TY - CONF A1 - Gräning, Dirk T1 - Sliding wear tests of martensitic steels in hydrogen – the role of water traces N2 - The martensitic steels X30CrMoN15-1 and 100Cr6 did not show any hydrogen enhanced wear in sliding friction tests against alumina balls in hydrogen gas environment. However, depending on the purity of the environment, unexpected high wear occurred at the alumina ball. The results of a tests series with a broad variation of test parameters are presented. T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - Tribology KW - Hydrogen environment KW - Alumina KW - Martensitic steel KW - Adsorbed water film PY - 2016 AN - OPUS4-40119 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gräning, Dirk A1 - Gradt, Thomas T1 - Sliding wear of martensitic steels in hydrogen – X30CrMoN15-1 and 100Cr6 – the role of water traces N2 - Die Untersuchung befasste sich ursprünglich mit dem Einfluss von gasförmigem Wasserstoff bei Normaldruck auf den Verschleiß von martensitischen Stählen. Dabei wurde als Gegenkörper eine Al2O3-Kugel verwendet, da dieser Werkstoff inert und zugleich hart ist und somit immer einen geringen Abtrag aufweisen sollte. Um 1 ppm Wasserstoff ohne thermomechanische Unterstützung in reines α-Eisen zu drücken, wird nämlich ein Druck von 15·105 MPa(~15 Mbar) benötigt. In der Versuchsreihe wiesen die Al2O3-Kugel in N2- und H2-Atmosphäre einen hohen Verschleiß auf, während bei Luft-Versuchen die Spur klein und der Verschleiß an der Scheibe groß war. Durch Streuungen und daraus folgenden Untersuchungen zeigte sich, dass Wasserstoff keinen merkbaren Einfluss hatte, Wasserspuren im Gas aber dafür umso deutlicher den Verschleiß beeinflussten. N2 - Initially the primary objective of the project has been the investigation of the influence of gaseous hydrogen on the wear of martensitic steels under heavy tribological stress. As a counter body an Al2O3 ball has been used because the material is inert and hard so that a low amount of wear was expected. If only the gas pressure is responsible for the absorption of hydrogen from the gas to pure α-iron it would require 15·105 MPa (~15 Mbar) to press 1 ppm into the material. In the test series the Al2O3 balls showed in N2 and H2 atmosphere a higher wear compared to aerial experiments which showed a smaller wear track and a severer wear for the disc. Because of scattering and thereof following investigations it was shown that hydrogen has no noticeable influence but water traces in the gas are manipulating the outcome of the tests distinctly. T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - Tribology KW - Hydrogen environment KW - Alumina KW - Martensitic steel KW - Adsorbed water film PY - 2016 SN - 978-3-9817451-1-5 VL - 2016 SP - 1.3/1 EP - 1.3/6 AN - OPUS4-40105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -