TY - JOUR A1 - Fahmy, Alaa A1 - Kolmangadi, Mohamed Aejaz A1 - Schönhals, Andreas A1 - Friedrich, J. T1 - Structure of plasma‐deposited copolymer films preparedfrom acrylic acid and styrene: Part III sulfonation andelectrochemical properties N2 - Acrylic acid-styrene copolymer films were deposited plasma-chemically more gently using the pulsed plasma mode instead of the continuous mode, with linear and some slightly branched chains and marginal crosslinking. Then, the styrene unit of copolymers was wet-chemically sulfonated by chlorosulfuric acid. On exposure to air, the formed 4-chlorosulfonic acid groups hydrolyze to sulfonic acid groups (-SO3H). FTIR, XPS and broadband dielectric spectroscopy were employed to characterize the composition, the structure, the functional groups, and the electrochemical performance for the copolymers. A high concentration of sulfonic acid-containing groups was obtained in the sulfonated PS sample. The values of the DC conductivity DC for the sulfonated sample of the AA/S copolymer are ca. five orders of magnitude higher than that of the not-sulfonated copolymer materials. KW - Plasma Polymers KW - Electrolyte membrane PY - 2022 U6 - https://doi.org/10.1002/ppap.202100222 SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-54539 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fahmy, Alaa A1 - Saied, M. A. A. A1 - Morgan, N. A1 - Abdelbary, H. A1 - Bahy, S. M. A1 - Schönhals, Andreas A1 - Friedrich, J. F. T1 - Modified polyvinyl chloride membrane grafted with an ultra-thin polystyrene film: structure and electrochemical properties N2 - The work explores the synthesis and the properties of a novel composite membrane System based on modified polystyrene (PS) grafted onto a polyvinyl chloride (PVC) membrane. PVC membranes were prepared by solution-casting followed by exposure to an atmospheric pressure dielectric barrier discharge (DBD) with O2 to obtain an activated Surface for grafting PS to it. Moreover, the thus prepared membranes were chemically modified furthermore by amination with polyethyleneimine or sulfonation with 4 M sulfuric acid. The membrane surface characteristics such as wettability, structure and morphology were investigated using water contact angle measurements, attenuated total reflection Fourier transform infrared spectroscopy and scanning electron microscopy experiments. The thermogravimetric stability and electrolytic responses of the membranes were studied utilizing TGA, ion exchange capacity (IEC), and solvent uptake. A significant result of plasma and chemical modification was to produce a membrane material with low permeability. Thus, the methanol permeability of the sulfonated membranes measured for 12 h was measured to 2.34$10� 8 cm2 s� 1 compared to 177.00$10� 8 cm2 s� 1 of Nafion 117®which is considered as a benchmark. This result indicates that the prepared sulfonated samples are an innovative and effective material for decreasing the methanol crossover in fuel cells to a great extent. This makes the PVC-g-St membranes are promising and attractive as new materials for polyelectrolyte membrane for fuel cells. KW - Electrolyte membrane KW - Fuell cells PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-526794 VL - 12 SP - 2273 EP - 2284 PB - Elsevier B.V. AN - OPUS4-52679 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -