TY - CONF A1 - Engelking, Lorenz A1 - Scharf-Wildenhain, R. A1 - Schröpfer, Dirk A1 - Hälsig, A. A1 - Kannengießer, Thomas A1 - Hensel, J. T1 - Influence of heat input on properties and residual stresses in hybrid addi-tive manufacturing of high strength steels using MSG processes N2 - The application of steels with a higher yield strength allows reductions in wall thickness, component weight and production costs. Hybrid additive manufacturing based on Gas Metal Arc Welding (GMAW) processes (DED-Arc) can be used to realise highly effi-cient component modifications and repairs on semi-finished products and additively manufactured structures. There are still a number of key issues preventing widespread implementation, particularly for SMEs. In addition to the manufacturing design, detailed information about assembly strategy and geometric adaptation of the component for modifications or repairs are missing. These include the welding-related stresses associ-ated with the microstructural influences caused by the additive manufacturing steps, particularly in the transition area of the substrate and filler material interface. The pre-sent research focuses the effect of welding heat control during DED-Arc process on the residual stresses, especially in the transition area. Defined specimens were welded fully automatically with a high-strength solid wire (yield strength > 790 MPa) especially adapted for DED-Arc on S690QL substrate. The working temperature and heat input were systematically varied for a statistical effect analysis on the residual stress state of the hybrid manufactured components. Regarding heat control, t8/5 cooling times within the recommended processing range (approx. 5 s to 20 s) were complied. The investiga-tion revealed a significant influence of the working temperature Ti on the compressive residual stresses in the transition area and the tensile residual stresses at the base of the substrate. High working temperatures result in lower compressive residual stresses, heat input E does not significantly affect the tensile stresses. T2 - 6. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 20.02.2025 KW - DED-Arc KW - Residual stress KW - Heat control PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632188 DO - https://doi.org/10.21268/20250506-3 SP - 110 EP - 122 AN - OPUS4-63218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Hannemann, Andreas A1 - Kannengießer, Thomas ED - Seefeldt, Marc T1 - In-situ determination of critical welding stresses during assembly of thick-walled components made of high-strength steel N2 - The performance and safety of welded high-strength low-alloyed steel (HSLA) components are substantially affected by the stresses occurring during and after welding fabrication, especially if welding shrinkage and distortion are severely restrained. The surrounding structure of the whole component affects loads in the far-field superimposing with welding stresses in the near-field of the weld. In this study a unique testing facility was used to restrain shrinkage and bending while analyse multiaxial far-field loads (max. 2 MN) during assembly of thick-walled component. A novel approach for the assessment of the in-situ-measured far-field data in combination with the actual weld geometry was elaborated. For the first time, analyses of the global bending moments of restrained welds based on the neutral axis of the actual weld load bearing section were achieved. Hence, far-field measurements offered the possibility to determine critical near-field stresses of the weld crosssections for the entire joining process. This work presents the approach for far-to-near field in-situ determination of stresses in detail for the 2-MN-testing system based on an extensive experimental work on HSLA steel welds, which demonstrates sources and consequences of these high local welding stresses. Thus, it was clarified, why the first weld beads are crucial regarding welding stresses and cold cracking, which is well known, but has never been measured so far. Accompanying analyses using X-ray diffraction (XRD) after welding show effects on local residual stress distributions. These analyses indicated viable prospects for stress reduction during assembly of thick-walled HSLA steel components. T2 - European Conference on Residual Stresses 2018 - ECRS-10 CY - Leuven, Belgium DA - 11.09.2018 KW - Residual stress KW - Welding KW - Large-scale test KW - X-ray diffraction KW - HSLA steel PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-466053 SN - 978-1-9452-9188-3 SN - 978-1-9452-9189-0 DO - https://doi.org/10.21741/9781945291890-30 SN - 2474-395X SN - 2474-3941 VL - 6 SP - 191 EP - 196 PB - Materials Research Forum LLC CY - Millersville, PA, USA AN - OPUS4-46605 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Lausch, Thomas A1 - Schröpfer, Dirk A1 - Hannemann, Andreas T1 - In-situ Observation of Stress Evolution and Cracking during High Strength Steel Welding N2 - Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system with a load capacity of 2 MN specifically developed for online monitoring of stress formation and cracking are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be quantified in-situ during welding and post weld heat treatment. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. Elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of mechanical stresses resulting from welding on stress relief cracking is demonstrated by the example of a creep resistant steel. Reheat cracks were monitored online during post weld heat treatment. T2 - Visual-JW 2019 & WSE 2019 The 5th International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation & The 8th International Conference of Welding Science and Engineering CY - Osaka, Japan DA - 21.11.2019 KW - Residual stress KW - Restraint KW - Welding KW - Large-scale test KW - Reheat cracking PY - 2019 SP - 83 EP - 84 PB - SEIEI Printing Co., Ltd CY - Osaka, Japan AN - OPUS4-49773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -