TY - JOUR A1 - Breese, Philipp Peter A1 - Altenburg, Simon T1 - Absolute temperature determination in laser powder bed fusion (PBF-LB/M) via hyperspectral thermography N2 - Temperature is a key characteristic in laser powder bed fusion of metals (PBF-LB/M). As a quantitative physical property, the temperature can determine the actual process quality independently from the nominal process parameters. Thus, establishing a process evaluation on temperatures rather than the comparison of process conditions is expected to be more effective. However, quantitative in situ temperature measurements with classical thermographic methods are virtually impossible. The reason is that the required emissivity value changes drastically throughout the process. Additionally, large temperature ranges along with the highly dynamic nature of the PBF-LB/M process make temperature measurements difficult. Based on this challenge, this work presents a method for hyperspectral temperature determination. The spectral exitance (in W/m2⋅nm) was measured in situ at many adjacent wavelengths in the short-wave infrared (SWIR). This enabled a local temperature determination via Planck’s law in combination with a spectral emissivity function. The temperature field of the melt pool crossing the 1D measurement line was reconstructed from the information, gathered at nearly 20 kHz sampling rate. The reconstructed melt pool had a spatial resolution of 17 µm by 40 µm, and temperatures between 2700 and 1300 K were observable. Comparison of the 316L stainless steel solidification temperature and the observed solidification plateau in the gathered thermal data revealed a relative error of less than 6% in the absolute temperature measurement. These initial results of hyperspectral temperature determination in PBF-LB/M show the potential in the method. It allows for physically founded process evaluation, and the prospects for tuning and validation of numerical simulations are highly promising. KW - Additive Manufacturing KW - Infrared Thermography KW - In-situ Monitoring KW - Quantitative Temperature Measurement KW - Emissivity PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-631977 DO - https://doi.org/10.1007/s40964-025-01148-8 SN - 2363-9512 SP - 1 EP - 10 PB - Springer Science and Business Media LLC AN - OPUS4-63197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Tina A1 - Stark, T. A1 - Arduini, M. A1 - Manara, J. A1 - Altenburg, Simon T1 - Knowing the spectral directional emissivity of 316L and AlSi10Mg PBF-LB/M surfaces: Gamechanger for quantitative in situ monitoring N2 - For a deep process understanding of the laser powder bed fusion process (PBF-LB/M), recording of the occurring surface temperatures is of utmost interest and would help to pave the way for reliable process monitoring and quality assurance. A notable number of approaches for in-process monitoring of the PBF-LB/M process focus on the monitoring of thermal process signatures. However, due to the elaborate calibration effort and the lack of knowledge about the occurring spectral directional emissivity, only a few approaches attempt to measure real temperatures. In this study, to gain initial insights into occurring in the PBF-LB/M process, measurements on PBF-LB/M specimens and metal powder specimens were performed for higher temperatures up to T = 1290 °C by means of the emissivity measurement apparatus (EMMA) of the Center for Applied Energy Research (CAE, Wuerzburg, Germany). Also, measurements at ambient temperatures were performed with a suitable measurement setup. Two different materials—stainless steel 316L and aluminum AlSi10Mg—were examined. The investigated wavelength λ ranges from the visible range (λ-VIS= 0.40–0.75 µm) up to the infrared, λ = 20 µm. The influence of the following factors were investigated: azimuth angle φ, specimen temperature TS, surface texture as for PBF-LB/M surfaces with different scan angles α, and powder surfaces with different layer thicknesses t. T2 - Rapid.Tech 3D 2024 CY - Erfurt, Germany DA - 14.05.2024 KW - PBF-LB/M KW - In situ monitoring KW - Emissivity KW - Additive manufacturing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601471 DO - https://doi.org/10.1007/s40964-024-00665-2 SN - 2363-9520 SP - 1 EP - 10 PB - Springer CY - Cham, Switzerland AN - OPUS4-60147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Tina T1 - Emissivity – Gamechanger for quantitative in-situ monitoring N2 - For a deep process understanding of the laser powder bed fusion process (PBF-LB/M), recording of the occurring surface temperatures is of utmost interest and would help to pave the way for reliable process monitoring and quality assurance. A notable number of approaches for in-process monitoring of the PBF-LB/M process focus on the monitoring of thermal process signatures. However, due to the elaborate calibration effort and the lack of knowledge about the occurring spectral directional emissivity, only a few approaches attempt to measure real temperatures. In this study, to gain initial insights into occurring in the PBF-LB/M process, measurements on PBF-LB/M specimens and metal powder specimens were performed for higher temperatures up to T = 1290 °C by means of the emissivity measurement apparatus (EMMA) of the Center for Applied Energy Research (CAE, Wuerzburg, Germany). Also, measurements at ambient temperatures were performed with a suitable measurement setup. Two different materials—stainless steel 316L and aluminum AlSi10Mg—were examined. The investigated wavelength λ ranges from the visible range (λ-VIS = 0.40–0.75 µm) up to the infrared, λ = 20 µm. The influence of the following factors were investigated: azimuth angle φ, specimen temperature TS, surface texture as for PBF-LB/M surfaces with different scan angles α, and powder surfaces with different layer thicknesses t. T2 - Rapid.Tech 3D 2024 CY - Erfurt, Germany DA - 14.05.2024 KW - PBF-LB/M KW - In situ monitoring KW - Emissivity KW - Additive Manufacturing PY - 2024 AN - OPUS4-60148 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter T1 - Fundamentals of quantitative temperature determination during laser powder bed fusion of metals (PBF-LB/M) via hyperspectral thermography N2 - Additive manufacturing (AM, also known as 3D printing) of metals is becoming increasingly important in industrial applications. Reasons for this include the ability to realize complex component designs and the use of novel materials. This distinguishes AM from conventional manufacturing methods such as subtractive manufacturing (turning, milling, etc.). The most widely used AM process for metals is laser powder bed fusion (PBF-LB/M, also known as selective laser melting SLM). Currently, it has the highest degree of industrialization and the largest number of machines in use. In PBF-LB/M, the feedstock is present as metal powder in an inert gas atmosphere inside a process chamber where a laser melts it locally. By repeatedly lowering the build platform, applying a new layer of powder, and then selectively melting it with the laser, a component is built up layer by layer. The local temperature distributions that occur during this process determine not only the properties of the finished component, but also the possible formation of defects such as pores and cracks. Due to the high relevance of the thermal history for precise geometries and defect formation, a temporally and spatially resolved measurement of quantitative (or real/actual) temperatures would be optimal. Quantitative values would ensure comparability and repeatability of the AM process which would also positively affect the quality and safety of the manufactured component. Furthermore, it would also contribute to the validation of simulations and to a deeper understanding of the manufacturing process itself. At present, however, only qualitative monitoring of the thermal radiation is performed (e.g., by monitoring the melt pool using a photodiode), and safety-relevant components must be inspected ex situ afterwards which is time-consuming and costly. A reason for the lack of quantitative temperature data from the process are the challenging conditions of the PBF-LB/M process with high scanning speeds and a small laser spot diameter. Furthermore, the emissivity of the surface changes at high dynamics (temporally/spatially) as well as with temperature and wavelength. This specifically makes contactless temperature determination based on emitted infrared radiation challenging for PBF-LB/M. Although classical thermography offers very good qualitative insights, it is not sufficient for a reliable quantitative temperature determination without a complex temperature calibration including image segmentation and assignment of previously determined emissivities. For this reason, this publication presents the hyperspectral thermography approach for the PBF-LB/M process: The emitted infrared radiation is measured simultaneously at many adjacent wavelengths. In this study, this is realized via a fast hyperspectral line camera that operates in the short-wave infrared range. The thermal radiation of a line on the target is spectrally dispersed and detected to measure the radiant exitance along that line. If the melt pool of the PBF-LB/M process moves through this line at a sufficient frame rate, a spatial reconstruction of an effective melt pool is possible. One approach to determine the desired emissivities and the quantitative temperature from this hyperspectral data are temperature-emissivity separation (TES) methods. A major problem is that n spectral measurements are available, but n+1 parameters are required for each image pixel (n emissivity values + one temperature value). TES methods offer the possibility to approximate this mathematically underconstrained problem in a reliable and traceable way by analytically parameterizing the spectral emissivity with a few degrees of freedom. Using this approach, setup and method are applied to a research machine for PBF-LB/M, called SAMMIE (Sensor-based Additive Manufacturing Machine). First results under AM process conditions are shown which form the basis for the determination of quantitative temperatures in the PBFLB/M process. This marks an important contribution to improving the comparability and repeatability of production, validating simulations, and understanding the process itself. When fully developed and validated, the presented method can also provide reference measurements to evaluate and optimize other, more practical monitoring methods, such as melt pool monitoring or optical tomography. In the long run, this will help to increase confidence in the safety of AM products. T2 - QIRT 2024 CY - Zagreb, Croatia DA - 01.07.2024 KW - Additive Manufacturing KW - Additive Fertigung KW - Real Temperature KW - Melt Pool KW - Emissivity PY - 2024 AN - OPUS4-60762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Forero-Sandoval, I. A1 - Cervantes-Alvarez, F. A1 - Ramirez-Rincon, J. A1 - Macias, J. A1 - Pech May, Nelson Wilbur A1 - Ordonez-Miranda, J. A1 - Alvarado-Gil, J. T1 - Percolation Threshold of the Thermal, Electrical and Optical Properties of Carbonyl-Iron Microcomposites N2 - Composites made up of microparticles embedded in a polymeric matrix have attracted increasing attention due to the possibility of tailoring their physical properties by adding the adequate quantity of fillers. As the concentration of these fillers increases, their connectivity changes drastically at a given threshold and therefore the electrical, thermal and optical properties of these composites are expected to exhibit a percolation effect. In this work, the thermal and electrical conductivities along with the emissivity of Composites composed of carbonyl-iron microparticles randomly distributed in a polyester resin matrix are measured, for volume fractions ranging from 0 to 0.55. It is shown that both the thermal and electrical conductivities increase with the particles’ concentration, such that their percolation threshold appears at volume fractions of 0.46 and 0.38, respectively. The emissivity, on the other hand, decreases as the fillers’ concentration increases, such that it exhibits a substantial decay at a volume fraction of 0.41. The percolation threshold of the emissivity is thus higher than that of the thermal conductivity, but lower than the electrical conductivity one. This dispersion on the percolation concentration is justified by the different physical mechanisms required to activate the electrical, thermal, and optical responses of the considered composites. The obtained results thus show that the percolation phenomenon can efficiently be used to enhance or reduce the physical properties of particulate composites. KW - Thermal conductivity KW - Emissivity KW - Thermal percolation threshold PY - 2021 DO - https://doi.org/10.1007/s10443-021-09869-z VL - 28 IS - 2 SP - 447 EP - 463 PB - Springer AN - OPUS4-52355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Rehmer, Birgit A1 - Gower, M. A1 - Baker, G. A1 - Lodeiro, M. A1 - Aktas, A. A1 - Monte, C. A1 - Adibekyan, A. A1 - Gutschwager, B. T1 - Defect characterisation of tensile loaded CFRP and GFRP laminates used in energy applications by means of infrared thermography N2 - The increased use of fibre reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications, e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. In this contribution, results concerning the characterisation of CFRP and GFRP during and after quasi-static tensile loading are presented. It includes the measurement of optical properties in the infrared spectral range, tensile loading tests with the observation of the temperature distribution at one or both sides of the specimens using an infrared camera for the preparation and monitoring of intended natural defects, and active thermography inspections after tensile loading. It is shown that the defect preparation was successful. Thermographic monitoring during and active thermography testing after tensile loading enable the detection of the lateral extend of the generated defects. Differences between CFRP and GFRP materials are discussed. KW - Tensile loading KW - Fibre reinforced composites KW - Active and passive thermography KW - Emissivity PY - 2017 DO - https://doi.org/10.1080/17686733.2017.1334312 SN - 1768-6733 SN - 2116-7176 VL - 15 IS - 1 SP - 17 EP - 36 PB - Taylor and Francis CY - London AN - OPUS4-40968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane T1 - Characterisation of artificial and natural defects in fibre reinforced plastics designed for energy applications using active thermography - EMRP VITCEA N2 - Amongst various other NDT methods, within the EMRP-project ‘VITCEA’ active thermography is validated for testing of CFRP and GFRP structures constructed for energy application. In this contribution, the optical and thermal properties of CFRP and GFRP reference defect artefact (RDA) and natural defects artefact (NDA) test specimens are characterized. Different excitation techniques and techniques for data analysis are compared for optimizing the number of detected defects. T2 - 19th World Conference on Non-destructive Testing (WCNDT) CY - Munich, Germany DA - 13.06.2016 KW - Active thermography KW - CFRP KW - GFRP KW - Artificial and natural defects KW - Emissivity PY - 2016 AN - OPUS4-36700 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -