TY - CONF A1 - Bachmann, Marcel A1 - Kunze, R. A1 - Avilov, Vjaceslav A1 - Rethmeier, Michael T1 - Finite element modelling of an AC electromagnetic weld pool support in full penetration laser beam welding of thick duplex stainless steel plates N2 - An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an AC magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles-Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel surrounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modelled with a 3D turbulent steady-state model including heat transfer and fluid dynamics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagneticinduced pressure. The FE software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 mT and 90 mT. The corresponding oscillation frequencies were between 1 kHz and 10 kHz and the electromagnetic AC powers were between 1 kW and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 kW and 2.4 kW at oscillation frequencies between 1.2 kHz and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass fullpenetration laser beam welding of 15 mm and 20 mm thick AISI 2205. T2 - ICALEO 2015 - 34th International congress on applications of lasers & electro-optics CY - Atlanta, GA, USA DA - 2015-10-18 KW - Electromagnetic weld pool support KW - Laser beam welding KW - FE simulation KW - Duplex stainless steel PY - 2015 SN - 978-1-940168-05-0 SP - 650 EP - 659 AN - OPUS4-35036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of solidification cracking susceptibility of laser welded joints of austenitic stainless steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack. T2 - 3rd International conference in Africa and Asia CY - Luxor, Egypt DA - 02.11.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - A-29, 1 EP - A-29, 9 AN - OPUS4-36522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test N2 - Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test The strain rate has a significant influence on the formation of the hot crack It was possible to determine the critical strain and strain rate that led to shot crack formation A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed. Good agreement between the strain field measured using the DIC technique and the simulation results Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties T2 - 8th International Conference Beam Technologies & Laser Application CY - St. Petersburg, Russia DA - 21.09.2015 KW - CTW-Test KW - Investigated materials KW - FEM study KW - Hot cracking PY - 2015 AN - OPUS4-38347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120 N2 - Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120 Hybrid laser arc welding of the root pass: Significant reduction in the weld cross section – savings of filler material Lower heat input into the base material - improvement of mechanical properties of the weld joint  The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld  14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials: Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - High power laser KW - Hybrid laser arc welding KW - Weld specimens KW - Charpy V-notch tests KW - Tensile tests PY - 2015 AN - OPUS4-38342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Development of a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets N2 - Test procedure to characterize the cracking susceptibility of RSW-steels has been developed During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel Complex phase steels behavior during test procedure: Crack length growth with increasing force could not be determined The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case) 30 T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - Externally loaded hot cracking test KW - Variables influencing hot cracking KW - Self-restraint hot cracking KW - Welding jig PY - 2015 AN - OPUS4-38348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of hot crack susceptibility of laser welded joints of four austenitic steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding T2 - The METEC and 2nd European Steel Technology and Application Days CY - Düsseldorf, Germany DA - 15.06.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - 1 EP - 5 AN - OPUS4-36525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test. N2 - Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials. T2 - BEAM TECHNOLOGIES & LASER APPLICATION CY - St. Petersburg, Russia DA - 21.09.2015 KW - Solidification cracking KW - Hot cracking test KW - FEM KW - Laser beam welding PY - 2015 SN - 978-5-7422-5150-7 SP - 55 EP - 68 AN - OPUS4-36615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Schneider, G. ED - Zschech, E. ED - Petzow, G. T1 - Laserstrahl-MSG-Hybridschweißen von Rohren aus Hochfestem Stahl API-X80/ -X100 N2 - Das Laser-MSG-Hybridschweißverfahren führt bei untersuchten hochfesten Pipelinestählen API X80 und X120 reproduzierbar zu Schweißverbindungen mit anforderungsgerechten Zähigkeitseigenschaften. Eine metallurgische Beeinflussung der Schweißnahtzähigkeit ist durch eine gezielte Auswahl des Zusatzwerkstoffes möglich, wobei die maximale Eindringtiefe des Zusatzwerkstoffes in die Tiefe der Laserhybridnaht zu beachten ist. Die maximal erzielbare Eindringtiefe des Zusatzwerkstoffes ist auf ca. 14 mm begrenzt. Die eingesetzte Art des MSG-Lichtbogens hatte keinen erkennbaren Einfluss auf die Aufmischung im Laseranteil der Laserhybridnaht. Die besseren Ergebnisse der Kerbschlagzähigkeit konnten mit Metallpulverdrähten erreicht werden. Mit den erzielten gemittelten Werten der Schlagarbeit: ca. 200 J bei -60°C für X80 und ca. 53 J bei -40°C für X120 werden Anforderungen der Norm API 5L und DIN EN 10208-2 für die beiden untersuchten Grundwerkstoffe erfüllt. T2 - 49. Metallographie-Tagung CY - Dresden, Germany DA - 16.09.2015 KW - Hochfester Stahl KW - Laserstrahl-MSG-Hybridschweißen PY - 2015 SN - 978-3-88355-410-5 VL - 47 SP - 139 EP - 144 PB - Inventum CY - Sankt Augstin AN - OPUS4-44419 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Avilov, Vjaceslav A1 - Fritzsche, André A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Full penetration laser beam welding of thick duplex steel plates with electromagnetic weld pool support N2 - Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56kW for welding velocity of 1.0 and 0.5 m min(-1), respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current (AC) power needed to completely compensate the sagging on the root side was found to be approximate to 1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min(-1) was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible-the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW. (C) 2016 Laser Institute of America T2 - ICALEO 2015 - 34th International congress on applications of lasers & electro-optics CY - Atlanta, GA, USA DA - 2015-10-18 KW - Electromagnetic weld pool support KW - Laser beam welding KW - Duplex stainless steel PY - 2015 SN - 978-1-940168-05-0 SP - 571 EP - 579 PB - Amer inst physics CY - Melville, NY, USA AN - OPUS4-35035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Graf, B. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Combined laser additive manufacturing for complex turbine blades N2 - Laser beam processes are increasingly used in the field of additive manufacturing. Prominent methods are either powderbed-based like Laser Metal Fusion (LMF), or utilizing a powder nozzle like Laser Metal Deposition (LMD). While LMF allows the manufacturing of complex structures, build rate, part volumes and material flexibility are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, and materials can be changed easily during the process. However LMD shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates and increased material flexibility. In this paper, combined manufacturing with additive technologies LMF and LMD is described. Its benefit for industry with emphasis on turbomachinery is shown. As reality test for the innovation, an industrial turbine blade is manufactured. KW - Turbine blade KW - Additive manufacturing KW - Laser metal fusion KW - Laser metal deposition PY - 2016 SN - 2499-9733 VL - 3 IS - 20 SP - 34 EP - 42 AN - OPUS4-38709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Trends in European thin sheet welding N2 - 1. Steel Production and Processing in Europe 2. Design Trends in the Automotive Industry 3. Welding Technologies in the Automotive Industry 4. Problems while Processing AHSS/UHSS 5. Challenges in Joining Multi-Material Structures 6. Mechanical Joining Technologies 7. Thermal-Mechanical Joining Processes 8. Energy Efficiency of Welding Processes T2 - AWS Sheet Metal Welding Conference XVII CY - Livonia, MI, USA DA - 19.10.2016 KW - Lightweight concepts PY - 2016 AN - OPUS4-38763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Julian A1 - Rethmeier, Michael T1 - Influence of manufacturing conditions on the cracking susceptibility of AHSS during resistance spot welding N2 - The complex microstructure and the advanced mechanical properties of AHSS steel types lead to an increased susceptibility to weld cracking, especially during resistance spot welding under ‘rough’ manufacturing conditions. Various activities have been conducted in recent years at the Federal Institute for Materials Research and Testing (BAM) and the Fraunhofer IPK on this matter. Understandings about the safe spot weldability and the process of crack-forming itself were gained, and solutions for handling this issue given. The performed work includes investigations on the influence of initial gaps as well as restraint intensity. An experimental method for the determination of the general cracking susceptibility, i.e. a material ranking of AHSS in respective to current restraints was developed. Coupled mechanical and thermal simulations of the welding process show the present internal stress-strain-conditions and values responsible for the formation of cracks, deepening the understanding of the process. By using this easy to perform and material-independent method for the determination of the cracking susceptibility in resistance spot welded joints, small and medium sized companies can profit by rapidly evaluating the joinability of their handled material combinations as well as OEMs. T2 - Sheet Metal Welding Conference XVII CY - Livonia, Michigan, USA DA - 18.10.2016 KW - Welding under external loading KW - Cracking susceptibility of AHSS KW - Resistance spot welding KW - Initial gap PY - 2016 SP - Session 1-2, 1 EP - Session 1-2, 15 AN - OPUS4-38137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Anwendung der digitalen Bildkorrelationstechnik zur Untersuchung der Heißrissanfälligkeit laserstrahlgeschweißter Verbindungen mit dem CTW-Test N2 - In dieser Studie wurde die Heißrissanfälligkeit beim Laserstrahlschweißen für die Werkstoffe 1.4376, 1.4301 und 1.4828 mit Hilfe des CTW­ Test quantifiziert. Bei den Versuchen konnten Erstarrungsrisse in den Proben generiert werden. Zusätzlich können mit der Bildkorrelations-Technik die lokalen Dehnungen und Dehnungs­raten während des Heißrisstests gemessen wer­ den. In Verbindung mit einem externen Dioden­laser zum Beleuchten der zu messende Oberflä­che und lnterferenzfiltern an den Kameras konn­ten die DIC Messungen ohne optische Störungen durchgeführt werden. Die Ergebnisse zeigen, dass die Heißrissbildung bei einer externen Belastung von 3 % für die Stahlsorte 1.4376 zu erwarten ist. Für die Stahls­ orte 1.4301 beträgt dieser Grenzwert 2 % und 1,5 % für die Stahlgüte 1.4828. Außerdem ist zu beobachten, dass die Gesamtrisslänge mit zu­ nehmender äußerer Zugbeanspruchung steigt T2 - 35. Assistentenseminar Füge- und Schweißtechnik CY - Institut für Werkstoff- und Fügetechnik der Otto-von­ Guericke-Universität Magdeburg DA - 01.12.2014 KW - Digitale Bildkorrelationstechnik KW - Heißrissanfälligkeit KW - Untersuchung laserstrahlgeschweißter Verbindungen KW - CTW-Test PY - 2016 SN - 978-3-945023-55-6 VL - 2016/34 SP - 50 EP - 54 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-38065 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - European perspective on 21st century BIW joining challenges N2 - •Main Welding Technologies in the Automotive: RSW and laserbeam welding •Light Weight Design leads to increasing use of AHSS and UHSS which results in higher demands for the joining technology •Joining Multi-Material Structures offers opportunities for “new” Thermal-Mechanical Joining Processes and Hybrid Processes •In the coming years a trend towards sustainable manufacturing can be seen. Comparison between laserbeam and RSW will be a tight match! T2 - AWS Sheet Metal Welding Conference XVll CY - Livonia, MI, USA DA - 19.10.2016 KW - Resistance spot welding KW - Laser beam welding KW - Lightweight concepts KW - AHSS KW - Weld cracks PY - 2016 AN - OPUS4-38339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Welding with high-power lasers: trends and developments N2 - High power laser welding technology has made a large progress in the last decade and established itself in different industrial applications; Hybrid laser arc welding is one of the most prospective technologies for heavy components assembling; Modern high speed video observation, in situ x-ray screening as well as simulation techniques contributed to better understanding of laser welding process; New approaches e.g. application of electromagnetic fields for melt pool control and welding at reduced pressure ambient have significantly contributed to extending the process boundaries far beyond the known Limits. T2 - LANE 2016 CY - Fürth, Germany DA - 19.09.2016 KW - Laser hybrid welding KW - Process diagnostics and simulation KW - Electromagnetic weld support system KW - Laser beam welding under vacuum/reduced pressure PY - 2016 AN - OPUS4-38340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Influence of manufacturing conditions on the cracking susceptibility of AHSS during resistance spot welding N2 - The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested Surface cracks have no influence on the fatigue life Samples with cracks in the electrode indentation /HAZ where tested Stiffness curves are not significantly influenced by surface cracks 3D FE-Simulation demonstrate no changes of stress due to surface imperfections • Welding under external forces was found suitable for characterizing AHSS materials New quick and easy-to-perform procedure for establishing a material ranking regarding cracking susceptibility T2 - AWS Sheet Metal Welding Conference XVII CY - Livonia, MI, USA DA - 19.10.2016 KW - 3D-FE-Simulation PY - 2016 AN - OPUS4-38366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Graf, B. A1 - Schuch, M. A1 - Petrat, T. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Combined laser additive manufacturing with powderbed and powder nozzle for turbine parts N2 - Metal additive manufacturing is often based on laser beam processes like Laser Metal Fusion (LMF) or Laser Metal Deposition (LMD). The LMF process is in particular suitable for very complex geometries. However build rate, part volume and material flexibility are limited in LMF. In contrast, LMD achieves higher deposition rates, less restricted part sizes and the possibility to change the material composition during the build-up process. On the other hand, due to the lower spatial precision of the material deposition process, the complexity of geometries is limited. Therefore, combined manufacturing with both LMF and LMD has the potential to utilize the respective advantages of both technologies. In this paper, combined additive manufacturing with LMF and LMD is described for Ti-6Al-4V and Inconel 718. First, lattice structures with different wall thickness and void sizes are built with LMF. The influence of LMD material deposition on these LMF-structures is examined regarding metallurgical impact and distortion. Cross-sections, x-ray computer tomography and 3D-scanning results are shown. For the titanium alloy specimen, oxygen and Nitrogen content in the deposited material are analysed to evaluate the LMD shielding gas atmosphere. The results are used to develop guidelines for a LMD build-up strategy on LMF substrates. With these findings, a gas turbine burner is manufactured as reality test for the combined approach. T2 - 6th International Conference on Additive Technologies iCAT 2016 CY - Nürnberg, Germany DA - 29.11.2016 KW - Ti-6Al-4V KW - Inconel 718 KW - Combined laser manufacturing PY - 2016 SN - 978-691-285-537-6 SP - 317 EP - 323 AN - OPUS4-38702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Numerical Sensitivity Analysis of TRIP-Parameter K on Weld Residual Stresses and Weld Distortion N2 - A combined experimental numerical approach is applied for a sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on welding residual stresses and welding distortion for the welding of the low-alloyed high-strength S960QOL with the high-alloyed hig-strength filler material CN13-4-IG. A thermo-mechanical FE model of a real GMA welding process was experimentally validated against termperature field, X-Ray stress measurments and optical distortion measurement. Within the sensititvity analysis K was varied and the influence on the calculated welding residual stresses and welding distortion is evaluated by performing corresponding FEA. The correct order of K magnitude is necessary in order to reproduce the residual stresses qualitatively and quantitatively. For the sufficient reproducing of the welding distortion the transformation induced plasticity can be neglected. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - TRIP PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 361 EP - 383 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frei, J. A1 - Rethmeier, Michael ED - Rethmeier, Michael T1 - Einfach anwenderfreundlich - Numerische Simulation von Fügestellen N2 - Ob in der Automobilindustrie, beim Rohrleitungs- oder beim Kraftwerksbau – anspruchsvolle und hochwertige Fügeverbindungen entscheiden oft über die Qualität des Endproduktes. Um z. B. das Verzugsverhalten von Karosseriebauteilen vorab einschätzen zu können, setzen Hersteller auf die numerische Simulation der geschweißten Komponenten. Besondere Aufmerksamkeit gilt hier den Fügestellen. Da diese oft nur wenige Millimeter klein sind, kommen konventionelle Prüfverfahren wie der Zugversuch hier jedoch nicht ohne weiteres in Frage. Forscher des Fraunhofer IPK untersuchen deshalb eine alternative Methode, um die negativen Begleiterscheinungen des thermischen Schweißens im Vorfeld am PC zu analysieren und nötige Gegenmaßnahmen ableiten zu können. KW - Numerische Simulation PY - 2016 SN - 1438-1125 IS - 2 SP - 14 EP - 15 AN - OPUS4-38747 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Petrat, T. A1 - Rethmeier, Michael ED - Rethmeier, Michael T1 - Schicht für Schicht Auftragsschweißen dreidimensionaler Körper N2 - Die Anwendung der additiven Fertigung nimmt stark zu. Eine neue Designfreiheit erlaubt es hier den Konstrukteurinnen und Konstrukteuren, die Bauteilfunktion in den Vordergrund der Entwicklungen zu stellen. Leichtbaustrukturen sowie Funktionsintegration machen es möglich, vormals Bauteile aus vielen Einzelkomponenten jetzt in einem einzigen Bauteil zu vereinigen. Experten am Fraunhofer IPK qualifizieren das Laser-Pulver-Auftragschweißen für die additive Fertigung und legen dabei besonderen Wert auf die Automatisierung des Verfahrens. KW - Laser-Pulver-Auftragsschweißen PY - 2016 SN - 1438-1125 IS - 1 SP - 18 EP - 19 AN - OPUS4-38746 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -