TY - CONF A1 - Gumenyuk, Andrey T1 - Determination of critical local straining conditions for solidification cracking at laser beam welding by experimental and numerical methods N2 - The phenomenon of solidification cracking has been the subject of numerous research projects over the years. Great efforts have been made to understand the fundamentals of hot cracking. It is generally agreed that solidification cracks form in the solidification range between the liquidus and solidus temperatures under the combination of thermal, metallurgical and mechanical factors. There is still a need to determine the time-resolved strain distribution in the cracksensitive region in order to analyse the local critical conditions for solidification cracking phenomena. This was a strong motivation for the development of a measurement system used in this study to estimate the local strains and strain rates in the zone where the solidification crack is expected to occur. The laser beam welding experiments were conducted using the Controlled-Tensile-Weldability test (CTW test) to apply an external strain condition during welding to generate solidification cracks. The CTW test is a test method for investigating the suscep�tibility of laser-welded joints to solidification cracking, in which the sample can be subjected to a defined strain at a defined strain rate during welding. In combination with experimental investigations, numerical simulations provide spatially detailed and time-dependent information about the strain development during the welding process, especially regarding the critical conditions for solidification cracking. Therefore, this tool was also used in the present study to evaluate the accuracy of measurement methods and to estimate experimentally derived values and their concrete influence on the formation of solidification cracks. By integrating experimental methods and numerical simulations, this study investigates the spatially resolved and temporally changing development of strain during welding, with a particular focus on the critical conditions that lead to the formation of solidification cracks. T2 - GAMM 94th Annual Meeting CY - Magdeburg, Germany DA - 18.03.2024 KW - Laser beam welding KW - Solidification cracking KW - FEM simulation PY - 2024 AN - OPUS4-62417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey T1 - Two-colour thermography for measurement of temperature distribution in laser beam welding N2 - Solidification cracking is a frequently observed phenomenon in laser beam welding of austenitic stainless steels and other metallic alloys. Characterisation of cracking susceptibility requires knowledge of the precise and spatially resolved temperature distribution near the solidification front in the welding process. Thermography is a standard tool that provides a qualitative estimate of the 2D temperature field. The general disadvantage of this method is its dependence on the emission characteristics of the measured object. For welding applications, these can vary significantly in the temperature range above and below the melting temperature. For this purpose, we have developed a thermography-based measurement technique using a SWIR camera system in combination with two narrow bandpass filters that use the principle of two-wavelength pyrometry to estimate absolute temperature values. This technique was used to determine the temperature distributions and gradients near the solidification front of laser-welded austenitic steel. The results were validated by other measurements. T2 - 13th CIRP Conference on Photonic Technologies [LANE 2024] CY - Fürth, Germany DA - 16.09.2024 KW - Laser beam welding KW - Solidification cracking KW - FEM simulation PY - 2024 AN - OPUS4-62415 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey T1 - Strain distribution vs strain evolution during solidification cracking CTW test for laser beam welding of 1 mm austenitic stainless steels N2 - Laser welding is a widely established manufacturing process across many industrial sectors. However, solidification cracking and the weldability of materials have remained contentious issues for many years, particularly concerning the causes of hot crack formation. The local distribution of total strain was measured in close proximity to the solidification zone during laser welding of AISI 304 and AISI 310S stainless steels, using the Controlled Tensile Weldability (CTW) test. In this setup, 1 mm thick weld coupons were subjected to a defined external tensile load during welding. Mechanical loading parameters were varied by adjusting the strain rate and ultimate strain level to identify the critical conditions that lead to solidification crack formation along the weld seam centerline. Using Digital Image Correlation (DIC) and the optical flow method [1], we estimated the local strain distribution at the surface near the molten pool and tracked its evolution across several characteristic zones—before, during, and after the application of mechanical loading. The results revealed that solidification crack formation coincides with regions of high plastic deformation within a critical temperature range. Furthermore, we identified a clear relationship between strain rate and both crack initiation probability and maximum local strain. Importantly, neither strain rate nor maximum strain alone is sufficient to predict cracking; instead, their combined effect must be considered to accurately assess hot cracking susceptibility. T2 - AJP 2025 CY - Coimbra, Portugal DA - 16.10.2025 KW - Laser beam welding KW - Solidification cracking KW - Optical measurement PY - 2025 AN - OPUS4-64431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -