TY - JOUR A1 - Wäsche, Rolf A1 - Sato, K. A1 - Brandt, Guido A1 - Schmid, Thomas A1 - Sasaki, S. A1 - Woydt, Mathias T1 - Wear behaviour of MgO stabilized zirconia in hot steam environment up to 400°C JF - Wear N2 - Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates. KW - Hot steam KW - Zirconia KW - Friction KW - Wear KW - Tribofilm KW - Raman spectroscopy PY - 2019 DO - https://doi.org/10.1016/j.wear.2019.01.047 VL - 426-427 SP - 428 EP - 432 PB - Elsevier B.V. AN - OPUS4-47873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Ehrke, Roman A1 - Woydt, Mathias T1 - Wear of alpha-alumina in hot steam up to 300°C T2 - Progress in Mechanics and Materials in Design N2 - Selfmated alpha-alumina sliding couples have been investigated under oscillating sliding at 100 N load in different humidity conditions in air as in hot steam up to temperatures of 300°C and ambient pressures up to 4 bar. T2 - 7th International Conference on Mechanics and Materials in Design CY - Albufeira, Portugal DA - 11.06.2017 KW - Apha-alumina KW - Wear KW - Steam KW - Temperature KW - Abrasion PY - 2017 SN - 978-989-98832-6-0 SP - 265 EP - 266 PB - LusoImpress S.A. CY - Avintes, Portugal AN - OPUS4-41128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wäsche, Rolf A1 - Brandt, Guido A1 - Ehrke, Roman A1 - Nolze, Gert A1 - Schmid, Thomas A1 - Sasaki, S. A1 - Woydt, Mathias T1 - Wear behaviour of alpha-alumina in hot steam at high contact pressure JF - Wear N2 - The work examines the wear behaviour of α-aluminium oxide by combining thermodynamic modelling with advanced wear testing as well as analytical methods to get a better understanding of this structural ceramic material wear behavior and its possible use in high temperature steam environment. KW - Aluminium oxide KW - Temperature KW - Hot steam KW - Diaspore KW - Ceramic KW - Wear PY - 2018 DO - https://doi.org/10.1016/j.wear.2018.02.012 SN - 0043-1648 SN - 1873-2577 VL - 404-405 SP - 22 EP - 30 PB - Elsevier B.V. AN - OPUS4-44449 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Status of nickel bonded niobium carbide (NbC) as a substitute for cobalt-bonded tungsten carbide (WC) as cutting tools and for wear protection T2 - Advances in Powder Metallurgy & Particulate Materials N2 - Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded (NbC0.88-12Co SPS). The NiMo-bonded stoichiometric NbC1.0 grades enable the subtituion of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt bonded NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness. T2 - POWDERMET 2017 CY - Las Vegas, USA DA - 13.06.2017 KW - Niobium carbide (NbC) KW - Cutting tools KW - Wear PY - 2017 SP - 721 EP - 734 PB - Metal Powder Industries Federation AN - OPUS4-40671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection T2 - International Conference on Refractory Metals and Hard Materials N2 - The tool lifes of uncoated NiMo and NiMo2C-bonded stoichiometric NbC1.0 grades under dry turning 42CrMo4 and C45E were between +30 % to + 100 % higher and up compared to WC-6Co (fine grain). Niobium is today largely available. NbC grades displayed lower dry sliding friction over WC grades. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metal KW - Machining KW - Nickel PY - 2017 SP - HM 102/1 EP - HM 102/16 AN - OPUS4-40593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological property profile of hard metals and metal matrix composites based on niobium carbide T2 - Proceedings of the International Symposium on Wear Resistant Alloys for the Mining and Processing Industry N2 - This work is focused on the tribological profile of NbC-based material, as well as their potential applications and environmental implications. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Metal KW - Binder KW - Metal matrix composite KW - Friction KW - Wear KW - Hardness KW - Solubility KW - Toughness KW - Abrasion PY - 2018 SN - 978-0-692-05382-9 SP - 427 EP - 461 AN - OPUS4-44201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Cannizza, E. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection JF - International Journal of Refractory Metals & Hard Materials N2 - Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components. KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metals KW - Machining KW - Nickel PY - 2018 DO - https://doi.org/10.1016/j.ijrmhm.2018.01.009 SN - 0263-4368 VL - 72 SP - 380 EP - 387 PB - Elsevier Ltd. AN - OPUS4-44166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Cannizza, E. T1 - Tailoring the functional profile of niobium carbide (NbC) as cutting tool materials and for wear protection T2 - 2018 World Congress on Powder Metallurgy N2 - In the present work it was shown that the properties of NbCx, like micro-hardness, hot-hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. T2 - WORLDPM2018 CY - Beijing, China DA - 16.09.2018 KW - Niobium carbide KW - Properties KW - Wear KW - Machining PY - 2018 SP - Part 5, 785 EP - 795 AN - OPUS4-46204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Adjusting the functional properties of niobium carbide N2 - The process window and range of functional properties of NbC is wide, because micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, because Nb4C3, Nb6C5 and other short and long range ordered phases occur in the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary Phase diagram, and by the type of binder. Further improvements enable the addition of secondary carbides. Supporting results from literature and different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. NbC can be synthesized by carbothermal conversion of Nb2O5 or be metallurgically grown in melts and leached out as coarse NbC cubes. NbC provides comparably lower friction in many relevant tribo-contacts and displays low wear. NbC and Nb2O5 have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO3 and Co3O4. T2 - 2016 International Conference on Powder Metallurgy & Particulate Materials CY - Boston, MA, USA DA - 05.06.2016 KW - Niobium carbide KW - NbC KW - Wear KW - Friction PY - 2016 AN - OPUS4-36497 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Tribological profile of hydraulic oils by using SRV N2 - Hydraulic oils are well established formulations developed around the pump test. Requirements for energy efficiency and also environmentally acceptable properties increased the demand for development. In the same time, system pressure and the used of servo-hydraulic vanes increased bringing specific formulations and materials to their limit. The vane pump is a key component in hydraulic systems and many other tribosystems in hydraulic circuits operate under different tribological operating conditions. The concept for ranking of hydraulic oils consists in using existing SRV-based ASTM test methods for evaluation of friction, wear and extreme pressure properties: D6425, friction and wear of oils (homologue to DIN 51834-2), D7421, extreme pressure properties of oils and D7755, wear volumes of ball and disks (homologue to DIN 51834-3. The tribological properties are assessed under the regime of mixed/boundary lubrication The SRV-based concept of tribological profile generates the wear volumes on two triboelements (specimen) and the extreme pressure properties as well as the evolution of friction in the wear and extreme pressure load step test. Thus, the benchmark and validation of hydraulic oils bear on a wider range of tribological properties. Round robin test results using the aforementioned testing concept will be shown. Another outcome is tribological set limits for inclusion in hydrau¬lic oil speci¬fications. T2 - Workshop on Tribological Testing of Components Using the SRV Test Machine CY - Bellevue, WA, USA DA - 30.06.2016 KW - Tribology KW - Hydraulic oils KW - SRV KW - ASTM test method KW - Friction KW - Wear PY - 2016 AN - OPUS4-36734 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Substituting tungsten carbide (WC) as cutting tools and for wear protection by niobium carbide (NbC) N2 - As a refractory carbide, niobium carbide (NbC) is today still a forgotten carbide with hidden properties, such as wear resistance, thus qualifying NbC for the group of tribological materials with enhanced wear resistance. Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur In the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary phase diagram, which enable the tailoring of properties and offers a much wider process window than known from WC. The type binder (Co, Ni, NiMo) and its concentration as well as the sintering process (SPS, liquid phase sintering) determine the box “hardness-toughness”, which will be illuminated based on more than 100 grades. The impact of these tailored properties on sliding wear (T= 22/400°C; v= 0,1-10 m/s) and cutting performance will be illuminated by tribological and machining results. Cutting test results under emulsion and coolant-free operation of cobalt and Fe3Al bonded, straight NbC versus WC based inserts against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35) will be highlighted. T2 - STLE 2016 Annual Meeting and Exhibition CY - Las Vegas, NV, USA DA - 15.05.2016 KW - Niobium Carbide (NbC) KW - Friction KW - Wear PY - 2016 AN - OPUS4-36152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - Tailoring the functional properties of niobium carbide N2 - Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0,75≤ x ≤1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of These tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃O₄. T2 - 40th International Conference and Exposition on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 24.01.2016 KW - Niobium carbide KW - Hard metal KW - Wear KW - Friction KW - Machining KW - Cutting KW - Metal matrix composite PY - 2016 SP - Paper: 2347292, 1 EP - 13 AN - OPUS4-35640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias T1 - Sub-stoichiometric oxides for wear resistance JF - Wear N2 - In the present work it was shown that the tribologcal profiles of special model oxides under dry unidirectional sliding have shown, that sub-oxides have a contribution to the tribological behavior of carbides and cermets, when they are tribo-oxidatively formed, because their tribological profiles as monolithic materials are homologous in part or totally, or compete with hardmetals or cermets, depending from the operating conditions regarded. KW - Sub-oxide KW - Friction KW - Wear KW - Carbide KW - Hardmetal PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-498154 DO - https://doi.org/10.1016/j.wear.2019.203104 SN - 0043-1648 N1 - Eine identische Version zu diesem Artikel wurde publiziert unter: Wear 438-439 (2019) 102735, https://doi.org/10.1016/j.wear.2019.01.066 - An identical version to this article was published under: Wear 438-439 (2019) 102735, https://doi.org/10.1016/j.wear.2019.01.066 VL - 440-441 SP - 203104-1 EP - 203104-7 PB - Elsevier CY - Amsterdam AN - OPUS4-49815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection N2 - The differences between the binary phase diagrams W-C and Nb-C illuminate several parameters for tailoring the properties of NbC. In the region of homogeneity of NbCx, with Nb4C3 and Nb6C5 other Niobium carbide phases occur. Properties, like micro-hardness, hot hardness, sliding wear, elastic modules and toughness can be tailored by the C/Nb Ratio, secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types will be illuminated. Thus, the NbC system offers to producers a wider parameter window, than WC. T2 - 41st International Conference and Exposition on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 22.01.2017 KW - Cutting KW - Friction KW - Hard metal KW - Machining KW - Metal matrix composite KW - Niobium carbide KW - Wear PY - 2017 AN - OPUS4-39392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. T1 - Niobium carbide NbC as cutting tool material and for wear protection N2 - The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these develop¬ments without loosening the hardness level. Stoichiometric and sub-stoichiometric, submicron NbC powders were used. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions. The functional profile of NbC and WC grades bonded by cobalt and nickel are benchmarked by 4-point bending strength, elastic moduli and hot hardness until 1000°C, dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and cutting performances under emulsion and coolant-free turning and milling against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35). T2 - 42nd International Conference and Exposition on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 21.01.2018 KW - NbC KW - Cutting tools KW - Wear PY - 2018 AN - OPUS4-45854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Spaltmann, Dirk T1 - Generation of defined tribofilms and their stability under slip-rolling in a 2Disk test machine N2 - Tribofilms formed by additives in lubricants represent a key mechanism for preventing wear, but are difficult to investigate due to the complexity of the composition of lubricants, their tiny thickness and amorphous nature.The tribological profile of such tribofilms were investigated. T2 - Symposium on Tribometry and Tribochemistry CY - Boston, MA, USA DA - 28.06.2017 KW - Slip-rolling KW - 2Disk KW - Friction KW - Wear KW - Tribofilms KW - Additive PY - 2017 AN - OPUS4-40797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Status of nickel bonded niobium carbide (NbC) as a substitute for cobalt-bonded tungsten carbide (WC) as cutting tools and for wear protection N2 - Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded. The NiMo-bonded stoichiometric NbC1.0 grades enable the substitution of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness. T2 - POWDERMET 2017 CY - Las Vegas, USA DA - 13.06.2017 KW - Cutting tools KW - Wear KW - Niobium carbide (NbC) PY - 2017 AN - OPUS4-40653 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Machining with niobium carbide based tools T2 - Reibung, Schmierung, Verschleiß N2 - The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining. T2 - 59. Tribologie-Fachtagung CY - Goettingen, Germany DA - 24.09.2018 KW - Hard tungsten KW - Semi-finishing KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metal KW - Cobalt KW - Nickel KW - Fe3Al PY - 2018 SN - 978-3-9817451-3-9 SP - 48/1 EP - 48/11 AN - OPUS4-46170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Spaltmann, Dirk A1 - Woydt, Mathias T1 - An alternative approach to simulating an entire particle erosion experiment JF - Lubricants N2 - In the present work an approach is presented which combines various aspects of the former models with probability considerations. It is used to simulate the impact of more than one billion Alumina particles onto a steel substrate. This approach permits the simulation of an entire erosion experiment on an average PC within about six hours. KW - Particle erosion KW - Wear KW - DEM KW - FEM KW - Monte-Carlo simulation KW - Alumina PY - 2018 DO - https://doi.org/10.3390/lubricants6010029 VL - 6 IS - 29 SP - 1 EP - 11 PB - MDPI AN - OPUS4-44542 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spaltmann, Dirk A1 - Woydt, Mathias T1 - Alternative approach to simulate an entire particle erosion experiment T2 - WTC 2017 N2 - The cause and type of solid particle erosion varies across different industries and locations in plants, for instance the particles could be volcanic ash in aero-engines, fly ash in boilers, exfoliated scale in steam turbines or mineral matter in oil excavation. In all cases the durability of materials can be improved through better surface engineering and coatings, but the development of these is restricted also due to lack of generic models. In this respect, the simulation of a single impact with finite element methods using 100.000 knots would take about 15 minutes. In order to simulate an entire particle erosion experiment, up to one billion of such impacts would have to be considered. In order to simulate an entire particle erosion experiment, the current work presents an alternative approach capable of calculating about half a billion impacts on a substrate in less than six hours on a standard PC. The predictions of the simulation will be compared to a steel sample at 600°C eroded by aluminum oxide particles with a velocity around 210 m/s. T2 - The 6th World Tribology Congress CY - Beijing, China DA - 17.09.2017 KW - Particle erosion KW - Simulation KW - Wear PY - 2017 SP - 1 EP - 3 AN - OPUS4-42449 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -