TY - CONF A1 - Krütt, Enno A1 - Pirskawetz, Stephan A1 - Wallau, Wilma A1 - Meng, Birgit T1 - Development of an automated 60 °C Concrete Prism Test N2 - ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development. With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT. T2 - 16th International Conference on Alkali-Aggregate Reaction in Concrete CY - Lisboa, Portugal DA - 31.05.2022 KW - 60 °C-CPT KW - ASR expansion monitoring KW - Automated testing PY - 2021 SN - 978-972-49-2315-4 VL - 1 SP - 789 EP - 799 AN - OPUS4-54553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Weise, Frank A1 - Rieffel, Y. A1 - Gorbushina, Anna T1 - Die Schlossbrücke Berlin - Schutz der Göttinnen N2 - Vielleicht nannten es die Berliner „Puppen putzen“, wenn in den 1880er Jahren die Marmorstatuen auf der Schlossbrücke vor dem Berliner Stadtschloss mit Bürste, Wasser und Seife von Staub, Ruß und Taubendreck befreit wurden. Soviel Pflege wurde diesen Göttinnen aus der griechischen Mythologie nicht immer zuteil. So haben Klima, Luftverschmutzung und der 2. Weltkrieg, wie bei anderen Kunstwerken auch, tiefe Spuren hinterlassen. Der Erhalt dieser zwischen 1847 und 1857 aufgestellten Skulpturen und vieler vergleichbarer Objekte im Stadtbild ist durch die auch heute weiter fortschreitende Schädigung des Marmors gefährdet. In den Jahren 2006 bis 2010 förderte die Deutsche Bundesstiftung Umwelt (DBU) ein Projekt zur „Entwicklung und Überprüfung von Einhausungssystemen zur Reduzierung umweltbedingter Schädigungen von außenexponierten Marmorobjekten mit dem Ziel des langfristigen Erhalts in situ an einem national bedeutenden Objektkomplex, den Schlossbrückenfiguren unter den Linden, Berlin“. Geleitet und restauratorisch betreut wurde das Projekt durch das Landesdenkmalamt (LDA) Berlin. Durch die Abteilung Strukturgeologie und Geodynamik (GZG) der Georg-August Universität Göttinnen wurden die Verwitterungsmechanismen des Marmors untersucht und auf dieser Basis Anforderungen an das Schutzsystem formuliert. Anhand von numerischen Simulationen des Instituts für Bauklimatik der Technischen Universität Dresden (TUD) wurde das bauphysikalische Konzept des Einhausungssystems optimiert. Die konstruktive Gestaltung eines Prototyps und des finalen Entwurfs erfolgte durch das Fachgebiet Konstruktives Entwerfen und Tragwerkslehre der Universität der Künste Berlin. Durch den Fachbereich Baustoffe der BAM erfolgten die Realisierung des Prototyps der Einhausung sowie ein umfangreiches Klimamonitoring an den Skulpturen. Anhand dieses interdisziplinären Projektes und ergänzt durch weitere Messungen wird gezeigt, mit welchen Methoden die für die Degradation von Marmor relevanten Mechanismen untersucht werden können. Die Erkenntnisse aus dem Projekt sind die Grundlage für die Entwicklung nachhaltiger Pflege- und Schutzkonzepte für die kulturhistorisch wertvollen Skulpturen. Nur mit solchen modernen konservatorischen Programmen können die Originalskulpturen im Berliner Stadtraum erlebbar bleiben. T2 - Workshop Kulturerhaltung - Vom Dampfkessel zu Nanomaterialien CY - Berlin, Germany DA - 17.11.2021 KW - Baustoffe KW - Marmor KW - Verwitterung KW - Kulturelles Erbe KW - Wintereinhausungen KW - Klima KW - Zerstörungsfreie Prüfung KW - Building materials KW - Marble KW - Degradation KW - Cultural heritage KW - Winter shelters KW - Climate KW - Nondestructive testing PY - 2021 SN - 2567-1251 VL - 3 SP - 87 EP - 96 PB - Druckerei G. Bohm CY - Berlin AN - OPUS4-54637 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Meng, Birgit A1 - Pirskawetz, Stephan A1 - Voland, K. T1 - Influence of simultaneous cyclic loading and external alkali supply on the alkali-silica reaction in concrete pavements N2 - In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced life expectancy of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology, the main research focus up to now has been the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali penetration on road surfaces. The effects of mechanical pre-damage resulting from cyclic traffic loading and climatic impact had previously not been taken into consideration. Since 2011, the five-partner research group 1498 sponsored by the German Research Foundation (DFG) has been pursuing research on how simultaneous cyclic loading and external alkali penetration impacts destructive ASR in road surface concretes. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and their multi-scale modelling. This paper aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a sodium chloride (NaCl) solution, with simultaneous tracking of crack development. Subsequently, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks using micro X-ray 3D-computed tomography (3D-CT). Additionally, the effects of fatigue-induced cracks on alkali transport were investigated using Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced predamage on the ASR. T2 - 15th International Conference on Alkali-Aggregate reaction (ICAAR 2016) CY - Sao Paulo, Brazil DA - 03.07.2016 KW - concrete pavements KW - alkali-silica-reaction KW - fatigue KW - damage monitoring PY - 2016 SP - Paper 191 AN - OPUS4-37142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Meng, Birgit A1 - Rogge, Andreas T1 - Characterizing the Fatigue Behavior of High-Performance Concrete for Wind Energy Structures N2 - Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally. Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring. T2 - LORCENIS - Long Lasting Reinforced Concrete fpr Energy Infrastructure under Severe Operating Conditions CY - Ghent, Belgium DA - 10.09.2019 KW - Compressive Cyclic loading KW - Fatigue KW - High-strength concrete KW - Non destructive testing KW - Ultrasonic testing PY - 2019 SN - 978-9-463-88638-3 SP - 1 EP - 4 AN - OPUS4-49500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wallau, Wilma A1 - Pirskawetz, Stephan A1 - Voland, K. A1 - Weise, Frank A1 - Meng, Birgit ED - De Schutter, G. ED - De Belie, N. ED - Janssens, A. ED - Van Den Bossche, N. T1 - Online monitoring of the expansion of alkali-silica reaction affected concrete prisms implemented to the accelerated concrete prism test at 60 °C N2 - The accelerated concrete prism test (ACPT-60 °C) facilitates testing of alkali-silica reactivity of aggregates within five months. Manual measurement is usually conducted to determine expansion of test specimen every 28 days. This conventional procedure gives only limited insight to expansion behaviour of ASR-affected prisms. Due to the large time intervals, expansion exceeding the critical value of 0.3 mm/m is likely to be noticed late. Continuous recording resolves this problem and delivers beneficial information on the shape of the expansion curve. Displacement transducers integrated into a special testing equipment developed at BAM put continuous measurement into practice. Additionally, ultrasonic velocity and acoustic emissions are measured in-situ and provide deeper insights into hydration and crack formation processes during the test. Aiming for an automated testing method close to the German guideline, the following technical and methodical challenges arise. Changing of the vertical orientation of the prisms with every manual measurement as standardised cannot be implemented. Furthermore, preliminary results already proved true that cooling and heating cycles, as necessarily associated with each manual measurement, can evoke additional expansion. Therefore, interrupted and continuously measured expansions reveal systematic differences, indicating the necessity to adjust the threshold expansion value for automated testing. Results presented in the paper: Different types of reactive aggregate have been tested applying continuous and manual expansion measurement to the concrete specimens. Development of continuously measured ultrasonic velocity and acoustic emissions of the aggregates tested diverge significantly while the expansion curves vary in shape and maximum strain. Prisms produced from a slowly reacting aggregate do not exhibit noticeable crack formation. It shows that comprehensive measuring helps describing and distinguishing ASR-damage mechanisms. Models of ASR-induced expansion, available in the open literature, so far are validated with discontinuous data hardly tracing the modelled curve. Continuous measurement improves validation and further model development. T2 - XIV DBMC - 14th International Conference on Durability of Building Materials and Components CY - Gent, Belgium DA - 29.05.2017 KW - Alkali-silica reaction KW - Accelerated concrete prism test KW - Continuous monitoring KW - Expansion modelling PY - 2017 SN - 978-2-35158-159-9 VL - PRO 107 SP - 1 EP - 11 PB - RILEM Publications S.A.R.L. AN - OPUS4-40499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Pirskawetz, Stephan A1 - Thiele, Marc A1 - Rogge, Andreas T1 - Experimental investigation of size effect on fatigue behavior of high strength concrete - concept and preliminary results N2 - The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring. T2 - 5th International fib Congress: Better - Smarter - Stronger CY - Melbourne, Australia DA - 08.10.2018 KW - Acoustic emission testing KW - Compressive cyclic loading KW - Fatigue KW - High-strength concrete KW - Non-destructive testing KW - Size effect KW - Slenderness effect KW - Ultrasonic testing PY - 2018 SN - 978-1-877040-14-6 SP - 1 EP - 11 AN - OPUS4-46408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Birgit A1 - Dehn, F. A1 - Unger, Jörg F. A1 - Shepherd, D. A. A1 - Tamsen, Erik A1 - Pirskawetz, Stephan T1 - Wissensbasierte Digitalisierung von betontechnologischen Materialdaten N2 - Die sprunghaft zunehmende Wichtigkeit von FAIR- und Open-Data für die Qualitätssicherung, aber auch für die Nachnutzbarkeit von Daten und den Erkenntnisfortschritt führt zu enormem Flandlungsbedarf in Forschung und Entwicklung. Damit verbunden laufen derzeit vielfältige, ambitionierte Aktionen, z. B. bezüglich der Erstellung von Ontologien und Wissensgraphen. Das Knowhow entwickelt sich rasant, die Ansätze zur Implementation entstehen in verschiedenen Fachwelten bzw. mit unterschiedlichen Zielsetzungen parallel, so dass recht heterogene Herangehensweisen resultieren. Diese Veröffentlichung fokussiert auf Arbeiten, die derzeit als möglichst ganzheitlicher Ansatz für Materialdaten im Rahmen der Digitalisierungsinitiative „Plattform MaterialDigital" vorangetrieben werden. Die Autoren bearbeiten baustoffbezogene Aspekte im Verbundprojekt „LeBeDigital - Lebenszyklus von Beton". Zielsetzung ist die digitale Beschreibung des Materialverhaltens von Beton über den kompletten Herstellungsprozess eines Fertigteils mit einer Integration von Daten und Modellen innerhalb eines Workflows zur probabilistischen Material- und Prozessoptimierung. Es wird über die Vorgehensweise und die dabei gewonnenen Erfahrungen berichtet, nicht ohne den Blick auf die oft unterschätzte Komplexität der Thematik zu lenken. T2 - Internationale Baustofftagung (ibausil) CY - Weimar, Germany DA - 13.09.2023 KW - Beton KW - Digitalisierung KW - Materialdaten KW - Datenmanagement KW - FAIR-Prinzip KW - Metadaten KW - Ontologie KW - Wissengraph PY - 2023 UR - https://www.uni-weimar.de/de/bauingenieurwesen/institute/fib/ibausil/ VL - 2023 SP - 1 EP - 11 PB - Sonderausgabe des Online-Journals ce/papers von Wiley AN - OPUS4-58315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Steve A1 - Schmidt, Wolfram A1 - Pirskawetz, Stephan A1 - Rogge, Andreas ED - Khayat, Kamal Henry T1 - Fire spalling of self-compacting concrete mixtures with different limestone powder contents N2 - Self-compacting concrete typically contains a higher content of powder materials than normal concrete. Furthermore it is assumed that the use of superplasticizers yields a more homogenous microstructure in the hardened paste. Both aspects generate a very dense microstructure, which can be assumed to cause material behaviour that differs from than normal concrete when it is exposed to elevated temperatures. However, the paste volumes in SCC can vary significantly based on the mixture composition. At a low paste volumes SCC can be very similar to normal concrete at hardened state while it can vary greatly at higher paste volumes. Since the high temperature behaviour of concrete is strongly affected by the different physical behaviour of the paste and the aggregates, it is likely that the high temperature behaviour is consequently strongly affected by the ratio of these mixture components. In the present study different SCC mixtures were observed with similar mechanical properties, but with significantly differing paste to aggregate ratios. Based on observations of the heat evolution at the fire exposed surface and at different depths inside the specimens as well as based on photogrammetric observations of the spalled dimensions, the results indicate that with increasing paste volumes the heat conductivity is reduced and as a result concrete with higher paste to aggregate ratios shows less spalling. T2 - 8th RILEM Symposium on Self-Compacting Concrete CY - Washington, USA DA - 15.05.2016 KW - Spalling KW - High temperature behaviour KW - Fire exposure KW - Mixture composition KW - Photogrammetry PY - 2016 SN - 978-2-35158-157-5 SP - 353 EP - 363 PB - RILEM Publications S.A.R.L. CY - Paris, France AN - OPUS4-36873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -