TY - CONF A1 - Schwenk, C. A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - Restraint conditions and welding resiudal stresses in self-restrained cold cracking test N2 - In the last decade, high-strength fine grained steels and welding consumables have gained a strong raise of application ranging from mobile cranes to bridge constructions. However, the cracking susceptibility of these steels increases significantly in correspondence with the achieved improvements in yield strength and the loss in plastic deformation reserves. In order to determine this behavior a series of different standardized cold cracking tests has been developed. One remaining major problem of these tests is the uncertainty about the quantitative intensity of the restraint conditions as well as the corresponding welding residual stresses. Consequently, the comparison of different tests and welding conditions as well as the transferability of the results onto real parts is difficult at best. The main topic of this paper is the analysis of the restraint conditions and their link with the welding induced residual stresses. The importance of the given standardized selfrestrained tests and first results about the transferability of results onto real parts are discussed. The influence of the test specimen geometry on the restraint conditions of the test is investigated for a selected test with numerical Simulation using commercial FEA software. Additionally, the residual stresses caused by the welding process are measured and linked with the restraint conditions which are defined mainly by the geometry parameters. Finally the transferability of the selected cold cracking test results is validated experimentally. The test results of a multilayer weld on high-strength fine grained steel of real size weldments are investigated. For these experiments a 16 MN large scale testing facility is used which is capable of applying the high reaction forces and clamping conditions found at large scale demonstrator parts. The results show the importance of the quantitative knowledge of the restraint conditions and the welding residual stresses on the cold cracking resistance. T2 - 8th International Conference on Trends in Welding Research CY - Pine Mountain, USA DA - 01.06.2008 KW - Cold Cracking Test KW - Intensity of Restraint PY - 2008 DO - https://doi.org/10.1361/cp2008twr766 SP - 766 EP - 771 PB - ASM international AN - OPUS4-47623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Rethmeier, Michael T1 - Spot welding and weldbonding of high strength steels for lightweight auto body manufacturing N2 - The resistance spot weiding procedure is one of the most important joining technique in lightweight car body shell mass production. Especially for newly developed ultra high strength steels (UHSS) and advanced high strength steels (AHSS), this joining technique has more advantages than other thermal and mechanical joining procedures for thin Steel sheets. Additionally, the technique of adhesive bonding and its combination with the technique of resistance spot weiding called weldbonding becomes more and more important. The weldbonding affords many advantages, e.g. improved crash performance, fatigue behaviour and corrosion resistance. The main target of the contribution is to show the influence of different joined ultra and advanced high strength steels on the process reliability for both the resistance spot weiding process and the weldbonding process. In this connection the influence of surface conditions of the steel sheets, the applied adhesive and the choice of the weiding parameters on the process reliability will be studied. The results for the weldbonding procedure are based on different adhesives. Based on the representation of weiding current ranges by weldability lobes, Statements concerning the weldbonding process reliability for some special AHSS and UHSS will be given. The mechanical behaviour of spot welded and weldbonded joints for different AHSS and UHSS will be studied. T2 - EUROJOIN 8 - 8th European conference CY - Pula, Croatia DA - 24.05.2012 KW - Spot welding KW - Weldbonding KW - High strength steels KW - Process reliability KW - Mechanical properties of joints PY - 2012 SP - 633 EP - 643 AN - OPUS4-26383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Liu, X. C. A1 - Wu, Chuan Song A1 - Rethmeier, Michael A1 - Pittner, Andreas T1 - Mechanical properties of 2024-T4 aluminium alloy joints in ultrasonic vibration enhanced friction stir welding N2 - Ultrasonic vibration enhanced friction stir welding (UVeFSW) is a recent modification of conventional friction stir welding (FSW), which transmits ultrasonic vibration directly into the localized area of the workpiece near and ahead of the rotating tool. In this study, a high strength aluminium alloy (2024-T4) was welded by this process and conventional FSW, respectively. Then tensile tests, microhardness tests and fracture surface analysis were performed successively on the welding samples. The tests results reveal that ultrasonic vibration can improve the tensile strength and the elongation of welded joints. The microhardness of the stir zone also increases. KW - Ultrasonic vibration KW - Friction stir welding KW - Mechanical properties PY - 2013 UR - https://www.researchgate.net/publication/286735810_Mechanical_properties_of_2024-T4_aluminium_alloy_joints_in_ultrasonic_vibration_enhanced_friction_stir_welding VL - 22 IS - 4 SP - 8 EP - 13 AN - OPUS4-40773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Laserstrahl-Hybridschweißen für Rohranwendungen N2 - Mechanische Eigenschaften der laserhybridgeschweißten Schweißverbindungen von hochfesten niedriglegierten Stählen erfüllen die Anforderungen der geltenden Normen Eindringtiefe des Zusatzwerkstoff bis ca. 12 mm Halborbitales Schweißen an 36” Rohren mit einer Wandstärke von 16 mm bei einer Schweißgeschwindigkeit von bis zu 2,2 m/min und Laserleistung von 19 kW technisch möglich Rissfreie Schweißverbindungen an Präzisionsrohren können durch eine geeignete Schweißparameterauswahl mittels Laser-Hybridverfahren hergestellt werden T2 - IW-Kolloquium CY - Hannover, Germany DA - 07.05.2014 KW - Laserstrahlquelle KW - Hybridprozesse KW - MSG-Schweißen PY - 2014 AN - OPUS4-38338 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Experimental and numerical investigation of an electromagnetic weld pool control for laser beam welding N2 - Drop-out of molten material was avoided by EM pressure Compensation of the hydrostatic pressure of up to 20 mm thick aluminum and stainless steel (experiment and FEM) Mitigation of the weld bead dynamics Significant changes in the velocity distributions in the weld pool Weld pool geometry shape changes due to Hartmann effect Significant porosity reduction Surface quality improvements T2 - LANE 2014 -8thInternational Conference on Photonic Technologies CY - Fürth, Germany DA - 08.09.2014 KW - Welding of thick metal plates KW - AC weld pool support KW - Welding of aluminum KW - Welding of AlMg3 PY - 2014 AN - OPUS4-38349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Experimental and numerical investigation of an electromagnetic weld pool control for laser beam welding N2 - Drop-out of molten material was avoided by EM pressure Compensation of the hydrostatic pressure of up to 20 mm thick aluminum and stainless steel (experiment and FEM) Mitigation of the weld bead dynamics Significant changes in the velocity distributions in the weld pool Weld pool geometry shape changes due to Hartmann effect Significant porosity reduction Surface quality improvements T2 - LANE 2014 -8thInternational Conference on Photonic Technologies CY - Fürth, Germany DA - 08.09.2014 KW - Welding of thick metal plates KW - AC magnetic fields KW - AC weld pool support KW - Welding of aluminum PY - 2014 AN - OPUS4-38368 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Influence of weld imperfections on the fatigue behaviour of resistance spot welded advanced high strength steels N2 - The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested Surface cracks havenoinfluenceon thefatiguelife Samples with cracks in the electrode indentation /HAZ where tested Stiffness curves are not significantly influenced by surface cracks 3D FE-Simulation demonstrate no changes of stress due to surface imperfections T2 - 11th International Fatigue Congress CY - Melbourne, Australia DA - 02.03.2014 KW - 3D FE-simulation KW - Cracks in the HAZ PY - 2014 AN - OPUS4-38343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Bakir, Nasim T1 - Numerical simulation of solidification crack formation during laser beam welding of austenitic stainless steels under external load N2 - Solidification cracking phenomena taking place under Controlled Tensile Weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a three dimensional finite element model employing the contact elements technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure the resulting strain and displacement directed to the laser beam in the Close vicinity of the weld pool was measured at the surface of the workpiece using a Digital Image Correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good Agreement with those observed in experiments. T2 - The 3rd IIW South‐East European Welding Congress CY - Timisoara, Romania DA - 03.06.2015 KW - Solidification cracking KW - DIC technique KW - Laser beam welding KW - Contact element KW - FEA PY - 2015 SN - 978-606-554-955-5 SP - 1 EP - 6 CY - Timisoara, Romania AN - OPUS4-36519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, Torsten A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up strategies for generating components of cylindrical shape with laser metal deposition N2 - Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process. T2 - Lasers in Manufacturing Conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Ti - 6Al - 4V KW - Additive Manufacturing KW - Build - up Strategy KW - Laser Metal Deposition KW - Stainless Steel PY - 2015 UR - http://www.wlt.de/lim/Proceedings/Stick/sessions.html SP - 1 EP - 6 AN - OPUS4-37829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Na, S.-J. A1 - Han, S.-W. A1 - Muhammad, S. A1 - Zhang, L. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Karhu, M. A1 - Kujanpa, V. T1 - Flow and Bead Formation Characteristics in High Power Laser Welding at Different Welding Positions (Invited Talk) N2 - The numerical simulations of high power laser keyhole welding at different welding positions are performed by using Volume-Of-Fluid (VOF) method. The main material is SS400. The multi-physics phenomenon is considered using several models, such as the heat flux of Gaussian heat source, the recoil pressure with Clausisus-Clapeyron equation, the Marangoni flow considering temperature gradient, the buoyancy force with Boussinesq approximation, the additional shear stress and heat source due to metallic vapor ejected through keyhole entrance, the bubble formation assumed as adiabatic bubble, and the multiple-reflection by solving proper discriminant, are used. To analyze the fluid flow pattern, the concept of streamline formed by reconstructing the value of the velocity vector is applied. Partial and full penetration cases at different welding positions are considered. The welding position seems to have only a minor influence on bead formation characteristics in both cases. This is probably due to the fact that the recoil pressure has a major influence when compared to other driving forces. The flow characteristics and fluid velocity in weld pool are analyzed to compare the gravity direction effect at different welding positions. It is observed that the clockwise flow pattern is mainly formed by the recoil pressure on the keyhole surface in the case of partial penetration. The laser energy can't maintain the whole weld pool when the weld pool size becomes too large. And then the solidification starts from the middle part of weld pool and a necked weld pool shape is formed. In the full penetration welding, the weld pool flow patterns are affected by the leakage of laser power through the full penetration keyhole and also by surface tension. Furthermore, the numerical simulation of full penetration welding with AISI316L is also performed to analyze the effect of material properties. The weld bead shapes obtained by simulations were compared with the corresponding experimental results to confirm the validity of the process models adopted and the CFD simulation tool. T2 - Lasers in Manufacturing Conference 2015 CY - München, Germany DA - 22.06.2015 KW - Macro Processing (Joining, Welding) KW - Weld pool KW - Flow pattern KW - Different welding position KW - Numerical simulation KW - High power laser keyhole welding PY - 2015 SP - 1 EP - 6 AN - OPUS4-37163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -