TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of solidification cracking susceptibility of laser welded joints of austenitic stainless steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack. T2 - 3rd International conference in Africa and Asia CY - Luxor, Egypt DA - 02.11.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - A-29, 1 EP - A-29, 9 AN - OPUS4-36522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of hot crack susceptibility of laser welded joints of four austenitic steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding T2 - The METEC and 2nd European Steel Technology and Application Days CY - Düsseldorf, Germany DA - 15.06.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - 1 EP - 5 AN - OPUS4-36525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Na, S.-J. A1 - Han, S.-W. A1 - Muhammad, S. A1 - Zhang, L. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Karhu, M. A1 - Kujanpa, V. T1 - Flow and Bead Formation Characteristics in High Power Laser Welding at Different Welding Positions (Invited Talk) N2 - The numerical simulations of high power laser keyhole welding at different welding positions are performed by using Volume-Of-Fluid (VOF) method. The main material is SS400. The multi-physics phenomenon is considered using several models, such as the heat flux of Gaussian heat source, the recoil pressure with Clausisus-Clapeyron equation, the Marangoni flow considering temperature gradient, the buoyancy force with Boussinesq approximation, the additional shear stress and heat source due to metallic vapor ejected through keyhole entrance, the bubble formation assumed as adiabatic bubble, and the multiple-reflection by solving proper discriminant, are used. To analyze the fluid flow pattern, the concept of streamline formed by reconstructing the value of the velocity vector is applied. Partial and full penetration cases at different welding positions are considered. The welding position seems to have only a minor influence on bead formation characteristics in both cases. This is probably due to the fact that the recoil pressure has a major influence when compared to other driving forces. The flow characteristics and fluid velocity in weld pool are analyzed to compare the gravity direction effect at different welding positions. It is observed that the clockwise flow pattern is mainly formed by the recoil pressure on the keyhole surface in the case of partial penetration. The laser energy can't maintain the whole weld pool when the weld pool size becomes too large. And then the solidification starts from the middle part of weld pool and a necked weld pool shape is formed. In the full penetration welding, the weld pool flow patterns are affected by the leakage of laser power through the full penetration keyhole and also by surface tension. Furthermore, the numerical simulation of full penetration welding with AISI316L is also performed to analyze the effect of material properties. The weld bead shapes obtained by simulations were compared with the corresponding experimental results to confirm the validity of the process models adopted and the CFD simulation tool. T2 - Lasers in Manufacturing Conference 2015 CY - München, Germany DA - 22.06.2015 KW - Macro Processing (Joining, Welding) KW - Weld pool KW - Flow pattern KW - Different welding position KW - Numerical simulation KW - High power laser keyhole welding PY - 2015 SP - 1 EP - 6 AN - OPUS4-37163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, Torsten A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up strategies for generating components of cylindrical shape with laser metal deposition N2 - Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process. T2 - Lasers in Manufacturing Conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Ti - 6Al - 4V KW - Additive Manufacturing KW - Build - up Strategy KW - Laser Metal Deposition KW - Stainless Steel PY - 2015 UR - http://www.wlt.de/lim/Proceedings/Stick/sessions.html SP - 1 EP - 6 AN - OPUS4-37829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gook, S. A1 - Gumenyuk, Andrey T1 - Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120 N2 - Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120 Hybrid laser arc welding of the root pass: Significant reduction in the weld cross section – savings of filler material Lower heat input into the base material - improvement of mechanical properties of the weld joint  The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld  14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials: Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - High power laser KW - Hybrid laser arc welding KW - Weld specimens KW - Charpy V-notch tests KW - Tensile tests PY - 2015 AN - OPUS4-38342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Bakir, Nasim A1 - Gumenyuk, Andrey T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test N2 - Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test The strain rate has a significant influence on the formation of the hot crack It was possible to determine the critical strain and strain rate that led to shot crack formation A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed. Good agreement between the strain field measured using the DIC technique and the simulation results Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties T2 - 8th International Conference Beam Technologies & Laser Application CY - St. Petersburg, Russia DA - 21.09.2015 KW - CTW-Test KW - Investigated materials KW - FEM study KW - Hot cracking PY - 2015 AN - OPUS4-38347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Suwala, H. A1 - Gumenyuk, Andrey T1 - Development of a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets N2 - Test procedure to characterize the cracking susceptibility of RSW-steels has been developed During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel Complex phase steels behavior during test procedure: Crack length growth with increasing force could not be determined The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case) 30 T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - Externally loaded hot cracking test KW - Variables influencing hot cracking KW - Self-restraint hot cracking KW - Welding jig PY - 2015 AN - OPUS4-38348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test. N2 - Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials. T2 - BEAM TECHNOLOGIES & LASER APPLICATION CY - St. Petersburg, Russia DA - 21.09.2015 KW - Solidification cracking KW - Hot cracking test KW - FEM KW - Laser beam welding PY - 2015 SN - 978-5-7422-5150-7 SP - 55 EP - 68 AN - OPUS4-36615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Impiego di un dispositivo per il vuoto locale di tipo mobile nell'applicazione del processo laser. T1 - Deployment of mobile vacuum device in the application of laser beam welding N2 - Lo sviluppo del pennacchio di vapore durante la saldatura laser di metalli con direzioni di propagazione lungo l'asse del fascio laser comporta una riduzione della potenza del laser assorbita nel keyhole. Questi effetti negativi possono essere notevolmente attenuati mediante l'applicazione di una ridotta pressione ambientale, diminuendo così l'interazione tra il fascio laser ed i prodotti dell'evaporazione, condizione che favorisce la stabilità del processo di saldatura e si traduce in una maggiore profondità di penetrazione. Una tecnica convenzionale utilizza il principio della camera a vuoto, simile a quello utilizzato per la saldatura a fascio elettronico. L'applicazione di questa tecnica è limitata dalle dimensioni della camera e riduce quindi i vantaggi di questo approccio, particolarmente per componenti di grandi dimensioni. Abbiamo dimostrato la possibilità di applicazione del vuoto in forma localizzata con apparecchiature mobili, che consentono di generare una pressione ridotta solo in una piccola zona attorno al keyhole. Utilizzando un dispositivo di chiusura appositamente progettato per la pressione, di tipo mobile, che può essere spostato lungo l'asse del giunto è possibile ottenere una pressione assoluta di circa 200 mbar. Questo è sufficiente per aumentare la profondità di penetrazione di circa il 50%. I campioni di acciaio grado S355 sono stati saldati con una potenza laser incrementale da 5 kW a 12 kW a pressione atmosferica e confrontati con quelli saldati a pressione ambiente di 200 mbar. La valutazione della sezione longitudinale ha rivelato un aumento della profondità di penetrazione dei giunti di circa il 35%. Inoltre, sono stati eseguiti test di saldatura in configurazione di giunti testa a testa con lamiere di 15 mm di spessore con diverse potenze associate al fascio laser eseguiti a pressione atmosferica ed a pressione ambiente ridotta di circa 200 mbar. L'aumento nella profondità di penetrazione fino al 40% è relativo alla pressione ridotta. In particolare, basse velocità di saldatura con pressione ridotta si sono rivelate particolarmente vantaggiose in termini di aumento della penetrazione. N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the chamber size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Samples from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. KW - laser welding KW - Laserstrahlschweißen KW - vacuum KW - local effects KW - Vakuum KW - Lokale Effekte PY - 2016 SN - 0035-6794 VL - 04 IS - 04 SP - 1 EP - 8 AN - OPUS4-35619 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rethmeier, Michael A1 - Momeni, Kaveh A1 - Schippereit, Christian A1 - Weber, Gert T1 - Einfluss von fertigungsbedingten Spalten auf das Tragverhalten der Widerstandspunktschweißverbindungen aus hochfesten Stählen N2 - In einem Forschungsvorhaben wurde der Einfluss von fertigungsbedingten Spalten von bis zu 3 mm auf das Tragverhalten der Widerstandspunktschweißverbindungen aus Stählen am Beispiel von HX340LAD+Z (Werkstoffnummer 1.0933), HCT780X+Z (1.0943), HCT980C (1.0955) und 22MnB5+AS140 untersucht. Neben spaltabhängigen Schweißbereichen wurden auch statische Festigkeit, dynamische Festigkeit sowie Schwingfestigkeit betrachtet. Schließlich wurden ein Prozesssicherheitskoeffizient sowie eine Prozess-Festigkeits-Kenngröße abgeleitet, mit deren Hilfe der Anwender das Verhalten der Punktschweißverbindungen unter Spalteinfluss beurteilen kann. KW - resistance spot welding KW - strength KW - quality assurance KW - Qualitätssicherung KW - Festigkeit KW - Widerstandspunktschweißen PY - 2016 SN - 0036-7184 VL - 68 IS - 1-2 SP - 22 EP - 27 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-35366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -