TY - CONF A1 - Bäßler, Ralph A1 - Pötzsch, Sina A1 - Weltschev, Margit T1 - Compatibility of polymers exposed to heating oil blends with 10 % and 20 % biodiesel (FAME) N2 - Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers. The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion. The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1. It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR. T2 - AMPP Annual International Corrosion Conference CY - Online Meeting DA - 19.04.2021 KW - Biodiesel KW - FAME KW - RME KW - Polymer in fuels KW - Corrosion PY - 2021 AN - OPUS4-52498 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Sina A1 - Bäßler, Ralph A1 - Weltschev, Margit T1 - Resistance of metals exposed to heating oil blends with 10 % and 20 % biodiesel (FAME) N2 - In Europe biodiesel gained from rapeseeds are considered as an alternative to common fossil fuels due to its environmental performance and its independence from import of raw materials. Biodiesel is also suitable to serve as blending component to heating oil. In that case, it must be considered that changes of fuel composition might cause material degradation. The objective of this research was to investigate the resistance of metallic materials exposed to heating oil, heating oil blend B20 with 20 % biodiesel and pure biodiesel. Furthermore, the resistance of metals to eight-year aged B10 and six-year aged pure biodiesel was evaluated. Ageing of biodiesel forms acids and water which might propagate metal corrosion. The investigated metals (aluminium, unalloyed steel, austenitic CrNi-steel, copper, die cast zinc and brass) are commonly used for components in middle distillate facilities. According to DIN 50905-4 the immersed metals were exposed in a climate chamber at 50°C for 4 weeks. The metallic materials were evaluated as resistant if the annual corrosion rate due to uniform corrosion remained under 0.1 mm/year and no localized corrosion in the form of pitting occurred. The corrosion rates of the exposed materials stayed far below the limit of 0.1 mm/year for all tested fuels. An exception was die cast zinc ZP0410 in eight-year aged B10; a corrosion rate up to 0.3 mm/year due to uniform corrosion was measured. In no case localized corrosion occurred. Copper and brass caused discolouration of biodiesel from yellow to green. In conclusion, the tested metallic materials were resistant in heating oil, heating oil blend B20 and pure biodiesel at 50 °C. Even the metals exposed to six-year aged biodiesel and eight-year aged B10 showed no uniform or localized corrosion; except for zinc, which was not resistant in eight-year aged B10. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Metals KW - Heating oil KW - Biodiesel KW - RME KW - Corrosion KW - Compatibility KW - FAME PY - 2019 AN - OPUS4-49137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Sina A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Entwicklung einer Prüfmethode zur Bewertung der Materialbeständigkeit von Bauteilen in Mitteldestillatanwendungen N2 - Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungs­effekte des Mediums einzubeziehen. Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. T2 - DGMK-Projekttreffen CY - Hamburg, Germany DA - 24.10.2019 KW - Heizöl KW - Beständigkeitsbewertungen KW - Biodiesel KW - FAME KW - HVO PY - 2019 AN - OPUS4-50272 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Beständigkeit von Fluorkautschuk in Kraftstoffen und Heizöl mit biogenen Anteilen unter Druckbeanspruchung N2 - Die Bewertung der Werkstoffbeständigkeit ist von großer Bedeutung bei Änderung der Zusammensetzung der Kraftstoffe und des Heizöls, insbesondere die Frage nach der Beständigkeit der Dichtungswerkstoffe bei Zusätzen von Bioethanol und Biodiesel (Rapsölfettsäuremethylester). Vorhergehende Untersuchungen (Messungen der Veränderungen der Masse, der Zugeigenschaften und der Härte) bezogen sich auf die Bewertung der Beständigkeit häufig verwendeter Dichtungswerkstoffe wie FKM, FVMQ, VMQ, EPDM, CR, CSM, IIR, PA, NBR und PUR in Kraftstoffen und Heizöl mit 10 % Biodiesel (nicht gealtert und bis zu 5 Jahre gealtert) unter statischen Bedingungen. Ziel der Untersuchungen war die Bewertung der Beständigkeit von Fluorkautschuk unter verpressten Bedingungen in Analogie zu den Einsatzbedingungen in der Praxis. Die Masse und der Druckverformungsrest von Prüfkörpern aus FKM wurden vor und nach der Auslagerung über einen Zeitraum von 3, 7, 14, 28, 56 und 90 Tagen in E10 (Kraftstoff mit max. 10 % Ethanol), E85 (Kraftstoff mit 85 % Ethanol), Biodiesel (Rapsölfettsäuremethylester), Super (Kraftstoff mit max. 5 % Ethanol), Dieselkraftstoff mit max. 5 % Biodiesel, Super Plus (Kraftstoff ohne Ethanolzusatz) und Heizöl mit 10 % Biodiesel (B10) bei 40 °C gemäß ISO 815-1 bestimmt. Die Druckverformungsrestprüfung zählt neben der Messung der Härte, der Dichte und der Zugeigenschaften zu den wichtigsten Grundprüfverfahren der Elastomerindustrie. Nach Ende der Auslagerung in den Kraftstoffen und der Aufhebung der Verpressung wur-de der Druckverformungsrest der Prüfkörper in regelmäßigen Zeitabständen bis zu einer Rücktrocknung > 90 Tage bestimmt. Zum Vergleich wurden Prüfkörper aus FKM ohne Kraftstoff oder Heizöl unter Verpressung bei 40 °C ausgelagert. Die Masseänderung der Prüfkörper aus FKM betrug nach 90 Tagen Auslagerung in E10 9 %, in Super 8 %, in E85 4% und 0,6 % in Biodiesel. Die Erhöhung der Masse und die damit verbundene Quellung der Prüfkörper in E10 und Super mit 5 – 10% Ethanolzusatz hatte einen Einfluss auf den Druckverformungsrest, der sprunghaften Veränderungen unterlag im Vergleich zu den Werten nach Auslagerung in Biodiesel, Dieselkraftstoff und Heizöl B10 bei 40 °C. Zum Vergleich, unter statischen Bedingungen verringerte sich die Zugfestigkeit der Prüfkörper aus FKM nach Auslagerung in E10 bei 40 °C um 31 % und die Reißdehnung um 18 %. T2 - Gastvortrag im Rahmen des Seminars: Ausgewählte Kapitel der Werkstofftechnik an der Bergischen Universität Wuppertal CY - Wuppertal, Germany DA - 11.01.2019 KW - Dichtungswerkstoffe KW - Beständigkeit in Biokraftstoffen KW - Biodiesel KW - Heizöl mit 10% Biodiesel KW - E10 (Kraftstoff mit bis zu 10% Ethanol) PY - 2019 AN - OPUS4-47222 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Otremba, Frank A1 - Sklorz, Christian A1 - Rehfeldt, Rainer T1 - Impact of biocomponents in the fuel and heating oil on the compatibility of fluorocarbon rubber under compressed conditions N2 - Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether sealing materials are resistant to fuels with bioethanol and biodiesel (rapeseed oil fatty acid methyl ester). Previous research considered the resistance of frequently used sealing materials such as FKM (fluorocarbon rubber), FVMQ (methyl-fluoro-silicone rubber), VMQ (methyl-vinyl-silicone rubber), EPDM (ethylene-propylene-diene rubber), CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), IIR (butyl rubber), PA (polyamides), NBR (acrylonitrile-butadiene rubber) and PUR (polyester urethane rubber) in fuels and heating oil with admixtures of biogenic substances such as biodiesel and B10 (heating oil with 10 % biodiesel) under purely static conditions. The aim of this study was to evaluate the fluorocarbon rubber performance under compressed conditions. For the investigations, the mass and the compression set of the FKM test specimens were determined before and after exposure for 3, 7, 14, 28, 56 and 90 days in E10 (fuel with 10 % ethanol), E85 (fuel with 85 % ethanol), biodiesel (fatty acid methyl ester, FAME), Super (fuel with max. 5 % ethanol), diesel fuel with max. 5 % biodiesel, pure diesel fuel, Super Plus (fuel without ethanol) and heating oil with 10 % biodiesel (B10) at 40 °C according to ISO 815-1 “Rubber, vulcanized or thermoplastic - determination of compression set – Part 1: At ambient or elevated temperatures”. The compression set test belongs beside the determination of the Shore hardness, the density and the tensile properties to the basic test methods for elastomers. It was measured in regular time intervals up to a re-drying of more than 90 days after relaxation of test specimens. For comparison, FKM test specimens were exposed without fuel under compressed conditions at 40 °C. The highest mass increase of FKM test specimens was measured after 90 days exposure in E10 by 9 %, followed by 8 % in Super fuel, by 4 % in E85 and by 0.6 % in biodiesel. Mass increase and swelling of the test specimens in E10 and Super fuel with max. 5 % ethanol had an influence on the compression set values which were subject to high fluctuations in comparison to the values obtained after exposure to other fuels such as biodiesel, diesel fuel and B10. The results of the present work confirmed the higher swelling of the elastomers such as FKM in E10 obtained under static condition. It can be concluded on the basis of the mass increase and compression set values that FKM is resistant in all fuels under compressed conditions at 40 °C. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Sealing materials KW - Compression set KW - Compatibility KW - Fuels KW - Heating oil KW - Biodiesel KW - Bioethanol PY - 2018 AN - OPUS4-45935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erdmann, Maren A1 - Wachtendorf, Volker A1 - Böhning, Martin A1 - Niebergall, Ute T1 - PE-HD as a polymeric fuel storage tank material: Photooxidation, fuel sorption and long-term storage N2 - High-density polyethylene (PE-HD) is a commodity thermoplastic polymer which is typically used for packing of dangerous goods. Its good resistance against photooxidation, fuels, chemicals and other environmental factors in addition to low production costs makes PE-HD attractive for fuel storage applications. Typical engine fuels stored in polymer tanks are petrol, diesel and biodiesel that receives increasing attention as proper alternative to fossil fuels. One of the major problems with biodiesel is its susceptibility to oxidize due to its chemical composition of unsaturated fatty acids which also can cause polymer degradation. The aim of this study is to investigate the influence of different environmental factors, UV radiation and commonly stored fuels, on the mechanical, physical and chemical properties of two types of PE-HD polymers (stabilized and non-stabilized). The influence on the mechanical properties was tested by Charpy and tensile tests, chemical and physical properties were evaluated by Fourier-transform infrared spectroscopy (FTIR) and by dynamical mechanical analysis (DMA) tests. Samples were characterized after varying exposure time of UV radiation and after fully and partially immersion in biodiesel. In addition, similar experiments were conducted using diesel for comparison. T2 - MoDeSt2018 CY - Tokio, Japan DA - 02.09.2018 KW - PE-HD KW - Biodiesel KW - UV-irradiation KW - Long-term storage KW - Diesel PY - 2018 AN - OPUS4-45894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Compatibility of sealing materials with biofuels and biodiesel heating oil blends at different temperatures N2 - The objective of this research was to determine the resistance of frequently used sealing materials such as FKM (fluorocarbon rubber), FVMQ (methyl-fluoro-silicone rubber), VMQ (methyl-vinyl-silicone rubber), EPDM (ethylene-propylene-diene rubber), CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), IIR (butyl rubber), PA (polyamides), NBR (acrylonitrile-butadiene rubber) and PUR (polyester urethane rubber) in fuels and heating oil with admixtures of biogenic sources such as E10 (fuel with 10 % ethanol), E85 (fuel with 85 % ethanol), non-aged and aged biodiesel, diesel fuel with 5 % biodiesel, non-aged and aged B10 (heating oil with 10 % biodiesel) at 20 °C, 40 °C and 70 °C. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the fuels. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens in the biofuels for 42 days. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore a threshold of 15 % was determined for the evaluation of the compatibility. In summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one. T2 - 13th International Congress on Biofuels & Bioenergy CY - Ottawa, Canada DA - 18.10.2018 KW - Sealing materials KW - Biodiesel KW - Diesel fuel KW - Heating oil with 10 % biodiesel KW - Tensile properties KW - Shore hardness KW - Fuel with 10 % ethanol PY - 2018 AN - OPUS4-46358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus A1 - Niebergall, Ute A1 - Böhning, Martin T1 - Damage of PE-HD due to environmental stress cracking (ESC) induced by liquid media - Full Notch Creep Testing (FNCT) N2 - Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications. Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant mechanisms of damage. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure. To characterize the intrinsic resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used and of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD. In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigations of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed. The underlying diffusion-controlled sorption process was assessed before comparing non-saturated specimens with samples previously saturated with sorbing media. The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation. In addition to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Fracture surface analysis (LM, LSM) and quasi in-situ imaging (CT scan) via measurement in different load stages are considered explicitly. Correlations of elongation behavior and data derived from imaging analysis such as fracture plane roughness and height of areas of ductile deformation were obtained. T2 - EUROCORR2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - Environmental stress cracking (ESC) KW - Slow crack growth (SCG) KW - High-density polyethylene (PE-HD) KW - Full notch creep test (FNCT) KW - Biodiesel KW - Diesel PY - 2017 AN - OPUS4-43518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus A1 - Niebergall, Ute A1 - Böhning, Martin T1 - Environmental stress cracking (ESC) of PE-HD induced by liquid media N2 - Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications. Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant damage mechanisms. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure. To characterize the inherent resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used. Therefore, the FNCT is of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD – especially in the field of polymer development and improvement for high-performance applications. In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigation of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed. The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation. Additional to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Correlations of elongation behavior and data derived from imaging analysis were obtained. T2 - Europe / Africa Conference 2017 of the Polymer Processing Society (PPS) CY - Dresden, Germany DA - 26.06.2017 KW - Environmental stress cracking (ESC) KW - Full Notch Creep Test (FNCT) KW - High-density polyethylene (PE-HD) KW - Biodiesel PY - 2017 AN - OPUS4-43519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Evaluation of the resistance of metallic materials under the influence of biofuels N2 - Changes in fuel composition and the introduction of alternative fuels often create problems of corrosion and degradation in materials. The objective of this research was to determine the corrosion behaviour of commercial metallic tank materials (unalloyed steels, austenitic CrNi- and CrNiMo-steels, aluminium and its alloys) in fuels and heating oil with admixtures of biogenic sources, such as gasoline with addition of ethanol (E10, E85), pure biodiesel and heating oil with 10 % biodiesel (B10). Metallic tank materials were evaluated as resistant in a liquid if the annual corrosion rate due to uniform corrosion did not exceed 0.1 mm/year, and localized corrosion effects in the form of pitting corrosion, stress corrosion cracking and crevice corrosion did not occur. The corrosion rates of the tank materials after exposure to E10, E85, non-aged and two-year aged pure biodiesel, and non-aged and one-year aged heating oil B10 for four weeks at 50 °C, according to DIN 50905/4, were well below the limit of 0.1 mm/year. For the unalloyed steels, the formation of rust was observed independently of the biofuels amount of ageing. U-bend specimens made of unalloyed steel were not damaged in form of stress corrosion cracking in all test fuels at this test temperature. T2 - CORROSION 2017 CY - New Orleans, LA, USA DA - 26.03.2017 KW - Biodiesel KW - Bioethanol KW - Tank materials KW - Corrosion resistance KW - Stress corrosion cracking PY - 2017 AN - OPUS4-39642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -