS - 14 SP - 8704 EP - 8716 PB - Springer Nature AN - OPUS4-51989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Han, Ying A1 - Schriever, Sina A1 - von Hartrott, Philipp A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Creep dataset for aluminum alloy EN AW-2618A in the T61 and overaged condition 1000 h/190 °C N2 - The article presents creep data for the precipitation-hardened aluminum alloy EN AW-2618A, which was tested in its initial slightly underaged T61 condition and after being aged at 190 °C for 1000 h. The creep test temperatures ranged between 160 °C and 230 °C, and the applied initial stresses between 40 MPa and 290 MPa. The testing times reached up to 4700 h. 19 data sets are provided as creep strain vs. time series. A data schema originally developed to manage creep reference data of a single-crystalline nickel-based superalloy was adapted for the research data set of the polycrystalline aluminum alloy and used to enrich the test data with extensive metadata. The dataset can be used to calibrate and validate creep models. The creep data supplement the hardness and microstructure data that have been previously published. KW - Aluminum alloy EN AW-2618A KW - Aging KW - Overaging KW - High temperature KW - Creep PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641517 DO - https://doi.org/10.1016/j.dib.2025.112054 SN - 2352-3409 VL - 62 SP - 1 EP - 10 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-64151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bresch, Sophie A1 - Mieller, Björn A1 - Moos, R. A1 - Rabe, Torsten T1 - Lowering the sintering temperature of calcium manganate for thermoelectric applications N2 - This study combines three different approaches to lower the sintering temperature of Sm-doped CaMnO3 to save energy in production and facilitate co-firing with other low-firing oxides or metallization. The surface energy of the powder was increased by fine milling, sintering kinetics were enhanced by additives, and uniaxial pressure during sintering was applied. The shrinkage, density, microstructure, and thermoelectric properties were evaluated. Compared to micro-sized powder, the use of finely ground powder allows us to lower the sintering temperature by 150 K without reduction of the power factor. By screening the effect of various common additives on linear shrinkage of CaMnO3 after sintering at 1100 ○C for 2 h, CuO is identified as the most effective additive. Densification at sintering temperatures below 1000 ○C can be significantly increased by pressure-assisted sintering. The power factor at room temperature of CaMnO3 nano-powder sintered at 1250 ○C was 445 μW/(m K2). Sintering at 1100 ○C reduced the power factor to 130 μW/(m K2) for CaMnO3 nano-powder, while addition of 4 wt.% CuO to the same powder led to ∼290 μW/(m K2). The combination of fine milling, CuO addition, and pressureassisted sintering at 950 ○C resulted in a power factor of ∼130 μW/(m K2). These results show that nano-sized powder and CuO addition are successful and recommendable strategies to produce CaMnO3 with competitive properties at significantly reduced temperatures and dwell times. KW - Sintering additive KW - Liquid phase sintering KW - Pressure assisted sintering PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555467 DO - https://doi.org/10.1063/5.0098015 SN - 2158-3226 VL - 12 IS - 8 SP - 1 EP - 9 PB - American Institute of Physics (AIP) CY - New York, NY AN - OPUS4-55546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bresch, Sophie A1 - Stargardt, Patrick A1 - Moos, Ralf A1 - Mieller, Björn T1 - Co‐Fired Multilayer Thermoelectric Generators Based on Textured Calcium Cobaltite N2 - Thermoelectric generators are very attractive devices for waste heat energy harvesting as they transform a temperature difference into electrical power. However, commercially available generators show poor power density and limited operation temperatures. Research focuses on high‐temperature materials and innovative generator designs. Finding the optimal design for a given material system is challenging. Here, a theoretical framework is provided that allows appropriate generator design selection based on the particular material properties. For high‐temperature thermoelectric oxides, it can be clearly deduced that unileg multilayer generators have the highest potential for effective energy harvesting. Based on these considerations, prototype unileg multilayer generators from the currently best thermoelectric oxide Ca3Co4O9 are manufactured for the first time by industrially established ceramic multilayer technology. These generators exhibit a power density of 2.2 mW/cm² at a temperature difference of 260 K, matching simulated values and confirming the suitability of the technology. Further design improvements increase the power density by a factor of 22 to facilitate practicable power output at temperature differences as low as 7 K. This work demonstrates that reasonable energy harvesting at elevated temperatures is possible with oxide materials and appropriate multilayer design. KW - Optical and Magnetic Materials KW - Electronic PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-596306 DO - https://doi.org/10.1002/aelm.202300636 SN - 2199-160X VL - 10 IS - 3 SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-59630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Digital representation of materials testing data for semantic web analytics: Tensile stress relaxation testing use case N2 - This study aims to represent an approach for transferring the materials testing datasets to the digital schema that meets the prerequisites of the semantic web. As a use case, the tensile stress relaxation testing method was evaluated and the testing datasets for several copper alloys were prepared. The tensile stress relaxation testing ontology (TSRTO) was modeled following the test standard requirements and by utilizing the appropriate upper-level ontologies. Eventually, mapping the testing datasets into the knowledge graph and converting the data-mapped graphs to the machine-readable Resource Description Framework (RDF) schema led to the preparation of the digital version of testing data which can be efficiently queried on the web. KW - Digitalization KW - Tensile stress relaxation KW - Ontology KW - Mechanical testing KW - Semantic web PY - 2024 DO - https://doi.org/10.4028/p-xSmHN2 VL - 987 SP - 47 EP - 52 PB - Trans Tech Publications Ltd CY - Switzerland AN - OPUS4-61152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Jokisch, Torsten A1 - Olbricht, Jürgen A1 - Fedelich, Bernard T1 - Fatigue crack growth in nickel-based alloy 247DS with side-brazed pre-sintered preform N2 - Pre-sintered preform (PSP) brazing is employed in the repair of gas turbine components made of nickel-based alloys, including restoring the surface and dimensions of turbine blades and vanes. This study investigates the fatigue crack growth (FCG) behavior of Alloy 247DS specimens with side-brazed PSP material, mimicking a typical sandwich structure formed during such repairs. FCG tests were conducted at an elevated temperature of 950 °C and a stress ratio (R) of 0.1 on specimens with PSP layer thicknesses of 1.5 mm, 2 mm, 3 mm, and 4.5 mm to assess the influence of PSP thickness on fatigue crack growth behavior. Fractographic and metallographic analyses were performed to elucidate the underlying crack growth mechanisms and the microstructural characteristics of both materials. The results revealed that a crack consistently initiated in the PSP material, originating from the starter notch, particularly at the specimen corner during the pre-cracking phase. Additionally, crack propagation in the PSP material consistently advanced ahead of the crack in the Alloy 247DS. This crack growth behavior is attributed to the difference in elastic properties and microstructural differences between the PSP and base material. Metallographic analysis revealed the presence of porosity and brittle precipitates within the PSP material, which led to faster intergranular crack growth. Conversely, Alloy 247DS exhibited transgranular crack growth, contributing to the observed crack propagation behavior. This study demonstrates the applicability of standard FCG testing methods and an approach to characterize the FCG behavior in sandwich specimens, where crack growth occurs simultaneously in both materials, providing a preliminary understanding of crack growth behavior in Alloy 247DS with side-brazed PSP. KW - High-temperature fatigue crack growth (FCG) KW - Nickel-based alloys KW - Alloy 247DS KW - Pre-Sintered Preform (PSP) PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-629783 DO - https://doi.org/10.1016/j.ijfatigue.2025.108961 VL - 197 SP - 1 EP - 13 PB - Elsevier BV AN - OPUS4-62978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chahal, Shweta A1 - Xiao, Boyu A1 - Grant, Jessica A1 - Furniss, David A1 - Farries, Mark A1 - Phang, Sendy A1 - Neate, Nigel A1 - Robertson, Lorelei A1 - Roe, Martin A1 - Barney, Emma A1 - Seddon, Angela B. T1 - Ce3+-doped chalcogenide glass fibre for laser beyond 4 microns wavelength: Glass material-integrity N2 - The 4-μm wavelength barrier encountered for mid-infrared fibre lasing based on heavy metal fluoride glasses has been overcome. We reported, in 2021, the first continuous wave, mid-infrared fibre laser operating beyond 4 μm at room temperature in a fibre with a Ce3+-doped selenide-chalcogenide core. Defects, such as crystallites in the core glass, could cause unwanted light-scattering, diminishing fibre laser efficiency. It is important to identify such optical loss mechanisms and eradicate them. Here, we report on investigating the material nano-structure of a chalcogenide-glass lasing fibre which exhibits 7 mW laser power output; the fibre has a Ce3+-doped core (8.5 μm diameter), concentrically surrounded by an inner- and outer-cladding, where both cladding-glasses are nominally the same composition. High resolution transmission electron microscopy and electron diffraction show that the core, inner-cladding and outer-cladding of the lasing fibre are internally nano-crystallite-free and amorphous. However, the external outer surface of the last 10 m of fibre drawn, of the total 100 m, contains monoclinic GeSe2 crystallites adjacent to discrete, small (<0.5 mm) wrinkled defects. The final length of fibre is drawn from the final part of the glass fibreoptic preform. The glass preform has as its outermost component an extruded chalcogenide glass tube. It is the last part of the tube which spends the longest time at high temperature inside the extruder during tube manufacture, encouraging heterogeneous nucleation at the tube outer-surface in contact with the extruder. These heterogeneous nuclei subsequently nucleate crystal growth during fibre-drawing in the outermost fibre surface. KW - Optical glass KW - Photonics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653371 DO - https://doi.org/10.1016/j.optmat.2025.117219 SN - 0925-3467 VL - 166 SP - 1 EP - 14 PB - Elsevier CY - Amsterdam AN - OPUS4-65337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Ontology-Oriented Modeling of the Vickers Hardness Knowledge Graph N2 - This research deals with the development of the Vickers hardness knowledge graph, mapping the example dataset in them, and exporting the data-mapped knowledge graph as a machine-readable Resource Description Framework (RDF). Modeling the knowledge graph according to the standardized test procedure and using the appropriate upper-level ontologies were taken into consideration to develop the highly standardized, incorporable, and industrial applicable models. Furthermore, the Ontopanel approach was utilized for mapping the real experimental data in the developed knowledge graphs and the resulting RDF files were successfully evaluated through the SPARQL queries. KW - Data Mapping KW - FAIR Data KW - Ontology KW - Knowledge Graph KW - Vickers Hardness PY - 2024 DO - https://doi.org/10.4028/p-k8Gj2L VL - 149 SP - 33 EP - 38 PB - Trans Tech Publications Ltd CY - Switzerland AN - OPUS4-59981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stargardt, Patrick A1 - Bresch, Sophie A1 - Falkenberg, Rainer A1 - Mieller, Björn T1 - Effect of Reaction Layers on Internal Stresses in Co‐Fired Multilayers of Calcium Manganate and Calcium Cobaltite N2 - A widespread recovery of waste heat requires a cost‐effective production of thermoelectric generators. Thermoelectric oxides are predestined for use at high temperatures. For manufacturing reasons, a multilayer generator design will be easily scalable and cost‐effective. To evaluate the potential of ceramic multilayer technology for that purpose, a multilayer of the promising thermoelectric oxides calcium cobaltite (Ca3Co4O9), calcium manganate (CMO, CaMnO3), and glass–ceramic insulation layers is fabricated. Cracks and reaction layers at the interfaces are observed in the microstructure. The compositions of these reaction layers are identified by energy‐dispersive X‐ray spectroscopy and X‐ray diffraction. Mechanical and thermal properties of all layers are compiled from literature or determined by purposeful sample preparation and testing. Based on this data set, the internal stresses in the multilayer after co‐firing are calculated numerically. It is shown that tensile stresses in the range of 50 MPa occur in the CMO layers. The reaction layers have only a minor influence on the level of these residual stresses. Herein, it is proven that the material system is basically suitable for multilayer generator production, but that the co‐firing process and the layer structure must be adapted to improve densification and reduce the tensile stresses in the CMO. KW - Ceramic multilayers KW - Co-firings KW - Internal stresses PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601626 DO - https://doi.org/10.1002/pssa.202300956 SP - 1 EP - 9 PB - Wiley VHC-Verlag AN - OPUS4-60162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -