TY - CONF A1 - Winckelmann, Alexander T1 - Fluorine Depth Profiling in Lithium-Ion Battery Materials by GD-OES N2 - Lithium-ion batteries are a key technology for tackling challenges in energy and climate crisis, but up to 30 % are discarded right after production. Quality is closely related to the homogeneity of the used materials and coatings. Fluorine compounds, both in the polymer and from degradation of the electrolyte, are of special interest for the formation and aging of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) emerged as a fast and convenient method for depth-profiling of battery materials. However, fluorine remains a spectroscopic challenge due to a high excitation energy and only few strong emission lines in the UV/Vis spectral range. We investigated the partial substitution of argon with neon in the plasma gas. The main emission line at 685.603 nm was monitored by both photo multiplier tube (PMT) with Czerny-Turner monochromator at 20 µm slit-size, and charge-coupled device (CCD) with 1200 lines/mm grating. For calibration, we used a set of hot-pressed copper cylinders with varying calcium fluoride amount fraction, ranging from 1.6 % to 4.4 %. Plasma gas mixtures with a mole fraction of 5 %, 10 % and 20 % neon in argon were used. Sensitivity in comparison to pure argon was increased by factor 4, 7 and 14, respectively. In general, PMT detection was more sensitive than CCD. As expected, sputter rates decreased with higher neon content in the plasma gas. Depth-profiling of the cathodes was performed in pulsed mode at constant voltage and pressure, which resulted in stable plasma conditions. We achieve matrix-independent quantitative information on fluorine distribution by correction based on sputter rates. This advancement in GD-OES provides a more accurate analytical approach for evaluating the homogeneity of lithium-ion battery materials, potentially leading to more sustainable and cost-effective manufacturing processes. T2 - 6th International Glow Discharge Spectroscopy Symposium CY - Liverpool, United Kingdom DA - 21.04.2024 KW - Lithium Ion Batteries KW - GD-OES KW - depth-profiling KW - fluorine PY - 2024 AN - OPUS4-60200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winckelmann, Alexander T1 - Investigation of degradation of the aluminum current collector in lithium-ion batteries by glow-discharge optical emission spectroscopy N2 - Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs. T2 - Adlershofer Forschungsforum 2022 CY - Berlin, Germany DA - 11.11.2022 KW - Lithium Ion Batteries KW - GD-OES KW - FIB KW - SEM KW - EDX PY - 2022 AN - OPUS4-56246 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -