TY - CONF A1 - Kauss, N. A1 - Heyn, A. A1 - Rosemann, Paul T1 - How to Detect Sensitivity on Aged Lean-Duplex Stainless Steel With Electrochemical Methods N2 - The influence of isothermal ageing on microstructure, sensitisation and pitting corrosion resistance of the lean duplex stainless steel (LDSS) X2CrNiN23-4 was investigated with various electrochemical methods. The aging at 600 °C (from 0.1 h up to 20 h) lead to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries, inducing sensitisation due to chromium depletion. The degree of sensitisation was evaluated with the double loop electrochemical potentiokinetic reactivation method (DL-EPR) according to ASTM G108 and correlated with critical pitting potentials (Epit) as well as critical pitting temperature (CPT) measured in an electrolyte according to ASTM G48 using electrochemical noise. Up to an ageing time of 1 h, the sensitisation did rise significantly, stabilising at a nearly constant level with a slight drop at 20 h. This behaviour correlated perfectly with the potentiodynamically determined pitting potentials Epit and sensitisation. The CPT showed a higher sensitivity at short ageing times compared to the DL-EPR and Epit. Finally, the KorroPad method was applied to visualise the sensitisation induced reduction of pitting corrosion resistance. The “KorroPad” is an agar-based gel-electrolyte containing 0.1 mol/l sodium chloride (NaCl) and 0.1 mol/l potassium ferricyanide III (K3[Fe(CN)6]), invented at the Federal Institute of Materials Research and Testing in Berlin (Germany) to detect surfaces of stainless steel prone to pitting corrosion. The standard configuration of the KorroPad showed no differentiation for the various aging conditions. Increasing the concentration of both NaCl and potassium ferrocyanide III to 0.5 M shifts the detection limit of the KorroPad method to stainless steels with higher corrosion resistance, producing the same trends detected by standard electrochemical pitting corrosion values (Epit, CPT) and sensitisation (DL-EPR). By that, the KorroPad method was successfully adjusted to the lean-duplex stainless steel X2CrNiN23-4, enabling short-time testing to detect sensitization. T2 - Electrochemical Methods in Corrosion Research 2018 CY - Cambridge, UK DA - 22.07.2018 KW - Corrosion testing KW - Duplex stainless steels KW - Corrosion KW - KorroPad KW - Pitting corrosion KW - EPR KW - Electrochemical noise KW - Stainless steel PY - 2018 AN - OPUS4-45615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. T1 - Wärmebehandlung und Korrosionsbeständigkeit druckaufgestickter nichtrostender Stähle N2 - Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Insbesondere der Einfluss von Warmauslagerungsversuchen nach dem Abschrecken wird dabei charakterisiert. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden (EPR, KorroPad, Lochkorrosionspotentiale) ermittelt und interpretiert. T2 - Werkstoffwoche 2017 CY - Dresden, Germany DA - 27.09.2017 KW - Wärmebehandlung KW - Korrosion KW - Nichtrostender Stahl KW - EPR KW - KorroPad KW - Sensibilisierung KW - Stickstoff KW - ThermoCalc PY - 2017 AN - OPUS4-42831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, C. A1 - Rosemann, Paul T1 - Wärmebehandlung und Korrosionsbeständigkeit druckaufgestickter nichtrostender Stähle N2 - Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden ermittelt und interpretiert. T2 - GfKORR-Jahrestagung 2017 CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Wärmebehandlung KW - Korrosion KW - Nichtrostender Stahl KW - EPR KW - KorroPad KW - Sensibilisierung KW - Stickstoff KW - ThermoCalc PY - 2017 AN - OPUS4-42833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kauss, N. A1 - Rosemann, Paul T1 - Sensibilisierungsverhalten vom nichtrostenden Lean-Duplexstahl 1.4062 N2 - Der nichtrostende Lean-Duplexstahl 1.4062 (X2CrNiN22-2) verbindet die hohe Festigkeit des Ferrits mit der Duktilität und Zähigkeit des Austenits in einem zweiphasigen Gefüge mit sehr hoher Korrosionsbeständigkeit. Die höchste Korrosionsbeständigkeit wird erreicht, wenn das ferritisch-austenitische Gefüge frei von weiteren Sekundärphasen ist. Dies wird durch ein gezieltes Lösungsglühen bei 1050 °C mit anschließender Abschreckung in Wasser erreicht. Durch thermische Beeinflussung (z.B. beim Schweißen) können Sekundärphasen ausgeschieden und die Korrosionsbeständigkeit des Werkstoffs gesenkt werden. Dies wurde durch eine isotherme Warmauslagerung bei 500 °C bis 900 °C für 0,1 h bis zu 72 h simuliert. Die Veränderung der Korrosionsbeständigkeit wurde mit dem DL-EPR-Verfahren und durch die angepasste KorroPad-Prüfung ermittelt. Die ermittelten Anfälligkeitsbereiche wurden miteinander Verglichen und in zwei Sensibilisierungsschaubildern zusammengefasst. T2 - GfKORR-Jahrestagung CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Duplexstahl KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - EPR KW - KorroPad KW - Sensibilisierung PY - 2017 AN - OPUS4-42834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. A1 - Müller, C. A1 - Halle, T. T1 - Heat treatment and corrosion resistance of cutlery N2 - Hardness and pitting corrosion resistance are the major quality criteria of cutlery. Both are achieved by the heat treatment (austenitization, quenching and tempering) of the normally used martensitic stainless steels. The established quality control method regarding the pitting corrosion resistance is an alternating immersion test in 1 % NaCl solution at 60 °C according to DIN EN ISO 8442. This standard test shows a high deviation, which limits any optimization of the heat treatment process. New approaches for corrosion testing of martensitic stainless-steels were developed and used in the last years to connect the weak pitting corrosion resistance of martensitic stainless-steels with the phenomenon of chromium depletion. The tempering temperatures used in the industrial heat treatment of cutlery are too low to explain the appearance of chromium depletion. For this reason, a systematic investigation of three heat treatment parameters (austenitization time, cooling speed and tempering temperature) were performed on the martensitic stainless-steels X50CrMoV15 (1.4116) to detect their contribution to chromium depletion. The electrochemical potentiodynamic reactivation (EPR), which is very sensitive to any change of the microstructure, was used to quantify the degree of chromium depletion. The KorroPad indicator-test was applied to correlate low pitting corrosion resistance to the presence of chromium depletion. The results of all investigations allow conclusions about the very small process window, which is necessary to achieve cutlery with high pitting corrosion resistance. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Heat treatment KW - EPR KW - Pitting corrosion KW - Martensitic stainless steels KW - REM PY - 2018 AN - OPUS4-45952 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. T1 - Visualization of material-related susceptibility to pitting corrosion with the “KorroPad” indicator test N2 - The KorroPad indicator test was invented at the Federal Institute for Materials Research and Testing to detect stainless-steel surfaces susceptible to pitting corrosion. The KorroPad indicator test is thus an interesting alternative for manufacturers, processors, users and researchers to time consuming exposition experiments and complex electrochemical investigations, which are normally used to reveal surface-related processing errors resulting in reduced pitting corrosion resistance. Furthermore, the KorroPad indicator test can be used to visualize alloy- and microstructure-related factors causing susceptibility to pitting corrosion. The detection limit of the KorroPad indicator test was characterized in this work using reference alloys with different chromium content (5 % to 18 %). The alloy-specific detection limit was shifted successfully to higher chromium content by increasing the concentrations of NaCl and K3[Fe(CN)6]. The modified KorroPads can now be used to establish an alloy-specific quality control regarding the pitting corrosion resistance of different stainless steel grades. T2 - EUROCORR CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Corrosion testing KW - Pitting corrosion PY - 2018 AN - OPUS4-45953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Roßberg, S. A1 - Pensel, P. A1 - Halle, T. A1 - Burkert, A. T1 - Precipitation behavior and corrosion resistance of nickel-free, high-nitrogen austenitic stainless steels N2 - Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - KorroPad KW - Stainless steel KW - Corrosion resistance KW - Heat treatment KW - ThermoCalc KW - Pitting corrosion KW - Nitrogen PY - 2018 AN - OPUS4-45954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Baumann, O. A1 - Müller, C. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials). T2 - Materials Science and Engineering 2018 (MSE) CY - Darmstadt, Germany DA - 26.09.2018 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - KorroPad PY - 2018 AN - OPUS4-46090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -