TY - JOUR A1 - Chambers, M. S. A1 - Hunter, R. D. A1 - Hollamby, M. J. A1 - Pauw, Brian Richard A1 - Smith, A. J. A1 - Snow, T. A1 - Danks, A. E. A1 - Schnepp, Z. T1 - In Situ and Ex Situ X‑ray Diffraction and Small-Angle X‑ray Scattering Investigations of the Sol−Gel Synthesis of Fe3N and Fe3C N2 - Iron nitride (Fe3N) and iron carbide (Fe3C) nanoparticles can be prepared via sol−gel synthesis. While sol−gel methods are simple, it can be difficult to control the crystalline composition, i.e., to achieve a Rietveld-pure product. In a previous in situ synchrotron study of the sol−gel synthesis of Fe3N/Fe3C, we showed that the reaction proceeds as follows: Fe3O4 → FeOx → Fe3N → Fe3C. There was considerable overlap between the different phases, but we were unable to ascertain whether this was due to the experimental setup (side-on heating of a quartz capillary which could lead to thermal gradients) or whether individual particle reactions proceed at different rates. In this paper, we use in situ wide- and small-angle X-ray scattering (wide-angle X-ray scattering (WAXS) and small-angle X-ray scattering (SAXS)) to demonstrate that the overlapping phases are indeed due to variable reaction rates. While the initial oxide nanoparticles have a small range of diameters, the size range expands considerably and very rapidly during the oxide−nitride transition. This has implications for the isolation of Rietveld-pure Fe3N, and in an extensive laboratory study, we were indeed unable to isolate phasepure Fe3N. However, we made the surprising discovery that Rietveld-pure Fe3C nanoparticles can be produced at 500 °C with a sufficient furnace dwell time. This is considerably lower than the previous reports of the sol−gel synthesis of Fe3C nanoparticles. KW - Small-angle X-ray Scattering KW - SAXS KW - Diffraction KW - XRD KW - Scattering KW - Sol-gel KW - Iron nitride KW - Nanoparticles KW - Iron carbide KW - Catalyst KW - In-situ KW - Ex-situ KW - Synthesis KW - Synchrotron PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-548226 VL - 61 IS - 18 SP - 6742 EP - 6749 PB - ACS Publications CY - Washington AN - OPUS4-54822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Dixneit, Jonny A1 - Kannengießer, Thomas A1 - Vollert, F. A1 - Gibmeier, J. T1 - Phase Transformation and Strain Evolution during Welding of Low Transformation Temperature Alloys N2 - In this work, the phase and strain formation in multipass welding of LTT gas metal arc welds were observed under realistic restraints by means of time resolved angular-dispersive synchrotron X-ray diffraction at the High Energy Materials Science beamline HEMS at PETRA III (DESY), Hamburg Germany. It was shown that the strain evolution during cooling correlates with the amount of martensite formed. Both, the strain of martensite and austenite are affected during phase transformation. Even though dilution processes limit the LTT effect in the root compared to the top layer, the strains are significantly reduced compared to the conventional weld metal. The observed effects are found for both Ni and Mn based LTT filler metals regardless of their respective Ms temperature. T2 - 2nd International Conference on Advanced Joining Processes AJP 2021 CY - Sintra, Portugal DA - 21.10.2021 KW - Welding KW - Residual Stress KW - In-situ diffraction KW - Synchrotron PY - 2021 AN - OPUS4-53609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Schaupp, Thomas A1 - Müller, Bernd R. A1 - Griesche, Axel A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - 3D imaging of hydrogen assisted cracking using analyser-based imaging N2 - To better understand the mechanism of hydrogen assisted cracking (HAC), it is important to investigate the 3D structure of the cracks non-destructively. Since, cracks introduced by HAC are usually very small, conventional x-ray imaging methods often lack the required spatial resolution. However, the detection of those cracks can be enhanced by taking advantage of refraction at interfaces within the sample. To image this refractive deflection we employ analyser based imaging (ABI). In this work we aim at proving the enhanced crack detection of ABI by investigating an alluminum alloy weld. T2 - BESSY User Meeting 2015 CY - Berlin, Germany DA - 09.12.2015 KW - X-ray refraction KW - Synchrotron KW - Analyser-based imaging KW - Hydrogen assisted cracking KW - Welding PY - 2015 AN - OPUS4-38278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shashev, Yury A1 - Hentschel, M. P. A1 - Kupsch, Andreas A1 - Britzke, Ralf A1 - Lange, Alex A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Talbot- Lau interferometry with a non- binary phase grating for non-destructive testing N2 - Grating interferometric set-ups have been established in the last decade. They are promising candidates to obtain enhanced image contrast from weakly absorbing micro and nano structures. They are based on X-ray refraction and near-field diffraction using the Talbot effect. At the expense of taking multiple images, Talbot-Lau grating interferometry allows separating the absorption, refraction, and scattering contributions by analysing the disturbances of a phase grating interference pattern. Contrary to other refraction enhanced methods, this technique can be applied using conventional X-ray tubes (divergent, polychromatic source). This makes it attractive to solve typical non-destructive testing problems. We investigated the efficiency of phase gratings, i.e. the visibility (the amplitude of oscillations) upon variation of propagation distance and phase grating rotation around an axis parallel to the grid lines. This grating rotation changes the grating shape (i.e. the distributions of phase shifts). This can yield higher visibilities than derived from rectangular shapes. Our study includes experimental results obtained from synchrotron radiation, as well as simulations for monochromatic radiation. The advantages of Talbot-Lau interferometry are demonstrated at the example of glass capillaries. T2 - WCNDT 2016 CY - Munich, Germany DA - 13.06.2016 KW - Phase grating KW - X-ray phase contrast imaging KW - Talbot- Lau interferomerty KW - Visibility KW - Synchrotron PY - 2016 AN - OPUS4-36625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Müller, Bernd R. A1 - Kupsch, Andreas A1 - Nellesen, J. A1 - Tillmann, W. T1 - Characterizing damage evolution in metal matrix composites with X-ray refraction topography and in situ tensile loading N2 - In this study a metal-matrix-composite with aluminum matrix and Al2O3 particles was investigated with x-ray refraction topography and in-situ tensile loading. It could be observed that after reaching a certain load the specific surface increased steadily. However, the classical radiographs taken for comparison show no damage in the sample. T2 - 8th Joint BER II and BESSY II User Meeting CY - Berlin, Germany DA - 07.12.2016 KW - X-ray refraction KW - Metal matrix composites KW - In-situ loading KW - Synchrotron PY - 2016 AN - OPUS4-39113 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollwitzer, Christian A1 - Cabeza, Sandra A1 - Garces, G. T1 - Synchrotron based absorption edge tomography for §D characterization of the microstructure of MG-Y-Zn alloys N2 - Absorption edge tomography is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. The beamline BAMline at BESSY II, which is operated by the Federal Institute for Materials Research and Testing, can provide a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%. Together with the microtomography setup, this enables differential tomography sensitive to any element with N >= 24 (Cr) by using an appropriate K- or L-edge in this range. Here, absorption edge tomography at the Yttrium edge is employed to perform a non-destructive 3D characterization of the microstructure of a high strength Mg-Y-Zn alloy. The long period stacking ordered (LPSO) phase which forms fibres in this material was extracted based on the Yttrium content and the fibre length distribution was analysed. T2 - Ninth Joint BER II and BESSY II User Meeting CY - Berlin, Germany DA - 13.12.2017 KW - Synchrotron KW - Computed Tomography KW - Absorption edge KW - BAMline PY - 2017 AN - OPUS4-43854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheffler, F. A1 - Tielemann, Christopher A1 - Busch, R. A1 - Kober, M. A1 - Müller, Ralf A1 - Brauer, D. S. T1 - Crystallization of glasses studied with PEEM N2 - A heat treated glass that formed crystals under controlled conditions can be a glass ceramic. A proper understanding of crystallization in glassy melts is needed yet still lacking. Involved processes include the mobility of Elements within the glass during heat treatment and the reorganization of atomic bonds during crystallization. This change in coordination number of certain elements is easily observable in bulk glass samples during heat treatment with XAS. Our plan was to monitor these reorganization processes in situ at the immediate surface during heat treatment with PEEM to get time and spatial resolved data. T2 - Joint Meeting of the Polish Synchrotron Radiation Society and SOLARIS Users CY - Online meeting DA - 09.09.2020 KW - Glass KW - Surface KW - Peem KW - Synchrotron PY - 2020 AN - OPUS4-51336 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Kannengießer, Thomas T1 - Martensitumwandlung in situ analysiert mit Röntgenstrahlung N2 - Die dehnungsinduzierte Martensitbildung wurde mittels Röntgen-Diffraktion und -Radiographie mit dem EDDI-Instrument am BESSY II in supermartensitischem Stahl mit Anlassaustenit untersucht. Die Bildung wird durch Wasserstoff im Gefüge unterdrückt. Die Duktilität von wasserstofffreiem SMSS korreliert mit dem Anteil an dehnungs-induziertem Martensit T2 - Symposium on Materials and Joining Technology CY - Online meeting DA - 07.09.2020 KW - Wasserstoff KW - Materialschädigung KW - Materialschaedigung KW - Synchrotron PY - 2020 AN - OPUS4-51190 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz T1 - Scattering is a powerful tool to follow nucleation and growth of minerals from solutions N2 - In recent years, we have come to appreciate the astounding intricacy of the processes leading to the formation of minerals from ions in aqueous solutions. The original, and rather naive, ‘textbook’ image of these phenomena, stemming from the adaptation of classical nucleation and growth theories, has increased in complexity due to the discovery of a variety of precursor and intermediate species. These include solute clusters (e.g. prenucleation clusters, PNCs), liquid(-like) phases, as well as amorphous and nanocrystalline solids etc.. Does it, however, mean that all the minerals grow through intermediate phases, following a non-classical pathway? In general, the precursor or intermediate species constitute different, often short-lived, points along the pathway from dissolved ions to the final solids (typically crystals in this context). In this regard synchrotron-based scattering (SAXS/WAXS/total scattering) appears to be the perfect tool to follow in situ and in a time-resolved manner the crystallization pathway because of the temporal and spatial length scales that can be directly accessed with these techniques. In this presentation we show how we used scattering to probe the crystallisation mechanisms of calcium sulfate, This system contains minerals that are widespread in diverse natural environments, but they are also important in various industrial settings. Our data demonstrate that calcium sulfate precipitation involves formation and aggregation of sub-3 nm anisotropic primary species. The actual crystallisation and formation of imperfect single crystals of calcium sulfate phases, takes place from the inside of the in itial aggregates. Hence, calcium sulfate follows a non-classical pathway. T2 - X-ray Powder Diffraction at DESY - new opportunities for research and industry CY - Online meeting DA - 22.06.2020 KW - Nucleation KW - Calcium sulfate KW - Diffraction KW - Scattering KW - Synchrotron KW - SAXS/WAXS PY - 2020 AN - OPUS4-50943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander A1 - Léonard, Fabien A1 - Evsevleev, Sergei A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - To see and not to see - Möglichkeiten und Grenzen der Schadensanalyse mit CT an Kompositmaterialien N2 - Anhand von drei Beispielen (Datenfusion an CFK; Machine Learning an Metall-Matrix-Kompositen sowie Refraktion an CFK) wird gezeigt, wie die BAM mit neuen Analysemethoden mehr Informationen aus CT-Datensätzen extrahieren kann, sowie mit der Refraktion eine Analysemethode besitzt, die in Fällen eingesetzt werden kann, bei denen klassische Durchstrahlungsmethoden kein Ergebnis liefern. T2 - InnoTesting 2020 CY - Wildau, Germany DA - 27.02.2020 KW - Computed tomography KW - Computertomographie KW - Röntgenrefraktion KW - Machine Learning KW - Datenfusion KW - Data Fusion KW - Synchrotron PY - 2020 AN - OPUS4-50485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Online-Observation of Martensite Formation by combined use of Synchrotron Diffraction and Dilatometry N2 - Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material. T2 - Visual-JW 2019 & WSE 2019 The 5th International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation & The 8th International Conference of Welding Science and Engineering CY - Osaka, Japan DA - 21.11.2019 KW - Martensite KW - Synchrotron KW - Dilatometry KW - Residual stress KW - Phase transformation PY - 2019 SP - 83 EP - 84 PB - SEIEI Printing Co., Ltd CY - Osaka, Japan AN - OPUS4-49770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Online-Observation of Martensite Formation by combined use of Synchrotron Diffraction and Dilatometry N2 - Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material. T2 - Visual-JW 2019 & WSE 2019 The 5th International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation & The 8th International Conference of Welding Science and Engineering CY - Osaka, Japan DA - 21.11.2019 KW - Martensite KW - Synchrotron KW - Dilatometry KW - Residual stress KW - Phase transformation PY - 2019 AN - OPUS4-49768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Bernd R. A1 - Cooper, R.C. A1 - Lange, Axel A1 - Kupsch, Andreas A1 - Wheeler, M. A1 - Hentschel, Manfred P. A1 - Staude, Andreas A1 - Pandey, A. A1 - Shyam, A. A1 - Bruno, Giovanni T1 - Stress-induced microcrack density evolution in β-eucryptite ceramics: Experimental observations and possible route to strain hardening N2 - In order to investigate their microcracking behaviour, the microstructures of several β-eucryptite ceramics, obtained from glass precursor and cerammed to yield different grain sizes and microcrack densities, were characterized by laboratory and synchrotron x-ray refraction and tomography. Results were compared with those obtained from scanning electron microscopy (SEM). In SEM images, the characterized materials appeared fully dense but computed tomography showed the presence of pore clusters. Uniaxial tensile testing was performed on specimens while strain maps were recorded and analyzed by Digital Image Correlation (DIC). X-ray refraction techniques were applied on specimens before and after tensile testing to measure the amount of the internal specific surface (i.e., area per unit volume). X-ray refraction revealed that (a) the small grain size (SGS) material contained a large specific surface, originating from the grain boundaries and the interfaces of TiO2 precipitates; (b) the medium (MGS) and large grain size (LGS) materials possessed higher amounts of specific surface compared to SGS material due to microcracks, which decreased after tensile loading; (c) the precursor glass had negligible internal surface. The unexpected decrease in the internal surface of MGS and LGS after tensile testing is explained by the presence of compressive regions in the DIC strain maps and further by theoretical arguments. It is suggested that while some microcracks merge via propagation, more close mechanically, thereby explaining the observed X-ray refraction results. The mechanisms proposed would allow the development of a strain hardening route in ceramics. KW - Beta-eucryptite KW - Microcracked ceramics KW - X-ray refraction KW - Tensile load KW - Strain hardening KW - Synchrotron KW - BAMline KW - Computed Tomography KW - CT PY - 2018 UR - http://www.sciencedirect.com/science/article/pii/S1359645417308881 U6 - https://doi.org/10.1016/j.actamat.2017.10.030 SN - 1359-6454 SN - 1873-2453 VL - 144 IS - Supplement C SP - 627 EP - 641 PB - Elsevier B.V. AN - OPUS4-43024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Emmerling, Franziska T1 - New insights in mechanochemical processes using real-time in situ investigations N2 - Use of synchrotron radiation for special sample conditions. Recent work of the group at BESSY II. T2 - DESY Usermeeting Satelite Workshop CY - Hamburg, Germany DA - 22.01.2019 KW - XRD KW - In situ KW - Rietveld KW - Synchrotron PY - 2019 AN - OPUS4-47262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Oliveira Guilherme Buzanich, Ana T1 - Hard X-ray spectroscopy and imaging at the BAMline and MySpot beamlines at BESSY II (Berlin, Germany) N2 - Overview of the X-ray based analytical methods conducted at the BAMline and µSpot Beamline for structure analysis. T2 - Pccr2 + AfLS conference CY - Accra, Ghana DA - 29.01.2019 KW - X-ray spectroscopy KW - Synchrotron KW - Beamline KW - Material characterization PY - 2019 AN - OPUS4-47319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Griesche, Axel T1 - In-situ ED-XRD und Radiographie während eines Zugversuchs an wasserstoffbeladenem Supermartensit N2 - In diesem Vortrag werden Ergebnisse von in situ Experimenten am Berliner Elektronenspeicherring (BESSY II) vorgestellt. Es wurden Zugversuche an wasserstoffbeladenen und wasserstofffreien supermartensitischen Proben durchgeführt und gleichzeitig sowohl Diffraktionsspektren als auch röntgenradiographische Bilder aufgenommen. Die energiedispersive Röntgendiffraktion ermöglichte dabei in-situ die dehnungsinduzierte Phasenumwandlung von Restaustenit zu Martensit zu beobachten. Die Radiographiebilder der zerreisenden Probe gaben Einblicke in das Bruchverhalten in Abhängigkeit vom Wasserstoffgehalt des Supermartensits. T2 - WerkstoffWoche 2017 CY - Dresden, Germany DA - 27.09.2017 KW - Synchrotron KW - Wasserstoff KW - Phasenumwandlung PY - 2017 AN - OPUS4-42625 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollwitzer, Christian A1 - Ulbricht, Alexander A1 - Scholz, Philipp A1 - Joshi, Yogita A1 - Weidner, Steffen T1 - 3D printing material filled with metal organic frameworks analyzed by synchrotron based absorption edge tomography N2 - Absorption edge tomography, also known as differential tomography at absorption edges, is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. Synchrotron radiation is the best source for absorption edge tomography, because of its small bandwidth, high intensity and easily adjustable photon energy. The synchrotron beamline BAMline at the synchrotron radiation facility BESSY II in Berlin, which is operated by the Bundesanstalt für Materialforschung und -prüfung (BAM), provides a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%, when the double multilayer monochromator is used. Together with the microtomography setup, this enables differential tomography with submicron resolution at the K edge of the elements from chromium up to the lanthanides, and up to uranium, when the L edges are used as well. In this work, metal organic frameworks (MOFs) embedded in polymer are characterized using differential tomography. MOFs are microporous structures of metal ions, coordinated by organic linker molecules, that can be used in a broad field of applications, especially in gas storage and catalysis. In this work, polymer embedded MOFs were extruded into filaments, which could be used for 3d-printing to profit from the specific properties of the MOFs in polymeric materials combined with the arbitrary shapes provided by 3d-printing. For the extrusion, different polymer classes like ABS, polyester- and polyetherurethanes, as well as different MOFs (ZIF-8, ZIF-67, HKUST-1) were used to create MOF containing filaments with a nominal diameter of 3.0 mm. Differential tomography at the edges of the Zn, Co, and Cu was then used to find the distribution of the corresponding MOF in the filament and to analyze the shape of the inclusions. T2 - MSE 2018 CY - Darmstadt, Germany DA - 26.09.2018 KW - Absorption edge KW - Tomography KW - Metal organic framework KW - Synchrotron PY - 2018 AN - OPUS4-46429 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollwitzer, Christian A1 - Cabeza, S. A1 - Garces, G. T1 - Synchrotron based absorption edge tomography for 3D characterization of the microstructure of Mg-Y-Zn alloys N2 - Absorption edge tomography, also known as differential tomography at absorption edges, is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. Synchrotron radiation is the best source for absorption edge tomography, because of its small bandwidth, high intensity and easily adjustable photon energy. The synchrotron beamline BAMline at the synchrotron radiation facility BESSY II in Berlin, which is operated by the BundesanstaltfürMaterialforschung und -prüfung (BAM), provides a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%, when the double multilayer monochromator is used. Together with the microtomography setup, this enables differential tomography at the K edge of the elements from chromium up to the lanthanides, and up to uranium, when the L edges are used as well. In this work, the absorption edge tomography is employed to perform a non-destructive, three-dimensional characterization of the microstructure of metallic alloys. As an example, a high strength Mg-Y-Zn alloy containing long period stacking ordered (LPSO) phases is analysed. The alloy with a nominal composition of Mg97Y2Zn1 was synthesized by melting highly pure magnesium, zinc and a Mg-22%Y master alloy and casting an ingot, which was homogenised at 350 °C and then extruded using an extrusion ratio of 18:1. The results demonstrate that synchrotron based absorption edge tomography is a promising technique to perform a 3D characterization of the microstructure of metallic alloys. T2 - iCT 2018 CY - Wels, Austria DA - 13.02.2018 KW - Absorption edge KW - Synchrotron KW - Alloy KW - Tomography PY - 2018 AN - OPUS4-46427 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. T1 - Division 8.5 - Micro NDE - Key Competence Areas N2 - Der Vortrag gibt einen Überblick über die Kernkompetenzen des Fachbereichs 8.5 Mikro-ZfP (CT Apparaturen, Röntgen-Refraktion, WAXS - Texturanalyse, Datenkorrektur, Rekonstruktionsalgorithmen, Bildanalyse, dimensionelle Kontrolle, Multi-Source Datenfusion und Kombination, micromechanische Eigenschaften mittels Neutronen Diffraktion), im Hinblick auf die Charakterisierung von Leichtbauwerkstoffen (Faserverbunde, Aluminium und Titan MMCs), die in der Luftfahrt verwendet werden. Der Schwerpunkt liegt dabei auf der Charakterisierung mittels Synchrotron und Röntgen Refraktionstechniken sowie Computertomographie. N2 - The lecture gives an overview of the core competencies of the department 8.5 Micro NDT (CT equipment, X-Ray Refraction, WAXS - Texture analysis, Data correction, Reconstruction algorithms, Image analysis, Dimensional control, Multi-Source Data Fusion and Combination, Micromechanical Properties by Neutron Diffraction) with regard to the characterization of lightweight materials (fibre composites, aluminum and titanium MMCs) used in aviation. The focus is on characterization by synchrotron and X-ray refraction techniques as well as computed tomography. T2 - DGZfP Fachausschuss Luftfahrt CY - BAM - Berlin, Germany DA - 18.04.2019 KW - Synchrotron KW - Refraction KW - Microstructure Characterization PY - 2019 AN - OPUS4-47856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Matamoros-Veloza, A. A1 - Stawski, Tomasz A1 - Vargas, S. A1 - Neville, A. T1 - Study of a Local Structure at the Interface between Corrosion Films and Carbon Steel Surface in Undersaturated CO2 Environments N2 - Industries transporting CO2 gas-saturated fluids have infrastructures made of carbon steel. This is a good material with great mechanical properties but prone to corrosion and potential failure. Corrosion in sweet environments involves the formation of FeCO3 as a corrosion film, which is recognized to play a protective role under certain conditions. This work on the dissolution of corrosion films in sweet environments, under acidic and undersaturated conditions, demonstrates that the effects on the integrity of steel are far more significant than the damage observed on the surface of the corrosion film. Our results prove that dissolution of FeCO3 involved the presence of an amorphous phase, the intermediate formation of FeCl2 or FeCl+, and the presence of a phase with short distance atom–atom correlations. The amorphous phase was identified as a mixture of retained γ-Fe and Fe3C. Partially broken α-Fe and Fe3C structures were identified to prove the damage on the material, confirming the interface zone without evident damage on the corrosion film. Dissolution affected both the α-Fe and FeCO3, with the lattice [102̅] from the FeCO3 crystalline structure being the fastest to dissolve. The damage of steel at the molecular scale was evident at the macroscale with pit depths of up to 250 μm. The impact on the integrity of steel can be, therefore, more drastic than frequently reported in industrial operations of CO2 transport industries that use cleaning procedures (e.g., acid treatment, pigging) as part of their operational activities. KW - Steel KW - Corrosion KW - Siderite KW - Diffraction KW - Pair distribution function KW - Synchrotron PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-572156 SN - 2470-1343 VL - 8 IS - 9 SP - 8497 EP - 8504 PB - ACS AN - OPUS4-57215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -