TY - JOUR A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias T1 - Application of thermographic testing for the characterization of impact damage during and after impact load JF - Composites Part B N2 - Low-velocity impact damages were monitored in-situ using an infrared camera before, during and after Impact load. Thermal images were recorded as a function of time at the front side (impact) as well as at the rear side of the plates using a high frame rate. In CFRP and GFRP specimens with different thicknesses and made of various types of fibers and matrix materials, different kind of damages were observed. The sizes of the heated areas being related to the damages and the amount of energy dissipated into heat was determined quantitatively as a function of impact energy and are a measure of the resistance of the different materials against impact load. KW - Laminates KW - Impact behaviour KW - NDT KW - Thermal analysis PY - 2019 DO - https://doi.org/10.1016/j.compositesb.2019.106899 SN - 1359-8368 SN - 1879-1069 VL - 173 SP - 106899, 1 EP - 17 PB - Elsevier AN - OPUS4-48881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Küttenbaum, Stefan A1 - Taffe, A. A1 - Braml, T. A1 - Maack, Stefan T1 - Non-Destructive Testing: A valuable source of information for reliability assessments N2 - The reassessment of bridges is becoming increasingly important. The basic requirement for analyses of structural safety is reliable knowledge about individual structures. This paper introduces the new approach to evaluate the quality of measured data gained from non-destructive testing (NDT) to provide reliable, objective, and relevant information about existing bridges. The purpose is to relate this validated knowledge to probabilistic analyses. Bridging the gap between NDT and numerical reassessments indicates reduced numerical uncertainties and residual service time extensions. This paper deals with an application of this approach using measurement data collected by ultrasonic technique at a prestressed concrete bridge. T2 - IABSE Symposium 2019 CY - Guimarães, Portugal DA - 27.03.2019 KW - NDT KW - Measurement KW - Structural safety KW - Concrete bridges KW - Eexisting structures PY - 2019 AN - OPUS4-47714 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Lohde, Sebastian A1 - Aydoğdu, M. T1 - Non-Destructive Testing of Composite Pressure Vessels using Conventional and High-Frequency Eddy Current Technique N2 - Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch. In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt. In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss. N2 - Composite pressure vessels for transporting dangerous goods and for hydrogen and natural gas vehicles consist of a load-bearing composite and a gas-tight, metallic or polymeric barrier layer (liner). To investigate the aging behavior of such composite pressure vessels, BAM carried out the interdisciplinary project COD-AGE. The aim of the project was the development of methods and models for the description and determination of the aging behavior of carbon fiber composites using the example of pressure vessels in order to better predict aging and safe working life. One focus of this project was the provision of suitable NDT methods. These included both test-related tests and the possible development of test equipment for later practical use. In the lecture, test results of the age-related eddy current test on composite pressure vessels are presented. In aging tests, pressure vessels made of an approximately 4 mm thick aluminum liner and approx. 8 mm thick CFRP layer were examined. Typical application of such pressure vessels are respiratory protective devices of the fire department. The pressure vessels were tested using conventional eddy current technology from the outer and inner side as well as with high-frequency eddy current technology. Both damage to the metallic liner and structures of the CFRP could be detected. A particular mechanical challenge was the inspection of the inside of the liners, since a cylindrical surface with an inside diameter of 150 mm has to be tested with an access of only 15 mm diameter. T2 - TAHYA-Workshop CY - Berlin, Germany DA - 27.11.2019 KW - NDT KW - Composite pressure vessel KW - CFRP KW - Eddy current testing PY - 2019 AN - OPUS4-49829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nazarzadehmoafi, Maryam A1 - Zscherpel, Uwe A1 - Altenburg, Simon A1 - Mohr, Gunther A1 - Maierhofer, Christiane A1 - Waske, Anja T1 - Detection of imprinted artificial defects in additively-manufactured samples by means of radiological inspections N2 - As a part of ProMoAM project, we are optimizing a prototype X-ray backscatter to reach NDT requirements, and thereafter to apply it for process monitoring. Moreover, we studied the capability of a radiography approach to detect artificial defects in AM components made by laser powder bed fusion (L-PBF). T2 - Workshop on Additive Manufacturing: Process, materials, simulation & implants CY - Berlin, Germany DA - 13.05.2019 KW - Additive manufacturing KW - NDT KW - Radiological inspections PY - 2019 AN - OPUS4-48515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Mohr, Gunther A1 - Baesso, Ilaria A1 - Straße, Anne A1 - Pittner, Andreas A1 - Pignatelli, Giuseppe A1 - Seeger, Stefan A1 - Nazarzadehmoafi, Maryam A1 - Ehlers, Henrik A1 - Gohlke, Dirk A1 - Homann, Tobias A1 - Scheuschner, Nils A1 - Ulbricht, Alexander A1 - Heinrich, P. A1 - Maierhofer, Christiane T1 - Process monitoring of additive manufacturing of metals - an overview of the project ProMoAM N2 - The project ProMoAM is presented. The goal of the project is to evaluate which NDT techniques or combination of techniques is suited for in-situ quality assurance in additive manufacturing of metals. To this end, also 3d-data fusion and visualization techniques are applied. Additional ex-situ NDT-techniques are used as references for defect detection and quantification. Feasability studies for NDT-techniques that are presently not applicable for in-situ use are performed as well. The presentation gives a brief overview of the whole project and the different involved NDT-techniques. T2 - Workshop od Additive Manufacturing: Process, materials, simulation & implants CY - Berlin, Germany DA - 13.05.2019 KW - Additive manufacturing KW - Process monitoring KW - NDT PY - 2019 AN - OPUS4-48087 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -