TY - CONF A1 - Taparli, Ugur Alp A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Michalik, K. A1 - Mory, D. T1 - Online TIG-Weld Monitoring by Laser-Induced Breakdown Spectroscopy N2 - Chemical compositions of the welds have significant effect on weld quality. Current inspection methods for the weld seams employ mostly post factum methods and cannot prevent weld defects.Elemental burn offs may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. T2 - Forschungsseminar OvGU Magdeburg CY - Magdeburg, Germany DA - 27.11.2019 KW - In situ measurement KW - LIBS TIG welding KW - Austenitic stainless steels KW - Chemical composition PY - 2019 AN - OPUS4-49831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander A1 - Thiede, Tobias A1 - Mishurova, Tatiana A1 - Léonard, Fabien A1 - Laquai, René A1 - Ulbricht, Alexander A1 - Serrano Munoz, Itziar A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Non destructive characterization in Additive manufacturing N2 - An overview of non destructive characterisation in additively manufactured materials using computed tomography, refraction and diffraction based stress analysis T2 - BAM-IFW workshop CY - IFW Dresden, Germany DA - 28.03.2019 KW - Residual stress analysis KW - Additive manufacturing KW - Computed tomography KW - Diffraction KW - X-ray refraction PY - 2019 AN - OPUS4-49842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander A1 - Thiede, Tobias A1 - Mishurova, Tatiana A1 - Kromm, Arne A1 - Cabeza, Sandra A1 - Serrano Munoz, Itziar A1 - Ulbricht, Alexander A1 - Sprengel, Maximilian A1 - Bruno, Giovanni T1 - Residual stresses in am review and oulook of activities at BAM N2 - Critical discussion of residual stress Analysis in additive manufacturing from examples in literature and an overview of activities at BAM T2 - Workshop on Fatigue of Additive Manufactured Metallic Components CY - BAM, Berlin, Germany DA - 16.05.2019 KW - Diffraction KW - Additive Manufacturing KW - Residual stress PY - 2019 AN - OPUS4-49843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sprengel, Maximilian A1 - Kromm, Arne A1 - Cabeza, S. A1 - Mishurova, Tatiana A1 - Nadammal, N. A1 - Thiede, Tobias A1 - Serrano Munoz, Itziar A1 - Ulbricht, Alexander A1 - Evans, Alexander A1 - Bruno, Giovanni T1 - Combining diffraction methods to non-destructively characterize through thickness residual stress gradients in L-PBF IN718 N2 - Laser based Powder Bed Fusion (L-PBF) is an additive manufacturing technique that has been continuously developed in the past years. It offers unparalleled design freedom and the resulting mechanical properties match, in some cases even exceed, those of materials processed by conventional manufacturing techniques. Nonetheless the process is prone to create Residual Stresses (RS) resulting from the sequential melting and solidification of the material. RS can reduce load bearing capacity and generate unwanted distortions thus diminishing the potential of L-PBF. This research activity aimed at characterizing the RS state in Inconel 718 L-PBF specimens using multiple diffraction methods. The microstructure as well as the surface and bulk residual stresses were investigated. The RS analysis was performed using X-ray, synchrotron and neutron diffraction methods to provide information at different depths within the specimen. The measurements were performed at the Bundesanstalt für Materialforschung und –prüfung (BAM), the EDDI beamline at BESSY II synchrotron and E3 line at BER II neutron reactor of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results revealed a depth depending RS state. The longitudinal and transverse stress components measured by X-ray and synchrotron at the surface agree well, exhibiting stress values around the yield strength of the material. In addition, synchrotron mapping showed gradients along the width and length of the sample for the longitudinal and transverse stress components. Lower RS values compared to surface RS were measured in the bulk of the material using neutron diffraction. The longitudinal stress component in the bulk was tensile and gradually decreased towards the edge of the specimen. The normal component however did not change significantly along the specimen dimensions and was of compressive nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers, which has to be further investigated. T2 - First European Conference on Structural Integrity of Additively Manufactured Materials CY - Trondheim, Norway DA - 09.09.2019 KW - Additive Manufacturing KW - Residual Stress KW - Diffraction PY - 2019 AN - OPUS4-49804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sprengel, Maximilian A1 - Kromm, Arne A1 - Evans, Alexander A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - Insight into the residual stress formation in additively manufactured austenitic steel 316l N2 - Overview of residual stresses in austenitic stainless steel 316l manufactured by laser baser powder bed fusion and determined via x-ray and neutron diffraction T2 - Doktorandenseminar der Otto-von-Guericke Universität CY - Magdeburg, Germany DA - 28.11.2019 KW - Additive Manufacturing KW - Residual Stress KW - Neutron Diffraction KW - 316L PY - 2019 AN - OPUS4-49850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Birgit A1 - Simon, Sebastian A1 - Sigmund, Sandra A1 - Ziemann, M. A. A1 - von Werder, Julia T1 - Characterization of Alkali-Silica Reaction Products by means of Raman Spectroscopy before and after Application of Accelerated Tests N2 - Alkali silica reaction (ASR) is a major concrete durability problem resulting in significant maintenance and reconstruction costs for concrete infrastructures all over the world. To determine whether an aggregate is potentially reactive, accelerated concrete tests are used. Aim of this study is the chemical and microstructural characterization of ASR-products formed under the performance conditions of motorway pavements and during subsequent tests on the remaining ASR susceptibility. Samples were taken from concrete motorway pavements. Some of the samples already showed first indications for beginning damages whereas others showed deteriorations only after applying a performance testing procedure for the estimation of future risk of ASR damage. In a first step ASR-products were identified by polarized light microscopy in thin sections. The reaction products where then analyzed by Raman Spectroscopy and finally the chemical composition of the ASR-products was identified by SEM with EDX. The results indicate that most reaction products show an increasing Ca/Si-ratio with progressive crack length. If an ASR-product develops inside an aggregate and moves through the cement paste, it has a high (Na+K)/Si-ratio at the beginning which decreases with increasing distance from its place of origin. The Raman spectra of the ASR-products are characterized by two broad bands indicating specific Q-species of different amorphous gel networks. Within the scope of the analysis distinctions in the microstructure and the chemical composition of the ASR-gels were detected relating to various conditions of accelerated testing. T2 - 15th International Congress on Chemistry of Cement CY - Prague, Czech Republic DA - 16.09.2019 KW - Alkali-silica reaction KW - Raman microscopy KW - Microstructure KW - Concrete motorway pavements KW - Performance test PY - 2019 AN - OPUS4-49527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evsevleev, Sergei A1 - Mishurova, Tatiana A1 - Sevostianov, Igor A1 - Garcés, Gerardo A1 - Requena, Guillermo A1 - Cabeza, Sandra A1 - Bruno, Giovanni T1 - Load transfer and damage evolution in multiphase Al alloy matrix composites under uniaxial compression N2 - Aluminum alloys are extensively used in the automotive industry. Particularly, squeeze casting production of Al-Si alloys is employed in the conception of metal matrix composites (MMC) for combustion engines. Such materials are of a high interest since they allow combining improved mechanical properties and reduced weight and hence improve efficiency. We investigate two types of MMCs, which can be potentially used for production of combustion engine pistons: 1) a near-eutectic cast AlSi12CuMgNi alloy reinforced with 15%vol. Al2O3 random planar oriented short fibers and 2) the same alloy reinforced with 7%vol. Al2O3 random planar oriented short fibers + 15%vol. SiC particles. Complex 3D microstructure of the samples in as-cast condition, consisting of four and five phases (Al matrix, eutectic Si, intermetallics, Al2O3 fibers and SiC particles) was investigated by synchrotron computed tomography (CT). Advanced methods based on machine learning were applied for segmentation of all phases. This allowed extracting quantitative information such as volume fraction, shape and interconnectivity of every phase. In-situ compression tests during neutron diffraction experiments were used to track the load transfer among phases, while CT on pre-strained samples to monitor and quantify damage. A micromechanical model was developed to simulate the evolution of the internal stress of each phase during uniaxial compression. We showed that in composites with the Al2O3 fiber mat plane perpendicular to the load axis the Al-alloy matrix presents a large hydrostatic stress component, i.e. undergoes compression also in the direction transverse to the external load. This feature holds with and without the addition of SiC ceramic reinforcement and is absent in the case when the Al2O3 fiber mat plane is parallel to the load axis. We show, that the intermetallics play a decisive role at very high loads, when all other reinforcement phases suffer (extensive) damage. The addition of SiC particles does alleviate the load on the Al2O3 fibers, on the eutectic Si, and on the intermetallic phases in both cases of parallel and orthogonal (to the load axis) Al2O3 fiber orientation. Apart from the beneficial addition of ceramic reinforcement, the presence of intermetallic phase and eutectic silicon, forming an interconnected network even at high loads, when single particles break, confers peculiar properties to these multi-phase composites. T2 - The 3rd International Conference on Light Materials CY - Manchester, UK DA - 05.11.2019 KW - Aluminum alloy KW - Metal Matrix Composite KW - Computed tomography KW - Neutron diffraction KW - Stress analysis KW - Load partition PY - 2019 AN - OPUS4-49640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigt, Marieke A1 - von Werder, Julia A1 - Meng, Birgit T1 - Investigation of the zonation of thermally treated ultra high performance concrete N2 - Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 150 MPa and its high durability. Due to thermal treatment at 90°C a strength comparable to the 28-days-strength can be achieved immediately after the treatment and in some cases can be even further increased up to 30 %. The explanations for the increase in strength are the accelerated hydration of the clinker minerals and the intensified pozzolanic reaction contributing to a denser microstructure and hence, a high performance in compressive strength. Former research shows that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section. The width of the margin increases with shorter pre-storage time before the thermal treatment and with omitting protective measures against desiccation during the treatment. Specimens exhibiting a zonation typically show a lower compressive strength compared to the undisturbed reference whereas changes in chemistry, mineral content and microstructure were not reported in detail. In this study the zonation of thermally treated UHPC is investigated with respect to its chemistry, mineral composition and microstructure to allow predictions on durability and strength development. Measurements show a change in pore sizes, minerals phase composition and element distribution leading to the visible zonation and weaker bending tensile strength compared to the reference. T2 - 2nd International Conference of Sustainable Building Materials CY - Einhoven, Netherlands DA - 11.08.2019 KW - UHPC KW - Thermal treatment KW - Zonation KW - Desiccation KW - Microstructure KW - Durability PY - 2019 AN - OPUS4-49472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Meng, Birgit A1 - Rogge, Andreas T1 - Characterizing the Fatigue Behavior of High-Performance Concrete for Wind Energy Structures N2 - Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally. Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring. T2 - LORCENIS - Long Lasting Reinforced Concrete for Energy Infrastructue under Severe Operating Conditions CY - Gent, Belgium DA - 10.09.2019 KW - Compressive Cyclic loading KW - Fatigue KW - High-strength concrete KW - Non destructive testing KW - Ultrasonic testing PY - 2019 AN - OPUS4-49474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Orlov, N. K. A1 - Milkin, P. V. A1 - Evdokimov, P. A. A1 - Putlayev, V. I. A1 - Günster, Jens T1 - Sintering of sodium and potassium tcp based ceramic for bone grafting application N2 - Biomaterials for bone replacement and grafting should possess sufficient strength, be bioresorbable and demonstrate osteoconductive and osteoinductive properties. However, resorption of modern materials for bone grafting (hydroxyapatite (HA) and tricalcium phosphate (TCP)) is reported, in some cases, to be not enough, this is why the search for more soluble compounds compared to HA and TCP looks very perspective. A possible way to increase ceramics solubility leads to partial substitution of Ca2+ -ions in Ca3(PO4)2 by alkali cations, like Na+ or/and K+. Improvement of solubility stems from decreasing lattice energy of a substituted phase, as well as the increase in hydration energy of the ions releasing from the phase to ambient solution. From this viewpoint, bioceramics based on compositions from Ca3(PO4)2 - CaKPO4 - CaNaPO4 ternary system seems to be prospective for bone replacement and grafting in the sense of resorption properties. At the same time, one should bear in mind that solubility level (resorbability) is governed not only by reduction of lattice energy but also by microstructure features. Grain sizes and porosity contribute much to dissolution rate making the study of sintering of the ceramics mentioned above highly important. To control Ca3(PO4)2 - CaKPO4 - CaNaPO4 based ceramic microstructure it is necessary to know possible phase transformations in the system and the way to manage microstructure by sintering schedule or sintering process. In this work, an isothermal section for phase diagram of Ca3(PO4)2 - CaKPO4 - CaNaPO4 ternary system is studied with several techniques. According to the XRD of quenched samples, this phase triangle has four single-phase areas at 1200˚C (Figure 1). It was shown that single-phase CaK0.6Na0.4PO4 cannot be sintered to full-dense ceramics by conventional sintering regardless time-temperature schedule. Two-step sintering technique, beneficial in the case of HA-ceramics, was unsuccessful in all cases of calcium-alkali phosphate compositions. However, field-assisted sintering techniques like, e.g. Spark Plasma Sintering (SPS), can overcome this problem due to significant impact on grain boundary diffusion. In connection with this fact, grains grow much slower retaining sintering process in a pore control regime. In this work CaK0.6Na0.4PO4 low-porous ceramics was also fabricated by FAST-methods of sintering. Moreover, other alternative sintering techniques, such as reaction sintering, may be useful in accelerating ions diffusion but stopping excessive grain growth.Strength properties of ceramics were evaluated by B3B-testing, micro- and nanoindentation techniques. Fracture toughness also becomes higher with potassium content increase, guiding porosity level. Resorption properties of sintered ceramics were studied in different solutions with pH=5 and 7.4. Acknowledgements. The research of sintering processes in calcium phosphate materials were funded by RFBR according to the research project № 18-33-00974. T2 - XVI ECerS Conference 2019 CY - Turin, Italy DA - 16.06.2019 KW - Phase transformations KW - Bioceramics KW - Mixed Ca-K-Na phosphates KW - Na and K rhenanites KW - Phase diagram PY - 2019 AN - OPUS4-49622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -